ROLLED (FeCoNiCrRn/Al)-2024Al COMPOSITE PANEL AND FABRICATION METHOD THEREOF

Abstract

Disclosed are a rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel and a preparation method therefor. The preparation method involves taking pure aluminum as a matrix, adding an FeCoNiCrR.sub.n medium-entropy alloy with a high strength and toughness as an reinforcing phase to prepare an FeCoNiCrR.sub.n/Al composite material, then laminating the FeCoNiCrR.sub.n/Al composite material with aluminum alloy 2024, and preparing the (FeCoNiCrR.sub.n/Al)-2024Al composite board by means of hot-rolling recombination, which solves the problem that high-strength aluminum matrix composites (AMCs) are prone to instantaneous breakability and low ductility, thereby improving the overall performance of the material. The present disclosure adopts microwave sintering (MWS) to fabricate a medium-entropy alloy-reinforced AMC, and adopts hot-roll bonding to fabricate the (FeCoNiCrR.sub.n/Al)-2024Al metal composite panel. The composite panel fabricated by the present disclosure has excellent comprehensive mechanical properties, and has high application values for promoting the application of modern lightweight and high-efficiency industrial materials in aerospace, new energy vehicles, and the like.

Claims

1. A fabrication method of a rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel, comprising: adding FeCoNiCrR.sub.n medium-entropy alloy particles with high strength and toughness as a reinforcing phase to a matrix of pure aluminum to obtain a FeCoNiCrR.sub.n/Al aluminum matrix composite, wherein the FeCoNiCrR.sub.n medium-entropy alloy reinforcing phase is added in an amount of 10% to 30% based on a total mass of the FeCoNiCrR.sub.n/Al aluminum matrix composite, the FeCoNiCrR.sub.n medium-entropy alloy particles each have a composition with an atomic ratio expression of FeCoNiCrR.sub.n, wherein R is any one from the group consisting of B, Y and C, and 0<n≤0.8; and subjecting a 2024Al aluminum alloy plate and the FeCoNiCrR.sub.n/Al aluminum matrix composite as raw materials to hot-roll bonding to obtain the rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel.

2. (canceled)

3. The fabrication method of the rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel according to claim 1, comprising the following steps: step (1) weighing and mixing high-purity metal powders Fe, Co, Ni, and Cr and an R powder as raw materials according to a designed ratio to obtain a resulting mixed powder, and subjecting the resulting mixed powder to ball-milling in a ball mill tank to fabricate a medium-entropy alloy powder through mechanical alloying, wherein during the ball-milling, evacuation is conducted and then argon is introduced for protection; step (2) vacuum-drying the obtained medium-entropy alloy powder, mixing particles of the medium-entropy alloy powder with the matrix of aluminum powder particles to obtain a resulting mixture, and subjecting the resulting mixture to low-energy ball-milling in a ball mill to obtain a mixed powder, wherein during the low-energy ball-milling, evacuation is conducted and then argon is introduced for protection; step (3) drying the mixed powder, and subjecting the mixed powder to ultrasonic dispersion with an ultrasonic machine until homogeneous, followed by molding through cold isostatic pressing to obtain a blocky solid composite; step (4) placing the blocky solid composite in a crucible, followed by sintering and solidifying through microwave sintering to obtain the medium-entropy alloy particle-reinforced aluminum matrix composite FeCoNiCrR.sub.n/Al; and step (5) cutting the medium-entropy alloy particle-reinforced aluminum matrix composite FeCoNiCrR.sub.n/Al into composite plates, placing one composite plate of the composite plates between two aluminum alloy plates, fixing the stacked plates through rivets, followed by hot-rolling.

4. The fabrication method of the rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel according to claim 3, wherein, in the step (1), the high-purity metal powders Fe, Co, Ni, and Cr and the R powder each has a purity of higher than or equal to 99.95 wt % and a particle size of less than or equal to 40 μm.

