Abstract
To provide a sliding member which has hardness that is suitable for the circumstance, to which heavy load is applied, and which is excellent in abrasion resistance property. The sliding member contains a sliding layer for slidably supporting a body to be slid, shot blasting being performed on a surface of the sliding layer, and a sliding surface formed on a surface of the sliding layer, the sliding surface having an uneven configuration with arithmetic mean roughness (Ra) of 1.0 m through 2.5 m, 10-point average roughness (Rz) of 5.0 m through 10.0 m, and surface hardness (Hv) of 220 through 250.
Claims
1. A sliding member comprising: a sliding surface formed on a surface of a sliding layer which is impact-hardened by a shot-blasting treatment, wherein the surface of the sliding surface has an uneven shape to form an oil reservoir, wherein the sliding surface exhibits arithmetic mean roughness (Ra) in the range of 1.0 m through 2.5 m, 10-point average roughness (Rz) in the range of 5.0 m through 10.0 m and surface hardness (Hv) in the range of 220 through 250, and the sliding surface slidably supports a body to be slid, and wherein the sliding layer is composed of a copper alloy having a surface hardness (Hv) of 80 through 150 before the shot-blasting treatment.
2. The sliding member according to claim 1 wherein the shot blasting has been performed using blasting material which comprises steel-based metallic material, the blasting material comprising particles having a spherical shape with a particle size in the range of 180 m through 300 m and surface hardness (Hv) in the range of 280 through 600.
3. The sliding member according to claim 1 wherein the shot blasting includes using a blasting distance of not less than 50 mm and not more than 150 mm for a period of blasting time of not less than 5 seconds and not more than 30 seconds.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
(1) FIG. 1 is a diagram showing a configuration example of a piston pump to which a sliding member according to a subject embodiment is applied.
(2) FIG. 2A is a graph showing a form of surface roughness of a sliding surface in each embodiment.
(3) FIG. 2B is a graph showing a form of surface roughness of a sliding surface in each embodiment.
(4) FIG. 2C is a graph showing a form of surface roughness of a sliding surface in each embodiment.
(5) FIG. 3A is a graph showing a form of surface roughness of a sliding surface in each comparison example.
(6) FIG. 3B is a graph showing a form of surface roughness of a sliding surface in each comparison example.
(7) FIG. 3C is a graph showing a form of surface roughness of a sliding surface in each comparison example.
(8) FIG. 4A is a micrograph of the sliding surface in each embodiment.
(9) FIG. 4B is a micrograph of the sliding surface in each embodiment.
(10) FIG. 4C is a micrograph of the sliding surface in each embodiment.
(11) FIG. 5A is a micrograph of the sliding surface in each comparison example.
(12) FIG. 5B is a micrograph of the sliding surface in each comparison example.
(13) FIG. 5C is a micrograph of the sliding surface in each comparison example.
(14) FIG. 6A is a micrograph before and after a test of the sliding surface of a half bearing of an embodiment 1.
(15) FIG. 6B is a micrograph before and after the test of the sliding surface of the half bearing of the embodiment 1.
(16) FIG. 7A is a micrograph before and after a test of the sliding surface of a half bearing of an embodiment 2.
(17) FIG. 7B is a micrograph before and after the test of the sliding surface of the half bearing of the embodiment 2.
(18) FIG. 8A is a micrograph before and after a test of the sliding surface of a half bearing of an embodiment 3.
(19) FIG. 8B is a micrograph before and after the test of the sliding surface of a half bearing of the embodiment 3.
(20) FIG. 9A is a micrograph before and after a test of the sliding surface of a half bearing of a comparison example 1.
(21) FIG. 9B is a micrograph before and after the test of the sliding surface of the half bearing of the comparison example 1.
(22) FIG. 10A is a micrograph before and after a test of the sliding surface of a half bearing of a comparison example 2.
(23) FIG. 10B is a micrograph before and after the test of the sliding surface of the half bearing of the comparison example 2.
(24) FIG. 11A is a micrograph before and after a test of the sliding surface of a half bearing of a comparison example 3.
(25) FIG. 11B is a micrograph before and after the test of the sliding surface of the half bearing of the comparison example 3.
(26) FIG. 12A is a micrograph before and after a test of the sliding surface of a plain bearing of the embodiment 1.
(27) FIG. 12B is a micrograph before and after the test of the sliding surface of the plain bearing of the embodiment 1.
