Duplex stainless steel and manufacturing method thereof

Abstract

A duplex stainless steel and method of manufacturing the same, said steel having an amount of Cr in an extraction residue [Cr] of 0.005 to 0.050% and an amount of Nb in an extraction residue [Nb] of 0.001 to 0.080%, the [Nb]/[Cr] ratio being 0.2 or more. By slow cooling down to 800° C., then fast cooling down to 600° C., it is possible to control the precipitation of chromium nitrides and niobium nitrides, and by making the ratio [Nb]/[Cr] 0.2 or more, it is possible to raise the corrosion resistance. Further, by reducing Mn to less than 2.0% and N to 0.25% or less, then adding a trace amount of Nb, the effect of raising the critical pitting temperature CPT is obtained.

Claims

1. Duplex stainless steel comprising, by mass %, C: 0.001 to 0.03%, Si: 0.05 to 1.5%, Mn: 0.1 to 1.5%, Cr: 20.0 to 26.0%, Ni: 2.0 to 7.0%, Mo: 0.5 to 3.0%, N: 0.10 to 0.25%, Nb: 0.005 to 0.10%, and Al: 0.003 to 0.05%, further comprising one or more of W: 0.01 to 1%, Co: 0.01 to 1.0%, Cu: 0.01 to 2.0%, V: 0.01 to 0.3%, Ti: 0.001 to 0.03%, and B: 0.0001 to 0.0050%, having a balance of Fe and unavoidable impurities, and in impurities, restricting O: 0.006% or less, P: 0.05% or less, and S: 0.003% or less, said steel having an amount of Cr in an extraction residue [Cr] of 0.005 to 0.050 mass %, an amount of Nb in an extraction residue [Nb] of 0.001 to 0.080 mass %, and an [Nb]/[Cr] ratio being 0.2 or more.

2. Duplex stainless steel comprising, by mass %, C: 0.001 to 0.03%, Si: 0.05 to 1.5%, Mn: 0.1 to 1.5%, Cr: 20.0 to 26.0%, Ni: 2.0 to 7.0%, Mo: 0.5 to 3.0%, N: 0.10 to 0.25%, Nb: 0.005 to 0.10%, Al: 0.003 to 0.05%, Ca: 0.0005 to 0.005%, and Mg: 0.0001 to 0.003%, further comprising one or more of, W: 0.01% to 1%, Co: 0.01 to 1.0%, Cu: 0.01 to 2.0%, V: 0.01 to 0.3%, Ti: 0.001 to 0.03%, B: 0.0001 to 0.0050%, and REM: 0.005 to 0.10%, having a balance of Fe and unavoidable impurities, in impurities, restricting O: 0.006% or less, P: 0.05% or less, and S: 0.003% or less, said steel having an amount of Cr in an extraction residue [Cr] of 0.005 to 0.050 mass %, an amount of Nb in an extraction residue [Nb] of 0.001 to 0.080 mass %, and an [Nb]/[Cr] ratio being 0.2 or more.

3. The duplex stainless steel according to claim 1, wherein an actual critical pitting temperature (CPT measured value), in ° C., of the duplex stainless steel is greater than or equal to a CPT calculated value in ° C. obtained by equation 1:
CPT calculated value=2.86(Cr+3.3(Mo+0.5W)+16N—Mn)−45  (equation 1) wherein Cr, Mo, W, N, and Mn in equation 1 represent the content in mass % of the corresponding elements in the duplex stainless steel.

4. The duplex stainless steel according to claim 2, wherein an actual critical pitting temperature (CPT measured value), in ° C., of the duplex stainless steel is greater than or equal to a CPT calculated value in ° C. obtained by equation 1:
CPT calculated value=2.86(Cr+3.3(Mo+0.5W)+16N—Mn)−45  (equation 1) wherein Cr, Mo, W, N, and Mn in equation 1 represent the content in mass % of the corresponding elements in the duplex stainless steel.

5. A method of manufacturing the duplex stainless steel of claim 1, said method comprising heating to a temperature of a temperature region of 940 to 1150° C., wherein the steel has a composition comprising, by mass %, C: 0.001 to 0.03%, Si: 0.05 to 1.5%, Mn: 0.1 to 1.5%, Cr: 20.0 to 26.0%, Ni: 2.0 to 7.0%, Mo: 0.5 to 3.0%, N: 0.10 to 0.25%, Nb: 0.005 to 0.10%, and Al: 0.003 to 0.05%, further comprising one or more of W: 0.01% to 1%, Co: 0.01 to 1.0%, Cu: 0.01 to 2.0%, V: 0.01 to 0.3%, Ti: 0.001 to 0.03%, and B: 0.0001 to 0.0050%, having a balance of Fe and unavoidable impurities, in impurities, restricting O: 0.006% or less, P: 0.05% or less, and S: 0.003% or less, then cooling the steel by an average cooling rate of less than 5° C./s until a temperature of said steel becomes a temperature of 1080° C. to 800° C., then cooling the steel so that an average cooling rate from 800° C. to 600° C. in temperature of the steel becomes 3° C./s or more.

