ALD processes for low leakage current and low equivalent oxide thickness BiTaO films

Abstract

A high dielectric constant (k40), low leakage current (10.sup.6 A/cm.sup.2 at 0.6 nm or lower equivalent oxide thickness) non-crystalline metal oxide is described, including an oxide of two or more compatible metals selected from the group consisting of bismuth, tantalum, niobium, barium, strontium, calcium, magnesium, titanium, zirconium, hafnium, tin, and lanthanide series metals. Metal oxides of such type may be formed with relative proportions of constituent metals being varied along a thickness of such oxides, to enhance their stability. The metal oxide may be readily made by a disclosed atomic layer deposition process, to provide a metal oxide dielectric material that is usefully employed in DRAM and other microelectronic devices.

Claims

1. A high dielectric constant, low leakage current non-crystalline metal oxide, comprising an oxide of two or more compatible metals selected from the group consisting of bismuth, tantalum, niobium, barium, strontium, calcium, magnesium, titanium, zirconium, hafnium, tin, and lanthanide series metals, the metal oxide having a dielectric constant in a range of from 40 to 75, and a leakage current in a range of from 10.sup.6 A/cm.sup.2 to 10.sup.9 A/cm.sup.2 at 0.6 nm or lower equivalent oxide thickness, in a microelectronic device structure including a bottom electrode on which the high dielectric constant, low leakage current non-crystalline metal oxide is deposited, and a top electrode formed on the high dielectric constant, low leakage current non-crystalline metal oxide, optionally with a metal oxide capping layer between the high dielectric constant, low leakage current non-crystalline metal oxide and the top electrode.

2. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 1, comprising metal oxide selected from the group consisting of BiTaO, LnTaO, LnTiO, (Ba,Sr) tetratitanates, and ZrTiSnO, wherein Ln comprises a lanthanide series metal.

3. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 1, comprising BiTaO.

4. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 1, in which the metal oxide comprises different relative proportions of the metals therein.

5. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 1, wherein the high dielectric constant, low leakage current non-crystalline metal oxide is annealed at a temperature below crystallization temperature.

6. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 3, wherein metal proportions are 3Bi:2Ta.

7. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 3, wherein metal proportions are 5Bi:4Ta.

8. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 3, wherein metal proportions are 1Bi:1Ta.

9. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 3, wherein metal proportions are 4Bi:5Ta.

10. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 3, wherein metal proportions are 2Bi:3Ta.

11. The high dielectric constant, low leakage current non-crystalline metal oxide of claim 3, wherein metal proportions are 1Bi:2Ta.

12. A high dielectric constant, low leakage current non-crystalline metal oxide, comprising LnTaO, wherein Ln comprises a lanthanide series metal.

13. A high dielectric constant, low leakage current non-crystalline metal oxide, comprising LnTiO, wherein Ln comprises a lanthanide series metal.

14. A high dielectric constant, low leakage current non-crystalline metal oxide, comprising ZrTiSnO.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a schematic representation of a generalized high dielectric constant capacitor including a high k, low current leakage material of the present disclosure.

(2) FIG. 2 is a schematic representation of a portion of an integrated circuit with an integrated capacitor according to one embodiment of the disclosure.

(3) FIG. 3 is a graph of current density, J, in amperes per square centimeter (A/cm.sup.2) at voltage of +1 v, as a function of equivalent oxide thickness, in nanometers, for 3Ta/2La, 3Ta/1La, and BiTaO films, deposited by atomic layer deposition.

(4) FIG. 4 is a cycle sequence diagram for a precursor burst cycle with single boost of the precursor dose by the purge gas, as usefully employed in the method of the present disclosure for deposition of mixed metal oxide on a substrate.

(5) FIG. 5 is a cycle sequence diagram for a precursor pulse sequence including three boost doses of the precursor with purge gas, according to another embodiment of the disclosure.

(6) FIG. 6 is a graph of bismuth oxide deposition rate, in Angstroms per cycle, as a function of the number of doses, using triphenylbismuth as the bismuth precursor, in the deposition of a BiTaO material on a titanium nitride substrate.

(7) FIG. 7 is a graph of bismuth oxide deposition rate, in Angstroms per cycle, as a function of the number of doses, using (CH.sub.3).sub.2Bi(C.sub.6H.sub.4)CH.sub.2N(CH.sub.3).sub.2 as the bismuth precursor, in the deposition of a BiTaO material on a titanium nitride substrate.

(8) FIG. 8 is a graph of atomic % bismuth as a function of film thickness, in Angstroms, for different ratios of bismuth:tantalum, namely, 3Bi:2Ta, 5Bi:4Ta, 1Bi:1Ta, 4Bi:5Ta, 2Bi:3Ta, and 1Bi:2Ta, for films deposited in this evaluation, as baseline process response data.

(9) FIG. 9 is a graph of current density, J, in units of amperes per square centimeter (A/cm.sup.2), as measured at +1 volt, as a function of equivalent oxide thickness (EOT), in nanometers (nm), for films of different ratios of bismuth:tantalum, namely, 3Bi:2Ta, 5Bi:4Ta, 1Bi:1Ta, 4Bi:5Ta, 2Bi:3Ta, and 1Bi:2Ta.

(10) FIG. 10 is a graph of current density, J, in units of amperes per square centimeter (A/cm.sup.2), as measured at +1 volt, as a function of equivalent oxide thickness (EOT), in nanometers (nm), for films of different ratios of bismuth:tantalum capped with a tantalum cap (Tacap) or an aluminum cap (Alcap), namely, 3Bi:2Ta+Alcap, 5Bi:4Ta+Tacap, 1Bi:1Ta+Tacap, 1Bi:1Ta+Alcap, 4Bi:5Ta+Tacap, and 2Bi:3Ta+Alcap.

(11) FIG. 11 is a graph of current density, J, in units of amperes per square centimeter (A/cm.sup.2), as measured at +1 volt, as a function of film thickness, in Angstroms, showing the effect of film thickness and % Bi in the deposited film, for films of different ratios of bismuth:tantalum, namely, 3Bi:2Ta, 5Bi:4Ta, 1Bi:1Ta, 4Bi:5Ta, 2Bi:3Ta, and 1Bi:2Ta.

(12) FIG. 12 is a graph of minimum dielectric constant, k min, as a function of film thickness, in Angstroms, as determined by XRF technique, showing the effect of film thickness and % Bi in the deposited film, for films of different ratios of bismuth:tantalum, namely, 3Bi:2Ta, 5Bi:4Ta, 1Bi:1Ta, 4Bi:5Ta, 2Bi:3Ta, and 1Bi:2Ta.

(13) FIG. 13 is a graph of current density, J, measured at +1V, in Angstroms per square centimeter (A/cm.sup.2), as a function of equivalent oxide thickness, in nanometers (nm), for the following BiTaO films: (i) >30% Bi as-deposited, (ii) >30% Bi+450 RTO/400 RTN, (iii) 25-30% Bi as-deposited, (iv) 25-30% Bi+450 RTO/400 RTN, (v) 20-25% Bi as-deposited, and (vi) 20-25% Bi+450 RTO/400 RTN.

(14) FIG. 14 is a graph of current density, J, in amperes per square centimeter (A/cm.sup.2) at voltage of +1 v, as a function of equivalent oxide thickness (EOT), in nanometers, for BiTaO films containing 8% Bi, including 8% Bi-containing BiTaO films as deposited (.diamond-solid.), 8% Bi-containing BiTaO films processed by rapid thermal oxidation at 450 C. (.square-solid.), and 8% Bi-containing BiTaO films processed by rapid thermal nitridation at 450 C. (.box-tangle-solidup.).

(15) FIG. 15 is a graph of current density, J, in amperes per square centimeter (A/cm.sup.2) at voltage of +1 v, as a function of equivalent oxide thickness (EOT), in nanometers, for uniform composition films at higher bismuth content of 27% Bi and thickness of 3.7 nm, including 27% Bi-containing BiTaO films as deposited (.diamond-solid.), and 27% Bi-containing BiTaO films processed by rapid thermal oxidation at 450 C. (.square-solid.).

(16) FIG. 16 is a graph of current density, J, in amperes per square centimeter (A/cm.sup.2) at voltage of +1 v, as a function of equivalent oxide thickness (EOT), in nanometers, for compositionally modulated films in which deposition was carried out according to Modulated Scheme 1, including films as deposited (.diamond-solid.), as processed by rapid thermal oxidation at 450 C. (.square-solid.), and as processed by rapid thermal nitridation at 450 C. (.box-tangle-solidup.).

(17) FIG. 17 is a graph of current density, J, in amperes per square centimeter (A/cm.sup.2) at voltage of +1 v, as a function of equivalent oxide thickness (EOT), in nanometers, for compositionally modulated films in which deposition was carried out according to Modulated Scheme 2, including films as deposited (.diamond-solid.), as processed by rapid thermal oxidation at 450 C. (.square-solid.), and as processed by rapid thermal nitridation at 450 C. (.box-tangle-solidup.).

DETAILED DESCRIPTION

(18) The present disclosure relates to high dielectric constant (k40), low leakage current (10.sup.6 A/cm.sup.2 at 0.6 nm or lower equivalent oxide thickness) non-crystalline metal oxide materials and processes for making such materials by atomic layer deposition (ALD).

(19) As used herein and in the appended claims, the singular forms a, and, and the include plural referents unless the context clearly dictates otherwise.

(20) The disclosure, as variously set out herein in respect of features, aspects and embodiments thereof, may in particular implementations be constituted as comprising, consisting, or consisting essentially of, some or all of such features, aspects and embodiments, as well as elements and components thereof being aggregated to constitute various further implementations of the disclosure. The disclosure correspondingly contemplates such features, aspects and embodiments, or a selected one or ones thereof, in various permutations and combinations, as being within the scope of the present disclosure.

