Polyimides, coating composition formed therefrom and use thereof

Abstract

A polyimide (PI) having two COOH capping groups at each end is provided. A coating composition is further provided, which contains the PI and a hardening agent having 2 to 6 functional groups capable of reacting with COOH. A PI coating layer and PI film formed by the coating composition of the present invention possess excellent chemical resistance and coefficient of thermal expansion (CTE), which makes them applicable in fabrication of protective materials for active/passive devices, optical materials, touch panels, copper foil substrates, soft flexible electronic materials or integrated circuit elements, or film substrate for glass film touch panels.

Claims

1. A coating composition comprising at least 1% of polyimide (PI), based on the total weight of the composition, and a hardening agent having 2 to 6 functional groups capable of reacting with COOH, wherein the polyimide (PI) has a structure represented by Formula (I): ##STR00029## wherein: A, C and E are the same or different and are each independently a tetravalent organic group, and if n is greater than 1, each C is the same or a different tetravalent organic group; each B is the same or different, and is independently a divalent organic group; and n is an integer greater than 0, and wherein the 2 to 6 functional groups of the hardening agent are selected from the group consisting of an oxazolyl group, a benzoxazinyl group, and a mixture thereof.

2. The coating composition according to claim 1, wherein A, C and E are respectively a tetravalent organic group selected from the group consisting of the following groups: ##STR00030## wherein: each X is independently hydrogen, halogen, a linear or branched C.sub.1-C.sub.4 perfluoroalkyl group, or a linear or branched C.sub.1-C.sub.4 alkyl group; and A.sub.1 and B.sub.1 are each independently a covalent bond, a linear or branched C.sub.1-C.sub.4 alkyl group, a linear or branched C.sub.1-C.sub.4 perfluoroalkyl group, an alkoxy group, silanyl, oxygen, sulfur, carbonyl, a carboxylate group, sulfonyl, phenyl, biphenyl, fluorenyl, or ##STR00031## wherein J is O, SO.sub.2, CH.sub.2, C(CF.sub.3).sub.2, and C(CH.sub.3).sub.2.

3. The coating composition according to claim 2, wherein A, C and E are respectively a tetravalent organic group selected from the group consisting of the following groups: ##STR00032## ##STR00033## ##STR00034## wherein Z is hydrogen or halogen.

4. The coating composition according to claim 3, wherein A, C and E are respectively a tetravalent organic group selected from the group consisting of the following groups: ##STR00035##

5. The coating composition according to claim 1, wherein B is respectively a divalent organic group selected from the group consisting of the following groups: ##STR00036## wherein: each R.sub.17 is independently H, a C.sub.1-C.sub.4 alkyl group, a C.sub.1-C.sub.4 perfluoroalkyl group, methoxy, ethoxyl, halogen, OH, COOH, NH.sub.2, or SH; each a is independently an integer of 0 to 4; each b is independently an integer of 0 to 4; and R.sub.18 is a covalent bond or is selected from the following groups: ##STR00037## wherein: c and d are each independently an integer of 0 to 20; R.sub.17 and a are as defined above; R.sub.19 is S(O).sub.2, C(O), a covalent bond, or a linear or branched C.sub.1-C.sub.18 alkyl group; each R.sub.20 is independently H, methyl, ethyl, or phenyl; each R.sub.21 is independently a C.sub.1-C.sub.20 alkyl group or a cyclic alkyl group; each m is independently an integer of 1 to 20; and e and f are each independently an integer greater than 0.

6. The coating composition according to claim 5, wherein B is respectively a divalent organic group selected from the group consisting of the following groups: ##STR00038## ##STR00039## ##STR00040## ##STR00041## wherein: each a is independently an integer of 0 to 4; and each Z is independently hydrogen, methyl, trifluoromethyl or halogen.

7. The coating composition according to claim 6, wherein B is respectively a divalent organic group selected from the group consisting of the following groups: ##STR00042## ##STR00043##

8. The coating composition according to claim 1, wherein n is an integer of 1 to 100.

9. A flexible device, comprising a thin film formed by the coating composition according to claim 1.

10. The coating composition according to claim 1, wherein the hardening agent is (1,3-bis(4,5-dihydrooxazol-2-yl)benzene).

