CARBON-BASED SOLID ACID CATALYST, PREPARATION METHOD OF CATALYST, AND APPLICATION TO HYDROTHERMAL CONVERSION OF BIOMASS
20220395818 · 2022-12-15
Assignee
Inventors
- Shurong WANG (Hangzhou, CN)
- Shanshan XIONG (Hangzhou, CN)
- Hao XU (Hangzhou, CN)
- Lingjun ZHU (Hangzhou, CN)
- Yunchao LI (Hangzhou, CN)
Cpc classification
B01J27/02
PERFORMING OPERATIONS; TRANSPORTING
B01J37/084
PERFORMING OPERATIONS; TRANSPORTING
B01J37/009
PERFORMING OPERATIONS; TRANSPORTING
C07D307/36
CHEMISTRY; METALLURGY
International classification
B01J27/02
PERFORMING OPERATIONS; TRANSPORTING
B01J37/00
PERFORMING OPERATIONS; TRANSPORTING
Abstract
A carbon-based solid acid catalyst, a preparation method of the catalyst, and a method to use the catalyst for hydrothermal conversion of biomass are provided. The preparation method of the carbon-based solid acid catalyst includes the following steps: S1. mixing pectin with water, adding concentrated sulfuric acid for activation, and adding a resulting mixture to an ionic resin with an aromatic ring matrix; S2. drying a material obtained in S1, crushing a dried material into a powder, and subjecting the powder to pyrolysis in a dry inert gas; S3. subjecting a solid obtained after the pyrolysis to sulfonation with concentrated sulfuric acid; S4. diluting a material obtained in S3 with water, filtering a resulting mixture, and washing a resulting filter residue with water until no sulfate ions are detected in washing water; S5. drying the filter residue.
Claims
1. A preparation method of a carbon-based solid acid catalyst, comprising: mixing a pectin and an ionic resin with an aromatic ring matrix in a medium to obtain a first resulting mixture, wherein the pectin is used as a carbon-based precursor, then drying the first resulting mixture, subjecting the first resulting mixture to a pyrolysis, and performing a sulfonation with concentrated sulfuric acid to obtain the carbon-based solid acid catalyst.
2. The preparation method of the carbon-based solid acid catalyst according to claim 1, wherein the preparation method specifically comprises the following steps: S1. mixing the pectin with water, adding sulfuric acid for an activation to obtain a second resulting mixture, and adding the second resulting mixture to the ionic resin with the aromatic ring matrix to obtain the first resulting mixture; S2. drying the first resulting mixture obtained in S1 to obtain a dried material, crushing the dried material into a powder, and subjecting the powder to the pyrolysis in a dry inert gas to obtain a solid; S3. subjecting the solid obtained after the pyrolysis in S2 to the sulfonation with the concentrated sulfuric acid to obtain a material; S4. diluting the material obtained in S3 with water to obtain a third resulting mixture, filtering the third resulting mixture to obtain a resulting filter residue, and washing the resulting filter residue with water until no sulfate ions are detected in washing water; S5. drying the resulting filter residue.
3. The preparation method of the carbon-based solid acid catalyst according to claim 1, wherein the preparation method specifically comprises the following steps: S1. mixing the pectin with water in a mass ratio of 1:(4-10), adding sulfuric acid for an activation to obtain a second resulting mixture, and adding the second resulting mixture to the ionic resin with the aromatic ring matrix to obtain the first resulting mixture, wherein a mass ratio of the ionic resin to the pectin is 1:(0.5-3); S2. drying the first resulting mixture obtained in S1 to obtain a dried black material, crushing the dried black material into a powder, and subjecting the powder to the pyrolysis for 0.5 h to 3 h in a dry inert gas to obtain a solid; S3. subjecting the solid obtained after the pyrolysis in S2 to the sulfonation with the concentrated sulfuric acid at 20° C. to 120° C. to obtain a material; S4. diluting the material obtained in S3 with water to obtain a third resulting mixture, filtering the third resulting mixture to obtain a resulting filter residue, and washing the resulting filter residue with water until no sulfate ions are detected in washing water; and S5. oven-drying the resulting filter residue.
4. The preparation method of the carbon-based solid acid catalyst according to claim 3, wherein in S1, the pectin comprises one or more from the group consisting of an orange peel pectin, a pomelo peel pectin, a lemon peel pectin, an apple pectin, and a banana peel pectin.
