METHOD AND FACILITY FOR MANUFACTURING A FIBERGLASS MATERIAL

Abstract

The invention relates to a method and facility for manufacturing a fiberglass material, in which melted glass is produced in a melting furnace heated via combustion of a fuel with an oxygen-rich oxidant. The fumes generated are used to preheat a combustion reagent in two steps: a first step in which air is heated via heat exchange with the fumes, and a second step in which the combustion reagent is preheated via heat exchange with the hot air. The air is then used in the method for converting the melted glass into a fiberglass material.

Claims

1-13. (canceled)

14. A process for the manufacture of a glass fiber product in which molten glass is converted into a glass fiber product by: spinning the molten glass into at least one stream; attenuating the at least one stream into one or more filaments; collecting the filament or filaments; and optionally one or more of the following stages: sizing the filament or filaments upstream of their collection, drying the filament or filaments, application of adhesive to the filament or filaments before or after their collection, followed by a crosslinking of the adhesive-treated collective filament or filaments, and texturing the filament or filaments or strands containing them, wherein: in which process the molten glass is produced in a melting furnace heated by combustion of a fuel with a rich oxidizer having an oxygen content of 80 vol % to 100 vol %, with generation of heat and flue gases, said generated flue gases being discharged from the melting furnace at a temperature between 1000 C. and 1600 C.; air is heated by heat exchange with discharged flue gases in a heat-exchange assembly with hot air being obtained, a reactant chosen from rich oxidizers and gaseous fuels is preheated by heat exchange with the hot air in the heat-exchange assembly with the production of preheated reactant and of moderated air at a temperature between 200 C. and 500 C., the preheated reactant is used as combustion reactant in the furnace, and moderated air resulting from the heat-exchange assembly is employed during the conversion of the molten glass into a glass fiber product in at least one of the following stages: during the attenuation of the stream for the production of one or more attenuation gas currents, during the sizing of the filament or filaments as spraying agent for a sizing agent, during the application of adhesive to the filament or filaments as spraying agent for an adhesive binder, during the drying of the filament or filaments as drying agent, and during the texturing of the filaments or strands containing them as texturing gas current.

15. The process of claim 14, wherein the heat-exchange assembly comprises a primary exchanger and a secondary exchanger, air being heated by heat exchange with flue gases discharged from the furnace in the primary exchanger, with hot air at a temperature between 500 C. and 800 C. being obtained, and the combustion reactant is preheated in the secondary exchanger by heat exchange with hot air resulting from the primary exchanger.

16. The process of claim 14, wherein the moderated air resulting from the heat-exchange assembly is used for the production of one or more attenuation gas currents.

17. The process of claim 16, wherein the attenuation is a flame attenuation using an attenuation flame generated by combustion of a fuel with moderated air resulting from the heat-exchange assembly.

18. The process of claim 16, wherein the attenuation is a gas attenuation using an attenuation gas jet generated by combustion of a fuel with moderated air resulting from the heat-exchange assembly.

19. The process of claim 18, wherein the attenuation is a centrifugal attenuation followed by a gas attenuation with an attenuation gas jet generated by combustion of a fuel with moderated air resulting from the heat-exchange assembly.

20. The process of claim 14, wherein the glass fiber product is chosen from reinforcing fibers or strands, textile or reinforcing fabrics, acoustic insulation products, thermal insulation products and fire-protection products.