(28) FIG. 13A is a micrograph before and after a test of the sliding surface of a plain bearing of the embodiment 2.
(29) FIG. 13B is a micrograph before and after the test of the sliding surface of the plain bearing of the embodiment 2.
(30) FIG. 14A is a micrograph before and after a test of the sliding surface of a plain bearing of the embodiment 3.
(31) FIG. 14B is a micrograph before and after the test of the sliding surface of the plain bearing of the embodiment 3.
(32) FIG. 15A is a micrograph before and after a test of the sliding surface of a plain bearing of the comparison example 1.
(33) FIG. 15B is a micrograph before and after the test of the sliding surface of the plain bearing of the comparison example 1.
(34) FIG. 16A is a micrograph before and after a test of the sliding surface of a plain bearing of the comparison example 2.
(35) FIG. 16B is a micrograph before and after the test of the sliding surface of the plain bearing of the comparison example 2.
(36) FIG. 17A is a micrograph before and after a test of the sliding surface of a plain bearing of the comparison example 3.
(37) FIG. 17B is a micrograph before and after the test of the sliding surface of the plain bearing of the comparison example 3.
EMBODIMENT FOR CARRYING OUT THE INVENTION
(38) In a sliding member according to any of the embodiments, on a surface of a sliding layer for slidably supporting a body to be slid, a sliding surface is formed. The sliding surface has an uneven configuration with arithmetic mean roughness (Ra) of 1.0 m through 2.5 m, 10-point average roughness (Rz) of 5.0 m through 10.0 m, and surface hardness (Hv) of 220 through 250.
(39) In the sliding member according to any of the embodiments, the sliding layer is formed by metal material with a single composition, alloy materials with a predetermined composition, porous alloy materials into which plastic materials are impregnated, or the like. By performing the shot blasting on the surface of the sliding layer, oil reservoir is formed so that a sliding surface having a desired surface roughness that can improve slidability is formed. Further, by performing the shot blasting on the surface of the sliding layer, the surface hardness of the sliding layer rises so that the sliding surface having a desired surface hardness that is required under the circumstance to which heavy load is applied is formed.
(40) Blasting material composed of steel-based metallic material, which has an almost spherical shape, with a particle size of 180 m through 300 m and surface hardness (Hv) of 280 through 600 is used in the shot blasting. The shot blasting is performed by blasting the above-mentioned blasting material onto the surface of the sliding layer at a blasting distance of not less than 50 mm and not more than 150 mm for a period of blasting time of not less than 5 seconds and not more than 30 seconds.
(41) In any of the embodiments, by performing the shot blasting on the sliding layer made of existing copper alloy, for example, CuSn alloy, having the surface hardness (Hv) of about 80 through about 150, under the above-mentioned conditions, the sliding surface having the above-mentioned desired surface roughness and surface hardness is formed.
(42) The sliding member according to any of the embodiments has an effect of inhibiting alloy from being eroded or being hard to be fatigued because the shot blasting allows the sliding layer to have a higher hardness property so that it is excellent in cavitation erosion resistance property in a field of an oil machine. Particularly, it is preferably applied to an oil pump or the like. FIG. 1 is a diagram showing a configuration example of a piston pump as an example of the oil machine to which a sliding member according to any of the embodiments is applied. FIG. 1 is also a schematically side sectional view of the piston pump.
(43) The piston pump 1 is configured so that a cylinder block 2 is attached to a case 3 while being supported by an input axis 20 and the cylinder block 2 rotates based on any driving force transmitted to the input axis 20. Plural cylinders 21 are formed along a rotation direction and a piston 4 is fit into each cylinder 21 so as to be insertable thereto.
(44) In the piston pump 1, a plain bearing 5 for rotatably supporting the cylinder block 2 is installed. The plain bearing 5 is provided with an inlet port 50 and a discharge port 51, which are opened along the rotation direction of the cylinder block 2. It is installed between the cylinder block 2 and the case 3 while the inlet port 50 is communicated with an inlet 30 provided on the case 3 and the discharge port 51 is communicated with a discharge orifice 31 of the case 3. The sliding member according to any of the embodiments is applied to the plain bearing 5. Since the cylinder block 2 as a body to be slid rotates while being pushed toward an axis direction, the cylinder block 2 and the plain bearing 5 are relatively slid.
