DENITRATION CATALYST AND DENITRATION METHOD USING THE CATALYST

Abstract

Disclosed is a FER-type zeolite having at least silicon, aluminum, and oxygen as skeletal atoms, where a molar ratio between silicon atoms to aluminum atoms is 2-100:1. In addition, when .sup.29Si solid nuclear magnetic resonance spectroscopy is used to analyze the zeolite, a peak area in the chemical shift range of −90 ppm to −110 ppm accounts for 25% or more of a peak area in the chemical shift range of −90 ppm to −125 ppm. Also disclosed are a preparation method for and an application of the FER zeolite.

Claims

1-15. (canceled)

16. A FER-type zeolite, comprising silicon, aluminum, and oxygen as skeletal atoms, wherein a molar ratio of silicon atoms to aluminum atoms is 2-100:1, and when the zeolite is analyzed by .sup.29Si solid NMR spectrum, a peak area in a chemical shift range from −90 to −110 ppm accounts for 25% or more of a peak area in a chemical shift range from −90 to −125 ppm.

17. The FER-type zeolite according to claim 16, wherein a mole number of the aluminum atoms accounts for 1% to 33% of a total mole number of non-oxygen atoms in the zeolite; and a cation outside a skeleton of the zeolite further comprises a hydrogen ion.

18. The FER-type zeolite according to claim 16, wherein the skeletal atoms of the zeolite further comprise an atom of one or more of other elements selected from the group consisting of titanium, zirconium, vanadium, chromium, manganese, iron, cobalt, zinc, gallium, germanium, arsenic, tin, and boron.

19. The FER-type zeolite according to claim 18, wherein a mole number of the atom of the other elements accounts for 40% or less of the total mole number of the non-oxygen atoms in the zeolite.

20. The FER-type zeolite according to claim 17, wherein the zeolite further comprises a cation of one or more selected from the group consisting of an alkali metal, an alkali earth metal, a rare earth metal, and a transition metal.

21. A bismuth-containing FER-type zeolite, comprising silicon, aluminum, and oxygen as skeletal atoms, wherein a molar ratio of silicon atoms to aluminum atoms is 2-100:1, and when the zeolite is analyzed by .sup.27Al solid NMR spectrum, a peak area in a chemical shift range from −50 to 40 ppm accounts for 28% or more of a peak area in a chemical shift range from −50 to 150 ppm.

22. The FER-type zeolite according to claim 21, wherein a content of bismuth is 0.05 mass % or more and 20 mass % or less; and a mole number of the silicon atoms accounts for 50% to 95% of a total mole number of non-oxygen atoms in the zeolite; and a cation outside a skeleton of the zeolite further comprises a hydrogen ion.

23. The FER-type zeolite according to claim 21, wherein the skeletal atoms of the zeolite further comprise an atom of one or more of other elements selected from the group consisting of titanium, zirconium, vanadium, chromium, manganese, iron, cobalt, zinc, gallium, germanium, arsenic, tin, and boron.

24. The FER-type zeolite according to claim 23, wherein a mole number of the atom of the other elements accounts for 40% or less of the total mole number of the non-oxygen atoms in the zeolite.

25. The FER-type zeolite according to claim 22, wherein the zeolite further comprises a cation of one or more selected from the group consisting of an alkali metal, an alkali earth metal, a rare earth metal, and a transition metal.

26. A method for preparing the FER-type zeolite according to claim 16, comprising: (a) mixing a mixture comprising a silicon source, an aluminum source, an organic template, and an optional inorganic base in water to provide an initial gel; (b) subjecting the initial gel to a hydrothermal synthesis reaction to obtain a reaction product; and (c) calcinating the reaction product and removing the organic template to obtain the FER-type zeolite, wherein if the initial gel comprises an alkali metal ion, an ion exchange is conducted between the zeolite obtained by calcinating the reaction product and removing the organic template in step (c) and an ammonium salt to remove a portion or all of the alkali metal ions comprised in the zeolite, and then calcination is conducted to provide the FER-type zeolite.

27. The method according to claim 22, wherein in the initial gel, a molar ratio of the silicon source, the aluminum source, the organic template R, the optional inorganic base AOH, and the water is 5-100 SiO.sub.2: 1 Al.sub.2O.sub.3: 5-50 R: 2-20 A.sub.2O: 200-2000 H.sub.2O; and the organic template is one or more selected from the group consisting of pyrrolidine, morpholine, N-methylmorpholine, piperidine, piperazine, N,N′-dimethylpiperazine, 1,4-diazabicyclo(2,2,2)octane, N-methylpiperidine, 3-methylpiperidine, quinuclidine, N-methylpyrrolidone, and hexamethyleneimine.

28. A method for preparing the FER-type zeolite according to claim 21, comprising: (a) mixing a mixture comprising a silicon source, an aluminum source, an organic template, and an optional inorganic base in water to obtain a hydrogel, and mixing the hydrogel and a solution of a bismuth source dissolved in an organic solvent to obtain an initial gel; (b) subjecting the initial gel to a hydrothermal synthesis reaction to obtain a reaction product; and (c) calcinating the reaction product and removing the organic template to obtain the FER-type zeolite, wherein if the initial gel comprises an alkali metal ion, an ion exchange is conducted between the zeolite obtained by calcinating the reaction product and removing the organic template in step (c) and an ammonium salt to remove a portion or all of the alkali metal ions comprised in the zeolite, and then calcination is conducted to obtain the FER-type zeolite.

29. The method according to claim 28, wherein in the initial gel, a molar ratio of the silicon source, the aluminum source, the bismuth source, the organic template R, the optional inorganic base AOH, and the water is 5-100 SiO.sub.2: 1 Al.sub.2O.sub.3: 0-0.5 Bi.sub.2O.sub.3: 5-50 R: 2-20 A.sub.2O: 200-2000 H.sub.2O; and the organic template is one or more selected from the group consisting of pyrrolidine, morpholine, N-methylmorpholine, piperidine, piperazine, N,N′-dimethylpiperazine, 1,4-diazabicyclo(2,2,2)octane, N-methylpiperidine, 3-methylpiperidine, quinuclidine, N-methylpyrrolidone, and hexamethyleneimine.

