CERAMIC MATERIAL, POWDER, AND LAYER SYSTEM COMPRISING THE CERAMIC MATERIAL

Abstract

An improved ceramic material for heat insulation with selection of specific stabilizers and adapted proportions, includes zirconium oxide with 0.2 wt. % to 8.0 wt. % of the base stabilizers: yttrium oxide (Y.sub.2O.sub.3), hafnium oxide (HfO.sub.2), cerium oxide (CeO.sub.2), calcium oxide (CaO), and/or magnesium oxide (MgO), wherein at least yttrium oxide (Y.sub.2O.sub.3) is used, and optionally at least one of the additional stabilizers: 0.2 wt. % to 20 wt. % of erbium oxide (Er.sub.2O.sub.3) and/or ytterbium oxide (Yb.sub.2O.sub.3).

Claims

1. A ceramic material based on zirconium oxide (ZrO.sub.2) with 0.2 wt % to 8.0 wt % of base stabilizers:, more particularly with 0.2 wt % to 6.0 wt % of base stabilizers: yttrium oxide (Y.sub.2O.sub.3), hafnium oxide (HfO.sub.2), cerium oxide (CeO.sub.2), calcium oxide (CaO) and/or magnesium oxide (MgO), wherein at least yttrium oxide (Y.sub.2O.sub.3) is used, and optionally at least one of the additional stabilizers: 0.2 wt % to 20 wt % of erbium oxide (Er.sub.2O.sub.3) and/or ytterbium oxide (Yb.sub.2O.sub.3).

2. The ceramic material as claimed in claim 1, comprising: at least 0.5 wt % and not more than 6.0 wt % of yttrium oxide (Y.sub.2O.sub.3).

3. The ceramic material as claimed in claim 1, comprising: 2.5 wt % to 5.5 wt % of yttrium oxide (Y.sub.2O.sub.3), more particularly 3.0 wt % to 5.0 wt % of yttrium oxide (Y.sub.2O.sub.3), especially 3.5 wt % to 4.0 wt % of yttrium oxide (Y.sub.2O.sub.3).

4. The ceramic material as claimed in claim 1, comprising: 1.5 wt % to 3.0 wt % of yttrium oxide (Y.sub.2O.sub.3), more particularly 2.0 wt % to 2.5 wt % of yttrium oxide (Y.sub.2O.sub.3).

5. The ceramic material as claimed in claim 1, which comprises: at least yttrium oxide (Y.sub.2O.sub.3) and hafnium oxide (HfO.sub.2) as base stabilizers, and more particularly comprises only yttrium oxide (Y.sub.2O.sub.3) and hafnium oxide (HfO.sub.2) as base stabilizers.

6. The ceramic material as claimed in claim 1, wherein the hafnium oxide (HfO.sub.2) content is 0.2 wt % to 4.0 wt %, more particularly 0.6 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2), especially 0.8 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2).

7. The ceramic material as claimed in claim 1, which comprises: at least one of the additional stabilizers erbium oxide (Er.sub.2O.sub.3) and/or ytterbium oxide (Yb.sub.2O.sub.3).

8. The ceramic material as claimed in claim 1, comprising, more particularly consisting of, ZrO.sub.2—HfO.sub.2—Y.sub.2O.sub.3—Yb.sub.2O.sub.3.

9. (canceled)

10. The ceramic material as claimed in claim 1, comprising: 5.5 wt % to 8.5 wt % of ytterbium oxide (Yb.sub.2O.sub.3), more particularly 6.0 wt % to 8.0 wt % of ytterbium oxide (Yb.sub.2O.sub.3), especially 6.5 wt % to 7.5 wt % of ytterbium oxide (Yb.sub.2O.sub.3).

11. The ceramic material as claimed in claim 1, comprising: 3.0 wt % to 4.5 wt % of ytterbium oxide (Yb.sub.2O.sub.3), more particularly 3.5 wt % to 4.0 wt % of ytterbium oxide (Yb.sub.2O.sub.3).

12. (canceled)

13. (canceled)

14. The ceramic material as claimed in claim 1, wherein the hafnium oxide (HfO.sub.2) content is 0.2 wt % to 2.0 wt %, more particularly 0.6 wt % to 2.0 wt % of hafnium oxide (HfO.sub.2), especially 0.8 wt % to 2.0 wt % of hafnium oxide (HfO.sub.2).

15. The ceramic material as claimed in claim 1, wherein the hafnium oxide (HfO.sub.2) content is 2.0 wt % to 4.0 wt %, more particularly 2.4 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2), especially 3.0 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2).

16. A ceramic powder comprising, more particularly consisting of, a composition of a material as claimed in claim 1.

17. A system of layers at least comprising: a metallic substrate, optionally a metallic adhesion promoter layer, and an at least one ceramic layer (10.sup.I, 10.sup.II, 10.sup.III, 10.sup.IV) based on the ceramic material as claimed in claim 1.