(21) As used herein, the term film refers to a layer of deposited material having a thickness below 1000 micrometers, e.g., from such value down to atomic monolayer thickness values. In various embodiments, film thicknesses of deposited material layers in the practice of the invention may for example be below 100, 10, or 1 micrometers, or in various thin film regimes below 200, 100, or 50 nanometers, depending on the specific application involved. Typical dielectric thickness for high aspect ratio capacitors in DRAM devices is 3 to 12 nanometers. As used herein, the term thin film means a layer of a material having a thickness below 1 micrometer.

(22) As used herein, the term lower in reference to hydrocarbon groups means a linear, branched, or cyclic hydrocarbon group having from 1 to 6 carbon atoms in the group referenced by such term.

(23) The disclosure relates in one aspect to a high dielectric constant, low leakage current non-crystalline metal oxide, comprising an oxide of two or more compatible metals selected from the group consisting of bismuth, tantalum, niobium, barium, strontium, calcium, magnesium, titanium, zirconium, hafnium, tin, and lanthanide series metals. In a specific embodiment, the metals may be selected from the group consisting of bismuth, tantalum, lanthanum, titanium, barium, strontium, zirconium, and tin.

(24) The metal oxide of such character may for example comprise a metal oxide such as BiTaO, LnTaO, LnTiO, (Ba,Sr) tetratitanates, or ZrTiSnO, wherein Ln is a lanthanide series element, e.g., lanthanum, cerium, prasoedymium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, or ytterbium. The notation M.sup.1M.sup.2O is used herein to indicate a mixture of the oxide of M.sup.1 with the oxide of M.sup.2 over a broad range from 5-95% on a metals basis. For example, BiTaO indicates a mixture of Bi.sub.2O.sub.3 and Ta.sub.2O.sub.5. When reference is made to a mixture as having 20% Bi, it is meant that there are 0.2 moles of Bi atoms for every 1 mole of Bi atoms+Ta atoms. The oxygen content of the film is not explicitly specified in such nomenclature.

(25) The high dielectric constant, low leakage current non-crystalline metal oxide in various embodiments has a dielectric constant in a range of from 40 to 75. Metal oxides of the disclosure may additionally, or alternatively, have a leakage current in a range of from 10.sup.6 A/cm.sup.2 to 10.sup.9 A/cm.sup.2 at 0.6 nm or lower equivalent oxide thickness (EOT), e.g. at EOT of 0.5 nm. In some embodiments, the dielectric constant of the high dielectric constant, low leakage current non-crystalline metal oxide is in a range of from 45 to 75, and in other embodiments such dielectric constant is in a range of from 50 to 75. Higher dielectric constants, e.g., up to 90 or more, are useful in some applications and are contemplated in the broad practice of the present disclosure.

(26) High dielectric constant, low leakage current metal oxides of the disclosure are usefully employed in capacitor, inductor, or transistor devices or otherwise in microelectronic or integrated circuit devices, such as DRAM devices.

(27) In various embodiments, the high dielectric constant, low leakage current non-crystalline metal oxide of the disclosure comprises BiTaO or lanthanum tantalate, e.g., in the form of a film or more specifically a thin film.

(28) The disclosure relates in another aspect to a method of forming a high dielectric constant, low leakage current non-crystalline metal oxide, comprising depositing on a substrate in an atomic layer deposition process a first metal in a first pulsed deposition step, reacting the deposited first metal with an oxic co-reactant to form an oxide of the first metal, and depositing on the substrate in the atomic layer deposition process a second metal in a subsequent pulsed deposition step, to form a mixed metal oxide as said high dielectric constant, low leakage current non-crystalline metal oxide, wherein the metals in such mixed metal oxide comprise two or more compatible metals selected from the group consisting of bismuth, tantalum, niobium, barium, strontium, calcium, magnesium, titanium, zirconium, hafnium, tin, and lanthanide series metals.

(29) In this method, the oxic co-reactant may comprise ozone, or oxygen, or other oxidant. Other common examples include water, peroxides, and nitrogen oxides. The method of forming the metal oxide can be carried out at any suitable temperature, e.g., a temperature in a range of from 200 C. to 400 C.

(30) The method may be carried out to form the high dielectric constant, low leakage current non-crystalline metal oxide, wherein the two or more compatible metals are selected from the group consisting of bismuth, tantalum, lanthanum, titanium, barium, strontium, zirconium, and tin. The mixed metal oxide can for example comprise any of BiTaO, LnTaO, LnTiO, (Ba,Sr) tetratitanates, and ZrTiSnO, wherein Ln comprises a lanthanide series metal.

(31) The ALD method may be carried out using any suitable organometallic precursors for the metals of the mixed metal oxide. In one embodiment, wherein the mixed metal oxide comprises BiTaO, the atomic layer deposition process can be carried out using triphenylbismuth as a bismuth precursor therein. In other embodiments, the substituted phenylbismuth or substituted triphenylbismuth compounds hereinafter described may be employed. The tantalum precursor in various embodiments may for example comprise tris(diethylamino)(tert-butylimido)tantalum. [TaN-t-butyl(NEt.sub.2).sub.3]. In an atomic layer deposition process carried out with triphenylbismuth as a bismuth precursor therein, and tris(diethylamino)(tert-butylimino)tantalum. [TaN-t-butyl(NEt.sub.2).sub.3], as a tantalum precursor therein, ozone may advantageously be employed as an oxic co-reactant therein. For some metals, volatile halide-containing species can also be used as a metal source.

(32) The above-described method can be carried out to produce high dielectric constant, low leakage current non-crystalline metal oxide having a dielectric constant in a range of from 40 to 75, and/or a leakage current in a range of from 10.sup.6 A/cm.sup.2 to 10.sup.9 A/cm.sup.2 at 0.6 nm or lower equivalent oxide thickness.

(33) The high dielectric constant, low leakage current non-crystalline metal oxide produced by the above-describe method, or otherwise in the broad practice of the present disclosure, can be further processed for subsequent operation, by post-deposition processes such as annealing. Annealing, when employed, can be carried out at suitable temperature, preferably below crystallization temperature of the metal oxide. In various embodiments, it is preferred to anneal the non-crystalline high k dielectric in an oxidizing ambient to stabilize the properties for further processing. Subsequent thermal processing can include deposition of a top electrode followed by interconnection processes.

(34) The method described above may be carried out with the deposition of the metal oxide being performed on a titanium nitride surface, e.g., of a titanium nitride bottom electrode of a microelectronic device structure, wherein, after depositing metal oxide on the titanium nitride surface of the titanium nitride bottom electrode, a top electrode is deposited on the metal oxide, e.g., iridium oxide or other suitable top electrode material.

(35) In various embodiments, the ALD method of the present disclosure is employed to form a bismuth tantalate (BiTaO) material having high dielectric constant (k) value, e.g., from 40 up to 75 or more, and low current leakage character, as for example current leakage density in a range of from 10.sup.6 A/cm.sup.2 to 10.sup.9 A/cm.sup.2 at 0.6 nm or lower equivalent oxide thickness.

(36) Films of such composition may be formed by bismuth doping of a tantalum oxide thin film using ALD, to produce BiTaO films of the desired high dielectric constant and low current leakage character. The BiTaO film produced by such method is non-crystalline, and therefore lacks the leakage as it would otherwise be associated with grain boundaries and other extended defects in crystalline films. The use of ALD to produce the BiTaO films of the present disclosure enables the fabrication of high aspect ratio structures, such as those currently employed in dynamic random access memory (DRAM) metal-insulator-metal (MIM) structures, to be conformally coated with a uniform layer of the dielectric material.

(37) Among various bismuth precursors that may be used to form high dielectric constant, low leakage current bismuth-containing metal oxides in accordance with the present disclosure, bismuth compounds of the following Classes I, II, and III have been found to exhibit desirable vaporization characteristics and thermal stability:

(38) ##STR00001##
wherein R.sup.1 represents a lower alkyl group; R.sup.2 represents a lower alkyl group, a lower alkoxy group, a lower acyl group, a lower alkoxycarbonyl group, a lower halogenated alkyl group, or a halogen; n.sup.1 represents the number of the substituent R.sup.2 in the range of 0-4; and R.sup.3 to R.sup.6 each represents hydrogen, a lower alkyl group, or a lower halogenated alkyl group;

(39) ##STR00002##
wherein R.sup.7 represents a lower alkyl group; R.sup.8 represents a lower alkyl group, a lower alkoxy group, a lower acyl group, a lower alkoxycarbonyl group, a lower halogenated alkyl group, or a halogen; n.sup.2 represents the number of the substituent R.sup.8 in the range of 0-4; and R.sup.9 to R.sup.11 each represents hydrogen, a lower alkyl group, or a lower halogenated alkyl group; and

(40) ##STR00003##
wherein R.sup.12 and R.sup.13 each represents a lower alkyl group, a lower alkoxy group, a lower acyl group, a lower alkoxycarbonyl group, a lower halogenated alkyl group, or a halogen; m represents the number of the substituent R.sup.12 in the range of 0-5; n.sup.3 represents the number of the substituent R.sup.13 in the range of 0-4; R.sup.14 and R.sup.15 each represents hydrogen, a lower alkyl group, or a lower halogenated alkyl group; and X represents a substituent represented by the following formula 10 or 11:

(41) ##STR00004##
wherein R.sup.16 to R.sup.18 each represents hydrogen, a lower alkyl group, or a lower halogenated alkyl group.