30. A method for preparing the FER-type zeolite according to claim 21, comprising: (a) mixing a mixture comprising a silicon source, an aluminum source, an organic template, and an optional inorganic base with water to obtain an initial gel; (b) subjecting the initial gel to a hydrothermal synthesis reaction to obtain a reaction product; (c) calcinating the reaction product and removing the organic template to obtain a zeolite; and (d) conducting an ion exchange or impregnation of the zeolite and a bismuth source in an organic solvent, and then conducting calcination to obtain the FER-type zeolite, wherein if the initial gel comprises an alkali metal ion, an ion exchange is conducted between the zeolite obtained by calcinating the reaction product and removing the organic template in step (c) and an ammonium salt to remove a portion or all of the alkali metal ions comprised in the zeolite, and then calcination is conducted to obtain the zeolite in step (c).

31. A catalytic reactor for purifying nitrogen oxides, comprising the FER-type zeolite according to claim 16 as a denitration catalyst.

32. A catalytic reactor for purifying nitrogen oxides, comprising the FER-type zeolite according to claim 21 as a denitration catalyst.

33. A denitration method, comprising conducting selective catalytic reduction denitration using the FER-type zeolite according to claim 16 as a denitration catalyst, and using an alcohol containing 6 carbon atoms or less as a reducing agent.

34. A denitration method, comprising conducting selective catalytic reduction denitration using the FER-type zeolite according to claim 21 as a denitration catalyst, and using an alcohol containing 6 carbon atoms or less as a reducing agent.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0035] Embodiments illustrated herein are further described below with reference to the accompanying drawings. However, the accompanying drawings are provided only to allow those skilled in the art to better understand the present disclosure, and are not intended to limit the scope of the present disclosure.

[0036] FIG. 1 is an XRD pattern of a molecular sieve A prepared according to an example of the present disclosure;

[0037] FIG. 2 is a .sup.29Si solid NMR spectrum of the molecular sieve A prepared according to an example of the present disclosure;

[0038] FIG. 3 is a .sup.29Si solid NMR spectrum of a molecular sieve B prepared according to an example of the present disclosure;

[0039] FIG. 4 is a .sup.29Si solid NMR spectrum of a molecular sieve C prepared according to an example of the present disclosure;

[0040] FIG. 5 is a .sup.29Si solid NMR spectrum of a molecular sieve D prepared according to an example of the present disclosure;

[0041] FIG. 6 is a .sup.29Si solid NMR spectrum of a molecular sieve E prepared according to a comparative example of the present disclosure;

[0042] FIG. 7 is a .sup.27Al solid NMR spectrum of a molecular sieve F prepared according to an example of the present disclosure;

[0043] FIG. 8 is a .sup.27Al solid NMR spectrum of a molecular sieve G prepared according to an example of the present disclosure;

[0044] FIG. 9 is a .sup.27Al solid NMR spectrum of a molecular sieve H prepared according to an example of the present disclosure;

[0045] FIG. 10 is a .sup.27Al solid NMR spectrum of a molecular sieve I prepared according to an example of the present disclosure;

[0046] FIG. 11 is a .sup.27Al solid NMR spectrum of a molecular sieve J prepared according to an example of the present disclosure;

[0047] FIG. 12 is a .sup.27Al solid NMR spectrum of a molecular sieve K prepared according to a comparative example of the present disclosure;

[0048] FIG. 13 is a .sup.27Al solid NMR spectrum of a molecular sieve L prepared according to a comparative example of the present disclosure; and

[0049] FIG. 14 is a .sup.27Al solid NMR spectrum of a molecular sieve M prepared according to a comparative example of the present disclosure.

DETAILED DESCRIPTION OF EMBODIMENTS

[0050] The inventive concepts of the present disclosure will be further illustrated bellow in conjunction with specific embodiments. However, the specific embodiments are listed for illustrative purposes only, and are not intended to limit the scope of the present disclosure. As will be appreciated by those skilled in the art, specific features in any one of the following embodiments may be used for any other embodiment, as long as they do not deviate from the inventive concepts described herein.

[0051] Zeolite

[0052] The zeolite as used herein refers to a FER-type zeolite specified by the International Zeolite Association (hereinafter referred to as IZA). The zeolite is generally a regular mesh structure formed by sharing and connecting oxygen atoms at vertexes of a skeletal tetrahedron (such as SiO.sub.4 tetrahedron, AlO.sub.4 tetrahedron, or PO.sub.4 tetrahedron, and an atom of an element other than oxygen is generally referred to as a non-oxygen atom or T atom). The structure of the FER-type zeolite may be determined by X-ray diffraction (XRD), which needs to at least detect the interplanar distances d (Å) shown in Table 1 below. That is, a zeolite has the interplanar distances shown in Table 1 below may be considered as a FER-type molecular sieve.

TABLE-US-00001 TABLE 1 Relative intensity d-distance d (Å) [100 × I/I(0)] 9.4 ± 0.2 100 7.0 ± 0.1 23 6.7 ± 0.1 21 5.7 ± 0.1 11 5.6 ± 0.1 11 4.9 ± 0.1 14 3.9 ± 0.1 52  3.7 ± 0.05 39  3.6 ± 0.05 33  3.5 ± 0.05 65  3.4 ± 0.05 62  3.3 ± 0.05 27 3.1 ± 0.1 27

[0053] When the FER-type zeolite described herein is analyzed by .sup.29Si solid NMR spectrum, its peak area in a chemical shift range from −90 to −110 ppm accounts for 25% or more of its peak area in a chemical shift range from −90 to −125 ppm. When the bismuth-containing FER-type zeolite described herein is analyzed by .sup.27Al solid NMR spectrum, its peak area in a chemical shift range from −50 to 40 ppm accounts for 28% or more of its peak area in a chemical shift range from −50 to 150 ppm. It is found through researches that the zeolite with the above features has a high catalytic activity for alcohol-SCR denitration and excellent nitrogen selectivity.

[0054] While it is not expected to be bound by any theory, it is believed that the bismuth-free zeolite described herein has excellent catalytic denitration performance, which may be attributed to the distribution of skeletal silicon atoms at specific sites in the FER-type zeolite. It is generally believed that a characteristic peak within the chemical shift range from −90 to −110 ppm in the .sup.29Si solid NMR spectrum reflects the information of skeletal silicon connected to skeletal Al. The higher the area ratio of absorption peaks in this range is, the more the acid active sites of the FER-type zeolite are, and the higher the alcohol-SCR catalytic activity of the FER zeolite is.

