Corrosion resistant metal substrate

Abstract

A method for producing a corrosion resistant metal substrate and corrosion resistant metal substrate provided thereby. The method involves forming a plated substrate including a metal substrate provided with a nickel layer or with a nickel and cobalt layer followed by electrodepositing a molybdenum oxide layer from an aqueous solution onto the plated substrate, which is subsequently subjected to an annealing step in a reducing atmosphere to reduce the molybdenum oxide in the molybdenum oxide layer to molybdenum metal in a reduction annealing step and to form a diffusion layer which contains nickel and molybdenum, and optionally cobalt.

Claims

1. A corrosion resistant metal substrate comprising a plated substrate comprising a steel or aluminium substrate and a plating layer selected from: i. a nickel or nickel-based layer on the steel or aluminium substrate, or ii. a nickel or nickel-based layer on the steel or aluminium substrate having a cobalt layer on the nickel or nickel-based layer, and a diffusion layer directly on the plating layer; the diffusion layer being produced by electrodepositing a molybdenum oxide layer from an aqueous solution onto the plated substrate, wherein the plated substrate acts as a cathode, wherein the aqueous solution comprises a molybdenum salt and an alkali metal phosphate and wherein the pH of the aqueous solution is adjusted to between 4.0 and 6.5, wherein the plated substrate provided with the molybdenum oxide layer is subjected to an annealing step in a reducing atmosphere to, at least partly, reduce the molybdenum oxide in the molybdenum oxide layer to molybdenum metal in a reduction annealing step and to form, simultaneously or subsequently, in the annealing step the diffusion layer which contains nickel and molybdenum, wherein the nickel originates from the nickel or nickel-based layer, and the molybdenum originates from the molybdenum oxide layer, wherein if the cobalt layer is on the nickel or nickel-based layer then the diffusion layer further contains cobalt that originates from the cobalt layer, wherein the diffusion layer has a thickness of between 10 and 200 nm, and wherein the diffusion layer further comprises 5 to 15 wt. % phosphorus that originates from the alkali metal phosphate.

2. The corrosion resistant metal substrate according to claim 1, wherein the molybdenum salt is ammonium molybdate.

3. The corrosion resistant metal substrate according to claim 1, wherein the phosphate is sodium dihydrogen phosphate.

4. The corrosion resistant metal substrate according to claim 1, wherein the nickel or nickel-based layer provided on the steel or aluminium substrate is between 0.5 and 5 m in thickness.

5. The corrosion resistant metal substrate according to claim 1, wherein: the temperature of the aqueous solution for the electrodeposition of the molybdenum oxide layer onto the plating layer is between 40 C. and 75 C., and/or the plating time for the electrodeposition of the molybdenum oxide layer onto the plating layer is between 5 and 30 seconds, and/or the current density for the electrodeposition of the molybdenum oxide layer onto the plating layer is between 2 and 25 A/dm.sup.2, and/or the maximum annealing temperature during the annealing step is between 500 and 1050 C., and/or the annealing time is between 6 and 10 hours for a batch annealing process and between 10 and 120 seconds for a continuous annealing process.

6. The corrosion resistant metal substrate according to claim 1, wherein the aqueous solution for the electrodeposition of the molybdenum oxide layer onto the plating layer comprises: between 10 and 50 g/l of (NH.sub.4).sub.6Mo.sub.7O.sub.24, and/or between 20 and 80 g/l of NaH.sub.2PO.sub.4.

7. The corrosion resistant metal substrate according to claim 1, wherein the aqueous solution is maintained at a temperature between 50 and 70 C. and/or wherein the pH of the aqueous solution is at least 4.5 and/or at most 6.

8. The corrosion resistant metal substrate according to claim 1, wherein the thickness of the deposited molybdenum oxide layer is at most 50 nm.

9. The corrosion resistant metal substrate according to claim 1, wherein the cathodic current density is at least 12.5 A/dm.sup.2 and/or at most 22.5 A/dm.sup.2.

10. The corrosion resistant metal substrate according to claim 1, wherein the reducing atmosphere is a hydrogen containing atmosphere.

11. The corrosion resistant metal substrate according to claim 1, wherein the diffusion layer comprises 7 to 10 wt. % said phosphorus.

