Titanium-free alloy

Abstract

Titanium-free alloy which has great resistance to pitting and crevice corrosion and a high yield point in the strain-hardened state and includes (in wt %) a maximum of 0.02% C, a maximum of 0.01% S, a maximum of 0.03% N, 20.0-23.0% Cr, 39.0-44.0% Ni, 0.4-<1.0% Mn, 0.1-<0.5% Si, >4.0-<7.0% Mo, a maximum of 0.15% Nb, >1.5-<2.5% Cu, 0.05-<0.3% Al, a maximum of 0.5% Co, 0.001-<0.005% B, 0.005-<0.015% Mg, the remainder consisting of Fe and smelting-related impurities.

Claims

1. A process for the manufacture of a titanium-free alloy with pitting and crevice corrosion resistance as well as offset yield strength in the cold-worked condition, with the following composition in weight %: TABLE-US-00008 C max. 0.02% S max. 0.01% N max. 0.03% Cr 20.0-23.0% Ni 39.0-44.0% Mn 0.4-<1.0% Si 0.1-<0.5% Mo >4.0-<7.0% Nb max. 0.15% Cu >1.5-<2.5% Al 0.05-<0.3% Co max. 0.5% B 0.001-<0.005% Mg 0.005-<0.015% V 0.2-0.7% Fe the rest as well as melting-related impurities wherein a) the alloy is melted openly in continuous or ingot casting, b) to eliminate the segregations caused by the increased molybdenum content, a homogenizing annealing of the produced blooms/billets is performed at 1150-1250 C. for 15 to 25 h, wherein c) the homogenizing annealing is performed in particular following a first hot forming.

2. The process according to claim 1 wherein the alloy has the following composition in weight %: TABLE-US-00009 C max. 0.015% S max. 0.005% N max. 0.02% Cr 21.0-<23% Ni >39.0-<43.0% Mn 0.5-0.9% Si 0.2-<0.5% Mo >4.5-6.5% Nb max. 0.15% Cu >1.6-<2.3% Al 0.06-<0.25% Co max. 0.5% B 0.002-0.004% Mg 0.006-0.015% V 0.2-0.7% Fe the rest as well as melting-related impurities.

3. The process according to claim 1 wherein the alloy has the following composition in weight %: TABLE-US-00010 Cr 21.5-<23% Ni >39.0-<42% Mn 0.4-<1.0% Si 0.2-<0.5% Mo >5-<6.5% Cu >1.6-<2.2% Al 0.05-<0.3% B 0.001-<0.005% Mg 0.005-0.015% V 0.2-0.7% Fe the rest as well as melting-related impurities.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIGS. 1 and 2 are graphical representations of the results of tension tests at room temperature (mean values) versus condition;

(2) FIGS. 3 and 4 are graphical representations of the results of tension tests at room temperature (mean values) versus molybdenum content; and

(3) FIG. 5 shows critical deformation rates for the first hot crack (PT and stereomicroscope inspection) on Alloy 825, regardless of the type of cracking.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

(4) An expedient embodiment of the alloy according to the invention has the following composition (in wt %)

(5) C max. 0.015%

(6) S max. 0.005%

(7) N max. 0.02%

(8) Cr 21.0-<23%

(9) Ni>39.0-<43.0%

(10) Mn 0.5-0.9%

(11) Si 0.2-<0.5%

(12) Mo>4.5-6.5%

(13) Nb max. 0.15%

(14) Cu>1.6-<2.3%

(15) Al 0.06-<0.25%

(16) Co max. 0.5%

(17) B 0.002-0.004%

(18) Mg 0.006-0.015%

(19) Fe the rest as well as melting-related impurities.

(20) The content of chromium may be further modified if necessary as follows:

(21) Cr >21.5-<23%

(22) Cr 22.0-<23%

(23) The nickel content may be further modified if necessary as follows:

(24) Ni >39.0-<42%

(25) Ni >39.0-<41%

(26) The molybdenum content may be further modified if necessary as follows:

(27) Mo >5-<6.5%

(28) Mo >5-<6.2%

(29) The content of copper may be further adjusted if necessary as follows:

(30) Cu >1.6-<2.0%

(31) If necessary, the element V may also be added to the alloy in contents (in wt %) of

(32) V >0-1.0%

(33) V 0.2-0.7%

(34) The iron content in the alloy according to the invention should be >22%.

(35) If the element titanium is left out, thenas explained aboveedge cracks develop during rolling. The cracking tendency can be positively influenced by magnesium on the order of 50-150 ppm. The associated/investigated laboratory heats are listed in Table 1.

