CATALYST FOR PURIFICATION OF EXHAUST GAS FROM INTERNAL COMBUSTION ENGINE AND METHOD FOR PURIFICATION OF EXHAUST GAS USING THE CATALYST
20190232258 ยท 2019-08-01
Assignee
Inventors
- Hirotaka KUNO (Himeji-shi, Hyogo, JP)
- Masashi NAKASHIMA (Himeji-shi, Hyogo, JP)
- Yuzo HAMADA (Himeji-shi, Hyogo, JP)
- Masanori IKEDA (Himeji-shi, Hyogo, JP)
Cpc classification
B01J37/0236
PERFORMING OPERATIONS; TRANSPORTING
B01J37/02
PERFORMING OPERATIONS; TRANSPORTING
F01N2570/08
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N2370/02
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N2330/02
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N3/2828
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N2510/0684
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N2330/06
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
F01N3/281
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
B01J35/56
PERFORMING OPERATIONS; TRANSPORTING
F01N3/10
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
B01J33/00
PERFORMING OPERATIONS; TRANSPORTING
F01N2510/0682
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
International classification
B01J33/00
PERFORMING OPERATIONS; TRANSPORTING
B01J37/02
PERFORMING OPERATIONS; TRANSPORTING
F01N3/10
MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
Abstract
A catalyst for purification of exhaust gas containing a phosphorus compound includes: a lower catalyst layer containing at least one of noble metal provided on a refractory three-dimensional structure; and an upper catalyst layer at an inflow side of exhaust gas and an upper catalyst layer at an outflow side of exhaust gas provided on a surface of the lower catalyst layer. The upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side have different concentrations of noble metal. The catalyst has an intermediate zone with a length of 3 to 23% of the overall length of the refractory three-dimensional structure provided between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side. The intermediate zone starts from a position 10 to 38% from an end face of the catalyst at the inflow side of exhaust gas.
Claims
1. A catalyst for purification of exhaust gas containing a phosphorus compound comprising: a lower catalyst layer containing at least one of noble metal provided on a refractory three-dimensional structure; and an upper catalyst layer at an inflow side of exhaust gas and an upper catalyst layer at an outflow side of exhaust gas provided on a surface of the lower catalyst layer, wherein; the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side having different concentrations of noble metal, an intermediate zone with a length of 3 to 23% of the overall length of the refractory three-dimensional structure provided between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side, and the intermediate zone starting from a position 10 to 38% from an end face of the catalyst at the inflow side of exhaust gas.
2. The catalyst according to claim 1, wherein the intermediate zone has one layer less than the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side.
3. The catalyst according to claim 1, wherein the noble metal is at least one selected from rhodium, palladium, and platinum.
4. The catalyst according to claim 1, wherein the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side contain at least rhodium, and the upper catalyst layer at the inflow side has a higher rhodium concentration than the upper catalyst layer at the outflow side.
5. The catalyst according to claim 1, wherein the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side further contain palladium.
6. The catalyst according to claim 5, wherein a mass ratio of the palladium to the rhodium in the upper catalyst layers is from 0.05 to 5.0.
7. The catalyst according to claim 1, wherein the lower catalyst layer contains at least palladium.
8. A method for purification of exhaust gas containing a phosphorus compound using the catalyst according to claim 1.
9. A method for purification of exhaust gas containing a phosphorus compound using the catalyst according to claim 1 by depositing a phosphorus compound in the intermediate zone.
Description
BRIEF DESCRIPTION OF DRAWINGS
[0028]
[0029]
DESCRIPTION OF EMBODIMENTS
[0030] The catalyst for purification of phosphorus compound-containing exhaust gas according to the present invention has a lower catalyst layer containing at least one of noble metal provided on a refractory three-dimensional structure; an upper catalyst layer at an inflow side of exhaust gas and an upper catalyst layer at an outflow side thereof, provided on a surface of the lower catalyst layer, the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side having different concentrations of noble metal; and has an intermediate zone with a length of 3 to 23% of the overall length of the refractory three-dimensional structure provided between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side, the intermediate zone starting from a position 10 to 38% from an end face of the catalyst at the inflow side of exhaust gas.
[0031] Here, the length of each of the catalyst layers is defined as an average value of the shortest length of the catalyst layer (Lmin) and the longest length thereof (Lmax) (i.e., (Lmin+Lmax)/2). There may be one or more catalyst layers between the three-dimensional structure and the lower catalyst layer. Further, there may be one or more catalyst layers between the upper catalyst layer and the lower catalyst layer.
[0032] The refractory three-dimensional structure is not particularly limited, and those generally used in the field of exhaust gas purification catalyst can be appropriately employed, or preferably a honeycomb substrate. Examples of the honeycomb substrate include a monolithic honeycomb substrate, a metal honeycomb substrate, and a plug honeycomb substrate such as a particulate filter. As a material thereof, cordierite, silicon carbide, silicon nitride, or heat-resistant metal such as stainless steel and a FeCrAl alloy may be used.
[0033] These honeycomb substrates can be produced by an extrusion molding method, a method of winding tightly a sheet-shaped element, or the like. The shape of a gas passing port (cell shape) may have any of hexagonal, square, triangular, and corrugation shapes. In view of usability, the cell density (cell number/unit cross-sectional area) of 100 to 1200 cells/in.sup.2 (15.5 to 186 cells/cm.sup.2) is satisfactory, and 200 to 900 cells/in.sup.2 (31 to 139.5 cells/cm.sup.2) is preferable.
