DISC BRAKE PAD

Abstract

[Object]

To provide the disc brake pad including the friction material having the friction surface with the scorch treatment that can provide sufficient braking effectiveness while preventing the fading phenomenon at the initial stage of the disc brake pad usage.

[Means to Resolve]

In the disc brake pad including the friction material having the friction surface with the heat history due to the scorch treatment, the friction surface has the mixed areas including the area with the large heat history of the scorch treatment and the area with relatively small heat history of the scorch treatment. The following formula needs to be satisfied where the reduction rate of the mass of the inside of the friction material without the heat history due to the scorch treatment when performing the thermogravimetric analysis of the friction material at 500 centigrade is A, the reduction rate of the mass of the friction surface area with the largest heat history due to the scorch treatment when performing the thermogravimetric analysis at 500 centigrade is B1, and the reduction rate of the mass of the friction surface area with the relatively small heat history due to the scorch treatment relative to the friction surface area with the largest heat history when performing the thermogravimetric analysis at 500 centigrade is B2.

30≤B1/A×100≤90

50≤B2/A×100

B2/A×100−B1/A×100≤60  Formula:

Claims

1. A disc brake pad, comprising a friction material having a friction surface with a heat history due to a scorch treatment, wherein an area with a large heat history and an area with relatively small heat history both by the scorch treatment are arranged so as to be mixed on the friction surface.

2. A disc brake pad according to claim 1, wherein said disc brake pad satisfies a following formula:
30≤B1/A×100≤90
50≤B2/A×100
B2/A×100−B1/A×100≤60, where “A” represents a reduction rate of a mass of an inside of the friction material with no heat history due to the scorch treatment when performing a thermogravimetric analysis at 500 centigrade, “B1” represents a reduction rate of a mass of an area of the friction surface with the largest heat history due to the scorch treatment when performing the thermogravimetric analysis at 500 centigrade, and “B2” represents a reduction rate of a mass of an area of the friction surface with a relatively small heat history due to the scorch treatment relative to the area of the friction surface area with the largest heat history when performing the thermogravimetric analysis at 500 centigrade.

3. The disc brake pad according to claim 2, wherein 10-90% of an area of the friction surface of the friction material is scorch-treated so as to be an area with the largest heat history due to the scorch treatment.

Description

BRIEF EXPLANATION OF THE DRAWINGS

[0031] FIG. 1 is a perspective view of an entire disc brake pad of this invention;

[0032] FIG. 2 is a flow chart showing an example of the method of manufacturing the disc brake pad;

[0033] FIG. 3 is a cross section view of the disc brake pad in the process of performing the scorch treatment using a surface emitting laser module;

[0034] FIG. 4 is an explanatory view of a planar pattern of a scorch treatment layer viewing from a friction surface side of the friction material; and

[0035] FIG. 5 is an enlarged partial cross section view of disc brake pad after the scorch treatment.

EMBODIMENTS OF THE INVENTION

[0036] The disc brake pad of this invention is explained while referring to FIG. 1.

(1) Disc Brake Pad

[0037] A disc brake pad 10 has a metal back plate 11 and a friction material 12 integrally affixed to one side of the back plate 11.

[0038] In this invention, a friction surface of the friction material is arranged so that heat histories that the friction surface of the friction material receives due to a scorch treatment are not uniform and an area with large heat history and an area with relatively small heat history both due to scorch treatment are arranged so as to be mixed on the friction surface.

(2) Scorch Treatment

[0039] In the later descried manufacturing process, the scorch treatment is performed on the friction material 12 in a way to create different heat histories on the friction surface of the friction material, so that the large heat history of the scorch treatment (intensive treatment area) 13 and an area with relatively small heat history of the scorch treatment (mild treatment area) 14 are arranged so as to be mixed on the friction surface of the friction material.

