Methods of synthesizing nano-sized tungsten particles by sol-gel process and method of preparing light oil from extra-heavy oil using the synthesized nano-sized tungsten particles

Abstract

Disclosed is a method of synthesizing nano-sized tungsten-silica core-shell particles by a silica-based sol-gel process. According to the method, tungsten-silica nanoparticles are very easy to synthesize by a simple process at ambient pressure and temperature. In addition, tungsten oxide-silica (WO.sub.x@SiO.sub.2) nanoparticles including tungsten in a stable oxidation state can be synthesized. In the tungsten oxide-silica nanoparticles, the size of the tungsten protected with the silica shell can be maintained in the nanometer range without further processing. Also disclosed is a method of synthesizing nano-sized tungsten oxide (WO.sub.x) and tungsten carbide (WC) particles by further processing of the tungsten-silica core-shell particles.

Claims

1. A method of synthesizing tungsten-silica nanoparticles: comprising (a) dissolving a tungsten precursor and a surfactant in an organic solvent to obtain a mixture solution; (b) dissolving water, aqueous ammonia, and a silica precursor in the mixture solution to synthesize tungsten oxide-silica core-shell nanoparticles; and (c) dispersing the mixture solution containing the tungsten oxide-silica core-shell nanoparticles in a solvent to precipitate the tungsten oxide-silica core-shell nanoparticles and drying the precipitates.

2. The method according to claim 1, further comprising annealing the tungsten oxide-silica nanoparticles at a temperature of 400 to 500? C. in an oxygen or air atmosphere for complete oxidation.

3. The method according to claim 1, further comprising annealing the tungsten oxide-silica nanoparticles at a temperature of 700 to 900? C. in a 10-30% (v/v) CH.sub.4/H.sub.2 atmosphere.

4. The method according to claim 1, further comprising reducing the tungsten oxide-silica nanoparticles in an aqueous solution containing a small amount of sodium borohydride (NaBH.sub.4).

5. The method according to claim 4, wherein the reduction is performed with continuous stirring until hydrogen gas is no longer evolved or by annealing at a high temperature in a hydrogen atmosphere.

6. A method of synthesizing tungsten-based nanoparticles, comprising treating tungsten-silica nanoparticles synthesized by the method according to claim 1 with at least one material selected from the group consisting of KOH, NaOH, HF, and ammonium bifluoride to remove the silica.

7. A method of preparing light oil, comprising (a) mixing the tungsten nanoparticles synthesized by the method according to claim 1 with extra-heavy oil to obtain a mixture; (b) adding hydrogen to the mixture; and (c) hydrocracking the hydrogen-containing mixture at 400 to 500? C. for 3 to 4 hours.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) These and/or other aspects and advantages of the invention will become apparent and more readily appreciated from the following description of the embodiments, taken in conjunction with the accompanying drawings of which:

(2) FIG. 1 shows TEM images of tungsten oxide-silica (WO.sub.x@SiO.sub.2) core-shell particles (left) and tungsten carbide-silica (WC@SiO.sub.2) core-shell particles (right) synthesized in Example 1;

(3) FIG. 2 shows higher (10?) magnification images of FIG. 1;

(4) FIG. 3 is a TEM image of tungsten oxide-silica nanoparticles synthesized in Example 2;

(5) FIG. 4 is a TEM image of deformed tungsten oxide-silica nanoparticles synthesized in Comparative Example 1;

(6) FIG. 5 is a TEM image of tungsten carbide-silica nanoparticles synthesized in Example 3;

(7) FIG. 6 is an XRD patterns of tungsten oxide-silica (WO.sub.x@SiO.sub.2) tungsten carbide-silica (WC@SiO.sub.2) nanoparticles synthesized in Example 2 and Example 3, respectively;

(8) FIG. 7 is a TEM image of tungsten carbide nanoparticles synthesized in Example 3;

(9) FIG. 8 shows results obtained when extra-heavy oil was cracked using a nano-sized WC catalyst and a bulk WC catalyst; and

(10) FIG. 9 summarizes the amounts of cokes and the yields of high value-added liquids produced when extra-heavy oil was cracked using a nano-sized WC catalyst and a bulk WC catalyst.