[0034] The overall length of the refractory three-dimensional structure is from 10 to 1000 mm, preferably from 15 to 300 mm, and more preferably from 30 to 200 mm.
[0035] The intermediate zone is a zone where the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side are substantially not present. The state of being substantially not present includes a state of being supported without being affected as catalysis and/or a state of being involuntarily supported at the time of preparing a catalyst. The intermediate zone is provided at a ratio of its length to the overall length of the refractory three-dimensional structure of 3 to 23%, preferably 3.0 to 23%, more preferably 3 to 15%, further preferably 3.0 to 15%, particularly preferably 4.5 to 9.5%. The ratio of the length of the intermediate zone to the overall length of the catalyst is hereinafter simply referred to as ratio. The intermediate zone starts from a position 10 to 38%, preferably 12 to 35%, more preferably 14 to 33%, from the end face of the catalyst at the inflow side of exhaust gas. Specifically, the intermediate zone is provided from a position of preferably 11 to 44 mm, more preferably 13 to 38 mm, further preferably 15 to 35 mm from the end face of the refractory three-dimensional structure at the inflow side of exhaust gas.
[0036] The thickness of the catalyst layer from the surface of the refractory three-dimensional structure to the surface of the intermediate zone is preferably smaller than the thickness from the surface of the refractory three-dimensional structure to the surface of the upper catalyst layer at the inflow side. In addition, the thickness of the catalyst layer from the surface of the refractory three-dimensional structure to the surface of the intermediate zone is preferably smaller than the thickness from the surface of the refractory three-dimensional structure to the surface of the upper catalyst layer at the outflow side. Each of the thicknesses from the surface of the refractory three-dimensional structure to the surface of the upper catalyst layer at the inflow side and from the surface thereof to the upper catalyst layer at the outflow side can be set to the maximum value in each of the layers. In addition, the thickness of the catalyst layer from the surface of the refractory three-dimensional structure to the surface of the intermediate zone can be set to the minimum value in the intermediate zone portion.
[0037] The thickness of each of the catalyst layers is defined as an average value of the smallest thickness of the catalyst layer (Hmin) and the greatest thickness thereof (Hmax) (i.e., (Hmin+Hmax)/2). The thickness of each catalyst layer is not necessarily uniform throughout the layer, but is preferably substantially uniform almost entirely. It is considered that such a configuration can suppress the deterioration of catalytic activity due to the deposition of phosphorus compounds contained in the phosphorus compound-containing exhaust gas in the intermediate zone.
[0038] The noble metal used in the present invention may be those used in the exhaust gas purification catalyst, and is preferably rhodium, palladium, or platinum. The noble metal may be used alone or in combination, and may be used in combination of the same kind or different kinds for each catalyst layer. Specifically, the following configuration is preferable.
[0039] As the noble metal used in the lower catalyst layer, palladium, rhodium, or platinum is preferable; palladium or platinum is particularly preferable; and palladium is most preferable.
[0040] As noble metal used in the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side, palladium, rhodium, or platinum is preferable; rhodium or palladium is particularly preferable; and rhodium is most preferable. The rhodium concentration in the upper catalyst layer at the inflow side is preferably 1.1 to 5 times, more preferably 1.1 to 2 times, further preferably 1.1 to 1.35 times that of the upper catalyst layer at the outflow side. Here, the rhodium concentration in each layer is expressed as percentage obtained by dividing the mass of rhodium contained in the layer by the total mass of a solid contained in the layer. When the ratio thereof is 1.1 times or more, sufficient warming-up properties are exhibited, which is preferable. When the ratio thereof is 5 times or less, the deterioration of catalytic performance due to phosphorus poisoning is suppressed, which is preferable. The mass ratio of palladium to rhodium in the upper catalyst layer at the inflow side is preferably from 0.05 to 5.0, more preferably from 0.1 to 2.0, and further preferably from 0.3 to 0.8. When the ratio thereof is 0.05 or more, rhodium is less susceptible to phosphorus poisoning owing to palladium in the upper catalyst layer at the inflow side, which is preferable. When the ratio thereof is 5.0 or less, the deterioration of the reaction of rhodium caused by coating of rhodium with palladium is suppressed, which is preferable.
[0041] In the amount of the noble metal supported by the lower catalyst layer, the upper catalyst layer at the inflow side, and the upper catalyst layer at the outflow side, the amount of palladium is from 0.05 to 20 g, preferably from 0.5 to 15 g, further preferably from 1 to 10 g, per 1 L of the refractory three-dimensional structure. The amount of platinum is from 0.01 to 15 g, preferably from 0.1 to 10 g, further preferably from 0.5 to 5 g, per 1 L of the refractory three-dimensional structure. The amount of rhodium is from 0.01 to 10 g, preferably from 0.05 to 8 g, further preferably from 0.1 to 5 g, per 1 L of the refractory three-dimensional structure.
