METHOD FOR PRODUCING A MICROCIRCUIT CARD COMPRISING A FLEX CIRCUIT IN A CAVITY BY HOT LAMINATION AND CARD OBTAINED IN THIS WAY

Abstract

The method for producing a microcircuit card including a film having a very low level of shrinkage between two overlay layers, carrying at least one electronic component and an assembly of layers in which a cavity is formed containing the film and the electronic component, involves: forming the assembly to include a central layer 16 made from a material having a very low level of shrinkage between two layers of a plastic material having a substantially higher level of shrinkage, for example PVC, forming, through the assembly, a cavity of which the surface area advantageously equals between 30% and 90% of the surface area of the outer faces of the microcircuit card that is to be produced, embedding the film and the electronic component in a resin so as to occupy the space in the cavity and laminating the two overlay layers.

Claims

1. A process for manufacturing a microcircuit card comprising, between two overlay layers forming the outer faces of this card, a plastic film, of which the degree of shrinkage is less than 1% after heating between 100 C. and 250 C., and bearing at least one electronic component and an assembly of layers wherein a cavity is formed that contains said film and the electronic component, comprising the steps of: forming said assembly so that it comprises a central layer (16) made of a plastic, of which the degree of shrinkage is less than 1% after heating between 100 C. and 250 C., between two layers (15, 17) made of a plastic, of which the degree of shrinkage is between 3% and 5% after heating between 100 C. and 250 C., forming a cavity (13) through this assembly, embedding the film and the electronic component (12) in a resin (18) so as to occupy the volume of the cavity, hot laminating, at a temperature of at least 110 C., this assembly of layers comprising the resin and the film with the electronic component, between two overlay layers (19, 20) so as to obtain a microcircuit card having flat faces.

2. The process as claimed in claim 1, wherein the film is made of polyimide and said assembly is formed of a central layer (16) made of biaxially-oriented polyethylene terephthalate, or PETf, between two layers (15, 17) of polyvinyl chloride, or PVC, of equal thicknesses.

3. The process as claimed in claim 1, wherein this central layer has a thickness at most equal to 300 micrometers and representing between 25% and 150% of each of the two layers between which this central layer is sandwiched.

4. The process as claimed in claim 1, wherein the cavity (13) formed in said assembly is a through-cavity and the surface area of the cavity is equal to between 60% and 90% of the surface area of the outer faces of the microcircuit card to be manufactured.

5. The process as claimed in claim 1, wherein the layers made of plastic are symmetrical relative to the central layer.

6. The process as claimed in claim 1, wherein the two layers between which the central layer lies are split into two sublayers (15, 15, 17, 17).

7. The process as claimed in claim 2, wherein the sublayers (15, 17) bordering the central layer have a thickness of at least 150% of the thickness of the sublayers (15, 17) bordering the transparent overlay layers.

8. The process as claimed in claim, wherein, in one of the layers of said assembly located on either side of the central layer, at least one component (30) is formed which is connected to a microcircuit that the microcircuit card to be manufactured comprises.

9. A microcircuit card obtained by the process as claimed in claim 1, comprising between two overlay layers forming the outer faces of this card, a film made of plastic, of which the degree of shrinkage is less than 1% after heating between 100 C. and 250 C. and bearing at least one electronic component and an assembly of at least three layers wherein a cavity is formed that contains said film and the electronic component, wherein: said assembly of layers comprises a central layer made of a plastic, of which the degree of shrinkage is less than 1% after heating between 100 C. and 250 C., between two layers made of plastic, of which the degree of shrinkage is between 3% and 5% after heating between 100 C. and 250 C., the film and the electronic component being embedded in a resin occupying the volume of the cavity, this microcircuit card having flat outer faces.

10. The microcircuit card as claimed in claim 9, wherein the film is made of polyimide and said assembly is formed of a central layer (16) made of biaxially-oriented polyethylene terephthalate, or PETf, between two layers (15, 17) of polyvinyl chloride, or PVC, of equal thicknesses.

