MICROBEADS FOR EMBOLIZATION AND COMPOSITION FOR TREATING PROLIFERATIVE DISEASES

Abstract

The present disclosure provides a biocompatible polymer, and the polymer includes the embolic microbead including an iron adsorption block capable of adsorbing an iron component. The embolic microbead according to the an exemplary embodiment of the present disclosure adsorbs iron and thus effectively blocks an iron component delivered to cancer cells, and when used in embolization, it has an improved effect in treating cancers, such as liver cancer.

Claims

1. An embolic microbead, comprising a biocompatible polymer, wherein the biocompatible polymer comprises a gelatin and an iron adsorption block cross-linked.

2. The embolic microbead of claim 1, wherein the iron adsorption block includes a fucoidan and/or a polyphenol.

3. The embolic microbead of claim 2, wherein the polyphenol is a biodegradable anionic polyphenol, and wherein the polyphenol includes at least one selected from tannin, gallic acid, tannic acid, catechin, epicatechin, epigallocatechin gallate, quercetin, resveratrol, isoflavone, flavonoids, and polyphenols derived from seaweeds.

4. The embolic microbead of claim 1, wherein the gelatin is an aminated gelatin, and wherein the embolic microbead comprises cross-linking of a cationic aminated gelatin and an anionic fucoidan.

5. The embolic microbead of claim 1, wherein a weight ratio of the gelatin:the iron adsorption block is 4:1 to 10:1.

6. The embolic microbead of claim 1, wherein the gelatin comprises a first gelatin having a first average molecular weight; and a second gelatin having a second average molecular weight smaller than the first average molecular weight.

7. The embolic microbead of claim 1, wherein an iron adsorption rate after 24 hours (IAd24) based on 100 mg of the embolic microbead, represented by the following Formula 1, is 5%/100 mg or more: $\begin{array}{cc}\mathrm{IAd}24=\frac{\left(\mathrm{IC}0-\mathrm{IC}24\right)}{\mathrm{IC}0}\times 100;& \left[\mathrm{Formula}1\right]\end{array}$ wherein the IC0 is an initial molar concentration of a FeCl.sub.3 aqueous solution, and wherein the IC24 is a molar concentration of an iron ion of the FeCl.sub.3 aqueous solution left for 24 hours after adding the embolic microbead to the FeCl.sub.3 aqueous solution.

8. The embolic microbead of claim 1, wherein an iron adsorption rate after 48 hours (IAd48) based on 100 mg of the embolic microbead, represented by the following Formula 2, is 5%/100 mg or more: $\begin{array}{cc}\mathrm{IAd}48=\frac{\left(\mathrm{IC}0-\mathrm{IC}48\right)}{\mathrm{IC}0}\times 100;& \left[\mathrm{Formula}2\right]\end{array}$ wherein the IC0 is an initial molar concentration of a FeCl.sub.3 aqueous solution, and wherein the IC48 is a molar concentration of an iron ion of the FeCl.sub.3 aqueous solution left for 48 hours after adding the embolic microbead to the FeCl.sub.3 aqueous solution.

9. An embolic microbead, comprising a biocompatible polymer, wherein the biocompatible polymer comprises a gelatin and an iron adsorption block cross-linked, and wherein the embolic microbead is combined with an anticancer drug.

10. The embolic microbead of claim 9, wherein the anticancer drug is selected from doxorubicin, irinotecan, gemcitabine, oxaliplatin and docetaxel.

11. The embolic microbead of claim 9, wherein a combining rate with the anticancer drug after 1 hour (AAd) based on 100 mg of the embolic microbead, represented by the following Formula 6, is 10%/100 mg or more: $\begin{array}{cc}\mathrm{AAd}=\frac{\left(AC0-AC1\right)}{AC0}\times 100;& \left[\mathrm{Formula}6\right]\end{array}$ wherein the AC0 is an initial mg/ concentration of an anticancer drug solution, and wherein the AC1 is a mg/ concentration of the anticancer drug of the anticancer drug solution left for 1 hour after adding the embolic microbead to the anticancer drug solution.

12. A composition for treating proliferative diseases, comprising an embolic microbead, wherein the embolic microbead comprises a gelatin and an iron adsorption block crosslinked, and wherein the embolic microbead is combined with an iron component and/or an anticancer drug.

13. The composition for treating proliferative diseases of claim 12, wherein the proliferative diseases include at least one selected from neovascularization, tumor, cancer, bone diseases, fibroplasia disorders, statomegaly, renal cyst, and atherosclerosis.

14. The composition for treating proliferative diseases of claim 13, wherein the cancer includes at least one selected from solid tumor, hematologic malignancy, colorectal cancer, uterine cancer, uterine myoma, meningioma, lung cancer, small cell lung cancer, non-small cell lung cancer, gastrointestinal cancer, bowel cancer, breast cancer, ovarian cancer, prostate cancer, testicular cancer, liver cancer, renal cancer, bladder cancer, pancreatic cancer, sarcoma, osteosarcoma, kaposi's sarcoma and melanoma.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0036] FIG. 1 is a diagram showing a process of preparing an embolic microbead according to an example.

[0037] FIG. 2 shows a calibration curve for the absorbance of light of a wavelength of 550 nm, which is the basis of calculation of a doxorubicin conjugation rate according to an example, against the concentration of an embolic microbead according to the present disclosure.

BEST MODE FOR CARRYING OUT THE INVENTION

[0038] Hereinafter, the present disclosure will be described in more detail with reference to exemplary embodiments. The following exemplary embodiments are provided only for describing the present disclosure, and it is obvious to a person with ordinary skill in the art that the scope of the present disclosure is not limited to these exemplary embodiments.

[0039] An embolic microbead according to an exemplary embodiment of the present disclosure may include a biocompatible polymer. An embolic microbead according to an exemplary embodiment of the present disclosure may be composed of the biocompatible polymer.

[0040] The embolic microbead according to an exemplary embodiment of the present disclosure may include the biocompatible polymer in the amount of about 80 parts or more by weight based on 100 parts by weight of the microbead. The embolic microbead according to an exemplary embodiment of the present disclosure may include the biocompatible polymer in the amount of about 90 parts or more by weight based on 100 parts by weight of the microbead. The embolic microbead according to an exemplary embodiment of the present disclosure may include the biocompatible polymer in the amount of about 95 parts or more by weight based on 100 parts by weight of the microbead. The embolic microbead according to an exemplary embodiment of the present disclosure may include the biocompatible polymer in the amount of about 97 parts or more by weight based on 100 parts by weight of the microbead. The embolic microbead according to an exemplary embodiment of the present disclosure may include the biocompatible polymer in the amount of about 99 parts or more by weight based on 100 parts by weight of the microbead.

