SURFACE-STABILIZED AND PRELITHIATED ANODE ACTIVE MATERIALS FOR LITHIUM BATTERIES AND PRODUCTION METHOD

Abstract

A prelithiated and surface-stabilized anode active material for use in a lithium battery, comprising a protected anode active material particle comprising a surface-stabilizing layer embracing a core particle, wherein the surface-stabilizing layer comprises a lithium- or sodium-containing species chemically bonded to the core particle and the lithium- or sodium-containing species is selected from Li.sub.2CO.sub.3, Li.sub.2O, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, Li.sub.4B, Na.sub.4B, Na.sub.2CO.sub.3, Na.sub.2O, Na.sub.2C.sub.2O.sub.4, NaOH, NaiX, ROCO.sub.2Na, HCONa, RONa, (ROCO.sub.2Na).sub.2, (CH.sub.2OCO.sub.2Na).sub.2, Na.sub.2S, Na.sub.xSO.sub.y, or a combination thereof, wherein X=F, Cl, I, or Br, R=a hydrocarbon group, 0<x1, and 1y4; wherein the lithium- or sodium-containing species is preferably derived from an electrochemical decomposition reaction and the core particle is prelithiated to contain an amount of lithium from 1% to 100% of the maximum lithium content that can be included in the core particle of anode active material.

Claims

1. A prelithiated and surface-stabilized anode active material for use in a lithium battery, comprising a protected anode active material particle comprising a surface-stabilizing layer embracing a core particle, wherein said surface-stabilizing layer comprises a lithium- or sodium-containing species chemically bonded to said core particle and said lithium- or sodium-containing species is selected from Li.sub.2CO.sub.3, Li.sub.2C.sub.2O.sub.4, LiOH, LiCl, LiI, LiBr, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, Li.sub.4B, Na.sub.4B, Na.sub.2CO.sub.3, Na.sub.2O, Na.sub.2C.sub.2O.sub.4, NaOH, NaX, ROCO.sub.2Na, HCONa, RONa, (ROCO.sub.2Na).sub.2, (CH.sub.2OCO.sub.2Na).sub.2, Na.sub.2S, Na.sub.xSO.sub.y, a combination thereof, a combination thereof with Li.sub.2O or LiF, or a combination of Li.sub.2O and LiF, wherein X=F, Cl, I, or Br, R=a hydrocarbon group, 0<x1, 1y4; and wherein said core particle is prelithiated to contain an amount of lithium from 1% to 100% of a maximum lithium content contained in said core particle of anode active material.

2. The prelithiated and surface-stabilized anode active material of claim 1, wherein said core particle is selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo.sub.2O.sub.4; (f) particles of graphite and carbon; and (g) combinations thereof.

3. The prelithiated and surface-stabilized anode active material of claim 1, wherein said core particle is in a form of nano particle, nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn having a thickness or diameter from 0.5 nm to 100 nm.

4. The prelithiated and surface-stabilized anode active material of claim 1, wherein said core particle contains a sub-micron or micron particle having a dimension (diameter or thickness) from 100 nm to 30 m.

5. The prelithiated and surface-stabilized anode active material of claim 1, wherein said core particle is coated with a layer of carbon, graphene, electron-conducting polymer, ion-conducting polymer, or a combination thereof that is disposed between said core particle and said surface-stabilizing layer.

6. The prelithiated and surface-stabilized anode active material of claim 1, wherein said protected anode particle further contains a layer of carbon, graphene, electron-conducting polymer, ion-conducting polymer, or a combination thereof that is coated on said surface-stabilizing layer.

7. The prelithiated and surface-stabilized anode active material of claim 1, wherein said anode active material comprises silicon and said prelithiated core particle is selected from Li.sub.xSi, wherein numerical x is from 0.01 to 4.4.

8. A mass of anode active material powder comprising the prelithiated and surface-stabilized anode active material of claim 1.

9. An anode electrode comprising particles of the prelithiated and surface-stabilized anode active material of claim 1, an optional conductive additive, and an optional binder.

10. A lithium-ion or lithium metal battery containing the anode electrode of claim 9, a cathode electrode, and an electrolyte in ionic contact with the anode electrode and the cathode electrode.

11. A surface-stabilized anode active material for use in a lithium-ion battery, comprising a protected anode active material particle comprising a surface-stabilizing layer embracing a core particle, wherein said surface-stabilizing layer comprises a lithium- or sodium-containing species chemically bonded to said core particle and said lithium- or sodium-containing species is selected from Li.sub.2CO.sub.3, Li.sub.2O, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, Li.sub.4B, Na.sub.4B, Na.sub.2CO.sub.3, Na.sub.2O, Na.sub.2C.sub.2O.sub.4, NaOH, NaX, ROCO.sub.2Na, HCONa, RONa, (ROCO.sub.2Na).sub.2, (CH.sub.2OCO.sub.2Na).sub.2, Na.sub.2S, Na.sub.xSO.sub.y, or a combination thereof, wherein X=F, Cl, I, or Br, R=a hydrocarbon group, 0<x1, and 1y4.

12. The surface-stabilized anode active material of claim 11, wherein said core particle is selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo.sub.2O.sub.4; (f) particles of graphite and carbon; and (g) combinations thereof.

13. The surface-stabilized anode active material of claim 11, wherein said core particle is in a form of nano particle, nanowire, nanofiber, nanotube, nanosheet, nanobelt, nanoribbon, nanodisc, nanoplatelet, or nanohorn having a thickness or diameter from 0.5 nm to 100 nm.

14. The surface-stabilized anode active material of claim 11, wherein said core particle contains a sub-micron or micron particle having a dimension from 100 nm to 30 m.

15. The surface-stabilized anode active material of claim 11, wherein said core particle is coated with a layer of carbon, graphene, electron-conducting polymer, ion-conducting polymer, or a combination thereof that is disposed between said core particle and said surface-stabilizing layer.

16. The surface-stabilized anode active material of claim 11, wherein said protected anode particle further contains a layer of carbon, graphene, electron-conducting polymer, ion-conducting polymer, or a combination thereof that is coated on said surface-stabilizing layer.

17. A mass of anode active material powder comprising the surface-stabilized anode active material of claim 11.

18. An anode electrode comprising particles of the surface-stabilized anode active material of claim 11, an optional conductive additive, and an optional binder.

19. A lithium-ion or lithium metal battery containing the anode electrode of claim 18, a cathode electrode, and an electrolyte in ionic contact with the anode electrode and the cathode electrode.

20. The surface-stabilized anode active material of claim 1, wherein said core particle of anode active material comprises a doped semiconductor material selected from Si or Ge doped with n-type and/or p-type dopants.

21. The prelithiated and surface-stabilized anode active material of claim 1, further comprising a thin layer of a high-elasticity polymer encapsulating said surface stabilized and prelithiated core particles wherein said high-elasticity polymer has a fully recoverable tensile strain from 5% to 700%, a thickness from 0.5 nm to 2 m, and a lithium ion conductivity from 10.sup.7 S/cm to 510.sup.2 S/cm at room temperature.

22. The surface-stabilized anode active material of claim 11, further comprising a thin layer of a high-elasticity polymer encapsulating said surface stabilized core particles wherein said high-elasticity polymer has a fully recoverable tensile strain from 5% to 700%, a thickness from 0.5 nm to 2 m, and a lithium ion conductivity from 10.sup.7 S/cm to 510.sup.2 S/cm at room temperature.

23. A prelithiated and surface-stabilized anode active material for use in a lithium battery, comprising a protected anode active material particle comprising a surface-stabilizing layer embracing a core particle, wherein said surface-stabilizing layer comprises a lithium- or sodium-containing species chemically bonded to said core particle and said lithium- or sodium-containing species is selected from Li.sub.2CO.sub.3, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, Li.sub.2O, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, Li.sub.4B, Na.sub.4B, Na.sub.2CO.sub.3, Na.sub.2O, Na.sub.2C.sub.2O.sub.4, NaOH, NaX, ROCO.sub.2Na, HCONa, RONa, (ROCO.sub.2Na).sub.2, (CH.sub.2OCO.sub.2Na).sub.2, Na.sub.2S, Na.sub.xSO.sub.y, or a combination thereof, wherein X=F, Cl, I, or Br, R=a hydrocarbon group, 0<x1, 1y4; and wherein said core particle is prelithiated to contain an amount of lithium from 1% to 100% of a maximum lithium content contained in said core particle of anode active material and said core particle is selected from the group consisting of: (a) germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo.sub.2O.sub.4; (f) particles of graphite and carbon; (g) combinations thereof; and (h) combinations thereof with Si.

