QUANTITATIVE METHOD OF NUMBER SURFACE AREA OF GRAPHENE MATERIAL

Abstract

A quantitative method of number surface area of a graphene material includes the following steps. The graphene material is mixed with a solution to form a colloidal solution containing the graphene material. The colloidal solution is atomized to form a plurality of aerosols containing the graphene material. The size of the aerosols is screened. The screened aerosols are counted to obtain a number concentration of the screened aerosols. A surface of the screened aerosols is charged and a current amount on the surface-charged aerosols is measured. The number surface area of the graphene material is calculated based on the current amount and the number concentration.

Claims

1. A quantitative method of a number surface area of a graphene material, comprising: mixing a graphene material with a solution to form a colloidal solution containing the graphene material; atomizing the colloidal solution to form a plurality of aerosols containing the graphene material; screening a size of the aerosols; counting the screened aerosols to obtain a number concentration of the screened aerosols; a surface of the screened aerosols is charged and a current amount on the surface-charged aerosols is measured; and calculating a number surface area of the graphene material based on the current amount and the number concentration.

2. The quantitative method of the number surface area of the graphene material of claim 1, further comprising, before the colloidal solution is atomized, removing an aggregate of the graphene material settled in the colloidal solution.

3. The quantitative method of the number surface area of the graphene material of claim 1, wherein when the colloidal solution is atomized to form the plurality of aerosols containing the graphene material, each of the aerosols at most contains one of the graphene material.

4. The quantitative method of the number surface area of the graphene material of claim 1, wherein a method of atomizing the colloidal solution containing the graphene material comprises electrospraying, ultrasonic atomization, or gas atomization.

5. The quantitative method of the number surface area of the graphene material of claim 1, wherein a size of the screened aerosols is 7 nm to 100 nm.

6. The quantitative method of the number surface area of the graphene material of claim 1, wherein the step of charging the surface of the screened aerosols comprises: producing a gaseous ion using an ionizer; and mixing the gaseous ion with the screened aerosols to obtain the surface-charged aerosols.

7. The quantitative method of the number surface area of the graphene material of claim 1, wherein a method of calculating the number surface area of the graphene material comprises: calculating a total surface area of the graphene material according to formula (1), $\begin{array}{cc}\mathrm{SA}=\frac{I_P}{\left({\mathrm{DF}}_{a}C\right)}& \mathrm{formula}.Math..Math.\left(1\right)\end{array}$ wherein SA is the total surface area of the graphene material, I.sub.p is the current amount, DF.sub.a is a deposition efficiency of a surface charge, and C is a constant of converting a measured current into an equivalent surface area; and dividing the total surface area with the number concentration.

8. The quantitative method of the number surface area of the graphene material of claim 1, wherein the graphene material comprises a graphene or a graphene oxide.

9. The quantitative method of the number surface area of the graphene material of claim 1, wherein the solution comprises a deionized water.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0016] The accompanying drawings are included to provide a further understanding of the invention, and are incorporated in and constitute a part of this specification. The drawings illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.

[0017] FIG. 1 is a flowchart of a quantitative method of number surface area of a graphene material according to an embodiment of the invention.

DESCRIPTION OF THE EMBODIMENTS

[0018] FIG. 1 is a flowchart of a quantitative method of number surface area of a graphene material according to an embodiment of the invention.

[0019] Referring to FIG. 1, step S100 is performed to mix a graphene material with a solution to form a colloidal solution containing the graphene material. The graphene material is, for instance, graphene or graphene oxide. The solution is, for instance, deionized water, but the invention is not limited thereto, and any solution that can evenly disperse the graphene material can be used. In the present embodiment, three types of graphene oxide (GO) are measured and deionized water is used as the solution as an example, but the invention is not limited thereto.

[0020] In the present embodiment, graphene oxide is prepared. For instance, powdered single-walled carbon nanotube (SWCNT), powdered multi-walled carbon nanotube (MWCNT), and powdered graphite are respectively dispersed in deionized water to respectively obtain graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite suspended in an aqueous solution. Here, the amount of graphene material samples needed is only 0.01 mg, and therefore in a 0.1 mL aqueous solution, the weight concentration of the graphene material is 100 ppm.

