SURFACE-TREATED, TRANSPORTABLE ISO TANKS AND METHODS OF REDUCING DEPOSITION OF A FRICTION REDUCER ON A SURFACE

Abstract

The present invention provides treated, transportable ISO tanks comprising an interior metal surface and a hydrophobic surface layer applied thereto, directly or through an intermediate layer. The surface layer comprises a self-assembled monolayer prepared from a fluorinated material having the structure:

##STR00001##

wherein A is an oxygen radical or a chemical bond; n is 1 to 20; Y is H, F, C.sub.nH.sub.2n+1 or C.sub.nF.sub.2n+1; X is H or F; b is at least 1, m is 0 to 50, p is 1 to 20, and Z is an acid group or an acid derivative. Also provided is a method of reducing deposition of a friction reducer on a surface of an apparatus that stores or transports the same, comprising: contacting the surface with the above fluorinated material in a diluent, directly or through an intermediate layer; forming a film on the surface; and introducing the friction reducer therein.

Claims

1. A treated, transportable ISO tank comprising: a) an interior metal surface; and b) a hydrophobic surface layer applied to the interior metal surface either directly or through an intermediate organometallic layer, said hydrophobic surface layer comprising a self-assembled monolayer prepared from a fluorinated material having the following structure: ? wherein A is an oxygen radical or a chemical bond; n is 1 to 20; Y is H, F, C.sub.nH.sub.2n+1 or C.sub.nF.sub.2n+1; X is H or F; b is at least 1, m is 0 to 50, p is 1 to 20, and Z is an acid group or an acid derivative.

2. The treated, transportable ISO tank of claim 1, wherein the interior metal surface a) comprises stainless steel.

3. The treated, transportable ISO tank of claim 1 wherein Z is selected from: ? where R is a hydrocarbon or substituted hydrocarbon radical having up to 200 carbons, and R and R are each independently H, a metal or an amine or an aliphatic or substituted aliphatic radical having 1 to 50 carbons or an aryl or substituted aryl radical having 6 to 50 carbons.

4. The treated, transportable ISO tank of claim 3 wherein Z is ?

5. The treated, transportable ISO tank of claim 1 wherein n is 1 to 6; b is 5 to 12, m is 1 to 6, and p is 2 to 4.

6. The treated, transportable ISO tank of claim 1 wherein the fluorinated material is adhered to an intermediate organometallic layer.

7. The treated, transportable ISO tank of claim 6 wherein the intermediate organometallic layer is a polymeric metal oxide with alkoxide and hydroxyl groups.

8. A method of reducing deposition of a friction reducer on a metal surface of an apparatus that stores or transports the friction reducer, the method comprising: (a) contacting the surface either directly or through an intermediate organometallic layer with a fluorinated material in a diluent, wherein the fluorinated material has the following structure: ? wherein A is an oxygen radical or a chemical bond; n is 1 to 20; Y is H, F, C.sub.nH.sub.2n+1 or C.sub.nF.sub.2n+1; X is H or F; b is at least 1, m is 0 to 50, p is 1 to 20, and Z is an acid group or an acid derivative; (b) forming a hydrophobic surface layer on the metal surface; and (c) introducing the friction reducer into the apparatus.

9. The method of claim 8 wherein the friction reducer comprises a polyacrylamide polymer.

10. The method of claim 9 wherein the friction reducer is suspended in a carrier comprising mineral oil.

11. The method of claim 8 wherein the apparatus comprises an ISO tank.

12. The method of claim 8 wherein the surface comprises stainless steel.

13. The method of claim 8 wherein the fluorinated material is dissolved or dispersed in a diluent to form a solution or dispersion, and the solution or dispersion is coalesced on the surface to form the hydrophobic surface layer.

14. The method of claim 8 wherein Z is selected from: ? where R is a hydrocarbon or substituted hydrocarbon radical having up to 200 carbons, and R and R are each independently H, a metal or an amine or an aliphatic or substituted aliphatic radical having 1 to 50 carbons or an aryl or substituted aryl radical having 6 to 50 carbons.

15. The method of claim 14 wherein Z is ?

16. The method of claim 8 wherein n is 1 to 6; b is 5 to 12, m is 1 to 6, and p is 2 to 4.

17. The method of claim 8 wherein the fluorinated material in the hydrophobic surface layer is adhered to an intermediate organometallic layer.