24. A method of producing the prelithiated and surface-stabilized anode active material of claim 1, said method comprising: (a) providing a plurality of particles of an anode active material; (b) prelithiating said particles to form prelithiated particles that each contains an amount of lithium from 1% to 100% of a maximum lithium content contained in said anode active material; and (c) depositing a surface-stabilizing layer to embrace at least one of said prelithiated particles, wherein said surface-stabilizing layer comprises a lithium- or sodium-containing species chemically bonded to said at least one prelithiated particle and wherein said lithium- or sodium-containing species is selected from Li.sub.2CO.sub.3, Li.sub.2O, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, Li.sub.4B, Na.sub.4B, Na.sub.2CO.sub.3, Na.sub.2O, Na.sub.2C.sub.2O.sub.4, NaOH, NaX, ROCO.sub.2Na, HCONa, RONa, (ROCO.sub.2Na).sub.2, (CH.sub.2OCO.sub.2Na).sub.2, Na.sub.2S, Na.sub.xSO.sub.y, or a combination thereof, wherein X=F, Cl, I, or Br, R=a hydrocarbon group, 0<x1, and 1y4.

25. A method of producing the surface-stabilized anode active material of claim 11, said method comprising: (a) providing a plurality of particles of an anode active material; and (b) depositing a surface-stabilizing layer to embrace at least one of said particles, wherein said surface-stabilizing layer comprises a lithium- or sodium-containing species chemically bonded to said at least one particle and wherein said lithium- or sodium-containing species is selected from Li.sub.2CO.sub.3, Li.sub.2O, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, Li.sub.4B, Na.sub.4B, Na.sub.2CO.sub.3, Na.sub.2O, Na.sub.2C.sub.2O.sub.4, NaOH, NaX, ROCO.sub.2Na, HCONa, RONa, (ROCO.sub.2Na).sub.2, (CH.sub.2OCO.sub.2Na).sub.2, Na.sub.2S, Na.sub.xSO.sub.y, or a combination thereof, wherein X=F, Cl, I, or Br, R=a hydrocarbon group, 0<x1, and 1y4.

26. The method of claim 24, wherein said step of depositing includes conducting an electrochemical decomposition reaction of electrolyte to form said lithium- or sodium-containing species that chemically bond to a surface of at least one of said prelithiated particles.

27. The method of claim 25, wherein said step of depositing includes conducting an electrochemical decomposition reaction of electrolyte to form said lithium- or sodium-containing species that chemically bond to a surface of at least one of said particles.

28. The method of claim 24, wherein said particles of anode active material are selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo.sub.2O.sub.4; (f) particles of graphite and carbon; and (g) combinations thereof.

29. The method of claim 25, wherein said particles of anode active material are selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo.sub.2O.sub.4; (f) particles of graphite and carbon; and (g) combinations thereof.

30. The method of claim 24, wherein said step of prelithiating includes electrochemical prelithiation, chemical prelithiation, physical prelithiation, or a combination thereof.

31. The method of claim 24, wherein said anode active material comprises silicon and said prelithiated particles comprise a prelithiated silicon Li.sub.4Si, Li.sub.4.4Si, or Li.sub.xSi, wherein numerical x is from 1 to 4.4.

32. The method of claim 24, wherein said step of providing particles of an anode active material comprises providing a doped semiconductor material selected from Si or Ge doped with n-type and/or p-type dopants.

33. The method of claim 24, further comprising a step of coating a surface of said prelithiated particles with a thin layer of carbon, graphene, electron-conducting polymer, or ion-conducting polymer having a thickness from 0.5 nm to 1 m, prior to step (c).

34. The method of claim 33, wherein said thin layer of carbon is obtained from pyrolization of a polymer, pitch, or organic precursor or obtained by chemical vapor deposition, physical vapor deposition, or sputtering.

35. The method of claim 25, further comprising a step of coating a surface of said particles with a thin layer of carbon, graphene, electron-conducting polymer, or ion-conducting polymer having a thickness from 0.5 nm to 1 m prior to step (c).

36. The method of claim 35, wherein said thin layer of carbon is obtained from pyrolization of a polymer, pitch, or organic precursor or obtained by chemical vapor deposition, physical vapor deposition, or sputtering.

37. The method of claim 24, wherein said step of prelithiating includes conducting electrochemical prelithiation in a first electrochemical reactor and said step of depositing a surface-stabilizing layer includes conducting said depositing in a second electrochemical reactor, wherein said first electrochemical reactor is the same as the second electrochemical reactor.

38. A method of producing a lithium-ion battery comprising (A) preparing an anode from the prelithiated and surface-stabilized particles produced by the method of claim 24; and (B) combining said anode with a cathode, and an electrolyte to form said battery.

39. A method of producing a lithium-ion battery comprising (A) preparing an anode from the surface-stabilized particles produced by the method of claim 25; and (B) combining said anode with a cathode, and an electrolyte to form said battery.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0049] FIG. 1 Schematic of an electrochemical process for prelithiating particles of an anode active material, according to a preferred embodiment of the present invention.

[0050] FIG. 2 Electrochemical potential of the electrolyte relative to those of the anode and the cathode.

[0051] The anode can act as a reductant and the cathode an oxidant of the electrolyte.

[0052] FIG. 3 The specific capacities of 4 lithium batteries: one having an anode active material featuring surface-stabilized and prelithiated Co.sub.3O.sub.4 particles, one having prelithiated but non-stabilized Co.sub.3O.sub.4 particles, one having carbon-coated but non-prelithiated Co.sub.3O.sub.4 particles, and one having un-protected Co.sub.3O.sub.4 particles.

[0053] FIG. 4 The specific capacities of 4 lithium batteries having an anode active material featuring SnO.sub.2 particles that are prelithiated and surface-stabilized, prelithiated (not surface-stabilized), surface-stabilized (not prelithiated), and un-protected (non-stabilized and non-prelithiated, respectively.

[0054] FIG. 5 The specific capacities of 3 lithium batteries: one having an anode active material featuring surface-stabilized carbon-encapsulated Sn particles, one having carbon-encapsulated Sn particles, and one having un-protected Sn particles.

[0055] FIG. 6 Specific capacities of 3 lithium-ion cells having Si nanowires (SiNW) as an anode active material: carbon-coated SiNW, prelithiated carbon-coated SiNW, and surface-stabilized prelithiated carbon-coated SiNW, respectively.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0056] This invention is related to anode materials for high-capacity lithium batteries, which are preferably secondary batteries based on a non-aqueous electrolyte, a polymer gel electrolyte, polymer electrolyte, quasi-solid electrolyte, or solid-state electrolyte. The shape of a lithium metal or lithium ion battery can be cylindrical, square, button-like, etc. The present invention is not limited to any battery shape or configuration.

[0057] The present invention provides a method of producing surface-stabilized prelithiated particles of an anode active material for use in a rechargeable lithium-ion battery. This anode material enables the battery to exhibit a significantly improved specific capacity and much longer charge-discharge cycle life. The method comprises (a) providing an anode active material (preferably in the form of fine particles); (b) intercalating or absorbing a desired amount of lithium into the anode active material particles to produce prelithiated particles of the anode active material (the prelithiation step); (c) subjecting the prelithiated anode active material particles to a surface treatment that produces a surface-stabilizing coating embracing the prelithiated particles, wherein this surface-stabilizing coating is a layer of lithium- or sodium-containing species chemically bonded to the particles and the lithium- or sodium-containing species is selected from Li.sub.2CO.sub.3, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, Li.sub.4B, Na.sub.4B, Na.sub.2CO.sub.3, Na.sub.2O, Na.sub.2C.sub.2O.sub.4, NaOH, NaX, ROCO.sub.2Na, HCONa, RONa, (ROCO.sub.2Na).sub.2, (CH.sub.2OCO.sub.2Na).sub.2, Na.sub.2S, Na.sub.xSO.sub.y, a combination thereof, or a combination thereof with Li.sub.2O, wherein X=F, Cl, I, or Br, R=a hydrocarbon group, x=0-1, y=1-4.

[0058] For a lithium ion battery, according to a preferred embodiment of the present invention, the starting anode active material (in a fine powder form) may be selected is selected from the group consisting of: (a) silicon (Si), germanium (Ge), tin (Sn), lead (Pb), antimony (Sb), bismuth (Bi), zinc (Zn), aluminum (Al), titanium (Ti), nickel (Ni), cobalt (Co), and cadmium (Cd); (b) alloys or intermetallic compounds of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Ni, Co, or Cd with other elements; (c) oxides, carbides, nitrides, sulfides, phosphides, selenides, and tellurides of Si, Ge, Sn, Pb, Sb, Bi, Zn, Al, Ti, Fe, Ni, Co, V, or Cd, and their mixtures, composites, or lithium-containing composites; (d) salts and hydroxides of Sn; (e) lithium titanate, lithium manganate, lithium aluminate, lithium-containing titanium oxide, lithium transition metal oxide, ZnCo.sub.2O.sub.4; (f) particles of graphite and carbon; and (g) combinations thereof.