[0041] The biocompatible polymer refers to a polymer that does not cause problems when injected into a human body or the like. The biocompatible polymer may be a cross-linked biodegradable polymer that has excellent mechanical properties but can be degraded in vivo after a predetermined period of time. The biocompatible polymer may be a cross-linked biodegradable polymer. The biocompatible polymer may be an enzymatically hydrolyzable biodegradable polymer or a chemically hydrolyzable biodegradable polymer. The biocompatible polymer may be an enzymatically hydrolyzable biodegradable polymer that is easily degraded by an enzyme present in the internal metabolic system.

[0042] Also, the biocompatible polymer does not cause inflammation in vivo or cerebral thrombosis by spreading to other organs through blood vessels due to its biodegradability.

[0043] The biocompatible polymer may include a gelatin and an iron adsorption block (iron adsorption polymer) cross-linked. The iron adsorption block (iron adsorption polymer) may function to adsorb iron inside the biocompatible polymer.

[0044] The iron adsorption block may include a fucoidan and/or a polyphenol. Further, the iron adsorption block may include the fucoidan, or the fucoidan and polyphenol.

[0045] The iron (Fe) adsorption block may have a high concentration of hydroxyl group (—OH). Therefore, the iron adsorption block can adsorb a large amount of iron ions.

[0046] The polyphenol is an aromatic alcohol compound extracted from plants. The polyphenol is a functional group having one molecule with two or more phenol groups, and may have several hydroxyl groups. The polyphenol may be a biodegradable anionic polyphenol, and the polyphenol may include at least one selected from tannin, gallic acid, tannic acid, catechin, epicatechin, epigallocatechin gallate, quercetin, resveratrol, isoflavone, flavonoids, and polyphenols derived from seaweeds.

[0047] Also, the polyphenol may include catechins extracted from green tea, resveratrols extracted from wine or quercetins extracted from apples or onions. Further, the polyphenol may include flavonoids extracted from fruits or isoflavones extracted from soybeans.

[0048] The polyphenol may include epigallocatechin gallate (EGCG).

[0049] The embolic microbead according to an exemplary embodiment of the present disclosure includes the iron adsorption block and thus can effectively adsorb iron ions.

[0050] The gelatin may be aminated gelatin, and the embolic microbead may include cross-linking of a cationic aminated gelatin and an anionic fucoidan. The gelatin may include an amine group and a carboxylic acid group. Here, the aminated gelatin may have a relatively high concentration of the amine group. More specifically, the aminated gelatin may have an improved concentration of an amine group by reacting normally available gelatin with amine. Examples of the amine may include ethylenediamine (1,2-diaminoethane), 1,1-dimethylethylenediamine, 1,2-dimethylethylenediamine, ethambutol, tetrakis(dimethylamino)ethylene or tetramethylethylenediamine (TMEDA).

[0051] A weight ratio of the gelatin:the iron adsorption block may be about 4:1 to about 10:1, but may not be limited thereto. The weight ratio of the gelatin:the iron adsorption block may be about 4:1 to about 10:1, about 4:1 to about 9:1, about 4:1 to about 8:1, about 4:1 to about 7:1, about 4:1 to about 6:1, about 4:1 to about 5:1, about 5:1 to about 10:1, about 5:1 to about 9:1, about 5:1 to about 8:1, about 5:1 to about 7:1, about 5:1 to about 6:1, about 6:1 to about 10:1, about 6:1 to about 9:1, about 6:1 to about 8:1, about 6:1 to about 7:1, about 7:1 to about 10:1, about 7:1 to about 9:1, about 7:1 to about 8:1, about 8:1 to about 10:1, about 8:1 to about 9:1, or about 9:1 to about 10:1. The weight ratio of the gelatin:the iron adsorption block may be about 5:1 to about 7:1.

[0052] Also, the biocompatible polymer may include gelatin. The biocompatible polymer may include gelatin having different molecular weights. The biocompatible polymer may include a first gelatin having a first average molecular weight; and a second gelatin having a second average molecular weight smaller than the first average molecular weight. Further, the biocompatible polymer may further include a third gelatin having a third average molecular weight which is smaller than the second average molecular weight, and the first gelatin, the second gelatin and the third gelatin may be cross-linked to one another. Further, the biocompatible polymer may further include a fourth gelatin having a fourth average molecular weight which is smaller than the third average molecular weight, and the first gelatin, the second gelatin, the third gelatin and the fourth gelatin may be cross-linked to one another.

[0053] The first average molecular weight may be 40,000 to 100,000, 15,000 to 39,000 or 5,000 to 14,000, and the second average molecular weight may be 15,000 to 39,000, 5,000 to 14,000 or 500 to 4,000.

[0054] The first average molecular weight may be 40,000 to 100,000 or 15,000 to 39,000, the second average molecular weight may be 15,000 to 39,000 or 5,000 to 14,000, and the third average molecular weight may be 5,000 to 14,000 or 500 to 4,000.

[0055] Further, the first average molecular weight may be 40,000 to 100,000, the second average molecular weight may be 15,000 to 39,000, the third average molecular weight may be 5,000 to 14,000, and the fourth average molecular weight may be 500 to 4,000. The first average molecular weight may be 40,000 to 60,000, the second average molecular weight may be 15,000 to 30,000, the third average molecular weight may be 7,000 to 12,000, and the fourth average molecular weight may be 2,000 to 5,000.

[0056] The gelatin may include a greater amount of gelatin having a relatively high average molecular weight than gelatin having a relatively low average molecular weight. In this case, the embolic microbead formed by cross-linking the gelatin is relatively slowly degraded in vivo.

[0057] The gelatin may include a greater amount of gelatin having a relatively low average molecular weight than gelatin having a relatively high average molecular weight. In this case, the embolic microbead formed by cross-linking the gelatin is relatively fast degraded in vivo.

[0058] If the gelatin included in the biocompatible polymer include the first gelatin having the first average molecular weight and the second gelatin having the second average molecular weight which is smaller than the first average molecular weight, the biocompatible polymer may include the first gelatin in the amount of about 80 parts by weight or less, about 75 parts by weight or less, about 70 parts by weight or less, about 65 parts by weight or less or about 60 parts by weight or less based on 100 parts by weight of the gelatin.

[0059] The average molecular weight described above or to be described below refers to the weight average molecular weight. Also, the average molecular weight may have a unit of Dalton.