6. A method of manufacturing the duplex stainless steel of claim 2, said method comprising heating to a temperature of a temperature region of 940 to 1150° C., wherein the steel has a composition comprising, by mass %, C: 0.001 to 0.03%, Si: 0.05 to 1.5%, Mn: 0.1 to 1.5%, Cr: 20.0 to 26.0%, Ni: 2.0 to 7.0%, Mo: 0.5 to 3.0%, N: 0.10 to 0.25%, Nb: 0.005 to 0.10%, Al: 0.003 to 0.05%, Ca: 0.0005 to 0.005%, and Mg: 0.0001 to 0.003%, further comprising one or more of W: 0.01% to 1%, Co: 0.01 to 1.0%, Cu: 0.01 to 2.0%, V: 0.01 to 0.3%, Ti: 0.001 to 0.03%, B: 0.0001 to 0.0050%, and REM: 0.005 to 0.10%, having a balance of Fe and unavoidable impurities, in impurities, restricting O: 0.006% or less, P: 0.05% or less, and S: 0.003% or less, then cooling the steel by an average cooling rate of less than 5° C./s until a temperature of said steel becomes a temperature of 1080° C. to 800° C., then cooling the steel so that an average cooling rate from 800° C. to 600° C. in temperature of the steel becomes 3° C./s or more.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) FIG. 1 is a view showing a relationship between a value of PRE.sub.W,Mn of various types of stainless steel and critical pitting temperature (CPT).

DESCRIPTION OF EMBODIMENTS

(2) Below, the present invention will be explained. Note that, in this Description, unless particularly indicated otherwise, the % of the constituents indicate mass %.

(3) C is restricted to a content of 0.03% or less so as to secure the corrosion resistance of the stainless steel. If included in over 0.03%, at the time of hot rolling, Cr carbides are formed and the corrosion resistance and toughness deteriorate. Preferably, the content may be made 0.025% or less, more preferably 0.023% or less.

(4) On the other hand, from the viewpoint of the cost of reducing the amount of C of the stainless steel, 0.001% is made the lower limit.

(5) Si is added for deoxidation in 0.05% or more. Preferably, the content may be made 0.1% or more, more preferably 0.2% or more.

(6) On the other hand, if added in over 1.5%, the toughness deteriorates. For this reason, the content is made 1.5% or less. Preferably, the content may be made 1.2% or less, more preferably 1.0% or less.

(7) Mn has the effect of increasing the austenite phases and improving the toughness. Further, it has the effect of lowering the nitride precipitation temperature TN. For toughness of the matrix material and weld zone, 0.1% or more is added. Preferably, the content may be made 0.3% or more, more preferably 0.5% or more.

(8) On the other hand, Mn is an element lowering the corrosion resistance of stainless steel, so Mn is made less than 2.0%. Preferably, the content may be made 1.8% or less, more preferably 1.5% or less.

(9) Cr is made to be included in 20.0% or more for securing the basic corrosion resistance of the invention steel. Preferably, the content may be made 21.0% or more, more preferably 21.5% or more.

(10) On the other hand, if including Cr in over 26.0%, the ferrite phase fraction increases and the toughness and corrosion resistance of the weld zone are impaired. For this reason, the content of Cr was made 26.0% or less. Preferably, the content may be made 25.0% or less, more preferably 24.5% or less.

(11) Ni stabilizes the austenite structures and improves the corrosion resistance with respect to various types of acids and further the toughness by being included in 2.0% or more. By increasing the Ni content, it becomes possible to lower the nitride precipitation temperature. Preferably, the content may be made 3.0% or more, more preferably 4.0% or more.

(12) On the other hand, Ni is an expensive alloy element. In the steel of the present invention which covers alloy-conserving duplex stainless steel, from the viewpoint of cost, the Ni is limited to 7.0% or less in content. Preferably, the content may be made 6.5% or less, more preferably 6.0% or less.

(13) Mo is an element extremely effective for raising the corrosion resistance of stainless steel. To impart a corrosion resistance of SUS 316 or more, 0.5% or more may be included. Preferably, the content may be made 0.8% or more, more preferably 1.0% or more.

(14) On the other hand, Mo is expensive and is an element promoting precipitation of intermetallic compounds. In the steel of the present invention, from the viewpoint of suppressing precipitation at the time of hot rolling and the economic viewpoint, the Mo content should be as small as possible, so it is made 3.0% or less. Preferably, the content may be made less than 2.5%, more preferably 2.0% or less, still more preferably 1.5% or less.

(15) N is an element forming solid solution austenite phases and effective for raising the strength and corrosion resistance of duplex stainless steel, so 0.10% or more is included. Preferably, the content may be made 0.12% or more, more preferably 0.15% or more.

