NANO SIZE CRYSTAL ZSM-5 AND ITS PREPARATION AND APPLICATIONS THEREOF

Abstract

The present invention provides a novel, cost-effective and simple synthetic process for preparing a nano ZSM-5 catalyst which is further utilized in fluid catalytic cracking of feedstock oil containing organic compounds. The nano-ZSM-5 catalyst shows higher selectivity towards olefines and low selectivity towards LCO and bottoms.

Claims

1. A process for synthesising a nano ZSM-5 catalyst, comprising: (i) adding an aluminium precursor, a quaternary ammonium template and a size controlling agent in an aqueous basic solution in a hydrothermal reactor to obtain a first solution; (ii) adding a silica precursor to the first solution to obtain a second solution; (iii) stirring the second solution and then conducting aging to form a reaction mixture; (iv) heating the reaction mixture in the hydrothermal reactor followed by cooling, then filtering, washing and drying to obtain a solid product; and (v) calcining the solid product to obtain a calcined product comprising the nano ZSM-5 catalyst, wherein the size controlling agent comprises phosphino carboxylic acid.

2. The process as claimed in claim 1 further comprising the step of conducting an ion exchange treatment of the calcined product to convert to H.sup.+-form.

3. The process as claimed in claim 1, wherein the aluminium precursor is selected form aluminium nitrate, aluminium sulfate, sodium aluminate, aluminium propoxide, and aluminium oxide.

4. The process as claimed in claim 1, wherein the wherein the quaternary ammonium templet is selected from tetrapropyl ammonium bromide, tetrapropyl ammonium hydroxide, and cetyl ammonium bromide.

5. The process as claimed in claim 1, wherein the silica precursor is selected form Si-tetraethyl ortho silicate, colloidal silica, and sodium silicate.

6. The process as claimed in claim 1, wherein the aging of the second solution is conducted at variable temperature and time and is performed in two steps comprising: (i) first step aging is conducted at a temperature in the range of 25 to 100? C. for 0.5 to 5 hrs; and (ii) second step aging is conducted at a temperature in the range of 35 to 120? C. for 0.5 to 8 hrs.

7. The process as claimed in claim 1, wherein the reaction mixture is heated in hydrothermal reactor at a temperature in a range of 140-190? C. for 12-56 hrs.

8. The process as claimed in claim 1, wherein the calcination of the solid product is done at a temperature in the range of 500-600? C. for 2-6 hrs.

9. The process as claimed in claim 2, wherein the ion exchange treatment is done with ammonium salt, wherein the ammonium salt is selected from ammonium sulfate, ammonium chloride, ammonium nitrate, and ammonium acetate.

10. A nano ZSM-5 catalyst obtained by the process as claimed in claim 1, comprising of self-assembled ZSM-5 nanoparticles of size 25-250 nm, BET surface area of nano ZSM-5 catalyst is 350-500 m.sup.2/g and micropore volume is 0.20-0.40 cc/g.

11. A process for fluid catalytic cracking of feedstock oil to a conversion product, the process comprising contacting the feedstock oil with a catalyst under fluid catalytic cracking condition to obtain the conversion product, wherein the catalyst comprising an equilibrium catalyst and a nano ZSM-5 additive formulation; and wherein the nano ZSM-5 additive formulation is prepared by reacting the nano ZSM-5 catalyst obtained according to the process of claim 1, with clay, colloidal silica and alumina.

12. The process as claimed in claim 11, wherein the feedstock oil is a vacuum gas oil comprising saturates, aromatics, resins, and asphaltenes, wherein the catalyst comprises 90 to 99 wt. % of refinery-based FCC equilibrium catalyst and 10 to 1 wt. % of nano ZSM-5 additive formulation; wherein the catalyst to oil ratio is in the range of 4 to 6; and wherein the conversion product comprises dry gas (DG), liquefied petroleum gas (LPG), gasoline, heavy naphtha, light cycle naphtha, clarified oil and coke.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0028] FIG. 1. SEM images of nano ZSM-5 and micron ZSM-5.

ABBREVIATIONS

[0029] ZSM-5Zeolite Socony Mobil-5

[0030] FCCFluid catalytic cracking

[0031] LPGLiquefied petroleum gas

[0032] LCOLight cycle oil

[0033] ACE-MATAdvanced Cracking EvaluationMicro-Activity test

DETAILED DESCRIPTION OF THE INVENTION

[0034] For the purpose of promoting an understanding of the principles of the invention, reference will now be made to the embodiments in the specific language will be used to describe the same. It will nevertheless be understood that no limitation of the scope of the invention is thereby intended, such alterations and further modifications in the illustrated process, and such further applications of the principles of the invention as illustrated therein being contemplated as would normally occur to one skilled in the art to which the invention relates. Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skilled in the art to which this invention belongs. The composition, methods, and examples provided herein are illustrative only and not intended to be limiting.