[0060] The average molecular weights of the first gelatin, the second gelatin, the third gelatin and the fourth gelatin may be regulated through a hydrolysis process. That is, gelatin having a high average molecular weight may be hydrolyzed and gelatin having a low average molecular weight may be produced.

[0061] The gelatin may include mammal-derived gelatin or fish-derived gelatin. In particular, if the gelatin includes the fish-derived gelatin, the risk of mad cow disease or foot-and-mouth disease of conventional gelatin derived from cows or pigs can be eliminated.

[0062] If the gelatin is composed of the fish-derived gelatin, the embolic microbead according to an exemplary embodiment of the present disclosure may be formed at a relatively low temperature and may have a uniform porous spherical shape.

[0063] The gelatin may include glycine, proline and hydroxyproline. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure may have elasticity, flexibility and expansibility depending on reaction conditions. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure may be applied to blood vessels so that the blood blocking time can be predicted.

[0064] The gelatin may be fish-derived gelatin. The fish-derived gelatin is prepared from skins of warm current fish and may be gelated at a lower temperature than gelatin derived from cows or pigs. For example, the fish-derived gelatin may be easily cross-linked in a sol state at a temperature of from about 20° C. to about 40° C., and the embolic microbead according to an an exemplary embodiment of the present disclosure may be prepared.

[0065] Also, the gelatin may be prepared from animal-derived collagen or fish-derived collagen. The gelatin may be extracted from the collagen when heat is applied to the collagen. Further, as the gelatin, marine collagen peptide or collagen peptide is available from the market.

[0066] The fucoidan may be extracted from brown algae such as sea mustard, mozuku Cladosiphon novae-caledoniae kylin), kelp and Hizikia fusiforme. Also, the fucoidan may include a sulfuric acid group and a polysaccharide such as fucose. That is, the fucoidan may have a chemical structure in which the sulfuric acid group and the polysaccharide are coupled to each other.

[0067] The fucoidan may include glucuronic acid represented by the following Chemical Formula 1.

##STR00001##

[0068] The fucoidan may include a unit represented by the following Chemical Formula 2.

##STR00002##

[0069] The fucoidan may have an average molecular weight of from about 3,000 to about 40,000. The fucoidan may have the average molecular weight of from about 5,000 to about 30,000. The fucoidan may have the average molecular weight of from about 6,000 to about 25,000. The fucoidan may have an average molecular weight of from about 7,000 to about 20,000.

[0070] Since the fucoidan simultaneously includes the hydroxyl group and the sulfuric acid group, it can adsorb iron ions and can be efficiently coupled to an anticancer agent such as doxorubicin or the like. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure can adsorb iron ions and effectively deliver an anticancer agent such as doxorubicin or the like.

[0071] Also, the fucoidan may help improve the liver function. That is, the fucoidan can be used as an adjuvant for improving the liver function. Further, the fucoidan may be used as an adjuvant having an anticancer effect. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure can be effective in liver cancer or the like.

[0072] The embolic microbead according to an exemplary embodiment of the present disclosure may have a high iron adsorption rate. The embolic microbead according to an exemplary embodiment of the present disclosure may have a high iron adsorption rate as shown in the following Equations 1 to 5.

[0073] In an exemplary embodiment of the present disclosure, an iron adsorption rate after 24 hours (IAd24) based on 100 mg of the embolic microbead, represented by the following Formula 1, may be about 5%/100 mg or more:

[00004]$\begin{array}{cc}\mathrm{IAd}24=\frac{\left(\mathrm{IC}0-\mathrm{IC}24\right)}{\mathrm{IC}0}\times 100;& \left[\mathrm{Formula}1\right]\end{array}$

[0074] in the Formula 1, the IC0 is an initial molar concentration of a FeCl.sub.3 aqueous solution, and the IC24 is a molar concentration of an iron ion of the FeCl.sub.3 aqueous solution left for 24 hours after adding the embolic microbead to the FeCl.sub.3 aqueous solution.

[0075] The iron adsorption rate after 24 hours (IAd24) may be about 6%/100 mg or more. The iron adsorption rate after 24 hours (IAd24) may be about 7%/100 mg or more. The iron adsorption rate after 24 hours (IAd24) may be about 8%/100 mg or more. The iron adsorption rate after 24 hours (IAd24) may be about 9%/100 mg or more. The iron adsorption rate after 24 hours (IAd24) may be about 10%/100 mg or more. The iron adsorption rate after 24 hours (IAd24) may be about 50%/100 mg or less.

[0076] In an exemplary embodiment of the present disclosure, an iron adsorption rate after 48 hours (IAd48) based on 100 mg of the embolic microbead, represented by the following Formula 2, may be about 5%/100 mg or more:

[00005]$\begin{array}{cc}\mathrm{IAd}48=\frac{\left(\mathrm{IC}0-\mathrm{IC}48\right)}{\mathrm{IC}0}\times 100;& \left[\mathrm{Formula}2\right]\end{array}$

[0077] in the Formula 2, the IC0 is an initial molar concentration of a FeCl.sub.3 aqueous solution, and the IC48 is a molar concentration of an iron ion of the FeCl.sub.3 aqueous solution left for 48 hours after adding the embolic microbead to the FeCl.sub.3 aqueous solution.

[0078] The iron adsorption rate after 48 hours (IAd48) may be about 6%/100 mg or more. The iron adsorption rate after 48 hours (IAd48) may be about 7%/100 mg or more. The iron adsorption rate after 48 hours (IAd48) may be about 8%/100 mg or more. The iron adsorption rate after 48 hours (IAd48) may be about 9%/100 mg or more. The iron adsorption rate after 48 hours (IAd48) may be about 10%/100 mg or more. The iron adsorption rate after 48 hours (IAd48) may be about 50%/100 mg or less.

[0079] In an exemplary embodiment of the present disclosure, an iron adsorption rate after 1 hour (IAd1) based on 100 mg of the embolic microbead, represented by the following Formula 3, may be about 5%/100 mg or more:

[00006]$\begin{array}{cc}\mathrm{IAd}1=\frac{\left(\mathrm{IC}0-\mathrm{IC}1\right)}{\mathrm{IC}0}\times 100;& \left[\mathrm{Formula}3\right]\end{array}$

[0080] in the Formula 3, the IC0 is an initial molar concentration of a FeCl.sub.3 aqueous solution, and the IC1 is a molar concentration of an iron ion of the FeCl.sub.3 aqueous solution left for 1 hour after adding the embolic microbead to the FeCl.sub.3 aqueous solution.