5. The preparation method of the carbon-based solid acid catalyst according to claim 3, wherein in S2, the dry inert gas is nitrogen, and the pyrolysis is conducted at 300° C. to 800° C. for 1 h to 2 h.
6. The preparation method of the carbon-based solid acid catalyst according to claim 3, wherein in S3, a mass ratio of the solid obtained after the pyrolysis in S2 to the concentrated sulfuric acid is 1:(3-8); and the sulfonation is conducted at 80° C. for 10 h to 48 h.
7. The preparation method of the carbon-based solid acid catalyst according to claim 2, wherein the ionic resin with the aromatic ring matrix comprises one or more from the group consisting of a sulfonated styrene-divinylbenzene cation-exchange resin and a chloromethylated polystyrene resin.
8. A carbon-based solid acid catalyst prepared by the preparation method according to claim 1.
9. A method of using a carbon-based solid acid catalyst prepared by the preparation method according to claim 1 for a hydrothermal conversion of biomass, comprising: using the carbon-based solid acid catalyst as a catalyst, and mixing the carbon-based solid acid catalyst with a biomass raw material or a carbohydrate in a solvent system to conduct the hydrothermal conversion to obtain a furan platform compound.
10. The method of using the carbon-based solid acid catalyst for the hydrothermal conversion of biomass according to claim 9, comprising: mixing the carbon-based solid acid catalyst with the biomass raw material in the solvent system to conduct the hydrothermal conversion, wherein a mass ratio of the carbon-based solid acid catalyst to the biomass raw material is 1:(1-10); the hydrothermal conversion is conducted at 120° C. to 190° C. for 0.5 h to 3 h; after the mixing, the biomass raw material has a concentration of 0.012 g/ml to 0.32 g/ml; and the solvent system is an organic solvent, water, or a mixture of the organic solvent and the water.
11. The method of using the carbon-based solid acid catalyst for the hydrothermal conversion of biomass according to claim 10, wherein the organic solvent comprises one or more from the group consisting of γ-valerolactone (GVL), dimethyl sulfoxide (DMSO), isopropyl alcohol (IPA), methyl isobutyl ketone (MIBK), tetrahydrofuran (THF), and N,N-dimethylformamide (DMF).
12. The method of using the carbon-based solid acid catalyst for the hydrothermal conversion of biomass according to claim 10, wherein when a biphasic solvent system of the water and the organic solvent is used, a product yield is further improved by adding a chloride salt; and the chloride salt comprises one or more from the group consisting of sodium chloride, potassium chloride, copper chloride, and aluminum chloride.
13. The method of using the carbon-based solid acid catalyst for the hydrothermal conversion of biomass according to claim 10, wherein the biomass raw material comprises one or more from the group consisting of glucose, xylose, arabinose, cellobiose, inulin, corn starch, peel, and crop straw; and the carbohydrate comprises one or more from the group consisting of glucose, xylose, disaccharide, and polysaccharide.
14. The method of using the carbon-based solid acid catalyst for the hydrothermal conversion of biomass according to claim 10, wherein the furan platform compound is furfural or pentahydroxymethyl furfural.
15. The carbon-based solid acid catalyst according to claim 8, wherein the preparation method specifically comprises the following steps: S1. mixing the pectin with water, adding sulfuric acid for an activation to obtain a second resulting mixture, and adding the second resulting mixture to the ionic resin with the aromatic ring matrix to obtain the first resulting mixture; S2. drying the first resulting mixture obtained in S1 to obtain a dried material, crushing the dried material into a powder, and subjecting the powder to the pyrolysis in a dry inert gas to obtain a solid; S3. subjecting the solid obtained after the pyrolysis in S2 to the sulfonation with the concentrated sulfuric acid to obtain a material; S4. diluting the material obtained in S3 with water to obtain a third resulting mixture, filtering the third resulting mixture to obtain a resulting filter residue, and washing the resulting filter residue with water until no sulfate ions are detected in washing water; S5. drying the resulting filter residue.
16. The carbon-based solid acid catalyst according to claim 8, wherein the preparation method specifically comprises the following steps: S1. mixing the pectin with water in a mass ratio of 1:(4-10), adding sulfuric acid for an activation to obtain a second resulting mixture, and adding the second resulting mixture to the ionic resin with the aromatic ring matrix to obtain the first resulting mixture, wherein a mass ratio of the ionic resin to the pectin is 1:(0.5-3); S2. drying the first resulting mixture obtained in S1 to obtain a dried black material, crushing the dried black material into a powder, and subjecting the powder to the pyrolysis for 0.5 h to 3 h in a dry inert gas to obtain a solid; S3. subjecting the solid obtained after the pyrolysis in S2 to the sulfonation with the concentrated sulfuric acid at 20° C. to 120° C. to obtain a material; S4. diluting the material obtained in S3 with water to obtain a third resulting mixture, filtering the third resulting mixture to obtain a resulting filter residue, and washing the resulting filter residue with water until no sulfate ions are detected in washing water; S5. oven-drying the resulting filter residue.