[0021] Next, step S110 is performed to remove the aggregate of the graphene material settled in the colloidal solution. In the present embodiment, the aggregate of larger graphene oxide not dispersed in the aqueous solution is removed via settlement, such as natural settlement by gravity or centrifuge.

[0022] Next, step S120 is performed to atomize the colloidal solution to form a plurality of aerosols containing the graphene material. In the present embodiment, the three types of graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite suspended in the aqueous solution are atomized via electrospraying, ultrasonic atomization, or gas atomization to respectively obtain a plurality of aerosols containing the graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite. It should be mentioned that, during atomization, each aerosol must at most contain one graphene oxide, in other words, after atomization, aerosols without graphene oxide and aerosols containing one graphene oxide may be present, but aerosols containing two or more graphene oxides are not present.

[0023] Next, step S130 is performed to screen the size of the aerosols. In the present embodiment, the size of the aerosols is screened via, for instance, a differential mobility analyzer or an aerosol diffusion battery such that the size of the screened aerosols is between 7 nm and 100 nm. Specifically, the differential mobility analyzer can measure the mobility diameter (d.sub.p,m) of the aerosols and screen aerosols having a specific size according to the mobility diameter, and therefor in the invention, the number surface area of the screened aerosols having a specific size can be quantified.

[0024] Moreover, although the aerosol diffusion battery cannot screen aerosols having a specific size, the aerosol diffusion battery can screen aerosols having a size of 7 nm or greater. In other words, particles having a size of 7 nm or less such as salt ion or aerosols without graphene oxide can be removed via the aerosol diffusion battery to prevent the particles less than 7 nm from interfering with the accuracy of subsequent measurements.

[0025] Next, step S140 is performed to count the screened aerosols to obtain a number concentration of the screened aerosols. In the present embodiment, the screened aerosols are counted via, for instance, a condensation particle counter. Since in step S120, aerosols without graphene oxide are removed, the screened aerosols all should only contain one graphene oxide. As a result, the number concentration of the aerosols obtained by the condensation particle counter can represent the number concentration of graphene oxide.

[0026] Next, step S150 is performed to charge a surface of the screened aerosols and a measure a current amount on the surface-charged aerosols. In the present embodiment, first, a gaseous ion is generated using, for instance, an ionizer, and then the gaseous ion is mixed with the screened aerosols such that the gaseous ion is attached to the surface of all of the graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite to obtain aerosols with a charged surface. Next, the current amount of the surface-charged aerosols is measured using, for instance, an electrometer.

[0027] It should be mentioned that, in the invention, the order of step S140 and step S150 is not limited. In other words, in other embodiments, step S150 can also be performed first, and then step S140 is performed.

[0028] Next, step S160 is performed to calculate the number surface area of the graphene material based on the current amount and the number concentration. In the present embodiment, the method of calculating the number surface area of the graphene material includes the following steps. First, the total surface area of the graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite can be calculated according to formula (1),

[00002]$\begin{array}{cc}\mathrm{SA}=\frac{I_P}{\left({\mathrm{DF}}_{a}C\right)},& \mathrm{formula}.Math..Math.\left(1\right)\end{array}$

wherein SA is the total surface area of the graphene material, I.sub.p is the current amount of the surface-charged aerosols (containing the graphene material), DF.sub.a is the deposition efficiency of surface charge, and C is the constant of converting a measured current into an equivalent surface area.

[0029] In the present embodiment, DF.sub.a in formula (1) can be calculated first according to formula (2)

[00003]$\begin{array}{cc}{\mathrm{DF}}_a=\left[\frac{0.01555}{d_{p,m}}\right]\left[\begin{array}{c}\exp \left(-0.416.Math.{\left(\ln .Math..Math.d_{p,m}+2.84\right)}^2\right).Math.\\ +19.11.Math.\exp \left(-0.482.Math.{\left(\ln .Math..Math.d_{p,m}-1.362\right)}^2\right)\end{array}\right],& \mathrm{formula}.Math..Math.\left(2\right)\end{array}$

wherein electrical mobility diameter d.sub.p,m can be measured using the differential mobility analyzer. Therefore, different electrical mobility diameters d.sub.p,m can be respectively measured for graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite having different sizes. Next, the measured electrical mobility diameter d.sub.p,m is introduced in formula (2) to calculate the corresponding DF.sub.a.

