SCINTILLATOR AND ELECTRON DETECTOR

Abstract

A scintillator includes a support substrate, an emission layer formed on the substrate, made of ZnO with impurities added to have an electron concentration of 2?10.sup.19 cm.sup.?3 or more and 2?10.sup.20 cm.sup.?3 or less, and for generating scintillation light in response to incidence of radiation, a protective layer formed on the emission layer and made of a material having a band gap wider than that of ZnO, and a metal layer formed on the protective layer. The support substrate is made of a material transmitting the scintillation light generated in the emission layer. Further, the metal layer functions as a reflection layer for reflecting the scintillation light from the emission layer.

Claims

1: A scintillator comprising: a support substrate; an emission layer formed on the support substrate, made of ZnO with impurities added to have an electron concentration of 2?10.sup.19 cm.sup.?3 or more and 2?10.sup.20 cm.sup.?3 or less, and configured to generate scintillation light in response to incidence of radiation; a protective layer formed on the emission layer and made of a material having a band gap wider than that of ZnO; and a metal layer formed on the protective layer, wherein the support substrate is made of a material transmitting the scintillation light generated in the emission layer, and the metal layer functions as a reflection layer configured to reflect the scintillation light from the emission layer.

2: The scintillator according to claim 1, wherein the emission layer has a layer thickness of 0.5 ?m or more and 3.0 ?m or less.

3: The scintillator according to claim 1, wherein the impurities to be added to ZnO in the emission layer include at least one element selected from the group consisting of Ga, Al, and In.

4: The scintillator according to claim 1, wherein a buffer layer made of ZnO is formed between the support substrate and the emission layer.

5: The scintillator according to claim 4, wherein the buffer layer has a layer thickness of 20 nm or more and 400 nm or less.

6: The scintillator according to claim 1, wherein the material constituting the protective layer includes at least one material selected from the group consisting of SiO.sub.2, Al.sub.2O.sub.3, MgO, CaF.sub.2, BeO, MgF.sub.2, and LiF.

7: The scintillator according to claim 1, wherein the protective layer has a layer thickness of 10 nm or more and 200 nm or less.

8: The scintillator according to claim 1, wherein the support substrate is a sapphire substrate, a quartz substrate, or a glass substrate.

9: The scintillator according to claim 1, wherein the support substrate is an a-plane sapphire substrate.

10: The scintillator according to claim 1, wherein a material constituting the metal layer is Al.

11: An electron detector comprising: the scintillator according to claim 1 configured to output the scintillation light generated in the emission layer in response to incidence of an electron; and a photodetector configured to detect the scintillation light output from the scintillator.

12: The electron detector according to claim 11, wherein the metal layer in the scintillator functions as an acceleration electrode configured to accelerate the electron incident on the scintillator.

Description

BRIEF DESCRIPTION OF DRAWINGS

[0025] FIG. 1 is a side sectional view schematically showing a configuration of an embodiment of a scintillator.

[0026] FIG. 2 includes graphs showing fluorescence lifetimes of (a) a ZnO scintillator, and (b) a plastic scintillator.

[0027] FIG. 3 is a band diagram showing a layer structure in the scintillator.

[0028] FIG. 4 is a table showing band gaps of materials constituting a protective layer.

[0029] FIG. 5 is a side view showing a configuration of an embodiment of an electron detector.

[0030] FIG. 6 is a diagram schematically showing a configuration of a scanning electron microscope.

[0031] FIG. 7 is a diagram schematically showing a configuration of a time of flight mass spectrometer.

[0032] FIG. 8 is a graph showing a wavelength dependency of emission intensity in the scintillator.

[0033] FIG. 9 is a graph showing an electron concentration dependency of emission efficiency.

[0034] FIG. 10 is a graph showing an electron acceleration voltage dependency of emission efficiency.

DESCRIPTION OF EMBODIMENTS

[0035] Hereinafter, embodiments of a scintillator and an electron detector according to the present invention will be described in detail with reference to the drawings. In the description of the drawings, the same elements will be denoted by the same reference signs, without redundant description. Further, the dimensional ratios in the drawings are not always equal to those in the description.