(42) Precursors of Class I can be formed by reaction of a monoaryl dihalogenated bismuth compound of the formula

(43) ##STR00005##
wherein R.sup.2, n.sup.1, and R.sup.3 to R.sup.6 are the same as defined above; and Z.sup.1 represents a halogen, with an R.sup.1 converting reagent, wherein R.sup.1 is the same as defined above.

(44) Precursors of Class I can also be synthesized by reacting a dialkyl monohalogenated bismuth compound of the formula

(45) ##STR00006##
wherein R.sup.1 and Z.sup.1 are the same as defined above,
with an arylating reagent represented by the following formula:

(46) ##STR00007##
wherein R.sup.2, n.sup.1, and R.sup.3 to R.sup.6 are the same as defined above; and Q.sup.1 represents any of lithium, sodium, potassium, MgCl, MgBr, or MgI.

(47) Precursors of Class II can be formed by reaction of a monoaryl dihalogenated bismuth compound of the formula

(48) ##STR00008##
wherein R.sup.8, n.sup.2, and R.sup.9 to R.sup.11 are the same as defined above; and Z.sup.2 represents a halogen, with an R.sup.7 converting reagent, wherein R.sup.7 is the same as defined above.

(49) Precursors of Class II can also be formed by reaction of a dialkyl monohalogenated bismuth compound of the formula

(50) ##STR00009##
wherein R.sup.7 and Z.sup.2 are the same as defined above, with an arylating reagent of the formula

(51) ##STR00010##
wherein R.sup.8, n.sup.2, and R.sup.9 to R.sup.11 are the same as defined above; and Q.sup.2 represents any of lithium, sodium, potassium, MgCl, MgBr, or MgI.

(52) Precursors of Class III can be formed by reacting a diaryl monohalogenated bismuth compound of the following formula

(53) ##STR00011##
wherein R.sup.12 and m are the same as defined above; and Z.sup.3 represents a halogen, with an arylating reagent of the following formula

(54) ##STR00012##
wherein R.sup.13, R.sup.14, R.sup.15, n.sup.3, and X are the same as defined above; and Q.sup.3 represents an alkali metal, MgCl, MgBr, or MgI.

(55) Illustrative bismuth compounds of the foregoing Classes I-III include: diisopropyl(2-(N,N-diethylaminomethyl)-4-propylphenyl)bismuth, dimethyl(2-(N,N-dimethylaminomethyl)-4-methoxyphenyl)bismuth, diisopropyl(2-(N,N-diethylaminomethyl)-4-methoxyphenyl)bismuth, dimethyl(2-methoxymethyl-4-propylphenyl)bismuth, diisopropyl(2-methoxymethyl-4-propylphenyl)bismuth, dimethyl(2-methoxymethyl-4-methoxyphenyl)bismuth, diisopropyl(2-methoxymethyl-4-methoxyphenyl)bismuth, dimethyl(2-(N-ethyl-N-methylaminomethyl)phenyl)bismuth, dimethyl(2-(N,N-diethylaminomethyl)phenyl)bismuth, dimethyl(2-(1-(N,N-dimethylamino)ethyl)phenyl)bismuth, dimethyl(2-(1-(N,N-diethylamino)ethyl)phenyl)bismuth, dimethyl(2-(1-(N,N-dimethylamino)-1-methylethyl)phenyl)bismuth, dimethyl(2-(1-(N,N-diethylamino)-1-methylethyl)phenyl)bismuth, dimethyl(2-(N,N-dimethylaminomethyl)-3-tolyl)bismuth, dimethyl(2-(N,N-dimethylaminomethyl)-4-tolyl)bismuth, dimethyl(2-(N,N-dimethylaminomethyl)-5-tolyl)bismuth, dimethyl(2-(N,N-dimethylaminomethyl)-6-tolyl)bismuth, dimethyl(2-(1-ethoxyethyl)phenyl)bismuth, dimethyl(2-(1-methoxy-1-methylethyl)phenyl)bismuth, dimethyl(2-methoxymethyl-3-tolyl)bismuth, dimethyl(2-methoxymethyl-4-tolyl)bismuth, dimethyl(2-methoxymethyl-5-tolyl)bismuth, dimethyl(2-methoxymethyl-6-tolyl)bismuth, dimethyl(2-ethoxymethyl-3-tolyl)bismuth, dimethyl(2-ethoxymethyl-4-tolyl)bismuth, dimethyl(2-ethoxymethyl-5-tolyl)bismuth, dimethyl(2-ethoxymethyl-6-tolyl)bismuth, di(4-propylphenyl)(2-(N,N-dimethylaminomethyl)-4-propylphenyl)bismuth, di(4-acetylphenyl)(2-(N,N-dimethylaminomethyl)-4-propylphenyl)bismuth, di(4-propylphenyl)(2-methoxymethyl-4-propylphenyl)bismuth, di(4-acetylphenyl)(2-methoxymethyl-4-propylphenyl)bismuth, di(2-tolyl)(2-(N,N-dimethylaminomethyl)phenyl)bismuth, di(3-tolyl)(2-(N,N-dimethylaminomethyl)phenyl)bismuth, diphenyl(2-(N,N-dimethylaminomethyl)-4-methylphenyl)bismuth, di(2-tolyl)(2-(N,N-dimethylaminomethyl)-4-methylphenyl)bismuth, di(3-tolyl)(2-(N,N-dimethylaminomethyl)-4-methylphenyl)bismuth, di(4-tolyl)(2-(N,N-dimethylaminomethyl)-4-methylphenyl)bismuth, di(2-ethylphenyl)(2-(N,N-dimethylaminomethyl)-4-methylphenyl)bismuth, di(3-ethylphenyl)(2-(N,N-dimethylaminomethyl)-4-methylphenyl)bismuth, di(4-ethylphenyl)(2-(N,N-dimethylaminomethyl)-4-methylphenyl)bismuth, diphenyl(2-(N,N-diethylaminomethyl)phenyl)bismuth, di(2-tolyl)(2-(N,N-diethylaminomethyl)phenyl)bismuth, di(3-tolyl)(2-(N,N-diethylaminomethyl)phenyl)bismuth, di(4-tolyl)(2-(N,N-diethylaminomethyl)phenyl)bismuth, diphenyl(2-(N,N-diethylaminomethyl)-4-methylphenyl)bismuth, di(2-tolyl)(2-(N,N-diethylaminomethyl)-4-methylphenyl)bismuth, di(3-tolyl)(2-(N,N-diethylaminomethyl)-4-methylphenyl)bismuth, di(4-tolyl)(2-(N,N-diethylaminomethyl)-4-methylphenyl)bismuth, di(2-ethylphenyl)(2-(N,N-diethylaminomethyl)-4-methylphenyl)bismuth, di(3-ethylphenyl)(2-(N,N-diethylaminomethyl)-4-methylphenyl)bismuth, di(4-ethylphenyl)(2-(N,N-diethylaminomethyl)-4-methylphenyl)bismuth, diphenyl(2-(N-ethyl-N-methylaminomethyl)phenyl)bismuth, di(2-tolyl)(2-N-ethyl-N-methylaminomethyl)phenyl)bismuth, di(3-tolyl)(2-N-ethyl-N-methylaminomethyl)phenyl)bismuth, di(4-tolyl)(2-N-ethyl-N-methylaminomethyl)phenyl)bismuth, diphenyl(2-(N-ethyl-N-methylaminomethyl)-4-methylphenyl)bismuth, di(2-tolyl)(2-(N-ethyl-N-methylaminomethyl)-4-methylphenyl)bismuth, di(3-tolyl)(2-(N-ethyl-N-methylaminomethyl)-4-methylphenyl)bismuth, di(4-tolyl)(2-(N-ethyl-N-methylaminomethyl)-4-methylphenyl)bismuth, di(2-ethylphenyl)(2-(N-ethyl-N-methylaminomethyl)-4-methylphenyl)bismuth, di(3-ethylphenyl)(2-(N-ethyl-N-methylaminomethyl)-4-methylphenyl)bismuth, di(4-ethylphenyl)(2-(N-ethyl-N-methylaminomethyl)-4-methylphenyl)bismuth, diphenyl(2-(methoxymethyl)phenyl)bismuth, di(2-tolyl)(2-(methoxymethyl)phenyl)bismuth, di(3-tolyl)(2-(methoxymethyl)phenyl)bismuth, di(4-tolyl)(2-(Methoxymethyl)phenyl)bismuth, di(2-ethylphenyl)(2-(methoxymethyl)phenyl)bismuth, di(3-ethylphenyl)(2-(methoxymethyl)phenyl)bismuth, di(4-ethylphenyl)(2-(methoxymethyl)phenyl)bismuth, diphenyl(2-(methoxymethyl)-4-methylphenyl)bismuth, di(2-tolyl)(2-(methoxymethyl)-4-methylphenyl)bismuth, di(3-tolyl)(2-(methoxymethyl)-4-methylphenyl)bismuth, di(4-tolyl)(2-(methoxymethyl)-4-methylphenyl)bismuth, di(2-ethylphenyl)(2-(methoxymethyl)-4-methylphenyl)bismuth, di(3-ethylphenyl)(2-(methoxymethyl)-4-methylphenyl)bismuth, di(4-ethylphenyl)(2-(methoxymethyl)-4-methylphenyl)bismuth, diphenyl(2-(ethoxymethyl)phenyl)bismuth, di(2-tolyl)(2-(ethoxymethyl)phenyl)bismuth, di(3-tolyl)(2-(ethoxymethyl)phenyl)bismuth, di(4-tolyl)(2-(ethoxymethyl)phenyl)bismuth, di(2-ethylphenyl)(2-(ethoxymethyl)phenyl)bismuth, di(3-ethylphenyl)(2-(ethoxymethyl)phenyl)bismuth, di(4-ethylphenyl)(2-(ethoxymethyl)phenyl)bismuth, diphenyl(2-(ethoxymethyl)-4-methylphenyl)bismuth, di(2-tolyl)(2-(ethoxymethyl)-4-methylphenyl)bismuth, di(3-tolyl)(2-(ethoxymethyl)-4-methylphenyl)bismuth, di(4-tolyl)(2-(ethoxymethyl)-4-methylphenyl)bismuth, di(2-ethylphenyl)(2-(ethoxymethyl)-4-methylphenyl)bismuth, di(3-ethylphenyl)(2-(ethoxymethyl)-4-methylphenyl)bismuth, and di(4-ethylphenyl)(2-(ethoxymethyl)-4-methylphenyl)bismuth.

