METHOD FOR PRODUCING BIO-PET RESIN

Abstract

Provided is a method for producing a bio-PET resin derived from substantially 100% a biomass resource, using a raw material derived from a carbon-neutral biomass resource as much as possible in place of a raw material derived from a petroleum resource. Ethylene glycol derived from a biomass resource is polymerized with terephthalic acid derived from a biomass resource in the presence of a catalyst containing an aluminum compound or a germanium compound.

Claims

1. A method for producing a Bio-PET resin, comprising the step of polymerizing ethylene glycol derived from a biomass resource with terephthalic acid derived from a biomass resource, in the presence of a catalyst comprising an aluminum compound or a germanium compound.

2. The method according to claim 1, wherein a copolymerizing component is not added.

3. The method according to claim 2, wherein the copolymerizing component is isophthalic acid, cyclohexanedimethanol, or diethylene glycol.

4. The method according to claim 1, wherein the aluminum compound is an organic aluminum compound selected from aluminum acetate, aluminum lactate, aluminum chloride, aluminum hydroxide, aluminum hydroxychloride, aluminum acetylacetonate, acetylacetone aluminum, aluminum oxalate, aluminum oxide or alkylaluminum, or partial hydrolysates of the organic aluminum compound, or any combinations thereof.

5. The method according to claim 1, wherein the germanium compound is germanium tetroxide, germanium tetraethoxide, germanium tetra-n-butoxide, crystalline germanium dioxide, amorphous germanium dioxide, germanium hydroxide, germanium oxalate, germanium chloride or germanium phosphite, or any combinations thereof.

6. The method according to claim 1, wherein the biomass resource is a saccharide material selected from sugarcane, molasses or beet, a starchy material selected from corn, sorghum, potato, sweet potato, barley and cassava, a cellulosic plant-derived material selected from pulp spent liquor, bagasse, scrap wood, wood chips, husks, rice straw, fruit fiber, fruit kernel shells or empty fruit bunches, a natural fiber product or its waste product, or any combination thereof.

7. The method according to claim 1, wherein the step of polymerizing the ethylene glycol derived from a biomass resource and the terephthalic acid derived from a biomass resource comprises producing bis(?-hydroxyethyl)terephthalate (BHET) and/or oligomer thereof as an intermediate by suspension polymerization of the ethylene glycol derived from a biomass resource and the terephthalic acid derived from a biomass resource to, and melt-polycondensing the obtained BHET and/or oligomer thereof in the presence of the catalyst.

8. The method according to claim 7, further comprising processing the Bio-PET resin obtained by the melt-polycondensation into pellets and subjecting them to solid phase polymerization.

9. The method according to claim 1, wherein the intrinsic viscosity (IV) of the Bio-PET resin is 0.7 to 0.85 dl/g.

10. The method according to claim 1, wherein more than 97 wt % of the components of the Bio-PET resin are derived from a biomass resource.

11. The method according to claim 10, wherein more than 99 wt % of the components of the Bio-PET resin are derived from a biomass resource.

12. The method according to claim 11, wherein more than 99.9 wt % of the components of the Bio-PET resin are derived from a biomass resource.

13. A method for producing a PET product, comprising supplying a Bio-PET resin by the method according to claim 1, and processing the Bio-PET resin into a PET product.

14. The method according to claim 13, wherein the PET product is a PET bottle.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0044] FIG. 1 shows a typical production scheme for a Bio-PET resin of the invention.

DESCRIPTION OF THE EMBODIMENTS

[0045] A biomass resource is generally defined as a renewable, organism-derived organic resource, excluding petroleum resources. Since a biomass resource is an organic material its combustion discharges carbon dioxide, but the carbon contained within it is derived from the carbon dioxide absorbed from the atmosphere by photosynthesis and the like during the course of growth of the organism that is the biomass resource, and therefore even if a biomass resource is utilized, it is considered to be carbon-neutral, i.e. not increasing the amount of carbon dioxide in the atmosphere in an overall sense. Based on this viewpoint, it does not constitute a cause of global warming since it does not increase the overall carbon dioxide concentration in the atmosphere. Furthermore, with appropriate management, biomass resources can be utilized without depletion, unlike fossil resources such as petroleum.