[0055] Further, for the bismuth-containing zeolite described herein, it is believed that its peak area in the chemical shift range from −50 to 40 ppm in the .sup.27Al solid NMR spectrum reflects the information of non-tetracoordinate aluminum in the zeolite. The higher the area ratio of absorption peak in this range is, the higher the content of non-skeletal aluminum in the zeolite is. For the bismuth-containing FER-type zeolite, the higher the content of non-skeletal aluminum is, the greater the interaction between bismuth and non-skeletal aluminum is, thereby resulting in excellent catalytic activity and catalytic selectivity.

[0056] Therefore, when the FER-type zeolite described herein is analyzed by .sup.29Si solid NMR spectrum, its peak area in the chemical shift range from −90 to −110 ppm accounts for 25% or more, e.g., 30% or more, 35% or more, 40% or more, or 45% or more, of its peak area in the chemical shift range from −90 to −125 ppm. When the bismuth-containing FER-type zeolite described herein is analyzed by .sup.27Al solid NMR spectrum, its peak area in the chemical shift range from −50 to 40 ppm accounts for 28% or more, e.g., 30% or more, 35% or more, or 40% or more, of its peak area in the chemical shift range from −50 to 150 ppm.

[0057] The zeolite as used herein refers to a zeolite at least comprising oxygen, aluminum, and silicon as the atoms constituting a skeleton structure, and a portion of skeletal atoms may be substituted with one or more elements other than the above three elements. A ratio (molar ratio) of silicon to aluminum constituting the zeolite is not particularly limited. In an embodiment, the molar ratio of silicon atoms to aluminum atoms is 2-100:1, e.g., 2:1, 5:1, 10:1, 15:1, 20:1, 30:1, 40:1, or 50:1. In another embodiment, the mole number of the aluminum atoms accounts for 1% to 33%, e.g., 2%, 3%, 4%, 5%, 10%, 15%, 20%, 25%, or 30%, of the total mole number of non-oxygen atoms in the zeolite. In still another embodiment, the mole number of the silicon atoms accounts for 50% to 95%, e.g., 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, or 95%, of the total mole number of the non-oxygen atoms in the zeolite.

[0058] In the zeolite herein, the site of bismuth in the zeolite and its specific chemical valence state are not particularly limited. Bismuth may exist in the skeleton of the zeolite, or may exist outside the skeleton of the zeolite. From the perspective of catalytic activity, bismuth preferably exists outside the skeleton. In an embodiment, a mass percent of bismuth is from 0.05% to 20%, e.g., from 0.1% to 10%, or may be any value within the above ranges, e.g., 0.5%, 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, or 10%. When the bismuth content is less than 0.05%, the low-temperature activity tends to decrease, and the catalytic activity is insufficient. When the bismuth content is more than 20%, an aggregated bismuth oxide usually tends to be generated, thereby reducing the catalytic performance.

[0059] In addition, the zeolite described herein may also comprise other elements than oxygen, aluminum, and silicon, such as phosphorus, titanium, zirconium, vanadium, chromium, manganese, iron, cobalt, zinc, gallium, germanium, arsenic, tin, boron and the like. The content of an atom of other elements accounts for 40% or less, preferably 30% or less, and more preferably 20% or less, of the total mole number of the non-oxygen atoms in the zeolite. In addition to comprising the components constituting a skeletal structure of the zeolite, the zeolite in the present disclosure may further comprise a cationic component outside the skeleton. The cation is not particularly limited, e.g., may be an alkali metal element such as H, Li, Na, or K, or an alkali earth metal element such as Mg, or Ca, or a rare earth metal element such as La or Ce, or a transition metal element such as Cu or Fe, and is preferably a hydrogen cation.

[0060] Synthesis of Zeolite

[0061] In the present disclosure, the zeolite is synthesized by hydrothermal synthesis, including preparing an initial gel (hereinafter also referred to as a hydrogel) from raw materials and water, and then conducting hydrothermal synthesis reaction on the initial gel in a reactor, thereby synthesizing the zeolite.

[0062] <Raw Materials>

[0063] The raw materials used in a manufacturing process of a FER-type molecular sieve described herein mainly include a silicon raw material, an aluminum raw material, an optional bismuth raw material, a nitrogen-containing alicyclic heterocyclic compound as a template (i.e., an organic template), an optional inorganic base, and water. In addition, a component having a promoting effect on crystallization, such as a seed crystal, may also be added.

[0064] The silicon raw material (also referred to as silicon source herein) may also be 1, or 2, or more of colloidal silicon dioxide, amorphous silicon dioxide, fumed silica, water glass (sodium silicate), trimethylethoxysilane, tetraethyl orthosilicate, aluminum silicate gel, and the like. The aluminum raw material (also referred to as an aluminum source herein) may also be 1, or 2, or more of aluminum sulfate, aluminum nitrate, sodium aluminate, aluminum oxide, aluminum hydroxide, boehmite, aluminum chloride, aluminum silicate gel, metal aluminum, and the like. The bismuth raw material (also referred to as a bismuth source herein) may also be 1, or 2, or more of bismuth nitrate, bismuth phosphate, bismuth sulfate, bismuth acetate, bismuth chloride, bismuth chlorate, and the like. These raw materials are not particularly limited, as long as they can be fully mixed with other ingredients.

[0065] The inorganic base may be 1, or 2, or more of an alkali metal hydroxide such as sodium hydroxide, potassium hydroxide, rubidium hydroxide, and cesium hydroxide, an aluminate mentioned in the above aluminum raw material, or an alkali component in the silicate or an alkali component in the silicate gel mentioned in the above silicon raw material. In the manufacturing process of the molecular sieve, at least one metal ion selected from the group consisting of lithium, sodium, potassium, rubidium, cesium, calcium, magnesium, strontium, and barium is preferably used as an alkali metal ion or an alkali earth metal ion for crystallization. By comprising these alkali metal ions, crystallization is easily conducted, and by-products (impurity crystals) can hardly be generated. It should be noted that the molar ratio of components in a gel is computed generally based on the corresponding oxide A.sub.2O of an inorganic base AOH.

[0066] The structure of the synthesized zeolite is related to the selected template. In an embodiment, the template may be a nitrogen-containing alicyclic heterocyclic compound, such as pyrrolidine, morpholine, N-methylmorpholine, piperidine, piperazine, N,N′-dimethylpiperazine, 1,4-diazabicyclo(2,2,2)octane, N-methylpiperidine, 3-methylpiperidine, quinuclidine, N-methylpyrrolidone, hexamethyleneimine and the like, preferably pyrrolidine, morpholine, hexamethyleneimine, or piperidine, and particularly preferably pyrrolidine.