[0059] Prelithiation can be accomplished in several different ways that can be classified into 3 categories: physical methods, electrochemical methods, and chemical methods. The chemical methods are typically conducted by sourcing lithium atoms from active reactants or lithium metal. The active reactants can include organometallic compounds and lithium salts and the reactions can be effectuated ex-situ (in a chemical reactor before anode fabrication, or after anode fabrication but before cell assembly). One may also bring lithium metal in direct contact with particles of the desired anode active material in a dry condition or with the presence of a liquid electrolyte.

[0060] A physical process entails depositing a Li coating on a surface of an anode active material substrate (e.g., a layer of fine Si particles), followed by promoting thermally induced diffusion of Li into the substrate (e.g., into the interior of a Si particles). A thin lithium layer can be deposited on the surface of an anode material substrate using a standard thin film process, such as thermal evaporation, electron beam evaporation, sputtering, and laser ablation. A vacuum is used during the deposition process to avoid reactivity between the atomic lithium and molecules of lithium-reactive substances such as water, oxygen, and nitrogen. A vacuum of greater than 1 milli-Torr is desirable. When electron beam deposition is used a vacuum of 10.sup.4 Torr is desired and a vacuum of 10.sup.6 Torr is preferred to avoid interaction between the electron beam and any residual air molecules.

[0061] The evaporative deposition techniques involve the heating of a lithium metal to create a lithium vapor. The lithium metal can be heated by an electron beam or by resistive heating of the lithium metal. The lithium vapor deposits lithium onto a substrate composed of packed Si particles. To promote the deposition of lithium metal the substrate can be cooled or maintained at a temperature lower than the temperature of the lithium vapor. A thickness monitor such as a quartz crystal type monitor can be placed near the substrate to monitor the thickness of the film being deposited. Alternatively, laser ablation and sputtering techniques can be used to promote thin lithium film growth on a substrate. For example, argon ions can be used in the sputtering process to bombard a solid lithium metal target. The bombarding knocks lithium off of the target and deposits it on the surface of a substrate. Laser ablation processes can be used to knock lithium off of a lithium target. The separated lithium atoms are then deposited onto the substrate. The lithium-coated layer of packed Si particles (as an example of an anode active material) is then immersed into a liquid electrolyte containing a lithium salt dissolved in an organic solvent. Lithium atoms rapidly permeate into the bulk of Si particles to form prelithiated Si particles. Physical methods may also be conducted by simply mixing molten lithium metal with particles of the anode active materials (e.g. Si, Ge, SiO, Co.sub.3O.sub.4, Sn, SnO.sub.2, ZnCo.sub.2O.sub.4, etc.).

[0062] A more preferred pre-lithiation process involves electro-chemically forcing Li atoms to migrate into the bulk of multiple Si particles under the influence of an electromotive force (emf). In a typical arrangement, again using Si as an example, a compacted mass of Si particles (having carbon particles as a conductive additive mixed with these Si particles or having individual Si particles coated with a carbon material or embraced with graphene sheets) is used as a positive electrode and Li metal sheet or rod as a negative electrode. The two electrodes are then immersed in a liquid electrolyte containing a lithium salt dissolved in an organic solvent. An electric current is then applied between the anode and the cathode. This is similar to an electro-plating procedure, but, surprisingly, Li atoms are capable of permeating into the bulk of the Si particles. For electro-chemical lithiation of Si particles, the particles may be confined in a porous container (e.g., fine metal mesh) that is permeable to electrolyte, but does not allow solid Si particles to escape. The fine metal mesh serves as a working electrode while a lithium metal rod or sheet serves as a counter electrode. The entire set-up is preferably immersed in a liquid electrolyte contained in an electrochemical reactor.

[0063] Preferably, the lithium salt in the liquid electrolyte is selected from lithium perchlorate (LiClO.sub.4), lithium hexafluorophosphate (LiPF.sub.6), lithium borofluoride (LiBF.sub.4), lithium hexafluoroarsenide (LiAsF.sub.6), lithium trifluoro-metasulfonate (LiCF.sub.3SO.sub.3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF.sub.3SO.sub.2).sub.2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), lithium nitrate (LiNO.sub.3), Li-Fluoroalkyl-Phosphates (LiPF.sub.3(CF.sub.2CF.sub.3).sub.3), lithium bisperfluoro-ethysulfonylimide (LiBETI), lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), or a combination thereof. It may be noted that these metal salts are also commonly used in the electrolytes of rechargeable lithium batteries.

[0064] The electrolytes used in this electrochemical reactor may contain a solvent selected from 1,3-dioxolane (DOL), 1,2-dimethoxyethane (DME), tetraethylene glycol dimethylether (TEGDME), poly(ethylene glycol) dimethyl ether (PEGDME), diethylene glycol dibutyl ether (DEGDBE), 2-ethoxyethyl ether (EEE), sulfone, sulfolane, ethylene carbonate (EC), dimethyl carbonate (DMC), methylethyl carbonate (MEC), diethyl carbonate (DEC), ethyl propionate, methyl propionate, propylene carbonate (PC), gamma-butyrolactone (-BL), acetonitrile (AN), ethyl acetate (EA), propyl formate (PF), methyl formate (MF), toluene, xylene, methyl acetate (MA), fluoroethylene carbonate (FEC), vinylene carbonate (VC), allyl ethyl carbonate (AEC), a hydrofluoroether, a room temperature ionic liquid solvent, or a combination thereof. These solvents are also commonly used in the electrolytes of rechargeable lithium batteries.

[0065] The aforementioned prelithiation processes are applicable to all of the anode active materials discussed in the present specification, not just Si, although Si is used as an example to illustrate the best-mode practice. The anode active material preferably comprises silicon and the prelithiated particles comprise a prelithiated silicon Li.sub.4Si, Li.sub.4.4Si, or Li.sub.xSi, wherein numerical x is between 1 and 4.4. The step of providing an anode active material may comprise providing a doped semiconductor material. Such a doped semiconductor material may be selected from Si or Ge doped with n-type and/or p-type dopants. Commonly used n-type dopants are P, As, and Sb and commonly used p-type dopants are Al, Ga, and In.

[0066] The prelithiated anode active material particles are then subjected to a surface treatment that produces a surface-stabilizing coating to embrace the prelithiated particles, wherein this surface-stabilizing coating is a layer of lithium- or sodium-containing species that are chemically bonded to the prelithiated particles.

[0067] These bonding species (lithium- or sodium-containing species) can be simply generated as the products or by-products of select chemical or electrochemical reactions between the electrolyte (Li or Na salt dissolved in a solvent) and the anode active material particle surfaces (where elements such as C, O, H, and N are often present or prescribed to exist). These reactions may be preferably induced by externally applied current/voltage in an electrochemical reactor. This will be discussed in more detail later. The following procedure for producing surface stabilizing species is applicable to both prelithiated and non-lithiated particles of an anode active material. There is no limitation on the type of anode materials; all types of anode active materials that can be used in a lithium battery anode can be protected or embraced by using this invented method.

[0068] In a preferred embodiment, the lithium- or sodium-containing species may be selected from Li.sub.2CO.sub.3, Li.sub.2O, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, Li.sub.4B, Na.sub.4B, Na.sub.2CO.sub.3, Na.sub.2O, Na.sub.2C.sub.2O.sub.4, NaOH, NaX, ROCO.sub.2Na, HCONa, RONa, (ROCO.sub.2Na).sub.2, (CH.sub.2OCO.sub.2Na).sub.2, Na.sub.2S, Na.sub.xSO.sub.y, or a combination thereof, wherein X=F, Cl, I, or Br, R=a hydrocarbon group (e.g. RCH, CH.sub.2, CH.sub.3CH.sub.2, etc.), x=0-1, y=1-4. These species are surprisingly capable of chemically bonding to surfaces of various anode active material particles to form a structurally sound encapsulating layer. Such a layer is also permeable to lithium ions, enabling subsequent lithium intercalation/insertion and de-intercalation/extraction into/from the protected particles. Typically, not just one, but at least two types of lithium- or sodium-containing species in the above list are present in the protective layer embracing the prelithiated or non-lithiated particles if this layer is produced electrochemically.

