Modified sodium fluoride adsorbent for special purpose, preparation and application thereof

Abstract

A method for preparing a modified sodium fluoride adsorbent includes the following steps: S1. producing spherical particles of NiCl.sub.12.6H.sub.2O and porous NaF with a mass ratio of 1:3.0-3.5; S2. sintering the spherical particles in a vacuum environment at a temperature of 120-130° C. for 10-40 hours and at a temperature of 280-300° C. for 10-40 hours, respectively, to form an adsorbent intermediate with a NiCl.sub.2—NaF framework, wherein, a vacuum degree is less than or equal to 500 pa; and S3. treating the adsorbent intermediate by fluorine-nitrogen mixtures with high purity to obtain the novel sodium fluoride adsorbent having NiCl.sub.2—NaF framework. The modified sodium fluoride adsorbent can effectively separate chlorine trifluoride and hydrogen fluoride molecules, and the optimal adsorption rate of hydrogen fluoride is upgraded to more than 98%. While, the optimal adsorption rate of chlorine trifluoride is lowered down to around 3%.

Claims

1. A method for preparing a modified sodium fluoride adsorbent, comprising the following steps: S1. producing spherical particles of NiCl.sub.2.6H.sub.2O and porous NaF with a mass ratio of 1:3.0-3.5; S2. sintering the spherical particles in a vacuum environment at a temperature of 120-130° C. for 10-40 hours and at a temperature of 280-300° C. for 10-40 hours, respectively, to form an adsorbent intermediate with a NiCl.sub.2—NaF framework, wherein, a vacuum degree is less than or equal to 500 pa; and S3. treating the adsorbent intermediate by fluorine-nitrogen mixtures with high purity.

2. The method for preparing a modified sodium fluoride adsorbent according to claim 1, wherein a preparation of the porous NaF in step S1 comprises: S11.treating NaHF.sub.2 by a vacuum drying process to form a loose and porous substance having properties of sodium fluoride; wherein, a drying temperature ranges 200-210° C., a drying time ranges 20-30 h, and a vacuum degree is less than or equal to 500 pa.

3. The method for preparing modified sodium fluoride adsorbent according to claim 1, wherein in step S1,particle sizes of the spherical particles range 5-8 mm.

4. The method for preparing a modified sodium fluoride adsorbent according to claim 1, wherein in step S3, the fluorine-nitrogen mixtures with high purity contain F.sub.2 with a volume fraction of 5-.15% and N.sub.2 with a volume fraction of 85-95%.

5. The method for preparing a modified sodium fluoride adsorbent according to claim 1, wherein in step S3, the step of treating the adsorbent intermediate by the fluorine-nitrogen mixtures with high purity comprises: fluorinating the adsorbent intermediate by the fluorine-nitrogen mixtures with high purity for 24-72 hours.

Description

BRIE DESCRIPTION OF DRAWINGS

(1) In order to clearly illustrate the technical solutions used in the implementations of the present disclosure, the drawings that are related to the illustration of the implementations will be briefly introduced below. It should be understood that the following drawings only show parts of the embodiments of the present disclosure. Therefore, the drawings should not be regarded as a limit to the scope of the present disclosure. For those of ordinary skill in the art, other related drawings can be derived from these drawings without creative effort.

(2) FIG. 1 shows a scanning electron microscope photograph of conventional sodium fluoride.

(3) FIG. 2 shows a scanning electron microscope photograph of a novel modified sodium fluoride adsorbent for special purpose according to an embodiment of the present disclosure.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(4) In order to make the objectives, technical solutions, and advantages of the embodiments of the present disclosure clearer, the technical solutions of the embodiments of the present disclosure will be described clearly and completely below with reference to the drawings of the embodiments of the present disclosure. Obviously, the described embodiments are parts of, rather than all of, the embodiments of the present disclosure. Based on the embodiments of the present disclosure, all other embodiments derived by those of ordinary skills in the art without creative effort fall within the scope of protection of the present disclosure. Accordingly, the following detailed description of the embodiments of the present disclosure shown in the drawings is not intended to limit the scope of protection of the present disclosure, but merely to represent selected embodiments of the present disclosure. Based on the embodiments of the present disclosure, all other embodiments derived by those of ordinary skills in the art without creative effort fall within the scope of protection of the present disclosure.

(5) In the description of the present disclosure, the terms “first”, “second” are used only for descriptive purposes and cannot be understood as indicating or implying relative importance or implying the quantity of indicated technical features. Thus, an element that is referred to by “first” and “second” may include, expressly or implicitly, one or more of the element. Also, in the description of the present disclosure, the phrase “a plurality of” refers to two or more elements, unless otherwise specified.