[0067] <Preparation of an Aluminum Raw Material Solution>

[0068] The aluminum raw material solution is prepared by dissolving the above aluminum raw material in water. The aluminum raw material concentration of the aluminum raw material solution is preferably from 5% to 50% by weight, and particularly preferably from 10% to 40% by weight, in consideration of ease of gel preparation and production efficiency.

[0069] It should be noted that the aluminum raw material solution is substantially free of a silicon atom. Here, the “substantially free of” means that the silicon content in the aluminum raw material solution is 1% or less by weight, and preferably silicon is not comprised at all.

[0070] <Preparation of a Bismuth Raw Material Solution>

[0071] The bismuth raw material solution is prepared by dissolving the above bismuth raw material (also referred to as a bismuth source herein) in a liquid. Bismuth ions are easily hydrolyzed in an aqueous solution, thereby resulting in precipitation. Therefore, the bismuth raw material is dissolved in an organic solvent, such as ethylene glycol, glycerol, toluene, or other organic solvents. The concentration is preferably from 1% to 20% by weight, and particularly preferably from 2% to 10% by weight, in consideration of ease of gel preparation and production efficiency.

[0072] <Preparation of a Hydrogel>

[0073] An inorganic base is added to an aqueous solution to prepare an inorganic base solution. Then, the inorganic base solution, the silicon raw material solution, the aluminum raw material solution, and the organic template are fully mixed to prepare a gel-like mixture, which is a hydrogel for the next reaction. If it is intended to prepare a bismuth-containing zeolite, the bismuth raw material solution may be uniformly added to the above gel-like mixture to provide the hydrogel for the next reaction.

[0074] In the process of preparing the gel-like mixture, an addition speed of each raw material solution is not limited, and may be appropriately selected based on use conditions. When the bismuth raw material solution is added, the addition speed is not limited, either, and may be appropriately selected based on use conditions.

[0075] It should be noted that if the silicon raw material is a liquid, the silicon raw material may be used as long as the silicon raw material is formulated into an aqueous dispersion of silicon dioxide at about 5% to 60% by weight like a silicon dioxide gel. When a liquid of other silicon atom-containing raw materials is prepared, it is preferable to prepare an aqueous solution or aqueous dispersion in which the concentration of the silicon atom-containing raw material is 5% or more by weight, especially 10% or more by weight, and 60% or less by weight, especially 50% or less by weight.

[0076] Similar to the aluminum raw material solution, the liquid of the silicon raw material is substantially free of an aluminum atom. Here, the “substantially free of” means that the aluminum content in the liquid of the silicon-containing raw material is 1% or less by weight, and preferably aluminum is not comprised at all.

[0077] The water content of the hydrogel supplied to the hydrothermal synthesis reaction is 20% or more by weight, especially 30% or more by weight, and 80% or less by weight, especially 70% or less by weight, in consideration of ease of generation of molecular sieve crystals and production costs.

[0078] The hydrogel prepared as described above may be hydrothermally synthesized immediately after preparation, but in order to obtain a molecular sieve with high crystallinity, it is preferable to cure the hydrogel for a specific duration under a specified temperature condition. The curing temperature is generally 100° C. or lower, preferably 80° C. or lower, and more preferably 60° C. or lower; its lower limit is not particularly limited, but is generally 0° C. or higher, and is preferably 10° C. or higher. The curing temperature during the curing may be constant, or may be gradually changing. The curing duration is not particularly limited, but may be generally 2 hours or more, 3 hours or more, 5 hours or more, or 8 hours or more, and generally 30 days or less, 10 days or less, 4 days or less, or 2 days or less.

[0079] <Hydrothermal Synthesis>

[0080] The hydrothermal synthesis is carried out as follows: the hydrogel obtained from the above operations is put into a pressure-resistant container, and kept at a constant temperature, under an autogenous pressure, or under a gas pressure to a degree that does not hinder crystallization, with stirring conditions or conditions of rotating or swinging the container, so as to carry out the hydrothermal synthesis.

[0081] The reaction temperature during the hydrothermal synthesis is generally 90° C. or higher, preferably 120° C. or higher, and more preferably 150° C. or higher, and generally 300° C. or lower, preferably 250° C. or lower, and more preferably 220° C. or lower. The reaction duration is not particularly limited, but may be generally 2 hours or more, 6 hours or more, or 12 hours or more, and generally 30 days or less, 10 days or less, or 7 days or less. The reaction temperature in the reaction may be constant, or may be gradually changing.

[0082] After the above hydrothermal synthesis, the FER-type molecular sieve as the product is separated from the hydrothermal synthesis reaction mixture. The resulting FER-type molecular sieve (hereinafter referred to as a “template-containing FER-type molecular sieve”) comprises one or more of an organic template, bismuth, and other alkali metals in its pores. The method of separating the template-containing molecular sieve from the hydrothermal synthesis reaction mixture is not particularly limited, and a method, such as filtration, decantation, or direct drying, may generally be used.

[0083] <Impurity Removal, Calcination, and Ion Exchange>

[0084] In order to remove the organic template, alkali metal ion, and the like used in the manufacturing process, the FER-type molecular sieves comprising template or the like separated and recovered from the hydrothermal synthesis reaction mixture may be washed with water and dried (for example, dried at 80° C. to 100° C. for 1 hour to 12 hours), and then the organic template and the alkali metal ion may be subsequently removed.

[0085] The template and/or alkali metal may be removed by a liquid phase treatment using an acidic solution and a chemical solution containing a template-decomposing component, an ion exchange treatment using a resin or the like, a thermal decomposition treatment, or a combination of these treatments. Generally, the included organic matters (e.g., the template or the like) can be removed by calcination at a temperature from 300° C. to 1000° C. in an air, or an oxygen-containing non-active gas atmosphere, or a non-active gas atmosphere, or by extraction using an organic solvent such as an aqueous ethanol solution.

[0086] In consideration of manufacturing, the template and the like are preferably removed by calcination. In this case, the calcination temperature is preferably 400° C. or higher, more preferably 450° C. or higher, and most preferably 500° C. or higher, and preferably 900° C. or lower, more preferably 850° C. or lower, and most preferably 800° C. or lower. The non-active gas may be a gas such as nitrogen, or may be a gas in which a non-active component such as water vapor is added (for example, 5% to 10% water vapor).