DETAILED DESCRIPTION OF THE INVENTION

(11) The present invention will now be described in more detail.

(12) The present invention is directed to methods of synthesizing nano-sized tungsten particles by a sol-gel process. More specifically, the present invention is directed to a method of synthesizing tungsten-silica core-shell nanoparticles and a method of synthesizing tungsten oxide-based nanoparticles by further processing of the synthesized tungsten-silica core-shell nanoparticles.

(13) Desired nanoparticles are generally synthesized by mixing a support (e.g., a surfactant) with bare nanoparticles in a liquid to form micelles or reverse micelles, which suppress and control the growth of the bare nanoparticles, and further processing the controlled particles by annealing or reduction.

(14) Tungsten chlorides, ammonium metatungstate, ammonium paratungstate, and tungsten alkoxides can be used as tungsten precursors for the synthesis of tungsten nanoparticles.

(15) Ammonium metatungstate and ammonium paratungstate are the most widely used precursors and can be extensively applied to reactions in aqueous solution due to their high water solubility.

(16) The chlorine atoms of tungsten chlorides are easily replaced by oxygen atoms due to their instability in air. Tungsten chlorides are readily soluble in organic solvents. When dissolved in an organic solvent, a tungsten chloride forms a red solution in which it exists in a molecular form.

(17) Tungsten alkoxides easily bond with water to form the corresponding alcohols and tungsten oxides. Tungsten alkoxides are readily soluble in organic solvents. A tungsten alkoxide with less number of carbon atoms more rapidly reacts with water. When dissolved in an organic solvent, a tungsten alkoxide forms a transparent solution.

(18) Tungsten cations formed from the precursors have a wide range of oxidation numbers, which explains their high reactivity at ambient temperature and pressure. Particularly, when the tungsten compounds are dissolved in liquids to prepare liquid nanoparticles, various kinds of tungsten cations may be formed depending on the liquid environments.

(19) The present invention is directed to a method of preparing light oil from extra-heavy oil using an unsupported nano-sized WC catalyst. The present invention is also directed to an unsupported dispersible WC nanocatalyst for preparing light oil from extra-heavy oil.

(20) The method of synthesizing tungsten-silica nanoparticles according to the present invention includes (a) dissolving a tungsten precursor and a surfactant in an organic solvent to obtain a mixture solution; (b) dissolving water, aqueous ammonia, and a silica precursor in the mixture solution to synthesize tungsten oxide-silica core-shell nanoparticles; and (c) dispersing the mixture solution containing the tungsten oxide-silica core-shell nanoparticles in a solvent to precipitate the tungsten oxide-silica core-shell nanoparticles and drying the precipitates.

(21) The individual steps of the method according to the present invention will be explained.

(22) In step (a), a tungsten precursor and a surfactant are dissolved in an organic solvent to obtain a mixture solution.

(23) The tungsten precursor refers to a group of tungsten chlorides. The use of a tungsten chloride unsubstituted with oxygen is preferred.

(24) The surfactant is selected from Triton X, Igepal CO, and Brij series nonionic surfactants. The use of Igepal CO-520 is preferred.

(25) The organic solvent is preferably selected from the group consisting of cyclohexane, ethanol, and a mixture thereof.

(26) The tungsten precursor is preferably used in such an amount that the weight of the tungsten precursor per millimeter of the organic solvent is from 0.0009 g to 0.004 g.

(27) The surfactant is preferably used in such an amount that the weight of the surfactant per millimeter of the organic solvent is from 0.05 g to 0.2 g.

(28) The mixture solution is transparent and is colored pale red.