[0036] FIG. 1 is a side sectional view schematically showing a configuration of an embodiment of a scintillator. A scintillator 1A according to the present embodiment is used for detecting radiation such as electrons, and includes a support substrate 10, a buffer layer 12, an emission layer 14, a protective layer 16, and a metal layer 18. Here, examples of radiation to be detected by the scintillator 1A of the present embodiment generally include particles such as electrons, protons, neutrons, ? particles, and ions, and electromagnetic waves such as a ? ray, an X ray, and light, and further, as will be described below, the scintillator 1A can be used preferably for detection of for example, electrons with energy of 5 keV to 20 keV.

[0037] The support substrate 10 is a substrate made of a material which transmits scintillation light (fluorescence) generated in the emission layer 14 with sufficient transmittance. For example, an a-plane sapphire substrate can be used preferably as the support substrate 10. The emission layer 14 is formed on the support substrate 10, and generates scintillation light in response to incidence of radiation such as electrons. Further, the emission layer 14 in the present embodiment is made of a ZnO (zinc oxide) to which impurities have been added so as to have an electron concentration of 2?10.sup.19 cm.sup.?3 or more and 2?10.sup.20 cm.sup.?3 or less. Examples of impurities to be added to the emission layer 14 include Ga doped at a concentration of 2?10.sup.19 cm.sup.?3 to 4?10.sup.20 cm.sup.?3.

[0038] In the configuration example shown in FIG. 1, the buffer layer 12 made of ZnO is further formed between the support substrate 10 and the emission layer 14, and the emission layer 14 is formed on the buffer layer 12. The buffer layer 12 is made of, for example, ZnO to which no impurities have been added.

[0039] The protective layer 16 for protecting ZnO of the emission layer 14, having hygroscopic property, is formed on the impurity-added ZnO emission layer 14. Further, the protective layer 16 is made of a material having a band gap wider than that of ZnO. Based on the use of such a material, the protective layer 16 has a function to enhance characteristics and efficiency of detection of radiation performed by the scintillator 1A including the ZnO emission layer 14. Specifically, for example, SiO.sub.2 can be used preferably as a material constituting the protective layer 16.

[0040] Further, the metal layer 18, which functions as a reflection layer for reflecting scintillation light from the emission layer 14, is formed on the protective layer 16. For example, Al can be used preferably as a material constituting the metal layer 18.

[0041] The effects of the scintillator 1A according to the present embodiment will be described below.

[0042] In the scintillator 1A shown in FIG. 1, the emission layer 14 made of ZnO, to which impurities (for example, Ga) have been added at a predetermined concentration, is formed on the support substrate 10. The ZnO scintillator with impurities added, as described above, attains a very short fluorescence lifetime of scintillation light of, for example, 1 ns or less, and thus, the scintillator has fast response.

[0043] Here, FIG. 2 includes graphs showing fluorescence lifetimes of (a) a ZnO scintillator, and (b) a plastic scintillator. A graph of (a) in FIG. 2 shows a temporal waveform of scintillation light generated in the ZnO scintillator, and a graph of (b) in FIG. 2 shows a temporal waveform of scintillation light generated in the plastic scintillator, as a comparative example. As shown in these graphs, 90%-10% decay characteristic corresponding to fluorescence lifetime is 2.17 ns in the plastic scintillator, while 90%-10% decay characteristic is 0.517 ns in the ZnO scintillator, and thus, it is clear that the ZnO scintillator has fast response.

[0044] It is possible to set a scanning rate in a scanning electron microscope to be used for, for example, semiconductor inspection to 300 MHz or more, by reducing the fluorescence lifetime of scintillation light generated in the emission layer 14 to 1 ns or less as described above. Further, resolution of mass spectrometry can be enhanced in a time of flight mass spectrometer, compared to the conventional plastic scintillator.