[0087] In addition, the alkali metal may be partially exchanged to H and NH.sub.4 using the ion exchange capacity of the zeolite, the method of which may be a known technique. It may be treated with an ammonium salt, such as NH.sub.4NO.sub.3, NH.sub.4Cl, or (NH.sub.4).sub.2SO.sub.4, or an acid solution such as hydrochloric acid at room temperature to 100° C. and then washed with water. The NH.sub.4-type molecular sieve may be further converted to a H-type molecular sieve by calcination. Its calcination temperature is preferably 300° C. or higher, more preferably 350° C. or higher, and most preferably 400° C. or higher, and preferably 900° C. or lower, more preferably 800° C. or lower, and most preferably 600° C. or lower. The non-active gas may be a gas such as nitrogen, or may be a gas in which a non-active component such as water vapor is added (for example, 5% to 10% water vapor).

[0088] Similarly, ion exchange may be conducted between the hydrothermally synthesized zeolite or the zeolite obtained after removing the organic template and the bismuth source in the organic solvent using the ion exchange capacity of the zeolite. Then, the zeolite after the ion exchange may be dried (for example, dried at 80° C. to 100° C. for 1 hour to 12 hours), and calcined. Its calcination temperature is preferably 300° C. or higher, more preferably 350° C. or higher, and most preferably 400° C. or higher, and preferably 900° C. or lower, more preferably 800° C. or lower, and most preferably 600° C. or lower. The calcination duration may be from 1 hour to 6 hours, e.g., 2 hours, 3 hours, 4 hours, or 5 hours. The non-active gas may be a gas such as nitrogen, or may be a gas in which a non-active component such as water vapor is added (for example, 5% to 10% water vapor).

[0089] The calcinating device in the present disclosure is not particularly limited, and may be a common industrial kiln, such as a muffle furnace, a tunnel kiln, or a rotary kiln. In consideration of convenience of continuous production, the rotary kiln is preferably used.

[0090] Use Method of the Zeolite

[0091] The zeolite of the present disclosure may be used directly in the form of powders, or may be used in the form of a zeolite-containing mixture prepared by mixing the zeolite with a binder. The binder may be an inorganic binder such as silicon dioxide, aluminum oxide, or zirconium oxide, or may be an organic binder such as polysiloxane. Polysiloxane refers to an oligomer or polymer having a polysiloxane bond in the main chain, and also includes a substance formed by hydrolyzing a part of substituents of the polysiloxane bond main chain to a hydroxyl. The amount of the binder is not particularly limited, but may be from 1% to 20% by weight, and may be from 2% to 15% by weight in consideration of strength during shaping.

[0092] The zeolite or the zeolite-containing mixture in the present disclosure may also be used after granulation or shaping. The granulation or shaping method is not particularly limited, and various known methods may be used. Generally, the zeolite mixture is shaped and used as a shaped body. The shaped body may be of various shapes. For example, when the zeolite in the present disclosure is used as a catalyst for purifying nitrogen oxides in waste gas from a mobile object (e.g., a vehicle or a ship), the zeolite may be applied by coating or shaping to shape the zeolite into a honeycomb catalyst. The coating method generally includes mixing the zeolite with the inorganic binder such as silicon dioxide, aluminum oxide, or zirconium oxide to form a slurry, and coating the slurry on the surface of a honeycomb made of an inorganic material such as cordierite, then drying and calcination. The shaping method generally includes mixing the zeolite with the inorganic binder such as silicon dioxide or aluminum oxide, or an inorganic fiber such as an alumina fiber or a glass fiber, forming the mixture into a honeycomb by extrusion or compression, and then drying and calcination.

[0093] Nitrogen Oxides and Purification Thereof

[0094] When the zeolite of the present disclosure is used as a catalyst, the zeolite purifies the nitrogen oxides by contacting with waste gas comprising the nitrogen oxides. The nitrogen oxides to be purified herein includes nitrogen monoxide, nitrogen dioxide, nitrous oxide, and the like. The purifying the nitrogen oxides herein refers to reacting the nitrogen oxides on the catalyst for conversion into nitrogen, oxygen, and the like. In this case, the nitrogen oxides may be directly reacted, or may coexist with a reducing agent in the catalyst for the purpose of improving the purification efficiency. When the reducing agent is used, the zeolite described herein can contribute to the purification reaction of the nitrogen oxides. In the catalyst for industrial waste gas purification, an alcohol may be used as the reducing agent as long as the alcohol has the reducing capacity at a temperature of the reduction treatment of the industrial waste gas. The reducing agent is not particularly limited, but may be preferably an alcohol having 6 carbon atoms or less, such as methanol, ethanol, propanol, or isopropanol, and more preferably methanol or ethanol. When the zeolite of the present disclosure is used as the catalyst, the zeolite may purify nitrogen oxides comprised in various waste gases discharged from a diesel vehicle, a gasoline vehicle, a stationary power-generating ship, agricultural machinery, construction machinery, a two-wheeled or three-wheeled motor vehicle, various gasoline or diesel engines for aircrafts, a boiler, a gas turbine, and the like.

EXAMPLES

[0095] The following examples are provided to facilitate better understanding of the present disclosure, and are not intended to impose any limitation on the present disclosure. Unless otherwise particularly specified, the test methods used in the following examples are conventional methods; and unless otherwise particularly specified, the employed materials, reagents, etc. are commercially available.

[0096] Determination by X-Ray Powder Diffraction (XRD)

[0097] The X-ray diffraction instrument is Rigaku MiniFlex600 with a detection light source of Cu Kα at a tube voltage of 40 kV and at a tube current of 40 mA, in a detection angle range from 3 to 55° and at a scanning speed of 8°/min. A phase structure of a synthesized zeolite is determined by X-ray diffraction: the ground sample powders are added into a square hole on a glass plate, and then the glass plate is inserted into an axis position of a goniometer, with a probe rotating at a speed of 20/min under the irradiation of the Cu Kα light source.

[0098] Determination by Solid Nuclear Magnetic Resonance (NMR)

[0099] The solid nuclear magnetic resonance instrument is Bruker Avance III HD 400WB at a resonance frequency of 104.3 MHz for .sup.27Al NMR, at a repetition time of 0.1 s and at a rotation frequency of 10 kHz; and at a resonance frequency of 79.5 MHz for .sup.29Si NMR, at a repetition time of 6 s and at a rotation frequency of 5 kHz.