(56) Although the disclosure herein is primarily directed to formation of BiTaO materials and films, the disclosure more broadly contemplates high dielectric constant, low current leakage oxides of two or more compatible metals. Examples of specific dielectric material compositions include, without limitation, BiTaO, LnTaO, LnTiO, (Ba,Sr) tetratitanates, and ZrTiSnO, wherein Ln is a lanthanide series element, e.g., lanthanum, cerium, neodymium, terbium, gadolinium, erbium, or ytterbium. In the aforementioned chemical formulae, atomic or molar subscripts have not been set out, in order to provide a generalized nomenclature, in recognition that the particular atomic proportions of the constituent elements may vary, within potential compositional forms of such metal oxides.

(57) The films of the present disclosure may be formed by atomic layer deposition of respective metals, utilizing any suitable oxic co-reactant (oxygen, ozone, etc.), and involving formation of an oxide film of a first one of the multiple metals, followed by reaction in a subsequent ALD step with the other dopant metal(s) species. The ALD process may be carried out at suitable process conditions appropriate to the metals involved. The respective metals of the high k, low current leakage oxide films may be derived from a variety of suitable organometallic precursors, including organo moieties that may comprise aliphatic and/or aromatic components, comprising hydrocarbonaceous moieties per se as well as hydrocarbonaceous moieties further comprising heteroatoms and heteroatomic organic moieties. Suitable precursors for specific metal components may be readily determined within the skill of the art, based on the disclosure herein, for a given high k, low current leakage oxide film.

(58) The substrate on which the high k, low current leakage film material is deposited by ALD may be of any suitable type, and may for example include titanium nitride, tantalum nitride, titanium aluminum nitride, iridium, ruthenium and ruthenium-based surfaces or device elements.

(59) By way of specific example, BiTaO films of high k, low current leakage character can be prepared using triphenylbismuth and tris(diethylamino)(tert-butylimido)tantalum, [TaN-t-butyl(NEt.sub.2).sub.3], denoted TBTDETa, in an ALD process conducted at 300 C. using ozone as a co-reactant, to produce a BiTaO film having a high dielectric constant and a leakage current of about 610.sup.7 A/cm.sup.2 at 0.6 nm equivalent oxide thickness (EOT), using iridium oxide (IrO.sub.2) top electrodes and titanium nitride (TiN) bottom electrodes. Dielectric films produced by such process can be further improved in performance by annealing at temperature below crystallization temperature (750 C.).

(60) The annealing can be carried out for appropriate time providing the desired ultimate characteristics, and a suitable annealing operation may for example have a duration of from a few milliseconds up to 1 hour or more. The ambient environment of the dielectric film in the annealing operation may be widely varied, and may for example include atmospheres ranging from inert gas environments (utilizing a nitrogen or argon ambient) to ambient atmospheres including some amount of oxygen and/or water. In some embodiments, it is preferred to anneal the non-crystalline high k, low current leakage dielectric film in an oxidizing ambient to stabilize its properties for subsequent processing.

(61) In various embodiments, the high k, low current leakage film material is formed as a non-crystalline ALD film having a dielectric constant greater than 50, which is processed by thermal treatment in an oxidizing environment prior to additional thermal treatments to form the final high k, low current leakage film. The oxidizing environment may include an ambient gas environment of from 0.1% to 100% of O.sub.2 or N.sub.2O, or from 0.1 to 30% O.sub.3, wherein such percentages are volume percentages of the total gas volume. The thermal treatment in an oxidizing environment can be carried out for any suitable period of time providing the desired film properties. In some embodiments, such thermal treatment is carried out for a period of from 1 to 1000 seconds. The temperature of the thermal treatment in an oxidizing environment can be conducted at any appropriate temperature, e.g., a temperature that is above the ALD deposition temperature and less than the crystallization temperature of the film material. In some embodiments, the temperature of the thermal treatment in an oxidizing environment is in a range of from 375 C. to 575 C. In other embodiments, the temperature of the thermal treatment in an oxidizing environment is in a range of from 440 C. to 520 C.

(62) Non-crystalline high k, low leakage films of the present disclosure exhibit high dielectric constant and low leakage properties in very thin films, e.g., a BiTaO film having an EOT of 0.3 or 0.4 nm. To ensure that such films retain a robust character under subsequent semiconductor processing conditions such as elevated temperature and a range of oxidizing to reducing conditions, it is desirable to stabilize the film with annealing in an oxidizing ambient before other thermal treatment.

(63) In the absence of such oxidizing stabilization, the film may be susceptible to loss of its low leakage character under exposure to nitrogen at temperatures higher than 400 C., such as rapid thermal nitridation (RTN) annealing at these temperatures, or in the formation of a top electrode of titanium nitride (TiN) involving use of ammonia (NH.sub.3) or other nitrogen-containing source gas. Oxidizing stabilization therefore is desirable to improve the robustness of the noncrystalline film with respect to subsequent processing.

(64) The high k, low current leakage films of the present disclosure may be usefully employed as a dielectric material in DRAM capacitor or other microelectronic device applications. The films of the disclosure may also be employed as gate dielectric material films in applications where hafnium oxide (HfO.sub.2) is conventionally employed, to afford lower EOT with low current leakage in such applications, utilizing gate metal materials such as titanium nitride or tantalum nitride.

(65) In various specific applications, the high dielectric constant, low leakage current non-crystalline metal oxide of the present disclosure is provided in a microelectronic device structure including a bottom electrode on which the high dielectric constant, low leakage current non-crystalline metal oxide is deposited, and a top electrode formed on the high dielectric constant, low leakage current non-crystalline metal oxide.

(66) In such microelectronic device structure, the top and bottom electrodes may be formed of any suitable material. In some embodiments, at least one of the top and bottom electrodes comprises a conductive metal nitride, e.g., titanium nitride, or tantalum nitride. In other applications and embodiments, at least one of the top and bottom electrodes may comprise a conductive metal or metal oxide, such as material selected from the group consisting of MoO.sub.2, Ni.sub.2O.sub.3, RuO.sub.2, IrO.sub.2, Al, Mo, Ru and Ir.

(67) The high dielectric constant, low leakage current non-crystalline metal oxide of the present disclosure may be utilized in a wide variety of microelectronic devices, including, without limitation, memory devices and logic devices.

(68) FIG. 1 is a schematic representation of a generalized high dielectric constant capacitor including a high k, low current leakage material of the present disclosure.

(69) As illustrated in FIG. 1, the high k capacitor comprises a metal oxide layer 2 of high dielectric constant, low current leakage character, e.g., a BiTaO film having a dielectric constant k of 60, and a current leakage of 510.sup.7 A/cm.sup.2 at 0.6 nm EOT. Two conductive barrier layers 3 and 4 are in direct contact with such metal oxide layer 2. Cu or Al electrode layers 6 and 7 overlay such conductive barrier layers 3 and 4 on their respective outer surfaces.

(70) Such capacitor may be incorporated in a large integrated circuit or other electronic device. The capacitor can for example be placed on a semiconductor substrate having vias and plugs therein (not shown).

(71) It is to be appreciated that the capacitor in FIG. 1 is illustratively depicted as a generalization of various capacitor structures, for ease of understanding. In commercial embodiments, the capacitor can be substantially planar with multiple layers of electrodes and dielectric materials. The capacitor can take the form of stack capacitors or trench capacitors with high aspect ratios, wherein the sides of the electrodes contribute substantially to the total surface area of the electrodes in contact with the high dielectric constant metal oxide. The capacitor can also take various other forms and conformations, as readily determinable by a person of ordinary skill in the art.

(72) For example, FIG. 2 is a schematic representation of a portion of an integrated circuit with an integrated capacitor according to one embodiment of the disclosure.

(73) The illustrated portion of integrated circuit 1 includes a first active device 10, such as a conventional metal-oxide-semiconductor field effect transistor (MOSFET), and a capacitor 5 employing a high k, low current leakage dielectric film layer of BiTaO formed on a substrate 15, such as a silicon substrate. A drain region of a second transistor 20 is also shown. The particular types of active devices employed, e.g., NMOS, PMOS or CMOS, are based on the desired operation of the integrated circuit and are not critical for achieving the benefits of the present disclosure. Other suitable active devices include, for example, bipolar junction transistors and GaAs MESFETs. The transistors 10 and 20 can be fabricated, for example, by conventional processing methods. In FIG. 2, the transistors 10 and 20 include field oxide regions 25 and 30 that are formed, for example, by SiO.sub.2 and operate as insulators between the transistor 10 and adjacent devices, such as the transistor 20. Source and drain regions 35 and 40 of the transistor 10 are formed by doping with n-type impurities, such as arsenic or phosphorous for NMOS. An optional layer of silicide 45 is deposited over the source and drain regions 35 and 40 to reduce the source and drain resistance, which enables greater current delivery by the transistor 10.

