METHOD FOR PRODUCING A MOLDED PART AND MOLDED PART

Abstract

A method for producing a molded part, in particular a component of a sporting good, includes providing a mixture of a polymer melt and a foaming agent and injecting the mixture into a mold. The method includes solidifying at least a first portion of the molded part without foaming and at least a second portion of the molded part after foaming inside the mold, wherein the mixture includes a polymer having an average molecular mass corresponding to a viscosity number 130 ml/g, preferably 170 ml/g, more preferably 190 ml/g and most preferably 225 ml/g, wherein the viscosity number is determined via solution viscometry according to the ISO 307 standard.

Claims

1. A method for producing a molded part, in particular a component of a sporting good, comprising the following steps: providing a mixture of a polymer melt and a foaming agent; injecting the mixture into a mold; and solidifying at least a first portion of the molded part without foaming and at least a second portion of the molded part after foaming inside the mold, wherein the mixture comprises a polymer having an average molecular mass corresponding to a viscosity number 130 ml/g, preferably 170 ml/g, more preferably 190 ml/g and most preferably 225 ml/g, wherein the viscosity number is determined via solution viscometry according to the ISO 307 standard.

2. The method according to claim 1, wherein the mixture comprises a polyamide.

3. The method according to claim 1, wherein the mixture comprises a polyamide 12.

4. The method of claim 1, wherein the mixture is maintained in its non-foamed state during step b.

5. The method according to claim 1, wherein the foaming agent comprises a supercritical gas, in particular N.sub.2.

6. The method according to claim 1, wherein foaming is induced by reducing the pressure inside the mold.

7. The method according to claim 1, wherein foaming is induced by increasing the volume of at least a section of the mold.

8. The method according to claim 7, wherein the increase of the volume of the mold is between 0.1% and 500%, preferably between 1% and 150%, more preferably between 10% and 100% and most preferably between 25% and 75%.

9. The method according to claim 1, wherein the mold comprises at least a first and a second cavity, wherein the mixture at least partly solidifies inside the first cavity while the mixture at least partially undergoes foaming inside the second cavity.

10. The method according to claim 1, wherein the mixture prior to injection into the mold is maintained at a temperature between 150 C. and 300 C., preferably between 180 C. and 280 C. and most preferably between 240 C. and 260 C.

11. The method according to claim 1, wherein at least the section of the mold is maintained at a temperature between 20 C. and 120 C., preferably between 40 C. and 90 C. and most preferably between 50 C. and 70 C.

12. A molded part produced according to any of claim 1.

13. A sole plate for a shoe, in particular a soccer boot, wherein the sole plate comprises a molded part according to claim 12.

14. The sole plate according to claim 13, further comprising an essentially non-foamed forefoot section and a at least partially foamed midfoot section.

15. The sole plate according to claim 14, wherein the midfoot section has a greater thickness than the forefoot section.

16. The sole plate according to claim 13, wherein the midfoot section is adapted to provide a higher bending strength than the forefoot section.

17. A shoe sole comprising a sole plate according to claim 13.

18. A shoe, in particular a soccer boot, comprising a shoe sole according to claim 17.

19. A mold configured for producing a molded part according to claim 12, wherein the volume of a portion of the interior of the mold can be increased in order to achieve localized foaming of the mixture inside the portion.

20. A mold according to claim 19, comprising at least a first section and a at least a second section, wherein the volume of the portion can be increased by moving the second section.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0028] Aspects of the present invention are described in more detail in the following by reference to the accompanying figures. These figures show:

[0029] FIG. 1: a schematic illustrating an embodiment of the method according to the invention;

[0030] FIG. 2: a schematic illustrating another embodiment of the method according to the invention;

[0031] FIG. 3: a micrograph of a cross-section of an exemplary polymer part produced by a method according an embodiment of the invention;

[0032] FIG. 4: a schematic top view of an exemplary sole plate;

[0033] FIG. 5: a schematic cross-sectional view of an exemplary sole plate;

[0034] FIG. 6: photographs of a sole plate for a soccer boot in top (FIG. 6a) and bottom (FIG. 6b) view; and

[0035] FIG. 7: a schematic cross-sectional view of an exemplary mold comprising a movable section.

