Vermicompost made of aquatic plants and preparation method and use thereof

Abstract

The present disclosure provides vermicompost made of aquatic plants and a preparation method of the vermicompost. The preparation method includes: mixing aquatic plant residues and fresh cow dung according to a proportion, and crushing the aquatic plant residues while stirring until even mixing; adding earthworms to a mixture of the aquatic plant residues and the cow dung, where the earthworms transform the mixture of the aquatic plant residues and the cow dung in a forest at 15-35? C., and moisture in the mixture is maintained at 65-75% in the process; and after 35-45 days, separating the earthworms and vermicompost, and drying the vermicompost to obtain the vermicompost made of aquatic plants.

Claims

1. A preparation method of vermicompost made of aquatic plants, comprising: mixing aquatic plant residues and fresh cow dung according to a 1:1 weight ratio, and crushing the aquatic plant residues while stirring until even mixing to obtain a mixture; adding earthworms to the mixture of the aquatic plant residues and the cow dung, wherein the earthworms transform the mixture of the aquatic plant residues and the cow dung in a forest at 15-35? C., and moisture in the mixture is maintained at 65-75% in the process; and after 35-45 days, separating the earthworms and vermicompost, and drying the vermicompost to obtain the vermicompost made of aquatic plants; wherein the aquatic plant residues are lotus leaves or cress.

2. The preparation method of vermicompost made of aquatic plants according to claim 1, wherein the mixture of the aquatic plant residues and the cow dung and the earthworms have a weight ratio of 20:1.

3. The preparation method of vermicompost made of aquatic plants according to claim 1, wherein the vermicompost has a moisture content less than or equal to 30%.

4. The preparation method of vermicompost made of aquatic plants according to claim 1, wherein the aquatic plant residues are stirred and crushed with a shovel or forklift.

5. The preparation method of vermicompost made of aquatic plants according to claim 1, wherein the earthworm is Eisenia foetida.

6. Vermicompost made of aquatic plants prepared by the preparation method according to claim 1, wherein the vermicompost comprises aquatic plant residues and cow dung in a weight ratio of 1:1, and wherein the aquatic plant residues are lotus leaves or cress.

7. The vermicompost made of aquatic plants according to claim 6, wherein the mixture of the aquatic plant residues and the cow dung and the earthworms have a weight ratio of 20:1.

8. The vermicompost made of aquatic plants according to claim 6, wherein the vermicompost has a moisture content less than or equal to 30%.

9. The vermicompost made of aquatic plants according to claim 6, wherein the aquatic plant residues are stirred and crushed with a shovel or forklift.

10. The vermicompost made of aquatic plants according to claim 6, wherein the earthworm is Eisenia foetida.

11. A method for removing copper-zinc compound pollution from a water body, comprising putting the vermicompost made of aquatic plants according to claim 6 into a water body polluted by a copper-zinc compound.

12. The method according to claim 11, wherein the mixture of the aquatic plant residues and the cow dung and the earthworms have a weight ratio of 20:1.

13. The method according to claim 11, wherein the vermicompost has a moisture content less than or equal to 30%.

14. The method according to claim 11, wherein the aquatic plant residues are stirred and crushed with a shovel or forklift before putting the vermicompost made of aquatic plants according to claim 6 into a water body polluted by a copper-zinc compound.

15. The method according to claim 11, wherein the earthworm is Eisenia foetida.

16. The method according to claim 11, wherein the vermicompost made of aquatic plants has a dosage of 1.0-2.0 g L.sup.?1.

17. The method according to claim 12, wherein the vermicompost made of aquatic plants has a dosage of 1.0-2.0 g L.sup.?1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 shows removal effects of vermicompost made of aquatic plants on copper and zinc in a compound polluted water body;

(2) FIG. 2 shows effects of added aquatic plants on quality of earthworms;

(3) FIG. 3 shows removal effects of dosages of the vermicompost made of aquatic plants on the copper (A) and the zinc (B) in the compound polluted water body;

(4) FIG. 4 shows effects of dosages of different vermicompost made of aquatic plants on concentrations of the copper (A) and the zinc (B) in the compound polluted water body;

(5) FIG. 5 shows removal effects of cress vermicompost on copper and zinc in their single and compound polluted water bodies; and

(6) FIG. 6 shows proportions of forms of copper and zinc adsorbed by the cress vermicompost in the compound polluted water body.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(7) The present disclosure is further described below with reference to examples. The following examples are only used for describing the technical solutions of the present disclosure more clearly, and are not intended to limit the protection scope of the present disclosure.

(8) Based on the enterprise standards for wastewater discharge involving heavy metals, CuSO.sub.4 and ZnCl.sub.2 are used to prepare a copper-zinc compound polluted water body, and copper and zinc have concentrations of 2.0 and 8.0 mg L.sup.?1 respectively.

EXAMPLE 1

Preparation of Lotus Leaf Vermicompost and its Removal Effect on Copper-Zinc Compound Pollution in a Water Body

(9) A preparation method of lotus leaf vermicompost included the following steps.

