INFRARED TRANSMISSION CHALCOGENIDE GLASSES

Abstract

A glass composition and a method for producing the glass composition having an improved infrared transmission are provided. The composition includes indium and or cadmium; germanium; phosphorus, arsenic, and/or antimony; silver; lead; and sulfur, selenium, and/or tellurium. The method is performed by melting a mixture for a time period of between about 5 to about 48 hours and mixing the mixture at a temperature range that is between about 600-1000 C.

Claims

1. A chalcogenide glass composition, the composition consisting essentially of, in percent by weight of the total weight of the composition: gallium; indium in an amount from about 2% to about 20%; germanium; and at least one chalcogen selected from the group consisting of: sulfur, selenium, and tellurium, wherein the at least one chalcogen is in an amount from about 30% to about 80%.

2. The composition of claim 1, wherein the chalcogen is sulfur.

3. The composition of claim 1, wherein the amount of germanium is from about 10% to about 30%.

4. The composition of claim 1, wherein the at least one chalcogen is in an amount from about 50% to about 80%.

5. The composition of claim 1, wherein the composition is prepared by mixing in a temperature range from about 850 C. to 1000 C.

6. A chalcogenide glass composition, the composition consisting essentially of, in percent by weight of the total weight of the composition: indium; germanium in an amount from about 10% to about 30%; at least one alkali selected from the group consisting of: potassium, rubidium, or cesium; at least one chalcogen selected from the group consisting of: sulfur, selenium, and tellurium; and at least one halide selected from the group consisting of: chlorine, bromine, and iodine.

7. The composition of claim 6, wherein the at least one halide is in an amount from about 7% to about 25%.

8. The composition of claim 6, wherein the at least one halide is bromine.

9. The composition of claim 6, wherein the chalcogen is sulfur.

10. The composition of claim 6, wherein the amount of indium is from about 2% to about 20%.

11. The composition of claim 6, wherein the at east one chalcogen is in an amount from about 30% to about 80%.

12. The composition of claim 6, wherein the composition is prepared by mixing in a temperature range from about 850 C. to 1000 C.

13. The composition of claim 6, wherein the at east one alkali is in an amount from about 5% to about 20%.

14. The composition of claim 6, wherein the at east one alkali is cesium.

15. A chalcogenide glass composition, the composition consisting essentially of, in percent by weight of the total weight of the composition: indium; germanium; at least one element selected from the group consisting of: phosphorus, arsenic, and antimony, wherein the at least one element is in an amount from about 2% to about 40%; and at least one chalcogen selected from the group consisting of: sulfur, selenium, and tellurium, wherein the at least one chalcogen is in an amount from about 30% to about 80%.

16. The composition of claim 15, wherein the composition is prepared by mixing in a temperature range from about 850 C. to 1000 C.

17. The composition of claim 15, wherein the amount of germanium is from about 10% to about 30%.

18. The composition of claim 15, wherein the amount of indium is about 2% to about 20%.

19. The composition of claim 15, wherein the at least one chalcogen is in an amount from about 50% to about 80%.

20. The composition of claim 15, wherein the chalcogen is selenium.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0013] FIG. 1 is a plot of comparing transmission percentage of various commercial (prior art) glasses at a given wavelength.

[0014] FIG. 2 is a plot of comparing transmission percentage at a given wavelength for germanium-galium-selenium (GeGaSe) and germanium-indium-selenium (GeInSe).

DETAILED DESCRIPTION OF THE DISCLOSURE

[0015] The present disclosure provides for glass for use in glasses that have an improved transmission in the long wavelength infrared (IR) range. Further, the improved transmission is in the 8 m to 15 m range over present, commercially available glasses.

[0016] The glasses of the present disclosure are chalcogenide glasses. Thus, the present glasses have chemical elements in group 16 of the periodic table. Although Oxygen is in group 16, oxygen itself is not a chalcogenide. These chalcogenide glasses also have cadmium, indium, or a combination thereof, to increase transmission. The chalcogenide glasses of the present disclosure can be sulfur (S), selenium (Se), or tellurium (Te) based.