[0069] The preparation of the surface-protecting layers containing these lithium- or sodium-containing species may be conducted in an electrochemical reactor, which is an apparatus very similar to an electrode plating system. In this reactor, an anode material-containing porous structure (in the form of a mat, paper, film, etc. or simply in a compacted mass confined by a mess of conducting wires) is used as a working electrode and lithium sheet (or sodium sheet) as a counter electrode. Contained in the reactor is an electrolyte composed of a lithium or sodium salt dissolved in a solvent (e.g. 1M LiPF.sub.6 dissolved in a mixture of ethylene carbonate (EC) and dimethyl carbonate (DMC) at a 1:1 ratio by volume). A current is then imposed between these two electrodes (lithium or sodium sheet electrode and the anode active material-based working electrode). The particles of the anode active material in the working electrode are galvanostatically discharged (e.g. Li ions being sent to and inserted into the anode active material particles) and charged (Li ions released by these particles) in the voltage range from 0.01V to 4.9V at the current densities of 100-1000 mA/g following a voltage-current program similar to what would be used in a lithium-ion battery. However, the system is intentionally subjected to conditions conducive to oxidative degradation of electrolyte (e.g. close to 0.01-1.0 V vs. Li/Li.sup.+) or reductive degradation of electrolyte (4.1-4.9 V vs. Li/Li.sup.+) for a sufficient length of time. The degradation products react with Li.sup.+ ions, Li salt, functional groups (if any) or carbon atoms coated on particles to form the lithium-containing species that also chemically bond to the particles.

[0070] The chemical compositions of the lithium-containing species are governed by the voltage range, the number of cycles (from 0.01 V to 4.9 V, and back), solvent type, lithium salt type, chemical composition of graphene sheets (e.g. % of 0, H, and N), and electrolyte additives (e.g. LiNO.sub.3, if available). The morphology, structure and composition of graphene oxide (GO), reduced graphene oxide (RGO), the lithium-containing species that are bonded to graphene sheets can be characterized by scanning electron microscope (SEM), transmission electron microscope (TEM), Raman spectrum, X-ray diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), elemental analysis, and X-ray photoelectron spectroscopy (XPS).

[0071] The decomposition of non-aqueous electrolyte leads to the formation of lithium or sodium chemical compounds that bond to graphene surfaces and edges. The reasons why the non-aqueous electrolyte decomposed during discharge-charge cycling in an electrochemical reactor may be explained as follows. As illustrated in FIG. 2, in an electrochemical reactor system where there are a cathode and an anode in contact with an electrolyte, the thermodynamic stability of the electrolyte is dictated by the relative electron energies of the two electrodes relative to the energy level of the non-aqueous electrolyte. The anode is potentially a reductant, and the cathode an oxidant. The two electrodes are typically electronic conductors and, in this diagram, their electrochemical potential are designated as .sub.A and .sub.C (or Fermi energies .sub.F), respectively. The energy separation, E.sub.g, between the lowest unoccupied molecular orbital (LUMO) and the highest occupied molecular orbital (HOMO) of the electrolyte is the stable electrochemical window of the electrolyte. In other words, in order for the electrolyte to remain thermodynamically stable (i.e. not to decompose), the electrochemical potential of the anode (.sub.A) must be maintained below the LOMO and .sub.C of the cathode must be above the HOMO.

[0072] From the schematic diagram of FIG. 2, we can see that an anode with .sub.A above the LUMO and a cathode with .sub.C below the HOMO will reduce and oxidize the electrolyte, respectively, unless a passivating film is formed that creates a barrier to electron transfer between the anode and the electrolyte or between the cathode and the electrolyte. In the presently invented method, an external current/voltage is intentionally applied over the anode and the cathode to bias their respective electrochemical potential levels so that the electrolyte can go outside of the stable electrochemical potential window, undergoing oxidative and/or reductive degradation. The degradation products are reactive species that react among themselves and with the functional groups or active atoms on particles of the anode active material or their surface coverage layer (carbon, graphene, conductive polymers, etc.), forming a mass of lithium- or sodium-containing species that bond to surfaces of these particles (with or without a surface coverage.

[0073] For the list of lithium/sodium salts and solvents investigated, the electrolytes have an oxidation potential (HOMO) at about 4.7 V and a reduction potential (LUMO) near 1.0 V. (All voltages in this specification are with respect to Li.sup.+/Li or Na.sup.+/Na). We have observed that the chemical interaction of Li.sup.+ or Na.sup.+ ions with particles of an anode active material (with or without carbon or graphene coverage) typically occur at about 0.01-0.8 V, so electrolytes are prone to reductive degradation in the voltage range of 0.01-0.8 V. By imposing a voltage close to 4.7 volts, the electrolytes are also subject to oxidative degradation. The degradation products spontaneously react with chemical species associated with these particles, forming a protective layer embracing/encapsulating these particles during the charge-discharge cycling (electrolyte reduction-oxidation cycling). In general, these lithium- or sodium-containing species are not electrically conducting and, hence, these reactions can self-terminate to form essentially a passivating phase.

[0074] The electrolytes that can be used in this electrochemical decomposition reactor may be selected from any lithium or sodium metal salt that is dissolvable in a solvent to produce an electrolyte. Preferably, the metal salt is selected from lithium perchlorate (LiClO.sub.4), lithium hexafluorophosphate (LiPF.sub.6), lithium borofluoride (LiBF.sub.4), lithium hexafluoroarsenide (LiAsF.sub.6), lithium trifluoro-metasulfonate (LiCF.sub.3SO.sub.3), bis-trifluoromethyl sulfonylimide lithium (LiN(CF.sub.3SO.sub.2).sub.2), lithium bis(oxalato)borate (LiBOB), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), lithium oxalyldifluoroborate (LiBF.sub.2C.sub.2O.sub.4), lithium nitrate (LiNO.sub.3), Li-Fluoroalkyl-Phosphates (LiPF.sub.3(CF.sub.2CF.sub.3).sub.3), lithium bisperfluoro-ethysulfonylimide (LiBETI), lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide (LiTFSI), sodium perchlorate (NaClO.sub.4), sodium hexafluorophosphate (NaPF.sub.6), sodium borofluoride (NaBF.sub.4), sodium trifluoro-metasulfonate (NaCF.sub.3SO.sub.3), bis-trifluoromethyl sulfonylimide sodium (NaN(CF.sub.3SO.sub.2).sub.2), sodium trifluoromethanesulfonimide (NaTF SI), bis-trifluoromethyl sulfonylimide sodium (NaN(CF.sub.3SO.sub.2).sub.2), or a combination thereof. It may be noted that these metal salts are also commonly used in the electrolytes of rechargeable lithium or sodium batteries.

[0075] The electrolytes used in this electrochemical decomposition reactor may contain a solvent selected from 1,3-dioxolane (DOL), 1,2-dimethoxyethane (DME), tetraethylene glycol dimethylether (TEGDME), poly(ethylene glycol) dimethyl ether (PEGDME), diethylene glycol dibutyl ether (DEGDBE), 2-ethoxyethyl ether (EEE), sulfone, sulfolane, ethylene carbonate (EC), dimethyl carbonate (DMC), methylethyl carbonate (MEC), diethyl carbonate (DEC), ethyl propionate, methyl propionate, propylene carbonate (PC), gamma-butyrolactone (-BL), acetonitrile (AN), ethyl acetate (EA), propyl formate (PF), methyl formate (MF), toluene, xylene, methyl acetate (MA), fluoroethylene carbonate (FEC), vinylene carbonate (VC), allyl ethyl carbonate (AEC), a hydrofluoroether, a room temperature ionic liquid solvent, or a combination thereof. These solvents are also commonly used in the electrolytes of rechargeable lithium or sodium batteries.

[0076] It may be noted that the electrochemical decomposition reactor used for the formation of a surface protection layer may be the same electrochemical reactor for prelithiation. As illustrated in FIG. 1, the prelithiation process may be allowed to proceed at a current/voltage condition that is in favor of electrochemically inserting lithium ions into the anode active material particles (this condition being in the thermodynamic stability regions depicted in FIG. 2). For example, the voltage difference between the working electrode (containing Si particles, for instance) and the counter electrode may be cycled between 0.6 volts and 3.3 volts for prelithiation of Si. Following this prelithiation procedure, the voltage difference is then cycled between 0.1 volts and 4.8 volts (as an example) to effectuate electrochemical decomposition of the electrode for forming the Li- and/or Na-containing species. The electrolyte used in prelithiation can be the same as or different than the electrolyte used for protective species formation.

[0077] The protective layer of the instant invention typically exhibits a lithium ion or sodium ion conductivity from 2.510.sup.5 S/cm to 5.510.sup.3 S/cm, and more typically from 1.010.sup.4 S/cm to 2.510.sup.3 S/cm. The anode active material may be made into a thin film and then the Li- or Na-containing species are coated thereon and then peeled off to allow for ion conductivity measurement.

[0078] Several micro-encapsulation processes can be used to embrace/encapsulate particles of an anode active material (with or without prelithiation) with a protective layer containing the invented lithium- and/or sodium-containing species. This requires dissolution of a lithium salt, a sodium salt, multiple lithium salts, and/or multiple sodium salts in a solvent (including mixture of multiple solvents) to form a solution. This solution can then be used to encapsulate solid particles via several of the micro-encapsulation methods to be discussed in what follows.