(29) In step (b), the mixture solution is mixed with water and aqueous ammonia and a silica precursor is dissolved therein to synthesize tungsten oxide-silica core-shell nanoparticles or nanoparticles embedded in silica.

(30) The water is preferably added in such an amount that the volume of the water per gram of the tungsten precursor is from 3.58 ml to 12 ml, preferably from 3.5 ml to 4 ml.

(31) Preferably, the aqueous ammonia has a concentration of 28 to 30% and is added in such an amount that the volume of the aqueous ammonia per gram of the tungsten precursor is from 1.0 ml to 12 ml and the pH of the aqueous ammonia is from 9 to 11. If the volume of the aqueous ammonia per gram of the tungsten precursor is less than 2.5 ml, the mixture solution becomes strongly acidic, thus being unsuitable for use in the synthesis of porous silica. Meanwhile, if the volume of the aqueous ammonia per gram of the tungsten precursor exceeds 12 ml, no problems are encountered in a sol-gel reaction but silica is relatively rapidly synthesized, resulting in the formation of tungsten oxide particles outside rather than inside the silica shell.

(32) The silica precursor added to the mixture solution is preferably tetraethyl orthosilicate (TEOS). TEOS is added in such an amount that the volume of TEOS per gram of the tungsten precursor is from 5 ml to 30 ml.

(33) When the water is used in an amount such that the mixture solution does not become cloudy and the resulting mixture has a pH of 9 or above, core-shell structures are synthesized in which tungsten is embedded in silica. Depending on the conditions, well-defined core-shell structures may be obtained, which is described in detail in Examples 1 and 2.

(34) In step (c), the mixture solution containing the tungsten oxide-silica core-shell nanoparticles is dispersed in a solvent to precipitate the tungsten oxide-silica core-shell nanoparticles and the precipitates are then dried.

(35) The solvent is selected from the group consisting of ethanol, acetone, and a mixture thereof. Ethanol is preferably used.

(36) The precipitates are collected by centrifugation at 6000 to 150000 rpm for at least 5 minutes, dried in an oven at 60? C. for at least 12 hours, and stored before use.

(37) The tungsten oxide-silica nanoparticles may be additionally processed to synthesize the various tungsten nanoparticles.

(38) The additional processing may be done as follows:

(39) (1) the tungsten oxide-silica nanoparticles may be pretreated for a subsequent reaction;

(40) (2) the tungsten oxide-silica nanoparticles may be processed to synthesize WC-silica nanoparticles; or

(41) (3) the tungsten oxide-silica nanoparticles may be processed to synthesize reduced tungsten-silica nanoparticles.

(42) Optionally, (4) the particles obtained in (1), (2), and (3) may be processed to remove the silica shells.

(43) Process (1) includes annealing the tungsten oxide-silica nanoparticles at a temperature of 400 to 500? C. in an oxygen or air atmosphere.

(44) Process (2) includes annealing the tungsten oxide-silica nanoparticles at a temperature of 700 to 900? C. in a 10-30% (v/v) CH.sub.4/H.sub.2 atmosphere.

(45) Process (3) includes reducing the tungsten oxide-silica nanoparticles in an aqueous solution containing a small amount of sodium borohydride (NaBH.sub.4). The reduction may be performed with continuous stirring until hydrogen gas is no longer evolved or by annealing at a high temperature in a hydrogen atmosphere.

(46) Process (4) includes treating the particles obtained in Processes (1), (2), and (3) with at least one material selected from the group consisting of KOH, NaOH, HF, and ammonium bifluoride to remove the silica.

(47) The present invention also provides a method of preparing light oil, including (a) mixing the tungsten nanoparticles with extra-heavy oil to obtain a mixture; (b) adding hydrogen to the mixture; and (c) hydrocracking the hydrogen-containing mixture at 400 to 500? C. for 3 to 4 hours.

(48) According to the present invention, the final nanoparticles may be WC particles.

