MANUFACTURE OF PHOTO-CROSSLINKABLE BIODEGRADABLE TISSUE ADHESIVE USING COPOLYMER

Abstract

The present invention relates to the manufacture of a photo-crosslinkable biodegradable tissue adhesive using a multinetwork-forming copolymer, and provides a hyaluronic acid copolymer compound having excellent elongation, mechanical properties, and tissue adhesion. The compound fundamentally does not undergo phase separation, and enables the manufacture of a tissue adhesive with desired adhesive characteristics and physical characteristics.

Claims

1. A compound represented by Chemical Formula 1: ##STR00008## wherein, in Chemical Formula 1, m or n is an integer of 1 to 10,000, respectively, X.sub.1˜X.sub.8 each may be the same or different and is OH or a substituent of Chemical Formula 1-1, and ##STR00009## in Chemical Formula 1-1, p or q is an integer of 0 to 10, respectively.

2. The compound of claim 1, wherein, in Chemical Formula 1, m or n is an integer of 1 to 10,000, respectively, X.sub.1˜X.sub.4 include at least one substituent of Chemical Formula 1-1, and X.sub.5˜X.sub.8 include at least one substituent of Chemical Formula 1-1 which is different from the substituent of X.sub.1˜X.sub.4, and p or q is an integer of 0 to 10, respectively.

3. The compound of claim 1, wherein the compound represented by Chemical Formula 1 is a compound represented by Chemical Formula 2 or Chemical Formula 3: ##STR00010## wherein, in Chemical Formula 2 or Chemical Formula 3, m or n is an integer of 1 to 10,000.

4. The compound of claim 1, wherein the compound represented by Chemical Formula 1 is randomly copolymerized with m and n in a ratio of 9:1 to 7:3.

5. A hydrogel, comprising the compound of claim 1 and formed via a photo-crosslinking reaction.

6. A biodegradable tissue adhesive, comprising the compound of claim 1.

7. The biodegradable tissue adhesive of claim 6, wherein the compound forms a hydrogel by a light-induced crosslinking reaction.

Description

BRIEF DESCRIPTIONS OF THE DRAWINGS

[0020] FIG. 1 is a diagram showing changes in tensile strength according to a mixing ratio of HAMA and HAPA.

[0021] FIG. 2 is a diagram showing changes in mechanical properties according to a component ratio in a HAMA-co-HAPA copolymer and shows analysis results of (a) tensile strength, (b) tensile modulus, (c) toughness, and (d) elongation.

[0022] FIG. 3 shows results of an adhesion test for a HAMA-co-HAPA copolymer.

[0023] FIG. 4 is an NMR image of a HAMA-co-HAPA copolymer.

[0024] FIGS. 5 and 6 are NMR images of HAMA and HAPA, respectively.

MODES FOR CARRYING OUT INVENTION

[0025]

[0026] Hereinafter, the present invention will be described in detail.

[0027] The present inventors synthesized a hyaluronic acid copolymer compound copolymerized with hyaluronic acid compounds having different photo-crosslinking lengths with excellent properties such as elongation, mechanical strength, and tissue adhesion, enabling manufacture of tissue adhesives having desired adhesiveness and physical properties while not fundamentally undergoing phase separation. Therefore, the inventors completed the present invention by discovering that the hyaluronic acid copolymer compound may be usefully used as a medical adhesive, a medical hemostatic agent, a wound dressing agent, and an anti-adhesion agent that are applicable to various parts of the body.

[0028]

[0029] An example embodiment of the present disclosure provides a compound represented by Chemical Formula 1.

##STR00003##

[0030]

[0031] In Chemical Formula 1,

[0032] m or n is an integer of 1 to 10,000, respectively,

[0033] X.sub.1˜X.sub.8 may be the same or different and is OH or a substituent represented by Chemical Formula 1-1, and

##STR00004##

[0034]

[0035] in Chemical Formula 1-1, p or q is an integer of 0 to 10, respectively.

[0036] In this case, each of X.sub.1˜X.sub.4 and X.sub.5˜X.sub.8 essentially includes at least one substituent represented by Chemical Formula 1-1, the remainder may be a hydroxyl group, and the substitution rate of the substituent of Chemical Formula 1-1 may be 1 to 400%.

[0037] In particular, in Chemical Formula 1, m or n is an integer of 1 to 10000 respectively, X.sub.1˜X.sub.8 include at least one substituent of Chemical Formula 1-1, and X.sub.5˜X.sub.8 also include at least one substituent of Chemical Formula 1-1 which is different from the substituent of X.sub.1˜X.sub.4, and p or q is preferably an integer of 0 to 10, respectively.

[0038] As described above, the compound of Chemical Formula 1 has an ethylenically unsaturated group in a hyaluronic acid.

[0039] In addition, the compound represented by Chemical Formula 1 may be a compound represented by Chemical Formula 2 or Chemical Formula 3 below.