[0045] Further, in the above scintillator 1A, the electron concentration in the impurity-added ZnO emission layer 14 is set within the range of 2?10.sup.19 cm.sup.?3 or more and 2?10.sup.20 cm.sup.?3 or less, based on, for example, the setting of concentration of impurities to be added. The electron concentration is set in the ZnO emission layer 14, and the electron concentration is increased by addition of impurities to ZnO as described above, and as a result, being a counterpart of excited carriers in recombination in the case of weak excitation intensity reduces the fluorescence lifetime of scintillation light, and further, enhances emission efficiency.

[0046] Further, since defects in the ZnO crystal are compensated by addition of impurities in the emission layer 14 of the above configuration, defect luminescence of a long fluorescence lifetime is reduced. Further, a sufficiently increased electron concentration causes the lower part of a conduction band to be filled with electrons, and also causes an effective band gap to be wide, and as a result, the occurrence of self-absorption can be reduced.

[0047] Further, in the above configuration, the protective layer 16 to protect ZnO, which is hygroscopic, is formed on the ZnO emission layer 14, and the protective layer 16 is made of a material (for example, SiO.sub.2) having a band gap wider than that of ZnO. It is possible to further enhance emission efficiency in the emission layer 14 by providing the emission layer 14 with the protective layer 16 as described above. Here, the band gap of ZnO is 3.4 eV, and it is necessary to use a material having a band gap wider than 3.4 eV for forming the protective layer 16.

[0048] Further, in the above configuration, the metal layer 18 is further formed on the protective layer 16. The metal layer 18 functions as a reflection layer which reflects scintillation light from the ZnO emission layer 14, and this enhances output efficiency of scintillation light from the back surface of the support substrate 10, which is an output surface of light. Based on the above, it is possible to realize the scintillator 1A with fast response which can be used preferably for detection of radiation such as electrons.

[0049] FIG. 3 is a band diagram showing the layer structure in the scintillator 1A shown in FIG. 1. Here, for simplicity, the band diagram of FIG. 3 shows only the magnitude of energy without consideration of bending of a band and the like due to a surface level or charge transfer. Further, for example, the spread of electron distribution due to thermal energy is ignored in the above band diagram. By providing the ZnO emission layer 14 with the protective layer 16 made of a material having a band gap wider than that of ZnO, as shown in FIG. 3, it is possible to prevent electrons and holes generated in the emission layer 14 from flowing out to the metal layer 18 of the outside, and thus, emission efficiency for incidence of radiation such as electrons can be enhanced.

[0050] Further, the electron concentration in the emission layer 14 has been sufficiently increased by addition of impurities as described above, and this increases the probability of recombination of holes and electrons generated by incidence of radiation, and enhances emission efficiency. Further, high-concentration impurities have been added to the emission layer 14, which is of an n-type, and this causes electrons to accumulate in the conduction band, as shown in FIG. 3. In this case, the energy level of the lower part of the conduction band is filled with electrons, and absorption and excitation due to, for example, incidence of radiation occur only under higher energy than this. Meanwhile, since emission of scintillation light occurs between electrons in the lower part of the conduction band and holes accumulated in the upper part of a valence band, energy thereof is lower than energy of absorption. Therefore, the emission layer 14 with an electron concentration set as described above can reduce the occurrence of self-absorption.

[0051] In the scintillator 1A of the above configuration, it is preferable that the emission layer 14 has a layer thickness of 0.5 ?m or more and 3.0 ?m or less. The scintillator 1A having the impurity-added ZnO emission layer 14 with the above layer thickness can be used preferably for detecting electrons having energy of about 5 keV to 20 keV in, for example, a scanning electron microscope and a time of flight mass spectrometer.

[0052] Here, when electrons are assumed to be radiation as a detection object, the penetration depth of electrons into ZnO is about 1 ?m under acceleration voltage of 10 kV. In the case of, for example, a scanning electron microscope and a time of flight mass spectrometer, the acceleration voltage for electrons ranges from about 5 kV to 20 kV, and in this case, it is preferable to set the layer thickness of the emission layer 14 within a range from 0.5 ?m to 3.0 ?m, as described above. When the layer thickness of the emission layer 14 is larger than the above value, emission efficiency decreases due to self-absorption.