21. A plant comprising a glass melting furnace and a conversion unit for the conversion of molten glass into a glass fiber product: a melting furnace comprising a molten glass outlet, an outlet for flue gases and at least one burner for the combustion of a fuel with a rich oxidizer having an oxygen content of 80 vol % to 100 vol %; a conversion unit comprising: a bushing for the spinning of molten glass resulting from the melting furnace into at least one stream, said bushing being fluidically connected to the molten glass outlet of the furnace; an attenuation device for the attenuation of at least one stream resulting from the bushing into one or more filaments; a collector for the collecting of the filament or filaments resulting from the attenuation device; optionally one or more of a sizer for the sizing of the filament or filaments upstream of the collector, a dryer for the drying of the filament or filaments upstream of the collector, an adhesive applicator for the application of adhesive (a binder) to the filament or filaments, and a crosslinking chamber for the crosslinking of the adhesive-treated collected filament or filaments; and a texturing chamber for the texturing of the filament or filaments or of strands containing it; and a heat-exchange assembly for the heating of air by heat exchange with flue gases discharged from the furnace and for the preheating of a combustion reactant by heat exchange with the hot air, with preheated combustion reactant and moderated air being obtained, the heat-exchange assembly being fluidically connected to a source of air, to the flue gas outlet of the furnace and to a source of a combustion reactant chosen between rich oxidizer and gaseous fuel, wherein the moderated air being used in one or more of: the heat-exchange assembly in case the heat-exchange assembly includes a preheated combustion reactant outlet fluidically connected to the burner of the melting furnace and also a moderated air outlet fluidically connected to at least one of the following devices: the attenuation device in which case the moderated air is used for the production of an attenuation flame or of an attenuation gas current; the optional sizer in which case the moderated air is used as a spraying agent for a sizing agent; the optional dryer in which case the moderated air is used as a drying agent in contact with the filament or filaments; the optional adhesive applicator in which case the moderated air is used as a spraying agent for the binder; the optional texturing chamber in which case the moderated air is used as a texturing gas current; and the optional texturing chamber in which case the moderated air is used for generating a texturing gas current.

22. The plant of claim 21, wherein the heat-exchange assembly comprises a primary exchanger for heat exchange between the flue gases discharged from the furnace and the air and a secondary exchanger for heat exchange between the heated air resulting from the primary exchanger and the combustion reactant.

23. The plant of claim 21, wherein the moderated air outlet is fluidically connected to the attenuation device for the production of an attenuation flame or of an attenuation gas current.

24. The plant of claim 23, wherein the attenuation device comprises an attenuation burner fluidically connected to the moderated air outlet for the preparation of an attenuation flame or of an attenuation gas current by combustion of a fuel with moderated air resulting from the secondary exchanger.

25. The plant of claim 24, wherein the attenuation device also comprises a centrifuge, the attenuation burner being annular and capable of generating an attenuation gas current around the centrifuge.

26. The plant of claim 21, comprising a hood surrounding the attenuation device, said hood optionally also surrounding one or more of the following devices: the sizer, the dryer and the adhesive applicator.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0116] FIG. 1 is a diagrammatic representation of a process and of a plant for the manufacture of a thermal insulation/acoustic insulation and/or fire-protection fleece.

DETAILED DESCRIPTION OF THE INVENTION

[0117] The plant illustrated in FIG. 1 comprises a glass melting furnace 10 heated by a number of burners 12 (just one burner is shown in the FIGURE).

[0118] To this end, rich oxidizer 28a, typically a gas containing between 80 vol % and 100 vol % of oxygen, and a gaseous fuel 29a, such as natural gas, are supplied to said burners 12.

[0119] The flue gases or combustion gases generated by the combustion of the fuel 29a with the rich oxidizer 28a are discharged from the melting furnace 10 and introduced into a primary exchanger 20 in order to heat the compressed or uncompressed air 24 supplied by the compressor or a fan 23.

[0120] Downstream of the primary exchanger 20, the flue gases are discharged through the chimney 11, typically after having been subjected to a treatment for removal of pollutants and dust.

[0121] The hot air 25 resulting from the primary exchanger 20 is introduced into a first secondary exchanger 21 for the preheating of the rich oxidizer 28a and subsequently, in the form of partially moderated air 26, into a second secondary exchanger 22 for the preheating of the gaseous fuel 29a.

[0122] The preheated rich oxidizer 28b resulting from the first secondary exchanger 21 and the preheated gaseous fuel 29b resulting from the second secondary exchanger 22 are supplied to the burners 12 as combustion reactants.

[0123] This makes possible a first very significant saving in energy in the manufacturing process according to the invention.

[0124] The molten glass resulting from the melting furnace 10 is introduced in the form of a stream of molten glass into a centrifuge 34 and the filaments resulting from the centrifuge 34 are attenuated by means of an annular current of attenuation gas generated by the crown-shaped attenuation burner 31.

[0125] The filaments resulting from this attenuation assembly are treated with adhesive by the sprayers 32 of binder 35 and subsequently dried by gaseous drying agent jets 36 injected by the dryers 33.