18. The layer system as claimed in claim 17, comprising: a metallic adhesion promoter layer between the ceramic layer (13.sup.II, 13.sup.IV; 10.sup.I, 10.sup.III) and the metallic substrate, more particularly directly on the substrate, wherein the adhesion promoter layer comprises an alloy of the type NiCoCrAlY—X, X being optionally=Ta, Re and/or Si, more particularly NiCoCrAlY or NiCoCrAlY—Ta.

19. The layer system as claimed in claim 17, wherein a ceramic sublayer (13.sup.II, 13.sup.IV) is present below the ceramic layer (10.sup.II, 10.sup.IV), which more particularly is at least 20% thinner in configuration and comprises yttrium-stabilized zirconium oxide (YSZ), more particularly 8YSZ, i.e., zirconium oxide stabilized with 3 mol % to 4 mol % of yttrium.

20. The layer system as claimed in claim 17, which comprises a segmentation, more particularly by means of relatively long vertical cracks (14; 15, 15.sup.I), in the one or more ceramic layers (10.sup.III, 10.sup.IV; 13.sup.IV), more particularly also in the ceramic sublayer (13.sup.IV).

21. The layer system as claimed in claim 20, in which the segmentation is present by means of vertical cracks (15, 15.sup.I) only in the outermost ceramic layer (10.sup.III, 10.sup.IV).

22. The layer system as claimed in claim 20, in which the segmentation runs by means of vertical cracks through both ceramic layers (10.sup.III; 13.sup.IV).

23. The layer system as claimed in claim 20, in which numerous vertical cracks extend up to the attachment layer.

24. The layer system as claimed in claim 22, in which a number of, more particularly numerous, vertical cracks extend from the surface up to the attachment layer.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0009] FIGS. 1 to 4 show exemplary embodiments of the invention.

DETAILED DESCRIPTION OF INVENTION

[0010] The zirconium oxide is stabilized with 0.2 wt % to 8 wt %, more particularly with 0.2 wt % to 6.0 wt %, of base stabilizers: yttrium oxide, hafnium oxide, cerium oxide, calcium oxide and/or magnesium oxide and optionally with additional stabilizers— 0.2 wt % to 20 wt % of erbium oxide and/or ytterbium oxide.

[0011] Yttrium oxide is used in any case and at least one of the base stabilizers hafnium oxide, cerium oxide, calcium oxide and/or magnesium oxide is used.

[0012] This ceramic composition may be prepared as a powder, and so further additions, as in the use of abrasive layers, comprise cubic boron nitride or other abrasive particles.

[0013] In a layer system 1.sup.I (FIG. 1) a ceramic layer 10.sup.I is applied to metal, the substrate 4 present, in the case of nickel- or cobalt-based superalloys used preferably, being a metallic adhesion layer 7 which forms aluminum oxide (TGO; not shown), with the metallic adhesion promoter layer constituting preferably an aluminide, platinum-aluminide or, as a basis, an NiCoCrAlY alloy, optionally with x=Ta, Re, Fe and/or Si.

[0014] The ceramic layer of the ceramic material in accordance with the invention may be produced by means of EB-PVD, plasma spraying (APS, etc.), etc. and has a columnar structure or a segmented structure.

[0015] The layer 10.sup.I, 10″, 10′″, 10.sup.IV (FIGS. 2-4) preferably has a layer thickness of 100 μm to 1000 μm.

[0016] As shown in FIG. 2, a ceramic layer 10.sup.II as in FIG. 1 may also have a ceramic sublayer 13.sup.II, the layer thickness of which, however, is at least 20% thinner in configuration than that of the ceramic material of the invention in the ceramic layer 10.sup.II.

[0017] The ceramic sublayer 13.sup.II preferably comprises 8YSZ, i.e., zirconium oxide stabilized with 3 mol % to 4 mol % of yttrium, and is therefore distinctly different from the material of the ceramic layer 10.sup.II.

[0018] FIGS. 3 and 4 show further examples of layer structures 1.sup.III, 1.sup.IV of the invention.

[0019] According to FIG. 3, in comparison to FIG. 1, there is a segmented ceramic layer 10.sup.III of a layer system 1.sup.III, which comprises numerous, relatively long and vertical cracks 15, 15.sup.I, starting from the surface 18 of the outermost ceramic layer 10.sup.III, and extending very largely over the entire ceramic layer thickness, here in particular up to the metallic adhesion layer 7 or the TGO thereof (not shown).

[0020] A layer system 1.sup.IV may also comprise a ceramic attachment layer 13.sup.IV (FIG. 4) for the outermost TBC 10.sup.IV, in which case the attachment layer 13.sup.IV may be configured as described in FIG. 2.

[0021] The outermost ceramic layer 10.sup.IV is more particularly configured like the outermost layer 10.sup.III in FIG. 3.