[0081] The iron adsorption rate after 1 hour (IAd1) may be about 6%/100 mg or more. The iron adsorption rate after 1 hour (IAd1) may be about 7%/100 mg or more. The iron adsorption rate after 1 hour (IAd1) may be about 8%/100 mg or more. The iron adsorption rate after 1 hour (IAd1) may be about 9%/100 mg or more. The iron adsorption rate after 1 hour (IAd1) may be about 10%/100 mg or more. The iron adsorption rate after 1 hour (IAd1) may be about 50%/100 mg or less.

[0082] In an exemplary embodiment of the present disclosure, an iron adsorption rate after 12 hours (IAd12) based on 100 mg of the embolic microbead, represented by the following Formula 4, may be about 5%/100 mg or more:

[00007]$\begin{array}{cc}\mathrm{IAd}12=\frac{\left(\mathrm{IC}0-\mathrm{IC}12\right)}{\mathrm{IC}0}\times 100;& \left[\mathrm{Formula}4\right]\end{array}$

[0083] in the Formula 4, the IC0 is an initial molar concentration of a FeCl.sub.3 aqueous solution, and the IC12 is a molar concentration of an iron ion of the FeCl.sub.3 aqueous solution left for 12 hours after adding the embolic microbead to the FeCl.sub.3 aqueous solution.

[0084] The iron adsorption rate after 12 hours (IAd12) may be about 6%/100 mg or more. The iron adsorption rate after 12 hours (IAd12) may be about 7%/100 mg or more. The iron adsorption rate after 12 hours (IAd12) may be about 8%/100 mg or more. The iron adsorption rate after 12 hours (IAd12) may be about 9%/100 mg or more. The iron adsorption rate after 12 hours (IAd12) may be about 10%/100 mg or more. The iron adsorption rate after 12 hours (IAd12) may be about 50%/100 mg or less.

[0085] In an exemplary embodiment of the present disclosure, an iron adsorption rate after 72 hours (IAd72) based on 100 mg of the embolic microbead, represented by the following Formula 5, may be about 5%/100 mg or more:

[00008]$\begin{array}{cc}\mathrm{IAd}72=\frac{\left(\mathrm{IC}0-\mathrm{IC}72\right)}{\mathrm{IC}0}\times 100;& \left[\mathrm{Formula}5\right]\end{array}$

[0086] in the Formula 5, the IC0 is an initial molar concentration of a FeCl.sub.3 aqueous solution, and the IC72 is a molar concentration of an iron ion of the FeCl.sub.3 aqueous solution left for 72 hours after adding the embolic microbead to the FeCl.sub.3 aqueous solution.

[0087] The iron adsorption rate after 72 hours (IAd72) may be about 6%/100 mg or more. The iron adsorption rate after 72 hours (IAd72) may be about 7%/100 mg or more. The iron adsorption rate after 72 hours (IAd72) may be about 8%/100 mg or more. The iron adsorption rate after 72 hours (IAd72) may be about 9%/100 mg or more. The iron adsorption rate after 72 hours (IAd72) may be about 10%/100 mg or more. The iron adsorption rate after 72 hours (IAd72) may be about 50%/100 mg or less.

[0088] In the Formula 1 to 5, the IC0 may be 0.18 M.

[0089] The embolic microbead according to an exemplary embodiment of the present disclosure may include a biocompatible polymer, the biocompatible polymer may include a gelatin and an iron adsorption block cross-linked, and the embolic microbead may be combined with an anticancer drug. Herein, the embolic microbead may chelate an anticancer agent.

[0090] The coupled anticancer agent is not specifically limited, and any anticancer agent which can be coupled to the embolic microbead according to an exemplary embodiment of the present disclosure can be used without limitations. For example, the the anticancer drug may be selected from doxorubicin, irinotecan, gemcitabine, oxaliplatin and docetaxel.

[0091] The embolic microbead according to an exemplary embodiment of the present disclosure may have a high anticancer conjugation rate, particularly a high doxorubicin conjugation rate. In particular, since the biocompatible polymer has the fucoidan, the embolic microbead according to an exemplary embodiment of the present disclosure may have a high iron adsorption rate as well as a high anticancer conjugation rate, particularly a high doxorubicin conjugation rate.

[0092] In an exemplary embodiment of the present disclosure, a combining rate with the anticancer drug after 1 hour (AAd) based on 100 mg of the embolic microbead, represented by the following Formula 6, may be about 10%/100 mg or more:

[00009]$\begin{array}{cc}\mathrm{AAd}=\frac{\left(AC0-AC1\right)}{AC0}\times 100;& \left[\mathrm{Formula}6\right]\end{array}$

[0093] in the Formula 6, the AC0 is an initial mg/ concentration of an anticancer drug solution, and the AC1 is a mg/ concentration of the anticancer drug of the anticancer drug solution left for 1 hour after adding the embolic microbead to the anticancer drug solution. Herein, the anticancer drug may be doxorubicin. The combining rate (AAd) may be about 10%/100 mg or more. The combining rate (AAd) may be about 20%/100 mg or more. The combining rate (AAd) may be about 30%/100 mg or more. The combining rate (AAd) may be about 50%/100 mg or more. The combining rate (AAd) may be about 60%/100 mg or more. The combining rate (AAd) may be about 90%/100 mg or less.

[0094] Herein, the AC0 may be about 1 mg/

[0095] The embolic microbead according to an exemplary embodiment of the present disclosure is formed by cross-linking the gelatin and the iron adsorption block. The embolic microbead according to an exemplary embodiment of the present disclosure includes a cross-linker. The cross-linker serves to cross-link the gelatin and the iron adsorption block.

[0096] Here, the cross-linker includes at least one selected from the group consisting of formaldehyde, glutaraldehyde, dialdehyde starch, epoxy compound, glutaraldehyde glyoxal, glyoxal, 2 2-dimethoxy-2-phenylacetophenone, tripolyphosphate sodium salt, diacetaldehyde PEG, scleraldehyde, diethyl squarate, epichlorohydrin and genipin.

[0097] The embolic microbead according to an exemplary embodiment of the present disclosure may include the cross-linker in the amount of from about 0.20 parts by weight to about 50 parts by weight based on 100 parts by weight of the gelatin. More specifically, the embolic microbead may may include the cross-linker in the amount of from about 3 parts by weight to about 20 parts by weight based on 100 parts by weight of the gelatin.

[0098] The embolic microbead according to an exemplary embodiment of the present disclosure may have an average particle size of from about 10 μm to about 2000 μm. More specifically, the embolic microbead according to an exemplary embodiment of the present disclosure may have an average particle size of from about 50 μm to about 2000 μm. More specifically, the embolic microbead according to an exemplary embodiment of the present disclosure may have an average particle size of from about 50 μm to about 1000 μm.