[0053] Further, it is preferable that impurities to be added to ZnO in the emission layer 14 include at least one impurity selected from the group consisting of Ga, Al, and In, and in particular, it is preferable that Ga is added to ZnO as impurities. Ga, Al, and In are all favorable donor impurities that supply conduction electrons to ZnO.

[0054] Further, in the scintillator 1A of the above configuration, the buffer layer 12 made of ZnO is formed between the support substrate 10 and the ZnO emission layer 14. It is possible to form the emission layer 14 preferably on the substrate 10, by forming the impurity-added ZnO emission layer 14 on the ZnO buffer layer 12 as described above.

[0055] The above buffer layer 12 and the emission layer 14 on the support substrate 10 can be formed preferably by, for example, the MOCVD method with good controllability of thin film formation. Further, in the case of providing the ZnO buffer layer 12 between the support substrate 10 and the emission layer 14 as describe above, it is preferable that the buffer layer 12 has a layer thickness of 20 nm or more and 400 nm or less. That is, it is preferable that the buffer layer 12 has a layer thickness of 20 nm or more so as to form a base of ZnO crystal. Meanwhile, in consideration of self-absorbability and high possibility of defect luminescence, it is preferable that the layer thickness of the buffer layer 12 is 400 nm or less. Here, if the ZnO buffer layer 12 is unnecessary, it is possible to adopt a configuration with no buffer layer provided.

[0056] With regard to the protective layer 16, which is formed on the emission layer 14 and made of a material having a band gap wider than that of ZnO, it is preferable that a material constituting the protective layer 16 includes at least one material selected from the group consisting of SiO.sub.2, Al.sub.2O.sub.3, MgO, CaF.sub.2, BeO, MgF.sub.2, and LiF, and in particular, it is preferable that the protective layer 16 is made of SiO.sub.2, which is a material chemically stable.

[0057] FIG. 4 is a table showing band gaps of materials constituting the protective layer 16. As shown in FIG. 4, it is clear that all the materials described above for the protective layer 16 have band gaps wider than that of ZnO. For example, while the band gap of ZnO is 3.4 eV, the band gap of SiO.sub.2 is 7.9 eV. Further, it is preferable that the protective layer 16 has a layer thickness of 10 nm or more and 200 nm or less.

[0058] For example, a sapphire substrate, a quartz substrate, or a glass substrate can be used as the support substrate 10 made of a material that transmits scintillation light. Specific examples of the material of the support substrate 10 include a-plane sapphire, c-plane sapphire, quartz glass, UV transmitting glass (350 nm or more), and borosilicate glass. Further, it is in particular preferable to use an a-plane sapphire substrate as the support substrate 10 so that the ZnO emission layer 14 grows preferably on the support substrate 10.

[0059] It is preferable that Al is used as a material constituting the metal layer 18 formed on the protective layer 16. Further, metals other than Al can also be used as a material of the metal layer 18. Further, in the case of for example, Al being used as a material of the metal layer 18, it is preferable that the metal layer has a layer thickness of 10 nm or more and 50 nm or less so as to ensure a function as a reflection layer.

[0060] The configurations of an electron detector, a scanning electron microscope, and a time of flight mass spectrometer using the scintillator 1A of the above configuration will be described below.

[0061] FIG. 5 is a side view showing a configuration of an embodiment of an electron detector. An electron detector 2A according to the present embodiment includes the scintillator 1A, a photodetector 20, and a light guide 22. The scintillator 1A, which has the same configuration as that shown in FIG. 1, includes a support substrate 10, a buffer layer 12, an emission layer 14, a protective layer 16, and a metal layer 18. Here, FIG. 5 shows the cross-sectional structure of the scintillator 1A.