(45) The piston pump 1 is also provided with a swash plate 6 for allowing the pistons 4 to be inserted into the cylinders 21 of the cylinder block 2 together with the rotation of the cylinder block 2, a yoke 60 for changing an angle of the swash plate 6, a manipulation piston 7 for allowing the swash plate 6 and the yoke 60 to be operated, and a return spring 8.
(46) The piston pump 1 is configured so that the cylinder 21 from which the piston 4 is projected over the cylinder block 2 sucks oil and the cylinder 21 into which the piston 4 is inserted discharges the oil, together with the rotation of the cylinder block 2. The piston pump 1 is also configured so that by changing an angle of the swash plate 6 and the yoke 60, a stroke of any of the pistons 4 alters and an amount of discharged oil is adjustable.
(47) In the piston pump 1, the case 3 is provided with a half bearing 9 for swingably supporting the swash plate 6 and the yoke 60. The sliding member according to any of the embodiments is applied to the half bearing 9 and the axis portion 61 of the yoke 60 as a body to be slid swings while being pushed toward a circumferential direction so that the axis 61 and the half bearing 9 are relatively swung.
(48) When the piston pump 1 is configured so that the cylinder block 2 rotates in one direction, it is configured so that the inlet side of the oil and the discharge side thereof are fixed but when it is configured so that the cylinder block 2 rotates in both of forward and reverse directions, it is configured so that the Inlet side of the oil and the discharge side thereof are changed. While heavy load is applied to the plain bearing 5 by pushing the cylinder block 2 to the axis direction, the cylinder block 2 slides on one direction along the circumferential direction or both of the forward and reverse directions along the same. This allows the cylinder block 2 and the plain bearing 5 to slide in a circumferential direction while heavy load is applied thereto.
(49) Further, in the piston pump 1, it is configured so that by swinging the swash plate 6 and the yoke 60 in both of the forward and reverse directions, an amount of discharged oil alters. While heavy load is applied to the half bearing 9 by pushing the axis portion 61 of the yoke 60 to the circumferential direction, the axis portion 61 slides in both of the forward and reverse directions along the circumferential direction. This allows the axis portion 61 and the half bearing 9 to slide in a linear direction under a condition in which heavy load is applied thereto.
EMBODIMENTS
(50) (1) Form of the Sliding Surfaces with or without the Shot Blasting
(51) The shot blasting was performed on the sliding layers made of the alloy materials shown in the following Table 1 under the above-mentioned conditions and a form and surface hardness of the produced sliding surfaces of the embodiments 1 through 3, which were produced by performing the shot blasting thereon, were compared with those of the sliding surfaces of the comparison examples 1 through 3, which were produced by performing no shot blasting thereon.
(52) TABLE-US-00001 TABLE 1 Surface Hardness Alloy Composition Hv(0.1) Embodiment 1 CuSn 229 Embodiment 2 CuSnBi 231 Embodiment 3 CuSnPb 236 Comparison Example 1 CuSn 118 Comparison Example 2 CuSnBi 116 Comparison Example 3 CuSnPb 114
(53) FIGS. 2A, 2B, and 2C are graphs each showing a form of surface roughness of the sliding surface in each embodiment. Here, FIGS. 2A, 2B and 2C show forms of the surface roughness of the sliding surfaces based on Japanese Industrial Standard (JIS) B0601 (1994). FIG. 2A shows a form of surface roughness of the sliding surface having the alloy composition of the embodiment 1, on which the shot blasting is performed. FIG. 2B shows a form of surface roughness of the sliding surface having the alloy composition of the embodiment 2, on which the shot blasting is performed. FIG. 2C shows a form of surface roughness of the sliding surface having the alloy composition of the embodiment 3, on which the shot blasting is performed.
(54) FIGS. 3A, 3B, and 3C are graphs each showing a form of surface roughness of the sliding surface in each comparison example. Here, FIGS. 3A, 3B and 3C show forms of the surface roughness of the sliding surfaces based on Japanese Industrial Standard (JIS) B0601 (1994). FIG. 3A shows a form of surface roughness of the sliding surface having the alloy composition of the comparison example 1, on which no shot blasting is performed. FIG. 3B shows a form of surface roughness of the sliding surface having the alloy composition of the comparison example 2, on which no shot blasting is performed. FIG. 3C shows a form of surface roughness of the sliding surface having the alloy composition of the comparison example 3, on which no shot blasting is performed.