18. The method of claim 17 wherein the intermediate organometallic layer is a polymeric metal oxide with alkoxide and hydroxyl groups.

19. The method of claim 8, wherein the diluent comprises at least one of a glycol, a glycol ether, 1,1,1,2,2,3,3,4,4-nonafluoro-4-methoxybutane, 1,1,1,2,2,3,3,4,4-nonafluoro-4-ethoxybutane, 3-ethoxyperfluoro(2-methylhexane), 1H,1H,5H-Octafluoropentyl-1,1,2,2-tetrafluoroethyl ether, and 1,1,1,2,3,4,4,5,5,5-Decafluoropentane.

20. The method of claim 19 wherein Z is selected from: ? where R is a hydrocarbon or substituted hydrocarbon radical having up to 200 carbons, and R and R are each independently H, a metal or an amine or an aliphatic or substituted aliphatic radical having 1 to 50 carbons or an aryl or substituted aryl radical having 6 to 50 carbons.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] FIGS. 1A and 1B are schematic side elevation and end elevation views, respectively, of a treated, transportable ISO tank of the present invention.

[0015] FIG. 2 is a schematic cross-sectional view of a portion of a treated, transportable ISO tank of the present invention according to one embodiment.

[0016] FIG. 3 is a schematic cross-sectional view of a portion of a treated, transportable ISO tank of another embodiment of the present invention that includes an intermediate organo-metallic layer.

DETAILED DESCRIPTION OF THE INVENTION

[0017] Other than in any operating examples, or where otherwise indicated, all numbers expressing quantities of ingredients, reaction conditions and so forth used in the specification and claims are to be understood as being modified in all instances by the term about. Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that may vary depending upon the desired properties to be obtained by the present invention. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques.

[0018] Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contain certain errors necessarily resulting from the standard deviation found in their respective testing measurements.

[0019] Also, it should be understood that any numerical range recited herein is intended to include all sub-ranges subsumed therein. For example, a range of 1 to 10 is intended to include all sub-ranges between (and including) the recited minimum value of 1 and the recited maximum value of 10, that is, having a minimum value equal to or greater than 1 and a maximum value of equal to or less than 10.

[0020] As used in this specification and the appended claims, the articles a, an, and the include plural referents unless expressly and unequivocally limited to one referent.

[0021] The various embodiments and examples of the present invention as presented herein are each understood to be non-limiting with respect to the scope of the invention.

[0022] As used in the following description and claims, the following terms have the meanings indicated below:

[0023] By polymer is meant a polymer including homopolymers and copolymers, and oligomers. By composite material is meant a combination of two or more differing materials.

[0024] As used herein, formed from denotes open, e. g., comprising, claim language. As such, it is intended that a composition formed from a list of recited components be a composition comprising at least these recited components, and can further comprise other, non-recited components, during the composition's formation.

[0025] As used herein, the term inorganic material means any material that is not an organic material.

[0026] As noted above, the present invention is directed to a treated, transportable ISO tank 10 as shown, for example, in FIGS. 1A and 1B in schematic elevational side and end views, respectively. The tank 10 may have any necessary shape, but is typically shaped like a cylinder. The tank 10 has an interior metal surface 202, shown in FIGS. 2 and 3. As a tank built to ISO standards, it typically has an interior stainless steel surface to minimize corrosion and possible contamination of the liquid being stored or transported.

[0027] The interior of the tank 10 is surface-treated with a hydrophobic surface layer 201 applied to the interior metal surface 202. A schematic cross-sectional view of a portion 200 of a treated, transportable ISO tank is illustrated in FIG. 2. The hydrophobic surface layer 201 comprises a self-assembled monolayer prepared from a fluorinated material in a treatment composition. The fluorinated material has the following structure:

##STR00003##

wherein A is an oxygen radical or a chemical bond; n is 1 to 20; Y is H, F, C.sub.nH.sub.2n+1 or C.sub.nF.sub.2n+1; X is H or F; b is at least 1, m is 0 to 50, p is 1 to 20, and Z is an acid group or an acid derivative.