(16) On the other hand, the solid solution limit becomes higher corresponding to the Cr content, but in the steel of the present invention, if over 0.25% is included, the Cr nitrides precipitate and the toughness and corrosion resistance are impaired. For this reason, the N content was made 0.25% or less. Preferably, the content may be made 0.23% or less, more preferably 0.20% or less.

(17) Nb is an element which is strong in affinity with N and has the action of further lowering the speed of precipitation of chromium nitrides. For this reason, in the steel of the present invention, 0.005% or more is included. Preferably, the content may be made 0.010% or more, more preferably 0.020% or more, still more preferably 0.030% or more.

(18) On the other hand, if Nb is included in over 0.10%, nitrides of Nb precipitate in large amounts and impair the toughness, so the content is made 0.10% or less. Preferably, the content may be made 0.090% or less, more preferably 0.085% or less, still more preferably 0.080% or less.

(19) Note that, Nb is an expensive element, but by proactively utilizing Nb contained in low grade scrap, it is possible to render the melting and raw material costs of stainless steel inexpensive. It is preferable to use such a method to reduce the cost of melting Nb-containing steel.

(20) Al is an important element for deoxidation of steel. Further, it is included together with Ca and Mg so as to control the composition of the inclusions of the present steel. To decrease the oxygen in the steel, Al may be included together with Si. Al is included in 0.003% or more so as to control the composition of the inclusions and raise the pitting resistance. Preferably, the content may be made 0.005% or more.

(21) On the other hand, Al is an element with a relatively large affinity with N. If excessively adding it, nitrides of Al form and the toughness of the stainless steel is impaired. The extent depends on the N content, but if Al exceeds 0.05%, the toughness remarkably drops, so the content may be made 0.05% or less. Preferably, the content may be made 0.04% or less, more preferably 0.035% or less.

(22) Ca and Mg are added to control the composition of the inclusions in the present invention steel and improve the pitting resistance and hot workability of the present invention steel. In steel to which Ca and Mg are added, these are added together with 0.003% to 0.05% of Al using melting material. Alternatively, the contents are adjusted through deoxidation and desulfurization operations. By this, the content of Ca is controlled to 0.0005% or more and the content of Mg is controlled to 0.0001% or more. Preferably, Ca may be made 0.0010% or more and Mg may be made 0.0003% or more, more preferably Ca may be made 0.0015% or more and

(23) Mg may be made 0.0005% or more.

(24) On the other hand, Ca and Mg conversely both lower the hot workability and toughness if added in excess, so Ca may be controlled to a content of 0.0050% or less and Mg to 0.0030% or less. Preferably, Ca may be made 0.0040% or less and Mg may be made 0.0025% or less, more preferably Ca may be made 0.0035% or less and Mg may be made 0.0020% or less.

(25) O (oxygen) is an unavoidable impurity and an element impairing the hot workability, toughness, and corrosion resistance of stainless steel, so is preferably as small in content as possible. For this reason, the O content is preferably made 0.006% or less. Further, for extreme decrease of the oxygen, extremely large cost becomes required for refining, so if considering economy, the amount of oxygen may be 0.001% or more.

(26) Furthermore, one or more of the following elements can be included.

(27) W is an element for improving the corrosion resistance of stainless steel in the same way as Mo. It is optionally included. In the steel of the present invention, it may be included for the purpose of raising the corrosion resistance. However, it is an expensive element, so the content may be made 1.0% or less. Preferably, the content may be made 0.7% or less, more preferably 0.5% or less. If added, preferably this may be included in 0.05 or more. If including W, to obtain its effect, 0.01% or more may be added. Preferably, the content may be made 0.05% or more, more preferably 0.10% or more.

(28) Co is an element effective for raising the toughness and corrosion resistance of steel. It is optionally included. Even if included in over 1.0%, an effect commensurate with the cost appears not to be exhibited since Co is an expensive element, so the Co may be included in 1.0% or less. Preferably, the content may be made 0.7% or less, more preferably 0.5% or less. If including Co, to obtain this effect, 0.01% or more may be added. Preferably, the content may be made 0.03% or more, more preferably 0.10% or more.

(29) Cu is an element raising the corrosion resistance of stainless steel against acid in an additional manner and has the action of improving the toughness, so may be included. If including Cu in over 2.0%, εCu precipitates over the solubility at the time of cooling after hot rolling and embrittles the steel, so 2.0% or less may be included. Preferably, the content may be made 1.7% or less, more preferably 1.5% or less. If Cu is included, the content may be made 0.01% or more, preferably 0.33% or more, more preferably 0.45% or more.

(30) V is an element which has affinity with N and has the action of lowering the speed of precipitation of chromium nitrides. For this reason, it may be included. However, if over 0.3% is included, nitrides of V precipitate in large amounts and the toughness is impaired, so the content of V may be made 0.3% or less, preferably 0.25% or less, more preferably 0.20% or less. If V is included, to obtain that effect, 0.01% or more may be added. Preferably, the content may be made 0.03% or more, more preferably 0.08% or more.