[0100] Evaluation of Catalyst Activity

[0101] After punch forming, the resulting zeolite is pulverized and granulated. The granulated zeolite (2 ml) is filled into an atmospheric circulating fixed-bed reaction tube. At 1000 ml/min (space velocity SV=30000/hour), a gas containing the composition of Table 2 is circulated on the catalyst layer whilst heating the catalyst layer. The nitrogen oxide removal activity of the catalyst is evaluated using the following equations based on outlet concentrations of NO, N.sub.2O, and NO.sub.2 at different temperatures, respectively.

(NO conversion rate)={(inlet concentration of NO)−(outlet concentration of NO)}/(inlet concentration of NO)

(N.sub.2 Selectivity)={(inlet concentration of NO)−(outlet concentration of NO)−(outlet concentration of NO.sub.2)−½ (outlet concentration of N.sub.2O)}/{(inlet concentration of NO)−(outlet concentration of NO)}

TABLE-US-00002 TABLE 2 NO concentration 1000 ppm Methanol concentration 2000 ppm Nitrogen concentration Balance Water vapor concentration 5.0% by volume Oxygen concentration 14.0% by volume Gas flow rate 1 L/min Catalyst amount 2 mL Volumetric space velocity 30000/hour

Example 1

[0102] 0.04 g of sodium hydroxide was dissolved in 15 g of water, and then 17 g of liquid sodium silicate (molar value: 3.3, referring to a molar ratio of SiO.sub.2 to Na.sub.2O here and below) and 3.7 g of pyrrolidine were added to prepare a mixed solution. 2.94 g of aluminum sulfate octadecahydrate was dissolved in 26.5 g of water, then the solution was added to the above mixed solution dropwise, and the mixture was fully stirred to provide a hydrogel with the composition of: 17 SiO.sub.2: 1 Al.sub.2O.sub.3: 11.9 C.sub.4H.sub.9N: 5.27 Na.sub.2O: 680 H.sub.2O. After stirring and curing at room temperature for 12 hours, the hydrothermal synthesis was conducted on the hydrogel in a high temperature-resistant and pressure-resistant container at 160° C. for 72 hours, and then the reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours to provide a template-containing molecular sieve A1. The molecular sieve A1 was calcined in air at 600° C. for 6 hours to remove an organic template to provide a molecular sieve A2.

[0103] 1.1 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve A2 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air at 500° C. for 2 hours to provide a molecular sieve A. Based on the XRD result of the molecular sieve A shown in FIG. 1, the molecular sieve A is a FER-type molecular sieve. As shown by the .sup.29Si solid NMR spectrum of the molecular sieve A in FIG. 2, its peak area in a chemical shift range from −90 to −110 ppm accounts for 45% of its peak area in a chemical shift range from −90 to −125 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve A is shown in Table 3.

Example 2

[0104] 0.04 g of sodium hydroxide was dissolved in 15 g of water, and then 17 g of liquid sodium silicate (molar value: 3.3) and 3.7 g of pyrrolidine were added to prepare a mixed solution. 1.77 g of aluminum sulfate octadecahydrate was dissolved in 27.1 g of water, then the solution was added to the above mixed solution dropwise, and the mixture was fully stirred to provide a hydrogel with the composition of: 28 SiO.sub.2: 1 Al.sub.2O.sub.3: 19.6 C.sub.4H.sub.9N: 8.68 Na.sub.2O: 1120 H.sub.2O. After stirring and curing at room temperature for 12 hours, the hydrothermal synthesis was conducted on the hydrogel in a high temperature-resistant and pressure-resistant container at 160° C. for 72 hours, and then the reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours to provide a template-containing molecular sieve B1. The molecular sieve B1 was calcined in air at 600° C. for 6 hours to remove an organic template to provide a molecular sieve B2.

[0105] 0.72 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve B2 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air at 500° C. for 2 hours to provide a molecular sieve B. The XRD result of the molecular sieve B showed that the molecular sieve B is a FER-type molecular sieve. As shown by the .sup.29Si solid NMR spectrum of the molecular sieve B in FIG. 3, its peak area in a chemical shift range from −90 to −110 ppm accounts for 36% of its peak area in a chemical shift range from −90 to −125 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve B is shown in Table 3.

Example 3

[0106] 0.04 g of sodium hydroxide was dissolved in 15 g of water, and then 17 g of liquid sodium silicate (molar value: 3.3) and 3.7 g of pyrrolidine were added to prepare a mixed solution. 1.665 g of aluminum sulfate octadecahydrate was dissolved in 28 g of water, then the solution was added to the above mixed solution dropwise, and the mixture was fully stirred to provide a hydrogel with the composition of: 30 SiO.sub.2: 1 Al.sub.2O.sub.3: 21 C.sub.4H.sub.9N: 9.3 Na.sub.2O: 1200 H.sub.2O. After stirring and curing at room temperature for 12 hours, the hydrothermal synthesis was conducted on the hydrogel in a high temperature-resistant and pressure-resistant container at 160° C. for 72 hours, and then the reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours to provide a template-containing molecular sieve C1. The molecular sieve C1 was calcined in air at 600° C. for 6 hours to remove an organic template to provide a molecular sieve C2.

[0107] 0.72 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve C2 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air at 500° C. for 2 hours to provide a molecular sieve C. The XRD result of the molecular sieve C showed that the molecular sieve C is a FER-type molecular sieve. As shown by the .sup.29Si solid NMR spectrum of the molecular sieve C in FIG. 4, its peak area in a chemical shift range from −90 to −110 ppm accounts for 32.2% of its peak area in a chemical shift range from −90 to −125 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve C is shown in Table 3.

Example 4

[0108] 0.04 g of sodium hydroxide was dissolved in 15 g of water, and then 17 g of liquid sodium silicate (molar value: 3.3) and 3.7 g of pyrrolidine were added to prepare a mixed solution. 1.249 g of aluminum sulfate octadecahydrate was dissolved in 28 g of water, then the solution was added to the above mixed solution dropwise, and the mixture was fully stirred to provide a hydrogel with the composition of: 40 SiO.sub.2: 1 Al.sub.2O.sub.3: 28 C.sub.4H.sub.9N: 12.4 Na.sub.2O: 1600 H.sub.2O. After stirring and curing at room temperature for 12 hours, the hydrothermal synthesis was conducted on the hydrogel in a high temperature-resistant and pressure-resistant container at 160° C. for 72 hours, and then the reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours to provide a template-containing molecular sieve D1. The molecular sieve D1 was calcined in air at 600° C. for 6 hours to remove an organic template to provide a molecular sieve D2.