[0079] There are three broad categories of micro-encapsulation methods that can be implemented to produce encapsulated particles of an anode active material: physical methods, physico-chemical methods, and chemical methods. The physical methods include pan-coating, air-suspension coating, centrifugal extrusion, vibration nozzle, and spray-drying methods. The physico-chemical methods include ionotropic gelation and coacervation-phase separation methods. The chemical methods include interfacial polycondensation or other surface reactions. Several methods are discussed below as examples.

[0080] Pan-Coating Method:

[0081] The pan coating process involves tumbling the active material particles in a pan or a similar device while the encapsulating material (e.g. highly concentrated solution of Li/Na salts in a solvent) is applied slowly until a desired encapsulating shell thickness is attained.

[0082] Air-Suspension Coating Method:

[0083] In the air suspension coating process, the solid particles (core material) are dispersed into the supporting air stream in an encapsulating chamber. A controlled stream of a salt-solvent solution (with an optional polymer) is concurrently introduced into this chamber, allowing the solution to hit and coat the suspended particles. These suspended particles are encapsulated (fully coated) with the salts while the volatile solvent is removed, leaving a very thin layer of Li and/or Na salts on surfaces of these particles. This process may be repeated several times until the required parameters, such as full-coating thickness (i.e. encapsulating shell or wall thickness), are achieved. The air stream which supports the particles also helps to dry them, and the rate of drying is directly proportional to the temperature of the air stream, which can be adjusted for optimized shell thickness.

[0084] In a preferred mode, the particles in the encapsulating zone portion may be subjected to re-circulation for repeated coating. Preferably, the encapsulating chamber is arranged such that the particles pass upwards through the encapsulating zone, then are dispersed into slower moving air and sink back to the base of the encapsulating chamber, enabling repeated passes of the particles through the encapsulating zone until the desired encapsulating shell thickness is achieved.

[0085] Centrifugal Extrusion:

[0086] Anode active materials may be encapsulated using a rotating extrusion head containing concentric nozzles. In this process, a stream of core fluid (slurry containing particles of an anode active material dispersed in a solvent) is surrounded by a sheath of shell solution or melt. As the device rotates and the stream moves through the air it breaks, due to Rayleigh instability, into droplets of core, each coated with the shell solution. While the droplets are in flight, the molten shell may be hardened or the solvent may be evaporated from the shell solution. If needed, the capsules can be hardened after formation by catching them in a hardening bath. Since the drops are formed by the breakup of a liquid stream, the process is only suitable for liquid or slurry. A high production rate can be achieved. Up to 22.5 kg of microcapsules can be produced per nozzle per hour and extrusion heads containing 16 nozzles are readily available.

[0087] Vibrational Nozzle Method:

[0088] Core-shell encapsulation of an anode active material can be conducted using a laminar flow through a nozzle and vibration of the nozzle or the liquid. The vibration has to be done in resonance with the Rayleigh instability, leading to very uniform droplets. The liquid can consist of any liquids with limited viscosities (1-50,000 mPa.Math.s): emulsions, suspensions or slurry containing the anode active material. The solidification can be done according to the used gelation system with an internal gelation (e.g. sol-gel processing, melt) or an external (additional binder system, e.g. in a slurry).

[0089] Spray-Drying:

[0090] Spray drying may be used to encapsulate particles of an active material when the active material is dissolved or suspended in a melt or polymer solution. In spray drying, the liquid feed (solution or suspension) is atomized to form droplets which, upon contacts with hot gas, allow solvent to get vaporized and thin polymer shell to fully embrace the solid particles of the active material.

[0091] It may be noted that the anode active material (e.g., prelithiated or non-lithiated Si nano particles) may be coated with a carbonizable coating material (e.g., phenolic resin, poly(furfuryl alcohol), coal tar pitch, or petroleum pitch). The coating can then be carbonized to produce an amorphous carbon or polymeric carbon coating on the surface of these Si particles. Such a conductive surface coating can help maintain a network of electron-conducting paths during repeated charge/discharge cycles and prevent undesirable chemical reactions between Si and electrolyte from happening. Hence, the presently invented method may further comprise a step of coating a surface of the fine particles with a thin layer of carbon having a thickness less than 1 m prior to the formation of the protective Li and/or Na-containing species. The thin layer of carbon preferably has a thickness less than 100 nm. Such a thin layer of carbon may be obtained from pyrolization of a polymer, pitch, or organic precursor or obtained by chemical vapor deposition, physical vapor deposition, sputtering, etc.

[0092] Alternatively, the particles of an anode active material may be coated with a layer of graphene, electron-conducting polymer, or ion-conducting polymer. Such coating processes are well-known in the art.

[0093] The surface-stabilized or surface-stabilized and prelithiated particles of an anode active material (with or without a coating of carbon, graphene, electron-conducting polymer, or ion-conducting polymer) may be further encapsulated by a thin layer of a high-elasticity polymer (e.g. an elastomer) having a fully recoverable tensile strain of from 5% to 700% and a thickness preferably from 0.5 nm to 2 m (preferably from 1 nm to 100 nm). The elastomer preferably has a lithium ion conductivity from 10.sup.7 S/cm to 510.sup.2 S/cm at room temperature (preferably and typically no less than 10.sup.6 S/cm, further preferably no less than 10.sup.5 S/cm, more preferably no less than 10.sup.4 S/cm, and most preferably no less than 10.sup.3 S/cm).

[0094] In others, the elastomeric material is an elastomer matrix composite containing from 0.1% to 50% by weight (preferably from 1% to 35% by weight) of a lithium ion-conducting additive dispersed in an elastomer matrix material.

[0095] In some embodiments, the elastomeric material contains a material selected from natural polyisoprene (e.g. cis-1,4-polyisoprene natural rubber (NR) and trans-1,4-polyisoprene gutta-percha), synthetic polyisoprene (IR for isoprene rubber), polybutadiene (BR for butadiene rubber), chloroprene rubber (CR), polychloroprene (e.g. Neoprene, Baypren etc.), butyl rubber (copolymer of isobutylene and isoprene, IIR), including halogenated butyl rubbers (chloro butyl rubber (CIIR) and bromo butyl rubber (BIIR), styrene-butadiene rubber (copolymer of styrene and butadiene, SBR), nitrile rubber (copolymer of butadiene and acrylonitrile, NBR), EPM (ethylene propylene rubber, a copolymer of ethylene and propylene), EPDM rubber (ethylene propylene diene rubber, a terpolymer of ethylene, propylene and a diene-component), epichlorohydrin rubber (ECO), polyacrylic rubber (ACM, ABR), silicone rubber (SI, Q, VMQ), fluorosilicone rubber (FVMQ), fluoroelastomers (FKM, and FEPM; such as Viton, Tecnoflon, Fluorel, Aflas and Dai-El), perfluoroelastomers (FFKM: Tecnoflon PFR, Kalrez, Chemraz, Perlast), polyether block amides (PEBA), chlorosulfonated polyethylene (CSM; e.g. Hypalon), and ethylene-vinyl acetate (EVA), thermoplastic elastomers (TPE), protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, and combinations thereof.

[0096] The urethane-urea copolymer film usually consists of two types of domains, soft domains and hard ones. Entangled linear backbone chains consisting of poly(tetramethylene ether) glycol (PTMEG) units constitute the soft domains, while repeated methylene diphenyl diisocyanate (MDI) and ethylene diamine (EDA) units constitute the hard domains. The lithium ion-conducting additive can be incorporated in the soft domains or other more amorphous zones.

[0097] In some embodiments, the elastomeric material is an elastomer matrix composite containing a lithium ion-conducting additive dispersed in an elastomer matrix material, wherein said lithium ion-conducting additive is selected from Li.sub.2CO.sub.3, Li.sub.2O, Li.sub.2C.sub.2O.sub.4, LiOH, LiX, ROCO.sub.2Li, HCOLi, ROLi, (ROCO.sub.2Li).sub.2, (CH.sub.2OCO.sub.2Li).sub.2, Li.sub.2S, Li.sub.xSO.sub.y, or a combination thereof, wherein X=F, Cl, I, or Br, R=a hydrocarbon group, x=0-1, y=1-4.