(31) Ti has extremely strong affinity with N and forms nitrides of Ti in the steel, so may be included. For this reason, if including Ti, it is necessary to make the amount extremely small. If included in over 0.03%, the nitrides of Ti start to impair the toughness, so the content may be made 0.03% or less. Preferably, the content may be made 0.02% or less, more preferably 0.015% or less. If including Ti, to obtain its effect, 0.001% or more may be added. Preferably, the content may be made 0.003% or more, more preferably 0.005% or more.

(32) B is an element improving the hot workability of steel and may be included in accordance with need. Further, it is an element with an extremely strong affinity with N. If included in a large amount, the nitrides of B precipitate and start to impair the toughness. For this reason, the content may be made 0.0050% or less, preferably 0.0040% or less, more preferably 0.0030% or less. If including B, to obtain this effect, 0.0001% or more may be added. Preferably, the content may be made 0.0005% or more, more preferably 0.0014% or more.

(33) The balance comprises Fe and unavoidable impurities. The “unavoidable impurities” mean elements which cannot be avoided and end up being included when producing the duplex stainless steel according to the present invention. The impurities, in particular P and S, are restricted for the following reasons:

(34) P is an element unavoidably mixed in from the raw materials. It causes the hot workability and toughness to deteriorate, so is preferably as small in content as possible. It is limited to 0.05% or less. Preferably, the content may be made 0.03% or less. For decreasing the P to an extremely low amount, the cost of refining rises. For this reason, from the balance with the cost, the lower limit of the amount of P may be made 0.001%.

(35) S is an element unavoidably entering from the raw materials. It causes deterioration of the hot workability, toughness, and corrosion resistance, so the content is preferably as small as possible. The upper limit is made 0.003% or less. For decreasing the S to an extremely low amount, the cost of refining rises. For this reason, from the balance with the cost, the lower limit of the amount of S may be made 0.0001%.

(36) REMs are elements improving the hot workability of steel. For this purpose, 0.005% or more is sometimes added. Preferably, the content may be made 0.010% or more, more preferably 0.020% or more. On the other hand, excessive addition conversely lowers the hot workability and toughness, so 0.100% or less may be included. Preferably, the content may be made 0.080% or less, more preferably 0.070% or less.

(37) Here, “REM” is the total of the contents of La, Ce, and other lanthanoid system rare earth elements.

(38) Next, matters relating to the extraction residue will be explained.

(39) The duplex stainless steel according to the present invention is steel in which carbonitrides containing Nb and Cr precipitate due to the inclusion of a trace amount of Nb. The corrosion resistance, toughness, and other properties of a product in a state with the steel heated for solution heat treatment in various ways are affected by the ratios of the Nb and Cr contained in the extraction residue of the carbonitrides in the steel (below, respectively referred to as [Nb] and [Cr]) and the ratio of the same ([Nb]/[Cr]).

(40) If the amount of Cr in the extraction residue ([Cr]) is large, the corrosion resistance and toughness are impaired. In the past, these properties were thought to be improved the smaller the [Cr]. However, in the steel of the present invention containing a trace amount of Nb, it was learned that having a certain amount of [Cr] leads to improvement of the corrosion resistance of the finished product. According to research of the inventors, it was learned that [Cr] may be made 0.005% or more. On the other hand, if [Cr] exceeds 0.050%, the toughness and corrosion resistance are impaired, so the value may be made 0.050% or less.

(41) If the amount of Nb in the extraction residue ([Nb]) is large, the toughness of the steel is impaired. In the past, it was thought that if Nb precipitates, the effect of inclusion of Nb becomes harder to obtain, but according to research of the inventors, the finding was obtained that including [Nb] in a certain amount is effective for improvement of the corrosion resistance of the finished product. The [Nb] for this may be made 0.001% or more. Preferably, it may be made 0.003% or more.

(42) On the other hand, if including an extremely large amount of [Nb], the toughness of the steel starts to be impaired, so [Nb] may be made 0.080% or less. Preferably, it may be made 0.050% or less.

(43) The ratio ([Nb]/[Cr]) of the amount of Nb and amount of Cr in the extraction residue is an indicator representing the composition of the nitrides precipitating in the steel. According to research of the inventors, the finding was obtained that if the ratio is small, the corrosion resistance of the product becomes lower. As the threshold value, the value of 0.2 was obtained. For this reason, [Nb]/[Cr] may be made 0.2 or more. Preferably, the value may be made 0.3 or more, more preferably 0.4 or more.

(44) Next, the manufacturing method will be explained.

(45) Solution heat treatment of the stainless steel is performed for the purpose of making the chrome carbonitrides enter solid solution. Therefore, the usual practice has been to soak the steel material at a high temperature and fast cool it. In this regard, however, according to research of the inventors, the finding was obtained that not causing all of the chrome carbonitrides to enter a solid solution leads to improvement of the corrosion resistance of duplex stainless steel.