(6) According to an embodiment of the present disclosure, a method for preparing a novel modified sodium fluoride adsorbent for special purpose is provided, which includes the following steps:

(7) S1. producing spherical particles of NiCl.sub.2.6H.sub.2O and porous NaF with a mass ratio of 1:3.0-3.5;

(8) S2. sintering the spherical particles in a vacuum environment at a temperature of 120-130° C. for 10-40 hours and at a temperature of 280-300° C. for 10-40 hours, respectively, to form an adsorbent intermediate with a NiCl.sub.2—NaF framework, wherein, a vacuum degree is less than or equal to 500 pa; and

(9) S3. treating the adsorbent intermediate by fluorine-nitrogen mixtures with high purity.

(10) As a further improvement, in step S1, test result shows that a well-controlled mass ratio of NiCl.sub.2.6H.sub.2O and porous NaF is favorable for ensuring a sufficient interaction between NiF.sub.2, a resultant formed after NiCl.sub.2 is fluorinated, and NaF, so as to minimize the adsorption of chlorine trifluoride. Therefore, preferably, spherical particles of NiCl.sub.2.6H.sub.2O and porous NaF are produced in a mass ratio of 1:3.1-3.3. In one embodiment, spherical particles of NiCl.sub.2.6H.sub.2O and porous NaF are produced in a mass ratio of 1:3.2.

(11) The porous NaF may be prepared by the following steps:

(12) S11. treating NaHF.sub.2 by a vacuum drying process to let at least part of hydrogen atoms escape from the NaHF.sub.2 molecule and form a loose and porous substance having properties of sodium fluoride; wherein, the drying temperature ranges 200-210° C., the drying time ranges 20-30 h, and vacuum degree is less than or equal to 500 pa. According to one embodiment, the drying temperature is about 205° C., the drying time is about 24 h, and the vacuum degree is about 100 pa.

(13) As a further improvement, in step S1, particle sizes of the spherical particles range 5-8 mm, which is favorable for the packing of adsorption towers to obtain larger porosity. As a further improvement, NiCl.sub.2 may undergo further treatment to form a polyfluorinated substance and nickel fluoride with a higher fluorine content.

(14) As a further improvement, in step S2, sintering in a stepped manner may prevent cracking of the spherical particles which may happen due to a sudden rise of temperature, thereby improving the yield of sintered products, and the specific surface area and pore volume of the sintered adsorbent particles are increased several times. Furthermore, thanks to the stepped sintering, the water molecules of NiCl.sub.2.6H.sub.2O and part of the H atoms carried by NaHF.sub.2 may be set free to form a loose and porous particle structure. In one embodiment, the spherical particles are sintered at a temperature of 125° C. for 24 hours and at a temperature of 290° C. for 24 hours, respectively. The vacuum degree is about 100 pa, the final BET specific surface area can reach 4.0756 m.sup.2.Math.g.sup.−1, and the pore volume can reach 0.000301 cm.sup.3.Math.g.sup.−1. In another embodiment, the spherical particles are sintered in a vacuum environment at a temperature of 130° C. for 24 hours and at a temperature of 280° C. for 24 hours, respectively. The vacuum degree is about 100 pa, the final BET specific surface area can reach 4.8995 m.sup.2.Math.g.sup.−1, and the pore volume can reach 0.000356 cm.sup.3.Math.g.sup.−1. In yet another embodiment, the spherical particles are sintered in a vacuum environment at a temperature of 120° C. for 24 hours and at a temperature of 300° C. for 24 hours, respectively. The vacuum degree is about 100 pa, the final BET specific surface area can reach 3.9781 m.sup.2.Math.g.sup.−1, and the pore volume can reach 0.000293 cm.sup.3.Math.g.sup.−1.

(15) As a further improvement, in step S3, the use of fluorine-nitrogen mixtures with high purity aims to let nickel chloride react with fluorine gas to form nickel fluoride. Nickel fluoride with higher fluorine content (in each molecule, one nickel atom combines two fluorine atoms) is introduced into sodium fluoride, and through the interaction between sodium fluoride molecules and nickel difluoride molecules, “molecules” of polyfluorine groups with a three-dimensional configuration similar to that of chlorine trifluoride are formed, while the bond length and bond angle with the chlorine trifluoride molecules are twisted and broken to certain extent, so as to achieve the purpose of separating sodium fluoride molecules and chlorine trifluoride molecules. The “molecules” of polyfluorine groups, when interacting with hydrogen fluoride molecules, are more likely to form weak intermolecular forces. By controlling the temperature of the mixture system, the formation of high polymers of hydrogen fluoride molecules is reduced, and the bimolecular association of chlorine trifluoride molecules is suppressed as well. Additionally, the repulsive force between these molecules with higher mobility and the “modified” sodium fluoride molecules also increases simultaneously, so that the “modified” sodium fluoride can reduce the adsorption rate of chlorine trifluoride and improve the adsorption rate of hydrogen fluoride. Nitrogen plays the role of diluting fluorine gas, preventing the potential risks that may occur due to the strong activity of fluorine gas. Tests have shown that fluorine gas is inactive with low concentration and would become risky with high concentration. Therefore, preferably, the fluorine-nitrogen mixtures with high purity may contain F.sub.2 with a volume fraction of 5-15% and N.sub.2 with a volume fraction of 85-95%. In one embodiment, the fluorine-nitrogen mixtures contain F.sub.2 with a volume fraction of 10% and N.sub.2 with a volume fraction of 90%.