17. The carbon-based solid acid catalyst according to claim 16, wherein in S1, the pectin comprises one or more from the group consisting of an orange peel pectin, a pomelo peel pectin, a lemon peel pectin, an apple pectin, and a banana peel pectin.
18. The carbon-based solid acid catalyst according to claim 16, wherein in S2, the dry inert gas is nitrogen, and the pyrolysis is conducted at 300° C. to 800° C. for 1 h to 2 h.
19. The carbon-based solid acid catalyst according to claim 16, wherein in S3, a mass ratio of the solid obtained after the pyrolysis in S2 to the concentrated sulfuric acid is 1:(3-8); and the sulfonation is conducted at 80° C. for 10 h to 48 h.
20. The carbon-based solid acid catalyst according to claim 15, wherein the ionic resin with the aromatic ring matrix comprises one or more from the group consisting of a sulfonated styrene-divinylbenzene cation-exchange resin and a chloromethylated polystyrene resin.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0045]
[0046]
[0047]
[0048]
[0049]
DETAILED DESCRIPTION OF THE EMBODIMENTS
[0050] In the present disclosure, pectin with a large number of active groups is used as the carbon-based precursor, and an ionic resin with aromatic ring structure as a matrix is added to expand the liquid phase and improve the availability of acidic sites on the surface of a solid acid. And anaerobic carbonization is conducted at 300° C. to 800° C., and the product is ground and then subjected to sulfonation with concentrated sulfuric acid to obtain a highly-active carbon-based solid acid catalyst with strong adaptability and prominent recovery performance. According to existing patent technologies and literature reports, there is no technology similar to the present disclosure that uses the same carbon source to prepare a carbon-based solid acid catalyst through the combination of an ionic resin with aromatic ring matrix and a pectin carbon-based support. The catalyst prepared by the present disclosure has a significantly-improved effect, and can exhibit prominent catalytic performance under various reaction conditions. Moreover, the catalyst is not easy to coke, which has distinct particles and is easy to recycle. Specific effects will be described in detail in the examples.
[0051] The present disclosure provides a preparation method of a carbon-based solid acid catalyst, where pectin is used as the carbon-based precursor. And the pectin and an ionic resin with aromatic ring matrix are mixed in a medium, then dried, and subjected to pyrolysis and sulfonation with concentrated sulfuric acid to obtain the carbon-based solid acid catalyst. The preparation method may include the following steps:
[0052] S1. mixing the pectin with water, adding sulfuric acid for activation, and adding a resulting mixture to the ionic resin of the aromatic ring matrix;
[0053] S2. drying a material obtained in S1, crushing a dried material into a powder, and subjecting the powder to pyrolysis in a dry inert gas;
[0054] S3. subjecting a solid obtained after the pyrolysis in S2 to sulfonation with the concentrated sulfuric acid;
[0055] S4. diluting a material obtained in S3 with water, filtering a resulting mixture, and washing a resulting filter residue with water until no sulfate ions are detected in washing water;
[0056] S5. drying the filter residue.
[0057] Further, the preparation method may specifically include the following steps:
[0058] S1. mixing the pectin with water in a mass ratio of 1:(4-10), adding sulfuric acid for activation, and adding a resulting mixture to the ionic resin with aromatic ring matrix, where a mass ratio of the ionic resin to the pectin is 1:(0.5-3); the sulfuric acid has a mass fraction of 98%; and the pectin is fruit pectin, including one or more from the group consisting of orange peel pectin, pomelo peel pectin, lemon peel pectin, apple pectin, and banana peel pectin;
[0059] S2. drying a material obtained in S1 to a constant weight at 110° C. to 120° C., crushing a dried black material into a powder, and subjecting the powder to pyrolysis in a horizontal tube furnace at 300° C. to 800° C. for 0.5 h to 3 h in a dry inert gas;
[0060] S3. subjecting a solid obtained after the pyrolysis in S2 to sulfonation with the concentrated sulfuric acid at 20° C. to 120° C.;
[0061] S4. diluting a material obtained in S3 with water, filtering a resulting mixture, and washing a resulting filter residue with water until no sulfate ions are detected in washing water;
[0062] S5. oven-drying the filter residue.