[0099] The embolic microbead according to an exemplary embodiment of the present disclosure has a porous structure. The embolic microbead according to an exemplary embodiment of the present disclosure may have a sponge structure. That is, the embolic microbead according to an exemplary embodiment of the present disclosure may include micropores. The embolic microbead according to an exemplary embodiment of the present disclosure may have a porosity of from about 20 vol % to about 70 vol %. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure may have a high elasticity and a high swelling coefficient.

[0100] The embolic microbead according to an exemplary embodiment of the present disclosure is formed by cross-linking gelatin having a relatively high average molecular weight and gelatin having a relatively low average molecular weight. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure may have a desired particle size and a desired degradation rate. For example, an average diameter of the embolic microbead according to an exemplary embodiment of the present disclosure may be determined by the amount and the average molecular weight of the gelatin having a relatively high average molecular weight. Also, a degradation rate of the embolic microbead according to an exemplary embodiment of the present disclosure may be determined by the amount and the average molecular weight of the gelatin having a relatively low average molecular weight.

[0101] Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure may have a desired particle size and a desired degradation rate depending on the amounts and average molecular weights of the first gelatin and the second gelatin. As a result, the embolic microbead according to an exemplary embodiment of the present disclosure may have an appropriate size and an appropriate degradation rate, and when it is embolized into a target blood vessel, it can maintain an embolic effect until a desired time and then can be degraded.

[0102] Particularly, the embolic microbead according to an exemplary embodiment of the present disclosure may have a high degradation rate, and after it is injected into a patient, it can be replaced and injected into other blood vessels of the patient many times depending on the conditions of the patient. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure can effectively treat the patient.

[0103] The embolic microbead according to an exemplary embodiment of the present disclosure is prepared using gelatin. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure is excellent in biocompatibility, expansibility, elasticity and flexibility. Also, the embolic microbead according to an exemplary embodiment of the present disclosure may have various particle sizes of from about 50 μm to about 2000 μm, and the embolic microbead according to an exemplary embodiment of the present disclosure has a porous spherical shape having a uniform sponge structure. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure can minimize blood vessel stimulation.

[0104] Also, the embolic microbead according to an exemplary embodiment of the present disclosure may be prepared by cross-linking various amounts of gelatin having various average molecular weights. Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure may be used alone or in combination so that the blood vessel blocking time can be predicted.

[0105] Also, the embolic microbead according to an exemplary embodiment of the present disclosure has the high iron adsorption rate after 24 hours (IAd24) and the high iron adsorption rate after 48 hours (IAd48). Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure is capable of fast iron adsorption.

[0106] Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure is injected into a human body, particularly the liver carotid artery so that blood flow to cancer cells or the like can be blocked and the supply of iron ions, which are required for existence or proliferation of cancer cells, to the cancer cells can be blocked.

[0107] Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure can effectively necrotize cancer cells by blocking a blood vessel.

[0108] Also, the embolic microbead according to an exemplary embodiment of the present disclosure can effectively adsorb iron ions that are eluted when cancer cells or the like are necrotized.

[0109] Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure can effectively suppress regrowth of cancer cells.

[0110] The embolic microbead according to an exemplary embodiment of the present disclosure can be very effectively used for treating cancers, such as liver cancer, and treating proliferative diseases.

[0111] Referring to FIG. 1, the embolic microbead according to an example may be prepared by the following process.

[0112] First, gelatin is prepared (S10). The gelatin maybe mammal-derived gelatin or fish-derived gelatin. The gelatin may have a weight average molecular weight of from about 50,000 to about 100,000.

[0113] The gelatin may be obtained from collagen of mammals or collagen of fish. Otherwise, the gelatin may be commercially obtained. The gelatin can be referred to the above description.

[0114] Then, the gelatin may be hydrolyzed to have an appropriate molecular weight. The gelatin may be hydrolyzed in a subcritical water state.

[0115] More specifically, the gelatin is dissolved or dispersed in water to form an aqueous solution or aqueous dispersion. Here, the amount of the gelatin in the aqueous solution or aqueous dispersion may be from about 3 wt % to about 20 wt %.

[0116] Then, the aqueous solution or aqueous dispersion is maintained in the subcritical water state for a predetermined period of time. For example, the aqueous solution or aqueous dispersion may be maintained at a temperature of from about 100° C. to about 250° C. and a pressure of from about 30 atm. to about 80 atm for from about 10 minutes to about 5 hours. Therefore, the gelatin is hydrolyzed to form a polypeptide. Also, the hydrolysis process in the subcritical water state may be performed in the presence of carbon dioxide (CO.sub.2) and nitrogen (N.sub.2).

[0117] Further, the gelatin may be hydrolyzed with an enzyme. Furthermore, the gelatin may be hydrolyzed with an acid. The gelatin may be hydrolyzed with both the subcritical water and the enzyme.

[0118] Then, the hydrolyzed gelatin may be fractionated. The hydrolyzed gelatin may be fractionated by molecular weight in water serving as a solvent by gel filtration chromatography. The hydrolyzed gelatin may be fractionated by an HPLC (1260 HPLC system, Agilent, USA) connected to a fraction collector (G1364C 1260 FC-AS, Agilent, USA) and divided by molecular weight. A polypeptide divided by molecular weight may be obtained by various methods capable of fractionating an oligomer or polymer by molecular weight. The hydrolyzed gelatin may be separated by molecular weight through a column.

[0119] Therefore, gelatin with different molecular weights can be obtained. For example, the gelatin, the second gelatin and the third gelatin may be obtained.

[0120] As described above, gelatin divided by molecular weight may be obtained.

[0121] For example, the hydrolyzed gelatin is fractionated so that gelatin having an average molecular weight of from about 40,000 to about 60,000, gelatin having an average molecular weight of from about 20,000 to about 30,000, gelatin having an average molecular weight of from about 8,000 to about 12,000 and gelatin having an average molecular weight of from about 1,000 to about 2,000 may be obtained.

[0122] Then, the gelatin may be aminated. The aminated gelatin may be effectively reacted with the iron adsorption polymer, particularly the fucoidan and/or polyphenol.

[0123] The amination process may be performed as follows.

[0124] The gelatin and a sufficient amount of diamine are mixed under subacid conditions, for example, at a pH of from about 4.5 to about 6. Then, a catalyst is added into the mixed solution of the gelatin and the diamine and then reacted at a temperature of from about 30° C. to about 45° C. Thus, the aminated gelatin may be prepared.

[0125] Thereafter, the iron adsorption polymer is prepared (S20). The fucoidan may be extracted and prepared from algae. Also, the polyphenol may be extracted and prepared from plants such as green tea.