5. The fabrication method of the rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel according to claim 3, characterized in thatwherein experimental parameters of the ball-milling in the step (1) are as follows: a ball to material mass ratio is 8:1 to 15:1; the ball-milling comprises dry milling and wet milling; the dry milling is conducted, and then the wet milling is conducted; the wet milling is conducted with absolute ethanol as a process control agent in a mass fraction of 10% to 20%; the dry milling is conducted at a rotational speed of 100 r/min to 300 r/minfor 20 h to 40 h, and the wet milling is conducted at a rotational speed of 200 r/min to 400 r/minfor 10 h to 20 h; the powder obtained after the ball-milling has a particle size of 0.1 μm to 5 μm; and after the ball-milling is completed, the powder is vacuum-dried for 48 h to 72 h and then taken out; and parameters of the low-energy ball-milling in the step (2) are as follows: a ball to material mass ratio is 5:1 to 10:1; and wet milling is conductedfor 10 h to 30 h at a rotational speed of 120 r/min to 180 r/min, with absolute ethanol as a process control agent in a mass fraction of 15% to 25%.

6. The fabrication method of the rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel according to claim 3, characterized in thatwherein in the step (3), experimental parameters of the molding through the cold isostatic pressing are as follows: holding time: 2 min to 5 min, and molding pressure: 200 Mpa to 300 Mpa.

7. The fabrication method of the rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel according to claim 3, characterized in thatwherein in the step (4), experimental parameters of the microwave sintering are as follows: sintering temperature: 400° C. to 600° C., holding time: 30 min to 50 min, heating rate: 20° C./min to 60° C./min, and vacuum degree: less than 20 Pa.

8. The fabrication method of the rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel according to claim 7, characterized in thatwherein the step (5) comprises: cutting the medium-entropy alloy particle-reinforced aluminum matrix composite FeCoNiCrR.sub.n/Al made by the microwave sintering into the composite plates each with a diameter of 3 mm to 5 mm and a thickness of 2 mm to 3 mm, cutting an aluminum alloy into aluminum alloy plates each with a length×a width of 90 mm×70 mm and a thickness of 1 mm to 2 mm, subjecting the aluminum alloy plates to a vacuum preheating treatment in a microwave muffle furnace, followed by riveting, wherein parameters of the vacuum preheating treatment are as follows: preheating temperature: 400° C. to 600° C., and holding time: 1 h to 3 h.

9. The fabrication method of the rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel according to claim 8, characterized in thatwherein the composite plates and the aluminum alloy plates are each subjected to a surface cleaning treatment with an angle grinder, sandpaper, and acetone, and after the surface cleaning treatment is completed, a first one of the aluminum alloy plates, one of the FeCoNiCrR.sub.n/Al aluminum matrix composite plates, and a second one of the aluminum alloy plates are sequentially stacked and riveted to obtain a riveted composite panel; and parameters of the hot-rolling are as follows: the riveted composite panel is placed in a heating furnace at 300° C. to 500° C. for 5 min to 10 min and then subjected to roll bonding immediately, with a rolling reduction of 20% to 60%, a rolling speed controlled at 20 r/min to 40 r/min, and a rolling temperature of 100° C. to 150° C.

10. A rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel fabricated by the fabrication method according to claim 1.

11. A rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel fabricated by the fabrication method according to claim 3.

12. A rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel fabricated by the fabrication method according to claim 4.

13. A rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel fabricated by the fabrication method according to claim 5.

14. A rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel fabricated by the fabrication method according to claim 6.

15. A rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel fabricated by the fabrication method according to claim 7.

16. A rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel fabricated by the fabrication method according to claim 8.

17. A rolled (FeCoNiCrR.sub.n/Al)-2024Al composite panel fabricated by the fabrication method according to claim 9.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0025] FIG. 1 shows an optical metallographic structure of the composite panel fabricated by the method of the present disclosure.

[0026] FIG. 2 shows a scanning electron microscopy (SEM) image of the composite panel fabricated by the method of the present disclosure.

DESCRIPTION OF THE EMBODIMENTS

[0027] The present disclosure will be further described below in conjunction with the accompanying drawings and specific examples, but the protection scope of the present disclosure is not limited thereto.