Description

DETAILED DESCRIPTION OF THE INVENTION

(1) The PI of the present invention has a structure represented by Formula (I):

(2) ##STR00005##
where: A, C, and E may be the same or different and are each independently a tetravalent organic group, and if n is greater than 1, each C may be the same or different tetravalent organic group; each B may be the same or different, and is independently a divalent organic group; and n is an integer greater than 0.

(3) Preferably, A, C, and E are respectively a tetravalent organic group selected from the group consisting of the following groups:

(4) ##STR00006##
where: each X is independently hydrogen, halogen, a linear or branched C.sub.1-C.sub.4 perfluoroalkyl group, or a linear or branched C.sub.1-C.sub.4 alkyl group; and

(5) A.sub.1 and B.sub.1 are each independently a covalent bond, a linear or branched C.sub.1-C.sub.4 alkyl group, a linear or branched C.sub.1-C.sub.4 perfluoroalkyl group, an alkoxy group, silanyl, oxygen, sulfur, carbonyl, a carboxylate group, sulfonyl, phenyl, biphenyl, fluorenyl, or

(6) ##STR00007##
where J is O, SO.sub.2, CH.sub.2, C(CF.sub.3).sub.2, or C(CH.sub.3).sub.2.

(7) More preferably, A, C, and E are respectively a tetravalent organic group selected from the group consisting of the following groups:

(8) ##STR00008## ##STR00009## ##STR00010##
where Z is hydrogen or halogen.

(9) Especially preferably, A, C, and E are respectively a tetravalent organic group selected from the group consisting of the following groups:

(10) ##STR00011##

(11) Preferably, B is respectively a divalent organic group selected from the group consisting of the following groups:

(12) ##STR00012##
where: each R.sub.17 is independently H, a C.sub.1-C.sub.4 alkyl group, a C.sub.1-C.sub.4 perfluoroalkyl group, methoxy, ethoxyl, halogen, OH, COOH, NH.sub.2 or SH; each a is independently an integer of 0 to 4; each b is independently an integer of 0 to 4; and R.sub.18 is a covalent bond or a group selected from the following groups:

(13) ##STR00013##
where: c and d are each independently an integer of 0 to 20; R.sub.17 and a are as defined above; R.sub.19 is S(O).sub.2, C(O), a covalent bond, or a linear or branched C.sub.1-C.sub.18 alkyl group; each R.sub.20 is independently H, methyl, ethyl, or phenyl; each R.sub.21 is independently a C.sub.1-C.sub.20 alkyl group or a cyclic alkyl group; each m is independently an integer of 1 to 20; and e and f are each independently an integer greater than 0.

(14) More preferably, B is respectively a divalent organic group selected from the group consisting of the following groups:

(15) ##STR00014## ##STR00015## ##STR00016## ##STR00017## ##STR00018##
where: each a is independently an integer of 0 to 4; and each Z is independently hydrogen, methyl, trifluoromethyl or halogen.

(16) To allow the PI to have a preferred solubility and be resistant to yellowing after being solidified, according to a specific embodiment of the present invention, B is respectively a divalent organic group selected from the group consisting of the following groups:

(17) ##STR00019## ##STR00020##

(18) In Formula (I), n is an integer of 1 to 100, and preferably, an integer of 10 to 50.

(19) The PI of the present invention may be obtained by any conventional preparation methods known to persons of ordinary skill in the art. For example, the PI may be prepared by a method including the following steps: (a) reacting a dianhydride monomer represented by Formula (1) below in an excess amount with a diamine monomer represented by Formula (2) in a solvent to form a compound represented by Formula (3-1) below; or reacting a diamine monomer represented by Formula (2) in an excess amount with a dianhydride monomer represented by Formula (1) below to form a compound represented by Formula (3-2) below:

(20) ##STR00021## (b) next, subjecting the compound represented by Formula (3-1) to ring closure through heating dehydration or chemical cyclization, to form a compound represented by Formula (4) below:

(21) ##STR00022## (c) or, adding another dianhydride monomer represented by Formula (5) or (6) below to the compound represented by Formula (3-2) above, and subjecting the mixture to ring closure through heating dehydration or chemical cyclization, to form a compound represented by Formula (7) below:

(22) ##STR00023## (d) next, subjecting the compound represented by Formula (4) or (7) to ring opening, to form a compound represented by Formula (8) or (9) below:

(23) ##STR00024##
In the above step, a ratio between the total moles of the dianhydride monomer and the diamine monomer is 1:0.99 to 1:0.66, and A, B, C, E, and n are as defined above.