11. The card as claimed in claim 9 wherein the cavity (13) formed in said assembly is a through-cavity and the surface area of the cavity is equal to between 60% and 90% of the surface area of the outer faces of the microcircuit card.

12. The microcircuit card as claimed in claim 1, wherein at least one component is located in one of the layers between which the central layer is located while being connected to a microcircuit that said microcircuit card comprises.

13. The microcircuit card as claimed in claim 12, wherein said component is a contactless communication antenna.

14. An intermediate product formed of an assembly of layers, intended to be used in the process as claimed in claim 1 for manufacturing a microcircuit card comprised of comprising between two overlay layers forming the outer faces of this card, a film made of plastic, of which the degree of shrinkage is less than 1% after heating between 100 C. and 250 C. and bearing at least one electronic component and an assembly of at least three layers wherein a cavity is formed that contains said film and the electronic component, wherein: said assembly of layers comprises a central layer made of a plastic, of which the degree of shrinkage is less than 1% after heating between 100 C. and 250 C., between two layers made of plastic, of which the degree of shrinkage is between 3% and 5% after heating between 100 C. and 250 C., the film and the electronic component being embedded in a resin occupying the volume of the cavity, this microcircuit card having flat outer faces, wherein: said assembly of layers comprises a central layer made of a plastic, of which the degree of shrinkage is less than 1% after heating between 100 C. and 250 C., between two layers made of a plastic, of which the degree of shrinkage is between 3% and 5% after heating between 100 C. and 250 C., a cavity passes through the whole of the assembly of layers.

15. The product as claimed in claim 14, wherein the central layer is made of biaxially-oriented polyethylene terephthalate, or PETf, and this central layer is sandwiched between two layers made of polyvinyl chloride, or PVC, of equal thicknesses.

16. The process as claimed in claim 2, wherein this central layer has a thickness at most equal to 300 micrometers and representing between 25% and 150% of each of the two layers between which this central layer is sandwiched.

17. The process as claimed in claim 2, wherein the cavity (13) formed in said assembly is a through-cavity and the surface area of the cavity is equal to between 60% and 90% of the surface area of the outer faces of the microcircuit card to be manufactured.

18. The process as claimed in claim 3, wherein the cavity (13) formed in said assembly is a through-cavity and the surface area of the cavity is equal to between 60% and 90% of the surface area of the outer faces of the microcircuit card to be manufactured.

19. The process as claimed in claim 16, wherein the cavity (13) formed in said assembly is a through-cavity and the surface area of the cavity is equal to between 60% and 90% of the surface area of the outer faces of the microcircuit card to be manufactured.

20. The process as claimed in claim 4, wherein the layers made of plastic are symmetrical relative to the central layer, and wherein the two layers between which the central layer lies are split into two sublayers (15, 15, 17, 17).

Description

DESCRIPTION OF THE INVENTION

[0050] Objectives, features and advantages of the invention will become apparent from the following description, given by way of nonlimiting illustrative example, with regard to the appended drawing, in which:

[0051] FIG. 1 is a partial cross-sectional view of a card obtained by cold lamination, in a known manner, and

[0052] FIG. 2 is a partial cross-sectional view of a card obtained by hot lamination, in accordance with the invention.

[0053] The microcircuit card represented in part in FIG. 1 comprises, in a known manner, a flex circuit 1, bearing electronic components 2 and mounted within a cavity 3 formed inside a prelam 4 formed of several layers, here three layers, namely the layers 5 to 7. The flex circuit is embedded in a mass of resin 8 which fills the cavity; two overlay layers 9 and 10 cover the lower and upper faces of the prelam and of the mass of resin encompassing the flex circuit. The cavity is barely any bigger than the flex circuit, typically from 1 to 2 mm bigger, parallel to the flat faces of the card, than the contour of this flex circuit.

