TURBOPUMP WITH A SINGLE PIECE HOUSING AND A SMOOTH ENAMEL GLASS SURFACE

Abstract

A turbopump such as a liquid oxygen (LOX) turbopump for a liquid rocket engine is formed using a metal additive manufacturing process in which a single-piece impeller is formed within a single piece housing, the impeller being trapped within the single piece housing. The impeller is formed with an axial bore in which a shaft is inserted after the impeller and housing have been formed. The turbopump includes a protective coating that forms a reaction resistant surface on the base metal in areas of the base metal that are exposed to an oxidizer during pumping. The protective coating may be an enamel glass, a superalloy layer beneath an enamel glass layer, a composite layer of a mixture of enamel glass and superalloy, a composite mixture of oxide and superalloy, or a composite layer of a mixture of enamel glass, superalloy, and oxide.

Claims

1. A liquid rocket engine oxidizer turbopump comprising: a housing (29) with a liquid oxygen inlet and a liquid oxygen outlet; an impeller (25) rotatable within the housing (29); and a forward bearing (12) and an aft bearing (12) to rotatably support the impeller (25) within the housing (29), both the housing (29) and the impeller (25) being formed as a single piece with the impeller (25) trapped within the housing (29).

2. The liquid rocket engine oxidizer turbopump of claim 1, wherein an entirety of surfaces (35) of the oxidizer turbopump that are exposed to an oxidizer during pumping have a protective coating (36) of at least one protective material to prevent reaction of the oxidizer with the surfaces (35).

3. The liquid rocket engine oxidizer turbopump of claim 2, wherein the protective coating (36) includes enamel glass.

4. The liquid rocket engine oxidizer turbopump of claim 3, wherein the enamel glass is a first layer (36b) of the protective coating (36), the protective coating (36) further including a second layer (36a) that includes a superalloy, the second layer (36a) being beneath the first layer (36b).

5. The liquid rocket engine oxidizer turbopump of claim 4, wherein the superalloy is a Mondaloy material, the Mondaloy material being at least one of Mondaloy 100 and Mondaloy 200.

6. The liquid rocket engine oxidizer turbopump of claim 2, wherein the protective coating (36) includes a superalloy.

7. The liquid rocket engine oxidizer turbopump of claim 1, wherein the oxidizer turbopump is a centrifugal pump.

8. The liquid rocket engine oxidizer turbopump of claim 2, wherein the protective coating (36) is a mixture that includes Mondaloy powder and enamel glass powder that is deposited using a thermal spray process.

9. The liquid rocket engine oxidizer turbopump of claim 8, wherein the coating (36) mixture further includes an oxide.

10. The liquid rocket engine oxidizer turbopump of claim 9, wherein the oxide is one of aluminum oxide and yttria stabilized zirconia.

11. An oxidizer turbopump comprising: a single-piece housing (29); the single-piece housing (29) having an inner minimum diameter; a single-piece impeller (25) having a maximum outer diameter greater than the inner minimum diameter of the single-piece housing (29); and a forward bearing (12) and an aft bearing (12) to rotatably support the single-piece impeller (25) within the single-piece housing (29).

12. The oxidizer turbopump of claim 11, wherein surfaces (35) of the oxidizer turbopump that are exposed to an oxidizer during pumping have a protective coating (36) to prevent reaction of the oxidizer with the surfaces (35), the protective coating (36) including enamel glass.

13. The oxidizer turbopump of claim 11, wherein: the single-piece impeller (25) includes an axial bore (30); and a shaft (26) is inserted within the axial bore (30).

14. The oxidizer turbopump of claim 12, wherein the single-piece impeller (25) is manufactured within the one-piece housing (29) and the protective coating (36) is deposited on the surfaces (35) within the one-piece housing (29).

