Biodegradable magnesium alloy nerve conduit for nerve defect repair and its preparation method

Abstract

A biodegradable magnesium alloy nerve conduit for nerve defect repair has multiple lines of through holes in the tube wall thereof, the through holes in each line are axially arranged along a circular tube at equal distances, and the through holes in adjacent lines are arranged in a staggered way. A method for preparing the nerve conduit includes steps of: (step 1) processing a 45-degree conical surface at one end of a magnesium alloy tube blank, carrying out extrusion, and obtaining a magnesium alloy intermediate tube material; (step 2) obtaining a capillary tube after carrying out multi-pass rolling and drawing on the magnesium alloy intermediate tube material; (step 3) carrying out stress relief annealing on the capillary tube, laser cutting and punching, and obtaining a porous conduit; and (step 4) carrying out acid pickling on the porous conduit, and then carrying out electrochemical polishing treatment, and obtaining the nerve conduit.

Claims

1. A biodegradable magnesium alloy nerve conduit for nerve defect repair, wherein the biodegradable magnesium alloy nerve conduit is in a circular tube shape, the biodegradable magnesium alloy nerve conduit has multiple lines of through holes in a tube wall thereof, the through holes in each line are axially arranged along a circular tube at equal distances, and the through holes in adjacent lines are arranged in a staggered way.

2. The biodegradable magnesium alloy nerve conduit for nerve defect repair according to claim 1, wherein a length of the nerve conduit is 5-50 mm, a thickness of the nerve conduit is 0.1-0.2 mm.

3. The biodegradable magnesium alloy nerve conduit for nerve defect repair according to claim 1, wherein an aperture of the through holes is 0.03-0.3 mm, and a porosity of the nerve conduit is 2-20%.

4. A method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to claim 1, wherein the method comprises steps of: (step 1) processing a 45-degree conical surface at one end of a magnesium alloy tube blank, carrying out extrusion, and obtaining a magnesium alloy intermediate tube material; (step 2) obtaining a capillary tube after carrying out multi-pass rolling and drawing on the magnesium alloy intermediate tube material; (step 3) carrying out stress relief annealing on the capillary tube laser cutting and punching, and obtaining a porous conduit; and (step 4) carrying out acid pickling on the porous conduit in an ultrasound cleaning machine, and then carrying out electrochemical polishing treatment, and obtaining the biodegradable magnesium alloy nerve conduit for nerve defect repair.

5. The method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to claim 4, wherein in the (step 1), an outer diameter of the magnesium alloy tube blank is 20 mm, an extrusion temperature is 300-400 C., and an outer diameter of the magnesium alloy intermediate tube material is 6-8 mm, and a wall thickness is 0.5-1 mm.

6. The method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to claim 4, wherein in the (step 2), an outer diameter of the capillary tube 1-3 mm, and a wall thickness thereof is 0.1-0.2 mm.

7. The method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to claim 4, wherein in the (step 3), a stress relief annealing temperature is 300-350 C., and an annealing time is 20-30 min.

8. The method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to claim 4, wherein in the (step 4), the acid pickling is specifically as carrying out ultrasonic pickling in a pickling solution for 5-30 min.

9. The method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to claim 8, wherein the pickling solution comprises 80-100 ml/L of phosphoric acid and 40-60 g/L of ammonium bifluoride; a solvent is deionized water.

10. The method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to claim 4, wherein in the (step 4), a polishing solution used for the electrochemical polishing treatment comprises phosphoric acid and absolute ethanol with a volume ratio of 1:1 or comprises ethylene glycol monoethyl ether and hydrochloric acid with a volume ratio of 9:1; a polishing treatment voltage is 2-8 V, a polishing treatment time is 20-240 s, and a polishing treatment temperature is room temperature.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0029] Other features, objects, and advantages of the present invention will become more apparent from reading the description of non-limiting embodiments detailed with reference to the following drawings:

[0030] FIG. 1 is a 3D rendering of a biodegradable magnesium alloy nerve conduit for nerve defect repair in the present invention.

[0031] FIG. 2 is a schematic view of operation that the biodegradable magnesium alloy nerve conduit for nerve defect repair in the present invention is implanted into the 6 mm defect area of sciatic nerve of adult SD rat.