##STR00005##

[0040]

[0041] In Chemical Formula 2 or Chemical Formula 3,

[0042] m or n is an integer of 1 to 10,000, respectively.

[0043]

[0044] In this case, the compound represented by Chemical Formula 1 may be randomly copolymerized with m and n in a ratio of 9:1 to 7:3 and may preferably be formed by random copolymerization in a ratio of 7:3, but is not limited thereto.

[0045]

[0046] The compounds of Chemical Formulas 1 to 3 are hyaluronic acid copolymer compounds obtained by random copolymerization of hyaluronic acid compounds having different photo-crosslinking lengths, and problems such as phase separation and degradation in the commercial value of a product that may occur by simply mixing two or more polymers may be solved.

[0047] According to an example embodiment of the present disclosure, it was confirmed that the compound of Chemical Formula 2 manufactured by random copolymerization of HAMA and HAPA shows improved mechanical strength than a simple mixture of HAMA and HAPA and also exhibits excellent elongation and adhesion. In other words, according to the example embodiment of the present disclosure, a multi-network structure is formed inside a copolymer hydrogel, which increases flexibility as well as mechanical strength at the same time, whereas, generally in the case of a mixture, the strength of the mixture is difficult to be higher than that of a single material (HAMA) having high strength, showing only strength of an average value.

[0048]

[0049] In addition, an example embodiment of the present disclosure provides a hydrogel which includes the compounds represented by Chemical Formula 1 to Chemical Formula 3 and is formed via a photo-crosslinking reaction. The hydrogel may be used as a carrier for a physiologically active material or drug delivery, and tissue regeneration and implant material for filling, but is not limited thereto.

[0050]

[0051] In addition, an example embodiment of the present disclosure provides a biodegradable tissue adhesive including any one of the compounds represented by the Chemical Formula 1 to Chemical Formula 3.

[0052] In this case, the compound is a photo-crosslinkable biodegradable tissue adhesive capable of maintaining a high adhesion with tissues by forming a hydrogel through a light-induced crosslinking reaction. In this case, the photo-crosslinking reaction, as well as a UV-induced crosslinking reaction, enables the formation of a hydrogel by the photo-crosslinking reaction even under light of other wavelengths including visible light if using a photoinitiator having different absorption wavelength.

[0053]

[0054] In addition, the biodegradable tissue adhesive may be used as any one or more selected from the group consisting of a medical adhesive, a medical hemostatic agent, a wound dressing agent, an anti-adhesion agent, a cell culture support, a 3D printer bioink, and a bio-coating material, but is not limited thereto.

[0055]

[0056] Conventional photo-crosslinkable hyaluronic acid methacrylate (HAMA) has been applied in limited area due to lack of flexibility during photo-crosslinking. In order to improve the same, through adjustment of the mechanical properties of the hydrogel tissue adhesive by mixing hyaluronic acid butylacrylate (HABA) or hyaluronic acid pentacrylate (HAPA) with excellent elongation, the range of use may be broadened for a portion where movement occurs, thereby expecting the increase in the adhesion of tissues.

[0057] However, simply mixing two or more polymers may cause phase separation due to internal and external factors, which leads to degradation in the commercial value of a product.

[0058] In the present disclosure, in order to solve the issue, two or more photo-crosslinkable functional groups having different lengths were simultaneously introduced to hyaluronic acid to synthesize a new photo-crosslinkable copolymer with excellent mechanical properties while being flexible.

[0059] As a single component, the copolymer fundamentally has no risk of undergoing the phase separation. In addition, the newly synthesized photo-crosslinkable copolymer is flexible and has excellent mechanical strength while the physical properties of an adhesive are freely adjustable, thereby enabling development of medical adhesives to be used in various parts of the body.

[0060] In addition, the copolymer compound according to the example embodiment of the present disclosure may be applied as a medical hemostatic agent, a wound dressing agent, an anti-adhesion agent, a cell culture support, a 3D printer bioink, and a bio-coating material, but any application is possible if being usable as a bioadhesive without limitation.

[0061]

[0062] Hereinafter, the present disclosure will be described in more detail through examples. These examples are merely for describing the present disclosure in more detail, and it is apparent to a person of an ordinary skill in the art to which the present invention pertains that the scope of the present invention is not limited by the examples according to the gist of the present invention.

[0063]

[0064] <Synthesis Example 1>Synthesis of HAMA-co-HAPA copolymer

##STR00006##

[0065]

[0066] As in Scheme 1, 10 g (26 mmol) of hyaluronic acid was dissolved in 100 ml of purified water and cooled to 0-5° C. 36.4 mmol of methacrylic anhydride, 15.6 mmol of 4-pentenoic anhydride, and 100 ml of 3M NaOH solution were added thereto, followed by stirring for 2 days. The reaction product was purified by precipitation in ethanol and vacuum-dried to prepare a HAMA-HAPA random copolymer (hereinafter referred to as ‘HAMA-co-HAPA’).