[0040] Organic substances such as a cashew dust in a surface layer of the friction material are burned and ceased to exist in the intensive treatment area 13 with large heat history of the scorch treatment on the friction surface, while relatively large amount of the organic substances such as the cashew dust remains in the mild treatment area 14 with relatively small heat history of the scorch treatment on the friction surface comparing to the intensive treatment area 13 with large history of the scorch treatment on the friction material.

[0041] Here in this invention, the mild treatment area 14 with relatively small heat history of the scorch treatment can be an area of the friction surface without the heat history of the scorch treatment.

(3) Reason for Arrangement of Surface Areas with Different Heat Histories of the Scorch Treatment on the Friction Surface of the Friction Material

[0042] In this invention, the heat histories by the scorch treatment on the friction surface of the friction material 12 are arranged so that the heat histories on the friction surface are not uniform and different heat histories of the scorch treatment are arranged so as to be mixed on the friction surface of the friction material 12.

[0043] The reason for arranging the areas having the difference heat histories so as to be mixed on the friction surface of the friction material 12 is to create differences in the amount of the organic substances such as the cashew dust remaining in different areas of the friction surface of the friction material 12 and use the differences to obtain the sufficient braking effectiveness while preventing the fading phenomenon at the initial stage of the usage of a disc brake pad 10.

(3.1) Fading Resistance

[0044] The scorch treatment is performed on the friction surface of the friction material 12, and the organic substances such as the cashew dust existing in the vicinity of the friction surface are partially removed, so that the fading phenomenon at the initial stage of the usage of the disc brake pad 10 can effectively be prevented.

(3.2) Braking Effectiveness

[0045] The friction material 12 of the disc brake pad 10 of this invention has the intensive treatment area 13 with large heat history of the scorch treatment and the mild treatment area 14 with relatively small heat history of the scorch treatment comparing to the intensive treatment area 13 with large heat history of the scorch treatment.

[0046] Relatively larger amount of the organic substances such as the cashew dust remains in the mild treatment area 14 with relatively small heat history of the scorch treatment than the intensive treatment area 13 with large heat history of the scorch treatment.

[0047] Therefore, the cashew dust film can be formed on the friction surface of the disc rotor during the braking action, thereby generating the adhesive friction to provide the excellent and stable braking effectiveness.

Method for Manufacturing Disc Brake Pad

[0048] The method for manufacturing the disc brake pad is explained with reference to FIG. 2 and FIG. 3.

(1) Mixing Step

[0049] A friction material composition containing the predetermined amount of raw friction materials such as a binder, a fiber base, a lubricant, an organic friction modifier, an inorganic friction modifier, a pH adjuster, and a filler, is positioned in a mixer such as Loedige mixer and Eirich mixer to agitate the friction material composition until the friction material composition is uniformly dispersed to obtain a raw friction material mixture.

(2) Pre-Forming Step

[0050] The obtained raw friction material mixture is positioned in a preforming die, and a pressing apparatus is used to press-form the raw friction material mixture to obtain an intermediate molded article.

[0051] In addition, prior to the pre-forming step, it is an option to add a kneading step to knead the raw friction material mixture by a pressure kneader before the pre-forming step to obtain a kneaded substance of the raw friction material and a granulating step to granulate the raw friction material mixture to obtain a granulated substance of the raw friction material.

(3) Heat Press Forming Step

[0052] The intermediate molded article obtained through the pre-forming step is superposed on a pre-washed, pre-surface treated, and adhesive-coated steel back plate to be positioned in a heat forming die and to be heat-press-formed using the pressing apparatus at the temperature of 140-200 centigrade under the pressure of 20-80 MPa for 1-10 minutes to obtain the molded article of the friction material.

[0053] Here, the pre-forming step may be omitted, and any one of the raw friction material mixture, the kneaded substance of the raw friction material, or the granulated substance of the raw friction material may be position to process the heat press forming.

(4) Grinding Step and Other Processing Steps

[0054] A grinder with a grinding stone may be used to grind the surface of the friction material to form the friction surface.