DETAILED DESCRIPTION

[0036] In the following, exemplary embodiments of the present invention of a method for producing a molded part are described in more detail with reference to specific microcellular foam molding processes, such as, for example, the so-called MUCELL injection molding process. However, it is to be understood that the present invention is not limited to such a specific process but could also be applied to other production methods of molded parts, for example foam molding processes that employ at least one chemical foaming agent or a combination of one or more physical and one or more chemical foaming agent.

[0037] Moreover, while specific feature combinations are described in the following with respect to certain embodiments of the present invention, it is to be understood that the disclosure is not limited to such embodiments. In other words, not all the described features have to be present for realizing the invention and the embodiments may be modified by combining certain features of one embodiment with one or more features of another embodiment.

[0038] FIG. 1 schematically shows a method 100 for producing a molded part 105 according to an embodiment of the present invention. First, a mixture 120, that may be pressurized, wherein the mixture 120 comprises a polymer melt comprising, for example a thermoplastic polyurethane (TPU) and/or a polyether block amide (PEBA) and/or a polyamide 12 (PA12) and/or any other polymer suited for injection molding and at least a physical (e.g. N2 or CO2) and/or at least a chemical foaming agent, is injected into a mold 110 while the mixture 120 may be maintained in its non-foamed or pre-foamed state. Prior to injection of the mixture 120 into the mold 110 and/or during injection and/or after injection, the temperature of the walls of the mold 110 or at least a section of the walls of the mold 110 may be adjusted such that a portion of the mixture 120 inside the mold 110 solidifies and forms at least a portion of solid, essentially non-foamed material 130.

[0039] According to the embodiment shown in FIG. 1, there are two portions of solid material 130 arranged on the outer surfaces of the molded part 105. However, it is to be understood that mold configurations are conceivable that allow to solidify without foaming only a single or more than two portions of the surface of the molded part 105 or even portions of the molded part 105 that are arranged inside the molded part 105.

[0040] The thickness of the portion or portions 130 can be controlled during the molding process 100 by adjusting the temperature of the walls of the mold 110 and/or by adjusting the injected volume of the polymer melt that is injected into the mold.

[0041] After a certain hold time or immediately during or after injection of the mixture 120 into the mold 110 foaming may be induced in the non-solidified portion 140 of the mixture 120. According to the present embodiment, foaming is induced by expanding the mixture 120 through a nozzle into the mold 110 thereby reducing the pressure of the mixture 120 below a critical value for foaming. The degree of foaming may be controlled by adjusting the injected volume of the mixture 120 that is injected into the mold 110. According to other embodiments of the invention, foaming may also be induced by pressure control and/or a spontaneous or controlled chemical reaction or any other means suitable to induce foaming inside a polymer melt or a mixture 120 of a polymer melt with a physical and/or chemical foaming agent.

[0042] In an exemplary embodiment of the above described method, the density of the polymer material inside the foamed core 140 can be reduced by as much as 45% as compared to a non-foamed sample of the same material with the same dimensions. If the polymer comprises, for example, a polyamide 12 with a non-foamed density of 1010 kg/m3 the density of the foamed core 140 of a molded part 105 may be only 566 kg/m3.

[0043] After foaming is complete or even still during foaming of at least a portion of the molded part 105, the molded part 105 may be cooled and removed from the mold 110. The resulting molded part 105 may exhibit a sandwich structure, wherein an at least partially foamed inner portion 140 is sandwiched by a bottom and a top portion 130 of non-foamed solid material. The molded part 105 according to this embodiment of the invention may be an outsole or sole plate or a component of an outsole or sole plate of a sports shoe or a soccer boot or any other conceivable sporting goods such as a ski, skateboard and many more.

