Abstract

The present invention relates to a suspension comprising at least one pigment, a dispersing agent and a solvent. Preferably, the suspension has a volatile organic compound (VOC) content less than 3% w/w. Furthermore, the invention relates to an ink comprising the suspension and a printing process comprising at least one step of using the ink.

Claims

1. A suspension comprising at least one pigment, a dispersing agent and a solvent, wherein said at least one pigment is present in a concentration comprised between 18 and 65% weight/weight (w/w) with respect to the weight of the suspension, wherein the dispersing agent is present in the suspension in a concentration comprised between 5 and 55% w/w, wherein the solvent is an aqueous solvent and is present in a concentration comprised between 25 and 80% w/w and wherein the suspension has a volatile organic compound (VOC) content of less than 3% w/w.

2. The suspension according to claim 1, wherein the VOC content is less than 1% w/w with respect to the weight of the suspension.

3. The suspension according to claim 1, wherein the aqueous solvent is water, preferably distilled water.

4. The suspension according to claim 1, wherein said at least one pigment is present in a concentration comprised between 20 and 60% w/w with respect to the weight of the suspension.

5. The suspension according to claim 1, wherein said at least one pigment is present in a concentration comprised between 20 and 35% w/w.

6. The suspension according to claim 1, wherein the dispersing agent is present in a concentration comprised between 10 and 35% w/w with respect to the weight of the suspension, preferably comprised between 15 and 25% w/w.

7. The suspension according to claim 1, wherein the solvent is present in a concentration comprised between 20 and 40% w/w with respect to the weight of the suspension.

8. The suspension according to claim 1, wherein the solvent is present in a concentration comprised between 50 and 65% w/w with respect to the weight of the suspension.

9. An ink comprising the suspension according to claim 1, wherein the ink has a VOC content less than 1% w/w.

10. The ink according to claim 9, wherein the suspension is present in a concentration comprised between 5 and 35% w/w with respect to the weight of the ink, preferably comprised between 8 and 30% w/w, more preferably comprised between 10 and 20% w/w.

11. The ink according to claim 9, comprising an aqueous solvent in a concentration comprised between 30 and 55% w/w with respect to the weight of the ink, more preferably comprised between 35 and 50% w/w.

12. The ink according to claim 9, comprising at least one binding agent in a concentration comprised between 5 and 20% w/w with respect to the weight of the ink, preferably said at least one binding agent is at least one resin.

13. A printing process for forming at least one image or writing on at least one substrate, comprising at least one step of using an ink according to claim 9.

14. The process according to claim 13, wherein the printing is a piezoelectric ink-jet printing with drop-on-demand technology.

15. The process according to claim 13, wherein the printing process has a printing speed comprised between 5 and 300 metres/minute, preferably comprised between 80 and 250 metres/minute.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0022] The percentages are expressed in weight with respect to the weight of the suspension or the ink, unless otherwise specified.

[0023] A first aspect of the present invention relates to a suspension having a volatile organic compound (VOC) content of less than 3% by weight, preferably less than 2% weight/weight (w/w), even more preferably less than 1.5% w/w. In a preferred embodiment of the invention, the suspension has a VOC content of about 1% w/w, preferably less than 1% w/w.

[0024] In one embodiment, the suspension comprises or consists of at least one pigment, a dispersing agent and a solvent. Preferably, said at least one pigment is dispersed in the dispersing agent.

[0025] In one embodiment, the pigment particles have an average size less than about 700 nm, preferably 650 nm. Preferably, at least 95% of the pigment particles of the suspension, more preferably at least 98% have an average size less than 650 nm.

[0026] In another embodiment, the at least one pigment comprises particles with an average size less than about 350 nm, preferably less than 300 nm, even more preferably less than 200 nm. In one embodiment, the pigment particles have an average size comprised between 350 nm and 50 nm, preferably comprised between 300 and 40 nm, even more preferably comprised between 250 and 30 nm. In another embodiment, the pigment particles have an average size comprised between 100 and 700 nm and, in still other examples, the pigment particles have an average size comprised between 50 and 500 nm. Preferably, less than 5% of the pigment particles have a size less than 30 nm, preferably less than 3%, even more preferably less than 1%.