[0055] As necessary, a chamfer or a slit may be formed on the surface of the friction material.

(5) Coating Step

[0056] A coating step is performed by coating areas other than the friction surface of the friction material of the disc brake pad by a spray coating or an electrostatic powder coating. A baking is conducted in a next heat treatment step.

(6) Heat Treatment Step

[0057] The coated molded article is heated at 180-250 centigrade for 1-5 hours to complete curing of a thermosetting resin contained in the friction material as the binder and at the same time the coating formed during the coating step is baked.

(7) Scorch Treatment Step

[0058] To explain the present invention referring to FIG. 3, a vertical cavity surface emitting laser module 20 (hereinafter, surface emitting laser module 20), which is one type of semiconductor lasers, is used as a heating means for the scorch treatment of the friction material 12 formed on one side of the back plate 11, and multiple lasers with different energy densities irradiate the friction surface of the friction material 12, while the surface emitting laser module 20 and the disc brake pad 10 are relatively making a parallel movement, in order to form the friction surface having mixed areas including the area with large heat history of the scorch treatment 13 and the area with relatively small heat history of the scorch treatment 14 comparing to the area with large heat history of the scorch treatment 13.

[0059] The scorch treatment is explained in the following sections.

(7.1) Surface Emitting Laser Module (VCSEL Module)

[0060] The surface emitting laser module 20 is a module on which multiple vertical cavity surface emitting laser (VCSE) elements 21 (hereinafter surface emitting laser element 21) are arranged, and the respective surface emitting laser element 21 is capable of changing an energy density of the laser.

[0061] The respective surface emitting laser element 21 arranged to face each other on the surface of the friction material 12 is preset to arrange the energy density to provide the heat history of the scorch treatment correspond to the area of the friction surface of the friction material 12, which facilitates forming of the friction surface with the mixed areas including the area with large heat history of the scorch treatment 13 and the area with relatively small heat history of the scorch treatment 14 comparing to the area with large heat history of the scorch treatment 13.

[0062] As the surface emitting laser module 20, Vertical Cavity Surface Emitting Laser Module by Philips Photonics Company Limited, which is manufactured such as by the method disclosed in the Japanese Patent Publication No. 2015-51027, may be used. However, the surface emitting laser element 21 is not limited to the one for the vertical cavity surface emitting laser.

(7.2) Laser Density

[0063] The energy density for forming the area with large heat history of the scorch treatment 13 is 150-1100 kW/m2, and the energy density of the area with relatively small heat history of the scorch treatment 14 comparing to the area with large heat history of the scorch treatment 13 is 0-300 kW/m2.

(7.3) Irradiation Distance

[0064] A distance (hereinafter irradiation distance) G between an irradiation surface of the surface emitting laser element 21 when performing the scorch treatment of the friction material 12 and the surface of the friction material 12 is 15-300 mm and is preferably 30-200 mm but more preferably 50-100 mm.

(7.4) Processing Time

[0065] A processing time for the scorch treatment of the friction material 12 is 0.5-60 seconds and is preferably 3-10 but more preferably 4-8 seconds.

[0066] If the processing time for the scorch treatment exceeds 60 seconds, the organic substances on the friction material surface are excessively burned, which significantly reduces the strength of the friction material.

(7.5) Arrangement of the Surface Emitting Laser

[0067] Positions of the surface emitting laser modules 20 relative to the friction material 12 are not limited to the positions in FIG. 3 showing the surface emitting laser module 20 arranged laterally and parallel to the disc brake pad 10. Positions of the surface emitting laser modules 20 may be arranged vertically facing each other on the friction material 12 or may be arranged widening toward the posterior ends to surround the friction material 12.