(49) According to the present invention, the extra-heavy oil may be selected from the group consisting of crude oil whose density is from 1 to 10? API (American Petroleum Institute), bitumen, vacuum residue, and mixtures thereof.

(50) The present invention will be explained in detail with reference to the following examples. However, these examples are provided to assist in understanding the invention and are not intended to limit the scope of the invention.

Example 1

(51) 120 ml of cyclohexane, 0.12 g of WCl.sub.6, and 12 g of Igepal CO-520 were mixed together in a 250 ml media bottle. The mixture was stirred with a magnetic stirrer at 250 rpm for 10 min. To the mixture was added 1.00 ml of distilled water. The resulting mixture was stirred for 10 min. Thereafter, 0.92 ml of aqueous ammonia was added and stirring was continued for 15 min. Finally, 2.00 ml of TEOS was added, followed by stirring for 16 h. The reaction mixture was precipitated by adding ethanol and centrifuged at 6000 rpm for 5 min to separate tungsten oxide silica nanoparticles. The nanoparticles were collected, dried at 60? C. for 12 h, and stored before use.

(52) The tungsten oxide-silica nanoparticles were ca. 15-25 nm in size and had a structure in which tungsten oxide particles were distributed. TEM images of the tungsten oxide-silica nanoparticles are shown in FIGS. 1 and 2.

Example 2

(53) Nanoparticles were synthesized in the same manner as in Example 1, except that the amount of aqueous ammonia was changed.

(54) Specifically, 120 ml of cyclohexane, 0.12 g of WCl.sub.6, and 12 g of Igepal CO-520 were mixed together in a 250 ml media bottle. The mixture was stirred with a magnetic stirrer at 250 rpm for 10 min. To the mixture were added 1.00 ml of water and 0.63 ml of aqueous ammonia. The resulting mixture was stirred for 10 min. Finally, 2.00 ml of TEOS was added, followed by stirring for 16 h. The reaction mixture was precipitated by adding ethanol and centrifuged at 6000 rpm for 5 min to separate tungsten oxide silica nanoparticles. The nanoparticles were collected, dried at 60? C. for 12 h, and stored before use.

(55) The tungsten oxide-silica nanoparticles were found to have a size of ca. 15-25 nm and a structure in which single tungsten oxide particle was normally formed in silica shell. Particularly, the water was evaporated during drying, leaving empty spaces in the nanoparticles. A TEM image of the nanoparticles is shown in FIG. 3.

Comparative Example 1

(56) Nanoparticles were synthesized in the same manner as in Example 1, except that the amount of aqueous ammonia was changed.

(57) Specifically, 100 ml of cyclohexane, 0.12 g of WCl.sub.6, and 12 g of lgepal CO-520 were mixed together in a 250 ml media bottle. The mixture was stirred with a magnetic stirrer at 250 rpm for 10 min. To the mixture were added 1.00 ml of water and 0.40 ml of aqueous ammonia. The resulting mixture was stirred for 10 min. Finally, 2.00 ml of TEOS was added, followed by stirring for 16 h. The reaction mixture was precipitated by adding ethanol and centrifuged at 6000 rpm for 5 min to separate tungsten oxide silica nanoparticles. The nanoparticles were collected, dried at 60? C. for 12 h, and stored before use.

(58) The tungsten oxide-silica nanoparticles were found to have a size of ca. 15-25 nm and a structure in which tungsten oxide particles were abnormally deformed in silica. A TEM image of the nanoparticles is shown in FIG. 4.

Example 3

(59) The tungsten oxide-silica nanoparticles synthesized in Example 2 were transferred to a calcination furnace. The particles were heated to 450? C. in air over 3.5 h and kept at the same temperature for 1 h. The particles were allowed to cool to room temperature.

