Bonding dissimilar materials with adhesive paste

Abstract

A rivetable adhesive for use in a joint between dissimilar materials, comprising a liquid epoxy resin, an expoxidized polysulfide, a flexibilizer, a solid epoxy CTBN adduct based upon bisphenol A, a phenoxy resin, an impact modifier including methacrylate-butadiene-styrene, a curing agent; and a blowing agent. The adhesive finds particular suitability for use in riveting aluminum panels to steel structures, such as for forming automotive vehicle roof structures.

Claims

1. A rivetable adhesive for use in a joint between dissimilar materials, comprising: a. a first liquid epoxy resin in an amount of about 15 to about 25 parts by weight per 100 parts by weight of the rivetable adhesive and a second liquid epoxy resin in amount of about 3 to about 20 parts by weight per 100 parts by weight of the rivetable adhesive; b. an expoxidized polysulfide; c. a flexibilizer; d. a solid epoxy CTBN adduct based upon bisphenol A in an amount not greater than about 15 parts by weight per 100 parts by weight of the rivetable adhesive; e. a phenoxy resin; f. an impact modifier including methacrylate-butadiene-styrene; g. a curing agent; and h. a blowing agent having a decomposition temperature of about 190 to about 220 C.; and wherein the adhesive exhibits a capillary viscosity of below 800 PaS for a shear rate of 100 sec1 or higher at a temperature of 70 or 90 C.; wherein a ratio of the amount by weight of the first liquid epoxy resin to the amount by weight of the second liquid epoxy resin is from about 1.6:1 to about 2.4:1; and wherein the decomposition temperature of the blowing agent facilitates robotic application such that the adhesive is heated to be applied above room temperature, but below a temperature at which it would be activated for curing, expanding or both curing and expanding.

2. The adhesive of claim 1, wherein the first liquid epoxy resin has an epoxide equivalent weight (g/eq) per ASTM D-1652-11e1 of about 182-192.

3. The adhesive of claim 1, wherein the impact modifier is a core shell impact modifier.

4. The adhesive of claim 1, further including an aromatic substituted urea curing accelerator.

5. The adhesive of claim 3, wherein the first liquid epoxy resin is a resin reaction product of epichlorohydrin and bisphenol A having an epoxide equivalent weight per ASTM D-1652-11e1 of about 182 to about 192.

6. The adhesive of claim 1, wherein the second liquid epoxy resin has an epoxide equivalent weight (g/eq) per ASTM D-1652-11e1 of about 320.

7. The adhesive of claim 6, wherein the second liquid epoxy resin is a reaction product of an epichlorohydrin and a polypropylene glycol.

8. The adhesive of claim 1, wherein the flexibilizer is present in an amount of about 1 to about 5 parts by weight of the adhesive.

9. The adhesive of claim 1, wherein the impact modifier is present in an amount of about 15 to about 25 parts by weight of the adhesive.

10. The adhesive of claim 9, wherein the solid epoxy CTBN adduct based upon bisphenol A is present in an amount of about 3 to about 15 parts by weight of the adhesive.

11. The adhesive of claim 1, wherein the phenoxy resin is present in an amount of about 15 to about 30 parts by weight of the adhesive.

12. A rivetable adhesive for use in a joint between dissimilar materials, comprising an admixture of: a. a first liquid epoxy resin including a liquid epoxy resin reaction product of epichlorohydrin and bisphenol A and having an epoxide equivalent weight per ASTM D-1652-11e1 of about 182 to about 192; b. about 10 to about 20 parts by weight of an epoxidized polysulfide; c. a second liquid epoxy resin including a liquid epoxy resin reaction product of an epichlorohydrin and a polypropylene glycol; d. about 1 to about 5 parts by weight of a flexibilizer; e. about 3 to about 15 parts by weight of a solid epoxy carboxyl terminated butadiene-acrylontirile (CTBN) adduct based upon bisphenol A; f. a blowing agent having a decomposition temperature of about 190 to about 220 C.; and wherein the ratio of the amount by weight of the first liquid epoxy resin to the amount by weight of the second liquid epoxy resin in the adhesive is from about 1.6:1 to about 2.4:1; wherein the adhesive exhibits a capillary viscosity of below 800 PaS for a shear rate of 100 sec1 or higher at a temperature of 70 or 90 C.; and wherein the decomposition temperature of the blowing agent facilitates robotic application such that the adhesive is heated to be applied above room temperature, but below a temperature at which it would be activated for curing, expanding or both curing and expanding.