15. The oxidizer turbopump of claim 12, wherein the protective coating (36) further includes a superalloy.

16. The oxidizer turbopump of claim 15, wherein the superalloy is a Mondaloy material.

17. The oxidizer turbopump of claim 15, wherein the superalloy is deposited on the surfaces (35) in a first layer (36a) and the enamel glass is deposited on the surfaces (35) in a second layer (36b), the first layer (36a) being beneath the second layer (36b)

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] A more complete understanding of the present invention, and the attendant advantages and features thereof, will be more readily understood by reference to the following detailed description when considered in conjunction with the accompanying drawings wherein:

[0009] FIG. 1 shows a cross section view of a LOX turbopump;

[0010] FIG. 2 shows a cross section view of a LOX turbopump having a single-piece housing;

[0011] FIG. 3 shows a liquid rocket engine turbopump with a coating of protective material of the present invention;

[0012] FIG. 4 shows a close-up section view of a surface of the turbopump with the protective coating of the present invention; and

[0013] FIG. 5 shows a close-up section view of a surface of the turbopump with a two-layer protective coating of the present invention.

DETAILED DESCRIPTION

[0014] The present invention is liquid oxygen (LOX) turbopump used in a liquid rocket engine in which the rotor (which may also be referred to as the impeller) is formed by a metal additive manufacturing process and formed within a single piece housing that is also formed by a metal additive manufacturing process.

[0015] FIG. 1 shows a LOX turbopump with an extremely efficient design. The LOX turbopump is formed from only eleven part numbers (not including fasteners) and is very compact. The pump is located in the center and is a back-to-back design similar to the space shuttle main engine (SSME) high pressure oxidizer turbopump (HPOTP). This reduces or eliminates rotor axial thrust imbalance. There is an inducer in front of each impeller 15 to improve cavitation performance and the impellers 15 are shrouded to minimize secondary flow leakage without requiring extremely tight tolerance. The impeller 15 is rotatable within the housing due to bearings 12 that straddle the impeller 15, and the impeller 15 is cooled by recirculating the inlet LOX with the natural pumping of the impeller 15. The bearings 12 are axially held on the impeller 15 by identical spanner nuts 14. To minimize assembly time and components, the impeller 15 is integral with the shaft. In other words, the impeller 15 functions as both the impeller 15 and the shaft, and the turbopump does not include a separate shaft in addition to the impeller. To minimize cost, the two bearings 12 are the same, the spanner nuts 14 are the same, and the buffer seal 21 is the same as the fuel pump buffer seal. The housing 11 also includes a fluid inlet and a fluid outlet, such as a liquid oxygen inlet and a liquid oxygen outlet. Finally, since the size is so small and the discharge pressure is low, the rotor design speed is low so the stresses on the parts will be extremely low.

[0016] The LOX turbopump in FIG. 1 includes a cover plate 13 held on by several screws 20, a forward seal 16, and aft seal 17, a main housing 11, a nut 18 to secure the forward and aft seals 16 and 17 to the housing 11, an aft housing 19, and springs 22.

[0017] FIG. 2 shows a LOX turbopump that is formed by a metal additive manufacturing process in which a single-piece (or one-piece) impeller 25 is formed within a single-piece (or one-piece) housing 29. The double suction impeller 25 is manufactured within the housing 29 and the impeller 25 is rotatable within the housing 29 due to bearings 12. The housing 29 may include a fluid inlet and a fluid outlet, such as a liquid oxygen inlet and a liquid oxygen outlet, screws 20, and springs 22 as discussed above regarding FIG. 1. Forward and aft bearing support surfaces may be machined onto the outer surfaces of the impeller, which support a forward bearing and an aft bearing, respectively, to rotatably support the impeller 25. Additionally, the forward seal 16, the aft seal 17, and the nut 18 of the FIG. 1 embodiment are eliminated and the requirement to finish machining of the housing for the bearing outer diameter (OD) 27 of the FIG. 1 embodiment is eliminated. Additionally, the FIG. 2 embodiment provides for the elimination of all machining operations from the shaft 26, as the shaft is inserted into the impeller 25 as a separate component, as discussed below. The FIG. 2 embodiment also eliminates the aft housing 19 and associated interface flange, eliminates the seal and finish machining, and eliminates the screws required in the FIG. 1 embodiment.