[0126] The stages of attenuation, of application of adhesive and of drying are carried out in a controlled environment inside a hood 30.

[0127] The dried adhesive-treated filaments are collected in the form of a fleece 44 of filaments by a conveyor 42 in the bottom of the hood 30.

[0128] The conveyor 42 brings the fleece 44 toward a crosslinking oven 40 in which the adhesive-treated filaments are crosslinked under the effect of heat and are thus board together.

[0129] Downstream of the oven 40, the rigid, semirigid or flexible fleece is shaped and wrapped up.

[0130] According to the invention, the residual heat present in the moderated air 27 resulting from the secondary exchangers 21, 22 is made use of in order to improve the energy efficiency of the conversion process downstream of the melting furnace 10.

[0131] Thus, a portion of the moderated air 27 is introduced as oxidant into the attenuation burner 31 in order to more efficiently generate the attenuation gas current.

[0132] Another portion of the moderated air 27 is used as drying gas 36 by the dryers 33, the residual heat of the moderated air 27 making it possible to accelerate the drying of the filaments.

[0133] In the illustrated embodiment, a final portion of the moderated air 27 is introduced into the crosslinking oven and sucked through the fleece 44 inside the oven in order to promote the crosslinking of the filaments in the fleece 44.

[0134] The advantages of the present invention are illustrated in the example below.

[0135] The melting furnace produces 100 tpd of insulation fiber from 5 MW of thermal power. A contribution of electrical energy of the order of 1 to 5 MWe may be necessary according to the production conditions. The combustion flue gases exit at 1350 C. and can be cooled by dilution with ambient air to reach a temperature of 1200 C. at the inlet of the recuperator.

[0136] The 500 Sm.sup.3/h of natural gas (95% methane, 2% butane, 2% propane and 1% CO.sub.2) are preheated to 450 C. The 1000 Sm.sup.3/h of oxygen are preheated to 550 C.

[0137] In order to preheat these gases, close to 4000 Sm.sup.3/h are necessary. Heated to 650 C. in the primary exchanger, the air is cooled to 400 C. at the outlet of the secondary exchanger.

[0138] This moderated air, which has an energy value of 530 kW, is subsequently conveyed, in a pipe preferably made of stainless steel: [0139] on the one hand, toward the generator of hot attenuation gases surrounding the attenuation centrifuges [0140] on the other hand, toward the battery of drying gas guns.

[0141] By virtue of this hot air, the amount of fuel consumed during the attenuation is significantly reduced (10%).

[0142] While the invention has been described in conjunction with specific embodiments thereof, it is evident that many alternatives, modifications, and variations will be apparent to those skilled in the art in light of the foregoing description. Accordingly, it is intended to embrace all such alternatives, modifications, and variations as fall within the spirit and broad scope of the appended claims. The present invention may suitably comprise, consist or consist essentially of the elements disclosed and may be practiced in the absence of an element not disclosed. Furthermore, if there is language referring to order, such as first and second, it should be understood in an exemplary sense and not in a limiting sense. For example, it can be recognized by those skilled in the art that certain steps can be combined into a single step.

[0143] The singular forms a, an and the include plural referents, unless the context clearly dictates otherwise.

[0144] Comprising in a claim is an open transitional term which means the subsequently identified claim elements are a nonexclusive listing i.e. anything else may be additionally included and remain within the scope of comprising, Comprising is defined herein as necessarily encompassing the more limited transitional terms consisting essentially of and consisting of; comprising may therefore be replaced by consisting essentially of or consisting of and remain within the expressly defined scope of comprising.

[0145] Providing in a claim is defined to mean furnishing, supplying, making available, or preparing something. The step may be performed by any actor in the absence of express language in the claim to the contrary.

[0146] Optional or optionally means that the subsequently described event or circumstances may or may not occur. The description includes instances where the event or circumstance occurs and instances where it does not occur.

[0147] Ranges may be expressed herein as from about one particular value, and/or to about another particular value. When such a range is expressed, it is to be understood that another embodiment is from the one particular value and/or to the other particular value, along with all combinations within said range.

[0148] All references identified herein are each hereby incorporated by reference into this application in their entireties, as well as for the specific information for which each is cited.