3D Printable Biodegradable Polymer Composite

Abstract

A printable biodegradable polymer composite comprises PGSA, biodegradable photo-initiator and material selected from the group consisting PCL-DA and PEG-DA being uniformly blended together. By adjusting blending ratio of the present invention, the elasticity, mechanical properties and degradation patterns of the present invention may be adjusted for producing various tissue, organ or related bio-product by 3D-printing.

Claims

1. A 3D printable biodegradable polymer composite comprising: poly(glycerol sebacate acrylate); a photo-initiator; a material selected from a group consisting of polycaprolactone-diacrylate and polyethyleneglycol-diacrylate; and a degree of acrylation of poly(glycerol sebacate acrylate) is at a range of 5%60%.

2. The 3D printable biodegradable polymer composite as claimed in claim 1, wherein the 3D printable biodegradable polymer composite comprises poly(glycerol sebacate acrylate) 6090 wt % and polycaprolactone-diacrylate 1040%.

3. The 3D printable biodegradable polymer composite as claimed in claim 1, wherein the 3D printable biodegradable polymer composite comprises poly(glycerol sebacate acrylate) 3070 wt % and polyethyleneglycol-diacrylate 3070%.

4. The 3D printable biodegradable polymer composite as claimed in claim 2, wherein the 3D printable biodegradable polymer composite comprises poly(glycerol sebacate acrylate) 3070 wt % and polyethyleneglycol-diacrylate 3070%.

5. The 3D printable biodegradable polymer composite as claimed in claim 1, wherein the 3D printable biodegradable polymer composite comprises poly(glycerol sebacate acrylate) 3050 wt %, polycaprolactone-diacrylate 3040% and polyethyleneglycol-diacrylate 2030 wt %.

6. The 3D printable biodegradable polymer composite as claimed in claim 2, wherein the 3D printable biodegradable polymer composite comprises poly(glycerol sebacate acrylate) 3050 wt %, polycaprolactone-diacrylate 3040% and polyethyleneglycol-diacrylate 2030 wt %.

7. The 3D printable biodegradable polymer composite as claimed in claim 1, wherein: the 3D printable biodegradable polymer composite comprises the photo-initiator at a range of 0.055 wt %; the photo-initiator is UV light initiator or visible light initiator; the UV light initiator is TPO or Irgacure 784; and the visible light initiator is TPO, Irgacure 784 or camphorquinone.

8. The 3D printable biodegradable polymer composite as claimed in claim 2, wherein: the 3D printable biodegradable polymer composite comprises the photo-initiator at a range of 0.055 wt %; the photo-initiator is UV light initiator or visible light initiator; the UV light initiator is TPO or Irgacure 784; and the visible light initiator is TPO, Irgacure 784 or camphorquinone.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0011] FIG. 1 is Young's Modulus of a preferred embodiment in accordance with the present invention.

[0012] FIG. 2 is ultimate tensile strength of the preferred embodiments in accordance with the present invention.

[0013] FIG. 3 is elongation at break of the preferred embodiments in accordance with the present invention.

[0014] FIG. 4 is degradation rate of the preferred embodiments in accordance with the present invention.

[0015] FIG. 5 is SEM of stem cells for showing bio-compatibility in accordance with the present invention.

[0016] FIG. 6 is SEM of human pulmonary alveolar epithelial cells for showing bio-compatibility in accordance with the present invention.

[0017] FIG. 7 is hematoxylin and eosin-stained picture for showing degradability of sample A in accordance with the present invention.

[0018] FIG. 8 is hematoxylin and eosin-stained picture for showing degradability of sample C in accordance with the present invention.

[0019] FIG. 9 is hematoxylin and eosin-stained picture for showing degradability of sample H in accordance with the present invention.