(46) That is, the finding was obtained that by heating stainless steel of predetermined constituents to a temperature of a temperature region of 940 to 1150° C., then (for example, after extraction from the heat treatment furnace) cooling by an average cooling rate of less than 5° C./s (seconds) until the temperature of the steel becomes a temperature between 1080° C. to 800° C., then cooling by an average cooling rate of 3° C./s or more until the temperature of the steel falls from 800° C. to 600° C. (fast cooling), the corrosion resistance of the duplex stainless steel product becomes excellent.

(47) In the past, the general thinking had been to raise the temperature of the solution heat treatment and then quickly cool the stainless steel to keep down the precipitates. The steel of the present invention is duplex stainless steel containing Nb and Cr and steel in which chromium nitrides and niobium nitride are complexly precipitated. The inventors engaged in repeated experiments based on the findings of research relating to the thermodynamics of equilibrium precipitation of such complex nitrides and speed of precipitation. As a result, they found that if the solution heat treatment temperature and temperature of starting fast cooling are too high and if the content of Nb is small, the ratio of chrome in the nitrides becomes higher and the pitting resistance falls correspondingly.

(48) The lower limit of the solution heat treatment temperature may be made 940° C. or more so as to promote recrystallization of the steel. Preferably, it may be made 950° C. or more, more preferably 970° C. or more. On the other hand, the upper limit of the solution heat treatment temperature may be made 1150° C. so as to keep down excessive formation of chromium nitrides during cooling of the steel material. Preferably, it may be made 1100° C. or less, more preferably 1050° C. or less.

(49) To sufficiently secure solid solution, the steel material is preferably held at the solution heat treatment temperature for 1 minute or more. The upper limit of the holding time is not particularly prescribed so long as not obstructing actual operation, but from the productivity and other economic viewpoints, 30 minutes or less is preferable.

(50) The cooling rate after heating and until starting fast cooling is preferably slow. At the fastest, it may be made less than 5° C./s. Preferably, the speed may be made less than 3° C./s, more preferably 2° C./s or less. More preferably, it may be made 1.5° C./s or less. The lower limit of the average cooling rate at this time is not particularly set.

(51) The temperature of starting the fast cooling is preferably low, but to increase the amount of precipitation of the Nb nitrides, the temperature of starting the fast cooling may be made 1080° C. or less. On the other hand, it is necessary to start the fast cooling at the temperature region where chromium nitrides precipitate or higher, so the temperature of starting the fast cooling may be made 800° C. or more.

(52) If the solution heat treatment temperature is 1080° C. or less, fast cooling may be started without slow cooling. This is because precipitation of chromium nitrides can be suppressed.

(53) However, by causing precipitation of niobium nitrides, precipitation of chromium nitrides can be suppressed, so it is preferable to slow cool as much as possible.

(54) During the cooling after solution heat treatment, if chromium nitrides proceed to precipitate in the duplex stainless steel, the Cr-poor phases increase by that amount and the pitting resistance falls. For this reason, it is preferable to increase the cooling rate (fast cool) at the temperature region where the speed of precipitation of chromium nitrides becomes greater (800 to 600° C.). In the steel of the present invention, by including Nb, the speed of precipitation of the chromium nitrides is kept down, but if the cooling rate is less than 3° C./s, the speed of production of chromium nitrides is insufficiently kept down, the Cr-poor phases increase, and the critical pitting temperature falls. For this reason, the cooling rate may be made 3° C./s or more. Preferably, the speed may be made 5° C./s or more, more preferably 10° C./s or more. No upper limit is particularly set for the average cooling rate at the time of fast cooling, but from the restrictions in facilities, it may be made 100° C./s or less.

(55) From the above, preferably the steel material is heated for solution heat treatment, then cooled (slow cooled) so that the average cooling rate until the temperature of the steel becomes 800° C. becomes less than 5° C./s (preferably less than 3° C./s, more preferably 2° C./s or less), then cooled (fast cooled) so that the average cooling rate from when the temperature of the steel falls from 800° C. to 600° C. becomes 3° C./s or more (preferably 5° C./s or more, more preferably 10° C./s or more). The method of cooling is not particularly limited. For slow cooling, allowing the steel material to stand and cool inside the heat treatment furnace, putting a covering on it for cooling or allowing it to stand in the atmosphere may be considered. For fast cooling, immersion in a water tank may be considered.

(56) As a result, the stainless steel according to the present invention contains an amount of Cr in the extraction residue [Cr] of 0.005 to 0.050% and an amount of Nb in the extraction residue [Nb] of 0.001 to 0.080% and can secure a [Nb]/[Cr] ratio of 0.2 or more.

(57) From these, it is possible to maintain the Cr nitrides in the steel at a constant amount and the Cr-poor phases are reduced, so the corrosion resistance is improved.

(58) The thickness of the duplex stainless steel according to the present invention is not particularly limited, but since the steel of the present invention is applied to facilities and equipment and containers used in environments with a high chloride ion concentration close to brackish water or seawater, since, in place of existing austenitic stainless steel, the steel according to the present invention enables design of steel materials reduced in thickness due to its high strength and thereby gives high economy, and due to the heat treatment and cooling controllability, the effect is better obtained if the thickness is greater than 6 mm. Preferably, it is 8 mm or more, more preferably 10 mm or more.