[0063] Further, in S2, the inert gas may be nitrogen, and the pyrolysis may be conducted at 300° C. for 1 h.
[0064] Further, in S3, the mass ratio of the solid obtained after the pyrolysis in S2 to the concentrated sulfuric acid may be 1:(3-8). The concentrated sulfuric acid may be used to conduct sulfonation at 80° C. for 10 h to 48 h in an oil bath with magnetic stirring. And the concentrated sulfuric acid may have a mass fraction of 98%.
[0065] Further, the ionic resin with aromatic ring matrix may include one or more from the group consisting of sulfonated styrene-divinylbenzene cation-exchange resin and chloromethylated polystyrene resin.
[0066] In addition, the present disclosure also provides a carbon-based solid acid catalyst prepared by the preparation method described above.
[0067] The present disclosure also provides a method to use a carbon-based solid acid catalyst prepared by the preparation method described above for hydrothermal conversion of biomass, including mixing the carbon-based solid acid catalyst with a biomass raw material or a carbohydrate in a solvent system to conduct the hydrothermal conversion to obtain a furan platform compound.
[0068] The method may specifically include mixing the carbon-based solid acid catalyst with the biomass in the solvent system to conduct the hydrothermal conversion, where a mass ratio of the carbon-based solid acid catalyst to the biomass may be 1:(1-10). The hydrothermal conversion may be conducted at 120° C. to 190° C. for 0.5 h to 3 h. After the mixing, the feedstock may have a concentration of 0.012 g/ml to 0.32 g/ml. And the solvent system may be an organic solvent or water, or a mixture of the two. The organic solvent may include one or more from the group consisting of GVL, DMSO, IPA, MIBK, THF, and DMF. The biomass may include one or more from the group consisting of glucose, xylose, arabinose, cellobiose, inulin, corn starch, peel, and crop straw. And the carbohydrate may include one or more from the group consisting of glucose, xylose, disaccharide, and polysaccharide. The furan platform compound may be furfural or 5-(hydroxymethyl)furfural.
[0069] Furthermore, when a biphasic solvent system of water and an organic solvent is used, the product yield may be further improved by adding chloride salt. And the chloride salt may include one or more from the group consisting of sodium chloride, potassium chloride, copper chloride, and aluminum chloride.
[0070] In order to explain the content of the present disclosure more clearly, the following examples are described in detail. However, the present disclosure is not limited to the examples, that is, the examples should not limit the protection scope of the present disclosure.
Example 1
[0071] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water. 1 ml of concentrated sulfuric acid (98%) was added, and then a resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. A resulting mixture was dried at 110° C. to 120° C. for 48 h, and a resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. The black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of a dried black solid was added to a 10 ml test tube, then 0.1 g of xylose and 5 ml of GVL were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 140° C. to 180° C. The furfural yield was higher than 71 mol. %, and the highest yield could reach 85 mol. %.
[0072] From the electron microscopy images of
[0073] With reference to
TABLE-US-00001 TABLE 1 Surface acid Surface acid Surface acid concentration concentration concentration Catalyst type (mmol/g) 1 (mmol/g) 2 (mmol/g) 3 Pectin 0.15 0.11 0.09 Pectin carbon-based 1.35 1.43 1.37 solid acid
[0074] Table 1 shows acidity of the catalyst prepared in Example 1 of the present disclosure and acidity of pure pectin. The results not only show that the catalyst prepared by the present disclosure has reasonable acidity, but also confirm that the pectin itself has some weak acidity, which is conducive to the preparation of a carbon-based solid acid.
Example 2
[0075] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 100° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of xylose and 5 ml of GVL were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 130° C. The furfural yield was 57.6 mol. %.
Example 3
[0076] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 450° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of xylose and 5 ml of GVL were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 190° C. The furfural yield was 69.8 mol. %.
Example 4
[0077] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 800° C. for 0.5 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of xylose, 2 ml of GVL, and 3 ml of deionized water were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 52.9 mol. %.
Example 5
[0078] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 3 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of a dried black solid was added to a 10 ml test tube, then 0.1 g of xylose, 4 ml of GVL, 1 ml of deionized water, and 0.16 g of NaCl were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 70.6 mol. %.