[0020] FIG. 10 is hematoxylin and eosin-stained picture for showing degradability of sample J in accordance with the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0021] Present invention is related to a three-dimensional (3D) printable biodegradable polymer composite comprising PGSA (Poly(glycerol sebacate acrylate)), a photo-initiator 0.055 wt % and a material selected from the group consisting of PCL-DA (Polycaprolactone-diacrylate) and PEG-DA (Polyethyleneglycol-diacrylate) being uniformly blended together. Degree of acrylation of PGSA in the present invention is preferred at a range of 5%60% and more preferred at the range of 7%30%. Blending ratio of the combination of PGSA and PCL-DA in the present invention is preferred at a range of PGSA 6090 wt % and PCL-DA 1040%. Blending ratio of the combination of PGSA and PEG-DA in the present invention is preferred at a range of PGSA 3070 wt % and PEG-DA 3070%. Blending ratio of the combination of PGSA, PCLG-DA and PEG-DA in the present invention is preferred at a range of PGSA 3050 wt %, PCL-DA 3040% and PEG-DA 2030 wt %.

[0022] PGSA, PCL-DA and PEG-DA of the present invention are bio-compatible and bio-degradable material. By grafted PCL and PEG with diacrylate (DA) functional group, PCL-DA and PEG-DA are able to form strong crosslink reaction with PGSA after curing under certain light wave.

[0023] The photo-initiator of the present invention is preferred to be a bio-compatible material. The photo-initiator of the present invention may be but not limited to TPO (diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide), Irgacure 784 or Camphorquinone (CQ). TPO and Irgacure 784 can be activated under UV light or visible light. Camphorquinone can be activated under visible light.

[0024] PGSA of the present invention is preferably produced by grafting PGS (Poly(glycerol sebacate)) with a solution contained different ratio of acryloyl chloride, triethylamine, 4-dimethylamino pyridine (DMAP) and dichloromethane (DCM). With reference to below chart 1, some preferred embodiments of the present invention are shown for producing PGSA with 730% degree of acrylation.

TABLE-US-00001 CHART 1 Material Acryloyl PGS chloride Triethylamine DMAP DCM PGSA Group (g) (ml) (ml) (mg) (ml) (%) Group 1 30 1.42 3.06 30 300 7 Group 2 30 2.84 6.13 30 300 15 Group 3 30 5.69 12.26 30 300 30

[0025] Besides abovementioned triethylamine, potassium carbonate (K.sub.2CO.sub.3) may also be used for producing PGSA with different degree of acrylation. By utilizing potassium carbonate (K.sub.2CO.sub.3), less toxic or non-biocompatible solvent will be used during the production which may lead to better bio-compatibility for PGSA.

[0026] In order to obtain the 3D printable biodegradable polymer composite of the present invention, it is preferred to blend the PGSA, the photo-initiator, PCL-DA and PEG-DA in dichloromethane. After abstracting the dichloromethane, the 3D printable biodegradable polymer composite of the present invention is produced.

[0027] In order to proof mechanical property and bio-degradability of the present invention are adjustable, testing blocks are produced by 3D printing with different acrylation degree of PGSA or different blending ratio of the main materials of the present invention (PGSA, the photo-initiator, PCL-DA and PEG-DA). Each testing block is produced by depositing 5 layers of blended materials and 100 m thicknesses in each layer. During depositing, the first layer of the testing block is cured by exposing to UV/visible light in 30 second. The second to fifth layers of the testing blocks are cured by exposing to UV/visible light in 15 second.

[0028] The first embodiment of the present invention is 3D printed testing blocks comprising PGSA, PCL-DA and the photo-initiator where the PGSA and PCL-DA has blending ratio of 2:1 and the photo-initiator is at a range of 15 wt %. The PGSA of the first embodiment has 7%30% of arcylation. Test results show that Young's Modules of the testing blocks in the first embodiment are increased from 1.42 MPa to 6.4 MPa as the acrylation of PGSA increased. Ultimate tensile strength (UTS) of the testing blocks in the first embodiment are increased from 0.19 MPa to 0.69 MPa as the acrylation of PGSA increased.