[0126] Then, the gelatin and the iron adsorption polymer are cross-linked by a cross-linker (S30).

[0127] The cross-linker may be the same as described above

[0128] The cross-link reaction is carried out in an aqueous solution that includes the gelatin and the iron adsorption polymer in the amount of form about 3 wt % to about 10 wt %. After the cross-linker is added into the aqueous solution in the amount as described above, the gelatin and the iron adsorption polymer are cross-linked by the cross-linker at a temperature of from about 20° C. to about 40° C. for from about 6 hours to about 12 hours.

[0129] For example, the aqueous solution of the gelatin and the iron adsorption polymer and the cross-linker solution are mixed at a weight ratio of from about 100:0.5 to about 100:10. Then, the mixed solution is firstly stirred at a temperature of from about 20° C. to about 40° C. and a speed of from about 1000 rpm to about 1500 rpm for from about 5 minutes to about 120 minutes. Thereafter, the firstly stirred mixed solution is secondly stirred at a temperature of from about 20° C. to about 40° C. and a speed of from about 1 rpm to about 500 rpm for from about 10 minutes to about 48 hours. Therefore, a polymer aqueous solution in which the gelatin and the iron adsorption polymer are cross-linked can be prepared.

[0130] More specifically, in the first stirring process, if the stirring speed exceeds the range of stirring speed of from about 1000 rpm to about 1500 rpm, bubbles are formed, which may cause a decrease in density. Also, in the first stirring process, if the stirring is performed at a temperature of about 20° C. or less, the mixed solution may be gelated. Further, in the first stirring process, if the stirring is performed at a temperature of about 40° C. or more, bubbles are formed, which may cause a decrease in density.

[0131] Further, in the second stirring process, if the stirring speed exceeds about 500 rpm, the mixed solution may be gelated and thus cannot be easily cross-linked to a sol state, which may cause a remarkable decrease in absorbency. Therefore, if the stirring speed exceeds about 500 rpm, the function of the embolic microbead may deteriorate.

[0132] Furthermore, in the second stirring process, if the temperature exceeds the above-described range of temperature, the mixed solution may be gelated and hardened, which may make it difficult to prepare a cross-linked gelatin aqueous solution. In the second stirring process, the stirring is performed for from about 10 minutes to about 48 hours in order to improve the absorbency and maintain the shape.

[0133] Therefore, a cross-linked gelatin aqueous solution is prepared through the stirring process. Then, the cross-linked gelatin aqueous solution is dripped or dispersed onto oil so that aggregation of the cross-linked gelatin in a gel state can be suppressed. Also, a porous spherical cross-linked gelatin particle having a uniform sponge structure with a particle size of from about 50 μm to about 2,000 μm can be prepared. Further, the cross-linked gelatin is less exposed to the oil, the oil can be easily separated from the cross-linked gelatin.

[0134] A cross-linked gelatin particle having a spherical sponge structure is formed. The cross-linked gelatin particle may have various average particle sizes depending on the amounts of the gelatin having various average molecular weights, the amount of the fucoidan or polyphenol, the amount of the cross-linker, the cross-linking temperature and the cross-linking time. For example, the cross-linked gelatin particle may have an average particle size of from about 50 μm to about 2000 μm under the above-described conditions.

[0135] More specifically, the gelatin may be fish gelatin. That is, gelatin used for the hydrolysis may be derived from fish. Particularly, the fish gelatin is prepared from skins of warm current fish and may be gelated at a lower temperature than gelatin derived from cows or pigs. Therefore, the fish gelatin may be easily cross-linked in a sol state at a temperature of from about 20° C. to about 40° C. to form a porous sphere having a uniform sponge structure with a particle size of from about 50 μm to about 2000 μm. If the gelatin is derived from the fish gelatin, it has a low viscosity in a non-gel state and has a low molecular weight. Thus, it can be dripped or dispersed at a higher concentration. Therefore, in the present example, gelatin microparticles having a high apparent density can be prepared.

[0136] Also, the concentration of the gelatin derived from the fish gelatin in an aqueous solution may be from about 3 wt % to about 20 wt %. Further, in the second stirring process, the concentration of the cross-linker in the prepared cross-linked gelatin aqueous solution may be from about 0.05 wt % to about 10 wt %.

[0137] More specifically, an emulsion of the gelatin particles is allowed to pass through a nozzle with compressed air in an encapsulator and dispersed or dripped onto oil. Here, the particle solution may have a temperature of from about 20° C. to about 40° C. and may pass through the nozzle at a temperature of from about 65° C. to about 75° C. Further, by setting a vibration frequency in a range of from about 40 Hz to about 6000 Hz, it is possible to control the size of a spherical gelatin liquid droplet to be dripped or dispersed.

[0138] Furthermore, the oil may be ester-based oil, hydrocarbon-based oil, animal oil or vegetable oil. Specifically, the oil may be olive oil, bean oil, canola oil, grapeseed oi, soybean oil, palm oil, paraffin oil, α-bisabolol, stearyl glycyrrhetinate, salicylic acid, tocopheryl acetate, panthenol, glyceryl stearate, cetyl octanolate, isopropyl myristate, 2-ethylene isopelagonate, di-c12-13 alkyl malate, cetearyl octanoate, butylene glycol dicaprylate/dicaprate, isononyl isostearate, isostearyl isostearate, cetyl octanoate, octyldodecyl myristate, cetyl esters, c10-30 cholesterol/lanosterol ester, hydrogenated castor oil, mono-glycerides, diglycerides, triglycerides, beeswax, canauba wax, sucrose distearate, PEG-8 beeswax, candelilla (Euphorbia cerifera) wax, mineral oil, squalene, squalane, monoglycerides, middle chain glycerides, myglyol or cremophor.

[0139] Desirably, the oil may be paraffin oil, but is not limited thereto. More desirably, the oil may be mixed with a cross-linker in the amount of from about 0 wt % to about 5 wt % based on 100 wt % of the oil in order for the gelatin particles to easily maintain their spherical shape on the oil.

[0140] Further, the oil is cooled and maintained at a temperature of from about 0° C. to about 10° C., which makes it easy to form spherical gelatin.

[0141] Therefore, a cross-linked gelatin particle can be prepared.

[0142] Then, the cross-linked gelatin particle is washed and dried (S40). After the oil including the spherical gelatin particles is stirred, washing and drying processes are performed. Thus, a porous gelatin microparticle having a sponge structure can be formed.

[0143] The cross-linked spherical gelatin particle may be washed with an organic solvent.