(7.6) Surface Pattern (Surface Form) of Scorch Treatment Layer

[0068] Either one of the surface emitting laser module 20 or the disc brake pad 10 makes a parallel movement or both of the surface emitting laser module 20 and the disc brake pad 10 make a parallel movement to form the friction surface having the mixed areas including the area with large heat history of the scorch treatment 13 and the area with relatively small heat history of the scorch treatment 14 comparing to the area with large heat history of the scorch treatment 13.

[0069] The surface pattern of the area with large heat history of the scorch treatment 13 viewing from the friction surface side of the friction material 12 is not limited to the stripe pattern in a vertical direction of the friction material 12 as shown in FIG. 1. For example, the pattern may be one pattern or any combination of the patterns as shown in FIG. 4 such as a stripe pattern in a horizontal direction of the friction material 12 as shown in FIG. 4(a), an oblique stripe pattern as shown in FIG. 4(b), a lattice pattern as shown in FIG. 4(c), and a wave pattern as shown in FIG. 4(d), and the houndstooth pattern.

[0070] Furthermore, the surface form of the area with large heat history of the scorch treatment 13 is not limited to a straight shape and can be a curve shape.

[0071] In addition, the surface form of the area with large heat history of the scorch treatment 13 is not limited to a continuous strip surface but can be a broken strip surface having gaps therebetween and a polka-dot strip surface having a polka-dot pattern.

[0072] A width of the area with large heat history of the scorch treatment 13 and a spacing or an interval between the areas with large heat history of the scorch treatment 13 are determined as appropriate.

[0073] As already explained above, this invention facilitates manufacturing of the disc brake pad 10 having the friction material 12 with the mixed areas including areas of different heat histories of the scorch treatment by irradiating the friction surface of the friction material 12 using multiple lasers with different energy densities while relatively moving the surface emitting laser module 20 and the disc brake pad 10.

Determination of Amount of Heat History being Large or Small

[0074] With reference to FIG. 5, a process of determining the amount of the heat history of the friction material 12 due to the scorch treatment is explained.

[0075] In this invention, as a process of determining the amount of the heat history of the friction material 12 due to the scorch treatment, Thermogravimetric Analysis or Thermal Gravimetric Analysis (TGA) is utilized.

(1) Determination Principle of Heat History

[0076] Whether the heat history of the particular area of the friction material 12 due to the scorch treatment is large or small can be determined from the mass reduction rate as the result of thermogravimetric analysis using the surface specimen collected from the surface of the friction material 12 with the heat history of the scorch treatment and the internal specimen collected from the inside of the friction material 12 without the heat history of the scorch treatment.

(1.1) Method of Collecting Specimen of Friction Material Surface

[0077] A drilling machine is used to drill a hole with a diameter of 6 mm and a depth of 0.1 mm in two portions of each of the area with large heat history of the scorch treatment 13 and the area with relatively small heat history of the scorch treatment 14 comparing to the area with large heat history of the scorch treatment 13 in order to collect 20 mg of specimen from each hole.

(1.2) Method of Collecting Specimen of Inside of Friction Material

[0078] A grinding machine is used to grind from the surface of the friction material 12 with the heat history due to the scorch treatment to the surface of the friction material 12 without the heat history of the scorch treatment, which is 3 mm depth.

[0079] Then, the drilling machine is used to drill a hole with a diameter of 6 mm and a depth of 0.1 mm in order to collect 20 mg of the internal specimen.

(1.3) Definition of Mass Reduction Rate

[0080] Prior to the thermogravimetric analysis of the specimens (the surface specimen and internal specimen) collected from the friction material 12, the mass reduction rate of the respective specimen is defined as follows.

TABLE-US-00001 A(%) A reduction rate of the mass of the inside of the friction material without the heat history due to the scorch treatment when performing the thermogravimetric analysis of the friction material at 500 centigrade B1(%) A reduction rate of the mass of the friction surface area with the largest heat history due to the scorch treatment 13 when performing the thermogravimetric analysis at 500 centigrade. B2(%) A reduction rate of the mass of the friction surface area with the relatively small heat history due to the scorch treatment 14 relative to the friction surface area with the largest heat history due to the scorch treatment 13 when performing the thermogravimetric analysis at 500 centigrade.