13. The adhesive of claim 1, wherein the adhesive further includes about 0.5 to about 3 parts by weight of calcined kaolin.

14. A rivetable adhesive according to claim 1, wherein the adhesive exhibits a capillary viscosity in the range of about 100 to about 700 PaS for a shear rate of about 100 to about 1000 sec1 at a temperature of 70 or 90 C.

15. A rivetable adhesive according to claim 11, wherein the adhesive exhibits a capillary viscosity in the range of about 100 to about 400 PaS for a shear rate of about 400 to about 1000 sec1 at a temperature of 70 or 90 C.

16. A rivetable adhesive according to claim 12, wherein the adhesive exhibits a capillary viscosity in the range of about 100 to about 700 PaS for a shear rate of about 100 to about 1000 sec1 at a temperature of 70 or 90 C.

17. A rivetable adhesive according to claim 12, wherein the adhesive exhibits a capillary viscosity in the range of about 100 to about 400 PaS for a shear rate of about 400 to about 1000 sec1 at a temperature of 70 or 90 C.

18. The adhesive of claim 1, wherein the viscosity of the adhesive is adapted to allow for robotic application of the adhesive via a robotic arm and applicator.

19. The adhesive of claim 1, wherein an amount of the solid epoxy CTBN adduct based upon bisphenol A relative to an amount of the impact modifier including methacrylate-butadiene-styrene is about 5 parts by weight of the solid epoxy CTBN adduct based upon bisphenol A to about 20 parts by weight of the impact modifier including methacrylate-butadiene-styrene.

Description

DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 illustrates performance data in accordance with the present teachings.

DETAILED DESCRIPTION

(2) This application claims the benefit of the filing date of U.S. Provisional Application Ser. No. 61/816,394 filed Apr. 26, 2013, the contents of such application being hereby incorporated by reference for all purposes.

(3) The explanations and illustrations presented herein are intended to acquaint others skilled in the art with the teachings, its principles, and its practical application. Those skilled in the art may adapt and apply the teachings in its numerous forms, as may be best suited to the requirements of a particular use. Accordingly, the specific embodiments of the present teachings as set forth are not intended as being exhaustive or limiting of the teachings. The scope of the teachings should, therefore, be determined not with reference to the above description, but should instead be determined with reference to the appended claims, along with the full scope of equivalents to which such claims are entitled. The disclosures of all articles and references, including patent applications and publications, are incorporated by reference for all purposes. Other combinations are also possible as will be gleaned from the following claims, which are also hereby incorporated by reference into this written description.

(4) The teachings herein make advantageous use of an improved composition for bonding dissimilar materials, and particularly for bonding steel and aluminum. The teachings herein also make advantageous use of an improved method for bonding dissimilar materials, where the method employs robotic application of a paste adhesive between components (e.g., components made of dissimilar materials, such as steel and aluminum) to be joined. Use of a rivet for joining is also contemplated.

(5) The adhesive material may be a polymeric material that is activated to flow, seal, expand or any combination thereof. It may be a material that forms a foam (e.g., an acoustic foam or a structural foam). It may expand from its original volume to at least 50%, or even at least about 100% (e.g., in the range of about 80 to about 100%) or larger of its original volume.

(6) The adhesive material may be applied through a die associated with a robot arm. It may be applied at about room temperature. The adhesive may be heated to be applied above room temperature, but below a temperature at which it would be activated for curing, expanding or both.