[0035] The articles a, an and the are used to refer to one or to more than one (i.e., to at least one) of the grammatical object of the article.

[0036] The terms comprise and comprising are used in the inclusive, open sense, meaning that additional elements may be included. It is not intended to be construed as consists of only.

[0037] Throughout this specification, unless the context requires otherwise the word comprise, and variations such as comprises and comprising, will be understood to imply the inclusion of a stated element or step or group of element or steps but not the exclusion of any other element or step or group of element or steps.

[0038] Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. Although any methods and materials similar or equivalent to those described herein can be used in the practice or testing of the disclosure, the preferred methods, and materials are now described. All publications mentioned herein are incorporated herein by reference.

[0039] The terminology and structure employed herein is for describing, teaching, and illuminating some embodiments and their specific features and elements and does not limit, restrict, or reduce the spirit and scope of the invention.

[0040] The present invention provides a novel cost-effective process for synthesis of nano ZSM-5. The prepared nano ZSM-5 shows higher selectivity towards olefines such as propylene, LPG, and lower LCO selectivity in ACE-MAT evaluation. In a feedstock mixture of n-hexane, cycloalkanes, napthenes, and BTX, nano ZSM-5 catalyst have ?15% higher olefins selectivity, ?15% lower BTX selectivity and ?14% lower coke selectivity.

[0041] The present invention provides, a process for synthesising a nano ZSM-5 catalyst, comprising: [0042] (i) adding an aluminium precursor, a quaternary ammonium template and a size controlling agent in an aqueous basic solution in a hydrothermal reactor to obtain a first solution; [0043] (ii) adding a silica precursor to the first solution to obtain a second solution; [0044] (iii) stirring the second solution and then conducting aging to form a reaction mixture; [0045] (iv) heating the reaction mixture in the hydrothermal reactor followed by cooling, then filtering, washing and drying to obtain a solid product; [0046] (v) calcining the solid product to obtain a calcined product comprising the nano ZSM-5 catalyst; and wherein the size controlling agent comprises phosphino carboxylic acid.

[0047] In one of the features of the present invention, the phosphino carboxylic acid in the second solution provides a unique combination having a ratio of elements as Si+Al/P in the range of 100-2500 moles.

[0048] In one of the features of the present invention, the process described above further comprising the step of conducting an ion exchange treatment of the calcined product to convert to H.sup.+-form. In yet another feature of the present invention, the ion exchange treatment is done with ammonium salt to convert nano-ZSM-5 from Na.sup.+ form to NH.sub.4.sup.+ form, wherein the ammonium salt is selected from ammonium sulfate, ammonium chloride, ammonium nitrate, and ammonium acetate. Prepared, we need to exchange the same.

[0049] In one of the features of the present invention, the aluminium precursor is selected form aluminium nitrate, aluminium sulfate, sodium aluminate, aluminium propoxide, and aluminium oxide.

[0050] In another feature of the present invention, the aqueous basic solution is prepared by dissolving base in water. The base is selected from NaOH and KOH.

[0051] In yet another feature of the present invention, the quaternary ammonium templet is tetrapropyl ammonium bromide, tetrapropyl ammonium hydroxide, and cetyl ammonium bromide.

[0052] In yet another feature of the present invention, the silica precursor is selected form Si- tetraethyl ortho silicate, colloidal silica, and sodium silicate.

[0053] In one of the features of the present invention, the aging of the second solution is conducted at variable temperature and time and is performed in two steps comprising: [0054] (i) first step aging is conducted at a temperature in the range of 25 to 100? C. for 0.5 to 5 hrs; and [0055] (ii) second step aging is conducted at a temperature in the range of 35 to 120? C. for 0.5 to 8 hrs.

[0056] In another feature of the present invention, the reaction mixture is heated in hydrothermal reactor at a temperature in a range of 140-190? C. for 12-56 hrs.

[0057] In yet another feature of the present invention, the entire reaction in the hydrothermal reactor is agitated at a speed in the range of 200-1000 rpm.

[0058] In yet another feature of the present invention, the calcination of the solid product is done at a temperature in the range of 500-600? C. for 2-6 hrs.