[0027] In one embodiment, the at least one pigment is present in the suspension in a concentration greater than or equal to 1% w/w with respect to the weight of the suspension. Preferably, the suspension comprises the at least one pigment in a concentration comprised between 18 and 65% w/w, preferably comprised between 20 and 60% w/w, even more preferably comprised between 20 and 35% w/w.

[0028] Preferably, the at least one pigment is chosen from cyan, magenta, yellow, white, black pigments and combinations thereof.

[0029] In one embodiment, the at least one pigment is an organic or inorganic pigment, more preferably it is an organic pigment.

[0030] Preferably, the at least one pigment is chosen from azo pigments, including diazo and monoazo pigments, polycyclic pigments (for example, phthalocyanine pigments), chelates of insoluble dyes, nitropigments, nitrous pigments and quinacridones.

[0031] Preferably, said at least one pigment is chosen from: Pigment Blue 15:4, Pigment Blue 15:3, Pigment Orange 71, Pigment Orange 34, Pigment Orange 64, Pigment Red 122, Pigment Red 254, Pigment Violet 19 and Pigment Violet 23, Pigment Red 43 and Pigment Red 202, Pigment Red 149 (Scarlet), Pigment Red 179, Pigment Red 190, Pigment and Pigment Red 254, Pigment Yellow 139, Pigment Yellow 185, Pigment Yellow 95, Pigment Yellow 93, Pigment Yellow 110, Pigment Yellow 155, Pigment Yellow 83, Pigment Yellow 138 and PBK7 Carbon black and combinations thereof.

[0032] In a preferred embodiment, the at least one pigment is chosen from: Pigment Yellow 138, a pigment comprising quinacridone, preferably Pigment Blue 15:4, Pigment Blue 15:3, Pigment Yellow 155 and PBK7 Carbon black and combinations thereof.

[0033] In one embodiment, the dispersing agent is present in the suspension in a concentration comprised between 5 and 55% w/w with respect to the weight of the suspension, preferably comprised between 10 and 30% w/w, even more preferably comprised between 15 and 25% w/w.

[0034] Preferably, said dispersing agent does not comprise VOCs and preferably does not comprise organic solvents.

[0035] In one embodiment, the dispersing agent is a polymer and/or a functionalised (co)polymer in which the functional groups are similar to the at least one pigment.

[0036] In one embodiment, the at least one dispersing agent can be added to the suspension in the form of a solution.

[0037] Preferably, the dispersing agent is chosen from: BYK 190 (BYK Additives & Instruments), Fluijet 1732 (Lamberti Spa) and combinations thereof.

[0038] In one embodiment, the solvent is preferably an aqueous solvent, for example water, more preferably distilled water. That is, the solvent is not and/or does not comprise organic solvents. Preferably, the solvent is present in a concentration comprised between 25 and 80% w/w with respect to the weight of the suspension, more preferably comprised between 20 and 40% w/w. In a further embodiment, the suspension further comprises at least one surfactant and/or an anti-foaming agent. Preferably, the suspension comprises at least one anti-foaming agent in a concentration comprised between 0.1 and 1% w/w, more preferably comprised between 0.2 and 0.7% w/w.

[0039] In a preferred embodiment, the suspension comprises or consists of at least one pigment, a dispersing agent, a solvent and an anti-foaming agent and/or a surfactant, in the concentrations and as described in detail above. Preferably, the suspension does not comprise organic solvents.

[0040] In a preferred embodiment of the invention, the suspension does not comprise humectants.