12. The corrosion resistant metal substrate according to claim 1, wherein the diffusion layer has a thickness of between 50 and 100 nm.

13. An exhaust system or parts for an exhaust system or a fuel line produced from the corrosion resistant metal substrate of claim 1.

14. The corrosion resistant metal substrate according to claim 1, wherein the plated substrate provided with the molybdenum oxide layer is subjected to the annealing step in the reducing atmosphere to fully reduce the molybdenum oxide in the molybdenum oxide layer to molybdenum metal in a reduction annealing step.

15. The corrosion resistant metal substrate according to claim 1, wherein nickel concentration in the diffusion layer progressively increases with depth of the diffusion layer from the surface of the corrosion resistant metal substrate.

16. The corrosion resistant metal substrate according to claim 1, wherein the diffusion layer comprises said cobalt.

17. The corrosion resistant metal substrate according to claim 1, wherein the diffusion layer further comprises molybdenum oxide.

18. The corrosion resistant metal substrate according to claim 1, wherein from the steel or aluminium substrate is selected the steel substrate.

19. The corrosion resistant metal substrate according to claim 18, wherein the steel substrate is a ferritic stainless steel substrate.

20. The corrosion resistant metal substrate according to claim 18, wherein the steel substrate is a carbon steel substrate.

21. The corrosion resistant metal substrate according to claim 18, wherein the steel substrate is a low carbon steel substrate.

22. A corrosion resistant metal substrate comprising: a plated substrate comprising a steel or aluminium substrate and a plating layer selected from: i. a nickel or nickel-based layer on the steel or aluminium substrate, or ii. a nickel or nickel-based layer on the steel or aluminium substrate having a cobalt layer on the nickel or nickel-based layer, and a diffusion layer directly on the plating layer, the diffusion layer comprising nickel and molybdenum and the diffusion layer being produced by electrodepositing a molybdenum oxide layer from an aqueous solution onto the plated substrate, wherein the plated substrate acts as a cathode, wherein the aqueous solution comprises a molybdenum salt and an alkali metal phosphate, wherein the plated substrate provided with the molybdenum oxide layer is subjected to an annealing step in a reducing atmosphere to at least partly reduce the molybdenum oxide in the molybdenum oxide layer to molybdenum metal and form the diffusion layer, wherein if the cobalt layer is on the nickel or nickel-based layer then the diffusion layer further contains cobalt that originates from the cobalt layer, wherein the diffusion layer has a thickness of between 10 and 200 nm, wherein the diffusion layer is pore free, and wherein the diffusion layer further comprises 5 to 15 wt. % phosphorus that originates from the alkali metal phosphate.

23. The corrosion resistant metal substrate according to claim 22, wherein nickel concentration in the diffusion layer progressively increases with depth of the diffusion layer from the surface of the corrosion resistant metal substrate.

24. The corrosion resistant metal substrate according to claim 22, wherein the diffusion layer comprises said cobalt.

25. The corrosion resistant metal substrate according to claim 22, wherein the diffusion layer further comprises molybdenum oxide.

26. The corrosion resistant metal substrate according to claim 22, wherein the diffusion layer has a thickness of between 150 and 200 nm, wherein the diffusion layer comprises molybdenum oxide, and wherein the molybdenum oxide of the diffusion layer is only at the top 20 to 30 nm of the diffusion layer.

27. The corrosion resistant metal substrate according to claim 22, wherein the plated substrate comprises the steel substrate.

28. An exhaust system or parts for an exhaust system or a fuel line produced from the corrosion resistant metal substrate of claim 22.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 shows a non-limitative example of the implementation of the process according to the invention.

(2) FIG. 2 shows a GDOES (Glow Discharge Optical Emission Spectroscopy)-measurement of the surface after depositing the molybdenum oxide on the nickel layer.

(3) FIG. 3 shows a GDOES-measurement of the surface after annealing the layers of FIG. 2.