EXAMPLE 1

[0028] (1) Fabrication of a medium-entropy alloy powder: A FeCoNiCrC.sub.0.2 medium-entropy alloy was adopted as a reinforcing phase. A corresponding mass of a powder of each element was calculated according to an atomic ratio of 1:1:1:1:0.2, and then powders were each weighed, mixed, and placed in a ball mill tank; evacuation was conducted and then argon was introduced; then high-energy ball-milling was conducted for mechanical alloying as follows: with a ball-to-material mass ratio of 12:1, dry milling was first conducted for 30 h at a rotational speed of 150 r/min, then absolute ethanol was added as a process control agent, and wet milling was conductedfor 12 h at a rotational speed of 300 r/min; and the resulting powder was dried for 60 h to obtain the high-entropy alloy powder.

[0029] (2) Fabrication of a composite powder: The high-entropy alloy powder particles and a pure aluminum powder were mixed, where the reinforcing phase high-entropy alloy powder particles had a mass fraction of 20%; and the resulting mixture was subjected to ball-milling with a ball mill under the protection of argon to obtain the composite powder, where the ball-milling was conducted as follows: in a ball-to-material mass ratio of 6:1, wet milling was conducted for 12 h at a rotational speed of 150 r/min, with absolute ethanol as a process control agent in a mass fraction of 20%.

[0030] (3) Cold isostatic pressing (CIP): The molding was conducted under the following experimental parameters: holding time: 2 min, and molding pressure: 250 Mpa.

[0031] (4) Sintering and molding: The blocky solid composite was placed in a crucible, and sintered by microwave sintering (MWS) to obtain a magnetic high-entropy alloy particle-reinforced AMC, where experimental parameters of the MWS were as follows: sintering temperature: 500° C., holding time: 40 min, heating rate: 30° C./min, and vacuum degree: less than 20 Pa.

[0032] (5) The FeCoNiCrC.sub.0.2/Al composite made by MWS was cut into plates each with a diameter of 4 mm and a thickness of 2.2 mm, an aluminum alloy was cut into plates each with length×width of 90 mm×70 mm and a thickness of 1.2 mm, and the aluminum alloy plate was subjected to a vacuum preheating treatment in a microwave muffle furnace at 500° C.for 2 h; the composite and aluminum alloy plates were each subjected to a surface cleaning treatment with an angle grinder, sandpaper, and acetone, and after the surface cleaning treatment was completed, the aluminum alloy, the FeCoNiCrC.sub.0.2/Al AMC, and the aluminum alloy were sequentially stacked and riveted; and a riveted composite panel was placed in a heating furnace at 450° C. for 8 min and then subjected to roll bonding immediately, with a rolling reduction of 36%, a rolling speed controlled at 30 r/min, and a rolling temperature of 120° C. FIG. 1 shows an optical metallographic structure of the composite panel fabricated in this example. The composite panel is fabricated by a roll bonding process in a very dry environment without any lubricant, resulting in a large friction force between a roll surface and a sample during rolling. A large amount of shear strain is caused by the uneven distribution of the 2024 layer due to rolling deformation. FIG. 2 shows an SEM image of the composite panel fabricated in this example, and it can be seen that the medium-entropy alloy particles are obviously slightly stretched along a rolling direction during the hot-roll bonding process.

[0033] The composite panel has a hardness of 90.4 HV, a tensile strength of 176 MPa, a yield strength of 120 MPa, and a strain of 19.7%.

EXAMPLE 2

[0034] (1) Fabrication of a medium-entropy alloy powder: A FeCoNiCrC.sub.0.5 medium-entropy alloy was adopted as a reinforcing phase. A corresponding mass of a powder of each element was calculated according to an atomic ratio of 1:1:1:1:0.5, and then powders were each weighed, mixed, and placed in a ball mill tank; evacuation was conducted and then argon was introduced; then high-energy ball-milling was conducted for mechanical alloying as follows: with a ball-to-material mass ratio of 12:1, dry milling was first conducted for 30 h at a rotational speed of 150 r/min, then absolute ethanol was added as a process control agent, and wet milling was conductedfor 12 h at a rotational speed of 300 r/min; and the resulting powder was dried for 60 h to obtain the high-entropy alloy powder.