[0042] There is no particular limitation on a rhodium (Rh) source as a starting material, and raw materials used in the field of exhaust gas purification can be used. Specific examples thereof include rhodium; halides such as rhodium chloride; inorganic salts of rhodium, such as nitrate, sulfate, acetate, ammonium salt, amine salt, hexaammine salt, carbonate, bicarbonate, nitrite, and oxalate; carboxylates such as formate; hydroxide, alkoxide, and oxide. Preferably, nitrate, ammonium salt, amine salt, and carbonate are exemplified. Here, the amount of the rhodium source added is such an amount as to lead to the amount of rhodium supported on a refractory three-dimensional structure as described above. Incidentally, in the present invention, the rhodium sources described above may be used singly or as a mixture of two or more kinds.
[0043] There is no particular limitation on a palladium (Pd) source as a starting material, and raw materials used in the field of exhaust gas purification can be used. Specific examples thereof include palladium; halides such as palladium chloride; inorganic salts of palladium, such as nitrate, sulfate, acetate, ammonium salt, amine salt, tetraammine salt, carbonate, bicarbonate, nitrite, and oxalate; carboxylates such as formate; hydroxide, alkoxide, and oxide. Preferably, nitrate, acetate, ammonium salt, amine salt, tetraammine salt, and carbonate are exemplified. Incidentally, in the present invention, the palladium sources described above may be used singly or as a mixture of two or more kinds. Here, the amount of the palladium source added is such an amount as to lead to the amount of palladium supported on a refractory three-dimensional structure as described above. Incidentally, in the present invention, the palladium sources described above may be used singly or as a mixture of two or more kinds.
[0044] Further, in the case where platinum is contained as a catalyst active component, there is no particular limitation on a platinum (Pt) source as a starting material, and raw materials used in the field of exhaust gas purification can be used. Specific examples thereof include platinum; halides such as platinum bromide and platinum chloride; inorganic salts of platinum, such as nitrate, dinitrodiammine salt, tetraammine salt, sulfate, ammonium salt, amine salt, bisethanolamine salt, bisacetylacetonate salt, carbonate, bicarbonate, nitrite and oxalate; carboxylates such as formate; hydroxides; alkoxides; and oxides. Among them, nitrate (platinum nitrate), dinitrodiammine salt (dinitrodiammine platinum), chloride (platinum chloride), tetraammine salt (tetraammine platinum), bisethanolamine salt (bisethanolamine platinum), and bisacetylacetonate salt (platinum bisacetylacetonate) are preferable. Incidentally, in the present invention, the platinum sources described above may be used singly or as a mixture of two or more kinds. Here, the amount of the platinum source added is such an amount as to lead to the amount of platinum supported on a three-dimensional structure as described above.
[0045] These upper and lower catalyst layers may use, in addition to the noble metals, oxygen storage material, refractory inorganic oxide, oxide of a group I element, oxide of a group II element, sulfate, carbonate, nitrate, or the like. The oxygen storage material is a material capable of taking in or discharging oxygen according to the oxygen concentration in the exhaust gas, and examples thereof include cerium oxide; and oxide composed of cerium and other elements, such as cerium-zirconium composite oxide, cerium-zirconium-lanthanum composite oxide, cerium-zirconium-lanthanum-neodymium composite oxide, and cerium-zirconium-lanthanum-yttrium composite oxide.
[0046] The oxygen storage material has a crystal structure of cubic, tetragonal, monoclinic, or orthorhombic system; preferably cubic, tetragonal, or monoclinic system; and more preferably cubic or tetragonal system.
[0047] There is no particular limitation on a cerium raw material such as cerium-zirconium composite oxide used as an oxygen storage material, and raw materials used in the field of exhaust gas purification can be used. Specific examples thereof include nitrate such as cerous nitrate, carbonate, and sulfate. Among them, nitrate is preferably used. Incidentally, in the present invention, the cerium sources described above may be used singly or as a mixture of two or more kinds. Here, the amount of the cerium source added is preferably from 5 to 200 g, more preferably from 5 to 100 g, further preferably from 5 to 50 g, in terms of cerium oxide (CeO.sub.2), per 1 L of the refractory three-dimensional structure.
[0048] There is no particular limitation on a zirconium raw material, and raw materials used in the field of exhaust gas purification can be used. Specific examples thereof include zirconium oxynitrate, zirconium oxychloride, zirconium nitrate, and basic zirconium sulfate. Among them, zirconium oxynitrate and zirconium nitrate are preferably used. Incidentally, in the present invention, the zirconium sources described above may be used singly or as a mixture of two or more kinds. Here, the amount of zirconium source added is preferably from 5 to 200 g, more preferably from 10 to 150 g, further preferably from 20 to 100 g, in terms of zirconium oxide (ZrO.sub.2), per 1 L of the refractory three-dimensional structure.
[0049] There is no particular limitation on a lanthanum raw material, and raw materials used in the field of exhaust gas purification can be used. Specific examples thereof include lanthanum hydroxide, lanthanum nitrate, lanthanum acetate, and lanthanum oxide. Among them, lanthanum nitrate or lanthanum hydroxide is preferable. Incidentally, in the present invention, the lanthanum sources described above may be used singly or as a mixture of two or more kinds. Here, the amount of the lanthanum source added is preferably from 1 to 50 g, more preferably from 1 to 35 g, further preferably from 1 to 20 g, in terms of lanthanum oxide (La.sub.2O.sub.3), per 1 L of the refractory three-dimensional structure.