[0041] The suspension described in detail above is preferably prepared by mixing together the dispersing agent, the solvent and the anti-foaming agent and/or at least one surfactant with techniques known to the person skilled in the art. In one embodiment, after mixing the dispersing agent, the solvent and the anti-foaming agent and/or at least one surfactant, the at least one pigment is added and the components mixed together are subjected to a grinding process, in order to obtain a suspension whose particles have a size less than about 350 nm, preferably less than 300 nm, even more preferably less than 200 nm. In one embodiment, the obtained suspension is then filtered.

[0042] A second aspect of the present invention relates to an ink for printing comprising the suspension as described in detail above. That is, the ink is a form of the suspension described above in detail, diluted with compounds or elements known to the person skilled in the art to obtain an ink suitable for printing, preferably for ink-jet printing, more preferably for ink-jet printing with piezoelectric technology, even more preferably suitable for piezoelectric ink-jet printing with drop-on-demand technology.

[0043] Preferably, the ink has a volatile organic compound (VOC) content of less than 3% w/w, preferably less than 2% w/w, even more preferably less than 1.5% w/w. In a preferred embodiment of the invention, the ink has a VOC content of about 1% w/w, preferably less than 1% p w/w.

[0044] Preferably, the ink has a viscosity comprised between 4 and 6 centipoise (cP), more preferably comprised between 4.5 and 5.8 cP.

[0045] In one embodiment, the suspension is present in a concentration comprised between 5 and 35% w/w with respect to the weight of the ink, preferably comprised between 8 and 30% w/w, more preferably comprised between 10 and 20% w/w. Preferably, the ink comprises about 10-15% w/w of the suspension described above.

[0046] In one embodiment, the ink comprises a solvent, preferably an aqueous solvent, more preferably distilled water. Preferably, the solvent is present in a concentration comprised between 30 and 70% w/w, more preferably comprised between 35 and 60% w/w.

[0047] Preferably, the ink comprises at least one additive and/or a wetting agent and/or binder and/or cross-linker known to the person skilled in the art.

[0048] In one embodiment, the ink comprises at least one wetting agent, preferably chosen from glycerol, sorbitol, urea, polyethylene glycol (PEG) and combinations thereof. Preferably, the wetting agent is glycerol. In one embodiment, the wetting agent is present in a concentration comprised between 20 and 45% w/w with respect to the weight of the ink, more preferably comprised between 25 and 40% w/w.

[0049] In a further embodiment, the ink comprises at least one binding agent, preferably at least one resin. The resin is preferably chosen from an acrylic and/or styrenic resin.

[0050] In one embodiment, the binding agent is present in a concentration comprised between 5 and 20% w/w with respect to the weight of the ink, more preferably comprised between 8 and 15% w/w.

[0051] In another embodiment, the ink comprises at least one preservative, for example a biocide, a pH modifier, a surfactant, a fixative or penetrating agent and further additives known to the person skilled in the art for the preparation of a printing ink.

[0052] The Applicant has surprisingly developed a suspension and an ink with a very low VOC content, i.e., less than 1% by weight. The suspension and the ink of the present invention allow a better wettability of the nozzles and parts of the printhead, avoiding clogging and occlusions which lead to nozzle leaks and/or drip deviations, increasing the life of the printheads and printer components, with a consequent reduction in maintenance costs.

[0053] Furthermore, the use of the suspension and of the ink described herein allows an excellent drying of the ink on the printing medium, without counter-printing problems arising, the elimination of problems in drying the printhead, in particular in the nozzle plate both during the printing process and in stand-by conditions.

[0054] The advantages given by the use of the suspension and of the ink described are numerous, including for example the possibility of high runs of single-pass ink-jet printing on flexible material which can be rewound in reels, lower costs and high productivity, convenient on-demand and just-in-time works, printing tests and rapid cycle prototypes, as well as personalised campaigns.

[0055] A third aspect of the present invention relates to a printing process. Said printing process comprises at least one step of using the ink described in detail above for forming at least one image or writing on at least one substrate.