(7) The adhesive material may be activated when subjected to heat during paint shop baking operations. In applications where the adhesive material is a heat activated, thermally expanding material, an important consideration involved with the selection and formulation of the material comprising the adhesive material is the temperature at which a material reaction or expansion, and possibly curing, will take place. For instance, in most applications, it is undesirable for the material to be reactive at room temperature or otherwise at the ambient temperature in a production line environment. More typically, the adhesive material becomes reactive at higher processing temperatures, such as those encountered in an automobile assembly plant, when the material is processed along with the automobile components at elevated temperatures or at higher applied energy levels, e.g., during paint or e-coat curing or baking steps. While temperatures encountered in an automobile assembly operation may be in the range of about 148.89 C. to 204.44 C. (about 300 F. to 400 F.), body and paint shop applications are commonly about 93.33 C. (about 200 F.) or slightly higher. Following activation of the adhesive material, the material will typically cure. Thus, it may be possible that the adhesive material may be heated, it may then expand, and may thereafter cure to form a resulting foamed material.

EXAMPLES

(8) Among the following examples are examples that illustrate materials that may are rivetable and exhibit attractive characteristics for the present application. The amounts shown are in preferred parts by weight. The teachings herein contemplate such amounts as well as amounts that are +/10%, 20%, 30%, 40% or even 50% of those shown. Examples 2 and 3 exhibit particularly attractive viscosity characteristics and exhibit good riveting characteristics. Example 1 is included by way of comparison. The compositions need not necessarily employ the specific commercial examples as set forth in the following Table 1. The compositions may employ the general components as described in the following Table 1. The composition may employ ingredients that exhibit the characteristics set forth in the following Table 1. Even if not explicitly specified, relative proportions of ingredients are within the scope of the teachings herein.

(9) TABLE-US-00001 TABLE 1 Example 1 Example 2 Example 3 Commercial (in parts (in parts (in parts Component Characteristic Example by weight) by weight) by weight) Liquid epoxy resin Epoxide DER 331 16.48 20.60 reaction product equivalent from The of epichlorohydrin weight (g/eq) Dow and bisphenol A per ASTM D- Chemical 1652 of about Company 182-192 Expoxidized Epoxide Thioplast 8.00 17.01 15.36 Polysulfide equivalent EPS-350 including epoxy weight (g/eq) from Akzo terminated per ASTM D- Nobel polymer with 1652-11e1 of diglycidyl ether of about 320 bisphenol A and chains with polysulfide Liquid epoxy resin Epoxide DER 732 6.70 6.70 12.92 reaction product equivalent from The of epichlorohydrin weight (g/eq) Dow and per ASTM D- Chemical polypropylene 1652-11e1 of Company glycol about 310-330 Flexibilizer Polyurethane DY 965 from 2.50 2.50 2.25 polyol Huntsman Solid epoxy resin Epoxide DER 662 11.00 reaction product equivalent from The of epichlorohydrin weight (g/eq) Dow and bisphenol A per ASTM D- Chemical 1652-11e1 of Company about 590-630 Solid epoxy Epoxide Araldite 16.00 5.00 4.52 carboxyl equivalent 1522 ES terminated weight (g/eq) butadiene- per ASTM D- acrylontirile 1652-11e1 of (CTBN) adduct about 1560- based upon 1820 bisphenol A Impact modifier of Paraloid 20.98 20.98 18.73 methacrylate- 2691A from butadiene-styrene the Dow (core-shell) Chemical company Phenoxy Resin TMEP-70 24.77 24.77 19.35 from Springfield Indus. Dicyandiamide Dycanex 2.85 3.40 3.40 curing agent 1400B from Air Products Aromatic Melting point Omicure U- 0.76 0.76 0.69 substituted urea of 220-230 C. 52M from curing accelerator Emerald (e.g., [4,4- Methylene bis (Phenyl Dimethyl Urea]) Calcined kaolin pH of about 6 Satintone W 5.49 1.47 1.25 and average from BASF particle size of about 1.3 m Blowing agent of Decomposition Celogen 0.90 Activated temperature of 754A from azodicarbonamide about 165 to Lion 180 C. Copolymer Blowing agent of Decomposition Celogen AZ- 0.90 0.90 azodicarbonamide temperature of 120 from about 190 to Lion 220 C. Copolymer Colorant Pigment 0.05 0.03 0.03

(10) FIG. 1 illustrates capillary viscosity data obtainable using the compositions of the teachings herein. As seen, the Example 1 formulation has a much higher viscosity than the viscosity of the Example 2 and 3 formulations. Two different test temperatures are used to cover the range of viscosities among the three materials. The reference test method for capillary viscosity employed is ASTM D 3835-08, pursuant to which the test parameters for the capillaries are as follows: diameter=1 mm, length=16 mm.