[0067] Yield: 82%, .sup.1H-NMR (300 MHz, D.sub.2O):δ (ppm)=6.5, 6.1, 5.6 (CH=CH.sub.2), 4.5-4.3 (CH.sub.2), 3.8-3.0 (CH), 2.5-2.35 (CH.sub.2CH.sub.2), 1.8 (CH.sub.3), 1.7 (CH.sub.3). (See FIG. 4)

[0068]

[0069] In the synthesized HAMA-co-HAPA, the ratio of m and n was 7:3, and HAMA-co-HAPA copolymers whose ratio of methacrylic anhydride and 4-pentenoic anhydride to be added varies from 10:0 to 9:1 were prepared to be used as a sample for Examples below.

[0070]

[0071] <Comparative Example 1>Preparation of mixture of HAMA and HAPA

##STR00007##

[0072]

[0073] 10 g (26 mmol) of hyaluronic acid was dissolved in 100 ml of purified water and cooled to 0-5° C. Here, 104 mmol of methacrylic anhydride and 100 ml of 3M NaOH solution were added thereto, followed by stirring for 2 days. The reaction product was purified by to precipitation in ethanol and vacuum-dried to prepare hyaluronic acid methacrylate (HAMA) (see FIG. 5).

[0074] 10 g (26 mmol) of hyaluronic acid was dissolved in 100 ml of purified water and cooled to 0-5° C. 156 mmol of 4-pentenoic anhydride and 100 ml of 3M NaOH solution were added thereto, followed by stirring for 2 days. The reaction product was purified by precipitation in ethanol and vacuum-dried to prepare hyaluronic acid pentacrylate (HAPA) (see FIG. 6).

[0075]

[0076] Mixtures of HAMA and HAPA were prepared by simply mixing the prepared HAMA and HAPA in varied mixing ratios of 10:0, 9:1, 8:2, 7:3, 6:4 and 5:5, respectively.

[0077]

[0078] <Example 1>Analysis of mechanical strength and flexibility of HAMA-co-HAPA

[0079] Tensile strength, tensile modulus, toughness, and elongation of the copolymer HAMA-co-HAPA were measure by a tensile test, wherein the copolymer HAMA-co-HAPA was synthesized to have HAMA and HAPA in a varied ratio of 10:0, 9:1, and 7:3 by varying the ratio of methacrylic anhydride and 4-pentenoic anhydride added in <Synthesis Example 1>.

[0080] For the tensile test, a test piece molded in the dogbone shape according to the ASTM method using AND's Universal testing machine was measured at a speed of 1 mm/min.

[0081] For tensile strength, the maximum stress was measured in a strain-stress curve, and for tensile modulus, the slope between stress and strain rate was measured. Toughness was analyzed by integrating the total area up to a fracture point of a specimen, and elongation was analyzed by measuring the strain rate at the fracture point.

[0082] As a result, as shown in FIG. 1, it was confirmed that the tensile strength of the formed hydrogel decreased as the ratio of HAPA with a long cross-linking length increased in the mixture formed by simply mixing HAMA and HAPA.

[0083] However, in the preparation of the HAMA-co-HAPA copolymer according to <Synthesis Example 1>, the tensile strength and tensile modulus of the formed hydrogel increased as the ratio of HAPA with a long cross-linking length increased in the tensile test (see FIGS. 2a and 2b).

[0084] In addition, in the toughness test showing resistance to deformation, the HAMA-co-HAPA copolymer showed a result that was more than twice higher than that of the HAMA compound (FIG. 2c) and also showed a significantly improved result in the elongation that was higher than that of the conventional photo-crosslinkable single polymer (HAMA, MA:PA=10:0) (FIG. 2d).

[0085] Therefore, it was confirmed that by synthesizing the copolymer, rather than simply mixing HAMA and HAPA, the mechanical strength as well as the flexibility were improved.

[0086] <Example 2>Analysis of adhesive performance of HAMA-co-HAPA

[0087] In order to evaluate the adhesive performance of the HAMA-co-HAPA copolymer prepared in <Synthesis Example 1>, a Lap shear test of the copolymer HAMA-co-HAPA was performed, wherein the HAMA-co-HAPA was synthesized by varying the mixing ratio of methacrylic anhydride and 4-pentenoic anhydride to be added from 10:0 to 9:1.

[0088] After applying a HAMA-co-HAPA solution within artificial skin made of gelatin, UV was irradiated for 5 seconds, and the adhesion was evaluated by pulling both ends.

[0089] As a result, as shown in FIG. 3, the HAMA-co-HAPA copolymer showed higher adhesion than the HAMA single polymer, which is determined to be due to the improvement in mechanical properties.

[0090]

[0091] As described above, a specific part of the present invention has been described in detail, for a person of an ordinary skill in the art, it is apparent that these specific descriptions are merely preferred embodiments, and the scope of the present invention is not limited thereby. Accordingly, the substantial scope of the present invention will be defined by the appended claims and equivalents thereof