[0081] The reduction rate of the mass of the friction surface when performing the thermogravimetric analysis of the respective specimen collected from the friction material 12 is as follows.

[0082] With respect to the internal portion of the friction material 12 without the heat history due to the scorch treatment, because no organic substances such as the cashew dust are not removed, the reduction rate A of the mass when conducting the thermogravimetric analysis is the largest among all.

[0083] With respect to the area with the largest heat history due to the scorch treatment 13 on the friction surface 12, because the largest amount of the organic substances such as the cashew dust is removed, the reduction rate B1 of the mass when conducing the thermogravimetric analysis is the smallest among all.

[0084] With respect to the area with relatively small heat history due to the scorch treatment 14 on the friction surface relative to the area with the largest heat history due to the scorch treatment 13 on the friction surface 12, because the amount of the organic substances such as the cashew dust removed is relatively small, the reduction rate B2 of the mass when conducing the thermogravimetric analysis is larger than the reduction rate B1.

[0085] In addition, when the scorch treatment is not performed on the area with relatively small heat history due to the scorch treatment 14, the reduction rate B2 of the mass when conducting the thermogravimetric analysis of the surface of the friction material 12 becomes approximately equal to the reduction rate A of the mass of the internal portion of the friction material 12.

[0086] In consideration of the above-discussion, the relation of the reduction rate of the mass when conducing the thermogravimetric analysis at 500 centigrade on the friction material surface is A≥B2>B1.

(1.4) Relational Expression of Mass Reduction Rate

[0087] Whether the heat history due to the scorch treatment of the friction material 12 is large or small is adjusted to satisfy the following formula in consideration of the mass reduction rate based on the thermogravimetric analysis using the surface specimen of the friction material 12 and the internal specimen of the friction 12 without the heat history due to the scorch treatment.

[0088] By satisfying the following formula, while preventing the fading phenomenon at the initial stage of the usage of the disc brake pad 10, the sufficient braking effectiveness can be obtained.

[0089] Also, in the case of not satisfying the following formula, in addition to not being able to obtain the above-advantage, problems of reducing the wear resistance and flatness of the friction surface exist.

[Equation 2]

Formula 1:

30≤B1/A×100≤90  (A)

50≤B2/A×100  (B)

B2/A×100−B1/A×100≤60  (C)

(2) Area Ratio of Area with the Largest Heat History due to Scorch Treatment

[0090] In this invention, while satisfying the above-Formula 1, the area ratio of the area with the largest heat history due to the scorch treatment 13 in the friction surface of the friction material 12 is set to be within the rage of 10-90%.

[0091] The area ratio of the area with the largest heat history due to the scorch treatment 13 is preferably within the range of 30-70% and is more preferably within the range of 40-60%. By setting the area ratio of the area with the largest heat history due to the scorch treatment 13, the fading resistance and the braking effectiveness can be improved.

(3) Thermogravimetric Analysis

[0092] The thermogravimetric analysis is conducted by Thermo plus EVO TG8120 by Rigaku Company Limited under the following conditions. A thermogravimetric reduction rate is calculated from the thermogravimetric reduction amount between the room temperature to 500 centigrade.

TABLE-US-00002 Atmosphere Air Amount of Specimen 10 mg Standard Specimen α alumina Measuring Temperature Between room temperature and 800 centigrade Temperature Elevation Rate 20 centigrade per minute

EMBODIMENTS

[0093] In the following sections, embodiments and comparative examples of this invention are concretely explained; however, this invention is not limited to the following embodiments.