[0050] There is no particular limitation on an yttria raw material, and raw materials used in the field of exhaust gas purification can be used. Specific examples thereof include yttrium hydroxide, yttrium nitrate, yttrium oxalate, and yttrium sulfate. Among them, yttrium hydroxide and yttrium nitrate are preferably used. Incidentally, in the present invention, the yttrium sources described above may be used singly or as a mixture of two or more kinds. Here, the amount of the yttrium source added is preferably from 0 to 50 g, more preferably from 0 to 35 g, further preferably from 0 to 20 g, in terms of yttrium oxide (Y.sub.2O.sub.3), per 1 L of the refractory three-dimensional structure.
[0051] There is no particular limitation on a neodymium raw material, and raw materials used in the field of exhaust gas purification can be used. Specific examples thereof include neodymium hydroxide, neodymium nitrate, neodymium oxalate, and neodymium sulfate. Among them, neodymium hydroxide and neodymium nitrate are preferably used. Incidentally, in the present invention, the neodymium sources described above may be used singly or as a mixture of two or more kinds. Here, the amount of the neodymium source added is preferably from 0 to 50 g, more preferably from 0 to 35 g, further preferably from 0 to 20 g, in terms of neodymium oxide (Nd.sub.2O.sub.5), per 1 L of the refractory three-dimensional structure.
[0052] As the refractory inorganic oxide, alumina, lanthanum-containing alumina, zirconia, silica-alumina, titania, and zeolite are included and can be used singly or in a form of a mixture of two or more kinds. The refractory inorganic oxide to be used in the present invention is preferably one having a little variation of specific surface area at a temperature of 700 C. or higher, preferably 1000 C. or higher. A BET specific surface area of the refractory inorganic oxide is not particularly limited, and is preferably 50 to 750 m.sup.2/g, and more preferably 150 to 750 m.sup.2/g, from the viewpoint of supporting a catalyst active component such as a noble metal. The average primary particle diameter of the refractory inorganic oxide is not particularly limited, but for example, is in a range of 5 nm to 20 nm, and more preferably 5 nm to 10 nm. Within such a range, it is possible to support a noble metal on the refractory inorganic oxide. Incidentally, the shape or the average primary particle diameter of the refractory inorganic oxide in the present invention can be measured by a known method such as a transmission electron microscope (TEM).
[0053] As the group I element or the group II element, potassium, magnesium, calcium, strontium, and barium are included and can be used singly or in a form of a mixture of two or more kinds. The group I element or the group II element to be used in the present invention can be used in a form of oxide, sulfate, carbonate, or nitrate, and is preferably oxide, sulfate, or carbonate after calcining the catalyst. As a barium sulfate, BaSO.sub.4 can be used, and the amount of barium sulfate added is preferably from 0 to 50 g, more preferably from 0.5 to 30 g, further preferably from 0.5 to 20 g, in terms of BaSO.sub.4, per 1 L of the refractory three-dimensional structure.
[0054] Further, in the case where the catalyst of the present invention contains a refractory inorganic oxide, cerium, a ceria-zirconia composite oxide, a rare-earth metal, or an alkaline earth metal, each of these components as a starting material may be used in a form as it is, or in another form, but preferably used in a form as it is. The amount of each of the above-described components added is such an amount as to lead to the amount of the component supported on a three-dimensional structure as described above, or to the amount of the component existing in the catalyst as described above.
[0055] The method of producing the catalyst of the present invention is not particularly limited as long as the effect of the present invention is achieved, and a known method can be used. The catalyst is preferably produced by a method including the steps of (1) preparing a slurry containing noble metal, oxygen storage material, refractory oxygen storage material other than the oxygen storage material, a group I element and/or a group II element; (2) coating a refractory three-dimensional structure with the slurry; and (3) drying and/or calcining the coated structure.
[0056] The slurry can be obtained by mixing a refractory inorganic oxide, an oxygen storage material, a noble metal-supported refractory inorganic oxide, or a noble metal-supported oxygen storage material with an aqueous medium, and wet-milling the mixture. Examples of such an aqueous medium include water, lower alcohols such as ethanol and 2-propanol, and organic alkali aqueous solutions. Water or a lower alcohol is preferably used, and water is particularly preferably used. The amount of a solid in the slurry is such an amount as to lead to be 5 to 60% by mass, and more preferably 10 to 50% by mass, relative to the slurry. A method of wet-milling is carried out generally according to a known method, and there is no particular limitation thereon. For example, wet-milling is carried out using a ball mill or the like.
[0057] The method of coating a refractory three-dimensional structure with a slurry may be (a) a method of coating the refractory three-dimensional structure with a slurry to be used in a lower catalyst layer, drying and calcining the coated structure, then coating a slurry to be used in an upper catalyst layer at an inflow side of exhaust gas from the inflow side of the structure, drying and calcining the coated structure, and then coating a slurry to be used in an upper catalyst layer at an outflow side of exhaust gas from the outflow side of the structure, drying and calcining the coated structure; (b) a method of coating the refractory three-dimensional structure with a slurry to be used in a lower catalyst layer, drying and calcining the coated structure, then coating a slurry to be used in an upper catalyst layer at an outflow side of exhaust gas from the outflow side of the structure, drying and calcining the coated structure, and then coating a slurry to be used in an upper catalyst layer at an inflow side of exhaust gas from the inflow side of the structure, drying and calcining the coated structure; or (c) a method of coating the refractory three-dimensional structure with a slurry to be used in a lower catalyst layer, drying and calcining the coated structure, then simultaneously coating the refractory three-dimensional structure with a slurry to be used in an upper catalyst layer at an inflow side of exhaust gas from the inflow side of the structure and a slurry to be used in an upper catalyst layer at an outflow side of exhaust gas from the outflow side of the structure, drying and calcining the coated structure. A catalyst can be obtained by combining these methods when each of the catalyst layers is formed.