[0017] For elements of interest in forming chalcogenide glasses, such as late-transition and post-transition metals (d.sup.10 ions) and metalloids, the electronegativity tends to increase with atomic mass. Of these elements, only indium and cadmium possess the ability to form a large part of a chalcogenide glass combined with high atomic mass and low electronegativity. The addition of these two elements to a chalcogenide glass leads to the preferential formation of cadmium-oxygen (CdO) or indium-oxygen (InO) bonds over germanium-oxygen (GeO) that have frequencies in the 250-300 cm.sup.1 range that correspond to wavelengths of 30-40 m. Alkaline, alkaline-earth and rare-earth elements have low electronegativity and can have high mass. However, these elements are ionic, have low solubility, and do not act to preferentially bind oxygen (O). The addition of these elements into sulfide, selenide and telluride glass results in the removal of oxide impurity absorption bands and restoration of the fundamental glass transmission range, typically 12 m for sulfide, 16 m for selenide, and 20 m for telluride glass.

[0018] The addition of indium (In), cadmium (Cd), or both, to the glass increases significantly the transmission of the glass. While not being bound by any theory, it is believed that the improved transmission arises from the combination of low electronegativity and high atomic mass indium (In), cadmium (Cd). It is further believed that the oxygen (O) will preferably bond to elements of the glass having lowest electronegativity, i.e the Cd In which also gives the highest possible metal-oxygen bond strength.

[0019] In a first embodiment, the chalcogenide glass has no cadmium (Cd). In this embodiment, the amount of indium (In) is between about 2% to about 20%, and more preferably, between about 5% to about 15%, of the total weight of the glass.

[0020] In a second embodiment, the chalcogenide glass has no indium (In). In this embodiment, cadmium (Cd) is present in an amount between about 0.5% to about 10% and, more preferably, between about 2% to about 5%.

[0021] In a third embodiment in which the chalcogenide glass has cadmium (Cd) and indium (In), the amount of cadmium (Cd) is between about 0.5% and about 10% and the amount of indium (In) is between about 5% and about 10%. More preferably, the amount of cadmium (Cd) is between about 2% and about 5% and the amount of indium (In) is between about 5% and about 10%.

[0022] In each of these three embodiments set forth above, the remainder of the composition is between about 10% to about 30% germanium (Ge); between about 2% to about 40% of phosphorus (P), arsenic (As) and/or antimony (Sb); 0% to about 10% lead (Pb); 0% to about 20% silver (Ag); and about 30% to about 80% of one or more of the chalogens, sulfur (S), selenium (Se) and/or tellurium (Te).

[0023] In each of the three embodiments described above, the remainder of the composition is alternatively comprised of at least about 5% of germanium (Ge) and at least about 1% of (P), arsenic (As) or antimony (Sb). These elements prevent the formation of crystals from the melt during cooling in the glass formation process.

[0024] Optionally, in each of the three embodiments, each composition can have between about 7% to about 25% of a halide. The halide can include, but not be limited to, chlorine (CI), bromine (Br), or iodine (I).

[0025] As a further option, each of the three embodiments can have between about 5% to about 20% of an alkali. The alkali can include, but not be limited to, potassium (K), rubidium (Rb), or cesium (Cs).

[0026] In addition to the three embodiments discussed above, the present disclosure further provides other embodiments. For example, in two other embodiments, namely fourth and fifth embodiments, each embodiment has indium (In). Generally, indium (In) is preferable in glass compositions (and methods of making same) as compared to cadmium (Cd), since indium (In) has lower toxicity, higher glass stability, and a wider array of compositions in which it can be used.

[0027] The fourth embodiment is a gallium sulfide (Ga.sub.2S.sub.3) lanthium sulfide (La.sub.2S.sub.3) based chalcogenide glass composition. The fifth embodiment is a gallium selenide (GaSe) lanthium selenide (LaSe) based chalcogenide glass composition. In each of these embodiments, the gallium (Ga) increases the solubility of ionic species, such as alkaline and rare-earth elements, in chalcogenide glass.

[0028] In these fourth and fifth embodiments, indium (In) can be substituted for gallium (Ga) to improve infrared transmission however there is some reduction of the ionic solubility. For example, indium (In) can be substituted for up to 50% for arsenic (As), antimony (Sb) or gallium (Ga) in sulfide based glass. Indium (In) can also be substituted up to 100% for arsenic (As), antimony (Sb) or gallium (Ga) in selenide based glass. This latter substitution and effect is not possible with cadmium (Cd).