[0054] Conventionally, the central layer 6 of the prelam is made of PVC, as well as the layers 5 and 7 that sandwich this central layer; the overlay layers, which are customarily transparent, (optionally bordered by printing layers) are also formed of PVC. As indicated above, such a configuration must customarily be cold laminated, to prevent different expansion/shrinkage phenomena from giving rise to the appearance of undulations at the location of the cavity, locally giving rise to undulations of the overlay layers 9 and 10. Indeed, the shrinkage of the PVC layers, greater than that of the flex circuit, results in a reduction in the circumference of the hole. This reduction is sufficient to compress and undulate the flex circuit and the resin mainly in the plane of the card, which will result in deformations in the form of waves or undulations at the surface of the card.

[0055] In accordance with the invention, the card from FIG. 2 has a structure in which the various parts have shrinkage behaviors that are substantially identical in the case of hot lamination, thus preventing such a hot lamination from resulting in a poor flatness of the large faces of the final card.

[0056] In fact, as indicated above, one of the materials commonly used for the manufacture of a flex circuit is polyimide, abbreviated to PI, which has an expansion/shrinkage coefficient of virtually zero up to temperatures of around 130 C., that does not exceed 1% after heating at 250 C. However, other material is also known in the field of manufacturing chip cards, that the hot lamination operators therefore know how to handle in a reliable and effective manner; these are PVC (polyvinyl chloride), PC (polycarbonate), PEN (polyethylene naphthalate), PETg (polyethylene terephthalate glycol-modified), and also PETf (polyethylene terephthalate film, or biaxially-oriented PET).

[0057] Yet it has become apparent that PETf, customarily valued for reasons of environmental safety, and tear resistance and durability for a reasonable low production cost, has the distinctive feature of having an expansion/shrinkage coefficient of several fractions of a percent, typically between 0.5%-1%. However, the use of a PETf single layer can only be envisaged for thin substrates, since in practice a PETf layer having a thickness greater than 300 m does not exist; moreover, PETf has printing and adhesive bonding properties that are much lower than those that are recognized for PVC in the chip card industry.

[0058] It became apparent that it was possible to combine PETf and PVC so as to combine the very low shrinkage of PETf and the exceptional printability and adhesive bonding properties of PVC, within a prelam containing a PI flex circuit formed of electronic components.

[0059] Thus, it was observed that, if the prelam is formed of a PETf layer between lower and upper layers of PVC or other plastics mentioned above, the undulation effect is eliminated since the PETf layer supports the PVC layers and prevents the latter from shrinking to a degree of greater than 1%. The wave phenomenon is therefore prevented.

[0060] Furthermore, if the prelam is formed of a central PETf layer between lower and upper layers of PVC of the same thickness (in other words, if the PETf layer, which is necessarily thin, is correctly centered in the middle of the thickness of the prelam furthermore formed of PVC), and/or if the cavity is a through-opening (therefore extending from one face to the other of the prelam) the area of which is equal to 60% to 90% of that of the prelam, no significant curvature/curling phenomenon occurs after a hot lamination (above 110 C., typically around 130 C., or even higher) between two overlay layers, typically made of PVC, that are optionally transparent.

[0061] Similar comments can be formulated with regard to PEN, the degree of shrinkage of which is also very low.

[0062] Thus, according to the invention, the curvature phenomenon, observed nevertheless in documents such as EP-0 488 574 or U.S. Pat. No. 6,644,552 with a PET layer in a PVC body, is not experienced.

[0063] In fact, it may be believed that this curvature effect is prevented due to this central position of the PETf layer, and also due to the fact that the through-cavity is large enough to limit the curvature effects (see the aforementioned range of around 60% to 90% of the total surface area of the card).

[0064] It is assumed that the aforementioned ratio of 60% to 90% of the area of the opening relative to the surface area of the card makes it possible to limit the effects of distortion between the PVC which shrinks and the PETf which barely shrinks at all, despite the thinness of this PETf layer relative to the thickness of the PVC layers. However it appears that if the cavity is smaller, its presence has no significant effect on the control of the shrinkage.