[0062] The photodetector 20 is optically coupled, via the light guide 22, to the back surface side of the support substrate 10 of the scintillator 1A, which is an output surface of light. Thus, scintillation light generated in the emission layer 14 of the scintillator 1A in response to incidence of electrons and output to the buffer layer 12 side passes through the support substrate 10 and the light guide 22, and reaches the photodetector 20 to be detected. Further, the scintillation light generated in the emission layer 14 and output to the protective layer 16 side passes through, in a similar manner, the support substrate 10 and the light guide 22 after being reflected by the metal layer 18 functioning as a reflection layer, and reaches the photodetector 20 to be detected.

[0063] The electron detector 2A of the above configuration enables electrons to be detected preferably by using the scintillator 1A with fast response. For example, a photomultiplier tube can be used as the photodetector 20 for detecting scintillation light output from the scintillator 1A. Further, a photodetection element other than a photomultiplier tube may be used as the photodetector 20. Further, if the light guide 22, which is used for guiding scintillation light between the scintillator 1A and the photodetector 20, is unnecessary, it is possible to adopt a configuration with no light guide provided.

[0064] Further, in the case of the electron detector 2A using the scintillator 1A, the following configuration may be adopted, the metal layer 18 in the scintillator 1A functions not only as a reflection layer for reflecting scintillation light, but also as an acceleration electrode for accelerating electrons which are incident from the outside on the scintillator 1A to be detected.

[0065] FIG. 6 is a diagram schematically showing a configuration of a scanning electron microscope. In the configuration example shown in FIG. 6, an electron detector including a scintillator 30, a light guide 34, and a photodetector 32 is provided for an observation object 36. In the above device, the observation object 36 is irradiated with an electron beam, secondary electrons emitted from the object 36 are accelerated with predetermined voltage, and caused to be incident on the scintillator 30, scintillation light generated in the scintillator 30 is detected in the photodetector 32 via the light guide 34, and then, electric signals are output. In the configuration as described above, the scintillator 1A shown in FIG. 1 can be used as the scintillator 30 for converting electrons from the object 36 into light. Further, in the configuration as described above, the metal layer 18 of the scintillator 1A can be used as an electrode for accelerating electrons emitted from the observation object 36.

[0066] FIG. 7 is a diagram schematically showing a configuration of a time of flight mass spectrometer. In the configuration example shown in FIG. 7, the electron detector including the scintillator 30, the light guide 34, and the photodetector 32 is provided for a micro channel plate (MCP) 38. In the above device, ions as a mass spectrometry object are converted into electrons by the MCP 38, the electrons emitted from the MCP 38 are caused to be incident on the scintillator 30, scintillation light generated in the scintillator 30 is detected in the photodetector 32 via the light guide 34, and then, electric signals are output. In the configuration as described above, the scintillator 1A shown in FIG. 1 can be used as the scintillator 30 for converting electrons from the MCP 38 into light.

[0067] The configuration of the scintillator 1A according to the above embodiment will be further described below with a specific configuration example. Here, formation of a ZnO film by the MOCVD method can be seen in, for example, Non Patent Document 2 (Y. Hiragino et al., Physica Status Solidi C Vol. 11 No. 7-8 (2014) pp. 1369-1372).

[0068] In the present configuration example, an a-plane sapphire substrate with a thickness of 500 ?m has been used as the support substrate 10, and the buffer layer 12 of a ZnO thin film with no impurities added has been formed with a film thickness of 250 nm on the substrate 10 by the MOCVD method. In forming the ZnO film, diethyl zinc has been used as a zinc (Zn) raw material, and tertiary butanol has been used as an oxygen (O) raw material. Further, the growth temperature has been set at 575? C., and the growth pressure has been set at 1000 hPa.

[0069] In addition, the emission layer 14 made of a ZnO single crystal thin film with Ga added has been formed on the above ZnO buffer layer 12, similarly by the MOCVD method. Here, triethyl gallium has been used as a gallium (Ga) raw material. Further, the protective layer 16 made of a SiO.sub.2 film has been formed with a film thickness of 10 nm on the impurity-added ZnO emission layer 14 by the EB evaporation method. Further, the Al metal layer 18 with a layer thickness of 50 nm has been formed on the SiO.sub.2 protective layer 16 by the vacuum evaporation method. Here, while the area of the scintillator 1A may be set to any value in accordance with, for example, the use of the scintillator, the area thereof has been set to 10 mm?10 mm here.