[0028] In particular examples of the present invention, n is 1 to 6; b is 5 to 12, m is 1 to 6, and p is 2 to 4. Often, Z is selected from:

##STR00004## [0029] where R is a hydrocarbon or substituted hydrocarbon radical having up to 200 carbons, and R and R are each independently H, a metal or an amine or an aliphatic or substituted aliphatic radical having 1 to 50 carbons or an aryl or substituted aryl radical having 6 to 50 carbons. Typically, Z is

##STR00005##

[0030] The treatment composition may further comprise a diluent to form a solution. Suitable diluents include alcohols such as methanol, ethanol or propanol; aliphatic hydrocarbons such as hexane, isooctane and decane, ethers, for example, tetrahydrofuran and dialkylethers such as diethylether. Diluents for fluorinated materials can include perfluorinated compounds such as perfluorinated tetrahydrofuran. Also, aqueous alkaline solutions such as sodium and potassium hydroxide can be used as the diluent. In certain examples of the present invention, the diluent may comprise a slow-drying solvent such as glycols, glycol ethers, and hydrofluoroether solvents. Examples of particular hydrofluoroether solvents include 1,1,1,2,2,3,3,4,4-nonafluoro-4-methoxybutane and/or 1,1,1,2,2,3,3,4,4-nonafluoro-4-ethoxybutane, commercially available from 3M Corporation as NOVEC 7200. Other exemplary solvents include 3-ethoxyperfluoro(2-methylhexane) (HFE 7500, also available from 3M Corporation); 1H,1H,5H-Octafluoropentyl-1,1,2,2-tetrafluoroethyl ether (HFE 6512, available from Fuxin Hengtong); and/or 1,1,1,2,3,4,4,5,5,5-Decafluoropentane (VERTREL XF, available from E. I. DuPont de Nemours). Slower drying solvents provide application latitude and control, and are particularly useful when the treatment composition is to be used in regions with warmer weather, and where climate control is not available.

[0031] Adjuvant materials may be present in the treatment composition. Examples include surface active agents, stabilizers, and anti-static agents. The adjuvants if present are present in amounts of up to 30 percent by weight, based on the non-volatile content of the treatment composition.

[0032] The concentration of the fluorinated material in the solution is not particularly critical but is at least 0.01 millimolar, typically 0.01 to 100 millimolar, and more typically 0.1 to 50 millimolar. The solution can be prepared by mixing all of the components at the same time or by adding the components in several steps.

[0033] The treatment composition can be contacted with the metal surface 202 typically by immersion, spraying, flow coating, brush application or the like, followed by evaporating the solution medium at ambient temperatures or by the application of heat to effect formation of the self-assembled monolayer. The treatment composition may also be applied by wiping with a cloth. Slower drying solvents in the formulation are particularly useful for wipe application to minimize waste.

[0034] Adherence of the hydrophobic surface layer 201 to the metal surface 202 as shown in FIG. 2 may be through physical attraction or through chemically bonding. With physical attraction it is believed the group Z is in the form of the acid, rather than a salt or ester. In the case of chemical bonding, it is believed the acid forms an ionic or covalent bond with reactive groups on the metal surface.

[0035] The resultant self-assembled monolayer typically is of nano dimensions, having a thickness of no greater than 100 nm, typically about 10-100 nanometers. The layer is hydrophobic, having a water contact angle greater than 70?, typically from 75-130?. The water contact angle can be determined using a contact angle goniometer such as a TANTEC contact angle meter Model CAM-MICRO.

[0036] The hydrophobic surface layer 201 may be adhered to the metal surface 202 either directly or indirectly through an intermediate organometallic coating 203 as shown in FIG. 3. When better adhesion and durability than that afforded by direct application is desired, an organometallic coating 203 should be applied to the metal surface 202, followed by application of the treatment composition.

[0037] The organometallic compound used in the intermediate organometallic coating 203 is usually derived from a metal or metalloid, often a transition metal, selected from Group III and Groups IIIB, IVB, VB and VIB of the Periodic Table. Transition metals are used most often, such as those selected from Groups IIIB, IVB, VB and VIB of the Periodic Table. Examples are tantalum, titanium, zirconium, lanthanum, hafnium and tungsten. Niobium is also a suitable metal. The organo portion of the organometallic compound is selected from those groups that are reactive with the organophosphorus acid. Also, as will be described later, the organo group of the organometallic compound is believed to be reactive with groups on the surfaces being treated such as oxide and hydroxyl groups. Examples of suitable organo groups of the organometallic compound are alkoxide groups containing from 1 to 18, usually 2 to 4 carbon atoms, such as ethoxide, propoxide, isopropoxide, butoxide, isobutoxide, tert-butoxide and ethylhexyloxide. Mixed groups such as alkoxide, acetyl acetonate and chloride groups can be used.