(4) FIG. 4 is Table 10, from page 354 of Nickel, Cobalt, and their Alloys, ASM Specialty Handbook, ed. J. R. Davis., ASM International, 2000.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

(5) One or more of the objects is reached by a method for producing a corrosion resistant metal substrate by electroplating: i. a nickel or nickel-based layer on a steel or aluminium substrate, or ii. a nickel or nickel-based layer on a steel or aluminium substrate followed by providing a cobalt layer on the nickel or nickel-based layer, to form a plated substrate followed by electrodepositing a molybdenum oxide layer from an aqueous solution onto the plated substrate, wherein the plated substrate acts as a cathode, wherein the aqueous solution comprises a molybdenum salt and an alkali metal phosphate and wherein the pH of the aqueous solution is adjusted to between 4.0 and 6.5, wherein the plated substrate provided with the molybdenum oxide layer is subjected to an annealing step in a reducing atmosphere to, at least partly, reduce the molybdenum oxide in the molybdenum oxide layer to molybdenum metal in a reduction annealing step and to form, simultaneously or subsequently, in the annealing step a diffusion layer which contains nickel and molybdenum, and optionally cobalt, wherein the nickel originates from the nickel or nickel-based layer, the cobalt originates from the optional cobalt layer, and the molybdenum originates from the molybdenum oxide layer.

(6) The diffusion layer contains nickel, molybdenum and optionally cobalt. There may be other components in the diffusion layer such as phosphate.

(7) The metal substrate, which may be provided in the form of a coiled strip of steel such as (low) carbon steel or stainless steel, or in the form a coiled strip of aluminium or aluminium alloy with a suitable chemical composition for the application of the final product, is provided with a nickel layer, or a nickel-based layer, and optionally with a cobalt layer on top of the nickel or nickel-based layer to form a plated substrate. Nickel layers can for instance be deposited onto the substrate in a Watts nickel plating bath. A nickel-based layer is a layer predominantly consisting of nickel but not solely of nickel. A nickel alloy layer is therefore considered a nickel based layer. Unless indicated otherwise, the term nickel layer hereinafter intends to include nickel-based layer. The corrosion protection offered by the nickel layer may be insufficient for certain applications as a result of the presence of pores in the nickel layer. The cobalt layer is used to improve the corrosion resistance of the nickel plated substrate. The plated substrate is then led through the said aqueous solution in an electroplating device in which the plated substrate acts as the cathode, and provided with the molybdenum oxide layer. The molybdenum oxide in the molybdenum oxide layer is then reduced to molybdenum metal in a reduction annealing step and, as a consequence of the high temperature during the reduction annealing step, the molybdenum diffuses into the nickel and/or cobalt layer, thereby forming a diffusion layer comprising nickel, molybdenum and optionally cobalt. So the reduction annealing step is also the diffusion annealing step. This is the preferable case. However, if necessary, the annealing step can be prolonged to further promote the diffusion after the reduction of the molybdenum oxide has been completed. Preferably the reducing atmosphere is a hydrogen containing atmosphere, such as substantially pure hydrogen or HNX.

(8) The inventors found that the diffusion layer comprising nickel and molybdenum, and optionally cobalt, is pore free, and provides an excellent protection of the substrate. The pores in the nickel or nickel-alloy layer, if present, are closed as a result of the use of the method according to the invention.

(9) It should be noted that after the reduction annealing step in principle all molybdenum oxide is reduced to molybdenum metal. However, after exposure of the annealed strip to the ambient atmosphere the outermost surface may reoxidise. On a 150 nm thick diffusion layer a 20 to 30 nm thick oxide layer may be present.

(10) In an embodiment the molybdenum salt is ammonium molybdate ((NH.sub.4).sub.6Mo.sub.7O.sub.24). The advantage of the use of ammonium as the cation is that it decomposes during the heat treatment. Other molybdenum salts would result in deposits on the surface. E.g. sodium-molybdate would result in the presence of sodium on the surface which would result in an undesirable alkaline corrosion reaction.

(11) In an embodiment the phosphate is sodium dihydrogen phosphate (NaH.sub.2PO.sub.4). This functions acts both a conducting salt in the electrolyte and as a buffer salt. The buffer ensures that the right pH-value of the electrolyte is maintained. Potassium dihydrogen phosphate (KH.sub.2PO.sub.4) could technically also be used, alone or as a mixture with NaH.sub.2PO.sub.4, but KH.sub.2PO.sub.4 is currently more expensive and therefore economically less attractive.