[0044] FIG. 2 schematically shows a method 200 for producing a molded part 205 according to another embodiment of the present invention. First, a mixture 220, that may be pressurized, wherein the mixture 220 comprises a polymer melt comprising, for example a thermoplastic polyurethane (TPU) and/or a polyether block amide (PEBA) and/or a polyamide 12 (PA12) and/or any other polymer suited for injection molding and at least a physical (e.g. N2 or CO2) and/or at least a chemical foaming agent, is injected into a mold 210 while the mixture 220 may be maintained in its non-foamed or pre-foamed state. Prior to injection of the mixture 220 into the mold 210 and/or during injection and/or after injection the temperature of the walls of the mold 210 or at least a section of the walls of the mold 210 may be adjusted such that a portion of the mixture 220 inside the mold 210 solidifies and forms portions of solid, non-foamed material 230.

[0045] Again, after a certain hold time or immediately during or after injection of the mixture 220 into the mold 210 foaming may be induced in the portion 240 of the mixture 220 that is injected into the mold 210 and has not solidified. However, in this embodiment foaming may be induced by increasing the volume of the mold 210 by, for example, displacing backwards or laterally at a section of the walls of the mold 210. As mentioned before, the foaming may in addition also be induced by reducing the pressure of the injected mixture 220, by expanding the polymer melt through a nozzle into the mold and/or by a spontaneous or controlled chemical reaction or any other means suitable to induce foaming inside a polymer melt or a mixture 220 of a polymer melt with a physical and/or chemical foaming agent.

[0046] In the described embodiment of the invention involving an increase of the mold volume, the density of the polymer material inside the foamed core 240 can be reduced by as much as 70% as compared to a non-foamed sample of the same material with the same dimensions. For example, if the polymer comprises polyamide 12 with a non-foamed density of approx. 1010 kg/m3, the density of the foamed core 240 of a molded part may be approx. 355 kg/mb 3.

[0047] After foaming is complete or still during foaming of the remaining non-foamed portion 240 of the molded part 205, the molded part 205 may be cooled and removed from the mold 210. Again, the molded part 205 may exhibit a sandwich structure, wherein an at least partially foamed inner portion 240 is sandwiched between a bottom and top portion 230 of non-foamed solid material. If the molded part 205 has an essentially round shape, there may also be a single, continuous solid surface portion surrounding a foamed inner portion.

[0048] FIG. 3 depicts a micrograph of a cross section through a molded part 300 produced according to an embodiment of the present invention. In this example, the molded part 300 comprises a high-grade polyamide 12 exhibiting a viscosity number 190 ml/g. In this embodiment, the polyamide 12 has been mixed with supercritical N2 as foaming agent. After the mixture has been injected into a cuboid-shaped mold or any mold of a different geometry, a solid non-foamed top layer 310 and bottom layer 320 were formed, while foaming is taking place inside the core layer 330 of the molded part 300 simultaneously to increasing the mold volume. In this specific case, the mold volume was increased by approx. 150%.

[0049] The resulting molded part 300 shown in FIG. 3 has a thickness of approx. 1000 m and comprises a foamed inner core 330 with a thickness of a approx. 800 m. The inner core 330 is enclosed by a surface layer of non-foamed material comprising a top 310 and bottom layer 320, each having a thickness of approx. 100 m. The inner core 330 exhibits a homogeneous microcellular foam and is integrally and continuously connected with the top 310 and bottom layer 320. Thus, a sandwich structure is formed, as for example desired for midfoot sections of sporting shoes and other application in many other sporting goods. In this example, the density of the foamed inner core 330 is by approx. 70% lower than the density of a molded part of the same volume comprising non-foamed polyamide 12. According to the invention, the thickness of the top 310 and bottom layer 320 can be adjusted by adjusting the temperature of the sections of the mold that are in contact with the top and bottom portion of the mixture inside the mold and/or by adjusting the hold time inside the mold prior to inducing foaming.

[0050] FIG. 4 depicts a schematic top view of an exemplary sole plate 400 for a sports shoe such as a soccer boot according to an embodiment of the present invention. The sole plate 400 may comprise a plurality of sections as, for example, a forefoot section 410, a midfoot section 420 and a heal section 430. For some embodiments of the invention, as for example the sole plate of a soccer boot, it may be desirable that the forefoot section 410 is designed to be thin and flexible, whereas the midfoot section 420 is designed to be thicker than the forefoot section 410 and to exhibit a larger bending strength than the forefoot section 410. This may be achieved with the production method according to the present invention by just using a single mold and a single injection molding process.