(24) Dianhydrides suitable for use in the above preparation method generally may be an aliphatic dianhydride or aromatic dianhydride. If a dianhydride having good chemical resistance is demanded, it is preferred to use an aromatic dianhydride. Examples of the aromatic dianhydride include (but are not limited to) pyromellitic dianhydride (PMDA), 3,3,4,4-biphenyltetracarboxylic dianhydride (S-BPDA), 4,4-diphthalic dianhydride, 4,4-hexafluoroisopropylidene-2,2-bis-(phthalic acid anhydride) (6FDA), 1-(trifluoromethyl)-2,3,5,6-benzenetetraearboxylic dianhydride (P3FDA), benzophenone-tetraearboxylic dianhydride (BTDA), 3,3,4,4-diphenyl ether tetracarboxylic dianhydride (ODPA), 1,4-bis-(trifluoromethyl)-2,3,5,6-benzenetetraearboxylic dianhydride (P6FDA), 1-(3,4-dicarboxyl phenyl)-1,3,3-trimethyl indane-5,6-dicarboxylic dianhydride, 1-(3,4-dicarboxyl phenyl)-1,3,3-trimethyl indane-6,7-dicarboxylic dianhydride, 1-(3,4-dicarboxyl phenyl)-3-methyl indane-5,6-dicarboxylic dianhydride, 1-(3,4-dicarboxyl phenyl)-3-methyl indane-6,7-dicarboxylic dianhydride, 2,3,9,10-perylenetetraearboxylic dianhydride, 1,4,5,8-naphthalenetetraearboxylic dianhydride, 2,6-dichloronaphtalene-1,4,5,8-tetraearboxylic dianhydride, 2,7-dichloronaphtalene-1,4,5,8-tetraearboxylic dianhydride, 2,3,6,7-tetrachloronaphthalene-2,4,5,8-tetraearboxylic dianhydride, phenanthrene-1,8,9,10-tetraearboxylic dianhydride, 3,3,4,4-benzophenonetetraearboxylic dianhydride, 1,2,3,3-benzophenonetetraearboxylic dianhydride, 3,3,4,4-benzophenonetetraearboxylic dianhydride, 2,2,3,3-biphenyl tetracarboxylic dianhydride, 4,4-isopropylidene diphthalic dianhydride, 3,3-isopropylidene diphthalic dianhydride, 4,4-oxydiphthalic dianhydride, 4,4-sulfonyl diphthalic dianhydride, 3,3-oxydiphthalic dianhydride, 4,4-methylene diphthalic dianhydride, 4,4-sulfenyl diphthalic dianhydride, 4,4-ethylidene diphthalic dianhydride, 2,3,6,7-naphthalenetetraearboxylic dianhydride, 1,2,4,5-naphthalenetetraearboxylic dianhydride, 1,2,5,6-naphthalenetetraearboxylic dianhydride, benzene-1,2,3,4-tetraearboxylic dianhydride, pyridine-2,3,5,6-tetraearboxylic dianhydride, 1,2,3,4-cyclobutanetetracarboxylic dianhydride (CBDA), 5,5-(9H-fluorene-9,9-diyl)diisobenzofuran-1,3-dione (BPAF), or a combination thereof.

(25) Preferably, an aromatic dianhydride selected from the following group is used: PMDA, S-BPDA, 4,4-diphthalic dianhydride, 6FDA, P3FDA, P6FDA, BTDA, ODPA, CBDA, BPAF, and a mixture thereof.