(12) In further embodiments of the invention wherein the nickel layer (or nickel-based layer) provided on the substrate is between 0.5 and 5 m in thickness. This thickness range provides sufficient thickness for the diffusion layer after the reduction annealing to be effective. It is preferable that the diffusion layer comprising of nickel, originating from the nickel or nickel-based layer, and optionally cobalt, originating from the optional cobalt layer, and molybdenum, originating from the reduced molybdenum oxide layer, has a thickness of between 10 and 200 nm. A preferable minimum thickness is 20 nm, and a preferable maximum thickness is 150 nm. Preferably the thickness of the diffusion layer is between 50 and 100 nm.

(13) In an embodiment the temperature of the aqueous solution for the electrodeposition of the molybdenum oxide layer onto the nickel plated substrate is between 40 C. and 75 C., and/or the plating time for the electrodeposition of the molybdenum oxide layer onto the nickel plated substrate is between 5 and 30 seconds, and/or the current density for the electrodeposition of the molybdenum oxide layer onto the nickel plated substrate is between 2 and 25 A/dm.sup.2, and/or the maximum annealing temperature during the annealing step is between 500 and 1050 C., and/or the annealing time is between 6 and 10 hours for a batch annealing process or between 10 and 120 seconds for a continuous annealing process.

(14) These features are independent and can be applied separately or in combination.

(15) Preferably the temperature of the aqueous solution is at least 51 C. and/or at most 69 C. The plating time is preferably at most 20 seconds, whereas it is preferable that the current density for the electrodeposition of the molybdenum oxide layer is at least 6 and/or at most 22 A/dm.sup.2. More preferably the temperature of the aqueous solution is at least 55 C. and/or at most 65 C.

(16) In an embodiment the plating time for the electrodeposition of the cobalt layer onto the nickel plated substrate is between 5 and 40 seconds, and/or the current density for the electrodeposition of the cobalt layer onto the nickel plated substrate is between 2 and 25 A/dm.sup.2, and/or

(17) The plating bath for the cobalt layer is a chloride based cobalt plating bath, see e.g. Table 10, page 354 of Nickel, Cobalt, and their Alloys, ASM Specialty Handbook, ed. J. R. Davis., ASM International, 2000 (See FIG. 4).

(18) In relation to the maximum annealing temperature during the annealing step a distinction can be made in dependence of the substrate. It was found that for a low-carbon steel substrate the maximum annealing temperature is 700 C., preferably 650 C. and more preferably 600 C. to prevent too large an impact on the properties of the steel substrate. For a stainless steel substrate the maximum annealing temperature is 900 C., preferably 850 C. and more preferably 800 C. to prevent too large an impact on the properties of the steel substrate. Both for low-carbon (LC) steel substrates as for stainless steel substrates the lower limit of the annealing temperature is controlled largely by the lay-out of the annealing facilities and of the economy of the process. The lower the temperature, the longer it takes for a NiMo-diffusion layer of a desired thickness to form.

(19) For an aluminium or aluminium alloy substrate, the allowable temperatures are lower. For such a substrate the maximum annealing temperature depends on the alloy is at most 500 and preferably at most 450 C. to prevent too large an impact on the properties of the substrate. A suitable temperature can be determined easily by simple trial and error. As the temperature is lower, the required diffusion time increases.

(20) The annealing time in the batch annealing process is between 6 and 10 hours, preferably at most 8.5 hours and more preferably at most 7.5 hours. For a continuous annealing process the annealing time is at most 120 seconds, preferably at most 95 s, more preferably at most 75 s and even more preferably at most 40 s. A suitable minimum continuous annealing temperature is 5 s, preferably at least 10 s. There is a degree of interchangeability between the annealing time and the annealing temperature. It should be noted that when referring to an annealing time of 8.5 hours in a batch annealing furnace this intends to mean that the cold spot of the (coiled) material reaches the set temperature in 8.5 hours, after which the cooling starts. A total cycle of heating and cooling may therefore be considerably longer than 8.5 hours and be more than double that value.

(21) In an embodiment the aqueous solution for the electrodeposition of the molybdenum oxide layer onto the plated substrate comprises: between 10 and 50 g/l of (NH.sub.4).sub.6Mo.sub.7O.sub.24, and/or between 20 and 80 g/l of NaH.sub.2PO.sub.4.