(59) Note that, the temperature of the steel is preferably the temperature of the center part of the steel, but it may also be the surface temperature of the steel. In actual operation, it is possible to measure the surface temperature of the stainless steel to perform the heat treatment and control the cooling.

(60) As explained above, in general, the pitting resistance of stainless steel is ranked by the pitting resistance equivalent. The pitting resistance equivalent (PRE) is often expressed by the formula
PRE=Cr+3.3Mo+16N
Further, considering the effects of Mn and W, the formula
PRE.sub.W,Mn=Cr+3.3(Mo+0.5 W)+16N−Mn
has been proposed (NPL 1). The inventors used this PRE.sub.W,Mn to research the correlation between various types of stainless steel and the CPT. As a result, they learned that the correlation generally follows the relationship of:
CPT calculated value (° C.)=2.86(Cr+3.3(Mo+0.5 W)+16N−Mn)−45(° C.)  (formula 1).
In experiments by the inventors, it became clear that the error between the actual critical pitting temperature (CPT) and the CPT calculated value, if any, is 5 to 10° C. or so (FIG. 1).

(61) The stainless steel according to the present invention is kept down in N, given a trace amount of Nb and subjected to solution heat treatment, and is made to contain suitable quantities of carbonitrides of Nb and Cr by precipitation to thereby raise the pitting resistance. As a result, it was confirmed that the critical pitting temperature (° C.) of the stainless steel according to the present invention becomes higher than the CPT calculated value (° C.) obtained by (formula 1). That is, it was confirmed that the actual critical pitting temperature (CPT (measured value)) of the stainless steel according to the present invention is a value of the CPT (calculated value) obtained by (formula 1) or more.
Critical pitting temperature (° C.)≥2.86(Cr+3.3(Mo+0.5 W)+16N−Mn)−45(° C.)

EXAMPLES

(62) Below, examples will be explained. Table 1 shows the chemical compositions of test steels. These steels were obtained by hot rolling laboratory melted materials or cutting out parts of actually produced materials. Fields of the constituents shown in Table 1 not describing contents show the levels were those of unavoidable impurities. “REM” means lanthanoid system rare earth elements. The content shows the total of these elements. The steel plates obtained by these steels (plate thickness×100 mm width×300 mm length) were heat treated in various ways. Thermocouples were inserted into the center parts of thickness of the steel plates and their temperatures were measured during the heat treatment. Further, the surface temperatures after extracting the steel plates from the heat treatment furnace were measured by radiation thermometers. The steel plates were mainly cooled by immersion in a water tank.

(63) First, each steel plate was placed in a heat treatment furnace and heated. It was soaked at a heating temperature (“heating temperature” of Table 2) for 5 to 30 minutes, then the steel plate was extracted from the heat treatment furnace. At the time when the surface temperature became a predetermined temperature (“cooling start temperature” of Table 2), the steel plate was immersed in a water tank to start the cooling (fast cooling). The cooling rate after extraction from the heat treatment furnace until start of cooling (fast cooling) was described in Table 2 as the “cooling rate 1”. The cooling rate at the time of fast cooling was adjusted by adding a commercially available additive to the water in the water tank so as to obtain the desired cooling rate. Further, for comparison, sometimes water cooling was omitted. The average cooling rate was found by continuously measuring the temperature of a thermocouple at the center of plate thickness. The average cooling rate from extraction from the heat treatment furnace to the start of fast cooling (for example, until immersion in a water tank) was described in Table 2 as the “cooling rate 1”. Next, the average cooling rate in the section where the temperature of the steel plate fell from 800° C. to 600° C. was described in Table 2 as the “cooling rate 2”. Note that, if immediately immersing the steel in a water tank after extraction from the heat treatment furnace, no cooling rate 1 is obtained, so “-” is described. Further, No. 19 of Table 2 was allowed to stand in the heat treatment furnace and slow cool after heating in the furnace, so the cooling start temperature and the cooling rate 1 are both not described.

(64) Table 2 shows the thicknesses of the steels, the heat treatment conditions, the amounts of Cr and Nb in the extraction residues ([Cr], [Nb]) and their ratios [Nb]/[Cr], the measured values of the CPT, the calculated values of the CPT (value of (formula 1)), and differences of the same.

(65) The [Cr] and [Nb] in the extraction residue and the ratio [Nb]/[Cr] were found by the following procedure: The steel was heated for solution heat treatment under various conditions.

(66) A 2×15×50 mm sample was cut out by machining from the surface layer of the steel material after cooling.

(67) The entire surface of the sample was wet polished by #600 abrasive.

(68) The sample was electrolyzed in a nonaqueous solution (3% maleic acid+1% tetramethylammonium chloride+balance methanol) (100 mV constant voltage) to dissolve the matrix.