[0058] As the method of forming an intermediate zone when the above-mentioned catalyst is prepared, the coating state of each slurry and the length of the formed layers are measured in advance to determine the formation states of the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side, so that an intermediate zone at a predetermined position and with a predetermined length can be formed. For measurement of the predetermined position and length of the intermediate zone, the catalyst is destroyed and a microscope such as a vernier caliper or a microscope can be used. Alternatively, the position or the length of the intermediate zone can be measured using an X-ray CT scanner without destroying the catalyst. Whether the catalyst is destroyed or not, any method can be used as long as the intermediate zone can be measured.
[0059] The slurry obtained according to the above-mentioned steps is coated on the refractory three-dimensional structure, and the coated structure is dried and calcined. Regarding the conditions for drying and calcining, as long as the refractory inorganic oxide can adhered to the refractory three-dimensional structure, and for example, drying and calcining are not particularly distinguished. Either of drying or calcining alone may be sufficient, but the structure is preferably dried in the air at a temperature of 50 to 300 C., further preferably 80 to 200 C. for 5 minutes to 10 hours, preferably for 30 minutes to 8 hours. Subsequently, the structure is calcined at a temperature of 300 to 1200 C., preferably 400 to 700 C. for 10 minutes to 10 hours, preferably 30 minutes to 5 hours.
[0060] The exhaust gas to be effective in the present invention is exhaust gas containing a phosphorus compound from an internal combustion engine, and even in the case where the catalyst of the present invention is exposed to the phosphorus compound in the exhaust gas for a long time, the exhaust gas can be purified. The phosphorus compound is deposited as phosphorus oxide (P.sub.2O.sub.5) on the catalyst exposed to the exhaust gas containing the phosphorus compound. According to the present invention, the catalyst can exhibit excellent exhaust gas purification performance even in a state where a phosphorous compound is accumulated on the catalyst in an amount of 1 g to 50 g, effectively 1 g to 30 g, further effectively 1 g to 15 g, and most effectively 1 g to 10 g, per 1 L of the refractory three-dimensional structure. Even though the phosphorus compound is generated on the upper catalyst layer at the inflow side, it is deposited in the intermediate zone (space portion), so that the activity of the catalyst component on the upper catalyst layer at the outflow side is less affected, which provides high purification capacity for a whole catalyst. The ratio of the amount of phosphorus compound deposited in terms of P.sub.2O.sub.5 to the volume of phosphorus compound deposited in the intermediate zone as phosphorus oxide (P.sub.2O.sub.5) is larger than the ratio of the amount of phosphorus compound deposited to the volume of phosphorus compound at the outflow side in terms of P.sub.2O.sub.5 deposited on the upper catalyst layer at the outflow side.
[0061] Further, when the catalyst is coated on a refractory three-dimensional structure, the above-mentioned phosphorus compound is generally deposited in a high concentration on the surface of the catalyst layer. That is, the concentration distribution of the phosphorus compound at the inside of the catalyst layer in the depth direction is uneven, and the concentration of the phosphorus compound becomes lower toward the refractory three-dimensional structure, while the concentration thereof becomes higher towards the upper most surface of the coat layer which comes in contact with a gaseous layer. Meanwhile, the concentration distribution of the phosphorus compound in the exhaust gas flowing direction is also uneven, and generally, the concentration of the phosphorus compound becomes higher toward the end face at the inflow side, while the concentration thereof becomes lower toward the end face at the outflow side, so that the concentration does not specifically become higher between the end face at the inflow side and the end face at the outflow side. However, since the catalyst of the present invention has the intermediate zone with a predetermined length provided at a predetermined position in the exhaust gas flowing direction, the amount of phosphorus compound deposited in the position of the intermediate zone is larger than that deposited without the intermediate zone. When the ratio of the total amount of phosphorus compound deposited in the intermediate zone to the amount of phosphorus compound deposited on the whole part is defined as an intermediate zone deposition rate, the phosphorus compound having an intermediate zone deposition rate of 12% to 30% is preferably deposited to purify exhaust gas, and the phosphorus compound having an intermediate zone deposition rate of 15% to 25% is more preferably deposited to purify exhaust gas.
[0062] Further, a large amount of the phosphorus compound is deposited on a side closer to the end face at the outflow side in the intermediate zone, which suppresses the deposition of the phosphorus compound toward the outflow side from the side closer to the end face at the outflow side. Therefore, in particular, the catalyst component at the outflow side could be less likely to be affected by poisoning due to the phosphorus compound. For this reason, the catalyst according to the present invention can be preferably used in purifying the exhaust gas containing a phosphorus compound of the internal combustion engine, and in particular, exhibits an excellent effect in purification of nitrogen oxide, carbon monoxide, and hydrocarbon which are contained in the exhaust gas from an internal combustion engine such as a gasoline engine.