[0144] The oil including the spherical gelatin particles prepared in the process S40 is stirred at a temperature of from about 0° C. to about 10° C. and a speed of from about 400 rpm to about 1400 rpm, settled and then washed with an organic solvent. Therefore, the oil and the cross-linker included in the cross-linked spherical gelatin particle are removed, and the cross-linked spherical gelatin particle is solidified.

[0145] Then, the solidified gelatin particle is lyophilized for from about 3 hours to about 48 hours. Therefore, a porous gelatin microparticle having a sponge structure is formed. Here, the porous gelatin microparticle having a sponge structure has a particle size of from about 150 μm to about 2000 μm.

[0146] More specifically, in the washing and drying processes, the oil including the gelatin particles is stirred at a speed of from about 400 rpm to about 1400 rpm, and, thus, a spherical gelatin particle can be easily formed and the spherical gelatin can have appropriate properties. Also, since the oil is maintained in the range of temperature of from about 0° C. to about 10° C., aggregation of the spherical gelatin particles on the oil can be suppressed and the spherical shape can be maintained.

[0147] Further, the organic solvent is petroleum ether, ethyl ether, isopropyl acetate, n-propyl acetate, isobutyl acetate, n-butyl acetate, isobutyl isobutyrate, 2-ethylhexyl acetate, ethylene glycol diacetate, C9 acetate, C10 acetate, methyl ethyl ketone, methyl isobutyl ketone, methyl isoamyl ketone, methyl n-amyl ketone, dibutyl ketone, cyclohexanone, isophorone, acetaldehyde, n-butyl aldehyde, croton aldehyde, 2-ethyl hexaldehyde, isobutyl aldehyde, propion aldehyde, ethyl 3-ethoxypropionate, toluene, xylene, trichloroethane, propylene glycol monomethyl ethyl acetate, ethylene glycol monoethyl ether acetate, ethylene glycol monobutyl ether, diethylene glycol monobutyl ether acetate, dibutyl phthalate, diethyl phthalate, dimethyl phthalate, dioctyl phthalate, dioctyl terephthalate, butyl octyl phthalate, butyl benzene phthalate, dioctyl adipate, triethylene glycol di-2-ethylhexanoate, trioctyl trimethylate, glyceryl triacetate, glyceryl/tripropionin, 2,2,4-trimethyl-1,3-pentanediol diisobutyrate or a mixture thereof.

[0148] Desirably, the organic solvent is ethyl ether or isobutyl acetate.

[0149] Then, the embolic microbead according to an exemplary embodiment of the present disclosure is added into deionized water to prepare a formulation (S50).

[0150] As described above, the embolic microparticle according to the present disclosure is prepared form fish gelatin and thus is excellent in biocompatibility, expansibility, elasticity and flexibility. The embolic microparticle according to the present disclosure is formed into a porous sphere having a uniform sponge structure with a particle size of from about 150 μm to about 2000 μm, which minimizes blood vessel stimulation and makes it easy to block a blood vessel. The embolic microparticle according to the present disclosure is prepared by the following preparation method.

[0151] Also, since the embolic microbead according to an exemplary embodiment of the present disclosure is formed by cross-linking the gelatin having different molecular weights, the embolic microbead according to an exemplary embodiment of the present disclosure can be degraded in vivo at a desired time point.

[0152] Further, the embolic microbead according to an exemplary embodiment of the present disclosure includes the fucoidan and/or the polyphenol as the iron adsorption polymer and thus has an improved iron adsorption rate.

[0153] Therefore, the embolic microbead according to an exemplary embodiment of the present disclosure can effectively remove cancer cells.

[0154] A composition for treating proliferative diseases according to an exemplary embodiment of the present disclosure may include an embolic microbead, the embolic microbead may include a gelatin and an iron adsorption block crosslinked, and the embolic microbead may be combined with an iron component and/or an anticancer drug. The embolic microbead may adsorb or may be coupled to or may chelate an iron component and/or an anticancer agent.

[0155] The proliferative diseases may include at least one selected from neovascularization, tumor, cancer, bone diseases, fibroplasia disorders, statomegaly, renal cyst, and atherosclerosis.

[0156] The cancer may include at least one selected from solid tumor, hematologic malignancy, colorectal cancer, uterine cancer, uterine myoma, meningioma, lung cancer, small cell lung cancer, non-small cell lung cancer, gastrointestinal cancer, bowel cancer, breast cancer, ovarian cancer, prostate cancer, testicular cancer, liver cancer, renal cancer, bladder cancer, pancreatic cancer, sarcoma, osteosarcoma, kaposi's sarcoma and melanoma. Particularly, the cancer may be the liver cancer.

MODE FOR CARRYING OUT THE INVENTION

[0157] Hereinafter, the present disclosure will be explained in more detail with reference to Examples. However, the following Examples are illustrative only for better understanding of the present disclosure but do not limit the present disclosure.

PREPARATION EXAMPLE

[0158] Preparation of Aminated Gelatin

[0159] A first gelatin solution was prepared by mixing 10 g of first gelatin (with an average molecular weight of about 42,000) in 250 mL of 0.1 M phosphate buffer solution (pH 5.3). After a 1,2-ethylenediamine solution was added into 5.6 g of the first gelatin solution, the pH was adjusted to 5 using HCl. Then, 5.35 g of 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride was added as a catalyst into the first gelatin solution. Thereafter, the first gelatin solution added with the 1,2-ethylenediamine solution and the catalyst was reacted at a temperature of 37° C. for about 8 hours. Then, the reacted first gelatin solution was washed with deionized water through dialysis for 48 hours, and first aminated gelatin was prepared through lyophilization.

[0160] A second gelatin solution was prepared by mixing 10 g of second gelatin (with an average molecular weight of about 31,000) in 250 mL of 0.1 M phosphate buffer solution (pH 5.3). After a 1,2-ethylenediamine solution was added into 5.6 g of the second gelatin solution, the pH was adjusted to 5 using HCl. Then, 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride was added as a catalyst into the second gelatin solution. Thereafter, the second gelatin solution added with the 1,2-ethylenediamine solution and the catalyst was reacted at a temperature of 37° C. for about 8 hours. Then, the reacted second gelatin solution was washed with deionized water through dialysis for 48 hours, and second aminated gelatin was prepared through lyophilization.

EXAMPLE 1

[0161] Preparation of Cross-Linked Gelatin Particle

[0162] A gelatin aqueous solution of about 5 wt % was prepared by dissolving 35 parts by weight of the first aminated gelatin, 15 parts by weight of the second aminated gelatin and 7.5 parts by weight of fucoidan (MSC, kelp fucoidan material) in deionized water. Then, a cross-linker aqueous solution was prepared by adding 37 mL of formaldehyde in 100 mL of an aqueous solution containing 15 wt % methanol.

