NOVEL COKE WITH ADDITIVES

Abstract

Coke including additives that are accumulated at the yield points or in the regions surrounded by the yield points. For homogeneous distribution, the additives are continuously dosed into the delayed coker during the filling time. The dosing can be carried out by powdery blowing with an inert gas (nitrogen) or also distributed in a slurry consisting of the reaction components and a partial flow of the coker feed (vacuum resid, pytar, decant oil or coal-tar distillates). According to an advantageous form of embodiment, the additives may optionally have a diameter of between 0.05 mm and 5 mm, preferably between 1 mm and 3 mm. Advantageously, the additives can be selected from at least one of acetylene coke, fluid coke, flexi coke, shot coke, carbon black, non-graphitisable carbons (chars), non-graphitic anthracite, silicon carbide, titanium carbide, titanium diboride or mixtures thereof.

Claims

1-11. (canceled)

12. A coke comprising: additives, the additives are accumulated at the yield points or in the regions surrounded by the yield points.

13. The coke according to claim 12, wherein the coke is chosen from the group consisting of petroleum coke, coal-tar pitch coke or from the residues of coal gasification, coal hydrogenation or also the cokes obtained from Fischer-Tropsch synthesis or from a petrol/coal-tar pitch mixture obtained from the mixture of petrol and coal-tar pitch residues, or any mixture of the named cokes.

14. The coke according to claim 12, wherein the additives are accumulated at the yield points or are embedded in the regions surrounded by the yield points or are both accumulated at the yield points and embedded in the regions surrounded by the yield points.

15. The coke according to claim 14, wherein the additives are selected from the group consisting of acetylene coke, fluid coke, flexi coke, shot coke, carbon black, non-graphitisable carbons (chars), non-graphitic anthracite, silicon carbide, titanium carbide, titanium diboride or mixtures thereof.

16. The coke according to claim 15, wherein the additives have a diameter of 0.1 to 49 m.

17. The coke according to claim 15, wherein the additives have a diameter of 0.05 mm to 5 mm.

18. The coke according to claim 15, wherein the additives are present as a mixture of additives with a diameter of 0.1 m to 49 m and a diameter of 0.05 mm to 5 mm.

19. The coke according to claim 16 wherein the proportion of additives is 0.5 to 8 wt.-%.

20. The coke according to claim 17 wherein the proportion of additives is 1 to 40 wt.-%.

21. The coke according to claim 18, wherein the proportion of the mixture of the additives with a diameter of 0.1 m to 49 m is 0.5 to 8 wt.-%, and the proportion of the mixture of the additives with a diameter of 0.05 mm to 5 mm is 5 to 20 wt.-%.

Description

[0042] Further features and advantages of the invention are now explained in more detail with reference to the subsequent figures, without being limited thereto.

[0043] These show, in:

[0044] FIG. 1 a schematic representation of a section from a coke with accumulation of additives at the yield points.

[0045] FIG. 2 a schematic representation of a section from a coke with accumulation of additives in the regions surrounded by the yield points.

[0046] FIG. 3 a schematic representation of a section from a coke with accumulation of additives at the yield points and in the regions surrounded by the yield points.

[0047] FIG. 1 shows a schematic representation of a section from a coke with an accumulation of additives (1) at the yield points (2). The additives (1) have a diameter which is selected from the range 0.1 m to 49 m.

[0048] FIG. 2 shows a schematic representation of a section from a coke with an accumulation of additives (3) in the regions (4) surrounded by the yield points. The additives (3) have a diameter which is selected from the range 0.05 mm to 5 mm.

[0049] FIG. 3 shows a schematic representation of a section from a coke with accumulation of additives (1) at the yield points (2) and in the regions (4) surrounded by the yield points. The additives (1) have a diameter which is selected from the range 0.1 m to 49 m. The additives (3) have a diameter which is selected from the range 0.05 mm to 5 mm.

[0050] The present invention is now explained using embodiment examples, wherein the embodiment examples do not represent any limitation of the invention.

EMBODIMENT EXAMPLE 1

[0051] For homogeneous distribution of the later reaction components in the coke material, TiO.sub.2 and B.sub.2O.sub.3 are continuously dosed, each with a particle diameter of 1-3 m and a stoichiometric ratio of 1:1, into the delayed coker during the filling time of 12 hours. The dosing can be carried out by powdery blowing with an inert gas (nitrogen) or also distributed in a slurry consisting of the reaction components and a partial flow of the coker feed (vacuum resid, pytar, decant oil or coal-tar distillates). The concentration of the reaction components conforms to the desired TiB.sub.2 concentrations in the end-product. In the present example, a slurry is dosed with the pro rata wt.-% as follows: Slurry (vacuum resid,)=84.3 wt.-%, TiO.sub.2 8.4 wt.-%, B.sub.2O.sub.3 7.3 wt.-% The result is the desired coke with the following proportions: Coke=61.6 wt.-%, TiO.sub.2=20.5 wt.-% and B.sub.2O.sub.3=17.9 wt.-%. The result is a synthetic graphite body with a finely distributed TiB.sub.2 proportion of 25.5 wt.-%, produced according to green manufacturing, baking and thermal finishing above 2200 C.

[0052] There is an additive particle percentage of 70 at the yield points.

[0053] Depending on the additive diameter, in this embodiment example the additives can be accumulated at the yield points or in the regions surrounded by the yield points. For example, the wetting behaviour of cathode blocks can be improved vis-a-vis aluminium melting. The wetting behaviour can be tailored by controlling the additive proportion.

EMBODIMENT EXAMPLE 2

[0054] A gas-calcined anthracite was ground on an impact mill to a diameter of approx. 3 m and a grain fraction of 1-3 m was produced as a result, by means of sieving. This was dispersed with 10 wt.-% in an ethylene tar. This dispersion was introduced into a delayed coker with a temperature of 490 C. Coking pressure was 6.6 bar with a coking time of 10 hours. The green petroleum coke was calcined at 1300 C. The result is an isotropic petroleum coke with a CTE of 4.5 10.sup.6 K.sup.1 and an ash content of 0.09%, wherein the boron content was 0.2 ppm. This coke is suitable for high purity isographites and reactor graphite in nuclear power plants.

[0055] In this embodiment example, the additives are accumulated at the yield points with an additive particle percentage of 70.

EMBODIMENT EXAMPLE 3

[0056] A petrol-based vacuum resid is supplied to a delayed coker at 460 C. Coking pressure was 5.0 bar with a coking time of 8 hours. During the entire coking period, 10% of the coker feed was added as a dispersion from the vacuum resid, and 10 wt.-% of acetylene coke with a diameter of 0.4 to 0.8 mm at the head of the coking drum. After calcining the green coke, the result is a petroleum coke with an embedded proportion of 4 wt.-% acetylene coke. The coke CTE was 3.5 10.sup.6 K.sup.1. Mechanical resistance was increased by 6% over a comparable coke without acetylene coke deposits. The additives in this embodiment example are accumulated in the regions surrounded by the yield points with an additive particle percentage of 70.

[0057] The use of this coke in a graphitic cathode in aluminium-fused-salt electrolysis would equate to a 1-2-year extension in lifespan.

LIST OF REFERENCE SIGNS

[0058] 1 Additive with a diameter in the range from 0.1 m to 49 m [0059] 2 Yield point [0060] 3 Additive with a diameter in the range from 0.05 mm to 5 mm [0061] 4 Regions surrounded by the yield points