(74) A gate 50 of the transistor includes, for example, polysilicon 55 doped with an n-type impurity, such as by an implant or vapor doping. An optional layer of silicide 62 is also deposited over the gate polysilicon 55 to reduce the electrical resistance of the gate 50. An insulating layer 65 of, for example, P-glass which is an oxide doped with phosphorous is then deposited on the transistors 10 and 20 to provide protection to the transistors 10 and 20 and to facilitate electrical connection. Contact windows 66 are then etched in the insulating layer 65 to expose the device gate 50 and source and drain regions, such as the regions 35 and 40. Although only the drain regions of the transistors 10 and 20 are exposed in the cross-section of the integrated circuit illustrated in FIG. 2, it should be readily understood that the gate and source are exposed at other areas of the integrated circuit 1 that are outside the illustrated cross-section.

(75) At least one capacitor, such as the capacitor 5, is formed on the integrated circuit, such as on the insulating layer surface. The capacitor 5 includes a first electrode 70 formed on the insulating layer surface, a dielectric thin film region 75 on the first electrode 70, and a second electrode 80 formed on the dielectric film region 75 opposite the first electrode 70. The dielectric thin film region 75 comprises a high k, low current leakage metal oxide film in accordance with the present disclosure.

(76) It is possible for the first electrode 70 to have a two layer structure. Such a structure may comprise, for example, a layer of platinum formed over a layer of Ti-nitride. Platinum is a suitable electrode material, however, it adversely chemically reacts with silicon. As a consequence, a diffusion barrier may be employed as the second electrode layer which is in contact with the insulating layer surface to substantially prevent a chemical reaction between the platinum and the silicon of the substrate 15.

(77) Suitable thicknesses for each layer of the two-layer structure may be in a range of from 0.005 to 0.5 m. Thicknesses less than 0.005 m may be undesirable in some applications because of high electrical resistance while thicknesses greater than 0.5 m are generally disadvantageous because of high fabrication cost and poor adherence. The first electrode 70 may be larger than the second electrode 80 in order to provide electrical connection to the first electrode 70.

(78) After formation of the capacitor 5, an insulating material 85, such as, for example, SiO.sub.2 is deposited on edge regions 90, 91 and 92 of the capacitor 5 to prevent short circuits between the first and second capacitor electrodes 70 and 80 when the interconnection layer is formed. An interconnection layer 95 then is formed on the insulation layer and corresponding etched contact windows to electrically connect the devices 10 and 20 and the capacitor 5 in a desired manner. Suitable materials for the interconnection layer 95 include aluminum and copper. In the integrated circuit 1, the drain 40 of the transistor 10 is electrically connected to the first electrode 70 of the capacitor 80 and the capacitor's second electrode 80 is electrically connected to the source of the transistor 20. As an alternative to the structure shown in FIG. 2, other integrated circuitry device structures may be utilized, such as the DRAM device structures disclosed in U.S. Pat. No. 7,829,410 and U.S. Pat. No. 7,271,051.

(79) FIG. 3 is a graph of current density, J, in amperes per square centimeter (A/cm.sup.2) at voltage of +1 v, as a function of equivalent oxide thickness, in nanometers, for 3Ta/2La, 3Ta/1La, and BiTaO films, deposited by atomic layer deposition.

(80) The data shown in FIG. 3 demonstrate high dielectric constant for very thin films deposited by ALD.

(81) In the use of ALD for forming mixed metal oxide on substrates in accordance with the present disclosure, a variety of pulse sequences may be employed in the ALD process. In various embodiments, so-called burst pulsing may be employed in which the purge gas is utilized as a booster medium to deliver precursor in a burst.

(82) One such burst delivery cycle is shown in FIG. 4, which is a cycle sequence diagram for a precursor burst cycle with single boost of the precursor dose by the purge gas, as usefully employed in the method of the present disclosure for deposition of mixed metal oxide on a substrate.

(83) In this cycle, a constant flow of purge gas, e.g., argon, is split between ALD valves with orifices in the atomic layer delivery manifold to ensure uniform purging. An open stop valve in the flow circuitry accommodates a purging pressure that may for example be on the order of 200-300 millitorr. A boost pulse of the purge gas is flowed to the precursor ampoule, so that precursor is delivered to the ALD manifold in a burst, with oxygen being metered to the manifold by an orifice.

(84) In the cycle diagram, pressures are shown as a function of time, for the argon purge, the argon boost, the precursor flowed to the ALD manifold, the ozone oxidant, and the. ALD chamber pressure

(85) FIG. 5 is a cycle sequence diagram for a precursor pulse sequence including three boost doses of the precursor with purge gas, according to another embodiment of the disclosure. In this sequence, multiple doses of the precursor sequentially saturate the surface of the wafer. In the cycle diagram, pressures are shown as a function of time, for the argon purge, the argon boost, the precursor flowed to the ALD manifold, the ozone oxidant, and the. ALD chamber pressure.

(86) FIG. 6 is a graph of bismuth oxide deposition rate, in Angstroms per cycle, as a function of the number of doses, using triphenylbismuth as the bismuth precursor, in the deposition of a BiTaO material on a titanium nitride substrate. The graph shows the saturation for the bismuth precursor, at temperature of 250 C., 275 C., and 300 C. Using the triphenylbismuth precursor, a cycle sequence including 3Bi/O.sub.3 cycles: 1Ta/O.sub.3 cycle yielded a composition of approximately 30% bismuth in the BiTaO film. The dose of the bismuth cycle was increased to measure saturation. Changes in deposition per bismuth cycle changed less than 10% from 30 to 100 doses at temperature below 275 C.

(87) It has been found that the duration of the oxidant pulse in the ALD process according to the present disclosure can have significant effect on carbon impurity levels in the product metal oxide.

(88) This was demonstrated in an illustrative ALD process carried out to form BiTaO films using t-butyl-tridiethylaminotantalum (TBTDETa) as the tantalum precursor and triphenylbismuth as the bismuth precursor, in different cycle time sequences. A first run was carried out at 300 C. according to the following cycle: 0.2 seconds ozone for Ta.sub.2O.sub.5, 1.0 second ozone for Bi.sub.2O.sub.3, which resulted in 1% carbon in the BiTaO film. A second run was carried out at 300 C. according to the following cycle: 5 seconds ozone for Ta.sub.2O.sub.5, 5 second ozone for Bi.sub.2O.sub.3, which resulted in approximately 0.1% carbon in the BiTaO film. These results showed that increasing the ozone pulse time reduced the carbon impurity levels in the BiTaO film.

(89) Saturation effects were also studied for the bismuth precursor Bi(OCMe2CH2OMe).sub.3, also known as Bi(mmp).sub.3, resulting in the determination that such bismuth precursor saturates on a titanium nitride substrate at 250 C. with dosages up to approximately 30 doses per cycle, but very high doses (100 doses/cycle) using such precursor exhibit some instability. This was also true at temperature of 300, but the bismuth oxide deposition rate was significantly higher at such temperature. From SIMS data, it was found that BiTaO films produced using Bi(mmp).sub.3 as the bismuth precursor exhibited 0.4% carbon in films formed at 275 C., and 0.7% carbon in films formed at 300 C.

(90) Saturation effects were also studied for the bismuth precursor (CH.sub.3).sub.2Bi(C.sub.6H.sub.4)CH.sub.2N(CH.sub.3).sub.2,

(91) ##STR00013##

(92) FIG. 7 is a graph of bismuth oxide deposition rate, in Angstroms per cycle, as a function of the number of doses, using (CH.sub.3).sub.2Bi(C.sub.6H.sub.4)CH.sub.2N(CH.sub.3).sub.2 as the bismuth precursor, in the deposition of a BiTaO material on a titanium nitride substrate, showing saturation at 300 C., with a cycle including a one second ozone pulse, 3 Bi.sub.2O.sub.3 layers, providing a BiTaO film containing approximately 40 atomic percent bismuth. This precursor produced excellent saturation at 300 C.

(93) From SIMS data, it was found that BiTaO films produced at 300 C. using (CH.sub.3).sub.2Bi(C.sub.6H.sub.4)CH.sub.2N(CH.sub.3).sub.2 as the bismuth precursor, with a 5 second ozone pulse, contained 0.2% carbon, and with a one second ozone pulse, contained 0.5% carbon. Such precursor thus demonstrated capability for producing films with low carbon incorporation over a substantial range of oxidant pulse duration.

(94) The features and advantages of the disclosure are more fully illustrated by the following example.

Example I

(95) BiTaO was deposited on three coupons of TiN bottom electrode structure with 40 Bi cycles to 61 Ta cycles. A second run of 3 coupons was deposited with 44 Bi cycles to 67 Ta cycles. From each run, one coupon was given a top electrode of IrO.sub.2 sputtered through a shadow mask; a second coupon was first given a 1 minute anneal in N.sub.2 for rapid thermal nitridation (RTN) and then a top electrode; a third coupon was given a 1 minute anneal in O.sub.2 for rapid thermal oxidation (RTO), then a 1 minute anneal in N.sub.2, and then given a top electrode. Capacitance and leakage were measured on 30 capacitors of each coupon and representative capacitors were chosen. The data are summarized in Table 1 below. The capacitance of the as-deposited films was 0.41 or 0.42 nm and the leakage was 5-1010.sup.7 A/cm.sup.2 in both polarities. Coupons that received just the 400 C. RTN had high tan 6, so capacitance could not be determined accurately; the leakage was >1 A/cm.sup.2. Coupons that received a 450 C. RTO prior to the 400 C. RTN maintained capacitance and leakage similar to the as-deposited films.