[0022] In the ceramic attachment layer 13.sup.IV, however, cracks 14 extend, preferably likewise vertical, which extend through both ceramic layers 10.sup.IV, 13.sup.IV.

[0023] The relatively long cracks have been formed by specific process parameters or production methods, and do not represent cracks between multiple grains.

Exemplary Embodiments

[0024] ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2
ZrO.sub.2+Y.sub.2O.sub.3+MgO
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2
ZrO.sub.2+Y.sub.2O.sub.3+CaO
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO
ZrO.sub.2+Y.sub.2O.sub.3+MgO+HfO.sub.2
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+HfO.sub.2
ZrO.sub.2+Y.sub.2O.sub.3+MgO+CaO
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+CaO
ZrO.sub.2+Y.sub.2O.sub.3+CaO+CeO.sub.2+HfO.sub.2
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+MgO+CaO
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+CaO
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+HfO.sub.2
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+CeO.sub.2+MgO
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+MgO+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+Yb.sub.2O.sub.3 (particularly preferred)
ZrO.sub.2+Y.sub.2O.sub.3+CaO+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+MgO+HfO.sub.2+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+HfO.sub.2+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+MgO+CaO+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+CaO+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CaO+CeO.sub.2+HfO.sub.2+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+MgO+CaO+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+CaO+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+HfO.sub.2+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+CeO.sub.2+MgO+Yb.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+MgO+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CaO+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+MgO+HfO.sub.2+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+HfO.sub.2+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+MgO+CaO+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+CaO+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CaO+CeO.sub.2+HfO.sub.2+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+MgO+CaO+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+CaO+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+HfO.sub.2+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+CeO.sub.2+MgO+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+MgO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3 (particularly preferred)
ZrO.sub.2+Y.sub.2O.sub.3+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+MgO+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+MgO+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CaO+CeO.sub.2+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+MgO+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+CaO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+CeO.sub.2+MgO+HfO.sub.2+Yb.sub.2O.sub.3+Er.sub.2O.sub.3
ZrO.sub.2+Y.sub.2O.sub.3+HfO.sub.2+CaO+CeO.sub.2+MgO+Yb.sub.2O.sub.3+Er.sub.2O.sub.3

[0025] The ceramic material comprises preferably 2.5 wt % to 5.5 wt % of yttrium oxide (Y.sub.2O.sub.3), more particularly 3.0 wt % to 5.0 wt % of yttrium oxide (Y.sub.2O.sub.3), especially 3.5 wt % to 4.0 wt %.

[0026] The ceramic material may also comprise preferably 1.5 wt % to 3.0 wt % of yttrium oxide (Y.sub.2O.sub.3), more particularly 2.0 wt % to 2.5 wt % of yttrium oxide (Y.sub.2O.sub.3).

[0027] The ceramic material preferably comprises: hafnium oxide (HfO.sub.2) at 0.2 wt % to 4.0 wt %, more particularly 0.5 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2), especially 0.6 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2).

[0028] For better, i.e., lower, thermal conductivity, the ceramic material preferably comprises: hafnium oxide (HfO.sub.2) at 0.2 wt % to 2.0 wt %, more particularly at 0.6 wt % to 2.0 wt % of hafnium oxide (HfO.sub.2), especially at 0.8 wt % to 2.0 wt % of hafnium oxide (HfO.sub.2).

[0029] For better thermal stability the ceramic material preferably comprises: hafnium oxide (HfO.sub.2) at 2.0 wt % to 4.0 wt %, more particularly 2.4 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2), especially 4.0 wt % to 4.0 wt % of hafnium oxide (HfO.sub.2).

[0030] The ceramic material preferably comprises 5.5 wt % to 8.5 wt % of ytterbium oxide (Yb.sub.2O.sub.3), more particularly 6.0 wt % to 8.0 wt % of Yb.sub.2O.sub.3, especially 6.5 wt % to 7.5 wt % of Yb.sub.2O.sub.3.

[0031] The ceramic material comprises preferably 3.0 wt % to 4.5 wt % of ytterbium oxide (Yb.sub.2O.sub.3), more particularly 3.5 wt % to 4.0 wt % of ytterbium oxide (Yb.sub.2O.sub.3).

[0032] The ceramic material also preferably comprises 2.0 wt % to 4.0 wt % of Er.sub.2O.sub.3, more particularly 2.5 wt % to 3.5 wt % of Er.sub.2O.sub.3.

[0033] With further preference the ceramic material comprises (6.0-x) wt % of Y.sub.2O.sub.3+(2-4) x wt % of Yb.sub.2O.sub.3/Er.sub.2O.sub.3, i.e., at 4.0 wt % of Y.sub.2O.sub.3, x corresponds to 2 and the fraction of Yb.sub.2O.sub.3/Er.sub.2O.sub.3 is (2-4)*2, i.e., between 4 wt % and 8 wt %.