(26) Diamines suitable for the aforementioned preparation method are not particularly limited, and an aromatic diamine is generally used. An aromatic diamine useful in the method of the present invention is well known to those skilled in the art. The aromatic diamine may be, for example, (but not limited to) selected from the following groups: 4,4-oxydianiline (ODA), p-phenylenediamine (pPDA), m-dimethyl p-diamino biphenyl (DMDB), 2,2-bis(trifluoromethyl)benzidine (TFMB), o-Tolidine (oTLD), 4,4-octafluorobenzidine (OFB), trafluoro-p-phenylene diamine (TFPD), 2,2-5,5-tetrachlorobenzidine (TCB), 3,3-dichlorobenzidine (DCB), 2,2-bis(3-aminophenyl)hexafluoropropane, 2,2-bis-(4-aminophenyl)hexafluoropropane, 4,4-oxy-bis[3-(trifluoromethyl)aniline, 3,5-diaminobenzotrifluoride, tetrafluoro-1,4-phenylene diamine, tetrafluoro-m-phenylene diamine, 1,4-bis(4-aminophenoxy)-2-tert-butylbenzene (BATB), 2,2-dimenthyl-4,4-bis-(4-aminophenoxy)biphenyl (DBAPB), 4,4-diaminodicyclohexylmethane (MDCA), 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane (BAPPH), 2,2-bis[4-(4-amino phenoxy)phenyl]norbornane (BAPN), 5-amino-1-(4-aminophenyl)-1,3,3-trimethyl indane, 6-amino-1-(4-aminophenyl)-1,3,3-trimethyl indane, 4,4-methylene-bis(o-chloroaniline), 3,3-dichlorodiphenylamine, 3,3-sulfonyl diphenylamine, 4,4-diaminobenzophenone, 1,5-diaminonaphthalene, bis(4-aminophenyl)diethyl silane, bis(4-aminophenyl)diphenyl silane, bis(4-aminophenyl)ethyl phosphine oxide, N-(bis(4-aminophenyl))-N-methylamine, N-(bis(4-aminophenyl))-N-phenylamine, 4,4-methylene-bis(2-methylaniline), 4,4-methylene-bis(2-anisidine), 5,5-methylene-bis(2-aminophenol), 4,4-methylene-bis(2-methylaniline), 4,4-oxybis(2-anisidine), 4,4-oxybis(2-chloroaniline), 2,2-bis(4-aminophenol), 5,5-oxybis(2-aminophenol), 4,4-sulfenyl-bis(2-methylaniline), 4,4-sulfenyl-bis(2-anisidine), 4,4-sulfenyl-bis(2-chloroaniline), 4,4-sulfonyl-bis(2-methylaniline), 4,4-sulfonyl-bis(2-ethoxyaniline), 4,4-sulfonyl-bis(2-chloroaniline), 5,5-sulfonyl-bis(2-aminophenol), 3,3-dimenthyl-4,4-diaminobenzophenone, 3,3-dimethoxy-4,4-diaminobenzophenone, 3,3-dichloro-4,4-diaminobenzophenone, 4,4-diaminodiphenyl, m-phenylenediamine, 4,4-methylenediphenylamine (MDA), 4,4-sulfenyl diphenylamine, 4,4-sulfonyl diphenylamine, 4,4-isopropylidene diphenylamine, 3,3-dimethoxybenzidine, 3,3-dicarboxylicbenzidine, 2,4-toluene diamine, 2,5-toluene diamine, 2,6-toluene diamine, m-xylyl diamine, 2,4-diamino-5-chlorotoluene, 2,4-diamino-6-chlorotoluene, 1,4-diaminocyclohexane (CHDA), 4-(9-(4-aminophenyl)-9H-fluoren-9-yl)benzenamine (BAFL), 9-(4-aminophenyl)-9-phenyl-9H-fluoren-3-amine, 1-(4-aminophenyl)-2,3-dihydro-1,3,3-trimethyl-1H-inden-5-amine (TMDA), and a combination thereof.

(27) Preferably, ODA, pPDA, DMDB, TFMB, oTLD, MDA, MDCA, CHDA, BAFL, 9-(4-aminophenyl)-9-phenyl-9H-fluoren-3-amine, TMDA, or a mixture thereof is used.

(28) Preferably, a diamine selected from the following group is used:

(29) ##STR00025## ##STR00026##

(30) A solvent suitable for the preparation method is not particularly limited, and includes, but is not limited to, a non-protonic solvent, an ester, an ether alcohol, or an ether ester. For example, the non-protonic solvent may be selected from the group consisting of alkyl pyrrolidone such as N-methyl pyrrolidone (NMP) and N-ethyl pyrrolidone (NEP); dimethyl acetamide (DMAC); dimethyl formamide (DMF); dimethyl sulfoxide (DMSO); toluene; xylene; and a mixture thereof. An ester solvent useful in the present invention includes, but is not limited to, isobutyl acetate (IBAC), ethyl acetate (EAC), butyl acetate (BAC), ethyl formate, methyl acetate, ethoxyethyl acetate, ethoxypropyl acetate, ethyl isobutyrate, monomethyl ether propylene glycol acetate, amyl acetate, Gamma-butyrolactone (GBL), or a mixture thereof. An ether alcohol solvent useful in the present invention includes, but is not limited to, butyl glycol (BCS), ethylene glycol ethyl ether acetate (CAC), ethylene glycol monomethyl ether (ECS), propylene glycol monomethyl ether (PGME), propylene glycol methyl ether acetate (PMA), propylene glycol monomethyl ether propionate (PMP), butylene glycol ether (DBE), or a mixture thereof.