[0109] 0.72 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve D2 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air at 500° C. for 2 hours to provide a molecular sieve D. The XRD result of the molecular sieve D showed that the molecular sieve D is a FER-type molecular sieve. As shown by the .sup.29Si solid NMR spectrum of the molecular sieve D in FIG. 5, its peak area in a chemical shift range from −90 to −110 ppm accounts for 33% of its peak area in a chemical shift range from −90 to −125 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve D is shown in Table 3.

Comparative Example 1

[0110] An NH.sub.4-type FER molecular sieve (HSZ-720NHA, molar ratio of SiO.sub.2/Al.sub.2O.sub.3=18) from TOSOH (Japan) was calcined in air at 600° C. for 12 hours to provide a molecular sieve E. As shown by the .sup.29Si solid NMR spectrum of the molecular sieve E in FIG. 6, its peak area in a chemical shift range from −90 to −110 ppm accounts for 23% of its peak area in a chemical shift range from −90 to −125 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve E is shown in Table 3.

Example 5

[0111] 0.3 g of bismuth nitrate pentahydrate was dissolved in 17.8 g of ethylene glycol to prepare a solution of bismuth nitrate in ethylene glycol. Then, the molecular sieve A prepared in Example 1 was added to the solution. The mixture was stirred at room temperature for 2 hours, and filtered. The recovered powder was dried at 80° C. for 12 hours, and then calcined in an air atmosphere comprising 10% water vapor at 600° C. for 5 hours to provide a molecular sieve F. The XRD result of the molecular sieve F showed that the molecular sieve F is a FER-type molecular sieve. As shown by the .sup.27Al solid NMR spectrum of the molecular sieve F in FIG. 7, its peak area in a chemical shift range from −50 to 40 ppm accounts for 31.5% of its peak area in a chemical shift range from −50 to 150 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve F is shown in Table 4.

Example 6

[0112] 0.04 g of sodium hydroxide was dissolved in 15 g of water, and then 17 g of liquid sodium silicate (molar value: 3.3) and 3.7 g of pyrrolidine were added to prepare a mixed solution. 2.85 g of aluminum sulfate octadecahydrate was dissolved in 26.5 g of water, then the solution was added to the above mixed solution dropwise, and the mixture was fully stirred to provide an initial hydrogel. Then, 0.12 g of bismuth nitrate pentahydrate was dissolved in 7.5 g of ethylene glycol, and the above solution of bismuth nitrate in ethylene glycol was added to the hydrogel dropwise to provide a final hydrogel with the composition of: 17.4 SiO.sub.2: 1 Al.sub.2O.sub.3: 0.03 Bi.sub.2O.sub.3: 12.18 C.sub.4H.sub.9N: 5.39 Na.sub.2O: 696 H.sub.2O. After stirring and curing at room temperature for 12 hours, the hydrothermal synthesis was conducted on the hydrogel in a high temperature-resistant and pressure-resistant container at 160° C. for 72 hours, and then the reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours to provide a template-containing molecular sieve G1. The molecular sieve G1 was calcined in air at 600° C. for 6 hours to remove an organic template to provide a molecular sieve G2.

[0113] 1.1 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve G2 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air at 600° C. for 5 hours to provide a molecular sieve G. The XRD result of the molecular sieve G showed that the molecular sieve G is a FER-type molecular sieve. As shown by the .sup.27Al solid NMR spectrum of the molecular sieve G in FIG. 8, its peak area in a chemical shift range from −50 to 40 ppm accounts for 39.8% of its peak area in a chemical shift range from −50 to 150 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve G is shown in Table 4.

Example 7

[0114] 1.1 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve G2 synthesized in Example 6 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air at 700° C. for 5 hours to provide a molecular sieve H. The XRD result of the molecular sieve H showed that the molecular sieve H is a FER-type molecular sieve. As shown by the .sup.27Al solid NMR spectrum of the molecular sieve H in FIG. 9, its peak area in a chemical shift range from −50 to 40 ppm accounts for 38.1% of its peak area in a chemical shift range from −50 to 150 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve H is shown in Table 4.

Example 8

[0115] 0.04 g of sodium hydroxide was dissolved in 15 g of water, and then 17 g of liquid sodium silicate (molar value: 3.3) and 3.7 g of pyrrolidine were added to prepare a mixed solution. 2.78 g of aluminum sulfate octadecahydrate was dissolved in 26.6 g of water, the solution was added to the above mixed solution dropwise, and the mixture was fully stirred to provide an initial hydrogel. Then, 0.2 g of bismuth nitrate pentahydrate was dissolved in 12.4 g of ethylene glycol, and the above solution of bismuth nitrate in ethylene glycol was added to the hydrogel dropwise to provide a final hydrogel with the composition of: 19.12 SiO.sub.2: 1 Al.sub.2O.sub.3: 0.05 Bi.sub.2O.sub.3: 13.38 C.sub.4H.sub.9N: 5.93 Na.sub.2O: 764.8 H.sub.2O. After stirring and curing at room temperature for 12 hours, the hydrothermal synthesis was conducted on the hydrogel in a high temperature-resistant and pressure-resistant container at 160° C. for 72 hours, and then the reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours to provide a template-containing molecular sieve I1. The molecular sieve I1 was calcined in air at 600° C. for 6 hours to remove an organic template to provide a molecular sieve 12.

