REFRACTORY COATING COMPOSITION FOR MAKING FACINGS ON TEMPORARY MOLDS OR ON CORES FOR IRON AND STEEL CASTING OPERATIONS

Abstract

The invention relates to a refractory coating composition for producing mold coatings on non-permanent molds or on cores for the casting of iron and steel, comprising a) an alkali metal salt or alkaline earth metal salt of carbonic acid and/or an alkali metal salt or alkaline earth metal salt of diphosphoric acid, b) a carrier liquid and c) refractory materials.

Claims

1. A refractory coating composition for producing mold coatings on non-permanent molds or on cores for the casting of iron and steel, comprising a) an alkali metal salt or alkaline earth metal salt of diphosphoric acid, b) a carrier liquid and c) refractory materials.

2. The refractory coating composition as claimed in claim 1 which additionally contains an alkali metal salt or alkaline earth metal salt of carbonic acid.

3. The refractory coating composition as claimed in claim 2, wherein the refractory coating composition has a molar ratio between the alkali metal salt or alkaline earth metal salt of carbonic acid and the alkali metal salt or alkaline earth metal salt of diphosphoric acid in the range from 1:26 to 10:2.6.

4. The refractory coating composition as claimed in claim 1, wherein the refractory coating composition has a pH of from 7 to 9.9.

5. The refractory coating composition as claimed in claim 1, wherein the alkali metal salt or alkaline earth metal salt of diphosphoric acid is a dihydrogendiphosphate.

6. The refractory coating composition as claimed in claim 1, wherein the refractory coating composition is a covering refractory coating.

7. The refractory coating composition as claimed in claim 1, wherein (i) the alkali metal salt or alkaline earth metal salt of carbonic acid is sodium hydrogencarbonate or sodium carbonate and/or (ii) the alkali metal salt or alkaline earth metal salt of diphosphoric acid is disodium dihydrogendiphosphate.

8. The refractory coating composition as claimed in claim 1, comprising (a) from 0.1 to 50% by weight of the alkali metal salt or alkaline earth metal salt of carbonic acid, based on the total weight of the refractory coating composition, and/or (b) from 0.1 to 50% by weight of the alkali metal salt or alkaline earth metal salt of diphosphoric acid, based on the total weight of the refractory coating composition.

9. The refractory coating composition as claimed in claim 1, wherein the carrier liquid a) is water or contains water and/or b) is one or more organic solvents or contains these, where one or all of the organic solvents is/are preferably alcohol or alcohols.

10. The refractory coating composition as claimed in claim 1, wherein the carrier liquid is an alcohol or contains alcohol.

11. The refractory coating composition as claimed in claim 1, comprising a) from 3 to 15% by weight of sodium hydrogencarbonate and/or sodium carbonate and from 3 to 15% by weight of disodium dihydrogendiphosphate, in each case based on the total weight of the refractory coating composition, b) a carrier liquid which is preferably selected from the group consisting of water, ethanol, 1-propanol, 2-propanol and mixtures thereof, c) refractory materials selected from the group consisting of silica, aluminum oxide (preferably -alumina), zirconium dioxide, aluminum silicates, mullite, zircon sands, zirconium silicates, olivine, talc, mica, coke, feldspar, diatomite, calcined kaolins, kaolinite, metakaolinite, magnesium silicates, iron oxide, bauxite, graphite and mixtures thereof, preferably consisting of magnesium silicates (in particular talc), zirconium silicates and mixtures thereof, where the refractory coating composition has a pH of from 7 to 9.9, preferably a pH of from 7.5 to 9.5, and the weight ratio between a) sodium hydrogencarbonate or sodium carbonate and b) disodium dihydrogendiphosphate is preferably in the range from 1:10 to 10:1, more preferably in the range from 1:5 to 5:1, particularly preferably in the range from 1:2 to 2:1.

12. A method of coating non-permanent molds or cores for the caseing of iron and steel, comprising: providing or producing a refractory coating composition as claimed in claim 1.

13. A process for producing a casting, comprising the following steps: (i) providing or producing a casting mold composed of chemically bound base mold material which preferably comprises one or more binders cured by means of acid and silica sand, (ii) coating at least one region of the casting mold with a refractory coating composition as defined in any of the preceding claims and drying of the coated refractory coating composition, (iii) filling the casting mold with a molten iron-carbon alloy, (iv) allowing the iron-carbon alloy to solidify in the casting mold so as to result in a casting.