(31) It is known that the cyclization temperature required for preparing PI is generally higher than 350 C. However, the present invention provides SPI which has undergone ring closure in a solvent in advance and has a lower thermosetting temperature. Hence, the SPI of the invention can be solidified at a temperature as low as 270 C. Consequently, operating cost is reduced. The PI of the present invention has a lower thermosetting temperature and excellent thermal stability such as excellent ageing resistance and excellent pyrolysis resistance.

(32) The present invention also relates to a coating composition, which contains the aforementioned PI represented by Formula (I) and a hardening agent having 2 to 6 functional groups capable of reacting with COOH. After the PI represented by Formula (I) in the coating composition of the present invention reacts with the hardening agent having 2 to 6 functional groups capable of reacting with COOH, net-like cross-linking occurs. Therefore, a coating layer and film formed by the coating composition of the present invention possess excellent chemical resistance and thermal properties.

(33) In the coating composition of the present invention, based on the total weight of the composition, the content of the PI represented by Formula (I) is at least 1 wt %, and preferably, from 2 wt % to 20 wt %.

(34) The functional group capable of reacting with COOH is selected from the group consisting of an epoxy group, an isocyanate group (NCO), an oxazolyl group, a benzoxazinyl group,

(35) ##STR00027##
and a mixture thereof. Each R.sub.22 may be the same or different, and is independently H or a C.sub.1-C.sub.6 alkyl group. The selection of the functional group of the hardening agent generally depends on the coating composition to be obtained, for example, requirements of properties such as chemical resistance, low CTE, yellowing resistance, and good flexibility. According to a specific embodiment of the present invention, the functional group capable of reacting with COOH is an epoxy group, an oxazolyl group, or

(36) ##STR00028##
where R.sub.22 is as described above.

(37) Examples of the hardening agent useful in the present invention may be selected from 2,2-[9H-fluoren-9-ylidene-bis(4,1-phenyleneoxymethylene)]bis-oxirane, 2,2-(4,4-(propane-2,2-diyl)bis(4,1-phenylene))bis(oxy)bis(methylene)bis-oxirane, 1,3-diisocyanatobenzene, toluenediisocyanate, cyclohexanediisocyanate, trimethylcyclohexanediisocyanate, cyclohexanebis(methylisocyanate), isophoronediisocyanate, xylenediisocyanate, diphenyl methane diisocyanate, (1,3-bis(4,5-dihydrooxazol-2-yl)benzene), hexa(methylformaldehyde)melamine resin, hexa(ethylanilineformaldehyde)melamine resin, tetra(methylformaldehyde)diaminomelamine resin, tetra(methylformaldehyde)bi(butylformaldehyde)melamine resin, tetra(methylformaldehyde)bi(propylformaldehyde)melamine resin, 2,4,6-tri[bis(methoxymethyl)amino]-1,3,5-triazine, N2,N2,N4,N4,N6,N6-hexa(methoxymethyl)-1,3,5-triazine-2,4,6-triamine), or a combination thereof.

(38) According to the present invention, the content of the hardening agent is about 0.01 wt % to 50 wt %, and preferably, about 0.1 wt % to 10 wt %, based on the total weight of solid content of the coating composition.

(39) The coating composition of the present invention may further contain a solvent. The solvent useful in the present invention is not particularly limited, and may include a polar non-protonic solvent, an ester, an ether alcohol, an ether ester, or a mixture thereof. According to a specific embodiment of the present invention, the solvent is an ether alcohol or an ether ester. Examples of the solvent are solvents described in the aforementioned preparation method. The content of the solvent is in a range of 30 wt % to 99 wt %, preferably from 70 wt % to 95 wt %, based on the total weight of the composition.

(40) The coating composition of the present invention may contain any additional component contained in conventional coating compositions. Such additional components may be, for example, (but are not limited to), an inorganic particulate, a UV light absorber, a leveling agent, a defoamer, a stabilizing agent, and a catalyst required for the reaction of a hardening agent.