(11) As seen from FIG. 1, Examples 2 and 3 exhibit a capillary viscosity well below 1000 PaS at temperatures of 70 or 90 C. and a shear rate (sec1) of 200 or higher. For use herein, it is desirable for materials to exhibit a capillary viscosity in the range of about 100 to about 700 PaS for a shear rate (sec1) of about 100 to about 1000 at a temperature of 70 or 90 C. For example, it is desirable for materials to exhibit a capillary viscosity in the range of about 100 to about 700 PaS for a shear rate (sec1) of about 100 to about 1000 at a temperature of 70 or 90 C. Materials may exhibit a capillary viscosity in the range of about 100 to about 400 PaS for a shear rate (sec1) of about 400 to about 1000 at a temperature of 70 or 90 C. For certain applications it is desirable that the materials (at 70 or 90 C.) will have a capillary viscosity at shear rate (sec1) in the range of about 200 to about 400 that is less than 700 PaS, or even less than 500 PaS. The materials (at 70 or 90 C.) will typically exhibit a capillary viscosity of at least about 100 PaS at a shear rate (sec1) of about 200 to about 1000.

(12) As used herein, unless otherwise stated, the teachings envision that any member of a genus (list) may be excluded from the genus; and/or any member of a Markush grouping may be excluded from the grouping.

(13) Unless otherwise stated, any numerical values recited herein include all values from the lower value to the upper value in increments of one unit provided that there is a separation of at least 2 units between any lower value and any higher value. As an example, if it is stated that the amount of a component, a property, or a value of a process variable such as, for example, temperature, pressure, time and the like is, for example, from 1 to 90, preferably from 20 to 80, more preferably from 30 to 70, it is intended that intermediate range values such as (for example, 15 to 85, 22 to 68, 43 to 51, 30 to 32 etc.) are within the teachings of this specification. Likewise, individual intermediate values are also within the present teachings. For values which are less than one, one unit is considered to be 0.0001, 0.001, 0.01 or 0.1 as appropriate. These are only examples of what is specifically intended and all possible combinations of numerical values between the lowest value and the highest value enumerated are to be considered to be expressly stated in this application in a similar manner. As can be seen, the teaching of amounts expressed as parts by weight herein also contemplates the same ranges expressed in terms of percent by weight. Thus, an expression in the of a range in terms of x parts by weight of the resulting polymeric blend composition also contemplates a teaching of ranges of same recited amount of x in percent by weight of the resulting polymeric blend composition.

(14) Unless otherwise stated, all ranges include both endpoints and all numbers between the endpoints. The use of about or approximately in connection with a range applies to both ends of the range. Thus, about 20 to 30 is intended to cover about 20 to about 30, inclusive of at least the specified endpoints.

(15) The disclosures of all articles and references, including patent applications and publications, are incorporated by reference for ail purposes. The term consisting essentially of to describe a combination shall include the elements, ingredients, components or steps identified, and such other elements ingredients, components or steps that do not materially affect the basic and novel characteristics of the combination. The use of the terms comprising or including to describe combinations of elements, ingredients, components or steps herein also contemplates embodiments that consist of, or consist essentially of the elements, ingredients, components or steps.

(16) Plural elements, ingredients, components or steps can be provided by a single integrated element, ingredient, component or step. Alternatively, a single integrated element, ingredient, component or step might be divided into separate plural elements, ingredients, components or steps. The disclosure of a or one to describe an element, ingredient, component or step is not intended to foreclose additional elements, ingredients, components or steps.

(17) It is understood that the above description is intended to be illustrative and not restrictive. Many embodiments as well as many applications besides the examples provided will be apparent to those of skill in the art upon reading the above description. The scope of the invention should, therefore, be determined not with reference to the above description, but should instead be determined with reference to the appended claims, along with the full scope of equivalents to which such claims are entitled. The disclosures of all articles and references, including patent applications and publications, are incorporated by reference for all purposes. The omission in the following claims of any aspect of subject matter that is disclosed herein is not a disclaimer of such subject matter, nor should it be regarded that the inventors did not consider such subject matter to be part of the disclosed inventive subject matter.