[0070] FIG. 8 is a graph showing a wavelength dependency of emission intensity in the scintillator according to the above configuration example. In the graph of FIG. 8, the horizontal axis shows the wavelength (nm), and the vertical axis shows the emission intensity (counts) of scintillation light. The above graph shows the emission spectrum of cathodoluminescence under electron beam excitation (6 kV) in the case of the emission layer 14 with a layer thickness of 1.2 ?m and an electron concentration of 6.7?10.sup.19 cm.sup.?3. It is clear from the emission spectrum that emission in the ZnO emission layer 14 has favorable characteristics in that the emission includes only band-edge emission with a short fluorescence lifetime, and includes no defect luminescence with a long fluorescence lifetime.

[0071] FIG. 9 is a graph showing an electron concentration dependency of emission efficiency under electron beam excitation in the scintillator. In the graph of FIG. 9, the horizontal axis shows the electron concentration (carrier concentration) (cm.sup.?3), and the vertical axis shows the emission efficiency (photon/electron).

[0072] As shown in the above graph, it is clear that emission intensity increases as the electron concentration in the emission layer 14 increases, while emission efficiency rapidly decreases when the electron concentration exceeds 10.sup.20 cm.sup.?3. This is caused by Auger effect that the energy of carrier recombination is absorbed by adjacent electrons due to the high electron concentration in the emission layer 14. In consideration of the above, it is preferable to set the electron concentration in the emission layer 14 within a range of 2?10.sup.19 cm.sup.?3 or more and 2?10.sup.20 cm.sup.?3 or less, as described above. Further, it is more preferable to set the electron concentration within a range of 5?10.sup.19 cm.sup.?3 or more and 2?10.sup.20 cm.sup.?3 or less

[0073] Here, the above-described phenomenon regarding emission intensity is not effect of concentration of impurities to be added to ZnO, but effect of the electron concentration obtained by impurities. Therefore, not only Ga (gallium) but also group III elements such as Al (aluminum) and In (indium), which serve as favorable donor impurities for ZnO, may be used as impurities to be added to ZnO.

[0074] FIG. 10 is a graph showing an electron acceleration voltage dependency of emission efficiency under electron beam excitation in the scintillator. In the graph of FIG. 10, the horizontal axis shows the acceleration voltage (kV) of an electron beam, and the vertical axis shows the emission efficiency (photon/electron). Further, in FIG. 10, a graph G1 shows emission efficiency in a configuration including no ZnO buffer layer 12, a graph G2 shows emission efficiency in a configuration including the buffer layer 12, and a graph G3 shows emission efficiency in a configuration including the SiO.sub.2 protective layer 16 having a layer thickness of 10 nm as well as the buffer layer 12. Further, a graph G5 shows emission efficiency in a plastic scintillator as a comparative example.

[0075] As shown in the above graphs, it is clear that emission efficiency is enhanced by formation of the ZnO emission layer 14 on the support substrate 10 via the buffer layer 12 in the scintillator 1A of the above configuration. Further, providing the protective layer 16 made of a material having a band gap wider than that of ZnO on the side opposite to the support substrate 10 for the emission layer 14 in addition to the buffer layer 12 allows emission efficiency to more significantly increase.

[0076] Here, shielding effect of energy from the emission layer 14 to the outside by the SiO.sub.2 protective layer 16 increases as the layer thickness increases, however, when the layer thickness of the protective layer 16 exceeds a certain value, the effect shows no change. In consideration of the above, it is preferable to set the layer thickness of the protective layer 16 within a range of 10 nm or more and 200 nm or less as described above. Further, examples of a material having a band gap wider than that of ZnO constituting the protective layer 16 include Al.sub.2O.sub.3, MgO, CaF.sub.2, BeO, MgF.sub.2, and LiF as well as SiO.sub.2 as described above.