[0029] The second embodiment of the present invention is 3D printed testing blocks comprising PGSA, PCL-DA and the photo-initiator where the PGSA and PCL-DA has blending ratio of 2:14:1 and the photo-initiator is at a range of 15 wt %. The PGSA of the second embodiment has 15% of arcylation. Test results show that Young's Modules of the testing blocks in the second embodiment are slightly decreased from 2.85 MPa to 2.3 MPa as the blending ratio of PGSA increased. Elongation at break of the testing blocks in the second embodiment are otherwise increased from 11.28% to 19.27% as the blending ratio of PGSA increased. After 24 days, degradation rate of the testing blocks in the second embodiment are also increased from 11.28% to 19.27% as the blending ratio of PGSA increased. Hence, elasticity and degradability of the present invention may be adjusted with different blending ratio of PGSA and PCL-DA.

[0030] The third embodiment of the present invention is 3D printed testing blocks comprising PGSA, PEG-DA and the photo-initiator where the PGSA and PEG-DA has blending ratio of 1:1 and the photo-initiator is at a range of 15 wt %. The PGSA of the third embodiment has 7%30% of arcylation. Test results show that Young's Modules of the testing blocks in the third embodiment are increased from 4.25 MPa to 10.54 MPa as the acrylation of PGSA increased. Ultimate tensile strength (UTS) of the testing blocks in the third embodiment are increased from 0.8 MPa to 1.1 MPa as the acrylation of PGSA increased. According to aforementioned test result, mechanical property of the present invention may be adjusted according to PGSA with different degree of acyrlation.

[0031] The fourth embodiment of the present invention is 3D printed testing blocks comprising PGSA, PEG-DA and the photo-initiator where the PGSA and PEG-DA has blending ratio of 1:12:1 and the photo-initiator is at a range of 15 wt %. The PGSA of the fourth embodiment has 15% of arcylation. Test results show that Young's Modules of the testing blocks in the fourth embodiment are slightly decreased from 7.58 MPa to 4.66 MPa as the blending ratio of PGSA increased. Elongation at break of the testing blocks in the fourth embodiment are otherwise increased from 13.63% to 18.41% as the blending ratio of PGSA increased. After 24 days, degradation rate of the testing blocks in the fourth embodiment are also increased from 13.63% to 18.41% as the blending ratio of PGSA increased. Hence, elasticity and degradability of the present invention may be adjusted with different blending ratio of PGSA and PEG-DA.

[0032] The fifth embodiment of the present invention is 3D printed testing blocks comprising PGSA, PCL-DA, PEG-DA and the photo-initiator where the PGSA, PCL-DA and PEG-DA has blending ratio of 1:1:12:1:1 and the photo-initiator is at a range of 15 wt %. The PGSA of the fifth embodiment has 30% of arcylation. Test results show that ultimate tensile strength (UTS) of the testing blocks in the fifth embodiment are increased from 0.40 MPa to 0.93 MPa as the blending ratio of PGSA increased. After 24 days, degradation rate of the testing blocks in the fifth embodiment are also increased from 10.55% to 25.05% as the blending ratio of PGSA increased. Young's Modules of the testing blocks in the fifth embodiment are slightly decreased from 4.32 MPa to 3.58 MPa as the blending ratio of PGSA increased.

[0033] The sixth embodiment of the present invention is 3D printed testing blocks comprising PGSA, PCL-DA, PEG-DA and the photo-initiator where the PGSA, PCL-DA and PEG-DA has blending ratio of 1:1:11:1:2 and the photo-initiator is at a range of 15 wt %. The PGSA of the sixth embodiment has 30% of arcylation. Test results show that Young's Modules of the testing blocks in the fifth embodiment are slightly decreased from 4.32 MPa to 6.38 MPa as the blending ratio of PCL-DA increased. Ultimate tensile strength (UTS) of the testing blocks in the sixth embodiment are increased from 0.40 MPa to 1.28 MPa as the blending ratio of PCL-DA increased.

[0034] According to abovementioned embodiments, the present invention is able to produce 3D printing products with different mechanical property and different degradability by adjusting blending ratio of PGSA, PCL-DA and PEG-DA and adjusting acrylation degrees of PGSA.