[0059] The present invention provides, a nano ZSM-5 catalyst comprising of self-assembled ZSM-5 nanoparticles of size 25-250 nm.

[0060] In another feature of the present invention, the BET surface area of nano ZSM-5 catalyst is 350-500 m.sup.2/g and micropore volume is 0.20-0.40 cc/g.

[0061] The present invention also provides, a process for fluid catalytic cracking of feedstock oil to a conversion product, the process comprising contacting the feedstock oil with a catalyst under fluid catalytic cracking condition to obtain the conversion product, wherein the catalyst comprising an equilibrium catalyst and a nano ZSM-5 additive formulation,

[0062] wherein the nano ZSM-5 additive formulation is prepared by reacting the nano ZSM-5 as defined above with clay, colloidal silica and alumina.

[0063] In one feature of the present invention, the catalyst comprises of 90 to 99 wt. % of refinery-based FCC equilibrium catalyst and 10 to 1 wt. % of nano ZSM-5 additive formulation.

[0064] In another feature of the present invention, the ratio of catalyst to oil ratio is in the range of 4 to 6.

[0065] In another feature of the present invention, the feedstock oil is a vacuum gas oil comprising saturates, aromatics, resins, and asphaltenes.

[0066] In yet another feature of the present invention, the conversion product comprises dry gas (DG), liquefied petroleum gas (LPG), gasoline, heavy naphtha, light cycle naphtha, clarified oil and coke.

EXAMPLES

[0067] The present disclosure with reference to the accompanying examples describes the present invention. However, those of skill in the art should, in light of the present disclosure, appreciate that many changes can be made in the specific embodiments which are disclosed and still obtain a like or similar result without departing from the spirit and scope of the invention. It is understood that the examples are provided for the purpose of illustrating the invention only and are not intended to limit the scope of the invention in any way.

Example 1: Nano ZSM-5

[0068] In a 1 Littre PARR reactor, approximately 16 g of NaOH is dissolved in 300 g water. To this solution, 20 g of aluminium precursor is added and stirred for 10 min followed by addition of 25 g of quaternary ammonium template and 0.25 g of phosphino carboxylic acid. Followed by addition of 120 g of silica precursor. The complete solution is stirred and aged at 60? C. for 2 h, and then aged at 100? C. for 6 h and later entire solution is hydrothermally treated at 170? C. for 2 days. After completion of reaction time, stop the reactor heating and allow the reactor to natural cooling. Speed of agitation in PARR for entire experiment is 550 rpm. After the synthesis, filter the solution through whatmann filter paper and wash with copious amount of water, dried and powdered. Calcine the entire powder at 550? C. for 4 hours to remove all the templates and other impurities. The material is ion exchanged with ammonium salt to convert to H.sup.+-form. SEM image of nano ZSM-5 is shown in FIG. 1. The physico-chemical properties of the nano-ZSM-5 is given in Table 1.

Example 2: Nano ZSM-5

[0069] In a 1 Littre PARR reactor, approximately 16 g of NaOH is dissolved in 300 g water. To this solution, 20 g of aluminium precursor is added and stirred for 10 min followed by addition of 25 g of quaternary ammonium template and 0.50 g of phosphino carboxylic acid. Followed by addition of 120 g of silica precursor. The complete solution is stirred and aged at 60? ? C. for 2 h, and then aged at 100? C. for 6 h and later entire solution is hydrothermally treated at 170? C. for 2 days. After completion of reaction time, stop the reactor heating and allow the reactor to natural cooling. Speed of agitation in PARR for entire experiment is 550 rpm. After the synthesis, filter the solution through whatmann filter paper and wash with copious amount of water, dried and powdered. Calcine the entire powder at 550? C. for 4 hours to remove all the templates and other impurities. The material is ion exchanged with ammonium salt to convert to H.sup.+-form. The physico-chemical properties of the nano-ZSM-5 is given in Table 1.

Example 3: Micron ZSM-5

[0070] Micron ZSM-5 is prepared through similar synthesis method as described in example 1, except the size controlling agent phosphino carboxylic acid is not added into the reaction mixture and without aging steps.

[0071] SEM image of micron ZSM-5 is shown in FIG. 1. The physico-chemical properties of the micron ZSM-5 is given in Table 1.