[0116] 1.1 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve 12 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air comprising 10% water vapor at 600° C. for 5 hours to provide a molecular sieve I. The XRD result of the molecular sieve I showed that the molecular sieve I is a FER-type molecular sieve. As shown by the .sup.27Al solid NMR spectrum of the molecular sieve I in FIG. 10, its peak area in a chemical shift range from −50 to 40 ppm accounts for 32.9% of its peak area in a chemical shift range from −50 to 150 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve I is shown in Table 4

Example 9

[0117] 0.04 g of sodium hydroxide was dissolved in 15 g of water, and then 17 g of liquid sodium silicate (molar value: 3.3) and 3.7 g of pyrrolidine were added to prepare a mixed solution. 1.71 g of aluminum sulfate octadecahydrate was dissolved in 27.1 g of water, the solution was added to the above mixed solution dropwise, and the mixture was fully stirred to provide an initial hydrosol. Then, 0.2 g of bismuth nitrate pentahydrate was dissolved in 12.2 g of ethylene glycol, and the above solution of bismuth nitrate in ethylene glycol was added to the hydrogel dropwise to provide a final hydrogel with the composition of: 30.4 SiO.sub.2: 1 Al.sub.2O.sub.3: 0.08 Bi.sub.2O.sub.3: 21.28 C.sub.4H.sub.9N: 9.4 Na.sub.2O: 1216 H.sub.2O. After stirring and curing at room temperature for 12 hours, the hydrothermal synthesis was conducted on the hydrosol in a high temperature-resistant and pressure-resistant container at 160° C. for 72 hours, and the reaction mixture was cooled. The resulting powder was filtered, recovered, and dried at 100° C. for 2 hours to provide a template-containing molecular sieve J1. The molecular sieve J1 was calcined in air at 600° C. for 6 hours to remove an organic template to provide a molecular sieve J2.

[0118] 0.72 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve J2 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air comprising 10% water vapor at 600° C. for 5 hours to provide a molecular sieve J. The XRD result of the molecular sieve J showed that the molecular sieve J is a FER-type molecular sieve. As shown by the .sup.27Al solid NMR spectrum of the molecular sieve J in FIG. 11, its peak area in a chemical shift range from −50 to 40 ppm accounts for 32.2% of its peak area in a chemical shift range from −50 to 150 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve J is shown in Table 4.

Comparative Example 2

[0119] 0.3 g of bismuth nitrate pentahydrate was dissolved in 17.8 g of ethylene glycol to prepare a solution of bismuth nitrate in ethylene glycol. Then, the molecular sieve E prepared in Comparative Example 1 was added to the solution. The mixture was stirred at room temperature for 2 hours, and filtered. The recovered powder was dried at 80° C. for 12 hours, and then calcined in an air atmosphere at 500° C. for 4 hours to provide a molecular sieve K. The XRD result of the molecular sieve K showed that the molecular sieve K is a FER-type molecular sieve. As shown by the .sup.27Al solid NMR spectrum of the molecular sieve K in FIG. 12, its peak area in a chemical shift range from −50 to 40 ppm accounts for 26% of its peak area in a chemical shift range from −50 to 150 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve K is shown in Table 4.

Comparative Example 3

[0120] 1.1 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve 12 synthesized in Example 8 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air at 500° C. for 2 hours to provide a molecular sieve L. The XRD result of the molecular sieve L showed that the molecular sieve L is a FER-type molecular sieve. As shown by the .sup.27Al solid NMR spectrum of the molecular sieve L in FIG. 13, its peak area in a chemical shift range from −50 to 40 ppm accounts for 24.1% of its peak area in a chemical shift range from −50 to 150 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve L is shown in Table 4.

Comparative Example 4

[0121] 0.72 g of ammonium chloride was dissolved in 16 g of water, and then 4 g of the molecular sieve J2 synthesized in Example 9 was added to form a slurry. Ion exchange was conducted after the slurry was kept at 80° C. for reaction for 2 hours. The reaction mixture was cooled. The powder obtained from filtration and recovery was dried at 100° C. for 2 hours, and calcined in air at 500° C. for 2 hours to provide a molecular sieve M. The XRD result of the molecular sieve M showed that the molecular sieve M is a FER-type molecular sieve. As shown by the .sup.27Al solid NMR spectrum of the molecular sieve M in FIG. 14, its peak area in a chemical shift range from −50 to 40 ppm accounts for 17.9% of its peak area in a chemical shift range from −50 to 150 ppm. The result of the methanol-SCR catalytic activity of the molecular sieve M is shown in Table 4.

TABLE-US-00003 TABLE 3 .sup.29Si NMR Area ratio % of NO conversion rate/% N.sub.2 selectivity/% (−110) to (−90) ppm 250° C. 300° C. 350° C. 250° C. 300° C. 350° C. Example 1 Molecular sieve A 45 69.9 97.8 94.3 91.4 96.9 99.4 Example 2 Molecular sieve B 36 78.5 99.7 93.5 90.4 97.7 99.1 Example 3 Molecular sieve C 32.2 75.7 98.7 92.5 91.2 95.6 99.0 Example 4 Molecular sieve D 33 78.3 92.5 97.7 84.8 91.0 98.9 Comparative Molecular sieve E 23 24.1 37.4 54.7 94.2 94.7 97.6 Example 1

TABLE-US-00004 TABLE 4 .sup.27Al NMR Area ratio % of NO conversion rate/% N.sub.2 selectivity/% (−50) to (40) ppm 250° C. 300° C. 350° C. 250° C. 300° C. 350° C. Example 5 Molecular sieve F 59.3 74.1 84.2 71.5 92.3 96.4 98.7 Example 6 Molecular sieve G 39.8 85.6 96.2 82.9 87.9 95.7 99.0 Example 7 Molecular sieve H 38.1 66.0 87.3 74.6 90.9 96.6 98.5 Example 8 Molecular sieve I 32.9 74.4 90.1 72.5 91.0 97.7 100.0 Example 9 Molecular sieve J 32.2 78.2 89.6 64.5 92.3 97.9 98.6 Comparative Molecular sieve K 26 87.1 88.3 84.1 69.8 95.9 97.7 Example 2 Comparative Molecular sieve L 24.1 85.3 86.3 81.2 58.7 87.5 98.5 Example 3 Comparative Molecular sieve M 17.9 54.0 35.6 48.5 55.6 84.6 95.7 Example 4

[0122] As can be seen from the results of the above examples and comparative examples, the FER molecular sieve with the peak area in the chemical shift range from −90 to −110 ppm accounting for 25% or more of the peak area in the chemical shift range from −90 to −125 ppm in the .sup.29Si solid NMR spectrum shows better methanol-SCR catalytic activity, and also has good nitrogen selectivity. The bismuth-containing FER molecular sieve with the peak area in the chemical shift range from −50 to 40 ppm accounting for 28% or more of the peak area in the chemical shift range from −50 to 150 ppm in the .sup.27Al solid NMR spectrum shows better methanol-SCR catalytic activity, greatly reduced amount of N.sub.2O generated at 250° C., and significantly improved nitrogen selectivity.

[0123] While the embodiments herein are described by referring to specific examples, it should be understood that those skilled in the art will make any modifications and alterations without departing from the scope and spirit of the present disclosure.