Example 6
[0079] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 36 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of a dried black solid was added to a 10 ml test tube, then 0.1 g of xylose and 5 ml of DMSO were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 74.3 mol. %.
Example 7
[0080] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 2 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of a dried black solid was added to a 10 ml test tube, then 0.16 g of xylose and 5 ml of DMSO were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 69.2 mol. %.
Example 8
[0081] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 20° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.10 g of arabinose and 5 ml of DMSO were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 32.09 mol. %.
Example 9
[0082] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and then 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of xylose and 5 ml of GVL were added. And a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 77.6 mol. %.
Example 10
[0083] 2 g of dried apple pectin was mixed with 20 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 4 g of pre-dried 732 strongly-acidic styrene cation-exchange resin. The resulting mixture was dried at 110° C. to 120° C. for 24 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain the black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of arabinose and 5 ml of GVL were added, and a reaction was conducted for 2 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 17.1 mol. %.
Example 11
[0084] 2 g of dried apple pectin was mixed with 15 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 1 g of pre-dried Amberlyst ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 24 h, and a resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 10 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of glucose, 4 ml of THF, 1 ml of deionized water, and 0.16 g of NaCl were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 160° C. The 5-hydroxymethyl furfural yield was 33.1 mol. %.
Example 12
[0085] 2 g of dried citrus pectin was mixed with 20 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried 732 strongly-acidic styrene cation-exchange resin. The resulting mixture was dried at 110° C. to 120° C. for 24 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 90° C. for 48 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of a dried black solid was added to a 10 ml test tube, then 0.15 g of xylose and 5 ml of DMSO were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 48.8 mol. %.
Example 13
[0086] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/3 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.01 g of a dried black solid was added to a 10 ml test tube, then 0.1 g of xylose and 5 ml of GVL were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 68.5 mol. %.
Example 14
[0087] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid, and the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of xylose and 5 ml of GVL were added, and a reaction was conducted for 0.5 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 70.6 mol. %.
Example 15
[0088] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of xylose, 4 ml of GVL, 1 ml of deionized water, and 0.16 g of NaCl were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 68.7 mol. %.
Example 16
[0089] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of xylose and 5 ml of GVL were added, and a reaction was conducted for 3 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 65.5 mol. %.
Example 17
[0090] 8 g of dried orange peel pectin was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and the resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid. And the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of a dried black solid was added to a 10 ml test tube, then 0.1 g of xylose, 4 ml of GVL, 1 ml of deionized water, and 0.08 g of NaCl were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 170° C. The furfural yield was 66.7 mol. %.
Example 18
[0091] 20 g of fresh citrus peel (8 g of dry product) was weighed, washed with clean water, and placed in a 250 ml beaker, then 120 ml of water was added, and the beaker was heated to 90° C. and kept at the temperature for 5 min to 10 min to achieve enzymatic deactivation. The citrus peel was rinsed with water, cut into 3 to 5 mm particles, and then rinsed with hot water at about 50° C. until rinsing water was colorless and the peel had no peculiar smell. After each rinse, the peel was squeeze-dried with nylon cloth, and then the next rinse was conducted. Treated peel particles were placed in a beaker, then 0.2 mol/L hydrochloric acid was added to immerse the peel particles, and a pH of a resulting mixture was adjusted to 2.0 to 2.5. The mixture was heated to 90° C. and kept in a constant-temperature water bath for 40 min, during which the mixture was stirred continuously. And a Buchner funnel lined with nylon cloth (100 mesh) was used to filter a resulting mixture while hot to obtain a filtrate. 0.5% to 1% activated carbon was added to the filtrate, and the resulting mixture was heated to 80° C., subjected to decolorization for 20 min, and then subjected to suction filtration while hot (if the citrus peel is thoroughly rinsed and the filtrate was clear, the decolorization is not necessary). The resulting filtrate was cooled, the pH was adjusted to 3 to 4 with 6 mol/L ammonia water, and a 95% alcohol solution was slowly added under constant stirring. A volume of added ethanol was 1.5 times a volume of the original filtrate (to make a mass fraction of alcohol reach 50% to 60%). A pectin-like substance was precipitated during the process of adding the alcohol. After standing for 20 min, the resulting mixture was filtered with nylon cloth. And the resulting filter residue was transferred to a 100 ml beaker, 30 ml of absolute ethanol was added for washing, and then the filter residue was filtered out with nylon cloth and squeezed to obtain wet pectin. 9 g of wet pectin prepared (or 8 g of dry pectin, which was prepared as follows: the wet pectin was spread in a watch glass, dried at 60° C. to 70° C., and ground and sieved to obtain the dry pectin) was mixed with 30 ml of deionized water, and 1 ml of concentrated sulfuric acid (98%) was added. The resulting mixture was slowly added to 8 g of pre-dried Amberlyst 15 ionic resin. The resulting mixture was dried at 110° C. to 120° C. for 48 h, and a resulting black material was subjected to pyrolysis in a horizontal tube furnace at 300° C. for 1 h in dry nitrogen. Sulfonation was conducted with concentrated sulfuric acid (1 g solid/5 g H.sub.2SO.sub.4) at 80° C. for 24 h in an oil bath with magnetic stirring. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid, and the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried in an oven at 80° C. for 24 h. 0.05 g of the dried black solid was added to a 10 ml test tube, then 0.1 g of xylose and 5 ml of GVL were added, and a reaction was conducted for 1 h under microwave heating, where at a reaction temperature of 180° C. The furfural yield was 71 mol. %.