(96) TABLE-US-00001 TABLE 1 as-deposited 400 C. RTN 450 C. RTO/400 C. RTN cycles EOT +J@+1 V J@1 V EOT +J@+1 V J@1 V EOT +J@+1 V J@1 V Bi:Ta (nm) (A/cm.sup.2) (A/cm.sup.2) (nm) (A/cm.sup.2) (A/cm.sup.2) (nm) (A/cm.sup.2) (A/cm.sup.2) 40:61 0.41 5.74E07 6.59E07 nd 2.18E+00 1.72E+00 0.44 1.17E06 3.84E07 44:67 0.42 1.11E06 6.57E07 nd 2.42E+00 1.92E+00 0.49 6.33E07 4.45E07 ndnot determined

Example II

(97) It was determined that BiTaO.sub.x films are susceptible to high leakage behavior after rapid thermal nitridation (RTN) at temperature of 400 C. for 60 seconds. In the oxide composition formulae used herein, x may have any suitable stoichiometric value. The suitability of BiTaO.sub.x films for formation of TiN top electrodes (TE) thereon using NH.sub.3 as a reactant gas, was therefore assessed using various processing approaches to enhance the robustness of the BiTaO.sub.x films to the TiN TE formation process. In this effort, resistance to RTN was used as a proxy for the TiN TE formation process, to determine the most effective film enhancement processing techniques.

(98) Three approaches were evaluated: (i) formation of a tantalum oxide (TaO.sub.x) cap over the BiTaO.sub.x film; (ii) formation of an aluminum oxide (AlO.sub.x) cap over the BiTaO.sub.x film; and (iii) rapid thermal oxidation (RTO) stabilization of the BiTaO.sub.x film.

(99) In this evaluation, the Bi:Ta cycle ratio was used to control film composition of the BiTaO.sub.x film. The number of ALD cycles was used to control thickness of the deposited BiTaO.sub.x film. 1 inch and 45 mm coupons were utilized, and BiTaO films were deposited on the film, with thickness of the film determined by x-ray fluorescence (XRF) technique. It should be noted that the XRF measures the Bi and Ta atoms/unit area and the reported thickness is calculated using the densities of fully dense crystalline Bi.sub.2O.sub.3 and Ta.sub.2O.sub.5 material. TEM analysis of these noncrystalline films indicates that the physical thickness of the films is 1.5 to 2 thickener than the values measured by XRF. One 45 mm coupon received an iridium oxide (IrO.sub.2) top electrode in the as-deposited condition. One coupon of each condition received a 400 C. RTN treatment prior to the top electrode (TE) being deposited. Additional coupons received rapid thermal oxidation (RTO) treatment prior to RTN and TE formation.

(100) Results of the evaluation are set out in Table 2 below.

(101) TABLE-US-00002 TABLE 2 BiTaO thickness coupon run # Bi:Ta (XRF) cycles 1 45 mm TaO cap P-165 5:4 20 0 1 2 P-170 5:4 30 0 1 2 P-166 5:4 40 0 1 2 P-167 5:4 57 0 1 2 P-168 5:4 57 P-169 5:4 40 10 1 4 P-171 5:4 40 20 1 4 P-172 5:4 40 40 1 4 P-173 1:1 P-174 1:1 30 0 1 2 P-175 1:1 40 0 1 2 P-179 1:1 50 0 1 2 P-180 1:1 40 10 1 4 P-181 1:1 40 20 1 4 P-182 1:1 40 40 1 4 P-183 4:5 30 0 1 2 P-186 4:5 40 0 1 2 P-184 4:5 50 0 1 2 P-185 4:5 70 0 1 2 P-187 4:5 40 10 1 4 P-188 4:5 40 20 1 4 P-189 4:5 40 40 1 4 AlO cap P-202 5:4 20 0 1 P-213 3:2 30 0 1 3 P-203 3:2 40 0 1 3 P-222 3:2 50 0 1 3 P-214 3:2 60 0 1 3 P-218 3:2 40 5 1 4 P-216 3:2 40 10 1 4 P-215 3:2 40 20 1 4 P-207 1:1 40 5 1 4 P-208 1:1 40 10 1 4 P-209 1:1 40 20 1 4 P-223 1:2 20 0 1 3 P-221 2:3 30 0 1 3 P-220 2:3 40 0 1 3 P-204 2:3 46 0 1 3 P-219 2:3 50 0 1 3 P-212 2:3 40 5 1 4 P-211 2:3 40 10 1 4 P-210 2:3 40 20 1 4

(102) FIG. 8 is a graph of atomic % bismuth as a function of film thickness, in Angstroms, for different ratios of bismuth:tantalum, namely, 3Bi:2Ta, 5Bi:4Ta, 1Bi:1Ta, 4Bi:5Ta, 2Bi:3Ta, and 1Bi:2Ta, for films deposited in this evaluation, as baseline process response data.

(103) It was determined that a 3:2 ratio of Bi:Ta did not substantially increase bismuth content at thicknesses below 50 , and that a 2:3 ratio was successful at thicknesses below 50 .

(104) Baseline electrical response data are set out in FIG. 9, which is a graph of current density, J, in units of amperes per square centimeter (A/cm.sup.2), as measured at +1 volt, as a function of equivalent oxide thickness (EOT), in nanometers (nm), for films of different ratios of bismuth:tantalum, namely, 3Bi:2Ta, 5Bi:4Ta, 1Bi:1Ta, 4Bi:5Ta, 2Bi:3Ta, and 1Bi:2Ta.

(105) FIG. 10 is a graph of current density, J, in units of amperes per square centimeter (A/cm.sup.2), as measured at +1 volt, as a function of equivalent oxide thickness (EOT), in nanometers (nm), for films of different ratios of bismuth:tantalum capped with a tantalum cap (Tacap) or an aluminum cap (Alcap), namely, 3Bi:2Ta+Alcap, 5Bi:4Ta+Tacap, 1Bi:1Ta+Tacap, 1Bi:1Ta+Alcap, 4Bi:5Ta+Tacap, and 2Bi:3Ta+Alcap. The data do not evidence a clear benefit for relatively higher or relatively lower Bi:Ta ratios, but an increase in thickness of either tantalum cap or aluminum cap was found to decrease variability of current density.

(106) FIG. 11 is a graph of current density, J, in units of amperes per square centimeter (A/cm.sup.2), as measured at +1 volt, as a function of film thickness, in Angstroms, showing the effect of film thickness and % Bi in the deposited film, for films of different ratios of bismuth:tantalum, namely, 3Bi:2Ta, 5Bi:4Ta, 1Bi:1Ta, 4Bi:5Ta, 2Bi:3Ta, and 1Bi:2Ta.

(107) FIG. 12 is a graph of minimum dielectric constant, k min, as a function of film thickness, in Angstroms, as determined by XRF technique, showing the effect of film thickness and % Bi in the deposited film, for films of different ratios of bismuth:tantalum, namely, 3Bi:2Ta, 5Bi:4Ta, 1Bi:1Ta, 4Bi:5Ta, 2Bi:3Ta, and 1Bi:2Ta.

(108) The results show that leakage values are consistent down to approximately 40 XRF film thickness, and that dielectric constant decreases with thickness for most films.

(109) Table 3 below shows data for BiTaO films capped using (tert-butylimido)tris(diethylamido) tantalum (TBTDET) and ozone (O.sub.3) to provide TaO capping, with post-deposition annealing of the capped film in nitrogen at 400 C. This treatment resulted in leaky BiTaO films. It was determined that 450 C. RTO was insufficient to stabilize TaOx-capped films. Table 4 below shows data for BiTaO films capped using trimethylaluminum (TMA) and ozone (O.sub.3) to provide aluminum oxide (Al.sub.2O.sub.3) capping, with post-deposition annealing of the deposited film in nitrogen at 400 C. This treatment resulted in leaky BiTaO films. Table 5 below shows data for BiTaO films, with post-deposition RTO annealing of the deposited film at 450 C., followed by RTN annealing in nitrogen at 400 C.