[0029] The fourth embodiment provides a gallium sulfide (Ga.sub.2S.sub.3) lanthium sulfide (La.sub.2S.sub.3) based chalcogenide glass composition. In this fourth embodiment, indium (In) is present between about 0.1% to about 50%, gallium sulfide (Ga.sub.2S.sub.3) is present between about 20% to about 80%, and lanthium sulfide (La.sub.2S.sub.3) is present between about 15% to about 35%. In this fourth embodiment, the combination of gallium sulfide (Ga.sub.2S.sub.3) and indium (In) does not exceed 80% of the total composition.

[0030] The fifth embodiment of gallium selenide (GaSe) lanthium selenide (LaSe) based chalcogenide glass composition, indium (In) is present between about 0.1% to about 80% and lanthium selenide (LaSe) is present between about 15% to about 35%. In this fifth embodiment, gallium selenide (GaSe) is optional because up to 100% of the gallium (Ga) can be substituted with indium (In). However, gallium selenide (GaSe) can be present in an amount up to about 80%, with the remainder being indium (In), such that the combination of gallium selenide (GaSe) and indium (In) does not exceed about 80% of the composition.

[0031] Examples 1 through 8 below are compositions according to the first embodiment, in which indium (In) is present, but there is no cadmium (Cd). These Examples encompass the first, third, fourth and fifth embodiments, but not the second embodiment.

Example 1

[0032]

TABLE-US-00001 Composition Percent (%) Total Weight of Glass indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or Between about 50-80%. tellurium (Te)

Example 2

[0033]

TABLE-US-00002 Composition Percent (%) Total Weight of Glass indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te)

Example 3

[0034]

TABLE-US-00003 Composition Percent (%) Total Weight of Glass indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 4

[0035]

TABLE-US-00004 Composition Percent (%) Total Weight of Glass indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 5

[0036]

TABLE-US-00005 Composition Percent (%) Total Weight of Glass indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs)

Example 6

[0037]

TABLE-US-00006 Composition Percent (%) Total Weight of Glass indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs)

Example 7

[0038]

TABLE-US-00007 Composition Percent (%) Total Weight of Glass indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 8

[0039]

TABLE-US-00008 Composition Percent (%) Total Weight of Glass indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

[0040] Examples 9 through 16 below are compositions according to the second embodiment, in which there is cadmium (Cd), but no indium (In).

Example 9

[0041]

TABLE-US-00009 Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te)

Example 10

[0042]

TABLE-US-00010 Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te)

Example 11

[0043]

TABLE-US-00011 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 12

[0044]

TABLE-US-00012 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 13

[0045]

TABLE-US-00013 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs)

Example 14

[0046]

TABLE-US-00014 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs)

Example 15

[0047]

TABLE-US-00015 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 16

[0048]

TABLE-US-00016 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

[0049] Examples 17 through 32 below are compositions according to the third embodiment, in which there is both indium n) and cadmium (Cd).

Example 17

[0050]

TABLE-US-00017 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te)

Example 18

[0051]

TABLE-US-00018 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te)

Example 19

[0052]

TABLE-US-00019 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 20

[0053]

TABLE-US-00020 Composition Percent (%)Total Weight of Glass cadmium (Cd) between about 2-5% indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 21

[0054]

TABLE-US-00021 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs)

Example 22

[0055]

TABLE-US-00022 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs)

Example 23

[0056]

TABLE-US-00023 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 24

[0057]

TABLE-US-00024 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 2-5% indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 25

[0058]

TABLE-US-00025 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te)

Example 26

[0059]

TABLE-US-00026 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te)

Example 27

[0060]

TABLE-US-00027 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 28

[0061]

TABLE-US-00028 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 29

[0062]

TABLE-US-00029 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs)

Example 30

[0063]

TABLE-US-00030 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 50-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs)

Example 31

[0064]

TABLE-US-00031 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% indium (In) between about 2-20% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

Example 32

[0065]