(16) As a further improvement, in step S3, the step of treating the adsorbent intermediate by fluorine-nitrogen mixtures with high purity includes:

(17) fluorinating the adsorbent intermediate by the fluorine-nitrogen mixtures with high purity for 24-72 hours. In one embodiment, the adsorbent intermediate is fluorinated with the fluorine-nitrogen mixtures with high purity for 48 hours, and after the fluorination is completed, nitrogen purge is performed to remove the fluorine-nitrogen mixtures with high purity.

(18) According to another aspect of the present disclosure, a novel modified sodium fluoride adsorbent for special purpose is provided. The novel modified sodium fluoride adsorbent has a NiCl.sub.2—NaF framework, a BET specific surface area greater than or equal to 2 m.sup.2.Math.g.sup.−1, and a pore volume greater than or equal to 0.00015 cm.sup.3.Math.g.sup.−1. In one embodiment, the BET specific surface area of the novel modified sodium fluoride adsorbent can reach 4.8995 m.sup.2.Math.g.sup.−1, and the pore volume can reach 0.000356 cm.sup.3.Math.g.sup.−1.

(19) Referring to FIGS. 1-2, the conventional sodium fluoride has a compact arrangement of crystals with a small specific surface area, which is unfavorable for an effective adsorption of hydrogen fluoride (conventional sodium fluoride has a BET specific surface area as low as 0.6591 m.sup.2.Math.g.sup.−1 and a pore volume as low as 0.000054 cm.sup.3.Math.g.sup.−1). The novel modified sodium fluoride adsorbent for special purpose has a sheet-like structure with larger specific surface area, and the number of pores is also increased compared with the conventional sodium fluoride, which can effectively improve the adsorption rate of hydrogen fluoride.

(20) According to yet another embodiment of the present disclosure, an application of the above-mentioned novel modified sodium fluoride adsorbent for special purpose is provided, in which the modified sodium fluoride adsorbent is used for the separation of chlorine trifluoride and hydrogen fluoride.

(21) In the present disclosure, orthogonal tests with the following processing conditions are performed to separate chlorine trifluoride with hydrogen fluoride:

(22) TABLE-US-00001 TABLE 1 Orthogonal test factors test factors temperature pressure flow rate (° C.) (MPa) (L/min) level A B C 1  20 0.2 0.2 2  40 0.4 0.4 3  60 0.6 0.6 4  80 0.8 0.8 5 100 1.0 1.0