[0035] (2) Fabrication of a composite powder: The high-entropy alloy powder particles and a pure aluminum powder were mixed, where the reinforcing phase high-entropy alloy powder particles had a mass fraction of 20%; and the resulting mixture was subjected to ball-milling with a ball mill under the protection of argon to obtain the composite powder, where the ball-milling was conducted as follows: in a ball-to-material mass ratio of 6:1, wet milling was conducted for 12 h at a rotational speed of 150 r/min, with absolute ethanol as a process control agent in a mass fraction of 20%.

[0036] (3) CIP: The molding was conducted under the following experimental parameters: holding time: 2 min, and molding pressure: 250 Mpa.

[0037] (4) Sintering and molding: The blocky solid composite was placed in a crucible, and sintered by MWS to obtain a magnetic high-entropy alloy particle-reinforced AMC, where experimental parameters of the MWS were as follows: sintering temperature: 500° C., holding time: 40 min, heating rate: 30° C./min, and vacuum degree: less than 20 Pa.

[0038] (5) The FeCoNiCrC.sub.0.5/Al composite made by MWS was cut into plates each with a diameter of 4 mm and a thickness of 2.2 mm, an aluminum alloy was cut into plates each with length×width of 90 mm×70 mm and a thickness of 1.2 mm, and the aluminum alloy plate was subjected to a vacuum preheating treatment in a microwave muffle furnace at 500° C.for 2 h; the composite and aluminum alloy plates were each subjected to a surface cleaning treatment with an angle grinder, sandpaper, and acetone, and after the surface cleaning treatment was completed, the aluminum alloy, the FeCoNiCrC.sub.0.5/Al AMC, and the aluminum alloy were sequentially stacked and riveted; and a riveted composite panel was placed in a heating furnace at 450° C. for 8 min and then subjected to roll bonding immediately, with a rolling reduction of 36%, a rolling speed controlled at 30 r/min, and a rolling temperature of 120° C.

[0039] The composite panel has a hardness of 99.8 HV, a tensile strength of 189 MPa, a yield strength of 135 MPa, and a strain of 22.1%.

EXAMPLE 3

[0040] (1) Fabrication of a medium-entropy alloy powder: A FeCoNiCrB.sub.0.5 medium-entropy alloy was adopted as a reinforcing phase. A corresponding mass of a powder of each element was calculated according to an atomic ratio of 1:1:1:1:0.5, and then powders were each weighed, mixed, and placed in a ball mill tank; evacuation was conducted and then argon was introduced; then high-energy ball-milling was conducted for mechanical alloying as follows: with a ball-to-material mass ratio of 12:1, dry milling was first conducted for 30 h at a rotational speed of 150 r/min, then absolute ethanol was added as a process control agent, and wet milling was conductedfor 12 h at a rotational speed of 300 r/min; and the resulting powder was dried for 60 h to obtain the high-entropy alloy powder.

[0041] (2) Fabrication of a composite powder: The high-entropy alloy powder particles and a pure aluminum powder were mixed, where the reinforcing phase high-entropy alloy powder particles had a mass fraction of 20%; and the resulting mixture was subjected to ball-milling with a ball mill under the protection of argon to obtain the composite powder, where the ball-milling was conducted as follows: in a ball-to-material mass ratio of 6:1, wet milling was conducted for 12 h at a rotational speed of 150 r/min, with absolute ethanol as a process control agent in a mass fraction of 20%.

[0042] (3) CIP: The molding was conducted under the following experimental parameters: holding time: 2 min, and molding pressure: 250 Mpa.

[0043] (4) Sintering and molding: The blocky solid composite was placed in a crucible, and sintered by MWS to obtain a magnetic high-entropy alloy particle-reinforced AMC, where experimental parameters of the MWS were as follows: sintering temperature: 500° C., holding time: 40 min, heating rate: 30° C./min, and vacuum degree: less than 20 Pa.