[0065] An example of a card according to the invention is thus formed, and is depicted in FIG. 2 (the thicknesses not being to scale for reasons of clarity of the drawing), of a prelam 14 formed of a central PETf layer 16, sandwiched between two PVC printing layers 15 and 17, and of a flex circuit 11 comprising electronic components 12, embedded in a resin 18 occupying, together with this flex circuit, the volume of a through-cavity 13 formed through this prelam. The assembly of this prelam and of this mass of resin is held and laminated between two overlay layers 19 and 20.

[0066] In the example represented, the layers 15 and 17 are in fact split (the layers 15 and 17 are respectively bordered by layers 15 and 17), the layer 17 here containing turns of an antenna 30 by means of which the card partly represented may communicate contactlessly with an external terminal.

[0067] By way of example, for an overall thickness of 760 micrometers, namely the standardized thickness of a chip card in accordance with the ISO-7816 or ISO-14443 standard: [0068] the central PETf layer has a thickness of 125 micrometers, [0069] the layers 15 and 17 each have a thickness of 100 micrometers, [0070] the layers 15 and 17 each have a thickness of 50 micrometers, and [0071] the overlay layers, capable of receiving printing, each have a thickness of 168 micrometers.

[0072] In case of transparent overlay layers, these may, as a variant, have a thickness of 40-50 micrometers, being bordered internally by a printing layer having a thickness of around 110-120 micrometers.

[0073] Thus, the central PETf layer has here a thickness representing between 25% and 150% of that of each of the double PVC layers located above and below this layer.

[0074] The PVC layers between which the central PETf layer lies have a thickness substantially greater than the thickness of the PVC layers which are adjacent to the overlay layers; their thickness is for example between 150% and 250% of the thickness of these layers adjacent to the overlay layers. This enables the implantation of circuit elements connected to the microcircuit (not shown) of the chip card to be manufactured.

[0075] The resin coating the flex circuit is here an epoxy or acrylic resin derived from the same family as the resins used for coating the module. These are resins that are widely used in the electronics field.

[0076] Tests carried out at 130 C. show that the flatness of the cards with a prelam formed of such a PVC/PETf complex is widely acceptable unlike pure PVC cards.

[0077] The fact that the PETf does not generally adhere very well to the PVC may be overcome by a surface treatment that the PETf manufacturers know well; it is typically an addition, by coextrusion, of a very thin layer (1 to 10 m) of copolymer. The thickness of this layer is so small that it has no influence on the shrinkage. There may in addition be a deposition of an (acrylic or other) adhesive to ensure the impermeability and/or the adhesion of the PET with another layer.

[0078] As indicated above, the PETf and the PVC are assembled by hot lamination if the PET is at the center; it is however understood that, if it is chosen to position the PETf layer in an off-centered manner (or if this layer does not exist), it is best to proceed by cold lamination (there is then no minimum surface area required for the cavity relative to the total surface area of the layers).

[0079] The PET can be replaced by PEN, in particular.

[0080] The electronic components may be visual display components or acquisition components, for example a fingerprint acquisition component or else a screen displaying a security code intended to be used in combination with a bank card identification number and an expiration date to carry out a payment; the card may be a bank card, typically in the ID-1 format as defined in the aforementioned ISO-7810 or ISO-7816 standard, of contact type, of contactless type or of dual type, i.e. a card enabling communication by contact with a certain type of external terminal and contactlessly with another type of external terminal; communication with the outside may be limited to what is referred to as near-field communication, namely a contactless communication with a range of barely a few tens of centimeters, or even barely a few centimeters.

[0081] The example considered above comprises a polyimide flex circuit but it is understood that the invention applies to any card formed of various materials having significantly different expansion/shrinkage coefficients but that it is desired to manufacture by hot lamination.