Lignin Composites Comprising Activated Carbon For Odor Reduction

Abstract

The present invention relates to lignin compositions and methods for producing lignin composite materials. Composites of this invention substantially reduce or eliminate odor emanating from lignin that would otherwise be present.

Claims

1. A lignin composition comprising solid lignin and an odor reducing compound wherein the proportion of the odor reducing compound in the composition is in the range of 1% to 5% of the dry weight of the lignin composition.

2. The lignin composition of claim 1, wherein the compound is blended with the lignin so that the compound is thoroughly dispersed within the composition.

3. The lignin composition of claim 2, wherein the compound is activated carbon.

4. The lignin composition of claim 3, wherein the activated carbon is derived from natural non-petrochemical sources.

5. The lignin composition of claim 4, wherein the sources comprise at least one of: coconut husks, wood, peat and lignin.

6. The lignin composition of claim 3, wherein the proportion of activated carbon in the composition is in the range of 1% to 2% of the dry weight of the lignin composition.

7. The lignin composition of claim 3, wherein the moisture content of the lignin is less than 60% by weight and wherein said lignin is considered a solid.

8. The lignin composition of claim 3, wherein carbon in the activated carbon is derived from at least one of: coconut husks, wood, peat and lignin, and the carbon is activated by an oxidative process.

9. An article comprising the lignin composition of claim 3.

10. An adhesive binder comprising the lignin composition of claim 3.

11. A composite wood panel comprising the adhesive binder of claim 10, wherein the wood panel is one of: plywood, oriented strand board (OSB), laminated veneer lumber (LVL) and medium density fiberboard (MDF).

12. The composite wood panel of claim 11, wherein the adhesive binder further comprises phenol formaldehyde resin.

13. Use of the lignin composition of claim 3 in a foundry sand in a casting process to reduce odor produced by phenol resins used to bind the sand wherein a binder for the sand at least partially comprises the lignin composition.

14. A method of treating solid lignin, the method comprising: mixing the solid lignin with an odor reducing compound to form a mixture, wherein the compound comprises 1% to 5% of the total dry weight of the mixture.

15. The method of claim 14, wherein the compound is activated carbon.

16. The method of claim 15, wherein the activated carbon comprises 1% to 2% of the total dry weight of the mixture.

17. The method of claim 15, wherein said mixing takes place at ambient temperature.

18. The method of claim 15, wherein the moisture content of the lignin is in the range of up to about 60% by weight.

19. The method of claim 18, wherein the moisture content of the lignin is less than 60% by weight and wherein said lignin is considered a solid.

20. The method of claim 15, wherein the activated carbon has an iodine number in the range of about 400 to about 3000.

21. The method of claim 20, wherein the lignin is powdered lignin with an average particle size of 90 microns, the activated carbon comprises 2% by weight of the mixture, and the activated carbon has an iodine number of 600.

22. The method of claim 20, wherein the activated carbon has an iodine number in the range of about 400 to about 800.

23. A method of treating solid lignin to selectively reduce odor, the method comprising blending the lignin with activated carbon, to obtain a mixture comprising activated carbon in a range of 1% to 5% of total dry weight of the mixture, wherein increasing the proportion of activated carbon in the mixture within the range, reduces the odor of the mixture.

24. The method of claim 23, wherein raising the proportion of activated carbon from 0.5% to 2%, reduces the odor of the mixture by at least 30% on a standardized 3-point scale as determined by a panel of testers.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0015] In the figures which illustrate by way of example only, embodiments of the present invention,

[0016] FIG. 1 is a color photograph showing a sample of lignin;

[0017] FIG. 2 is a color photograph showing a sample of lignin mixed with activated carbon; and

[0018] FIG. 3 is a flowchart of a process exemplary of an embodiment of the present invention.

DESCRIPTION OF EMBODIMENTS

[0019] The most common form of lignin is as a loose, amorphous powder that is usually beige or light brown in color. FIG. 1 is a color photograph showing a typical sample of lignin.