(22) This composition allows to effectively and reproducibly deposit the molybdenum oxide layer. It is noted that 30 g/l of (NH.sub.4).sub.6Mo.sub.7O.sub.24 corresponds to 0.024 mol/l and 50 g/l of NaH.sub.2PO.sub.4 to 0.42 mol/l.

(23) In a preferable embodiment the thickness of the deposited molybdenum oxide layer is at most 100 nm, preferably at most 75, more preferably 50 nm, and even more preferably 40 nm. Preferably the minimum thickness is at least 10 nm.

(24) In an embodiment the pH of the aqueous solution is at least 4.5 and/or at most 6. Preferably the pH is at least 5.25 and/or at most 5.75.

(25) In a preferable embodiment wherein the cathodic current density for depositing the molybdenum oxide layer is at least 12.5 A/dm.sup.2 and preferably at least 15 A/dm.sup.2.

(26) Preferably the steel substrate is a carbon steel, preferably a low carbon steel, extra-low carbon steel or a HSLA-steel. These unalloyed (LC and ELC) or micro-alloyed (HSLA) steels are relatively cheap substrates and provide good strength and formability. The steels are produced by means of commonly known processes such as casting, hot-rolling and cold-rolling. Low carbon steels typically comprise 0.05 to 0.15 wt. % C and extra low carbon steels typically comprise 0.02 to 0.05 wt. % C. Other elements may be present in addition to carbon in accordance with EN 10020-2000 which prescribes how much of a certain element may be present to still be considered an unalloyed steel. High-strength low-alloy (HSLA) steels (aka micro-alloyed steels) are designed to provide better mechanical properties and/or greater resistance to atmospheric corrosion than carbon steels. The HSLA steels have low carbon contents (0.05-0.15% C) in order to produce adequate formability and weldability, and they have manganese contents up to 2.0%. Small quantities of chromium, nickel, molybdenum, copper, nitrogen, vanadium, niobium, titanium and zirconium are used in various combinations to achieve the desired properties. It is preferable that the steel substrate has been cold-rolled to its final thickness, usually between 0.15 and 1.5 mm, and the cold-rolled steel substrate may or may not have been recrystallisation or recovery annealed prior to depositing the nickel and optional cobalt layer according to the invention. The steel substrate is preferably supplied in the form of a coiled strip.

(27) In an embodiment of the invention the steel substrate is a ferritic stainless steel, such as an SAE 400-series, which generally are considered to have better engineering properties than austenitic stainless steel grades, but have reduced corrosion resistance, because of the lower chromium and nickel content. They are also usually less expensive. Ferritic stainless steels have a body-centered cubic crystal structure and contain between 10.5% and 27% chromium with very little nickel, if any. By means of a non-limiting example the steel SAE 430 (1.4016) proved to be a useful substrate for the method according to the invention. It is preferable that the stainless steel substrate has been cold-rolled to its final thickness, usually between 0.15 and 1.5 mm, and the cold-rolled steel substrate may or may not have been recrystallisation or recovery annealed prior to depositing the nickel and optional cobalt layer according to the invention. The stainless steel substrate is preferably supplied in the form of a coiled strip.

(28) The substrate for the method according to the invention may also be an aluminium or an aluminium alloy substrate.

(29) In an embodiment the diffusion layer comprising of nickel originating from the nickel or nickel-based layer and molybdenum originating from the molybdenum oxide layer also comprises phosphor, preferably 5 to 15 wt. % of phosphor, more preferably 6 to 13 wt. %. A suitable maximum amount is 10 wt. %. A suitable minimum amount is 7 wt. %. Although the oxidation state of the phosphor is not exactly known, it is believed that the phosphor originated from the phosphate in the electrolyte. It may even still be present as phosphate in the layer. It is believed that its presence contributes to the corrosion protection of the layer.