[0018] In the FIG. 2 design, a double suction impeller 25 is trapped within the single-piece housing 29. Put another way, the housing 29 has a minimum inner diameter D.sub.MinI and the impeller 25 has a maximum outer diameter D.sub.MaxO, the maximum outer diameter D.sub.MaxO of impeller 25 being greater than the minimum inner diameter D.sub.MinI of the housing 29. This is achieved by printing the components simultaneously within a metal additive manufacturing process such as the selective laser melting (SLM) machine. Then, powder and support structure (if required) removal is performed. The impeller 25 includes an axial bore 30 into which a shaft 26 is inserted once the impeller 25 is created within the housing 29. The bearings 12 are installed on the ends of the shaft 26 and a shaft tie bolt is threaded on one end of the shaft 26 to secure the bearings 12 (for example, a forward bearing and an aft bearing) between the housing 29 and the impeller 25. Conventional manufacturing is required for the bearings 12 due to high precision requirements needed. The cover plate and buffer seal form support surfaces for outer races of the bearings 12. The impeller 25 is formed with forward and aft labyrinth seal teeth all as a single piece, and the housing 29 is formed with seal surfaces for the labyrinth teeth that form forward and aft labyrinth seals 28 between the impeller 25 and the housing 29. With the exception of the shaft tie-bolt and the shaft seal, all other components are printed on an SLM machine.

[0019] The single-piece housing 29 of FIG. 2 eliminates potential gaps between surfaces that would be held together by bolts, such as in the two-piece housing 11 shown in FIG. 1. Additionally, stress from internal pressure would be evenly spread throughout the housing 29 without having to pass from one section to another, such as through the two bolts 20 that connect the main housing 11 and aft housing 19 in FIG. 1.

[0020] Rotor balancing is another critical area. Typically, an assembly balance of the rotor is performed for turbopump rotors. That is, the full rotor, such as the impeller 25 of FIG. 2, is assembled and balanced on a balance machine. Since the impeller 25 is printed inside the single-piece housing 29, this method cannot be used without special tooling. In the present invention, a method of trim balancing is used where the impeller 25 is spun up to various high speeds and accelerometers on the housing along with a proximity probe looking at the impeller 25 is used to determine the impeller imbalance. The imbalance is corrected by grinding locations on each end of the shaft.

[0021] The present invention is a LOX turbopump used in a liquid rocket engine in which the impeller 25 is formed by a metal additive manufacturing (MAM) process and formed within a single-piece housing 29 that is also formed by a metal additive manufacturing process. By printing the impeller 25 within a one-piece housing 29, a dramatic reduction in part count, procurement activities, and assembly time is achieved over the prior art, which directly translates into a reduction in recurring cost and lead time. These reductions are estimated to reduce the cost of the LOX turbopump by approximately 40%. The turbomachinery for a typical rocket engine accounts for about one-third of the cost of the total engine. Thus, significant reductions in turbomachinery cost have large impacts on the overall cost of the engine.