[0035] In order to proof the present invention is suitable for 3D printing, the control groups are provided by directly coating the aforementioned materials in each embodiment on films and cured under UV light. Test results show that Young's Modulus of the control groups are increase from 0.57 MPa to only 4.08.

[0036] Comparing to coating, the reason why the present invention has better mechanical property when produced by 3D printing is that materials are able to be quickly shaped and cured without any precipitate being formed while 3D printing. This may enhance uniformity and mechanical property of materials which leads to better mechanical property of the present invention.

[0037] With reference to FIG. 1 to FIG. 4, Young's Modulus, ultimate tensile strength, elongation at break and degradation rate of other embodiments in the present invention are presented. Samples with blending ratio of 1:0, 4:1 and 2:1 are representing PGSA 0%, 80% and 33% being blended with PCL-DA. The arcylation degrees of PGSA in these samples are 7%, 15% and 30%.

[0038] With reference to FIG. 1 to FIG. 4, the sample with blending ratio 4:1 shows lesser mechanical property than the sample with blending ratio of 1:0. The mechanical property can be reduced by the existence of PGSA which is suitable for applying to soft tissue. Samples with blending ratio 4:1 and 2:1 show hardness of material being increased as acrylation degree of PGSA decreased. As blending ratio of PCL-DA increased, the mechanical property of samples are otherwise increased with elasticity remained. As acrylation degree of the PGSA increased, mechanical properties of these samples are only slightly effected by blending ratio of PCL-DA increased.

[0039] With reference to FIG. 5 to FIG. 6, SEM pictures for showing bio-compatibility of stem cells and human pulmonary alveolar epithelial cells are presented by utilizing the embodiments of the present invention as mentioned above. Samples A to O showed in FIG. 5 and FIG. 6 are presented with great bio-compatibility of the present invention.

[0040] With reference to FIG. 7 to FIG. 10, Hematoxylin and eosin-stained (H&E stain) pictures for showing degradability of present invention are presented. Samples showed in FIG. 7 and FIG. 8 comprise PGSA and PCL-DA corresponded to the samples A and C in FIG. 5 and FIG. 6. Samples showed in FIG. 9 and FIG. 10 comprise PGSA and PEG-DA corresponded to the samples H and J in FIG. 5 and FIG. 6. Degradability of samples in FIG. 7 and FIG. 8 are layered degradation which is gradually degraded layer by layer from outside to inside of the structure. Layer degradation is able to continually maintain mechanical property while degradation, which is suitable for applying to applications with high mechanical property demands. Degradability of samples showed in FIG. 9 and FIG. 10 are bulk degradation which is broke down in bulks by bulks. Since degradation surface is increased, bulk degradation is able to be quickly degraded which is suitable for applying to applications required high degradation rate.

[0041] Post treatment may be applied to further increase the mechanical property of the present invention. The post treatment may be but not limited to exposure to light or heat.

[0042] With reference to below chart 2, some bio-engineering applications are demonstrated according to the mechanical property, degradability and bio-compatibility of the main materials of the present invention. The present invention may be utilized to produce various human organ/tissue substitutes. Chart 2 is just some application examples of the present invention when applying to bio-engineering field. The present invention is not limited to the example being shown in chart 2.

TABLE-US-00002 CHART 2 Suitable for producing human organ/tissue PGSA + PCL-DA Heart, liver PGSA + PEG-DA Heart PGSA + PCL-DA + PEG-DA Cartilage

[0043] According to abovementioned properties, the present invention has advantages as following.

[0044] 1. By adjusting blending ratio of PGSA, PCL-DA and PEG-DA, the present invention is able to produce products with different elasticity, mechanical property, degradability and elongation property by 3D printing. The present invention is suitable for producing human tissue or organ in bio-engineering.

[0045] 2. The present invention is able to be cured under UV or visible light which is suitable for rapid tooling like 3D printing and is suitable for producing customized products corresponding to human tissue, organ or other related applications

[0046] 3. With adjustable elasticity, mechanical property, degradability and elongation property, the present invention is able to solve the problems of the conventional bio-material.