(36) TABLE-US-00001 TABLE 1 Influence of deoxidizing elements on the edge-cracking tendency during hot rolling Element Mg Ca in in in Edge wt % C S N Cr Ni Mn Si Mo Ti Nb Cu Fe Al B ppm ppm cracks Ref 825 0.002 0.0048 0.006 22.25 39.41 0.8 0.3 3.27 0.8 0.01 2 R 0.14 0 no LB2181 0.002 0.004 0.006 22.57 39.76 0.8 0.3 3.27 0.4 0.01 2.1 R 0.12 0 slight LB2182 0.006 0.003 0.052> 22.46 39.71 0.8 0.3 3.27 0.01 2 R 0.11 0 yes LB2183 0.002 0.004 0.094> 22.65 39.61 0.8 0.3 3.28 0.01 1.9 R 0.1 0 yes LB2218 0.005 0.0031 0.048> 22.50 39.59 0.8 0.3 3.27 0.01 2 R 0.12 0.01 100 no LB2219 0.005 0.0021 0.043> 22.71 39.99 0.8 0.3 4.00> 0.01 2 R 0.10 0.01 100 no LB2220 0.004 0.00202 0.042> 22.66 39.64 0.8 0.33 4.93> 0.01 2 R 0.11 0 100 no LB2221 0.004 0.0022 0.038> 22.43 39.66 0.8 0.3 3.74> 0.01 1.9 R 0.11 0 10 yes LB2222 0.003 0.0033 0.042> 22.5 39.62 0.8 0.3 3.66> 0.01 2 R 0.18 0 20 yes LB2223 0.002 0.0036 0.041> 22.4 39.78 0.7 0.3 3.65> 0.01 2.00 R 0.27> 0 20 yes LB2234 0.003 0.005 0.007 22.57 39.77 0.8 0.3 3.26 0.01 2.1 R 0.15 0 80 10 no LB2235 0.003 0.0034 0.006 22.56 39.67 0.8 0.3 3.28 0.01 2.1 R 0.12 0 150 12 no LB2236 0.002 0.004 0.006 22.34 39.46 0.8 0.3 3.27 0.01 2 R 0.11 0 30 42 slight LB2317 0.001 0.0025 0.030 22.48 40.09 0.8 0.3 4.21 0.01 2 R 0.16 0 100 5 no LB2318 0.002 0.0036 0.038> 22.76 39.77 0.8 0.3 5.20> 0.01 2.1 R 0.15 0 100 4 no LB2319 0.002( 0.0039 0.043> 22.93> 39.79 0.8 0.3 6.06 0.01 2.2 R 0.12 0 100 3 no LB2321 0.002 0.0051 0.040> 22.56 40.23> 0.7 0.3 6.23 0.01 2.1 R 0.10 0 100 4 no

(37) The effective sum PRE in regard to the corrosion resistance of the Alloy 825 is equal to PRE 33 and is very low compared with other alloys. Table 2 shows the effective sums PRE according to the prior art.

(38) TABLE-US-00002 TABLE 2 Effective sum PRE for various alloys corresponding to the prior art Alloy Ni Fe Cr Mo Others PRE Duplex 2205 5.5 Rest 22 3 0.15 N 37 825 40 31 23 3.2 33 28 31 35 27 3.5 1.3 Cu 38 926 25 Rest 19 6 0.16 N 47

(39) This effective sum and therefore the corrosion resistance can be increased by raising the molybdenum content. PRE=1% Cr+3.3% Mo (Pitting Resistance Equivalent).

(40) Table 3 shows the results of diverse pitting corrosion investigations. The reduced titanium content has no negative influence on the pitting corrosion temperature. The raised molybdenum content has positive effects.

(41) TABLE-US-00003 TABLE 3 Critical pitting corrosion temperature in 6% FeCl.sub.3 + 1% HCl, over 72 hours (ASTM G-48 Method C). T in C. Ni Cr Mo N Ti PRE LB 2316 35 39.2 22.4 3.1 0.04 <0.04 33 LB 2317 40 40.1 22.5 4.2 0.03 <0.04 36 LB 2318 50 39.8 22.8 5.2 0.04 <0.04 40 LB 2319 55 38.8 22.9 6.1 0.04 <0.04 43 LB 2320 50 39 22.1 6.2 0.1 <0.03 43 LB 2321 50 40.2 22.6 6.2 0.04 0.4 43 LB 2322 40 40 23.1 6.3 0.1 0.4 44 Alloy 825Reference 30 40 23 3.2 <0.02 0.8 33

(42) Further corrosion investigations likewise revealed an improvement of the critical crevice corrosion temperatures compared with Alloy 825. These are presented in Table 4.