[0046] The biomass resource is not particularly restricted so long as it can yield ethylene glycol and/or terephthalic acid, and it may be a waste biomass resource (e.g., paper, livestock feces or urine, food scrap material, construction scrap material, black liquor, sewer water sludge or food waste), or an unused biomass resource (e.g., rice straw, wheat straw, rice hull, forest land remainders, resource crops, feed crops or starch-based crops). Specifically, there may be mentioned natural fiber products and their waste products (including surplus unused products), examples of which include saccharide materials (sugarcane, molasses, beet and the like), starchy materials (corn, sorghum, potato, sweet potato, barley, cassava and the like), and other cellulosic plant-derived materials (pulp spent liquor, bagasse, scrap wood, wood chips, husk, rice straw, fruit fiber, fruit kernel shells and empty fruit bunches), as well as natural fiber products or its wastes (including unused products, such as excess stock products) exemplified as sundry goods or daily commodities that include cotton and hemp (such as towels, handkerchiefs, clothing, stuffed dolls and curtains).

[0047] The ethylene glycol derived from a biomass resource and the terephthalic acid derived from a biomass resource, which are to serve as starting materials for the Bio-PET resin, can be produced by known methods such as catalytic rapid thermal decomposition, liquid phase reforming, catalyst-based chemical conversion, acid hydrolysis, enzymatic hydrolysis, microbial decomposition, fermentative conversion, bacterial decomposition or hydrotreatment. For example, ethylene glycol derived from a biomass resource can be obtained, for example, by fermenting a biomass resource to extract bioethanol, converting the obtained bioethanol to ethylene, and further converting it to ethylene glycol via ethylene oxide. Terephthalic acid derived from a biomass resource can be obtained, for example, by catalytic rapid thermal decomposition of the biomass to produce xylene, followed by separation and purification and isomerization treatment to form para-xylene, and liquid phase oxidation reaction of the para-xylene.

[0048] The ethylene glycol derived from the biomass resource and the terephthalic acid derived from the biomass resource are polymerized in the presence of a catalyst comprising an aluminum compound or a germanium compound, to produce a Bio-PET resin.

[0049] In the conventional methods for producing PET resins, the catalyst used is an antimony compound such as antimony trioxide, which is inexpensive and has excellent catalytic activity, or a titanium compound that has excellent safety and reactivity. When antimony compounds or titanium compounds are used, however, they must be added in large amounts during the polymerization, and therefore their residual contents in the PET resin increase and the crystallization rates are higher. As a result, the transparency is impaired and the physical properties for use as bottles (e.g., heat resistance and pressure resistance) are no longer suitable. It therefore becomes necessary to add a copolymerizing component, such as isophthalic acid, cyclohexanedimethanol, or diethylene glycol, as a component that inhibits excess crystallization, in addition to the major polymerizing components of monoethylene glycol and terephthalic acid. While the copolymerizing component, such as isophthalic acid, cyclohexanedimethanol, or diethylene glycol, in a PET resin is present at a few wt % (about 0.1 to 3 wt %), considering the massive amounts of PET resins that are consumed throughout the world, it would clearly be a major contribution toward improving the earth environment if it were possible to avoid the use of starting materials derived from petroleum resources even for such trace components. Here, the present inventors have gained the surprising knowledge that the addition of a copolymerizing component, such as isophthalic acid, cyclohexanedimethanol, or diethylene glycol, in the production of Bio-PET resins can be avoided by using an aluminum compound or germanium compound as the catalyst, such catalysts having relatively high catalytic activity. Conventionally, in the production of PET resins using starting materials derived from petroleum resources, the use of aluminum compounds and germanium compounds as polyester polymerization catalysts has been known (PTLs 3 to 9). However, the production of a Bio-PET resin substantially 100% derived from a biomass resource by the use of such a catalyst to avoid the addition of a copolymerizing component, such as isophthalic acid, cyclohexanedimethanol, or diethylene glycol, has not been attempted. Furthermore, it was demonstrated that when an aluminum compound or germanium compound is used as the catalyst, the transparency or intrinsic viscosity (IV) retention of the PET resin is increased, compared to those when another catalyst such as an antimony compound or titanium compound is used. Such properties are also advantageous for processing or recycling into PET products.

[0050] Examples of aluminum compounds to be used for the invention include organic aluminum compounds such as aluminum acetate, aluminum lactate, aluminum chloride, aluminum hydroxide, aluminum hydroxychloride, aluminum acetylacetonate, acetylacetone aluminum, aluminum oxalate, aluminum oxide, or alkylaluminum, and partial hydrolysates of the foregoing, with no limitation to these. The aluminum compound may be used in an amount such that the content as aluminum atoms in the resin is typically about 1 to about 50 ppm, preferably about 3 to about 40 ppm, and most optimally about 10 to about 20 ppm.