[0051] To this end, the mold may be configured such that it comprises at least a forefoot section 410 and a midfoot section 420 which are in fluid communication with each other. During injection molding the polymer melt solidifies inside the forefoot section 410 while substantial foaming only takes place inside the midfoot section 420. In order to attain a high bending strength for the midfoot section 420 of the sole plate 400, the temperature of the midfoot section of the mold may be adjusted such that a solid, non-foamed surface layer forms adjacent to the foamed core region of the midfoot section 420.

[0052] FIG. 5 depicts a schematic cross-sectional view of a sole plate 500 for a soccer boot produced according to an embodiment of the present invention. The sole plate 500 may be constructed from a single material such as TPU or preferably a polyamide 12 with large molecular mass and/or melt strength. Of course, any other material that is suited for injection molding processes may be used as well. Alternatively, the sole plate 500 may be constructed from a plurality of different materials. The sole plate 500 may comprise a forefoot section 512, that may be designed to be thin and flexible. The forefoot section 512 may comprise integrated cleats 514 or other elements (not shown). The sole plate 500 may also comprise a midfoot section 520 that may comprise a non-foamed top 522 and non-foamed bottom layer 523 which may enclose an inner core 524 comprising a foamed material of lower density.

[0053] In the embodiment of FIG. 5, the midfoot section 540 continuously transitions via a transition zone 526 into the non-foamed forefoot section 512. A heal section 530 of the sole plate may be attached at the backside of the midfoot section 520. The heal section 530 may comprise a non-foamed material and/or foamed material of either the same type as the midfoot section 520 or a different one. The heal section 530 may be produced via the same production process as the midfoot section 520 and the forefoot section 512 or may be produced differently and may be attached to the midfoot section 520 via a suitable bonding method.

[0054] It is apparent, that the production method of the present invention allows to produce an integrated sole plate 500 with a single molding process comprising at least a forefoot section 512 and a midfoot section 520 that comprise a material of different density and different degree of foaming resulting in different mechanical properties for each of the sections, as it is desired for the sole plate of a soccer boot.

[0055] FIG. 6 shows two photographs of a sole plate for a soccer boot in top view (FIG. 6a) and bottom view (FIG. 6b), wherein the sole plate has been produced according to method of the present invention and exhibits a composition as schematically illustrated in FIG. 5 above.

[0056] In these photographs, it can clearly be observed that the midfoot section 620 and the heal section 630 comprise an essentially fully foamed polymer material, whereas the forefoot section 610 solidified without undergoing significant foaming. As explained above, this lightweight construction of a sole plate for a soccer boot was manufactured in a single injection molding process and resulted in a sole plate that exhibits exactly the desired mechanical and structural properties. The thin and essentially non-foamed forefoot section 610 exhibits a significantly higher flexibility than the stiff midfoot section 620 and heal section 630, exhibiting a high bending strength and superior stiffness to weight ratio as provided by the low-density microcellular foam structure.

[0057] FIG. 7 depicts a schematic cross-section of a novel mold design 700 that is configured to perform the production method for a molded part of a sporting good, such as a sole plate, according to the method provided by the present invention.

[0058] The mold 700 may comprise at least a first section 710 whose position may be fixed during production of the molded part and a second section 730 whose position relative to the first section 710 of the mold may be adjusted during production of the molded part.

[0059] This configuration allows to inject the polymer mixture 720 into the mold while the movable section 730 of the mold is in a first position. During injection or after the mold has been filled with the polymer mixture 720 the second section 730 of the mold may be moved to a second position and thereby the volume of a portion 740 of the interior of the mold 700 may be increased prior and/or during foaming.

[0060] As a result, the degree of foaming inside the portion of the molded part adjacent to the movable part 730 of the mold may be increased, potentially resulting in a higher bending strength and/or lower density of the portion of the molded part 740 adjacent to the movable part 730 of the mold.

[0061] In this way, the degree of foaming in the portion 740 of the molded part can be precisely controlled and therefore adjusted in response to changing requirements for various types of sporting goods such as sole plates for soccer boots, shoe soles for running boots and many other.