(43) TABLE-US-00004 TABLE 4 Critical pitting corrosion temperature (CPT) and crevice corrosion temperature (CCT) CPT CCT Alloy in C. in C. Ni Cr Mo V Ti PRE 825* 30 <5 33 PV661 40 15 40 23 3.3 <0.002 0.8 34 PV662 50 20 40 23 5.9 <0.002 <0.002 42 PV663 50 20 39 23 5.8 0.4 <0.002 42

(44) The offset yield strength and the tensile strength can be improved by 15% and 30% cold-working. The associated investigation results of diverse laboratory alloys are listed in the following table.

(45) TABLE-US-00005 TABLE 5 Tension tests at RT A Z Condition Alloy Rp0.2 Rm (%) (%) Solution- 825 304 646 51 annealed Reference 825 Plus (A) 389 754 39 59 369 772 39.5 61 825 Plus (B) 390 765 42.5 62 383 755 40 63 15% cold work 825 670 775 22 71 697 793 19.5 65 685 779 23.5 69 825 Plus (A) 903 973 14.5 51 893 964 13.5 50 943 987 13.5 54 825 Plus (B) 929 974 12.5 56 877 964 12.5 51 887 962 9.5 49 30% cold work 825 852 923 14 63 832 922 13.5 66 842 920 17.5 64 825 Plus (A) 979.0 1071.0 11.5 51.0 970.0 1079.0 8.5 35.0 996.0 1078.0 11.0 46.0 825 Plus (B) 980.0 1078.0 11.5 47.0 980.0 1071.0 11.0 48.0 996.0 1083.0 10.5 48.0

(46) FIGS. 1 and 2 show results of tension tests, on the one hand for the reference alloy 825 and on the other hand for alternative alloys.

(47) Molybdenum has a positive effect on the offset yield strength and the tensile strength. The positive influence of molybdenum is illustrated in FIGS. 3 and 4.

(48) The hot-cracking sensitivity of the Alloy 825, which is an Ni-base alloy, was investigated by means of the PVR test (program-controlled deformation cracking test). The critical crosshead speed V.sub.cr in tension was determined by applying a linearly increasing crosshead speed during TIG welding. The investigation results are illustrated in the following graph. The weldability of the material became better with higher crosshead speed and smaller hot-cracking tendency. The titanium-free, high-molybdenum variants (PV 506 and PV 507) exhibited fewer cracks than the standard alloy (PV 942).

(49) TABLE-US-00006 TABLE 6 (chemical composition in wt %) Heat C Mn Si P S Cr Ni Mo Ti 942 0.006 0.76 0.28 0.012 0.002 22.65 39.42 3.17 0.80 (Prior art) 506 0.01 0.86 0.31 0.005 0.005 23.2 39.0 4.9 0.06 (invention) 507 0.01 0.86 0.31 0.005 0.005 23.2 39.2 5.9 0.06 (invention) Heat V Nb Cu Fe Al Co B N W 942 1.94 R30.5 0.14 0.11 (Prior art) 506 (invention) 0.01 0.13 2.4 28.8 0.14 0.28 0.003 0.02 0.10 507 (invention) 0.01 0.13 2.4 28.7 0.14 0.28 0.003 0.02 0.11

(50) The task is also accomplished by a process for the manufacture of an alloy that has a composition according to one of the objective claims, wherein a) the alloy is melted openly in the continuous or ingot casting, b) to eliminate the segregations caused by the increased molybdenum content, a homogenizing annealing of the produced blooms/billets is performed at 1150-1250 C. for 15 to 25 h, wherein c) the homogenizing annealing is performed in particular following a first hot forming.

(51) Optionally, the alloy may also be produced by ESR/VAR remelting.

(52) The alloy according to the invention will preferably be used as a structural part in the oil and gas industry.

(53) Product forms suitable for this purpose are sheets, strips, pipes (longitudinally welded and seamless), bars or forgings.

(54) Table 7 compares Alloy 825 (standard) with two alloys according to the invention.

(55) TABLE-US-00007 TABLE 7 (chemical composition in wt %) Heat C Mn Si P S Cr Ni Mo Ti PV 661 0.006 0.75 0.28 0.003 22.9 39.9 3.32 0.79 (Prior art) PV 662 0.0066 0.75 0.26 0.003 0.0011 22.9 39.7 5.86 0.002 (invention) PV 663 0.0071 0.77 0.28 0.004 0.0013 22.7 39.4 5.76 <0.002 (invention) Heat V Nb Cu Fe Al Co B N Mg PV 661 <0.002 0.004 1.81 29.8 0.148 0.01 0.003 0.0011 0.012 (Prior art) PV 662 <0.002 <0.002 1.80 28.4 0.142 0.009 0.003 0.0016 0.01 (invention) PV 663 0.37 0.004 1.81 28.5 0.155 0.005 0.003 0.0015 0.01 (invention)