[0038] The organometallic compounds can be in the form of simple alkoxylates or polymeric forms of the alkoxylate, and various chelates and complexes. For example, in the case of titanium and zirconium, the organometallic compound can include one or more of: [0039] a) alkoxylates of titanium and zirconium having the general formula M(OR).sub.4, wherein M is selected from Ti and Zr and R is C.sub.1-18 alkyl, [0040] b) polymeric alkyl titanates and zirconates obtainable by condensation of the alkoxylates of (a), i.e., partially hydrolyzed alkoxylates of the general formula RO[-M(OR).sub.2O].sub.x-1R, wherein M and R are as above and x is a positive integer, [0041] c) titanium chelates, derived from ortho titanic acid and polyfunctional alcohols containing one or more additional hydroxyl, halo, keto, carboxyl or amino groups capable of donating electrons to titanium. Examples of these chelates are those having the general formula:

Ti(O).sub.a(OH).sub.b(OR).sub.c(XY).sub.d [0042] wherein a=4-b-c-d; b=4-a-c-d; c=4-a-b-d; d=4-a-b-c; R is H, C.sub.1-18 alkyl, or X-Y, wherein X is an electron donating group such as oxygen or nitrogen and Y is an aliphatic radical having a two- or three-carbon atom chain such as [0043] I. CH.sub.2CH.sub.2, e.g., of ethanolamine, diethanolamine and triethanolamine [0044] II.

##STR00006## e.g., of lactic acid; [0045] III.

##STR00007## e.g., of acetylacetone end form; or [0046] IV.

##STR00008## e.g., as in 1,3-octyleneglycol; [0047] d) titanium acrylates having the general formula Ti(OCOR).sub.4-n(OR).sub.n wherein R is C.sub.1-18 alkyl as above and n is an integer of from 1 to 3, and polymeric forms thereof, or [0048] e) mixtures thereof.

[0049] The organometallic compound can be dissolved or dispersed in a diluent to form a solution. Examples of suitable diluents are alcohols such as methanol, ethanol and propanol, aliphatic hydrocarbons, such as hexane, isooctane and decane, ethers, for example, tetrahydrofuran and dialkyl ethers such as diethyl ether. The concentration of the organometallic compound in the solution is not particularly critical but is usually at least 0.01 millimolar, typically from 0.01 to 100 millimolar, and more typically from 0.1 to 50 millimolar.

[0050] Also, adjuvant materials may be present in the solution. Examples include stabilizers such as sterically hindered alcohols, surfactants and anti-static agents. The adjuvants if present are present in amounts of up to 30 percent by weight, based on the non-volatile content of the composition.

[0051] The organometallic treatment solution can be prepared by mixing all of the components at the same time or by combining the ingredients in several steps. If the organometallic compound chosen is reactive with moisture, (e.g. in the case of titanium (IV) n-butoxide, tantalum (V) ethoxide, aluminum (III) isopropoxide, etc.), care should be taken that moisture is not introduced with the diluent or adjuvant materials and that mixing is conducted in a substantially anhydrous atmosphere.

[0052] The organometallic solution can be contacted with the metal surface 202 typically by immersion, spraying, flow coating, brush application or the like, followed by removing excess solution and evaporating the diluent. This can be accomplished by heating to 50-200? C. or by simple exposure to ambient temperature, that is, from 20-25? C. Alternatively, the organometallic compound can be used neat and applied by vapor deposition techniques.

[0053] The resulting film may be in the form of a polymeric metal oxide with unreacted alkoxide and hydroxyl groups. This is accomplished by depositing the film under conditions resulting in hydrolysis and self-condensation of the alkoxide. These reactions result in a polymeric metal oxide coating being formed. The conditions necessary for these reactions to occur is to deposit the film in the presence of water, such as a moisture containing atmosphere; however, these reactions can be performed in solution by the careful addition of water. The resulting film has some unreacted alkoxide groups and/or hydroxyl groups for subsequent reaction and possible covalent bonding with the organophosphorus acid. Note that the phrase and/or when used in a list is meant to encompass alternative embodiments including each individual component in the list as well as any combination of components. For example, the list A, B, and/or C is meant to encompass seven separate embodiments that include A, or B, or C, or A+B, or A+C, or B+C, or A+B+C.