[0098] In some embodiments, the elastomeric material is an elastomer matrix composite containing a lithium ion-conducting additive dispersed in an elastomer matrix material, wherein said lithium ion-conducting additive contains a lithium salt selected from lithium perchlorate, LiClO.sub.4, lithium hexafluorophosphate, LiPF.sub.6, lithium borofluoride, LiBF.sub.4, lithium hexafluoroarsenide, LiAsF.sub.6, lithium trifluoro-metasulfonate, LiCF.sub.3SO.sub.3, bis-trifluoromethyl sulfonylimide lithium, LiN(CF.sub.3SO.sub.2).sub.2, lithium bis(oxalato)borate, LiBOB, lithium oxalyldifluoroborate, LiBF.sub.2C.sub.2O.sub.4, lithium oxalyldifluoroborate, LiBF.sub.2C.sub.2O.sub.4, lithium nitrate, LiNO.sub.3, Li-Fluoroalkyl-Phosphates, LiPF.sub.3(CF.sub.2CF.sub.3).sub.3, lithium bisperfluoro-ethysulfonylimide, LiBETI, lithium bis(trifluoromethanesulphonyl)imide, lithium bis(fluorosulphonyl)imide, lithium trifluoromethanesulfonimide, LiTFSI, an ionic liquid-based lithium salt, or a combination thereof.

[0099] The elastomeric material may contain a mixture or blend of an elastomer and an electron-conducting polymer selected from polyaniline, polypyrrole, polythiophene, polyfuran, a bi-cyclic polymer, derivatives thereof (e.g. sulfonated versions), or a combination thereof.

[0100] In some embodiments, the elastomeric material contains a mixture or blend of an elastomer and a lithium ion-conducting polymer selected from poly(ethylene oxide) (PEO), Polypropylene oxide (PPO), poly(acrylonitrile) (PAN), poly(methyl methacrylate) (PMMA), poly(vinylidene fluoride) (PVdF), Poly bis-methoxy ethoxyethoxide-phosphazenex, Polyvinyl chloride, Polydimethylsiloxane, poly(vinylidene fluoride)-hexafluoropropylene (PVDF-HFP), a derivative thereof (e.g. sulfonated versions), or a combination thereof.

[0101] In the preparation of an anode electrode, acetylene black (AB), carbon black (CB), or ultra-fine graphite particles may be used as a conductive additive. Conductive additives may comprise an electrically conductive material selected from the group consisting of electro-spun nanofibers, carbonized electro-spun nanofibers, vapor-grown carbon or graphite nanofibers, carbon or graphite whiskers, carbon nano-tubes, nano-scaled graphene platelets, metal nanowires, metal-coated nanowires, carbon-coated nanowires, metal-coated nanofibers, carbon-coated nanofibers, and combinations thereof. A binder material may be chosen from polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), ethylene-propylene-diene copolymer (EPDM), or styrene-butadiene rubber (SBR), for example. Conductive materials such as electronically conductive polymers, meso-phase pitch, coal tar pitch, and petroleum pitch may also be used as a binder. A typical mixing ratio of these ingredients is 80 to 85% by weight for the anode active material, 5 to 15% by weight for the conductive additive, and 5 to 10% by weight for the binder. The current collector may be selected from aluminum foil, stainless steel foil, and nickel foil. There is no particularly significant restriction on the type of current collector, provided the material is a good electrical conductor and relatively corrosion resistant. The separator may be selected from a polymeric nonwoven fabric, porous polyethylene film, porous polypropylene film, or porous PTFE film.

[0102] The electrode fabrication may comprise combining multiple fine particles of prelithiated anode active material with a conductive additive and/or a binder material, plus a desired amount of another type of anode active materials selected from particles of graphite, hard carbon, soft carbon, meso-carbon micro-bead, surface-modified graphite, carbon-coated graphite, or a combination thereof.

[0103] Hence, a lithium ion battery may contain an anode that comprises at least two types of anode active material wherein at least one type of active material is prelithiated (e.g., Si and Sn) and at least one type of active material is not prelithiated (e.g., carbonaceous material, such as graphite, hard carbon, soft carbon, surface-modified graphite, chemically modified graphite, or meso-carbon micro-beads, MCMBs). Prelithiated carbonaceous anode materials are unstable in regular room air. The present invention enable the battery to contain an anode that comprises at least a non-carbon active material possessing an ultra-high lithium absorbing capacity (e.g., Si that exhibits a specific capacity up to 4,200 mAh/g). The battery comprises an anode that contains an excess amount of lithium (disposed inside a non-carbon anode active material, not on its surface) to compensate for the formation of SEI layers, in addition to providing enough lithium to intercalate into (or form a compound with) a cathode active material.

[0104] The present invention allows the excess amount of lithium to be stored in high-capacity anode active materials (there is no need to make use of the full capacity of Si, for instance). The capacity limitation is on the cathode side, rather than the anode side. The present approach obviates the need for the cathode to supply the needed lithium, thereby further reducing the needed initial weight of the cathode or increasing the cathode weight that can be incorporated in a cell. This strategy can increase the overall capacity of a lithium ion battery by another 10%-20%.

[0105] There is no limitation on the types of cathode materials that can pair up with the presently invented anode materials. The positive electrode active material may be selected from a wide variety of oxides, such as lithium-containing nickel oxide, lithium-containing cobalt oxide, lithium-containing nickel-cobalt oxide, lithium-containing vanadium oxide, lithium iron phosphate, lithium manganese phosphate, lithium manganese-iron phosphate, and other lithium metal (or mixed metals) phosphate. Positive electrode active material may also be selected from chalcogen compounds, such as titanium disulfate or molybdenum disulfate. More preferred are lithium cobalt oxide (e.g., Li.sub.xCoO.sub.2 where 0.8x1), lithium nickel oxide (e.g., LiNiO.sub.2), lithium manganese oxide (e.g., LiMn.sub.2O.sub.4 and LiMnO.sub.2), lithium iron phosphate, lithium manganese-iron phosphate, lithium vanadium phosphate because these oxides provide a relatively high cell voltage and relatively good cycling stability.

[0106] Lithium cobalt oxide (LiCoO.sub.2) is one of the most important cathode materials used in lithium-ion secondary batteries. LiCoO.sub.2 and other similar lithium transition metal oxides, such as lithium manganese oxide, lithium nickel oxide, and lithium vanadium oxide, can be prepared by various methods using different lithium and transition metal sources. In general, bulk transition metal oxides are prepared by solid-state reactions, which involve repeated heat processes at high temperatures. Such processes generally afford the thermodynamically more stable phases and in general, microcrystalline materials are obtained. Lower temperatures and mild processing conditions may be used for several methods, such as co-precipitation, sol-gel process with/without template, synthesis by precursor, ion-exchange reaction and hydrothermal. These methods also result in particles with better control of morphology and smaller size. Other methods include flame spray pyrolysis, dehydro-freezing evaporation, supercritical dehydration, supersonic hydrothermal synthesis, and ultrasonic processing.

[0107] As an example, a process for producing lithium-cobalt oxide my include (a) mixing cobalt oxide having an average particle size of not more than 0.1 m, with a lithium compound; and (b) calcining the obtained mixture at a temperature of 500 to 850 C. As compared to the conventional processes that begin with larger cobalt oxide particles (e.g., diameter >10 m), such a process is advantageous in that lithium-cobalt oxide particles (1) can be produced with a short calcination time, (2) have a narrow particle size distribution, and (3) have a uniform small particle size.

[0108] The flame-spray pyrolysis method may include the steps of: (a) spraying minute droplets containing a solution of dissolved lithium salt and cobalt salt at room temperature; (b) atomizing the minute droplets through rapid expansion into a high temperature environment generated by combusting oxygen and hydrogen; (c) decomposing and oxidizing the atomized minute droplets thermally at high temperature to produce nano-sized oxides in gaseous phase; and (d) collecting the produced nano-sized composite oxides particles.

[0109] Lithium iron phosphate LiFePO.sub.4 is a promising candidate of cathode material for lithium-ion batteries. The advantages of LiFePO.sub.4 as a cathode active material includes a high theoretical capacity (170 mAh/g), environmental benignity, low resource cost, good cycling stability, high temperature capability, and prospect for a safer cell compared with LiCoO.sub.2. A major drawback with this material is that it has very low electronic conductivity, on the order of 10.sup.9 S/cm.sup.2. This renders it difficult to prepare cathodes capable of operating at high rates. In addition, poor solid-phase transport means that the utilization of the active material is a strong function of the particle size. This major problem may be overcome by using a nano-scaled powder (to reduce the Li ion diffusion path and electron transport path distance) and doping the powder with a transition metal. Lithium iron phosphate (LiFePO.sub.4) nano particles may be prepared by ball milling of conventional micron-sized particles, which may be prepared by a solid state reaction using LiOH.H.sub.2O, (CH.sub.3COO).sub.2Fe, and NH.sub.4H.sub.2PO.sub.4 as raw materials. Additionally, Li.sub.1.3Al.sub.0.3Ti.sub.1.7(PO.sub.4).sub.3 materials, as an example of lithium mixed-metal phosphate, may be successfully prepared by the solution deposition using lithium acetate, aluminum nitrate, ammonium dihydrogen phosphate and titanium butoxide as starting materials. The resulting material may be ball-milled to sub-micron or nanometer scales. This is but one example of a host of complex metal phosphate-based cathode materials.