(41) The coating composition of the present invention has good storage stability and thermal stability. After the PI represented by Formula (I) reacts with the hardening agent in the coating composition of the present invention, cross-linking occurs. Consequently, a thin film formed by the coating composition of the present invention has excellent chemical resistance, a low CTE, and good flexibility, and does not crack easily. Therefore, the thin film can be used in thermosetting low-temperature hardening protective material for active/passive devices, optical materials, touch panels, copper foil substrates, soft flexible electronic materials, or integrated circuit elements. The thin film formed by the coating composition of the present invention has the characteristics of high transparency and resistance to yellowing. It is applicable to the manufacturing process for a thin glass film touch panel (G/F), whereby a glass base material can be replaced with a PI thin film substrate.

(42) The present invention further provides a flexible device, which includes a thin film formed by the coating composition described above. The flexible device may be a touch panel, an active/passive device, an optical material, a copper foil substrate, a soft flexible electronic material, or an integrated circuit element.

(43) The following examples are provided to further illustrate the present invention, but not intended to limit the scope of the present invention. Modifications and variations achievable by a person of ordinary skill in the art without departing from the spirit of the present invention shall fall within the scope of the present invention.

EXAMPLES

(44) In the following examples, abbreviations used are defined as follows: 6FDA: 4,4-hexafluoroisopropylidene-2,2-bis-(phthalic acid anhydride) S-BPDA: 3,3,4,4-Biphenyltetracarboxylic dianhydride CBDA: 1,2,3,4-cyclobutanetetracarboxylic dianhydride BPAF: 5,5-(9H-fluorene-9,9-diyl)diisobenzofuran-1,3-dione TFMB: 2,2-bis(trifluoromethyl)benzidine CHDA: 1,4-diaminocyclohexane BAFL: 4-(9-(4-aminophenyl)-9H-fluoren-9-yl)benzenamine TMDA: 1-(4-aminophenyl)-2,3-dihydro-1,3,3-trimethyl-1H-inden-5-amine MA: maleic anhydride PETA: phenylethynyl trimellitic anhydride FEP: 2,2-[9H-fluoren-9-ylidenebis(4,1-phenyleneoxymethylene)]bis-oxirane BPO: 1,3-bis(4,5-dihydrooxazol-2-yl)benzene MM1: N2,N2,N4,N4,N6,N6-hexa(methoxymethyl)-1,3,5-triazine-2,4,6-triamine DMAc: dimethyl acetamide NMP: N-methylpyrrolidone

SPI Synthesis Examples

Example A-1

Synthesis of a PI (PI-A1) Having a Tetracid End Group

(45) 97.7328 g (0.22 mol) 6FDA and 64.046 g (0.2 mol) TFMB were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 60 C. and stirred for 4 hours. After 4 hours of stirring, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 0.7208 g (0.04 mol) H.sub.2O was added. After that, the solution was heated to a temperature of 80 C., and stirred for 4 hours, to obtain PI-A1.

Example A-2

Synthesis of a PI (PI-A2) Having a Tetracid End Group

(46) 43.1442 g (0.22 mol) CBDA and 64.046 g (0.2 mol) TFMB were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 60 C., and stirred for 4 hours. After 4 hours of stirring, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 0.7208 g (0.04 mol) H.sub.2O was added. After that, the solution was heated to a temperature of 80 C., and stirred for 4 hours, to obtain PI-A2.

Example A-3

Synthesis of a PI (PI-A3) Having a Tetracid End Group

(47) 48.8664 g (0.11 mol) 6FDA and 64.046 g (0.2 mol) TFMB were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 60 C., and stirred for 4 hours. 32.3642 g (0.11 mol) S-BPDA was then added to the solution and the solution was stirred for 4 hours. After that, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 0.7208 g (0.04 mol) H.sub.2O was added. After that, the solution was heated to a temperature of 80 C., and stirred for 4 hours, to obtain PI-A3.

Example A-4

Synthesis of a PI (PI-A4) Having a Tetracid End Group

(48) 97.7328 g (0.22 mol) 6FDA and 22.8378 g (0.2 mol) CHDA were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 70 C., and stirred for 4 hours. After 4 hours of stirring, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 0.7208 g (0.04 mol) H.sub.2O was added. After that, the solution was heated to a temperature of 80 C., and stirred for 4 hours, to obtain PI-A4.