[0163] Then, an aqueous solution in which 0.2 mL of the cross-linker aqueous solution was added to and mixed with 20 mL of the gelatin aqueous solution was firstly stirred at a temperature of about 30° C. and a speed of 1000 rpm for 30 minutes and then secondly stirred at a temperature of 30° C. and a speed of 200 rpm for 24 hours to prepare a cross-linked gelatin aqueous solution in a sol state.

[0164] Thereafter, the prepared cross-linked gelatin aqueous solution was injected into an Encapsulator B-390 (BUCHI, Switzerland) whose vibration frequency is adjusted to 400 Hz, whose electronegativity is adjusted to 1200 V and whose nozzle temperature is adjusted to 75° C. and then dripped onto 100 mL of paraffin oil containing a cross-linker by using compressed air in the Encapsulator B-390. Thus, a spherical gelatin particle was formed on the paraffin oil. The paraffin oil used herein contains 1 mL of 37% formaldehyde in 100 mL of paraffin oil.

[0165] Then, the paraffin oil including the spherical gelatin particle was stirred at 0° C. and 1000 rpm and then settled for 30 minutes.

[0166] Thereafter, the spherical gelatin droplet was washed by adding isopropyl ethyl alcohol thereto so that the spherical gelatin was solidified, and the paraffin oil and the formaldehyde were removed.

[0167] The solidified gelatin spheres were lyophilized for 24 hours to prepare a gelatin microbead including fucoidan.

[0168] The gelatin microbead was used alone or mixed with deionized water at a ratio of 5:5.

EXAMPLES 2 TO 8 AND COMPARATIVE EXAMPLES 1 AND 2

[0169] The gelatin microbead was prepared in the same manner as in Example 1 except the amounts of the first aminated gelatin, the second aminated gelatin, the fucoidan and epigallocatechin gallate (EGCG, produced by R&O) shown in the following Table 1.

[0170] However, in Examples 5 to 8, EGCG was added to the gelatin aqueous solution according to the parts by weight shown in the following Table 1. Also, in Comparative Example 1 and Comparative Example 2, the gelatin aqueous solution was prepared according to the components and parts by weight shown in the following Table 1, and the gelatin microbead was prepared by the same process as in Example 1.

TABLE-US-00001 TABLE 1 First Second aminated aminated gelatin gelatin Fucoidan EGCG (wt %) (wt %) (wt %) (wt %) Example 1 35 15 7.5 — Example 2 35 15 5 — Example 3 35 15 2.5 — Example 4 35 15 1 — Example 5 10 40 7.5 0.5 Example 6 10 40 7.5 0.25 Example 7 15 35 7.5 0.5 Example 8 15 35 7.5 0.25 Comparative 50 0 0 0 Example 1 Comparative 15 35 0 0 Example 2

TEST EXAMPLE

[0171] Measurement of Iron Adsorption Rate

[0172] About 100 mg of gelatin microbeads prepared according to Examples 1 to 8 was added into 10 ml of 0.018 M FeCl.sub.3 aqueous solution and uniformly mixed. Then, the gelatin microbead was immersed in the FeCl.sub.3 aqueous solution, and a supernatant of the FeCl.sub.3 aqueous solution was collected every hour.

[0173] Then, the amount of iron contained in the supernatant was measured by ICP (Inductively Coupled Plasma), and the Fe concentration in the FeCl.sub.3 aqueous solution was calculated based on the volume of the collected aqueous solution and the amount of iron. Therefore, an iron adsorption rate was calculated according to Equation 1.

[0174] The following Table 2 shows iron adsorption rates of respective Examples:

[0175] As shown in Table 2, the gelatin microbeads prepared according to Examples 1 to 8 have a high iron adsorption rate.

TABLE-US-00002 TABLE 2 Iron Iron Iron Iron Iron adsorption adsorption adsorption adsorption adsorption rate after rate after rate after rate after rate after 1 hour 12 hours 24 hours 48 hours 72 hours (%/100 mg) (%/100 mg) (%/100 mg) (%/100 mg) (%/100 mg) Example 1 10.88 11.86 11.57 10.62 10.59 Example 2 9.00 11.60 10.51 8.46 9.28 Example 3 8.67 9.49 7.05 7.26 7.62 Example 4 6.41 8.62 7.06 6.72 6.83 Example 5 11.73 10.47 8.07 7.90 7.98 Example 6 10.63 10.47 8.07 7.90 7.98 Example 7 10.79 12.21 10.68 10.55 12.87 Example 8 13.07 12.70 9.57 10.61 11.88 Comparative No iron adsorption Example 1 Comparative No iron adsorption Example 2

[0176] Doxorubicin Conjugation Rate

[0177] About 100 mg of gelatin microbeads prepared according to Examples 1 to 8 and Comparative Examples 1 and 2 was added into 10 ml of a doxorubicin solution having a concentration of about 1 mg/ml and uniformly mixed. Then, the gelatin microbead was immersed, and a supernatant of the doxorubicin solution was collected to measure the absorbance using light of a wavelength of about 550 nm.

[0178] The absorbance of each of Examples 1 to 8 and Comparative Examples 1 and 2 at a wavelength of 550 nm was measured and the concentration of each was measured based on the calibration curve shown in FIG. 2, and the conjugation rate (%/100 mg) of doxorubicin adsorbed onto the gelatin microbead prepared according to each of Examples and Comparative Examples was calculated by comparison with the initial concentration.

TABLE-US-00003 TABLE 3 Concentration Doxorubicin after adsorption adsorption rate Absorbance (mg/ml) (%/100 mg) Example 1 0.6233 0.1956 84.44 Example 2 0.7947 0.2509 74.91 Example 3 1.1483 0.3651 63.49 Example 4 2.8003 0.8986 10.14 Example 5 1.0647 0.3381 66.19 Example 6 0.1860 0.0544 94.56 Example 7 0.4137 0.1279 87.21 Example 8 0.6960 0.2191 78.09 Comparative 3.107 0.9977 0.23 Example 1 Comparative 3.083 0.9899 1.01 Example 2

[0179] As shown in Table 3, the gelatin microbeads prepared according to Examples 1 to 8 have a high doxorubicin conjugation rate.

[0180] Particle Size Analysis

[0181] The gelatin microbeads prepared according to Example were analyzed through a scanning electron microscope, and it can be seen that the prepared porous spherical gelatin microbeads have a uniform sponge structure with a particle size of from about 150 μm to about 355 μm.