1. Manufacturing Method for Disc Brake Pad in Embodiments 1-26 and Comparative Examples 1-9

[0094] The friction material composition with compositions as shown in Table 1 is mixed by Loedige mixer for 5 minutes, and the mixed friction material composition is pressed in the pre-forming die under the pressure of 30 MPa for 10 seconds to obtain the intermediate molded article. This intermediate molded article is superposed on the pre-washed, surface treated, and adhesive coated steel back plate to be positioned in the heat forming die together with the back plate to be heat-pressed at the temperature of 150 centigrade under the pressure of 40 MPa for 10 minutes and is electrostatic powder coated to be heat-treated (post-cured) and baked at the temperature of 200 centigrade for 5 hours to be grinded to form the friction surface.

TABLE-US-00003 TABLE 1 Binder Phenol Resin 12 Fiber Base Aramid Fiber 4 Lubricant Zinc Sulfide 2 Artificial Graphite 3 Petroleum Coke 3 Inorganic Friction Modifier Plate Like Potassium Hexatitanate 20 Zirconium Silicate 2 Mica 3 Zirconium Oxide 20 Organic Friction Modifier Cashew Dust 5 Tire Tread Rubber Pulverized Powder 4 pH Adjuster Calcium Hydroxide 3 Filler Barium Sulfide 19 Total (Weight %) 100

[0095] Disc brake pads are manufactured by performing the scorch treatment under the conditions in the following Table 2 and Table 3 (Embodiments 1-26, Comparative Examples 1-9)

TABLE-US-00004 TABLE 2 Embodiments 1 2 3 4 5 6 7 8 9 10 11 12 13 Area with Largest Energy Density of 160 630 960 300 600 900 1100 400 700 1000 1100 500 700 Heat History due to Surface Emitting Scorch Treatment Laser Element Conditions for (kW/m2) Scorch Treatment Distance between 50 50 50 50 50 50 50 50 50 50 50 50 50 (Area B1) Irradiation Surface of Surface Emitting Laser Element and Friction Material Surface (mm) Processing Time for 5 5 5 5 5 5 5 5 5 5 5 5 5 Scorching Treatment (seconds) Area with Relatively Energy Density of 0 0 0 70 70 70 70 110 110 110 110 150 150 Smaller Heat History Surface Emitting due to Scorch Laser Element Treatment Comparing (kW/m2) to Area with Largest Distance between 50 50 50 50 50 50 50 50 50 50 50 50 50 Heat History due to Irradiation Surface Scorch Treatment of Surface Emitting Conditions for Laser Element and Scorch Treatment Friction Material (Area B2) Surface (mm) Processing Time for 5 5 5 5 5 5 5 5 5 5 5 5 5 Scorching Treatment (seconds) A 13.2 13.1 13.3 13.2 13.1 13.0 12.9 12.9 13.3 13.0 12.8 13.2 13.0 B1 11.7 7.9 5.2 10.8 8.1 5.8 4.4 9.8 7.1 5.3 4.0 9.0 7.2 B2 13.1 12.9 13.0 12.1 12.3 12.1 12.0 10.9 11.3 11.1 11.0 9.8 10.1 B1/A × 100 88.6 60.3 39.1 81.8 61.8 44.6 34.1 76.0 53.4 40.8 31.3 68.2 55.4 B2/A × 100 99.2 98.5 97.7 91.7 93.9 93.1 93.0 84.5 85.0 85.4 85.9 74.2 77.7 B2/A × 100 − B1 /A × 100 10.6 38.2 58.6 9.8 32.1 48.5 58.9 8.5 31.6 44.6 54.7 6.1 22.3 B1 Area Ratio (%) 50 50 50 50 50 50 50 50 50 50 50 50 50 Embodiments 14 15 16 17 18 19 20 21 22 23 24 25 26 Area with Largest Energy Density of 1100 600 1100 800 1100 900 1100 700 700 700 700 700 700 Heat History due to Surface Emitting Scorch Treatment Laser Element Conditions for (kW/m2) Scorch Treatment Distance between 50 50 50 50 50 50 50 50 50 50 50 50 50 (Area B1) Irradiation Surface of Surface Emitting Laser Element and Friction Material Surface (mm) Processing Time for 5 5 5 5 5 5 5 5 5 5 5 5 5 Scorching Treatment (seconds) Area with Relatively Energy Density of 150 190 190 220 220 270 270 110 110 110 110 110 110 Smaller Heat History Surface Emitting due to Scorch Laser Element Treatment Comparing (kW/m2) to Area with Largest Distance between 50 50 50 50 50 50 50 50 50 50 50 50 50 Heat History due to Irradiation Surface Scorch Treatment of Surface Emitting Conditions for Laser Element and Scorch Treatment Friction Material (Area B2) Surface (mm) Processing Time for 5 5 5 5 5 5 5 5 5 5 5 5 5 Scorching Treatment (seconds) A 13.3 13.3 13.1 13.2 12.9 13.1 13.2 13.1 13.2 13.0 12.9 13.0 13.3 B1 4.1 7.8 4.3 6.8 4.0 5.8 4.2 7.0 7.1 6.9 7.2 7.1 7.1 B2 9.8 9.1 9.0 8.1 8.0 6.8 7.0 11.0 11.2 10.9 11.1 11.3 11.1 B1/A × 100 30.8 58.6 32.8 51.5 31.0 44.3 31.8 53.4 53.8 53.1 55.8 54.6 53.4 B2/A × 100 73.7 68.4 68.7 61.4 62.0 51.9 53.0 84.0 84.8 83.8 86.0 86.9 83.5 B2/A × 100 − B1 /A × 100 42.9 9.8 35.9 9.8 31.0 7.6 21.2 30.5 31.1 30.8 30.2 32.3 30.1 B1 Area Ratio (%) 50 50 50 50 50 50 50 5 10 30 60 90 95