[0022] The metal printing process produces a relatively rough surface on the parts. FIG. 4 shows a surface 35 of the turbopump covered with a protective layer 36. The layer 36 may be a single material (for example, MONDALOY), a mixture of materials (for example, a mixture of MONDALOY and enamel glass powder, and/or oxide powder), or may include several distinct layers (for example, a layer of MONDALOY on the surface 35 and a enamel glass layer on the MONDALOY layer). Thus, the present invention also applies a protective coating of 36 of one or more materials to form a smooth surface that functions to increase the efficiency of the pump. Because the impeller 25 is formed within a single-piece housing 29, a machining tool that would form a smooth surface cannot be used because of lack of space to insert the tool. All surfaces of the turbopump that are exposed to the oxidizer (liquid oxygen) may have a protective coating 36 of one or more layers of one or more protective materials, such as a material that is resistant to corrosion, oxidation, impact, and/or heat. In one embodiment, an enamel glass coating can be applied over the required surfaces while the impeller and even the housing are rotating to form a smooth surface. The enamel glass protective coating 36 would also provide a burn resistance to the pump surfaces that would be exposed to the liquid oxygen. Because of the use of the burn resistant protective coating, INCONEL 718 (Huntington Alloys Corporation) can be used as the base metal material which is strong enough for use as the rotor material and cheap enough to keep costs down. INCONEL 718 is a nickel based superalloy which retains high strength at elevated temperatures and has high strength up to 1,300 degrees F., good cryogenic ductility, and good weldability. The enamel glass coating 36 is an ambient temperature applied coating using a spray or a brush to apply to selected surfaces. Or, the entire turbopump with the impeller 25 and the housing 29 can be submerged within a slurry of the liquid coating material to apply the coating 36. A masking tape can be used to mask surfaces 35 where the coating 36 is not to be applied.

[0023] The turbopump is formed using a metal powder bed fusion process in which thin layers of powder are applied to a platen, and then a laser is used to fuse or melt the powder to form a solid metal material. Subsequent layers of the powder are laid down and then selectively fused by the laser to build the parts. The turbopump is built up along the rotational axis of the turbopump in a vertical direction with surfaces between the impeller 25 and the housing 29 for the forward and aft bearings 12 to be placed. This way both the housing 29 and the impeller 25 can be formed.

[0024] After the impeller 25 and housing 29 have been formed by the powder bed fusion process, the turbopump is placed in a horizontal position and masking tape used over surfaces 35 that will not have the enamel glass protective coating 36 applied. The enamel glass coating 36 is formed over selected surfaces 35 by using a spray nozzle or a brush to apply the coating 36 while the impeller 25 is slowly rotating within the housing 29 to spread the coating 36. The housing 29 can also be rotated. The turbopump is then fired to harden the glass coating. The coating 36 is applied over the rough surface of the printed part to not only smooth the surface, but to add protection against heat, against oxidation, against erosion, and even against damage from a foreign object damage (FOD). Any masking tape used can be removed before the firing process. After the coating 36 has been hardened, the two bearings 12 are inserted and the open ends of the housing 29 are enclosed with cover plates 13.

[0025] The impeller 25 and the housing 29 are formed with bearing support surfaces that can be machined afterwards because the bearing surfaces are located close to the two open ends of the single-piece housing 29. Bearings 12 can then be inserted into position to rotatably support the rotor 25 within the housing 29 and the open end or ends of the housing closed by securing a cover plate 13. The opposite end would be connected to a driving mechanism such as an input shaft from a turbine.

[0026] The rocket engine uses a turbopump to pump both a liquid fuel and a liquid oxidizer to a common combustion chamber. For example, the liquid oxidizer would be liquid oxygen and the liquid fuel would be liquid hydrogen. A common shaft 31 is driven by a turbine 32 with the fuel pump 33 on one end and the oxidizer pump 34 on the opposite end (as shown in FIG. 3). The oxidizer pump 34 and the fuel pump 33 are typically centrifugal pumps because of the high pressures obtained. To prevent cavitation in the centrifugal pumps, an inducer 37 is used upstream of the oxidizer pump 34 and/or the fuel pump 33 to increase the pressure so as to eliminate cavitation in the higher pressure pump. To prevent the combustion resistance in the presence of high temperature and high pressure liquid or gaseous oxygen, the surfaces 35 of the turbopump that are exposed to the oxidizer are coated with a protective coating 36.