(23) TABLE-US-00002 TABLE 2 Results of the orthogonal tests Flow rate Flow Components Components after HF CIF.sub.3 Temperature Pressure rate before after adsorption adsorption adsorption Number ° C. MPa L/min adsorption adsorption L/min rate % rate % 1 20 0.2 0.2 0.832CIF.sub.3 0.8419CIF.sub.3 0.19309  66.65 2.31 0.023HF 0.0079HF 0.145 others 0.1502 others 2 20 0.4 0.4 0.833CIF.sub.3 0.8422CIF.sub.3 0.386988 65.33 2.18 0.022HF 0.0079HF 0.145 others 0.1499 others 3 20 0.6 0.6 0.833CIF.sub.3 0.8434CIF.sub.3 0.580135 60.45 2.10 0.024HF 0.0087HF 0.143 others 0.1479 others 4 20 0.8 0.8 0.831CIF.sub.3 0.8391CIF.sub.3 0.777162 57.62 1.91 0.022HF 0.0096HF 0.147 others 0.1513 others 5 20 1.0 1.0 0.830CIF.sub.3 0.8383CIF3 0.972359 53.27 1.79 0.024HF 0.0115HF 0.146 others 0.1502 others 6 40 0.2 0.4 0.832CIF.sub.3 0.8423CIF.sub.3 0.385958 69.50 2.31 0.022HF 0.0063HF 0.146 others 0.1514 others 7 40 0.4 0.6 0.834CIF.sub.3 0.8443CIF.sub.3 0.579198 68.42 2.27 0.023HF 0.0075HF 0.143 others 0.1482 others 8 40 0.6 0.8 0.833CIF.sub.3 0.8422CIF.sub.30. 0.773832 65.38 2.20 0.022HF 0079HF 0.145 others 0.1499 others 9 40 0.8 1.0 0.834CIF.sub.3 0.8446CIF.sub.3 0.966501 63.27 2.12 0.025HF 0.0095HF 0.141 others 0.1459 others 10 40 1.0 0.2 0.835CIF.sub.30.0 0.8475CIF.sub.3 0.192168 76.88 2.48 24HF 0.141 0.0058HF others 0.1467 others 11 60 0.2 0.6 0.832CIF.sub.3 0.8445CIF.sub.3 0.575226 82.21 2.69 0.023HF 0.0043HF 0.145 others 0.1512 others 12 60 0.4 0.8 0.833CIF.sub.3 0.8464CIF.sub.3 0.76667  79.35 2.62 0.025HF 0.0054HF 0.142 others 0.1482 others 13 60 0.6 1.0 0.835CIF.sub.3 0.8454CIF.sub.3 0.962229 77.28 2.58 0.021HF 0.0049HF 0.144 others 0.1497 others 14 60 0.8 0.2 0.833CIF.sub.3 0.8491CIF.sub.3 0.190794 88.62 2.76 0.026HF 0.0031HF 0.141 others 0.1478 others 15 60 1.0 0.4 0.834CIF.sub.3 0.8497C1F.sub.3 0.381927 86.53 2.72 0.026HF 0.0037HF 0.140 others 0.1466 others 16 80 0.2 0.8 0.833CIF.sub.3 0.8449CIF.sub.3 0.766867 87.34 2.77 0.021HF 0.0027HF 0.146 others 0.1604 others 17 80 0.4 1.0 0.833CIF.sub.3 0.8454CIF3 0.958638 85.40 2.71 0.022HF 0.0033HF 0.145 others 0.1513 others 18 80 0.6 0.2 0.831CIF.sub.3 0.8455C1F.sub.3 0.1908   93.61 2.91 0.023HF 0.0015HF 0.146 others 0.1503 others 19 80 0.8 0.4 0.831CIF.sub.3 0.8460CIF.sub.3 0.38165  91.78 2.87 0.024HF 0.0021HF 0.145 others 0.1519 others 20 80 1.0 0.6 0.832CIF.sub.3 0.8443CIF.sub.3 0.574513 90.15 2.83 0.021HF 0.0022HF 0.147 others 0.1535 others 21 100 0.2 1.0 0.832CIF.sub.3 0.0.8443CIF.sub.3 0.957522 90.81 2.93 0.023HF 0.0022HF 0.145 others 0.1535 others 22 100 0.4 0.2 0.833CIF.sub.3 0.8474CIF.sub.3 0.19064  98.01 3.03 0.022HF 0.0005HF 0.145 others 0.1521 others 23 100 0.6 0.4 0.831CIF.sub.3 0.8485CIF.sub.3 0.380001 96.42 3.00 0.026HF 0.0010HF 0.143 others 0.1505 others 24 100 0.8 0.6 0.831CIF.sub.3 0.8489CIF.sub.3 0.569819 94.58 2.98 0.027HF 0.0015HF 0.142 others 0.1496 others 25 100 1.0 0.8 0.833CIF.sub.3 0.8474CIF.sub.3 0.763089 93.04 2.97 0.023HF 0.0016HF 0.144 others 0.1510 others K1 60.66 79.30 84.80 average K2 68.69 79.31 80.94 average K3 82.80 78.63 79.16 average K4 89.66 79.17 76.55 average K5 94.57 79.97 74.01 average Range (R) 33.91 1.34 10.79 Priorities A > C > B Excellent A5 B5 C1 level Excellent A5B4C1, refers to optimal process conditions: combination temperature 100° C., pressure 1.0 MPa, flow rate 0.2 L/min

(24) According to table 2 presented above, the novel modified sodium fluoride adsorbent for special purpose provided by the present disclosure can effectively separate chlorine trifluoride and hydrogen fluoride molecules, and the optimal adsorption rate of hydrogen fluoride is upgraded to more than 98%. While, the optimal adsorption rate of chlorine trifluoride is lowered down to around 3%. Additionally, the novel modified sodium fluoride adsorbent exhibits high activity and high adsorption capacity under various working conditions. Moreover, the modified sodium fluoride adsorbent may be produced by simple processes with low production cost, good economic benefits, and can be industrially produced. Lastly, the modified sodium fluoride adsorbent has a long service life. Tests show that the optimal adsorption rate of hydrogen fluoride can still be maintained at around 98%, and the best adsorption rate of chlorine trifluoride can still be maintained at around 3%, after the modified sodium fluoride adsorbent is reused in 100 tests.

(25) The described embodiments are only the preferable embodiments of the present disclosure, which do not limit the present disclosure. Without departing from the spirit and principle of the present disclosure, the present disclosure may have various modifications and changes to those of ordinary skill in the art, and any changes, equivalent substitutions, and improvements derived from the present disclosure should be considered as falling within the scope of the present disclosure.