[0077] The scintillator and the electron detector according to the present invention are not limited to the above embodiments and configuration examples, and various modifications can be made. For example, the scintillator of the above configuration is applicable not only to the above electron detector, but also to other radiation detectors.

[0078] The scintillator according to the above embodiment includes (1) a support substrate; (2) an emission layer formed on the support substrate, made of ZnO with impurities added to have an electron concentration of 2?10.sup.19 cm.sup.?3 or more and 2?10.sup.20 cm.sup.?3 or less, and for generating scintillation light in response to incidence of radiation such as an electron; (3) a protective layer formed on the emission layer and made of a material having a band gap wider than that of ZnO; and (4) a metal layer formed on the protective layer, and (5) the support substrate is made of a material transmitting the scintillation light generated in the emission layer, and the metal layer functions as a reflection layer for reflecting the scintillation light from the emission layer.

[0079] Here, examples of radiation to be detected by the above-described scintillator include particles such as electrons, protons, neutrons, ? particles, and ions, and electromagnetic waves such as a ? ray, an X ray, and light.

[0080] In the scintillator of the above configuration, it is preferable that the emission layer has a layer thickness of 0.5 ?m or more and 3.0 ?m or less. The scintillator having the impurity-added ZnO emission layer with the above layer thickness can be used preferably for detecting electrons having energy of 5 keV to 20 keV in, for example, a scanning electron microscope and a time of flight mass spectrometer. Further, it is preferable that the impurities to be added to ZnO in the emission layer include at least one element selected from the group consisting of Ga, Al, and In, and in particular, it is preferable that Ga is added to ZnO as impurities.

[0081] Further, in the scintillator of the above configuration, a buffer layer made of ZnO may be formed between the support substrate and the emission layer. It is thus possible to form the emission layer preferably by forming the impurity-added ZnO emission layer on the ZnO buffer layer.

[0082] Such a ZnO buffer layer and an emission layer as described above can be formed on the support substrate by, for example, the MOCVD (metal organic chemical vapor deposition) method. Further, in the case of providing the ZnO buffer layer between the support substrate and the emission layer as describe above, it is preferable that the buffer layer has a layer thickness of 20 nm or more and 400 nm or less.

[0083] With regard to the protective layer made of a material having a band gap wider than that of ZnO, it is preferable that the material constituting the protective layer includes at least one material selected from the group consisting of SiO.sub.2, Al.sub.2O.sub.3, MgO, CaF.sub.2, BeO, MgF.sub.2, and LiF, and in particular, it is preferable that the material constituting the protective layer is SiO.sub.2. Further, it is preferable that the protective layer has a layer thickness of 10 nm or more and 200 nm or less.

[0084] With regard to the support substrate made of the material that transmits the scintillation light, it is preferable that the support substrate is a sapphire substrate, a quartz substrate, or a glass substrate. Further, in particular, it is preferable that the support substrate is an a-plane sapphire substrate.

[0085] With regard to the metal layer formed on the protective layer, it is preferable that Al is used as a material constituting the metal layer. Further, in the case of Al being used as a material of the metal layer, it is preferable that the metal layer has a layer thickness of 10 nm or more and 50 nm or less.

[0086] The electron detector according to the above embodiment includes the scintillator having the above configuration for outputting the scintillation light generated in the emission layer in response to incidence of an electron, and a photodetector for detecting the scintillation light output from the scintillator. Such an electron detector as described above enables electrons to be detected preferably by using the scintillator with fast response. Further, in this case, the metal layer in the scintillator may be configured to function as an acceleration electrode for accelerating the electron incident on the scintillator.

INDUSTRIAL APPLICABILITY

[0087] The present invention can be used as a scintillator which can be employed preferably for detecting radiation such as electrons, and as an electron detector using the scintillator.

REFERENCE SIGNS LIST

[0088] 1Ascintillator, 2Aelectron detector, 10support substrate, 12ZnO buffer layer, 14impurity-added ZnO emission layer, 16protective layer, 18metal layer, 20photodetector, 22light guide,

[0089] 30scintillator, 32photodetector, 34light guide, 36observation object, 38micro channel plate.