Example A-5

Synthesis of a PI (PI-A5) Having a Tetracid End Group

(49) 50.4260 g (0.11 mol) BPAF and 64.046 g (0.2 mol) TFMB were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 60 C., and stirred for 4 hours. 32.3642 g (0.11 mol) S-BPDA was then added to the solution, and the solution was stirred for 4 hours. After that, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 0.7208 g (0.04 mol) H.sub.2O was added to the solution. After that, the solution was heated to a temperature of 80 C., and stirred for 4 hours, to obtain PI-A5.

Example A-6

Synthesis of a PI (PI-A6) Having a Tetracid End Group

(50) 48.8664 g (0.11 mol) 6FDA, 32.026 g (0.1 mol) TFMB, and 34.8440 g (0.1 mol) BAFL were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 60 C., and stirred for 4 hours. 32.3642 g (0.11 mol) S-BPDA was then added to the solution, and the solution was stirred for 4 hours. After that, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 0.7208 g (0.04 mol) H.sub.2O was added to the solution. After that, the solution was heated to a temperature of 80 C., and stirred for 4 hours, to obtain PI-A6.

Example A-7

Synthesis of a PI (PI-A7) Having a Tetracid End Group

(51) 97.7328 g (0.22 mol) 6FDA, 32.026 g (0.1 mol) TFMB, and 26.6381 g (0.1 mol) TMDA were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 60 C., and stirred for 4 hours. 320 mL xylene was then added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 0.7208 g (0.04 mol) H.sub.2O was added to the solution. After that, the solution was heated to a temperature of 80 C., and stirred for 4 hours, to obtain PI-A7.

Comparative Example A-8

Synthesis of a PI (PI-M1) Having an MA End Group

(52) 88.848 g (0.2 mol) 6FDA and 70.4506 g (0.22 mol) TFMB were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 60 C., and stirred for 4 hours. After 4 hours of stirring, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 3.9224 g (0.04 mol) MA was added to the solution. After that, the solution was heated to a temperature of 80 C., and stirred for 8 hours, to obtain PI-M1.

Comparative Example A-9

Synthesis of a PI (PI-M2) Having an MA End Group

(53) 88.848 g (0.2 mol) 6FDA and 25.1216 g (0.22 mol) CHDA were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 70 C., and stirred for 4 hours. After 4 hours of stirring, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature and 3.9224 g (0.04 mol) MA was added to the solution. After that, the solution was heated to a temperature of 80 C., and stirred for 8 hours, to obtain PI-M2.

Comparative Example A-10

Synthesis of a PI (PI-P1) Having a PETA End Group

(54) 88.848 g (0.2 mol) 6FDA and 70.4506 g (0.22 mol) TFMB were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 60 C., and stirred for 4 hours. After 4 hours of stirring, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 11.0496 g (0.04 mol) PETA was added to the solution. After that, the solution was heated to a temperature of 80 C., and stirred for 8 hours, to obtain PI-P1.

Comparative Example A-11

Synthesis of a PI (PI-P2) Having a PETA End Group

(55) 88.848 g (0.2 mol) 6FDA and 25.1216 g (0.22 mol) CHDA were weighed and added to 640 mL NMP to form a solution, and the solution was stirred for 1 hour at room temperature, and then heated to a temperature of 50 C., and stirred for 4 hours. After 4 hours of stirring, 320 mL xylene was added to the solution, and the solution was dehydrated at a temperature of 180 C. by using a Dean-Stark apparatus. After dehydration was completed, the solution was cooled to room temperature, and 11.0496 g (0.04 mol) PETA was added to the solution. After that, the solution was heated to a temperature of 80 C., and stirred for 8 hours, to obtain PI-P2.

Coating Examples

Example R-1

(56) 100 g PI-A1 and 0.4 g FEP were mixed and stirred homogeneously to obtain a formulation RP-1.

Example R-2

(57) 100 g PI-A1 and 0.6 g BPO were mixed and stirred homogeneously to obtain a formulation RP-2.

Example R-3

(58) 100 g PI-A1 and 0.2 g MM1 were mixed and stirred homogeneously to obtain a formulation RP-3.

Example R-4

(59) 100 g PI-A2 and 0.4 g FEP were mixed and stirred homogeneously to obtain a formulation RP-4.