[0020] The unpleasant odor of lignin powder can be significantly reduced or eliminated by addition of activated carbon which is also commonly known as activated charcoal. Activated carbon is widely used to adsorb odorous or colored substances from gases or liquids, but not usually from solids, such as solid particulate materials.

[0021] Mixing lignin powder with a small proportion of activated carbon at ambient temperatures provides substantial reduction or elimination of the odor. The odor-reducing effect is substantially immediate.

[0022] FIG. 2 is a color photograph showing a sample of lignin mixed with about 2% by weight activated carbon, based on the dry weight of lignin. The color of the material is just slightly darker or greyer than the untreated lignin sample shown in FIG. 1.

[0023] The treatment process is simple and does not require the application of heat, pressure, or the use of water, organic solvents or harsh reagents. It does not generate a waste-stream or by-products, nor does it involve costly, complex or time-consuming processing steps or expensive equipment.

[0024] It seems that the activated carbon reacts with, or physically adsorbs, malodorous species that are often present in lignin materials, providing a thermally stable interaction (e.g. a physical or chemical bond) with the odor-causing species, thus reducing or eliminating the emission of odor.

[0025] Sufficient amounts of activated carbon can be incorporated so that a desirable degree of odor reduction or odor elimination is achieved. The amount of activated carbon generally required for providing substantially odor-free lignin has been found to be in the range of about 1% to 5%, and preferably about 1% to 2% by weight of the dry weight of the lignin. Generally no additional improvement is observed when higher levels of activated carbon are utilized.

[0026] In some embodiments, activated carbon with iodine numbers in the range of 400 to 3000 or more can be used. In some embodiments activated carbon with iodine numbers in the range of 400 to 800 can be used. For example, in one embodiment, malodorous powdered lignin samples having an approximate average particle size of 90 microns were blended with 2% by weight of 600 iodine number activated carbon to yield a substantially odor-free material.

[0027] FIG. 3 depicts a flowchart that depicts schematically the process steps in one exemplary embodiment. As shown, the process S100 starts with obtaining lignin (S102), and adding an activated carbon (S104), if the activated carbon is 1% to 5% by weight of mixture the process continues to step S110. Otherwise the activated carbon content is adjusted (S108) and the process returns to step S104. The process then determines if the iodine numbers are in the range of 400 to 3000 (S110) and if so the lignin composite is produced in S112 and the process terminates. Otherwise the process returns to step S108 to further adjust the activated carbon so as to satisfy the requirements in steps S106 and step S110.

[0028] Laboratory samples of up to about 15 kg have been prepared with 1% and 2% by weight additions of activated carbon. In a qualitative assessment, two industry experts commented that these were the lowest odor lignin materials they had encountered in 40 years.

[0029] Mixing can be achieved by addition of activated carbon or similar odor reducing compound during the lignin manufacturing or extraction process, or during the packaging process. Activated carbon can be added quantitatively by blending in varying proportions from 1% to about 5%, based on the dry weight of lignin, using a prescribed method of dry addition from a conveyor.

[0030] For most end-use applications it is not necessary to separate the treated lignin from the activated carbon. In other words, for most end-use applications, a lignin composition comprising a small proportion of activated carbon can be used in substantially the same way as untreated lignin. If it is desired to separate the lignin from the activated carbon, post-treatment, the lignin can be dissolved in a suitable solvent, the solution separated from the activated carbon by filtration or another suitable method. The lignin can then be precipitated from solution or the solvent can be removed to yield lignin powder.

[0031] Higher weight percentages of activated carbon can be used, for example, if the lignin has a particularly strong and noxious odor and/or if the presence of the activated carbon does not have a detrimental effect in the intended end-use application of the lignin.

[0032] It is believed that activated carbons derived from a wide variety of sources (including, but not limited to, coconut husks, wood, peat and even lignin) and activated by various oxidative processes to yield polar functionalities on the carbon surface will be effective for use as described herein.

[0033] The above-described method for lignin odor reduction or elimination is a simple, inexpensive process that uses small proportions of activated carbon, which is readily available at reasonable cost.