[0032] FIG. 3 is a schematic view of the sciatic nerve defect area of adult SD rat after the biodegradable magnesium alloy nerve conduit for nerve defect repair in the present invention is implanted for 2 months.

[0033] FIG. 4 is photos of toes of the rat, wherein a is the experimental side and b is the unaffected side.

[0034] FIG. 5 is histological HE staining graphs of cross section and longitudinal section of regenerated nerve, wherein the left one is the HE staining graph of cross section of regenerated nerve; the right one is the HE staining graph of longitudinal section of regenerated nerve.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0035] The present invention is described in detail as follows with reference to specific embodiments. The following embodiments will help provide further understanding of the present invention for those skilled in the art, and not in any way limit the present invention. It shall be noted that several variants and improvements can be made without departing from concept of the present invention for ordinary persons skilled in the art. All these fall within the protection scope of the disclosure.

First Embodiment

[0036] A biodegradable magnesium alloy nerve conduit for nerve defect repair according to a first embodiment is illustrated, as shown in FIG. 1, which is a circular tube with a length of 6 mm, an outer diameter of 2 mm and a wall thickness of 0.2 mm; wherein the biodegradable magnesium alloy nerve conduit has 4 lines of through holes in a tube wall thereof, the through holes in each line are axially arranged along the circular tube at equal distances, and the through holes in adjacent lines are arranged in a staggered way; an amount of the through holes in each line is 6, and an aperture thereof is 0.3 mm.

[0037] A method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to the first embodiment is also illustrated, wherein the method comprises steps of:

[0038] (step 1) processing a 45-degree conical surface at one end of a MgNdZnZr magnesium alloy tube blank with an outer diameter of 20 mm, carrying out extrusion at a temperature of 400 C., and obtaining a magnesium alloy intermediate tube material with a size of 80.5 mm (outer diameterwall thickness);

[0039] (step 2) obtaining a capillary tube with an outer diameter of 2 mm and a wall thickness of 0.2 mm after carrying out multi-pass rolling and drawing on the magnesium alloy intermediate tube material;

[0040] (step 3) carrying out stress relief annealing on the capillary tube at a temperature of 300 C. for 30 min, laser cutting and punching, and obtaining a porous conduit; and

[0041] (step 4) carrying out acid pickling on the porous conduit in an ultrasound cleaning machine for 5-30 min with a pickling solution which comprises 80-100 ml/L of phosphoric acid and 40-60 g/L of ammonium bifluoride, wherein a solvent is deionized water; and then carrying out electrochemical polishing treatment at room temperature with a polishing solution which comprises phosphoric acid and absolute ethanol with a volume ratio of 1:1, wherein a polishing treatment voltage is 2-8 V, a polishing treatment time is 20-240 s, and obtaining the biodegradable magnesium alloy nerve conduit for nerve defect repair.

Second Embodiment

[0042] A biodegradable magnesium alloy nerve conduit for nerve defect repair according to a second embodiment is illustrated, as shown in FIG. 1, which is in a circular tube with a length of 50 mm, a wall thickness of 0.15 mm and an outer diameter of 3 mm; wherein the biodegradable magnesium alloy nerve conduit has 8 lines of through holes in a tube wall thereof, the through holes in each line are axially arranged along the circular tube at equal distances, and the through holes in adjacent lines are arranged in a staggered way; an amount of the through holes in each line is 50, and an aperture thereof is 0.03 mm.