TABLE-US-00005 Comparative Examples 1 2 3 4 5 6 7 8 9 Area with Largest Energy Density of 120 1000 1150 1150 1150 1150 1150 1150 1000 Heat History due to Surface Emitting Scorch Treatment Laser Element Conditions for (kW/m2) Scorch Treatment Distance between 50 50 50 50 50 50 50 50 50 (Area B1) Irradiation Surface of Surface Emitting Laser Element and Friction Material Surface (mm) Processing Time for 5 5 5 5 5 5 5 5 5 Scorching Treatment (seconds) Area with Relatively Energy Density of 0 0 70 110 150 190 220 270 290 Smaller Heat History Surface Emitting due to Scorch Laser Element Treatment Comparing (kW/m2) to Area with Largest Distance between 50 50 50 50 50 50 50 50 50 Heat History due to Irradiation Surface Scorch Treatment of Surface Emitting Conditions for Laser Element and Scorch Treatment Friction Material (Area B2) Surface (mm) Processing Time for 5 5 5 5 5 5 5 5 5 Scorching Treatment (seconds) A 13.2 12.9 13.0 13.1 13.1 13.1 13.0 13.0 13.3 B1 12.1 4.9 3.8 3.7 3.6 3.8 3.7 3.8 4.9 B2 13.1 12.8 11.8 10.8 10.0 9.2 8.3 6.9 6.5 B1/A × 100 91.7 38.0 29.2 28.2 27.5 29.0 28.5 29.2 36.8 B2/A × 100 99.2 99.2 90.8 82.4 76.3 70.2 63.8 53.1 48.9 B2/A × 100 − B1/A × 100 7.6 61.2 61.5 54.2 48.9 41.2 35.4 23.8 12.0 B1 Area Ratio (%) 50 50 50 50 50 50 50 50 50

2. Evaluation Standard

[0096] The fading resistance, the braking effectiveness, the wear resistance, and the flatness level are evaluation for the obtained disc brake pads.