(10) (1) Fresh lotus leaves and fresh cow dung were mixed according to a proportion. The fresh lotus leaves and the cow dung were each 50% by weight. The lotus leaves were crushed with a shovel or forklift while stirring until even mixing.

(11) (2) Eisenia foetida was added to a mixture of the fresh lotus leaves and the cow dung. The mixture of the fresh lotus leaves and the cow dung and the earthworms had a weight ratio of 20:1. The earthworms transformed the mixture of the fresh lotus leaves and the cow dung in a forest at 15? C., and moisture in the mixture was maintained at 65% in the process.

(12) (3) After 45 days, the earthworms and vermicompost were separated, and the vermicompost was dried to obtain the lotus leaf vermicompost.

(13) The crude ash content of the earthworms was significantly reduced, from 24.24% of earthworms produced from pure cow dung to 13.07% (FIG. 2), reaching the level I of fishmeal (GB/T 19164-2003). The vermicompost had a pH of 9.08-9.12, which was 8.63% lower than that of vermicompost produced from pure cow dung on average. The dosages of the vermicompost were set as 0, 1.0, 2.0, 4.0, 5.0, 10.0, 15.0, 20.0, 25.0 and 30.0 g L.sup.?1. The vermicompost was shaken in a constant temperature shaker at 25? C. for 24 h and centrifuged, and concentrations of the copper and zinc in supernatant were tested. The results showed that the removal rates of copper and zinc from the water body by the vermicompost produced from pure cow dung were 70.93-86.14% and 90.06-96.17%, respectively, and with the increase of the dosage, the removal rate of copper decreased while that of zinc increased (FIG. 3). The addition of vermicompost produced from lotus leaves significantly improved the removal effect of copper and zinc from the water body, and the maximum removal rates reached 93.88% and 98.22% respectively. The optimum dosage of the lotus leaf vermicompost was 2 g L.sup.?1. At this time, copper and zinc in equilibrium liquid had concentrations of 0.13 and 0.25 mg L.sup.?1 respectively (FIG. 4), reaching the level II of surface water (GB 3838-2002).

EXAMPLE 2

Preparation of Cress Vermicompost and its Removal Effect on Copper-Zinc Compound Pollution in a Water Body

(14) A preparation method of cress vermicompost included the following steps.

(15) (1) Fresh cress and fresh cow dung were mixed according to a proportion. The fresh cress and the cow dung were each 50% by weight. The cress was crushed with a shovel or forklift while stirring until even mixing.

(16) (2) Eisenia foetida was added to a mixture of the fresh cress and the cow dung. The mixture of the fresh cress and the cow dung and the earthworms had a weight ratio of 20:1. The earthworms transformed the mixture of the fresh cress and the cow dung in a forest at 35? C., and moisture in the mixture was maintained at 75% in the process.

(17) (3) After 35 days, the earthworms and vermicompost were separated, and the vermicompost was dried to obtain the cress vermicompost.

(18) Compared with earthworms produced from pure cow dung, the quality of earthworms produced by adding cress decreased slightly (FIG. 2). The vermicompost had a pH of 9.90-9.92, which was equivalent to that of vermicompost produced from pure cow dung. The dosages of the vermicompost were set as 1.0, 2.0, 4.0, 5.0, 10.0, 15.0, 20.0, 25.0 and 30.0 g L.sup.?1. The vermicompost was shaken in a constant temperature shaker at 25? C. for 24 h and centrifuged, and concentrations of the copper and zinc in supernatant were tested. The results showed that compared with the vermicompost produced from pure cow dung, the vermicompost produced by adding cress improved the overall removal effects of copper and zinc from the water body (FIG. 3). With the increase of the dosage of the cress vermicompost, the removal efficiency of copper from the water body showed a downward trend, and the larger removal rates (93.56% and 93.87%) were reached when the dosages were 1.0 and 2.0 g L.sup.?1. The removal rate of zinc from the water body increased with its dosage, but there was no significant difference (p>0.05) in the removal efficiency of zinc from the water body among the last 8 dosages, which was significantly higher than that of 1.0 g L.sup.?1. It can be seen that the optimum dosage of the cress vermicompost was 2.0 g L.sup.?1. At this time, copper and zinc in equilibrium liquid had concentrations of 0.12 and 0.24 mg L.sup.?1 respectively (FIG. 4), reaching the level II of surface water (GB 3838-2002).

EXAMPLE 3

Lotus Leaf and Cress Combined Vermicompost and its Removal Effect on Copper-Zinc Compound Pollution in a Water Body

(19) A preparation method of lotus leaf and cress combined vermicompost included the following steps.

(20) (1) Fresh lotus leaves, cress, and fresh cow dung were mixed according to a proportion. The fresh lotus leaves, the cress, and the cow dung were 25%, 25%, and 50% by weight. The lotus leaves and the cress were crushed with a shovel or forklift while stirring until even mixing.