(110) TABLE-US-00003 TABLE 3 BiTaO thickness as-dep 400 C. PDA run # Bi:Ta (XRF) yield EOT +J J kmin yield EOT +J J TaO cap cycles P-165 5:4 20 0 13% 0.14 1.14E02 3.93E03 57 0% 0.27 1.28E+00 2.23E+00 P-170 5:4 30 0 47% 0.45 1.76E03 1.41E03 30 0% 0.24 1.03E+00 1.15E+00 P-166 5:4 40 0 93% 0.44 4.73E07 4.24E07 40 57% 0.56 1.25E02 5.11E03 P-167 5:4 57 0 60% 0.45 6.37E07 4.95E07 53 23% 0.80 2.45E02 1.34E02 P-168 5:4 57 100% 0.49 2.20E05 1.03E05 48 40% 0.59 1.62E02 8.65E03 P-169 5:4 40 10 100% 0.63 1.92E07 2.33E07 34 0% 0.40 5.68E01 4.69E01 P-171 5:4 40 20 100% 0.48 2.61E07 2.93E07 46 0% 0.33 2.10E+00 1.58E+00 P-172 5:4 40 40 100% 0.64 3.17E07 2.67E07 43 0% 0.33 1.06E+00 8.74E01 P-173 1:1 70% 0.46 8.89E05 3.46E05 16 0% 0.58 2.94E01 5.66E01 P-174 1:1 30 0 97% 0.48 3.40E06 2.49E06 27 0% 0.45 6.67E01 2.25E+00 P-175 1:1 40 0 97% 0.52 4.90E05 3.10E05 31 27% 0.58 3.67E02 1.85E02 P-179 1:1 50 0 93% 0.48 1.73E06 7.25E07 42 0% 0.39 4.85E01 3.75E01 P-180 1:1 40 10 100% 0.38 7.35E07 9.72E07 48 0% 0.49 6.31E01 5.62E01 P-181 1:1 40 20 80% 0.55 2.39E07 2.13E07 40 0% 0.33 2.36E+00 2.11E+00 P-182 1:1 40 40 93% 0.74 2.32E07 2.37E07 32 0% 0.31 8.85E01 7.26E01 P-183 4:5 30 0 40% 0.21 8.00E03 3.71E03 51 0% 0.39 5.21E+00 6.81E+00 P-186 4:5 40 0 90% 0.51 5.70E07 4.85E07 31 0% 0.38 2.17E+00 1.65E+00 P-184 4:5 50 0 97% 0.43 5.23E07 5.97E07 45 0% 0.44 6.74E01 4.96E01 P-185 4:5 70 0 100% 0.52 4.08E07 5.18E07 55 0% 0.41 6.54E01 5.72E01 P-187 4:5 40 10 100% 0.49 4.01E07 4.78E07 35 10% 0.41 1.85E01 1.14E01 P-188 4:5 40 20 80% 0.31 3.28E07 3.93E07 70 0% 0.43 1.85E+00 1.48E+00 P-189 4:5 40 40 100% 0.54 3.42E07 4.81E07 46 0% 0.39 8.29E01 7.28E01 450 C. RTO/400 C. RTN run # yield 4th best EOT +J J kmin P-165 P-170 P-166 P-167 P-168 P-169 P-171 P-172 10% 26 0.66 8.78E02 7.82E02 P-173 P-174 P-175 P-179 P-180 P-181 P-182 43% 5 0.62 1.20E01 6.68E02 P-183 P-186 P-184 P-185 P-187 P-188 P-189 0% 23 0.66 9.86E02 8.98E02

(111) TABLE-US-00004 TABLE 4 BiTaO thick- ness as-dep 400 C. PDA run # Bi:Ta (XRF) yield EOT +J J kmin yield EOT +J J kmin TaO cap cycles AlO cap cycles P-202 5:4 20 0 47% 0.22 1.59E05 5.03E06 46 0% 0.27 4.20E01 1.75E+00 35 P-213 3:2 30 0 50% 0.35 3.90E04 3.16E04 38 0% 0.46 2.84E+00 2.34E+00 28 P-203 3:2 40 0 100% 0.39 6.10E07 6.78E07 43 53% 0.47 7.62E02 2.60E02 35 P-222 3:2 50 0 97% 0.48 2.05E07 4.06E07 41 0% 0.43 1.89E+00 1.28E+00 46 P-214 3:2 60 0 90% 0.61 2.97E07 2.73E07 39 47% 0.58 4.27E02 2.07E02 40 P-218 3:2 40 5 93% 0.48 4.54E06 3.55E06 35 0% 0.38 4.13E+00 3.30E+00 43 P-216 3:2 40 10 100% 0.63 1.40E07 1.64E07 27 0% 0.65 4.72E+00 4.09E+00 25 P-215 3:2 40 20 100% 0.87 9.36E06 8.85E06 21 0% 0.61 2.73E01 3.75E01 27 P-207 1:1 40 5 100% 0.57 1.09E06 5.81E07 27 0% 0.29 5.47E+00 4.81E+00 52 P-208 1:1 40 10 100% 0.70 2.20E07 3.20E07 25 0% 0.32 4.67E+00 4.42E+00 50 P-209 1:1 40 20 100% 0.94 1.17E07 1.76E07 17 0% 0.39 2.42E01 3.07E01 42 P-223 1:2 20 0 93% 0.32 1.90E04 1.08E04 31 0% 0.46 5.77E+00 5.77E+00 18 P-221 2:3 30 0 63% 0.30 2.56E04 2.08E04 39 0% 0.53 3.08E+00 4.62E+00 22 P-220 2:3 40 0 60% 0.26 3.81E05 3.60E05 63 0% 0.53 2.11E+00 2.15E+00 29 P-204 2:3 46 0 100% 0.41 5.74E07 6.59E07 44 0% 0.36 2.18E+00 1.72E+00 52 P-219 2:3 50 0 100% 0.42 1.11E06 6.57E07 50 0% 0.31 2.42E+00 1.92E+00 71 P-212 2:3 40 5 100% 0.42 9.02E06 5.82E06 40 0% 0.39 4.54E+00 4.14E+00 41 P-211 2:3 40 10 100% 0.51 2.53E07 1.82E07 31 0% 0.45 5.80E+00 5.49E+00 39 P-210 2:3 40 20 90% 0.64 1.50E07 1.55E07 26 63% 0.64 8.53E02 9.45E02 23

(112) TABLE-US-00005 TABLE 5 BiTaO thick- ness as-dep 450 C. RTO/RTN run # Bi:Ta (XRF) yield EOT +J J RTN yield EOT +J J AlO cap cycles P-202 5:4 20 0 47% 0.22 1.59E05 5.03E06 400 10% 0.28 7.04E04 5.71E06 P-213 3:2 30 0 50% 0.35 3.90E04 3.16E04 400 67% 0.54 5.00E04 2.81E04 P-203 3:2 40 0 100% 0.39 6.10E07 6.78E07 400 90% 1.07 1.45E05 2.88E07 P-222 3:2 50 0 97% 0.48 2.05E07 4.06E07 400 90% 1.27 1.39E06 3.35E07 P-218 3:2 40 5 93% 0.48 4.54E06 3.55E06 400 93% 0.59 1.26E02 2.71E03 P-208 1:1 40 10 100% 0.70 2.20E07 3.20E07 400 0% 0.78 4.12E+00 4.17E+00 P-223 1:2 20 0 93% 0.32 1.90E04 1.08E04 400 33% 0.30 3.22E03 1.49E03 P-221 2:3 30 0 63% 0.30 2.56E04 2.08E04 400 50% 0.34 3.76E04 1.61E04 P-220 2:3 40 0 60% 0.26 3.81E05 3.60E05 400 100% 0.74 1.06E05 4.29E07 P-204 2:3 46 0 100% 0.41 5.74E07 6.59E07 400 100% 0.44 1.17E06 3.84E07 P-219 2:3 50 0 100% 0.42 1.11E06 6.57E07 400 97% 0.49 6.33E07 4.45E07 P-210 2:3 40 20 90% 0.64 1.50E07 1.55E07 400 60% 0.81 2.64E01 2.90E01

(113) The resulting annealed uncapped BiTaO films maintained low 1V leakage characteristics, and low % Bi films also maintained low +1V leakage characteristics. AlO.sub.x-capped films were not stabilized with 450 C./60 s RTO.

(114) As-deposited BiTaO films were compared with BiTaO films thermally treated by 450 C. RTO followed by 400 C. RTN, with the data shown in FIG. 13 for current density, J, measured at +1V, in Angstroms per square centimeter (A/cm.sup.2), as a function of equivalent oxide thickness, in nanometers (nm), for the following BiTaO films: (i) >30% Bi as-deposited, (ii) >30% Bi+450 RTO/400 RTN, (iii) 25-30% Bi as-deposited, (iv) 25-30% Bi+450 RTO/400 RTN, (v) 20-25% Bi as-deposited, and (vi) 20-25% Bi+450 RTO/400 RTN. It is evident that varying % Bi can be used to improve the stability of the film to subsequent thermal processing.

(115) Table 6 shows data for various RTO/RTN annealing treatments on AlO.sub.x-capped BiTaO.sub.x films.

(116) TABLE-US-00006 TABLE 6 BiTaO thick- ness as-dep 450 C. RTO/RTN run # Bi:Ta (XRF) yield EOT +J J RTN yield EOT +J J AlO cap cycles P-202 5:4 20 0 47% 0.22 1.59E05 5.03E06 400 10% 0.28 7.04E04 5.71E06 P-213 3:2 30 0 50% 0.35 3.90E04 3.16E04 400 67% 0.54 5.00E04 2.81E04 P-203 3:2 40 0 100% 0.39 6.10E07 6.78E07 400 90% 1.07 1.46E05 2.88E07 P-222 3:2 50 0 97% 0.48 2.05E07 4.06E07 400 90% 1.27 1.39E06 3.35E07 P-218 3:2 40 5 93% 0.48 4.54E06 3.55E06 400 93% 0.59 1.26E02 2.71E03 P-216 3:2 40 10 100% 0.63 1.40E07 1.64E07 450 0% 1.03 1.83E+00 3.15E+00 P-215 3:2 40 20 100% 0.87 9.36E06 8.85E06 475 0% 1.05 3.40E+00 7.31E+00 P-207 1:1 40 5 100% 0.57 1.09E06 5.81E07 475 0% 0.35 9.46E+00 9.46E+00 P-208 1:1 40 10 100% 0.70 2.20E07 3.20E07 400 0% 0.78 4.12E+00 4.17E+00 P-209 1:1 40 20 100% 0.94 1.17E07 1.76E07 450 0% 0.51 1.77E+00 3.72E+00 P-223 1:2 20 0 93% 0.32 1.90E04 1.08E04 400 33% 0.30 3.22E03 1.49E03 P-221 2:3 30 0 63% 0.30 2.56E04 2.08E04 400 50% 0.34 3.76E04 1.61E04 P-220 2:3 40 0 60% 0.26 3.81E05 3.60E05 400 100% 0.74 1.06E05 4.29E07 P-204 2:3 46 0 100% 0.41 5.74E07 6.59E07 400 100% 0.44 1.17E06 3.84E07 P-219 2:3 50 0 100% 0.42 1.11E06 6.57E07 400 97% 0.49 6.33E07 4.45E07 P-212 2:3 40 5 100% 0.42 9.02E06 5.82E06 450 0% 0.50 9.04E01 1.18E+00 P-211 2:3 40 10 100% 0.51 2.53E07 1.82E07 475 0% 0.95 1.01E+01 1.01E+01 P-210 2:3 40 20 90% 0.64 1.50E07 1.55E07 400 60% 0.81 2.64E01 2.90E01 475 C. RTO/RTN run # RTN yield EOT +J J P-202 P-213 P-203 P-222 P-218 400 97% 0.53 1.27E05 3.68E06 P-216 450 0% 0.46 1.96E+00 1.86E+00 P-215 475 0% 1.06 4.37E+00 8.57E+00 P-207 475 0% 0.36 1.22E+00 1.37E+00 P-208 400 0% 0.74 3.09E+00 3.25E+00 P-209 450 0% 1.20 2.29E+00 9.56E+00 P-223 P-221 P-220 P-204 P-219 P-212 450 40% 0.32 8.45E02 8.42E02 P-211 475 0% 0.92 7.52E+00 7.52E+00 P-210 400 33% 0.86 2.16E01 2.35E01