14. A casting mold composed of a chemically bound base mold material for producing a casting, wherein the chemically bound base mold material preferably comprises one or more binders which have been cured by means of acid and silica sand wherein at least one region of the casting mold has been coated with a refractory coating composition as defined in claim 1.

15. A method of forming refractory coatings for the refractory industry, comprising: producing or providing an alkali metal salt or alkaline earth metal salt of diphosphoric acid or a mixture of an alkali metal salt or alkaline earth metal salt of carbonic acid and an alkali metal salt or alkaline earth metal salt of diphosphoric acid as additive in refractory coatings for the foundry industry.

16. The refractory coating composition as claimed in claim 2 wherein the alkali metal salt or alkaline earth metal salt of carbonic acid is a primary or secondary carbonate.

17. The refractory coating composition as claimed in claim 2, wherein the refractory coating composition has a molar ratio between the alkali metal salt or alkaline earth metal salt of carbonic acid and the alkali metal salt or alkaline earth metal salt of diphosphoric acid in the range from 1:13 to 5:2.6.

18. The refractory coating composition as claimed in claim 1, wherein the refractory coating composition has a pH of from 7.5 to 9.5.

19. The refractory coating composition as claimed in claim 1, comprising (a) from 0.5 to 30% by weight of the alkali metal salt or alkaline earth metal salt of carbonic acid, based on the total weight of the refractory coating composition, and/or (b) from 0.5 to 30% by weight of the alkali metal salt or alkaline earth metal salt of diphosphoric acid, based on the total weight of the refractory coating composition.

20. The refractory coating composition as claimed in claim 1, wherein the carrier liquid is an alcohol selected from the group consisting of methanol, ethanol, 1-propanol, 2-propanol, n-butanol, isobutanol, sec-butanol, tert-butanol, pentan-1-ol, pentan-2-ol, pentan-3-ol, 2-methylbutan-1-ol, 2-methylbutan-2-ol, 3-methylbutan-1-ol, 3-methylbutan-2-ol, 2,2-dimethylpropan-1-ol, hexan-1-ol, hexan-2-ol, hexan-3-ol, 2-methylpentan-1-ol, 3-methylpentan-1-ol, 4-methylpentan-1-ol, 2-methylpentan-2-ol, 3-methylpentan-2-ol, 4-methylpentan-2-ol, 2-methylpentan-3-ol, 3-methylpentan-3-ol, 2,2-dimethylbutan-1-ol, 2,3-dimethylbutan-1-ol, 3,3-dimethylbutan-1-ol, 2,3-dimethylbutan-2-ol, 3,3-dimethylbutan-2-ol, 2-ethylbutan-1-ol, and mixtures thereof.

Description

[0110] The present invention will be illustrated below by means of examples and a figure.

[0111] FIG. 1 is a photograph of the casting produced in example 8 with a region denoted by X. The part of the casting denoted by X originates from the part of the mold which was coated with a refractory coating composition according to the invention in example 8. The surface of the casting is free of defects and displays no white film, no sintering or pitting of the surface.

EXAMPLES

Example 1

[0112] A mold for a casting (ANZ E 101) composed of EN-GJS 400-15 and having a casting weight of 19 200 kg and a piece weight of 15 800 kg was produced. The mold has a number of radii which are subjected to high thermal stress during casting. The iron-to-sand mass ratio was about 1:1. A mechanically regenerated furan sand having an average particle size of 0.33 mm was used as mold material for the mold. The binder SRV-1 from Httenes-Albertus, Dsseldorf, was used as binder and the activator 7809 from Httenes-Albertus, Dsseldorf, was used as activator.

[0113] A refractory coating composition according to the invention (pH 10.6) based on highly refactory magnesium silicates and oxide-ceramic components and water and containing 9% by weight of sodium carbonate was applied to a specifically characterized region (in this example, region A) of the mold.

[0114] After casting at a casting temperature of about 1320 C., the casting was assessed. In the region A which had been treated with the refractory coating composition according to the invention, the casting displayed no formation of white film. White film was found in the untreated region of the casting.

Example 2

[0115] Example 2 was carried out in a manner analogous to example 1, but a refractory coating composition according to the invention (pH 5.5) based on highly refractory magnesium silicates and oxide-ceramic components and water and containing 9% by weight of disodium dihydrogendiphosphate was applied.