[0051] The germanium compound to be used for the invention may be a compound such as germanium tetroxide, germanium tetraethoxide, germanium tetra-n-butoxide, crystalline germanium dioxide, amorphous germanium dioxide, germanium hydroxide, germanium oxalate, germanium chloride or germanium phosphite, with no limitation to these. The germanium compound may be used in an amount such that the content as germanium atoms in the resin is typically about 1 ppm to 100 ppm.

[0052] The polymerization step for the Bio-PET resin may be any of publicly known steps, but comprises, as shown in FIG. 1 for example, suspension polymerization of ethylene glycol (liquid) derived from a biomass resource and terephthalic acid (powder) derived from a biomass resource, to obtain bis(?-hydroxyethyl)terephthalate (BHET) and/or oligomer thereof as an intermediate, followed by dehydrating reaction in a high vacuum at about 270 to 300? C. in the presence of a catalyst comprising an aluminum compound or a germanium compound, for melt-polycondensation of the obtained BHET. The catalyst comprising an aluminum compound or a germanium compound may be added into a reaction system at any stage of the polymerization reaction. Such a catalyst may be added into the reaction system at any stage, for example, before the start of esterification or transesterification or at any stage during the reaction, or immediately before the start of polycondensation or at any stage during the polycondensation. However, the catalyst is preferably added immediately before the start of polycondensation. The method for adding the catalyst is not particularly limited. The catalyst may be added in the form of a powder or a neat or in the form of a slurry or a solution of a solvent such as ethylene glycol derived from a biomass resource. The melt polycondensation may be carried out in a batch reactor or a continuous reactor. The melt polycondensation may be carried out in one stage or in multiple stages.

[0053] A phosphorus compound may also be added as a stabilizer to prevent yellowing. Examples of the phosphorus compound include phosphoric acid, phosphoric acid esters, phosphonic acid-type compounds, phosphinic acid-type compounds, phosphine oxide-type compounds, phosphonous acid-type compounds, hypophosphinic acid-type compounds, and phosphine-type compounds. The phosphorus compound and the above catalyst may be added at the same time or separately.

[0054] The Bio-PET resin obtained by the melt-polycondensation may be extruded and processed into pellets with a pelletizer to obtain transparent pellets.

[0055] In cases where a low acetaldehyde content or low cyclic trimer content is required, such as for beverage bottle uses, and especially heat-proof blow molded containers for low flavor beverages or mineral water, the polyester obtained by melt polycondensation in this manner is subjected to solid-phase polymerization. Like the melt polycondensation, solid-phase polymerization may be carried out in a batch device or a continuous device. The solid-phase polymerization step and the melt polycondensation step may be operated continuously or dividedly. Pellets are heated for a prescribed time period at a temperature of 100 to 210? C., in an inert gas or under reduced pressure, or in water vapor or a water vapor-containing inert gas atmosphere, for pre-crystallization (white pellets: in order to prevent fusion between the pellets during solid-phase polymerization). Solid-phase polymerization is then conducted for a prescribed time period at a temperature of 190 to 230? C., under an inert gas atmosphere or under reduced pressure.

[0056] Conducting solid-phase polymerization can cause polymerization between the PET resin molecules and increase the strength of it. Conducting solid-phase polymerization can also reduce impurities such as acetaldehyde or cyclic oligomers present in the resin starting materials.

[0057] It is thus possible to obtain a Bio-PET resin derived from substantially 100% biomass resources by avoiding the addition of a copolymerizing component, such as isophthalic acid, cyclohexanedimethanol, or diethylene glycol. The phrase derived from substantially 100% biomass resources means that more than 97 wt %, preferably more than 98 wt %, more preferably more than 99 wt %, and optimally 99.9 wt % of the components of the obtained Bio-PET resin are derived from biomass resources. Moreover, the obtained Bio-PET resin has excellent transparency and intrinsic viscosity (IV) retention, and is highly useful as a material for a PET product such as a PET bottle.

[0058] By processing the Bio-PET resin into a PET product by a known method it is possible to produce a PET product with high added value. Such PET products include, but are not limited to, containers for beverages, foods, cosmetics, drugs, detergents and the like (and especially soft drink PET bottles), as well as photographic films, cassette tapes, and clothing fibers such as fleece. Examples of PET bottles for soft drinks include heat-resistant PET bottles, aseptic packaging PET bottles, pressure-resistant PET bottles and heat-resistant/pressure-resistant PET bottles.