(55) FIGS. 4A, 4B, and 4C are micrographs of the sliding surfaces in respective embodiments. Here, FIG. 4A is a micrograph of the sliding surface having the alloy composition of the embodiment 1, on which the shot blasting is performed. FIG. 4B is a micrograph of the sliding surface having the alloy composition of the embodiment 2, on which the shot blasting is performed. FIG. 4C is a micrograph of the sliding surface having the alloy composition of the embodiment 3, on which the shot blasting is performed.
(56) FIGS. 5A, 5B, and 5C are micrographs of the sliding surfaces in respective comparison examples. Here, FIG. 5A is a micrograph of the sliding surface having the alloy composition of the comparison example 1, on which no shot blasting is performed. FIG. 5B is a micrograph of the sliding surface having the alloy composition of the comparison example 2, on which no shot blasting is performed. FIG. 5C is a micrograph of the sliding surface having the alloy composition of the comparison example 3, on which no shot blasting is performed.
(57) As shown in FIGS. 2A, 2B and 2C as well as FIGS. 4A, 4B and 4C, in respective embodiments, by performing the shot blasting on the sliding layer 11, the sliding surface had an uneven configuration. In the embodiment 1 in which the alloy composition is CuSn, arithmetic mean roughness (Ra) was 2.299 m, 10-point average roughness (Rz) was 8.739 m, and average spacing in roughness (Sm) was 0.3114 mm. Further, the surface hardness (Hv) was 229 as shown in the Table 1.
(58) In the embodiment 2 in which the alloy composition is CuSnBi, arithmetic mean roughness (Ra) was 2.344 m, 10-point average roughness (Rz) was 8.286 m, and average spacing in roughness (Sm) was 0.2244 mm. Further, the surface hardness (Hv) was 231.
(59) In the embodiment 3 in which the alloy composition is CuSnPb, arithmetic mean roughness (Ra) was 1.821 m, 10-point average roughness (Rz) was 7.071 m, and average spacing in roughness (Sm) was 0.2067 mm. Further, the surface hardness (Hv) was 236.
(60) On the other hand, as shown in FIGS. 3A, 3B and 3C as well as FIGS. 5A, 5B and 5C, in respective comparison examples, by performing no shot blasting on the sliding layer 101, the sliding surface 100 had a flat configuration. In the comparison example 1 in which the alloy composition is CuSn, arithmetic mean roughness (Ra) was 1.198 m, 10-point average roughness (Rz) was 7.976 m, and average spacing in roughness (Sm) was 0.2378 mm. Further, the surface hardness (Hv) was 118 as shown in the Table 1.
(61) In the comparison example 2 in which the alloy composition is CuSnBi, arithmetic mean roughness (Ra) was 0.9313 m, 10-point average roughness (Rz) was 8.091 m, and average spacing in roughness (Sm) was 0.3547 mm. Further, the surface hardness (Hv) was 116.
(62) In the comparison example 3 in which the alloy composition is CuSnPb, arithmetic mean roughness (Ra) was 0.5784 m, 10-point average roughness (Rz) was 4.074 m, and average spacing in roughness (Sm) was 0.2732 mm. Further, the surface hardness (Hv) was 114.
(63) Based on the above results, it has been understood that in the respective embodiments on which the shot blasting was performed, any roughness is formed on both of upper and lower sides with respect to a center line O about the roughness. On the other hand, it has been understood that in the respective comparison examples on which no shot blasting was performed, they have surface configuration in which there is almost no protrusion above the center line O about the roughness. Further, it has been understood that when performing the shot blasting thereon, the surface hardness is improved about twofold as compared with a case in which no shot blasting is performed thereon.
(64) (2) Relationship on Durability with or without the Shot Blasting
(65) Tests for verifying any influence such as adhesion, abrasion and/or erosion, in which difference in the above-mentioned surface configuration exerted durability, were carried out using the piston pump 1 shown in FIG. 1. As the sliding member to be tested, the plain bearings 5 and the half bearings 9 having the sliding surfaces 10 according to the above mentioned embodiments 1 through 3 were manufactured by performing the shot blasting thereon and the plain bearings 5 and the half bearings 9 having the sliding surfaces 100 according to the above-mentioned comparison examples 1 through 3 were manufactured by performing no shot blasting thereon. Test conditions were as follows:
(66) Cut-Off Durability Test Discharging Power; 0 through 28 MPa Cycles; 30,000 cycles (ON: 1 sec, OFF: 1 sec) Oil temperature; 60 degrees C. Number of Revolutions of Axis; N=1800 rpm.