[0043] A method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to the second embodiment is also illustrated, wherein the method comprises steps of:

[0044] (step 1) processing a 45-degree conical surface at one end of a MgNdZnZr magnesium alloy tube blank with an outer diameter of 20 mm, carrying out extrusion at a temperature of 300 C., and obtaining a magnesium alloy intermediate tube material with a size of 70.8 mm (outer diameterwall thickness);

[0045] (step 2) obtaining a capillary tube with an outer diameter of 3 mm and a wall thickness of 0.15 mm after carrying out multi-pass rolling and drawing on the magnesium alloy intermediate tube material;

[0046] (step 3) carrying out stress relief annealing on the capillary tube at a temperature of 350 C. for 20 min, laser cutting and punching, and obtaining a porous conduit; and

[0047] (step 4) carrying out acid pickling on the porous conduit in an ultrasound cleaning machine for 5-30 min with a pickling solution which comprises 80-100 ml/L of phosphoric acid and 40-60 g/L of ammonium bifluoride, wherein a solvent is deionized water; and then carrying out electrochemical polishing treatment at room temperature with a polishing solution which comprises ethylene glycol monoethyl ether and hydrochloric acid with a volume ratio of 9:1, wherein a polishing treatment voltage is 2-8 V, a polishing treatment time is 20-240 s; and obtaining the biodegradable magnesium alloy nerve conduit for nerve defect repair.

Third Embodiment

[0048] A biodegradable magnesium alloy nerve conduit for nerve defect repair according to a third embodiment is illustrated, as shown in FIG. 1, which is a circular tube with a length of 5 mm, a wall thickness of 0.10 mm and an outer diameter of 1 mm; wherein the biodegradable magnesium alloy nerve conduit has 4 lines of through holes in a tube wall thereof, the through holes in each line are axially arranged along the circular tube at equal distances, and the through holes in adjacent lines are arranged in a staggered way, an amount of the through holes in each line is 5, and an aperture thereof is 0.2 mm.

[0049] A method for preparing the biodegradable magnesium alloy nerve conduit for nerve defect repair according to the third embodiment is also illustrated, wherein the method comprises steps of:

[0050] (step 1) processing a 45-degree conical surface at one end of a MgNdZnZr magnesium alloy tube blank with an outer diameter of 20 mm, carrying out extrusion at a temperature of 320 C., and obtaining a magnesium alloy intermediate tube material with a size of 61 mm (outer diameterwall thickness);

[0051] (step 2) obtaining a capillary tube with an outer diameter of 1 mm and a wall thickness of 0.10 mm after carrying out multi-pass rolling and drawing on the magnesium alloy intermediate tube material;

[0052] (step 3) carrying out stress relief annealing on the capillary tube at a temperature of 300 C. for 25 min, laser cutting and punching, and obtaining a porous conduit; and (step 4) carrying out acid pickling on the porous conduit in an ultrasound cleaning machine for 5-30 min with a pickling solution which comprises 80-100 ml/L of phosphoric acid and 40-60 g/L of ammonium bifluoride, wherein a solvent is deionized water; and then carrying out electrochemical polishing treatment at room temperature with a polishing solution which comprises phosphoric acid and absolute ethanol with a volume ratio of 1:1, wherein a polishing treatment voltage is 2-8 V, a polishing treatment time is 20-240 s; and obtaining the biodegradable magnesium alloy nerve conduit for nerve defect repair.

IMPLEMENTATION EFFECT

[0053] The porous biodegradable magnesium alloy nerve conduits prepared in the first, second and third embodiments are respectively implanted into the defect area of sciatic nerve of adult SD rat; the operation is shown in FIG. 2 immediately. After the nerve conduit is implanted in the rat for two months, the good nerve regeneration at the anastomotic stoma is generally observed; there is no scar tissue or inflammatory response around, and no bubble formation. Although the conduit is not completely degraded, it is softened, which confirms that the regenerated axons pass through the conduit, to achieve the purpose of nerve repair, as shown in FIG. 3. FIG. 4 is photos of toes of the rat (the left is the experimental side; the right is the unaffected side). The ulcer has healed, and there is no difference between the experimental side and the unaffected side. It indirectly confirms that the nerve axons have been well regenerated, and the nerve defects have been repaired. The histological HE staining graphs (FIG. 5) of cross section and longitudinal section of regenerated nerve confirms that there is regenerated nerve tissue in the lumen of conduit; the nerve tissue grows from proximal end to distal end through the anastomotic stoma to repair defects.

[0054] Specific embodiments of the present invention are described above. It shall be understood that the present invention is not limited to the above-mentioned specific embodiments, and those skilled in the art can make different variants and modifications within the scope of the claims, and it shall not affect the substance of the present invention.