[0056] In one embodiment, the process comprises projecting a flow of drops of the ink composition onto at least one surface of the substrate to form the desired printed image or writing. The ink is fixed on the substrate of the medium by means of any printing technique, digital or analogue, preferably digital printing. Preferably, the process is a digital printing process. Non-limiting examples of such ink-jet printing techniques are thermal, acoustic and piezoelectric ink-jet printing. In one embodiment, such an ink-jet printing technique is a piezoelectric ink-jet printing technique. Preferably, the ink is used in piezoelectric ink-jet printers. That is, the process includes the use of digital ink-jet printers with piezoelectric printheads.

[0057] Preferably, the process includes the use of a single-pass digital printer, i.e., a printer comprising a plurality of printheads. Said single-pass printer preferably comprises a plurality of printheads arranged to form an angle comprised between 30 and 150? with the printing substrate, preferably an angle of about 90?.

[0058] In one embodiment, the printing process is a printing process with a printing speed comprised between 5 and 300 metres/minute, preferably comprised between 80 and 250 metres/minute.

[0059] Preferably, the at least one substrate is a substrate known to the person skilled in the art for printing, preferably for digital printing. Preferably said substrate is a flexible substrate, preferably a substrate which can be wound in a reel, or is a rigid substrate, more preferably in the form of a sheet. In one embodiment, said substrate is chosen from paper, cardboard, cellulose.

EXAMPLE

[0060] The following methods and tools have been used to determine the properties indicated in the present application.

[0061] Particle size: Mastersizer 3000 (Malvern) (5% laser darkening, mixer 2,000 rpm; analysis with Mie diffusion model).

[0062] Viscosity: Kinexus Series rheometer (Malvern) with flat cone geometry (25? C., 100 s-1).

[0063] Dynamic surface tension: Tensiometer: Sita proline t15 (SITA) (bubble time 0.5-15 s).

[0064] Conductivity: Model COND51 conductivity meter (XS Instruments) pH value: 8 Series pHmeter (XS Instruments)

Example 1

[0065] In a rotating blade mixer, the components (ii), (iii) and (iv) shown in Table 1 were mixed. Subsequently, the component (i) was added and the suspension was transferred to a horizontal mill, loaded with yttrium-stabilized zirconium dioxide spheres, having dimensions 0.35-0.45 mm.

[0066] The grinding process, carried out at ambient pressure and without providing thermal energy to the system, was prolonged until obtaining a suspension in which the particle size (d(100)) is less than 200 nm. At the end of the grinding, the suspension was filtered on a 0.6 ?m filter.

[0067] The suspension (S01) was diluted with suitable solvents(v) to obtain the ink 1, suitable for printing on uncoated book paper in general, for SAMBA 3GL FUJIFILM printheads for single-pass ink-jet printing. The composition of the ink is shown in table 2.

TABLE-US-00001 TABLE 1 Description % by weight (i) pigment Pigment PBK 7 30 (ii) dispersing agent Disperbyk 190 30(a) (iii) solvent distilled water 39.5 (iv) anti-foaming agent BYK-1640 (BYK Additives) 0.5 (a)the product has a dispersing agent content of 40% by weight.

TABLE-US-00002 TABLE 2 Ink 1 - for printing on paper % by weight Suspension S01 12.0 Resin 2019NK004-1 binder (Basf) 10 solvent distilled water 42.0 glycerol 33.5 Biocide ACTICIDE BHD 1 0.23 pH modifier triethanolamine 1.5 Surfactant Surfynol 104z (Evonik) 0.77

[0068] The inks are characterised by the following properties:

TABLE-US-00003 Ink 1 - for printing on paper Viscosity [25? C., 100 s?1] 5.3 cP Surface tension [1.2 s] 35.0 mN/m Conductivity 450 ?S/cm pH 8.2

[0069] VOC content: ?1% determined by the UNI EN ISO 11890-2 2020 method.