(117) The data show data show that 450 C. RTO does not protect the capped films from leakage degradation, and that 475 C. RTO allowed thin cap films to accommodate 400 C. RTN, evidencing that capped films require most aggressive oxidation thermal treatment conditions to retain low leakage character. The RTO in some embodiments may be carried out in a temperature range of from 400 C. to 600 C., in other embodiments in a temperature range of from 450 C. to 575 C., and in still other embodiments in a temperature range of from 475 C. to 575 C.

(118) The foregoing results show that RTO can be used to effectively stabilize BiTaO.sub.x films against degradation that would otherwise occur as a consequence of RTN processing. RTO conditions necessary for stabilization of BiTaO.sub.x films include higher temperature and/or longer RTO processing time than the conditions required for uncapped BiTaO.sub.x films. Additional stability can be imparted to BiTaO.sub.x films with minimum thermal exposure by applying RTO, then capping, then depositing a top electrode using less-oxidizing (or reducing) conditions.

(119) Another aspect of the disclosure relates to compositional modulation of BiTaO films to enhance their stability, and specifically to enhancing BiTaO film robustness in respect of film dielectric constant and leakage current when such film is thermally treated for top electrode deposition in microelectronic device fabrication applications.

(120) The disclosure in such aspect provides improved BiTaO films that do not have a uniform Bi:Ta ratio. Instead, the Bi:Ta ratio is modulated through the thickness of the film. The thermal performance of such films is related to the modulation depth and modulation periods.

(121) Set out in Table 7 below is a compilation of information for various BiTaO films, including ultra-low Bi % films (films in this category having a bismuth concentration in the film of from 8-10%), high Bi % films modulated according to modulated Scheme 1 (films in this category having a bismuth concentration in the film of from 18-30%), and high Bi % films modulated according to modulated Scheme 2 (films in this category having a bismuth concentration in the film of from 20-28%). The wafers are specified by identification numbers in such table, together with an identification of the XRF thickness of the film, the Bi % of the film, and the treatment of the film (As Dep=as deposited; RTN 450 C.=rapid thermal nitridation at 450 C.; and RTO 450 C.=rapid thermal oxidation at 450 C.).

(122) TABLE-US-00007 TABLE 7 XRF BiTaO films Wafer No. Thickness Bi % Treatment Ultra-low BiTaO-323R 59.14 8.3% As Dep Bi % films BiTaO-323L1 62.83 8.2% RTN 450 C. (<10% Bi) BiTaO-323L2 48.25 9.2% RTO 450 C. High Bi % BiTaO-325R 60.25 28% As Dep films BiTaO-325L1 56.2 28% RTN 450 C. (modulated BiTaO-325L2 58.7 19.4% RTO 450 C. Scheme 1) High Bi % BiTaO-326R 67.03 22.1% As Dep films BiTaO-326L1 65.2 22.6% RTN 450 C. (modulated BiTaO-326L2 54.88 26.6% RTO 450 C. Scheme 2)

(123) In forming these films, the bismuth precursor used was BiMe.sub.2(Me.sub.2NCH.sub.2Ph),

(124) ##STR00014##
and the tantalum precursor was tris(diethylamino)(tert-butylimido)tantalum, (TBTDETa). In the samples that were treated by rapid thermal processing, either rapid thermal nitridation or rapid thermal oxidation, the rapid thermal processing techniques were carried out at temperature of 450 C. The substrate was titanium nitride (TiN).

(125) The Modulated Scheme 1 deposition process involved initial deposition of the mixed metals at a ratio of Bi:Ta of 3:1 to achieve a film thickness of 10 , intermediate deposition of mixed metals at a ratio of Bi:Ta of 1:1 to achieve additional film thickness of 20 , and final deposition of mixed metals at a ratio of Bi:Ta of 3:1 to achieve additional film thickness of 20 .

(126) The Modulated Scheme 2 deposition process involved initial deposition of the mixed metals at a ratio of Bi:Ta of 1:1 to achieve a film thickness of 10 , followed by deposition of mixed metals at a ratio of Bi:Ta of 3:1 to achieve additional film thickness of 10 , followed by deposition of mixed metals at a ratio of Bi:Ta of 1:1 to achieve additional film thickness of 10 , followed by deposition of mixed metals at a ratio of Bi:Ta of 3:1 to achieve additional film thickness of 20 , and final deposition of mixed metals at a ratio of Bi:Ta of 1:2 to achieve additional film thickness of 10 .

(127) FIGS. 14-17 are corresponding graphs of current density, J, in amperes per square centimeter (A/cm.sup.2) at voltage of +1 v, as a function of equivalent oxide thickness (EOT), in nanometers, for BiTaO films deposited by atomic layer deposition.

(128) FIG. 14 shows the plotted film values for BiTaO films containing 8% Bi, including 8% Bi-containing BiTaO films as deposited (.diamond-solid.), 8% Bi-containing BiTaO films processed by rapid thermal oxidation at 450 C. (.square-solid.), and 8% Bi-containing BiTaO films processed by rapid thermal nitridation at 450 C. (.box-tangle-solidup.). These low-bismuth films were uniform in composition and stable in character as regards their current density characteristics.

(129) FIG. 15 shows the data for uniform composition films at higher bismuth content of 27% Bi and thickness of 3.7 nm, including 27% Bi-containing BiTaO films as deposited (.diamond-solid.), and 27% Bi-containing BiTaO films processed by rapid thermal oxidation at 450 C. (.square-solid.). These high-Bi uniform composition films were of reduced stability character, as compared to the films of FIG. 14.

(130) FIG. 16 shows the data for compositionally modulated films in which deposition was carried out according to Modulated Scheme 1, including films as deposited (.diamond-solid.), as processed by rapid thermal oxidation at 450 C. (.square-solid.), and as processed by rapid thermal nitridation at 450 C. (.box-tangle-solidup.).

(131) FIG. 17 shows the data for compositionally modulated films in which deposition was carried out according to Modulated Scheme 2, including films as deposited (.diamond-solid.), as processed by rapid thermal oxidation at 450 C. (.square-solid.), and as processed by rapid thermal nitridation at 450 C. (.box-tangle-solidup.).

(132) The foregoing data for current density as a function of ETO showed that the compositionally modulated films of FIGS. 16-17 were better than the uniform composition 27% Bi film of FIG. 15, with respect to stability characteristics. The data therefore evidence that stability of the mixed metal oxide film when homogeneous in composition is satisfactory at low Bi level (FIG. 14) but is deteriorated at high Bi level, whereas compositional modulation of the mixed oxide film enables high Bi levels to be achieved without such loss of stability.

(133) Accordingly, the disclosure contemplates high dielectric constant (k40), low leakage current (10.sup.6 A/cm.sup.2 at 0.6 nm or lower equivalent oxide thickness) non-crystalline metal oxide, including two or more compatible metals selected from the group consisting of bismuth, tantalum, niobium, barium, strontium, calcium, magnesium, titanium, zirconium, hafnium, tin, and lanthanide series metals, in which the metal oxide comprises different relative proportions of the metals therein.

(134) The metal oxide may be in the form of a thin film comprising at least two thickness portions of differing relative proportions of the metals.

(135) The disclosure correspondingly contemplates a process of forming a high dielectric constant, low leakage current non-crystalline metal oxide, including two or more compatible metals selected from the group consisting of bismuth, tantalum, niobium, barium, strontium, calcium, magnesium, titanium, zirconium, hafnium, tin, and lanthanide series metals, comprising vapor depositing the metals on a substrate at at least two differing ratios of the metals during said depositing, so that the metal oxide comprises different relative proportions of the metals therein, for enhancement of stability of such metal oxide. The metals, for example, may be deposited to form a thin film comprising at least two thickness portions of differing relative proportions of the metals.

(136) The disclosure correspondingly contemplates BiTaO and methods of forming same, involving the aforementioned compositional modulation to provide such mixed metal oxide with differing metals ratios therein, for enhancement of stability of such oxide.

(137) While the disclosure has been set out herein in reference to specific aspects, features and illustrative embodiments, it will be appreciated that the utility of the disclosure is not thus limited, but rather extends to and encompasses numerous other variations, modifications and alternative embodiments, as will suggest themselves to those of ordinary skill in the field of the present disclosure, based on the description herein. Correspondingly, the invention as hereinafter claimed is intended to be broadly construed and interpreted, as including all such variations, modifications and alternative embodiments, within its spirit and scope.