[0027] In a second embodiment, the protective coating 36 may include a superalloy, such as a MONDALOY material such as at least one of the MONDALOY 100 or 200 materials. Thus, the turbo-pump can be constructed with the prior art metal materials for strength and light weight such as stainless steels or INCONEL, but have the combustion resistance to the high temperature and high pressure liquid or gaseous oxygen due to the MONDALOY coating on its surfaces on which the liquid or gaseous oxygen would make contact. No MONDALOY coating is required on the liquid hydrogen fuel pumps. The MONDALOY material is disclosed in US 2010/0266442 A1 by Jacinto et al., published on Oct. 21, 2010, and entitled BURN-RESISTANT AND HIGH TENSILE STRENGTH METAL ALLOYS, the entire disclosure of which is incorporated herein by reference.

[0028] The MONDALOY coating can also be used on other high pressure pumps or turbine that are exposed to liquid or gaseous oxygen. Because of the high pressure, the base metal material must be a high strength material such as stainless steel. Certain high strength materials are very reactive to oxygen. If the pump or turbine is exposed to oxygen, then the MONDALOY protective coating 36 on the surfaces 35 that are exposed to the oxygen will provide for the high strength required while also protecting the base material from reacting to the oxygen.

[0029] In another embodiment of the present invention, an enamel glass powder is mixed in with the MONDALOY powder to produce a protective coating 36 formed from a composite of MONDALOY and enamel glass that will have properties of the MONDALOY material and with a burn resistance that is produced with the enamel glass material. When the glass powder is fired, it becomes an enamel.

[0030] In another embodiment, the MONDALOY and enamel glass each form a protective coating. The MONDALOY and an enamel glass are deposited using a thermal spray process. For example, the MONDALOY layer 36a may be on the surfaces 35 of the turbopump that are exposed to the oxidizer and the enamel glass layer 36b may be on the MONDALOY layer (put another way, the MONDALOY layer 36a may be located beneath the enamel glass layer 36b, as shown in FIG. 5). The powder would be made of the enamel glass composition.

[0031] In another embodiment, the MONDALOY and enamel glass are combined to form a multi-component protective coating 36. The two constituents can be pre-blended, independently injected into a thermal plumb to allow for functional grading of the coating, or co-deposited on the surface 35 using a thermal spray process. Use of the fired enamel glass coating with the MONDALOY material has been shown to arrest burning of the metal substrate. Thus, use of the enamel glass constituent processed as a powder and deposited using thermal spray would enhance the burn resistance of the MONDALOY material in the coating.

[0032] In another embodiment, a surface can be created by coating a multiple component surface coating of MONDALOY and an oxide that is co-deposited using a thermal spray process. The two constituents can be pre-blended or independently injected into the thermal plumb to allow for functional grading of the coating. The addition of the oxide would enhance the burn resistance of the MONDALOY coating.

[0033] In still another embodiment, a surface can be created with high oxide content MONDALOY coating 36 through adjustment of the thermal spray parameters. MONDALOY powder is produced with little or no oxide impurities. Thermal spraying in air creates oxides in the coating deposit due to the interaction of the metal powder with a thermal heating source. Thermal spray parameters can be adjusted to regulate the oxide content of the coating deposit. The addition of the oxide content will enhance a burn resistance of the MONDALOY coating.

[0034] Instead of the enamel glass powder, an oxide powder can be used to produce similar properties for the protective coating 36 containing MONDALOY to resist burning. As a non-limiting example, aluminum oxide or yttria stabilized zirconia can be added as the oxide to the MONDALOY powder to create the coating. Combinations of these three materials (MONDALOY, enamel glass, and oxide powder) can be used to produce the coating. Thus, a coating can be produced from MONDALOY powder and glass powder, or from MONDALOY powder and oxide powder, or from MONDALOY powder and glass powder and oxide powder.