[0110] A wide range of electrolytes can be incorporated into the lithium cells. Most preferred are non-aqueous and polymer gel electrolytes although other types can be used. The non-aqueous electrolyte to be employed herein may be produced by dissolving an electrolytic salt in a non-aqueous solvent. Any known non-aqueous solvent which has been employed as a solvent for a lithium secondary battery can be employed. A non-aqueous solvent mainly consisting of a mixed solvent comprising ethylene carbonate (EC) and at least one kind of non-aqueous solvent whose melting point is lower than that of aforementioned ethylene carbonate (hereinafter referred to as a second solvent) may be preferably employed. This non-aqueous solvent is advantageous in that it is (a) stable against a negative electrode containing a carbonaceous material well developed in graphite structure; (b) effective in suppressing the reductive or oxidative decomposition of electrolyte; and (c) high in conductivity. A non-aqueous electrolyte solely composed of ethylene carbonate (EC) is advantageous in that it is relatively stable against decomposition through a reduction by a graphitized carbonaceous material. However, the melting point of EC is relatively high, 39 to 40 C., and the viscosity thereof is relatively high, so that the conductivity thereof is low, thus making EC alone unsuited for use as a secondary battery electrolyte to be operated at room temperature or lower. The second solvent to be used in a mixture with EC functions to make the viscosity of the solvent mixture lower than that of EC alone, thereby promoting the ion conductivity of the mixed solvent. Furthermore, when the second solvent having a donor number of 18 or less (the donor number of ethylene carbonate is 16.4) is employed, the aforementioned ethylene carbonate can be easily and selectively solvated with lithium ion, so that the reduction reaction of the second solvent with the carbonaceous material well developed in graphitization is assumed to be suppressed. Further, when the donor number of the second solvent is controlled to not more than 18, the oxidative decomposition potential to the lithium electrode can be easily increased to 4 V or more, so that it is possible to manufacture a lithium secondary battery of high voltage.

[0111] Preferable second solvents are dimethyl carbonate (DMC), methylethyl carbonate (MEC), diethyl carbonate (DEC), ethyl propionate, methyl propionate, propylene carbonate (PC), .gamma.-butyrolactone (.gamma.-BL), acetonitrile (AN), ethyl acetate (EA), propyl formate (PF), methyl formate (MF), toluene, xylene and methyl acetate (MA). These second solvents may be employed singly or in a combination of two or more. More desirably, this second solvent should be selected from those having a donor number of 16.5 or less. The viscosity of this second solvent should preferably be 28 cps or less at 25 C.

[0112] The mixing ratio of the aforementioned ethylene carbonate in the mixed solvent should preferably be 10 to 80% by volume. If the mixing ratio of the ethylene carbonate falls outside this range, the conductivity of the solvent may be lowered or the solvent tends to be more easily decomposed, thereby deteriorating the charge/discharge efficiency. More preferable mixing ratio of the ethylene carbonate is 20 to 75% by volume. When the mixing ratio of ethylene carbonate in a non-aqueous solvent is increased to 20% by volume or more, the solvating effect of ethylene carbonate to lithium ions will be facilitated and the solvent decomposition-inhibiting effect thereof can be improved.

[0113] Examples of preferred mixed solvent are a composition comprising EC and MEC; comprising EC, PC and MEC; comprising EC, MEC and DEC; comprising EC, MEC and DMC; and comprising EC, MEC, PC and DEC; with the volume ratio of MEC being controlled within the range of 30 to 80%. By selecting the volume ratio of MEC from the range of 30 to 80%, more preferably 40 to 70%, the conductivity of the solvent can be improved. With the purpose of suppressing the decomposition reaction of the solvent, an electrolyte having carbon dioxide dissolved therein may be employed, thereby effectively improving both the capacity and cycle life of the battery.

[0114] The electrolytic salts to be incorporated into a non-aqueous electrolyte may be selected from a lithium salt such as lithium perchlorate (LiClO.sub.4), lithium hexafluorophosphate (LiPF.sub.6), lithium borofluoride (LiBF.sub.4), lithium hexafluoroarsenide (LiAsF.sub.6), lithium trifluoro-metasulfonate (LiCF.sub.3SO.sub.3) and bis-trifluoromethyl sulfonylimide lithium [LiN(CF.sub.3SO.sub.2).sub.2]. Among them, LiPF.sub.6, LiBF.sub.4 and LiN(CF.sub.3SO.sub.2).sub.2 are preferred. The content of aforementioned electrolytic salts in the non-aqueous solvent is preferably from 0.5 to 2.0 mol/l.

Example 1: Cobalt Oxide (Co.SUB.3.O.SUB.4.) Anode Particles

[0115] An appropriate amount of inorganic salts Co(NO.sub.3).sub.2.6H.sub.2O and ammonia solution (NH.sub.3.H.sub.2O, 25 wt. %) were mixed together. The resulting suspension was stirred for 2 hours under an argon flow to ensure a complete reaction. The obtained Co(OH).sub.2 precursor suspension was calcined at 450 C. in air for 2 h to form particles of the layered Co.sub.3O.sub.4. Portion of the Co.sub.3O.sub.4 particles was then encapsulated with a phenolic resin, which was then carbonized at 500 C. for 2 hours and 900 C. for another 2 hours.

[0116] A sample of Co.sub.3O.sub.4 particles and a sample of carbon-coated Co.sub.3O.sub.4 particles were then electrochemically lithiated to produce prelithiated particles. Some of the prelithiated particles and, separately, some of the non-lithiated particles were then surface-protected by a layer of LiF and Li.sub.2O formed electrochemically.

[0117] For electrochemical testing, the working electrodes were prepared by mixing 85 wt. % active material (encapsulated or non-encapsulated particulates of Co.sub.3O.sub.4, separately), 7 wt. % acetylene black (Super-P), and 8 wt. % polyvinylidene fluoride (PVDF) binder dissolved in N-methyl-2-pyrrolidinoe (NMP) to form a slurry of 5 wt. % total solid content. After coating the slurries on Cu foil, the electrodes were dried at 120 C. in vacuum for 2 h to remove the solvent before pressing. Then, the electrodes were cut into a disk (d)=12 mm) and dried at 100 C. for 24 h in vacuum. Electrochemical measurements were carried out using CR2032 (3V) coin-type cells with lithium metal as the counter/reference electrode, Celgard 2400 membrane as separator, and 1 M LiPF.sub.6 electrolyte solution dissolved in a mixture of ethylene carbonate (EC) and diethyl carbonate (DEC) (EC-DEC, 1:1 v/v). The cell assembly was performed in an argon-filled glove-box. The CV measurements were carried out using an electrochemical workstation at a scanning rate of 1 mV/s.

[0118] The electrochemical performance of the particulates of encapsulated Co.sub.3O.sub.4 particles and that of non-protected Co.sub.3O.sub.4 were evaluated by galvanostatic charge/discharge cycling at a current density of 50 mA/g, using an electrochemical workstation. The results indicate that the charge/discharge profiles for the encapsulated Co.sub.3O.sub.4 particle- and un-protected Co.sub.3O.sub.4 particle-based electrodes show a long voltage plateau at about 1.06 V and 1.10 V, respectively, followed by a slopping curve down to the cut-off voltage of 0.01 V, indicative of typical characteristics of voltage trends for the Co.sub.3O.sub.4 electrode.

[0119] FIG. 3 shows the specific capacities of 4 lithium batteries: one having an anode active material featuring surface-stabilized and prelithiated Co.sub.3O.sub.4 particles, one having prelithiated but non-stabilized Co.sub.3O.sub.4 particles, one having carbon-coated but non-prelithiated Co.sub.3O.sub.4 particles, and one having un-protected Co.sub.3O.sub.4 particles. The testing results indicate that the first-cycle lithium insertion capacities for all the Co.sub.3O.sub.4-based anode active materials are 753-755 mAh/g, which are higher than the theoretical values of graphite (372 mAh/g). All cells, except for the one containing the surface-stabilized and prelithiated Co.sub.3O.sub.4, exhibit some first-cycle irreversibility. The first-cycle efficiency values for these 4 cells are 100% for surface-stabilized and prelithiated Co.sub.3O.sub.4 particles, 99.3% for prelithiated but non-stabilized Co.sub.3O.sub.4 particles, 96% for carbon-coated but non-prelithiated Co.sub.3O.sub.4 particles, and 93% for un-protected Co.sub.3O.sub.4 particles. The initial capacity loss likely has resulted mainly from the formation of solid electrolyte interface (SEI) layers on the surfaces of anode active material particles.