(21) (2) Eisenia foetida was added to a mixture of the fresh lotus leaves, the cress, and the cow dung. The mixture of the fresh lotus leaves, the cress, and the cow dung and the earthworms had a weight ratio of 20:1. The earthworms transformed the mixture of the fresh lotus leaves, the cress, and the cow dung in a forest at 25? C., and moisture in the mixture was maintained at 70% in the process.

(22) (3) After 40 days, the earthworms and vermicompost were separated, and the vermicompost was dried to obtain the lotus leaf and cress combined vermicompost.

(23) Compared with earthworms produced from pure cow dung, the quality of earthworms produced by adding a combination of cress and lotus leaves was significantly improved (FIG. 2). The increase rate of crude protein was 14.93%, while the decrease rates of crude fat and crude ash were 22.43% and 63.61% respectively, reaching the level I of fishmeal (GB/T 19164-2003). The lotus leaf and cress combined vermicompost had a pH of 10.02-10.06, which was equivalent to that of vermicompost produced from pure cow dung. The dosages of the lotus leaf and cress combined vermicompost were set as 0, 1.0, 2.0, 4.0, 5.0, 10.0, 15.0, 20.0, 25.0 and 30.0 g L.sup.?1. The vermicompost was shaken in a constant temperature shaker at 25? C. for 24 h and centrifuged, and concentrations of the copper and zinc in supernatant were tested. The results showed that compared with the vermicompost produced from pure cow dung, the vermicompost produced by adding a combination of cress and lotus leaves improved the overall removal effects of copper and zinc from the water body (FIG. 3). With the increase of the dosage of the lotus leaf and cress combined vermicompost, the removal efficiency of copper from the water body showed a downward trend, and the larger removal rates (93.83% and 93.84%) were reached when the dosages were 1.0 and 2.0 g L.sup.?1. The removal rate of zinc from the water body is relatively stable and not affected by its dosage (except 1.0 g L.sup.?1). It can be seen that the optimum dosage of the lotus leaf and cress combined vermicompost was 2.0 g L.sup.?1. At this time, copper and zinc in equilibrium liquid had concentrations of 0.13 and 0.25 mg L.sup.?1 respectively (FIG. 4), reaching the level II of surface water (GB 3838-2002).

EXAMPLE 4

Removal Effect and Mechanism of Cress Vermicompost on Copper, Zinc, and Copper-Zinc Compound Pollution

(24) A preparation method of cress vermicompost included the following steps.

(25) (1) Fresh cress and fresh cow dung were mixed according to a proportion. The fresh cress and the cow dung were each 50% by weight. The cress was crushed with a shovel or forklift while stirring until even mixing.

(26) (2) Eisenia foetida was added to a mixture of the fresh cress and the cow dung. The mixture of the fresh cress and the cow dung and the earthworms had a weight ratio of 20:1. The earthworms transformed the mixture of the fresh cress and the cow dung in a forest at 35? C., and moisture in the mixture was maintained at 75% in the process.

(27) (3) After 35 days, the earthworms and vermicompost were separated, and the vermicompost was dried to obtain the cress vermicompost.

(28) 2.0 g of cress vermicompost were put into three heavy metal solutions: a single copper solution (4.0 mg L.sup.?1), a single zinc solution (2.0 mg L.sup.?1), and a copper-zinc compound polluted solution (4.0 mg Cu L.sup.?1 and 2.0 mg Zn L.sup.?1). After 24 hours of action, the removal rates of copper and zinc by the cress vermicompost were 89.31-89.81% and 97.47-99.06% respectively (FIG. 5). Compared with single copper and zinc pollution, the removal effect of the cress vermicompost on copper and zinc in the copper-zinc compound polluted solution was not reduced, but improved slightly. It can be seen that the effect of the cress vermicompost on copper and zinc (including compound pollution) in the water body was obvious.

(29) After drying, the cress vermicompost adsorbed with copper and zinc was extracted step by step with water, 0.5 mol L.sup.?1 MgCl.sub.2, 1.0 mol L.sup.?1 NaOAc and mixed acid (9 ml of 36% HC1 and 3 ml of 70% HNO.sub.3) to obtain copper and zinc in a water-soluble/physically bound state, an ion-exchange state, an acid-soluble state, and a residual state. The results showed that there were significant differences in the binding forms of copper and zinc in the cress vermicompost (FIG. 6). The adsorbed copper was mainly in an acid-soluble state and a residual state, accounting for 20.47% and 74.89% respectively. The adsorbed zinc was mainly in an ion-exchange state, an acid-soluble state and a residual state, accounting for 26.65%, 55.56%, and 16.55% respectively. This also showed that the cress vermicompost was more closely bound to copper.

(30) The above described are preferred implementations of the present disclosure, and it should be noted that for those of ordinary skill in the art, various improvements and modifications may be made without departing from the principles of the present disclosure. These improvements and modifications should be regarded as falling within the protection scope of the present disclosure.