(30) According to a second aspect, the invention is also embodied in a corrosion resistant metal substrate provided with a diffusion layer comprising nickel, molybdenum and optionally cobalt, produced according to the invention wherein the diffusion layer (i.e. the NiMo or NiMoCo-diffusion layer) has a thickness of between 10 and 200 nm. A preferable minimum thickness is 20 nm, and a preferable maximum thickness is 150 nm. Preferably the thickness of the NiMo-diffusion layer is between 50 and 100 nm. This thickness can be determined e.g. by means of GDOES. The thickness of the layer is determined by locating the halfvalue (ignoring the surface effects) of the Mo-curve. The thickness in FIG. 2 (before annealing) results in a NiMo-layer thickness of 60 nm and in FIG. 3 in a Mo-alloy layer of 80 nm. It is noted that FIG. 3 shows that the tail of the Mo-signal in FIG. 3 is much more pronounced than in FIG. 2 as a result of the diffusion of the Mo into the nickel layer.

(31) According to a third aspect, the invention is embodied in an exhaust system or parts for an exhaust system produced from the metal substrate according to the invention. In another embodiment of the invention the metal substrate according to the invention is used in fuel lines for instance for internal combustion engines.

(32) The invention will now be further explained by means of the following, non-limitative examples.

(33) An aqueous solution was prepared consisting of 30 g/l of (NH.sub.4).sub.6Mo.sub.7O.sub.24 (0.024 mol/l) and 50 g/l of NaH.sub.2PO.sub.4 (0.42 mol/l) with a pH of 5.5 and maintained at 60 C. A molybdenum-oxide layer was deposited on a 2 m matt nickel plated low-carbon steel using a current density of 20 A/dm.sup.2 and a plating time of 15 and 10 seconds. This material was then annealed in a reducing hydrogen atmosphere for 7.3 hours in a batch annealing furnace. The resulting NiMo-diffusion layer has a thickness of about 150 nm at the surface of the coated substrate. These materials were subsequently tested in a salt spray test (NSS) according to ISO 9227:2012 at 5% NaCl and 35 C. and the corrosion protection for the 10 seconds plating time layer was up to 21 hrs (Ni-layer, both sides 2 m). Also the number of pores in the NiMo-diffusion layer was much reduced. The pores were determined visually on a sample which was subjected to an aqueous solution as described in the ferroxyl test in ASTM A380. The rating of samples is a qualitative rating, but quite indicative for its performance under corrosive conditions, such as in exhaust applications.

(34) Experiments using the conditions above result in the following linear dependence of the amount of Mo deposited on plating time (measured after annealing using Atomic Absorption Spectroscopy after dissolution of the layer of the substrate in HCl (1:1)).

(35) TABLE-US-00001 Plating time A/dm.sup.2 mg (Mo)/m.sup.2 5 20 94 10 20 128 15 20 174 20 20 220

(36) FIG. 1 shows a non-limitative example of the implementation of the process according to the invention. The hot-rolled starting product is pickled (in pickling device 10) to remove the oxides from the strip and clean the surface. After pickling the strip is cold-rolled (in cold rolling device 20). In the plating step (in plating device 30) the various layers are electrodeposited. In the annealing step (in annealing device 30) the diffusion annealing takes place. FIG. 1 also shows temper rolling (in temper rolling device 50) and Slitting/Packaging (in Slitting/Packaging device 60). The cold-rolling can obviously also take place elsewhere when the cold-rolled coil is bought from a supplier of cold rolled coil.

(37) FIG. 2 shows a GDOES-measurement of the surface after depositing the molybdenum oxide on the nickel layer. The X-axis gives the thickness in nm and the Y-axis gives the concentration in wt %. Note that the values for carbon and sulphur are in fact 10 times as low as presented. Clearly visible is the layer of molybdenum oxide on top of the nickel layer. The nickel layer is 2 m (i.e. 2000 nm), whereas the molybdenum oxide layer is about 60 nm.

(38) FIG. 3 shows a GDOES-measurement of the surface after annealing the layers of FIG. 2. Note that the values for carbon and sulphur are in fact 10 times as low as presented. The clearly discernible layer of molybdenum oxide on top of the nickel layer has vanished, and a diffusion layer comprising nickel and molybdenum is shown. There is still a degree of oxygen present in the surface layers, but this is believed to be associated with re-oxidation if the surface, and with the presence of the phosphates, and not with the molybdenum oxide which has reduced to metallic molybdenum.