[0120] As the number of cycles increases, the specific capacity of the bare Co.sub.3O.sub.4 electrode drops precipitously. Compared with its initial capacity value of approximately 755 mAh/g, its capacity suffers a 20% loss after 150 cycles and a 40% loss after 260 cycles. By contrast, the presently invented surface-stabilized and prelithiated particles provide the battery cell with a very stable and high specific capacity for a large number of cycles, experiencing a capacity loss of less than 1.33% after 260 cycles. The surface-stabilized particles (without prelithiation) enable the cell to sustain a 6% capacity loss after 260 cycles. These data have clearly demonstrated the surprising and superior performance of the presently invented electrode materials compared with prior art un-protected particle-based electrode materials.

[0121] It may be noted that the number of charge-discharge cycles at which the specific capacity decays to 80% of its initial value is commonly defined as the useful cycle life of a lithium-ion battery. Thus, the cycle life of the cell containing the non-encapsulated anode active material is approximately 150 cycles. In contrast, the cycle life of the presently invented cells (not just button cells, but large-scale full cells) is typically from 1,500 to 4,000.

Example 2: Surface-Stabilized Prelithiated Tin Oxide Particles

[0122] Tin oxide (SnO.sub.2) nano particles were obtained by the controlled hydrolysis of SnCl.sub.4.5H.sub.2O with NaOH using the following procedure: SnCl.sub.4.5H.sub.2O (0.95 g, 2.7 m-mol) and NaOH (0.212 g, 5.3 m-mol) were dissolved in 50 mL of distilled water each. The NaOH solution was added drop-wise under vigorous stirring to the tin chloride solution at a rate of 1 mL/min. This solution was homogenized by sonication for 5 m in. Subsequently, the resulting hydrosol was reacted with H.sub.2SO.sub.4. To this mixed solution, few drops of 0.1 M of H.sub.2SO.sub.4 were added to flocculate the product. The precipitated solid was collected by centrifugation, washed with water and ethanol, and dried in vacuum. The dried product was heat-treated at 400 C. for 2 h under Ar atmosphere.

[0123] Samples of various different tin oxide particles were subjected to electrochemical prelithiation and/or electrochemical formation of lithium-containing species bonded to particle surfaces using lithium hexafluorophosphate (LiPF.sub.6) as the salt dissolved in EC-PC (50/50) as an electrolyte solution. The resulting surface stabilizing layer is composed of predominantly a mixture of Li.sub.2O and LiF.

[0124] The battery cells from these nano-scaled SnO.sub.2 particles (with or without surface protection species or prelithiation) were prepared using a procedure described in Example 1. Shown in FIG. 4 are the specific capacities of 4 lithium batteries having an anode active material featuring SnO.sub.2 particles that are prelithiated and surface-stabilized, prelithiated (not surface-stabilized), surface-stabilized (not prelithiated), and un-protected (non-stabilized and non-prelithiated, respectively. The anode prepared according to the presently invented surface protection and prelithiation approach offers a significantly more stable and higher reversible capacity compared to the un-coated SnO.sub.2 particle-based anode.

Example 3: Surface-Stabilized Prelithiated Tin (Sn) Nano Particles

[0125] Nano particles (76 nm in diameter) of Sn were encapsulated with a thin layer of phenolic resin shell via the spray-drying method, followed by a heat treatment from 350-600 C. for 4 hours to obtain carbon-coated Sn nano particles. Half of these C-coated Sn particles were subjected to encapsulation by a mixture of Li.sub.4B, Na.sub.4B, LiF, and NaF, which were obtained by electrochemical decomposition of an electrolyte containing lithium boron-fluoride (LiBF.sub.4) and NaBF.sub.4 dissolved in DEC. Un-protected Sn nano particles from the same batch were also investigated to determine and compare the cycling behaviors of the lithium-ion batteries containing these particles as the anode active material.

[0126] Shown in FIG. 5 are the specific capacities of 3 lithium batteries: one having an anode active material featuring surface-stabilized carbon-encapsulated Sn particles, one having carbon-encapsulated Sn particles, and one having un-protected Sn particles. These results have clearly demonstrated that encapsulation of carbon-coated Sn particles by the presently invented surface-stabilizing species provides the very best protection against capacity decay of a lithium-ion battery featuring a high-capacity anode active material. Carbon encapsulation is not good enough to provide the necessary protection.

Example 4: Surface-Stabilized Prelithiated Si Nanowire-Based Anode Materials

[0127] In a typical procedure of Si nanowire production, approximately 2.112 g of silicon powders (average diameter 2.64 m) were mixed with 80 ml of a 0.1M aqueous solution of Ni(NO.sub.3).6H.sub.2O and vigorously stirred for 30 min. Then, water was evaporated in a rotary evaporator and the solid remnants were completely dried in an oven at 150 C. The final sample (Ni-impregnated Si powers) was obtained by grinding the solids in a mortar.

[0128] Subsequently, 0.03 g of Ni-impregnated Si particles was placed in a quartz boat, and the boat was placed in a tube furnace. The sample was reduced at 500 C. for 4 hours under flowing Ar (180 sccm) and H.sub.2 (20 sccm), then the temperature was raised to 990 C. to catalytically synthesize Si nanowires; Si nanowires were found to emanate from original micron-scaled Si particles. For the purpose of separating Si nanowires, for instance, every 0.1 g of the reacted Si powders was mixed with 10 ml of ethanol and the resulting mixture was sonicated for 1 hour. Subsequently, Si nanowires were separated from the Si powders by centrifuge at 5,000 rpm for 10 min.

[0129] Some Si nanowires were coated with a layer of amorphous carbon and then prelithiated using electrochemical prelithiation procedure. Some prelithiated Si nanowires was further encapsulated by a thin layer of Li.sub.2O and LiF using a dry-air exposure (to form Li.sub.2O) and then electrochemical decomposition. For comparison purposes, Si nanowires protected by carbon coating (but no prelithiation and no surface stabilization) were also prepared and implemented in a separate lithium-ion cell. In all three cells, approximately 25-30% of graphite particles were mixed with the protected or unprotected Si nanowires (SiNW), along with 5% binder resin, to make an anode electrode.

[0130] FIG. 6 shows the specific capacities of the 3 lithium-ion cells having Si nanowires (SiNW) as an anode active material: carbon-coated SiNW (first cycle efficiency 92.8%), prelithiated carbon-coated SiNW (first cycle efficiency 98.3%), and surface-stabilized prelithiated carbon-coated SiNW (first cycle efficiency=99.96%), respectively. These data indicate that surface stabilization and prelithiation of C-coated Si nanowires provides the most stable cycling response. Carbon coating alone is not effective in improving cycling stability.

Example 5: Cycle Stability of Various Rechargeable Lithium Battery Cells

[0131] In lithium-ion battery industry, it is a common practice to define the cycle life of a battery as the number of charge-discharge cycles that the battery suffers 20% decay in capacity based on the initial capacity measured after the required electrochemical formation. Summarized in Table 1 below are the cycle life data of a broad array of batteries featuring presently invented elastomer-encapsulated anode active material particles vs. other types of anode active materials.

TABLE-US-00001 TABLE 1 Cycle life data of various lithium secondary (rechargeable) batteries. Initial Sample Type & % of anode active capacity Cycle life (No. ID Protective means material (mAh/g) of cycles) Si-1 Prelithiation + surface 25% by wt. C-coated Si 1,115 1,540-1,650 Li.sub.2O encapsulation nano particles (80 nm) + 67% graphite + 8% binder Si-2 Carbon coating only 25% by wt. Si nano 1,242 251 particles (80 nm) SiNW-1 LiF + Li.sub.2O, further by 35% Si nanowires 1,258 2,533 Urea-Urethane encap. (diameter = 90 nm) SiNW-2 Encapsulation by 45% Si nano particles, 1,730 1,355 (pre- (LiF + NaF) pre-lithiated or non- lithiated); 1,025 prelithiated (no pre-Li) (no prelithiation) Co.sub.3O.sub.4-1 (Li.sub.2CO.sub.3 + Li.sub.2C.sub.2O.sub.4) 85% Co.sub.3O.sub.4 + 8% graphite 715 1,885 (Pre- encapsulation platelets + binder lithiated); 1,266 (no pre-Li) Co.sub.3O.sub.4-2 No encapsulation 85% Co.sub.3O.sub.4 + 8% graphite 725 266 platelets + binder SnO.sub.2-1 (LiOH + LiF) 75% SnO.sub.2 particles (3 733 1,054 encapsulation m initial size) SnO.sub.2-2 (LiOH + LiF) 75% SnO.sub.2 particles (87 732 3,245 (Pre-Li) encapsulation nm in diameter) Ge-1 Li.sub.2O encapsulation of 85% Ge + 8% graphite 850 1,643 (Pre-Li) C-coated Ge platelets + binder Ge-2 Carbon-coated 85% Ge + 8% graphite 856 120 platelets + binder