(60) The nanoparticles were collected, transferred to a calcination tube furnace, heated to 590? C. over 4 h 40 min under a flow of 150 sccm 21% CH.sub.4/H.sub.2, and kept for 1 h. Thereafter, the nanoparticles were heated to 800? C. over 1 h 45 min under the same gas atmosphere, kept for 6 h, maintained under a flow of 100 sccm H.sub.2 for 1 h, and naturally cooled. The resulting tungsten carbide-silica nanoparticles were collected and vacuum packed in a container protected from light before storage. FIGS. 5 and 6 show a TEM image and an XRD spectra of the tungsten carbide-silica nanoparticles, respectively.

(61) For removal of the shell, the collected WC silica particles were stirred in 20 wt. % of ammonium bifluoride for 24 h.

(62) The solution was neutralized with the same amount of aqueous ammonia, washed with distilled water, and centrifuged at 15000 rpm for 10 min to separate the WC nanoparticles. The WC nanoparticles were dried at reduced pressure and 60? C. and vacuum packed in a container protected from light before storage.

(63) The WC nanoparticles were found to have a size of ca. 1-5 nm and an average diameter of 2.8 nm. FIG. 7 is a TEM image of the WC nanoparticles.

Example 4

(64) 30 g of vacuum residue (API?=2.32, SK Innovation) as a reactant was filled in a 100 ml reactor and 30 mg of the tungsten carbide nanocatalyst was filled in the reactor. The reactor was purged three times with 10 bar of hydrogen, followed by filling with 70 bar of hydrogen. The reactor was heated for 30 min to adjust the reaction temperature to 400? C. The temperature was maintained for 10 min to reach the steady state. After stirring was continued at 1000 rpm for 4 h, the reactor was cooled to room temperature using a cooling jacket. The physical properties of the products were analyzed.

(65) The hydrocracking products from the extra-heavy oil were divided into solid products (cokes), liquid products (naphtha, middle distillate, gas oil, and residue), and gas products. The liquid products were analyzed by simulated distillation (SIMDIS). The results are shown in Table 1 and FIGS. 8 and 9.

(66) TABLE-US-00001 TABLE 1 Catalyst w/o Bulk Nano catalyst WC WC Gas products (wt. %) 17.3 14.0 14.3 Liquid products (wt. %) 64.0 75.8 82.4 Solid products (wt. %) 18.7 10.2 3.3 Distribution of liquid products (wt. %) <177? C. (naphtha) 2.3 6.14 8.4 177? C.-345? C. (middle distillate) 14.1 19.6 20.4 345? C.-525? C. (gas oil) 24.9 27.2 28.5 >525? C. (residue) 22.77 22.9 25

(67) The yields of the gas products, liquid products, and solid products were 17.3 wt. %, 64.0 wt. %, and 18.7 wt. %, respectively, in the control (w/o catalyst). The yield of the liquid products was low whereas the yields of the gas products and solid products were high.

(68) In contrast, the yield of the liquid products (82.4 wt. %) obtained when the unsupported dispersible WC nanocatalyst was used was higher than the yields of the liquid products obtained when no catalyst was used (control) and the bulk WC catalyst was used. In addition, the yield (3.3 wt. %) of the solid products obtained when the unsupported dispersible WC nanocatalyst was used was considerably low compared to the yields of the solid products obtained when no catalyst was used (control) and the bulk WC catalyst was used. The yield of the gas products obtained when the unsupported dispersible WC nanocatalyst was used was 14.3 wt. %.

(69) These results demonstrate that the unsupported dispersible WC nanocatalyst promoted the hydrocracking of extra-heavy oil.

(70) In conclusion, the unsupported nano-sized dispersible WC nanocatalyst showed improved catalytic activity for the production of light oil from vacuum residue.

(71) Although the particulars of the present disclosure have been described in detail, it will be obvious to those skilled in the art that such particulars are merely preferred embodiments and are not intended to limit the scope of the present invention. Therefore, the true scope of the present invention is defined by the appended claims and their equivalents.