Comparative Example 1
[0092] Literature (Antonyraj C A, Haridas A. Catalysis Communications, 2018, 104: 101-105): Crude lignin was subjected to pyrolysis in a vertical tube furnace at 450° C. for 1 h in a nitrogen atmosphere. 3 g of a pyrolysis solid product was added to a 150 ml round-bottom flask, then 100 ml of concentrated sulfuric acid (98%) was added, and the resulting mixture was magnetically stirred at 60° C. for 18 h in an oil bath. The resulting material was diluted with a large amount of deionized water, and filtered to obtain a black solid, and the black solid was washed with deionized water several times until no sulfate ions were detected in washing water. The black solid was dried to a constant weight in an oven at 100° C. 12 ml of a 6.67 wt. % xylose solution (equivalent to 0.08 g of xylose) and 28 ml of MIBK were taken and mixed with 0.2 g of the catalyst obtained above, and a resulting mixture was subjected to a reaction at 175° C. for 3 h. The furfural yield was 58.8 mol. %.
Comparative Example 2
[0093] Literature (Wang Li, Zhang Zhu. Guangzhou Chemical Industry. 2017, 45 (18): 47-48) and literature (Zhou Wenjun, Zhou Yu, Zhang Xiazhong, Zeng Bin. Chemical Journal of Chinese Universities. 2016, 37 (4): 669-673): Pectin was used as a support to prepare a catalyst, and pectin was allowed to adsorb active groups through impregnation, which was completely different from the preparation method of using pectin as a carbon-based precursor in the present disclosure. In addition, pectin exhibited no catalytic effect on the reaction itself. Through the weak acidity of pectin itself, the present disclosure strengthens the acidity strength of the catalyst system and optimizes the strong and weak acidic site distribution of the catalyst. The catalysts obtained in the comparative literatures are used in the oxidation of benzaldehyde into benzoic acid and the Suzuki reaction, respectively, which are completely different from the hydrothermal conversion of biomass in which the catalyst prepared in the present disclosure is used.
Comparative Example 3
[0094] Literature (Ma Y, You S, Jing B, et al. International journal of hydrogen energy. 2019, 44 (31): 16624-16638) and literature (Fan Y, Liu P, Yang Z, et al. Electrochimica acta. 2015, 163: 140-148): Pectin was used as a carbon source to prepare an electrode material, where the gelation, emulsification, and stabilization functions of pectin were beneficial to the introduction of a silica template and a Fe species to form a porous structure. Therefore, the product in the comparative literature is used in a scenario completely different from that of the present disclosure. The present disclosure fully utilizes the physical property that pectin is easy to form a porous structure and the chemical properties of weak acidity and abundant surface active groups, which realizes the comprehensive utilization of pectin. The carbon-based solid acid catalyst prepared by the present disclosure can not only optimize the acidic site distribution, but also ensure sufficiently-developed pore structures and abundant free radicals, which is very conducive to the grafting of active groups.
Comparative Example 4
[0095] Literature (Liang Yu, Chen Zhihao, Liang Baoyan, etc. Chemical Journal of Chinese Universities, 2016, 37 (6): 1123-1127): A pyrolysis product of rice husk was used as a support to prepare a carbon-based solid acid catalyst, and the catalyst was used to catalyze the hydrothermal conversion of xylose into furfural.
[0096] The above examples are provided to illustrate the present disclosure, but not to limit the present disclosure. Any solution obtained by making a simple modification to the present disclosure shall fall within the protection scope of the present disclosure.