TABLE-US-00032 Composition Percent (%) Total Weight of Glass cadmium (Cd) between about 0.5-10% indium (In) between about 5-15% germanium (Ge) between about 10-30% phosphorus (P), arsenic (As), and/or between about 2-40% antimony (Sb) silver (Ag) at most about 20% lead (Pb) at most about 10% sulfur (S), selenium (Se), and/or between about 30-80% tellurium (Te) potassium (K), rubidium (Rb), or between about 5-20% cesium (Cs) chlorine (Cl), bromine (Br), and/or between about 7-25% iodine (I)

[0066] The glass, and glasses formed therefrom, of the present disclosure are preferably prepared by melting a mixture of the raw elements or binary halide and/or chalcogenide compounds for a period of from 5 to 48 hours, preferably from 10 to 20 hours. The glass can be melted in a sealed container, such as a fused quartz ampoule, or in an open crucible, under controlled atmosphere and the liquid glass melt can be mixed via rocking or stirring. The mixing occurs in a temperature range of 600 C. to 1000 C., preferably in the temperature range of 850 C. to 1000 C.

[0067] Without being bound by a particular theory, it is believed that in the temperature range of 700 C. to 1000 C., the oxygen (O) atoms are effectively transferred from germanium-oxygen (GeO) to indium-oxygen (InO) and/or cadmium-oxygen (CdO) bonds. Less indium (In) or cadmium (Cd) are needed to achieve comparable optical properties when melted at higher temperatures than the same composition melted at lower temperatures. Thus, by melting at higher temperatures in the ranges according to the present disclosure, the indium (In) content can be reduced to as low as 2% while still achieving effective removal of oxygen (O) impurities.

[0068] It is also believed that there is also a kinetic component to the impurity removal process. Thus, at least six (6) hours is needed when the indium (In) content is 10%. It appears that there is an increased efficiency when a lower indium (In) content is present if the melt time is longer than twelve (12) hours.

[0069] Using long or longer melt times as a method for remediation of transmission of indium-free compositions results in the absence of a significantly altered refractive index or other adverse effects on the composition properties. This is particularly useful for compositions that do not have germanium (Ge), as the solubility for indium (In) in the glass is low, causing crystal formation.

[0070] Under such longer processing, notwithstanding the above discussed compositions and ranges, it is also possible to use indium (In) as a dopant if the indium (In) is in an amount under about 2%, more preferably, under about 1%. In such an embodiment, the impact on infrared transmission can be significant, but less in magnitude than the embodiments having more than about 2% indium (In).

[0071] Referring to FIG. 2, there is shown a graph of the percent transmission on the vertical axis and wavelength on the horizontal axis for Ge.sub.20In.sub.10Se.sub.70 that has been melted at different temperatures and times. The red line, reference numeral 30, is 950 C. for 4 hours, the blue line, reference numeral 32, is 950 C. for 12 hours and the black line, reference numeral 34, is 800 C. This graph shows that, in addition to indium (In), a longer time at a higher temperature is necessary to fully bind oxygen.

[0072] Applications for the glasses of the present disclosure include, but are not limited to, thermal imaging, night vision systems, motion control systems, spectroscopy, CO2 laser transmission, optical sensor systems based on thin films, and infrared transmitting optical fibers.

[0073] As used in this application, the word about for dimensions, weights, amounts, and other measures means a range that is 10% of the stated value, more preferably 5% of the stated value, and most preferably 1% of the stated value, including all subranges therebetween.

[0074] It should be noted that where a numerical range is provided herein, unless otherwise explicitly stated, the range is intended to include any and all numerical ranges or points within the provided numerical range and including the endpoints. Thus, the word between is intended to include endpoints.

[0075] It should also be noted that the terms first, second, third, and the like may be used herein to modify various elements. These modifiers do not imply a sequential or hierarchical order to the modified elements unless specifically stated.

[0076] Although described herein with reference to one or more exemplary embodiments, it will be understood by those skilled in the art that various changes can be made and equivalents can be substituted for elements thereof without departing from the scope of the present disclosure. In addition, many modifications can be made to adapt a particular situation, construction, operation, or material to the teachings of the disclosure without departing from the scope thereof. Therefore, it is intended that the present disclosure not be limited to the particular embodiment(s) disclosed as the best mode contemplated, but that the disclosure will include all embodiments falling within the spirit and scope of the appended claims.