(67) FIGS. 6A, 6B, 7A, 7B, 8A, and 8B are micrographs before and after the test of the sliding surfaces of the half bearings of the respective embodiments. Here, FIG. 6A is a micrograph before the test of the sliding surface of the half bearing having the alloy composition of the above-mentioned embodiment 1, on which the shot blasting is performed. FIG. 6B is a micrograph after the test of the sliding surface of the half bearing having the alloy composition of the embodiment 1, on which the shot blasting is performed.
(68) FIG. 7A is a micrograph before the test of the sliding surface of the half bearing having the alloy composition of the above-mentioned embodiment 2, on which the shot blasting is performed. FIG. 7B is a micrograph after the test of the sliding surface of the half bearing having the alloy composition of the embodiment 2, on which the shot blasting is performed.
(69) FIG. 8A is a micrograph before the test of the sliding surface of the half bearing having the alloy composition of the above-mentioned embodiment 3, on which the shot blasting is performed. FIG. 8B is a micrograph after the test of the sliding surface of the half bearing having the alloy composition of the embodiment 3, on which the shot blasting is performed.
(70) FIGS. 9A, 9B, 10A, 10B, 11A, and 11B are micrographs before and after the test of the sliding surfaces of the half bearings of the respective comparison examples. Here, FIG. 9A is a micrograph before the test of the sliding surface of the half bearing having the alloy composition of the above-mentioned comparison example 1, on which no shot blasting is performed. FIG. 9B is a micrograph after the test of the sliding surface of the half bearing having the alloy composition of the comparison example 1, on which no shot blasting is performed.
(71) FIG. 10A is a micrograph before the test of the sliding surface of the half bearing having the alloy composition of the above-mentioned comparison example 2, on which no shot blasting is performed. FIG. 10B is a micrograph after the test of the sliding surface of the half bearing having the alloy composition of the comparison example 2, on which no shot blasting is performed.
(72) FIG. 11A is a micrograph before the test of the sliding surface of the half bearing having the alloy composition of the above-mentioned comparison example 3, on which no shot blasting is performed. FIG. 11B is a micrograph after the test of the sliding surface of the half bearing having the alloy composition of the comparison example 3, on which no shot blasting is performed.
(73) As shown in FIGS. 6A and 6B, in the half bearing 9 to which the sliding member according to the embodiment 1 is applied, an alloy component of which is CuSn, the uneven configuration formed by the shot blasting on both of upper and lower sides with respect to a center line O about the roughness, as shown in FIG. 2A, becomes an oil reservoir on the sliding surface to act as any maintenance of oil film so that any evidence of adhesion has been not found on the sliding surface after the test, as shown in FIG. 6B.
(74) Further, the surface hardness of the sliding surface is improved by the shot blasting so that the uneven configuration formed by the shot blasting on the sliding surface as shown in FIG. 6A has remained on the sliding surface after the test, as shown in FIG. 6B.
(75) On the other hand, as shown in FIGS. 9A and 9B, in the half bearing 9 to which the sliding member of the comparison example 1 is applied, an alloy component of which is CuSn, almost no protrusion has been discovered above the center line O about the roughness, as shown in FIG. 3A, so that an oil reservoir is not formed and the evidence of adhesion has been found on the sliding surface after the test as shown in FIG. 9B. The evidence of adhesion has been also found on the axis portion 61, which is a body to be slid, as shown in FIG. 1, in addition to the sliding surface side. This gathers any generation of heat at a sliding portion between the sliding surface and the body to be slid in which they are contacted to each other.
(76) Here, the alloy composition of the embodiment 1 excludes Pb having a self-lubrication effect so that it has been understood that if the oil film is able to be suitably maintained under a boundary lubrication condition, a generation of adhesion could be inhibited without any addition of Pb.
(77) As shown in FIGS. 7A and 7B, in the half bearing 9 to which the sliding member according to the embodiment 2 is applied, an alloy component of which is CuSnBi, the uneven configuration formed by the shot blasting on both of upper and lower sides with respect to a center line O about the roughness, as shown in FIG. 2B, also becomes oil reservoir on the sliding surface to act as any maintenance of oil film so that any evidence of adhesion has been not found on the sliding surface after the test, as shown in FIG. 7B.
(78) Further, the surface hardness of the sliding surface is improved by the shot blasting so that the uneven configuration formed by the shot blasting on the sliding surface as shown in FIG. 7A has remained on the sliding surface after the test, as shown in FIG. 7B.