[0116] After casting at a casting temperature of about 1320 C., the casting was assessed. In the region which had been treated with the refractory coating composition according to the invention, the casting displayed no formation of white film. White film was found in the untreated region of the casting.

Example 3

[0117] Example 3 was carried out in a manner analogous to example 1, but a refractory coating composition according to the invention (pH 9.0) based on highly refractory magnesium silicates and oxide-ceramic components and water and containing 4.5% by weight of disodium dihydrogendiphosphate and 4.5% by weight of sodium carbonate was applied.

[0118] After casting at a casting temperature of about 1320 C., the casting was assessed. In the region which had been treated with the refractory coating composition according to the invention, the casting displayed no formation of white film. White film was found in the untreated region of the casting.

Example 4

[0119] Example 4 was carried out in a manner analogous to example 1, but a refractory coating composition according to the invention (pH 5.5) based on highly refractory magnesium silicates and oxide-ceramic components and water and containing 9% by weight of disodium dihydrogendiphosphate was applied.

[0120] The mold was pretreated with a penetrating refractory coating Foseco PDI 1658/1 before application of the refractory coating composition according to the invention.

[0121] After casting at a casting temperature of about 1320 C., the casting was assessed. In the region which had been treated with the refractory coating composition according to the invention, the casting displayed a strong reduction in the formation of white film. White film was found in the untreated region of the casting.

Example 5

[0122] Example 5 was carried out in a manner analogous to example 1, but a refractory coating composition according to the invention (pH 10.6) based on highly refractory magnesium silicates and oxide-ceramic components and water and containing 9% by weight of sodium carbonate was applied.

[0123] The mold was pretreated with a penetrating refractory coating Foseco PDI 1658/1 before application of the refractory coating composition according to the invention.

[0124] After casting at a casting temperature of about 1320 C., the casting was assessed. In the region which had been treated with the refractory coating composition according to the invention, the casting displayed a strong reduction in the formation of white film. White film was found in the untreated region of the casting.

Example 6

[0125] Example 6 was carried out in a manner analogous to example 1, but a refractory coating composition according to the invention (pH 5.5) based on highly refractory magnesium silicates and oxide-ceramic components and water and containing 9% by weight of disodium dihydrogendiphosphate was applied.

[0126] The mold was pretreated with a penetrating refractory coating Foseco PDI 1658/1 and subsequently with a first covering refractory coating Foseco PDI 1514/4 and subsequently dried before application of the refractory coating composition according to the invention.

[0127] After casting at a casting temperature of about 1320 C., the casting was assessed. In the region which had been treated with the refractory coating composition according to the invention, the casting displayed a very strong reduction in the formation of white film. White film was found in the untreated region of the casting.

Example 7

[0128] Example 7 was carried out in a manner analogous to example 1, but a refractory coating composition according to the invention (pH 10.6) based on highly refractory magnesium silicates and oxide-ceramic components and water and containing 9% by weight of sodium carbonate was applied.

[0129] The mold was pretreated with a penetrating refractory coating Foseco PDI 1658/1 and subsequently with a first covering refractory coating Foseco PDI 1514/4 and subsequently dried before application of the refractory coating composition according to the invention.

[0130] After casting at a casting temperature of about 1320 C., the casting was assessed. In the region which had been treated with the refractory coating composition according to the invention, the casting displayed a very strong reduction in the formation of white film. White film was found in the untreated region of the casting.

Example 8

[0131] Example 8 was carried out in a manner analogous to example 1, but a refractory coating composition according to the invention (pH 9.0) based on highly refractory magnesium silicates and oxide-ceramic components and water and containing 4.5% by weight of disodium dihydrogendiphosphate and 4.5% by weight of sodium carbonate was applied.

[0132] The mold was pretreated with a penetrating refractory coating Foseco PDI 1658/1 and subsequently with a first covering refractory coating Foseco PDI 1514/4 and subsequently dried before application of the refractory coating composition according to the invention.

[0133] After casting at a casting temperature of about 1320 C., the casting was assessed. In the region which had been treated with the refractory coating composition according to the invention, the casting displayed no formation of white film and no sintering of the surface. The surface of the casting in the treated region was absolutely defect-free and fettling of the treated region was not necessary. White film was found in the untreated region of the casting.

[0134] A photograph of the cast surface produced is depicted in FIG. 1 (region X).