[0063] The amount of the phosphorus compound deposited on the catalyst can be analyzed using XRF (X-ray fluorescence analysis), EPMA (electron probe microanalyzer), SEM-EDX, or the like. In the case of studying distribution of the catalyst in the exhaust gas flowing direction, the catalyst is cut into a predetermined length, and the amount of the phosphorus compound at each of the cut parts can be analyzed by the XRF or the like. The distribution of the catalyst can be studied by comparing the analysis results at the cut parts.
[0064] The internal combustion engine is not particularly limited. For example, a gasoline engine, a hybrid engine, or an engine using a fuel such as natural gas, ethanol, or dimethyl ether can be used. Among them, a gasoline engine is preferably used as the internal combustion engine.
[0065] The time for exposing the exhaust gas purification catalyst to the exhaust gas is not particularly limited, but it is sufficient to secure a time for which at least part of the exhaust gas purification catalyst can be brought into contact with the exhaust gas.
[0066] The temperature of the exhaust gas is not particularly limited and is preferably 0 C. to 800 C., that is, in a temperature range of the exhaust gas during normal driving. Here, an air/fuel ratio of the exhaust gas having a temperature of 0 C. to 800 C. of the internal combustion engine is 10 or more but less than 30, and preferably 11 to 14.7.
[0067] The catalyst of the present invention as described above or the catalyst produced by the method as described above may be exposed to exhaust gas having a temperature of 800 to 1200 C. Here, the air/fuel ratio of the exhaust gas having a temperature of 800 to 1200 C. is preferably 10 to 18.6. In addition, the time for exposing the exhaust gas purification catalyst to exhaust gas having a temperature of 800 C. to 1200 C. is not particularly limited and may be, for example, 5 to 500 hours. The catalyst of the present invention has high performance even after being exposed to such exhaust gas having a high temperature. In order to examine the exhaust gas purification performance of the catalyst after exposure to the exhaust gas having a high temperature, it is effective to examine the exhaust gas purification performance after the catalyst is exposed to exhaust gas having a temperature of 800 C. to 1200 C. for 5 to 500 hours as a heat treatment.
EXAMPLES
[0068] The effect of the present invention will be described with reference to the following Examples and Comparative Examples. However, the technical scope of the present invention is not limited to only the following Examples.
Example 1
[0069] Each of an aqueous solution of palladium nitrate, a CeO.sub.2ZrO.sub.2 composite oxide, aluminum oxide (Al.sub.2O.sub.3), lanthanum acetate, and barium sulfate was weighed such that a mass ratio of palladium (Pd):CeO.sub.2ZrO.sub.2 composite oxide:Al.sub.2O.sub.3:barium sulfate (BaSO.sub.4):lanthanum oxide would be 0.3:50:48:6:5, and then was wet-milled, to prepare a slurry a. The prepared slurry a as a refractory three-dimensional structure was coated onto a 0.875 L cylindrical cordierite substrate of 103-mm diameter and 105-mm length having 600 cells per square inch (1 inch=25.4 mm) and a thickness of each cell wall of 2.5 mil (1 mil=0.0254 mm) in an amount in which the amount of the slurry supported after calcination would be 109.3 g/L, dried at 150 C. for 15 minutes, and then calcined at 550 C. for 30 minutes, to yield an A0 having a lower catalyst layer provided on the refractory three-dimensional structure. The lower catalyst layer was disposed from an end face of the refractory three-dimensional structure at an inflow side of exhaust gas to an end face thereof at an outflow side of exhaust gas (from the end face at the inflow side of exhaust gas to the position of 100% of the overall length of the refractory three-dimensional structure).
[0070] Next, each of a CeO.sub.2ZrO.sub.2 composite oxide, aluminum oxide, and lanthanum oxide was weighed such that a mass ratio of CeO.sub.2ZrO.sub.2 composite oxide:Al.sub.2O.sub.3:La.sub.2O.sub.3 would be 57:61:1.5, and then was wet-milled, to prepare a slurry b. Each of an aqueous solution of rhodium nitrate, an aqueous solution of palladium nitrate, and the prepared slurry b was weighed such that a mass ratio of rhodium (Rh):palladium (Pd):(the total amount of CeO.sub.2ZrO.sub.2 composite oxide, Al.sub.2O.sub.3 and La.sub.2O.sub.3 contained in the slurry b) would be 0.17:0.08:29.4, and then mixed to prepare a slurry b1.
[0071] Next, each of an aqueous solution of rhodium nitrate, an aqueous solution of palladium nitrate, and the prepared slurry b was weighed such that a weight ratio of rhodium (Rh):palladium (Pd):(the total amount of CeO.sub.2ZrO.sub.2 composite oxide, Al.sub.2O.sub.3 and La.sub.2O.sub.3 contained in the slurry b) would be 0.23:0.12:90.1, and then mixed to prepare a slurry b2.