(79) On the other hand, as shown in FIGS. 10A and 10B, in the half bearing 9 to which the sliding member of the comparison example 2 is applied, an alloy component of which is CuSnBi, protrusion has been almost not discovered above the center line O about the roughness, as shown in FIG. 3B, so that any oil reservoir is not formed and evidence of adhesion has been found on the sliding surface after the test as shown in FIG. 10B. The evidence of adhesion has been also found on the axis portion 61, which is a body to be slid, as shown in FIG. 1, in addition to the sliding surface side. This gathers any generation of heat at a sliding portion between the sliding surface and the body to be slid in which they are contacted to each other.
(80) As shown in FIGS. 8A and 8B, in the half bearing 9 to which the sliding member according to the embodiment 3 is applied, an alloy component of which is CuSnPb, the uneven configuration formed by the shot blasting on both of upper and lower sides with respect to a center line O about the roughness, as shown in FIG. 2C, also becomes an oil reservoir on the sliding surface to act as any maintenance of oil film so that any evidence of adhesion has not been found on the sliding surface after the test, as shown in FIG. 8B.
(81) Further, the surface hardness of the sliding surface is improved by the shot blasting so that the uneven configuration formed by the shot blasting on the sliding surface as shown in FIG. 8A has remained on the sliding surface after the test, as shown in FIG. 8B.
(82) On the other hand, as shown in FIGS. 11A and 11B, in the half bearing 9 to which the sliding member of the comparison example 3 is applied, an alloy component of which is CuSnPb, almost no protrusion has been discovered above the center line O about the roughness, as shown in FIG. 3C, so that any oil reservoir is not formed and evidence of adhesion has been found on the sliding surface after the test as shown in FIG. 11B. The evidence of adhesion has been also found on the axis portion 61, which is a body to be slid, as shown in FIG. 1, in addition to the sliding surface side. This gathers any generation of heat at a sliding portion between the sliding surface and the body to be slid in which they are contacted to each other.
(83) From the above, it has been found that the uneven configuration is formed on the sliding surface by the shot blasting in connection with the oil film formation under a boundary lubrication condition in the sliding members according to the respective embodiments and the surface hardness is improved to inhibit any adhesion and abrasion. It has been also found that if any one of the sliding members according to the respective embodiments is applied to the half bearing 9 of the piston pump 1 shown in FIG. 1, adhesion resistance property and abrasion resistance property are improved.
(84) FIGS. 12A, 12B, 13A, 13B, 14A and 14B are micrographs before and after the test of the sliding surfaces of the plain bearing of the respective embodiments. Here, FIG. 12A is a micrograph before the test of the sliding surface of the plain bearing having the alloy composition of the above-mentioned embodiment 1, on which the shot blasting is performed. FIG. 12B is a micrograph after the test of the sliding surface of the plain bearing having the alloy composition of the embodiment 1, on which the shot blasting is performed.
(85) FIG. 13A is a micrograph before the test of the sliding surface of the plain bearing having the alloy composition of the above-mentioned embodiment 2, on which the shot blasting is performed. FIG. 13B is a micrograph after the test of the sliding surface of the plain bearing having the alloy composition of the embodiment 2, on which the shot blasting is performed.
(86) FIG. 14A is a micrograph before the test of the sliding surface of the plain bearing having the alloy composition of the above-mentioned embodiment 3, on which the shot blasting is performed. FIG. 14B is a micrograph after the test of the sliding surface of the plain bearing having the alloy composition of the embodiment 3, on which the shot blasting is performed.
(87) FIGS. 15A, 15B, 16A, 16B, 17A and 17B are micrographs before and after the test of the sliding surfaces of the plain bearing of the respective comparison examples. Here, FIG. 15A is a micrograph before the test of the sliding surface of the plain bearing having the alloy composition of the above-mentioned comparison example 1, on which no shot blasting is performed. FIG. 15B is a micrograph after the test of the sliding surface of the plain bearing having the alloy composition of the comparison example 1, on which no shot blasting is performed.
(88) FIG. 16A is a micrograph before the test of the sliding surface of the plain bearing having the alloy composition of the above-mentioned comparison example 2, on which no shot blasting is performed. FIG. 16B is a micrograph after the test of the sliding surface of the plain bearing having the alloy composition of the comparison example 2, on which no shot blasting is performed.