(69) A 0.2 μm pore size filter was used to filter the residue (=precipitate) and extract the precipitate.

(70) The chemical composition of the residue was analyzed and the contents of chrome and niobium were found. The content of chromium and the content of niobium in the residue were defined as [Cr] and [Nb] and the ratio [Nb]/[Cr] was found.

(71) The method of measuring the CPT will be explained. First, in the same way as the sample for extraction residue use, a 2×15×30 mm sample was cut out from the surface layer of the steel material by machining. The surface layer part was polished as a test surface and was tested in accordance with the method of JIS G0590. The part was started to be raised in temperature from 0° C., was held at a potential of 0.745mVvsSSE while started to be raised in temperature from 0° C., and was measured for the value of the current. The temperature at the point of time when the current density suddenly rose was found during this as the critical pitting temperature (CPT).

(72) It was learned that each of the steels of the working examples of the present invention had a difference of the critical pitting temperature (CPT measured value) and CPT calculated value (value of (formula 1)) of a value of 0° C. or more and an excellent corrosion resistance. On the other hand, it is learned that, in the comparative examples, the value of CPT becomes smaller than the calculated value (formula 1).

(73) In the above way, according to the present invention, it became clear that duplex stainless steel excellent in corrosion resistance is obtained.

(74) TABLE-US-00001 TABLE 1 (mass %) No. C Si Mn P S Cr Ni Mo W Co Cu N EX. 1 0.015 0.42 1.35 0.023 0.0011 23.8 4.58 1.15 0.23 0.193 2 0.018 0.38 0.35 0.019 0.0013 23.2 4.52 0.52 0.25 0.15 0.145 3 0.021 0.34 1.85 0.024 0.0024 21.5 2.53 0.55 0.15 0.172 4 0.019 0.34 1.63 0.023 0.0007 24.3 4.82 2.14 0.12 0.35 0.213 5 0.018 0.37 0.35 0.025 0.0006 23.9 5.02 1.12 0.15 0.33 0.168 6 0.008 1.23 1.53 0.021 0.0012 24.1 5.85 1.08 1.52 0.126 7 0.012 0.24 0.35 0.028 0.0004 25.2 5.45 2.82 0.32 0.45 0.238 8 0.025 0.41 1.23 0.025 0.0006 24.0 5.23 1.08 0.54 0.138 9 0.018 0.43 1.28 0.026 0.0007 23.8 5.01 1.14 0.05 0.14 0.35 0.176 10 0.017 0.40 1.45 0.020 0.0010 24.2 5.12 2.18 0.65 0.185 11 0.014 0.41 0.80 0.019 0.0005 25.6 6.02 1.85 0.72 0.73 0.205 12 0.012 0.36 1.33 0.026 0.0005 23.6 5.16 1.27 0.11 0.33 0.165 13 0.013 0.37 1.36 0.023 0.0008 23.5 5.01 1.31 0.166 14 0.015 0.45 1.75 0.032 0.0007 23.7 4.98 1.15 0.02 0.03 0.02 0.172 15 0.018 0.42 1.36 0.031 0.0004 24.3 5.86 2.21 0.01 0.12 0.45 0.185 16 0.021 0.45 1.73 0.028 0.0007 24.5 5.26 2.31 0.08 0.215 Comp. ex. a 0.015 0.42 0.81 0.022 0.0012 23.8 4.56 1.09 0.196 b 0.018 0.35 1.25 0.023 0.0008 21.5 3.12 0.85 0.142 c 0.013 0.62 0.85 0.025 0.0007 21.1 2.13 0.85 0.221 d 0.016 0.45 1.05 0.021 0.0008 23.4 3.23 1.03 0.082 e 0.014 0.45 1.02 0.026 0.0006 24.3 4.05 1.56 0.265 f 0.013 0.43 2.53 0.025 0.0004 25.1 5.05 2.18 0.165 g 0.008 0.52 1.05 0.028 0.0012 17.0 12.05 2.05 0.016 No. V Nb Ti B Al O Ca Mg REM PREw, Mn Ex. 1 0.050 0.022 0.003 29.33 2 0.08 0.030 0.0023 0.018 0.003 26.89 3 0.035 0.005 0.005 24.22 4 0.023 0.012 0.033 0.002 0.0018 33.14 5 0.13 0.035 0.0015 0.023 0.003 0.0024 30.18 6 0.02 0.008 0.005 0.025 0.003 0.0024 0.025 28.15 7 0.13 0.007 0.026 0.003 0.0019 38.49 8 0.07 0.082 0.015 0.0028 0.016 0.003 0.0025 0.0003 28.54 9 0.08 0.045 0.008 0.0022 0.036 0.001 0.0022 0.0015 0.010 29.18 10 0.10 0.030 0.003 0.0014 0.024 0.002 0.0020 0.0005 32.90 11 0.03 0.012 0.026 0.003 0.0026 0.038 35.37 12 0.13 0.037 0.004 0.0022 0.014 0.003 0.0021 0.0006 29.10 13 0.11 0.037 0.0018 0.021 0.004 29.12 14 0.03 0.035 0.002 0.0005 0.026 0.003 28.53 15 0.12 0.039 0.001 0.0017 0.023 0.003 0.0018 0.0005 33.21 16 0.023 0.0002 0.025 0.003 33.83 Comp. ex. a 0.001 0.024 0.003 29.72 b 0.15 0.015 0.003 25.33 c 0.003 0.035 0.002 26.59 d 0.025 0.016 0.003 27.06 e 0.012 0.027 0.003 32.67 f 0.001 0.032 0.003 32.40 g 0.002 0.018 0.003 22.97