[0035] In still another embodiment of the present invention, a burn resistant protective coating 36 that uses enamel glass fired with MONDALOY powder can be produced that will allow for higher operating temperatures (prevent thermal creep) and better manage the coefficient of thermal expansion mismatch. This embodiment will add MONDALOY powder after spraying on enamel slurry before firing the composition. The attributes of the coating are burn resistance, low cost, and easy application to complex geometry parts or internal passages such as in air cooled airfoils.

[0036] Further features of the invention are disclosed in the numbered Embodiments set forth below.

Embodiment 1

[0037] A liquid rocket engine oxidizer turbopump comprising: a housing with a liquid oxygen inlet and a liquid oxygen outlet; an impeller rotatable within the housing; a forward bearing and an aft bearing to rotatably support the impeller within the housing; both the housing and the impeller are formed as a single piece with the impeller trapped within the housing; and surfaces of the oxidizer pump exposed to an oxidizer during pumping having a composite coating of enamel glass to prevent reaction of the oxidizer.

Embodiment 2

[0038] A liquid rocket engine oxidizer turbopump as recited in Embodiment 1, and further comprising: the surface of the oxidizer pump includes a coating of Mondaloy material below the enamel glass coating.

Embodiment 3

[0039] A liquid rocket engine oxidizer turbopump as recited in Embodiment 2, and further comprising: the Mondaloy coating is Mondaloy 100 or Mondaloy 200.

Embodiment 4

[0040] A liquid rocket engine oxidizer turbopump as recited in Embodiment 1, and further comprising: the oxidizer pump is a centrifugal pump.

Embodiment 5

[0041] A liquid rocket engine oxidizer turbopump as recited in Embodiment 2, and further comprising: the composite coating of Mondaloy material and enamel glass is a mixture of Mondaloy powder and enamel glass powder that is deposited using a thermal spray process.

Embodiment 6

[0042] A liquid rocket engine oxidizer turbopump as recited in Embodiment 2, and further comprising: the Mondaloy and glass includes an oxide in the coating.

Embodiment 7

[0043] A liquid rocket engine oxidizer turbopump as recited in Embodiment 2, and further comprising: the oxide is one of aluminum oxide or yttria stabilized zirconia.

Embodiment 8

[0044] A liquid rocket engine oxidizer turbopump comprising: a single piece housing with an oxidizer inlet and an oxidizer outlet and a forward opening and an aft opening; the single piece housing having an inner minimum diameter; a single piece impeller having a maximum outer diameter greater than the inner minimum diameter of the single piece housing; a forward bearing and an aft bearing to rotatably support the single piece impeller within the single piece housing; and surfaces of the oxidizer pump exposed to an oxidizer during pumping having a coating of enamel glass to prevent reaction of the oxidizer.

Embodiment 9

[0045] A liquid rocket engine oxidizer turbopump as recited in Embodiment 8, and further comprising: the single piece impeller includes an axial bore; a shaft is inserted within the axial bore; and a shaft tie bolt is threaded on one end of the shaft to secure the forward and aft bearings between the housing and the impeller.

Embodiment 10

[0046] A liquid rocket engine oxidizer turbopump as recited in Embodiment 8, and further comprising: a forward cover plate encloses a forward opening of the housing; and an aft buffer seal encloses an aft opening of the housing.

Embodiment 11

[0047] A liquid rocket engine oxidizer turbopump as recited in Embodiment 10, and further comprising: forward cover plate forms a support surface for the forward bearing; and the aft buffer seal forms a support surface for the aft bearing.

Embodiment 12

[0048] A liquid rocket engine oxidizer turbopump as recited in Embodiment 8, and further comprising: a Mondaloy coating is used below the enamel glass coating.

[0049] It will be appreciated by persons skilled in the art that the present invention is not limited to what has been particularly shown and described herein above. In addition, unless mention was made above to the contrary, it should be noted that all of the accompanying drawings are not to scale. A variety of modifications and variations are possible in light of the above teachings without departing from the scope and spirit of the invention, which is limited only by the following claims.