[0054] Although not intending to be bound by any theory, it is believed the polymeric metal oxide is of the structure:

[M(O).sub.x(OH).sub.y(OR).sub.z].sub.n

where M is the metal being used, R is an alkyl group containing from 1 to 30 carbon atoms; x+y+z=V, the valence of M; x is at least 1, y is at least 1, z is at least 1; x=V?y?z; y=V?x?z; z=V?x?y; n is greater than 2, such as 2 to 1000.

[0055] When the organometallic compound is used neat and applied by chemical vapor deposition techniques in the absence of moisture, a thin metal alkoxide film is believed to form. Polymerization, if any occurs, is minimized and the film may be in monolayer configuration. The resulting film typically has a thickness of 0.5 to 100 nanometers. When the organometallic compound is subjected to hydrolysis and self-condensation conditions as mentioned above, somewhat thicker films are formed.

[0056] Although not intending to be bound by any theory, it is believed the acid groups of the Z moiety chemically bond with oxide or hydroxyl groups on the metal surface or chemically bond with the hydroxyl or alkoxide group of the organometallic coating, resulting in a durable film. It is believed that the fluorinated material forms a self-assembled monolayer on the surface of the substrate (i. e., the metal surface or organometallic coating layer). Self-assembled layers or films are formed by the chemisorption and spontaneous organization of the material on the surface of the substrate. The fluorinated materials useful in the practice of the invention are amphiphilic molecules that have two functional groups. The first functional group, i.e., the head functional group, is the acid group and attaches by physical attraction or by chemical bonding to the surface of the substrate. The second functional group, the fluoro-functional group, i.e., the tail, extends outwardly from the surface of the substrate.

[0057] Typically, the hydrophobic surface layer 201 is adhered to the metal surface 202 in the forming of the treated interior surfaces 200, 300 of the tank 10, rendering the interior surfaces 200, 300 of the tank 10 resistant to deposition of a friction reducer thereon.

[0058] As detailed above one aspect of the present invention is directed to a treated, transportable ISO tank comprising: a) an interior metal surface; and b) a hydrophobic surface layer applied to the interior metal surface either directly or through an intermediate organometallic layer, said hydrophobic surface layer comprising a self-assembled monolayer prepared from a fluorinated material having the following structure:

##STR00009## [0059] wherein A is an oxygen radical or a chemical bond; n is 1 to 20; Y is H, F, C.sub.nH.sub.2n+1 or C.sub.nF.sub.2n+1; X is H or F; b is at least 1, m is 0 to 50, p is 1 to 20, and Z is an acid group or an acid derivative.

[0060] The present invention is further directed to a method of reducing deposition of a friction reducer on a metal surface 202 of an apparatus that stores or transports the friction reducer, such as an ISO tank. The method comprises: (a) contacting the surface as discussed earlier, either directly or through an intermediate organometallic layer 203, with a fluorinated material in a diluent. The fluorinated material may have any of the structures shown above. The method further comprises (b) forming a hydrophobic surface layer 201 on the metal surface 202. Typically, the fluorinated material is dissolved or dispersed in a diluent to form a solution or dispersion (i. e., the treatment composition discussed above), and the solution or dispersion is coalesced on the surface to form the hydrophobic surface layer 201. Film formation may be achieved as discussed above. After formation of the hydrophobic surface layer 201 on the metal surface 202, the method comprises c) introducing the friction reducer into the apparatus. The friction reducer typically comprises a polyacrylamide polymer as known in the art, and may be suspended in a carrier such as mineral oil. The hydrophobic surface layer 201 on the metal surface 202 reduces deposition of the friction reducer on the metal surface, allowing for easier cleaning of the apparatus.

[0061] Whereas particular embodiments of this invention have been described above for purposes of illustration, it will be evident to those skilled in the art that numerous variations of the details of the present invention may be made without departing from the scope of the invention as defined in the appended claims.