[0044] (5) The FeCoNiCrB.sub.0.5/Al composite made by MWS was cut into plates each with a diameter of 4 mm and a thickness of 2.2 mm, an aluminum alloy was cut into plates each with length×width of 90 mm×70 mm and a thickness of 1.2 mm, and the aluminum alloy plate was subjected to a vacuum preheating treatment in a microwave muffle furnace at 500° C. for 2 h; the composite and aluminum alloy plates were each subjected to a surface cleaning treatment with an angle grinder, sandpaper, and acetone, and after the surface cleaning treatment was completed, the aluminum alloy, the FeCoNiCrB.sub.0.5/Al AMC, and the aluminum alloy were sequentially stacked and riveted; and a riveted composite panel was placed in a heating furnace at 450° C. for 8 min and then subjected to roll bonding immediately, with a rolling reduction of 56.8%, a rolling speed controlled at 30 r/min, and a rolling temperature of 120° C.

[0045] The composite panel has a hardness of 124.8 HV, a tensile strength of 247 MPa, a yield strength of 180 MPa, and a strain of 30.8%.

EXAMPLE 4

[0046] (1) Fabrication of a medium-entropy alloy powder: A FeCoNiCrY.sub.0.5 medium-entropy alloy was adopted as a reinforcing phase. A corresponding mass of a powder of each element was calculated according to an atomic ratio of 1:1:1:1:0.5, and then powders were each weighed, mixed, and placed in a ball mill tank; evacuation was conducted and then argon was introduced; then high-energy ball-milling was conducted for mechanical alloying as follows: with a ball-to-material mass ratio of 12:1, dry milling was first conducted for 30 h at a rotational speed of 150 r/min, then absolute ethanol was added as a process control agent, and wet milling was conductedfor 12 h at a rotational speed of 300 r/min; and the resulting powder was dried for 60 h to obtain the high-entropy alloy powder.

[0047] (2) Fabrication of a composite powder: The high-entropy alloy powder particles and a pure aluminum powder were mixed, where the reinforcing phase high-entropy alloy powder particles had a mass fraction of 20%; and the resulting mixture was subjected to ball-milling with a ball mill under the protection of argon to obtain the composite powder, where the ball-milling was conducted as follows: in a ball-to-material mass ratio of 6:1, wet milling was conducted for 12 h at a rotational speed of 150 r/min, with absolute ethanol as a process control agent in a mass fraction of 20%.

[0048] (3) CIP: The molding was conducted under the following experimental parameters: holding time: 2 min, and molding pressure: 250 Mpa.

[0049] (4) Sintering and molding: The blocky solid composite was placed in a crucible, and sintered by MWS to obtain a magnetic high-entropy alloy particle-reinforced AMC, where experimental parameters of the MWS were as follows: sintering temperature: 500° C., holding time: 40 min, heating rate: 30° C./min, and vacuum degree: less than 20 Pa.

[0050] (5) The FeCoNiCrYo.5/Al composite made by MWS was cut into plates each with a diameter of 4 mm and a thickness of 2.2 mm, an aluminum alloy was cut into plates each with length×width of 90 mm×70 mm and a thickness of 1.2 mm, and the aluminum alloy plate was subjected to a vacuum preheating treatment in a microwave muffle furnace at 500° C.for 2 h; the composite and aluminum alloy plates were each subjected to a surface cleaning treatment with an angle grinder, sandpaper, and acetone, and after the surface cleaning treatment was completed, the aluminum alloy, the FeCoNiCrY.sub.0.5/Al AMC, and the aluminum alloy were sequentially stacked and riveted; and a riveted composite panel was placed in a heating furnace at 500° C. for 8 min and then subjected to roll bonding immediately, with a rolling reduction of 56.8%, a rolling speed controlled at 30 r/min, and a rolling temperature of 120° C.

[0051] The composite panel has a hardness of 135.2 HV, a tensile strength of 278 MPa, a yield strength of 198 MPa, and a strain of 37.8%.

[0052] The above examples are preferred implementations of the present disclosure, but the present disclosure is not limited to the above implementations. Any obvious improvement, substitution, or modification made by those skilled in the art without departing from the essence of the present disclosure should fall within the protection scope of the present disclosure.