Example R-5

(60) 100 g PI-A4 and 0.4 g FEP were mixed and stirred homogeneously to obtain a formulation RP-5.

Example R-6

(61) 100 g PI-A4 and 0.6 g BPO were mixed and stirred homogeneously to obtain a formulation RP-6.

Example R-7

(62) 100 g PI-A4 and 0.2 g MM1 were mixed and stirred homogeneously to obtain a formulation RP-7.

Example R-8

(63) 100 g PI-A3 and 0.4 g FEP were mixed and stirred homogeneously to obtain a formulation RP-8.

Example R-9

(64) 100 g PI-A3 and 0.6 g BPO were mixed and stirred homogeneously to obtain a formulation RP-9.

Example R-10

(65) 100 g PI-A3 and 0.2 g MM1 were mixed and stirred v to obtain a formulation RP-10.

Example R-11

(66) 100 g PI-A5 and 0.4 g FEP were mixed and stirred homogeneously to obtain a formulation RP-11.

Example R-12

(67) 100 g PI-A6 and 0.4 g FEP were mixed and stirred homogeneously to obtain a formulation RP-12.

Example R-13

(68) 100 g PI-A7 and 0.4 g FEP were mixed and stirred homogeneously to obtain a formulation RP-13.

(69) In the above Examples R-1 to R-13, the formulations were diluted to a solid content of 10% with propylene glycol monomethyl ether (PGME).

(70) Physical Property Test:

(71) Next, the formulations of Example R-1 to R-13 and the formulations of the comparative examples A-8 to A-11 were coated on silica glass, respectively. The formed films were soft-baked at a temperature of 80 C., and once the films were not sticky, they were hard-baked at a high temperature (250 C.) for 1 hour. The thickness of the film was fixed to 10 m.

(72) Coloration Test:

(73) The films of the foregoing examples and comparative examples were baked again in air after being hard-baked, and a change of color before and after the baking was observed. The baking conditions were: baking at a temperature of 280 C. in air for 30 minutes. A film which did not experience color change was marked as good, and a film which turned yellow was marked as failed.

(74) Brittle Test:

(75) The hard-baked thin films were removed and folded in half at an angle of 180 degrees, and then checked to see if any fracture had occurred. A thin film without any fracture was marked as good, and a thin film having a fracture was marked as failed.

(76) Thermal Property Test:

(77) The CTE values of the thin films at a temperature from 20 C. to 200 C. were measured by using a thermal mechanical analyzer (TMA). A smaller CTE value indicates better thermal properties.

(78) Chemical Resistance Test:

(79) The hard-baked coating films of the foregoing examples and comparative examples were immersed in propylene glycol monomethyl ether acetate (PGMEA) for 4 minutes at a temperature of 25 C., and then checked to see if the surface of the coating film was abnormal. A film that produced white mist or dissolved was marked as failed, and a film without any abnormality was marked as good.

(80) The test results were recorded in Table 1.

(81) TABLE-US-00001 TABLE 1 CTE Chemical Coloration Brittle (ppm) Resistance Example R-1 good good 32 good Example R-2 good good 36 good Example R-3 good good 30 good Example R-4 good good 19 good Example R-5 good good 36 good Example R-6 good good 39 good Example R-7 good good 33 good Example R-8 good good 25 good Example R-9 good good 28 good Example R-10 good good 23 good Example R-11 good good 22 good Example R-12 good good 28 good Example R-13 good good 37 good Comparative good good 46 failed example A-8 Comparative good good 50 failed example A-9 Comparative failed failed 31 good example A-10 Comparative failed failed 34 good example A-11

(82) The main problems exhibited in Comparative Examples A-8 and A-9 are poor chemical resistance and excessively high CTE values. Although the coatings of Comparative Examples A-10 and A-11 have good chemical resistance, yellowing occurs, and the produced thin film may be brittle, thereby compromising its reliability.

(83) It can be known through comparison of Examples R-1 to R-3 and Comparative Examples A-8 and A-10 or through comparison of Examples R-5 to R-7 and Comparative Examples A-9 and A-11 that, when the same diamine and dianhydride are used, compared with a formulation using a double bond or a triple bond as an end group, the formulation using a tetracid group as an end group has the following advantages: 1) good yellowing resistance at high temperature, 2) good flexibility, 3) low CTE, and 4) good chemical resistance.