[0034] The resulting lignin compositions have no odor or only a slight odor, and can therefore command a premium price relative to untreated lignin material. Odorless lignin is more likely to be accepted or adopted as substitute for fossil-based chemicals and for conversion into other value-added products.

[0035] For end-use applications involving heating of a material comprising lignin, using an odorless lignin material will be especially beneficial, as often the heating process intensifies the odor.

[0036] Lignin has many potential applications, and in many of these applications it can be used to replace some or all of the petrochemical-based aromatic compounds that are conventionally used. For example, it can be used as a substitute material in various phenol formaldehyde (PF) resin applications, such as: adhesive binders in plywood; binders in foundry sands; surfactants; polyols; polyurethanes; and in plastics in combination with polypropylene and polyethylene. Lignin compositions containing activated carbon may be used to replace some or all of the phenol formaldehyde resin used in these applications.

[0037] Thus, in some aspects, some embodiments of the present invention may involve incorporating lignin and activated carbon into an adhesive binder for wood panels such as plywood, oriented strand board (OSB), laminated veneer lumber (LVL), medium density fiberboard (MDF) and the like. The adhesive binder includes lignin and activated carbon and phenol formaldehyde resins.

[0038] Casting operations at foundries often produce odor-causing compounds, and odors generated by foundries in populated areas often result in complaints. The majority of the phenolic resins used to bind the sand generate odors during core making, core curing and/or metal casting processes.

[0039] In some aspects the present technology comprises using lignin-activated carbon mixtures as binders for foundry sands to fully or partially replace conventional binders and resins used in this application.

[0040] To summarize, the technology described herein relates to methods to reduce or eliminate odors in lignin material. The methods comprise mixing activated carbon with the lignin material in an amount effective to reduce or eliminate odors in the treated materials. It has been discovered that activated carbon is useful for reduction or elimination of odors in finished products that incorporate the treated lignin, such as resin-wood composites. The odor reduction mechanism involves odor elimination, rather than odor masking.

[0041] In an exemplary of embodiment of the present invention, a sample of lignin was treated with different amounts of activated carbon, and treated and untreated samples were subject to a qualitative assessment of their odor. Sample 1A was untreated (no activated carbon added). Sample 1B was mixed with 0.5% by weight of activated carbon. Sample 1C was mixed with 2% by weight of activated carbon. Each of the 3 samples was placed in an air-tight jar. A human panel of seven testers evaluated the odor of each of the three samples by removing the lid of the jars, smelling the sample and rating the odor on a standardized 3-point scale (1representing the least odor to 3 representing a strong, unpleasant odor). The results are shown in Table 1 below. Sample 1B exhibited a reduced odor compared to untreated Sample 1A, and Sample 1C which contained the highest amount of activated carbon exhibited a reduced odor compared to Samples 1 A and 1B. As may be noted in Table 1, raising the proportion of active carbon from 0.5% to 2%, reduces the odor of the mixture from about 1.6 to about 1.1 a this standardized scalea reduction of about 31%.

TABLE-US-00001 TABLE 1 Sample 1A Sample 1B Sample 1C (0% AC) (0.5% AC) (2% AC) Tester 1 3 1 2 Tester 2 2 1 1 Tester 3 2 1 I Tester 4 2 2 1 Tester 5 2 2 1 Tester 6 3 2 1 Tester 7 1 2 1 Average odor rating 2.1 1.6 1.1

[0042] While particular elements, embodiments and applications of the present invention have been shown and described, it will be understood, that the invention is not limited thereto since modifications can be made by those skilled in the art without departing from the scope of the present disclosure, particularly in light of the foregoing teachings.

[0043] The disclosures of all patents, patent applications, publications and referenced in this specification are hereby specifically incorporated by reference in their entirety to the same extent as if each such individual patent, patent application, publication and database entry were specifically and individually indicated to be incorporated by reference.

[0044] Although the invention has been described with reference to certain specific embodiments, various modifications thereof will be apparent to those skilled in the art. Such modifications as would be apparent to one skilled in the art are intended to be included within the scope of the following claims.