(89) FIG. 17A is a micrograph before the test of the sliding surface of the plain bearing having the alloy composition of the above-mentioned comparison example 3, on which no shot blasting is performed. FIG. 17B is a micrograph after the test of the sliding surface of the plain bearing having the alloy composition of the comparison example 3, on which no shot blasting is performed.
(90) As shown in FIGS. 12A and 12B, in the plain bearing 5 to which the sliding member according to the embodiment 1 is applied, an alloy component of which is CuSn, the uneven configuration formed by the shot blasting on both of upper and lower sides with respect to a center line O about the roughness, as shown in FIG. 2A, also becomes oil reservoir on the sliding surface to act as any maintenance of oil film so that any erosion has been not found on the sliding surface around the discharge port 51 shown in FIG. 1 where a jet stream occurs even after the test, as shown in FIG. 12B.
(91) Further, the surface hardness of the sliding surface is improved by the shot blasting so that the uneven configuration formed by the shot blasting on the sliding surface as shown in FIG. 12A has remained on the sliding surface after the test, as shown in FIG. 12B.
(92) On the other hand, as shown in FIGS. 15A and 15B, in the plain bearing 5 to which the sliding member of the comparison example 1 is applied, an alloy component of which is CuSn, protrusion has been almost not discovered above the center line O about the roughness, as shown in FIG. 3A, so that any oil reservoir is not formed and the erosion by the jet stream has been found on the sliding surface after the test as shown in FIG. 15B.
(93) As shown in FIGS. 13A and 13B, in the plain bearing 5 to which the sliding member according to the embodiment 2 is applied, an alloy component of which is CuSnBi, the uneven configuration formed by the shot blasting on both of the upper and lower sides with respect to a center line O about the roughness, as shown in FIG. 2B, also becomes an oil reservoir on the sliding surface to act as any maintenance of oil film so that any erosion has been not found on the sliding surface around the discharge port 51 shown in FIG. 1 where a jet stream occurs even after the test, as shown in FIG. 13B.
(94) Further, the surface hardness of the sliding surface is improved by the shot blasting so that the uneven configuration formed by the shot blasting on the sliding surface as shown in FIG. 13A has remained on the sliding surface after the test, as shown in FIG. 13B.
(95) On the other hand, as shown in FIGS. 16A and 16B, in the plain bearing 5 to which the sliding member of the comparison example 2 is applied, an alloy component of which is CuSnBi, protrusion has been almost not discovered above the center line O about the roughness, as shown in FIG. 3B, so that any oil reservoir is not formed and the erosion by the jet stream has been found on the sliding surface after the test as shown in FIG. 16B.
(96) As shown in FIGS. 14A and 14B, in the plain bearing 5 to which the sliding member according to the embodiment 3 is applied, an alloy component of which is CuSnPb, the uneven configuration formed by the shot blasting on both of upper and lower sides with respect to a center line O about the roughness, as shown in FIG. 2C, also becomes oil reservoir on the sliding surface to act as any maintenance of oil film so that any erosion has been not found on the sliding surface around the discharge port 51 shown in FIG. 1 where a jet stream occurs even after the test, as shown in FIG. 14B.
(97) Further, the surface hardness of the sliding surface is improved by the shot blasting so that the uneven configuration formed by the shot blasting on the sliding surface as shown in FIG. 14A has remained on the sliding surface after the test, as shown in FIG. 14B.
(98) On the other hand, as shown in FIGS. 17A and 17B, in the plain bearing 5 to which the sliding member of the comparison example 3 is applied, an alloy component of which is CuSnPb, protrusion has been almost not discovered above the center line O about the roughness, as shown in FIG. 3B, so that any oil reservoir is not formed and the erosion by the jet stream has been found on the sliding surface after the test as shown in FIG. 17B.
(99) From the above, it has been found that the uneven configuration is formed on the sliding surface by the shot blasting in connection with the oil film formation under a boundary lubrication condition in the sliding members according to the respective embodiments and the surface hardness is improved to inhibit any erosion by the jet stream. It has been also found that if any one of the sliding members according to the respective embodiments is applied to the plain bearing 5 of the piston pump 1 shown in FIG. 1, erosion resistance property and abrasion resistance property are improved.
INDUSTRIAL APPLICABILITY
(100) The sliding member according to the invention is indicative of adhesion resistance property, erosion resistance property and abrasion resistance property even under the boundary lubrication condition so that it is preferably applied to a bearing of an oil machine, to which heavy load is applied.