[0072] The prepared slurry b1 was coated on A0 from the inflow side of the catalyst to 25 mm in an amount in which the amount of the slurry supported after calcination would be 29.65 g per 1 L of the substrate, dried, and then calcined to yield A1. Next, the slurry b2 was coated on A1 from the end face at the outflow side to a length of 65 mm as an upper catalyst layer at the outflow side in an amount of 90.45 g per 1 L of the substrate, dried, and then calcined. This yielded a catalyst A having an intermediate zone with a length of 15 mm (at a ratio of 14.3%, the ratio of the length of the intermediate zone to the overall length of the catalyst (hereinafter simply referred to as ratio)) in which the lower layer was exposed between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side. The rhodium concentration in the upper catalyst layer at the inflow side was 0.57% by mass, and the rhodium concentration in the upper catalyst layer at the outflow side was 0.25% by mass. The mass ratio of palladium to rhodium in the upper catalyst layer at the inflow side was 0.47, and the mass ratio of palladium to rhodium in the upper catalyst layer at the outflow side was 0.52.
Example 2
[0073] The slurry b2 was coated on the A1 obtained in Example 1 from the end face at the outflow side to a length of 70 mm in an amount of 90.45 g per 1 L of the substrate, dried, and then calcined. This yielded a catalyst B having an intermediate zone with a length of 10 mm (at a ratio of 9.5%) in which the lower layer was exposed between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side.
Example 3
[0074] The slurry b2 was coated on the A1 obtained in Example 1 from the end face at the outflow side to a length of 75 mm in an amount of 90.45 g per 1 L of the substrate, dried, and then calcined. This yielded a catalyst C having an intermediate zone with a length of 5 mm (at a ratio of 4.8%) in which the lower layer was exposed between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side.
Comparative Example 1
[0075] The slurry b2 was coated on the A1 obtained in Example 1 from the end face at the outflow side to a length of 77 mm in an amount of 90.45 g per 1 L of the substrate, dried, and then calcined. This yielded a catalyst D having an intermediate zone with a length of 3 mm (at a ratio of 2.9%) in which the lower layer was exposed between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side.
Comparative Example 2
[0076] The slurry b2 was coated on the A1 obtained in Example 1 from the end face at the outflow side to a length of 80 mm in an amount of 90.45 g per 1 L of the substrate, dried, and then calcined. This yielded a catalyst E without an intermediate zone in which the lower layer was exposed between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side.
Comparative Example 3
[0077] The slurry b2 was coated on the A1 obtained in Example 1 from the end face at the outflow side to a length of 55 mm in an amount of 90.45 g per 1 L of the substrate, dried, and then calcined. This yielded a catalyst F having an intermediate zone with a length of 25 mm (at a ratio of 23.8%) in which the lower layer was exposed between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side.
Comparative Example 4
[0078] The slurry b2 was coated on the A1 obtained in Example 1 from the end face at the outflow side to a length of 50 mm in an amount of 90.45 g per 1 L of the substrate, dried, and then calcined. This yielded a catalyst G having an intermediate zone with a length of 30 mm (at a ratio of 28.6%) in which the lower layer was exposed between the upper catalyst layer at the inflow side and the upper catalyst layer at the outflow side.
Comparative Example 5
[0079] Each of an aqueous solution of rhodium nitrate, an aqueous solution of palladium nitrate, and the slurry b was weighed such that a weight ratio of rhodium (Rh):palladium (Pd):(the total amount of CeO.sub.2ZrO.sub.2 composite oxide, Al.sub.2O.sub.3 and La.sub.2O.sub.3 contained in the slurry b) would be 0.4:0.2:119.5, and then mixed to prepare a slurry b3. The slurry b3 was coated from the end face of the A0 obtained in Example 1 at the inflow side to the end face thereof at the outflow side in an amount of 120.1 g per 1 L of the substrate, dried, and then calcined. This yielded a catalyst H having no noble metal distributed from the inflow side to the outflow side and not having an intermediate zone.
Comparative Example 6
[0080] The slurry b1 obtained in Example 1 was coated on the A0 obtained in Example 1 from the inflow side of the catalyst to 10 mm in an amount in which the amount of the slurry supported after calcination would be 29.65 g per 1 L of the substrate, dried, and then calcined to yield I1. Next, the slurry b2 was coated on I1 from the end face at the outflow side to a length of 85 mm in an amount of 90.45 g per 1 L of the substrate, dried, and then calcined. This yielded a catalyst I having an intermediate zone with a length of 10 mm (at a ratio of 9.5%) in which the lower layer was exposed at a position of 10 to 20 mm from the end face at the inflow side.
Example 4
[0081] The slurry b1 obtained in Example 1 was coated on the A0 obtained in Example 1 from the inflow side of the catalyst to 15 mm in an amount in which the amount of the slurry supported after calcination would be 29.65 g per 1 L of the substrate, dried, and then calcined to yield J1. Next, the slurry b2 was coated on J1 from the end face at the outflow side to a length of 80 mm, dried, and then calcined. This yielded a catalyst J having an intermediate zone with a length of 10 mm (at a ratio of 9.5%) in which the lower layer was exposed at a position of 15 mm to 25 mm from the end face at the inflow side.
Example 5
[0082] The slurry b1 obtained in Example 1 was coated on the A0 obtained in Example 1 from the inflow side of the catalyst to 35 mm in an amount in which the amount of the slurry supported after calcination would be 29.65 g per 1 L of the substrate, dried, and then calcined to yield K1. Next, the slurry b2 was coated on K1 from the end face at the outflow side to a length of 60 mm, dried, and then calcined. This yielded a catalyst K having an intermediate zone with a length of 10 mm (at a ratio of 9.5%) in which the lower layer was exposed at a position of 35 mm to 45 mm from the end face at the inflow side.