<1> Fading Resistance

[0097] In conformity to JASO C406, “Passenger Car Brake Dynamo Meter Method”, the minimum friction coefficient μ in the first fading test is measured. The evaluation standard is as follows:

TABLE-US-00006 Minimum friction Evaluation coefficient μ Excellent 0.30 or more Good 0.25 or more but less than 0.30 Pass 0.20 or more but less than 0.25 Fail Less than 0.20

<2> Braking Effectiveness

[0098] In conformity to JASO C406, “Passenger Car Brake Dynamo Meter Method”, the average friction coefficient μ in the second effect test is measured. The evaluation standard is as follows:

TABLE-US-00007 Average friction Evaluation coefficient μ Excellent 0.45 or more Good 0.42 or more but less than 0.45 Pass 0.38 or more but less than 0.42 Fail Less than 0.38

<3> Wear Resistance

[0099] In conformity to JASO C427, “Automobile Parts-Brake Lining and Disc Brake Pad-Wear Test Procedure on Inertia Dynamometer”, the amount of wear of the friction material (shown by millimeter or mm) is measured at the initial speed of braking of 50 km/h and the deceleration speed of braking of 0.3 G with the suitable number of brake actions under the brake temperature before braking of 200 centigrade, and after converting the obtained measurement into the amount of wear at 100 braking time, the value is evaluated under the following evaluation standards.

[0100] Evaluation standard is as follows.

TABLE-US-00008 Amount of wear of the Evaluation friction material (mm) Excellent Less than 0.15 mm Good 0.15 mm or more but less than 0.20 mm Pass 0.20 mm or more but less than 0.50 mm Fail 0.50 mm or more

<4> Flatness Level of Friction Surface

[0101] Three support blocks are mounted on a surface plate to make uniform in height. These support blocks support three ends of the back plate. A dial gauge is used to measure heights of five areas of the friction material with the largest heat history due to the scorch treatment and five areas of the friction material with relatively small heat history due to the scorch treatment comparing to the areas with the largest heat history due to the scorch treatment to determine the difference between the highest height and lowest height. Evaluation standard is as follows.

TABLE-US-00009 Flatness level of the Evaluation friction material (μm) Excellent Less than 70 μm Good 70 μm or more but less than 100 μm Pass 100 μm or more but less than 150 μm Fail 150 μm or more

3. Evaluation Results

[0102] Results of the evaluation are shown in Table 4 and Table 5.

TABLE-US-00010 TABLE 4 Embodiments 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 Evaluation Fading P G G P G G G G E E G G E G E G E G E G P G E E E E Results Resistance Braking E E E E E G G E E G G E E G E G G G G P E E E E G P Effectiveness Wear E E G E E G P E E G P E G P G P P P P P E E E E G G Resistance Flatness E G P E E G P E E G P E E G E E E E E E E E E E E E Level E = Excellent G = Good P = Pass F = Fail

TABLE-US-00011 TABLE 5 Comparative Examples 1 2 3 4 5 6 7 8 9 Evaluation Fading F G G P P P P P P Results Resistance Braking E E G G G G P P F Effectiveness Wear E G P F F F F F P Resistance Flatness E F F P P G E E E Level

[0103] From the respective tables, the respective friction material 12 that satisfies the conditions of this invention shows more sufficient and satisfactory evaluation result with respect to the fading resistance, the braking effectiveness, the wear resistance, and flatness level.

INDUSTRIAL APPLICABILITY

[0104] According to this invention, in the disc brake pad having the friction material with the friction surface with the heat history due to the scorch treatment, the disc brake pad offers an excellent practical value by providing, while preventing the fading phenomenon at the initial stage of the disc brake pad usage, the sufficient wear resistance and the braking effectiveness.

[0105] 10. Disc brake pad

[0106] 11. Back plate

[0107] 12. Friction material

[0108] 13. Area with the largest heat history due to scorch treatment

[0109] 14. Area with relatively small heat history due to scorch treatment comparing to the area with the largest heat history due to scorch treatment

[0110] 20. Surface emitting laser module

[0111] 21. Surface emitting laser element