(75) TABLE-US-00002 TABLE 2 Difference of Cooling CPT CPT measured value Heating start Cooling Cooling (measured (calculated and calculated Steel Thickness temp. temp. rate 1 rate 2 [Cr] [Nb] value) value) value of CPT No. no. mm ° C. ° C. ° C./s ° C./s mass % mass % [Nb]/[Cr] ° C. ° C. ° C. Ex. 1 1 10 1000 1000 — 60 0.030 0.040 1.3 42 39 3 2 1 10 1050 1050 — 60 0.025 0.025 1.0 41 39 2 3 1 10 1100 950 4.3 60 0.014 0.012 0.9 40 39 1 4 1 10 1150 950 4.8 60 0.010 0.002 0.2 40 39 1 5 1 10 1050 950 3.7 30 0.024 0.025 1.0 42 39 3 6 1 10 1050 850 2.8 30 0.023 0.025 1.1 43 39 4 7 2 20 1000 1000 — 15 0.015 0.017 1.1 35 32 3 8 3 50 1000 950 1.0 5 0.017 0.020 1.2 27 24 3 9 4 10 1050 950 3.5 30 0.007 0.006 0.9 52 50 2 10 5 10 1050 950 3.5 30 0.016 0.014 0.9 45 41 4 11 6 10 1050 1000 3.8 60 0.005 0.001 0.2 37 36 1 12 7 20 1050 950 2.2 30 0.007 0.002 0.3 66 65 1 13 8 10 1050 950 3.5 30 0.042 0.055 1.3 41 37 4 14 9 10 1050 900 3.2 30 0.019 0.022 1.2 43 38 5 15 10 10 1050 1000 3.8 60 0.007 0.007 1.0 55 49 6 16 11 10 1050 1000 3.8 60 0.006 0.002 0.3 58 56 2 101 1 15 1050 950 2.8 40 0.021 0.022 1.0 43 39 4 102 1 20 1050 975 2.4 20 0.022 0.021 1.0 42 39 3 103 1 30 1050 1000 1.8 10 0.023 0.018 0.8 41 39 2 201 12 20 1035 950 2.0 30 0.017 0.015 0.9 44 38 6 202 13 20 1035 950 2.0 30 0.016 0.014 0.9 41 38 3 203 14 20 1035 950 2.0 30 0.014 0.012 0.9 39 37 2 204 15 20 1035 950 2.0 30 0.015 0.015 1.0 57 50 7 205 16 20 1035 950 2.0 30 0.011 0.008 0.7 53 52 1 Comp. ex 17 a 10 1050 1050 — 60 0.007 0.000 0.0 36 38 −2 18 1 10 1150 1100 5.2 60 0.015 0.002 0.1 36 39 −3 19 7 20 1100 — — 1 0.023 0.002 0.1 58 65 −7 20 b 10 1050 1050 — 60 0.08 0.13 1.6 24 27 −3 21 c 10 1100 1050 4.2 60 0.013 0.000 0.0 27 31 −4 22 d 10 1100 1050 4.2 60 0.043 0.004 0.1 27 32 −5 23 e 10 1100 1050 4.2 60 0.015 0.005 0.3 43 48 −5 24 f 10 1100 1050 4.2 60 0.013 0.000 0.0 44 48 −4 25 g 10 1050 1050 — 60 0.001 0.000 0.0 15 21 −6 The “temperature 1” is the soaking temperature. The steel is soaked at this temperature for 5 minutes to 30 minutes. The “temperature 2” is the surface temperature at the start of immersion under conditions of immersion in a water tank for accelerated cooling. The “cooling rate 1” shows the average cooling rate from the temperature 1 at the time of extraction to the temperature 2 at the time of immersion in a water tank (both surface temperatures). The “cooling rate 2” shows the average cooling rate in the section where the temperature of a thermocouple buried at the center of thickness is 800° C. to 600° C.

INDUSTRIAL APPLICABILITY

(76) According to the present invention, it becomes possible to provide an economic duplex stainless steel material having a corrosion resistance of equal to or greater than SUS 316L in an environment with a chloride ion concentration close to brackish water or seawater. This can be used in riparian dams, sluice gates, tidal weirs, and other infrastructure structures or seawater desalination equipment, tanks of cargo ships, various containers, etc. In these and other ways, the contribution to industry is extremely great.