Comparative Example 7
[0083] The slurry b1 obtained in Example 1 was coated on the A0 obtained in Example 1 from the inflow side of the catalyst to 45 mm in an amount in which the amount of the slurry supported after calcination was 29.65 g per 1 L of the substrate, dried, and then calcined to yield L1. Next, the slurry b2 was coated on L1 from the end face at the outflow side to a length of 50 mm, dried, and then calcined. This yielded a catalyst L having an intermediate zone with a length of 10 mm (at a ratio of 9.5%) in which the lower layer was exposed at a position of 45 mm to 55 mm from the end face at the inflow side.
TABLE-US-00001 TABLE 1 Length of Catalyst Layer Upper catalyst Upper catalyst layer at layer at inflow Intermediate outflow side Catalyst side [mm] zone [mm] [mm] A 25 15 65 B 25 10 70 C 25 5 75 D 25 3 77 E 25 0 80 F 25 25 55 G 25 30 50 H 105 I 10 10 85 J 15 10 80 K 35 10 60 L 45 10 50
[0084] <Heat Treatment and Phosphorus Poisoning Treatment>
[0085] Each of the catalysts A to L obtained in Examples 1 to 5 and Comparative Examples 1 to 7 was positioned 25 cm downstream from an exhaust port of a 4.6-liter V-type eight-cylinder engine, the engine was operated while the A/F of a catalyst entry part was set to 14.6 and the temperature of a catalyst bed part was set to 1000 C. Subsequently, the engine was operated at an A/F of 13.8, and subsequently, a cycle in which the engine was operated while the fuel supply was stopped was repeated, and the operation was performed for 100 hours in total, so that the catalyst was subjected to heat treatment.
[0086] Next, each of the heat-treated catalysts was disposed at the downstream side of an exhaust port of a 3.0-liter engine and subjected to phosphorus poisoning treatment by operating the engine while an engine oil having a phosphorus (P) concentration of 3000 ppm was used and the temperature of a catalyst bed part was set to 880 C. It was checked that 2.6 g of the phosphorus compound per 1 L of the three-dimensional structure was contained as phosphorus oxide (P.sub.2O.sub.5) in the catalyst by analyzing the content of phosphorus in each catalyst treated in this way with XRF.
[0087] <Adhesion Amount of Phosphorus Compound to Exhaust Gas Purification Catalyst>
[0088] The distribution of the phosphorous adhesion amounts in catalysts B, E, and F was studied. Regarding the catalysts B, E, and F that were subjected to phosphorus poisoning, each of the catalysts was cut at positions of 25 mm, 35 mm, 50 mm, and 70 mm toward the outflow side direction when its end face at the inflow side of exhaust gas was set to 0 mm, the phosphorus compound (in terms of P.sub.2O.sub.5) contained in each of parts 0 to 25 mm, 25 mm to 35 mm, 35 mm to 50 mm, 50 mm to 70 mm, and 70 mm to 105 mm was studied by XRF analysis. Table 2 shows the ratio of the amount of the phosphorus compound deposited in each of the parts to the amount of the phosphorus compound deposited in the whole part of 0 to 105 mm and the ratio of the total amount of the phosphorus compound deposited in the intermediate zone to the amount of the phosphorus compound deposited in the whole part of 0 to 105 mm (hereinafter referred to as intermediate zone deposition rate). According to the table, the catalyst B having an intermediate zone with a length of 10 mm has higher phosphorus compound ratio in the 25 mm to 35 mm part where the intermediate zone is located than the catalyst E without an intermediate zone, and the catalyst F having an intermediate zone with a length of 25 mm has a high phosphorus compound ratio in the 35 to 50 mm part. It is found that the catalyst F has a lower phosphorus adhesion ratio in the 25 mm to 35 mm part that is equivalent to the part 10 mm at the inflow side of the intermediate zone than the 35 to 50 mm part, and has more phosphorus adhered on the outflow side in the intermediate zone along the exhaust gas flow, so that phosphorus is adhered in the intermediate zone.
TABLE-US-00002 TABLE 2 Ratio of the phosphorus compound deposited in each part to the phosphorus compound adhered to the whole part Length of upper catalyst Length of Intermediate layer at inflow intermediate 0-25 25-35 35-50 50-70 70-105 zone deposition Catalyst side [mm] zone [mm] [mm] [mm] [mm] [mm] [mm] rate [%] E 25 0 70 11 11 7 1 B 25 10 71 16 9 4 Below the 16 detection limit F 25 25 72 4 19 4 1 23
[0089] <Performance Evaluation of Exhaust Gas Purification Catalyst>
[0090] Each of the catalysts after being subjected to phosphorus poisoning treatment was disposed 30 cm downstream from an exhaust port of a 2.4-liter straight-six-cylinder engine, the temperature of the catalyst bed part was increased from 100 C. to 500 C. at a rate of 1800 C./min while the A/F was set to 14.6, the gas emitted from the catalyst outlet was sampled, and each of the purification efficiency of CO, THC, and NOx was calculated. The temperature at which each purification efficiency reaches 20% is denoted as T20, and the time to reach T20 is presented in
[0091] The results of