[0030] It should be mentioned that, C in formula (1) of the present embodiment is a constant of converting the measured current into equivalent surface area, and the constant can be obtained by measuring the electrical mobility diameter d.sub.p,m (sphere) and the current amount I.sub.sphere of the standards. The standards are, for instance, spherical colloids with known diameters. For instance, the standards are spherical Au colloids with a diameter of 30 nm (30 nm-AuNP for short), spherical (Au colloids with a diameter of 60 nm (60 nm-AuNP for short), and spherical polystyrene latex colloids with a diameter of 100 nm (100 nm-PSL for short).

[0031] In the present embodiment, the C value can be established using the standards 30 nm-AuNP, 60 nm-AuNP, and 100 nm-PSL. Specifically, first, the standards 30 nm-AuNP, 60 nm-AuNP, and 100 nm-PSL are dispersed in deionized water to form colloidal solutions containing the standards. Next, the colloidal solution containing the standards were respectively atomized to respectively form a plurality of aerosols containing the standards. Next, the mobility diameter d.sub.p,m (sphere) thereof is measured via a differential mobility analyzer and aerosols having a specific size and containing the standards are screened. After the surface of the screened aerosols containing the standards is charged, the corresponding current amount I.sub.sphere is measured.

[0032] Next, the C value is calculated according to formula (3),

[00004]$\begin{array}{cc}C=\frac{I_{\mathrm{sphere}}}{{\mathrm{SA}}_{\mathrm{sphere}}{\mathrm{DF}}_a\left(\mathrm{sphere}\right)},& \mathrm{formula}.Math..Math.\left(3\right)\end{array}$

wherein SA.sub.sphere is the total surface area of the standards, I.sub.sphere is the current amount of the surface-charged aerosols (containing the standards), DF.sub.a (sphere) is the deposition efficiency of surface charge, and C is the constant of converting a measured current into an equivalent surface area. The known diameter in the standards is introduced in the formula 4r.sup.2 ( is pi and r is radius) to calculate SA.sub.sphere in formula (3). The measured d.sub.p,m (sphere) is introduced in formula (2) to calculate DF.sub.a (sphere) in formula (3). Next, the measured current amount I.sub.sphere, the calculated DF.sub.a (sphere), and the calculated SA.sub.sphere were introduced in formula (3) to calculate the numerical value of C as 4.410.sup.9 pA nm.sup.2.

[0033] It should be mentioned that, C is a fixed numerical value and is not changed by different material shapes. Therefore, the surface areas of the 3 types of graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite in the present embodiment can be calculated using the calculated C value.

[0034] Referring next to step S160 in FIG. 1, the current amount I.sub.p measured for the graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite, the deposition efficiency DF.sub.a of the calculated surface charge, and the constant C are introduced in formula (3) to respectively calculate the total surface areas SA of the graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite.

[0035] Lastly, the total surface areas SA of the graphene oxides GO.sub.SWCNT, GO.sub.MWCNT, and GO.sub.graphite are respectively divided by the number concentration of the screened aerosols to obtain the number surface area of the graphene oxides.

[0036] It should be mentioned that, the invention does not limit the formula calculating the total surface area of the graphene material such as formula (1). In other words, in other embodiments, other suitable formulas can also be used to calculate the total surface area of the graphene material.

[0037] Based on the above, in the quantitative method of number surface area of a graphene material of the invention, by atomizing the graphene material dispersed in the colloidal solution into aerosols and charging a surface of the aerosols, the invention can calculate the number surface area of the graphene material by measuring the quantity and current amount of the surface-charged aerosols. Therefore, in comparison to the known BET method, the quantitative method of number surface area of a graphene material of the invention can use a smaller amount of sample and directly perform measurement in aqueous phase, and a time-consuming drying process is not needed. Via this design, the quantitative method of the invention can have the advantages of single-measurement high speed and small amount of samples required.

[0038] Although the invention has been described with reference to the above embodiments, it will be apparent to one of ordinary skill in the art that modifications to the described embodiments may be made without departing from the spirit of the invention. Accordingly, the scope of the invention is defined by the attached claims not by the above detailed descriptions.