TABLE-US-00001 TABLE 1 Physico-chemical properties of as-synthesized Nano ZSM-5 and micron ZSM-5 Nano ZSM-5 Nano ZSM-5 Micron ZSM-5 (As per (As per (As per Properties Example-1) Example-2) Example-3) BET surface area (m.sup.2/g) 440 425 385 External surface area (m.sup.2/g) 253 243 124 Micropore surface area (m.sup.2/g) 187 182 261 Micropore volume (cc/g) 0.30 0.29 0.24 Total acidity (?mol/g) 903 890 726 Crystallinity (from PXRD) 96% 96% 100%

Example 4: Nano ZSM-5 Additive Preparation

[0072] Nano ZSM-5 additive formulation is prepared by using nanocrystalline ZSM-5 of example 1 or 2, clay, colloidal silica and alumina in spray dryer.

Example 5: Micron Size ZSM-5 Additive Preparation

[0073] Micron ZSM-5 additive formulation is prepared by using Micron ZSM-5, clay, colloidal silica and alumina in spray dryer.

Example 6: Pre-Treatment of Nano ZSM-5 Additive by Hydrothermal Deactivation Method

[0074] In order to maintain the desired level of conversion (feed to useful products such as dry gas (DG), liquefied petroleum gas (LPG), gasoline, heavy naphtha, light cycle naphtha, clarified oil and coke) in the FCC unit, an equilibrium catalyst and along with ZSM-5 additive (E-CAT) is continuously removed from the regenerator and added with a fresh catalyst. Accurate prediction of catalyst deactivation rate which happens in the commercial units under real operating conditions in the laboratory is essential not only to the catalyst management strategy but also to the evaluation process and selection of catalysts. Catalyst deactivation of lab developed additives were carried out at 815? C. for 5 hours with 80% steaming recipe in Metal Cyclic Deactivation unit before performance evaluation.

Feedstock Characterization

[0075] The feed used in the present study is vacuum gas oil (VGO) and its properties are listed in below table 2.

TABLE-US-00002 TABLE 2 Vacuum Gas Oil Feed Properties Properties VGO Density at 15? C., gm/cc 0.9171 Sulphur, wt % 1.969 CCR, wt % 0.6 Pour point, ? C. 45 Kinematic viscosity @100? C., cSt 7.742 ASTM-7169 Distillation, wt % IBP 283 5 345 10 365 30 404 50 429 70 457 90 506 95 529 SARA, wt % Saturates 57.1 Aromatics 33.3 Resin 9.4 Asphaltenes 0.2

Example 7: Performance Evaluation Results

[0076] Advanced Cracking Evaluation (ACE)Micro-Activity test (MAT) unit (with online RGA) was used to measure the micro-activity of steam deactivated nano ZSM-5 and micron ZSM-5 additive with reference catalyst to get their relative activity/selectivity. The results show conversion and product yields at par with the reference additive as shown in below table 3. The product yields are compared with the reference catalyst, and it was observed the nano ZSM-5 additive showed higher conversion, LPG and propylene selectivity.

[0077] The detailed results are given in table 3.

TABLE-US-00003 TABLE 3 Product yields E-CAT (96%) + E-CAT (96%) + E-CAT (96%) E-CAT (96%) + Micron ZSM-5 Nano ZSM-5 + Micron ZSM-5 Nano ZSM-5 Catalyst Name additive (4%) additive (4%) additive (4%) additive (4%) Cracking 529.0 529.0 529.0 529.0 Temperature, ? C. Cat/oil ratio 4 6 Conv., wt % 61.75 64.69 65.06 66.05 Yield (wt. %) Coke 3.017 3.055 3.555 3.861 Dry Gas 2.682 3.061 2.906 3.179 LPG 16.946 18.221 16.520 20.506 Ethylene 0.819 1.078 0.940 1.131 Propylene 5.829 6.747 6.240 7.252 C4 Olefins 4.754 5.332 4.880 6.246 Gasoline 39.104 40.352 42.074 38.504 LCO 20.942 19.309 19.625 18.861 Bottoms 17.309 16.001 15.319 15.089

Advantages of the Invention

[0078] Nano size ZSM-5 synthesis requires expensive centrifugation step in commercial scale. The present invention provides a protocol to develop nano ZSM-5 zeolite in an ensemble fashion and requires only simple filtration instead of centrifugation. [0079] Nano ZSM-5 synthesized through the developed protocol, produces higher propylene yield and minimizes bottoms and LCO in Fluid catalytic cracking unit in refinery. [0080] The nano ZSM-5 as developed in the present invention opens the scope of application in fluid catalytic cracking catalyst, petrochemical catalyst, biomass to chemicals catalysts.