Manufacturing method for bumper beam of vehicle

Abstract

A manufacturing method for a bumper beam of a vehicle may include pipe making, producing a circular pipe by pipe molding a steel plate having a predetermined thickness between first and second molding rolls, heating the circular pipe to a set temperature in a heating furnace, pressurizing and molding the circular pipe heated in the heating furnace and having flexibility, while inserting the circular pipe between an upper mold and a lower mold to form a molding beam, and thereafter, rapidly cooling the molding beam to form the molding beam into a high-strength molding beam, and curvature-molding the high-strength molding beam at a predetermined curvature through a curvature molding machine.

Claims

1. A manufacturing method for a bumper beam of a vehicle, comprising: producing a circular pipe by pipe molding a steel plate having a predetermined thickness between first and second molding rolls; heating the circular pipe to a predetermined temperature in a heating furnace; pressurizing and molding the circular pipe heated in the heating furnace and having flexibility, while inserting the circular pipe between an upper mold and a lower mold to form a molding beam, and thereafter, cooling the molding beam to form the molding beam into a high-strength molding beam; and curvature-molding the high-strength molding beam at a predetermined curvature through a curvature molding machine.

2. The manufacturing method of claim 1, wherein the steel plate comprises a cold rolled steel plate having a thickness of 1 mm.

3. The manufacturing method of claim 2, wherein the cold rolled steel plate has a tensile strength of 550 MPa.

4. The manufacturing method of claim 1, wherein the heating furnace comprises a high-frequency heating furnace.

5. The manufacturing method of claim 1, wherein the heating furnace comprises an electric heating furnace.

6. The manufacturing method of claim 1, wherein the predetermined temperature is 900 C.

7. The manufacturing method of claim 1, wherein the molding beam comprises a straight beam material in which a lower surface of the molding beam is formed as a flat horizontal surface by the lower mold, and an upper surface of the molding beam is molded into a concave portion to contact the lower surface at a side by the upper mold to form at least two closed cross-sections between the lower surface and the upper surface.

8. The manufacturing method of claim 7, wherein in the high-strength molding beam, the lower surface of the high-strength molding beam is disposed on an edge of a curvature radius of the high-strength molding beam to be curvature-molded.

9. The manufacturing method of claim 1, wherein the high-strength molding beam has a tensile strength of 1800 MPa.

10. A manufacturing method for a bumper beam of a vehicle, comprising: producing a circular pipe by pipe molding a cold rolled steel plate having a thickness of 1 mm between a plurality of molding rolls; heating the circular pipe at 900 C. or higher in a high-frequency heating furnace; pressurizing and molding the circular pipe heated in the high-frequency heating furnace and having flexibility, while inputting the circular pipe between an upper mold and a lower mold to produce a molding beam comprising of a straight beam material in which a lower surface is formed as a flat horizontal surface by the lower mold, and an upper surface is molded to a concave portion to contact the lower surface at a side by the upper mold and form at least two closed cross-section between the lower surface and the upper surface, and thereafter, cooling the molding beam to produce a high-strength molding beam; and curvature-molding the high-strength molding beam at a predetermined curvature through a curvature molding machine.

11. The manufacturing method of claim 10, wherein the cold rolled steel plate has a tensile strength of 550 MPa.

12. The manufacturing method of claim 10, wherein in the high-strength molding beam, the lower surface of the high-strength molding beam is disposed on an edge of a curvature radius of the high-strength molding beam to be curvature-molded.

13. The manufacturing method of claim 10, wherein the high-strength molding beam has a tensile strength of 1800 MPa.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a conceptual view of a general roll forming system and a process for each step thereof.

(2) FIG. 2 is a side configuration diagram of a general round bender.

(3) FIG. 3 is a perspective view of one example of a buffer beam produced through the general roll forming system and process.

(4) FIG. 4 is a conceptual view of a step-by-step process of a manufacturing method for a bumper beam of a vehicle according to various embodiments of the present invention.

(5) FIG. 5 is a cross-sectional view of a bumper beam manufactured by the manufacturing method for a bumper beam of a vehicle according to various embodiments of the present invention.

(6) FIG. 6 is a perspective view of the bumper beam manufactured by the manufacturing method for a bumper beam of a vehicle according to various embodiments of the present invention.

(7) It should be understood that the appended drawings are not necessarily to scale, presenting a somewhat simplified representation of various features illustrative of the basic principles of the invention. The specific design features of the present invention as disclosed herein, including, for example, specific dimensions, orientations, locations, and shapes will be determined in part by the particular intended application and use environment.

DETAILED DESCRIPTION

(8) Reference will now be made in detail to various embodiments of the present invention(s), examples of which are illustrated in the accompanying drawings and described below. While the invention(s) will be described in conjunction with exemplary embodiments, it will be understood that the present description is not intended to limit the invention(s) to those exemplary embodiments. On the contrary, the invention(s) is/are intended to cover not only the exemplary embodiments, but also various alternatives, modifications, equivalents and other embodiments, which may be included within the spirit and scope of the invention as defined by the appended claims.

(9) FIG. 4 is a conceptual view of step-by-step process of a manufacturing method for a bumper beam of a vehicle according to various embodiments of the present invention, FIG. 5 is a cross-sectional view of a bumper beam manufactured by the manufacturing method for a bumper beam of a vehicle according to various embodiments of the present invention, and FIG. 6 is a perspective view of the bumper beam manufactured by the manufacturing method for a bumper beam of a vehicle according to various embodiments of the present invention.

(10) Referring to FIG. 4, the manufacturing method for molding the bumper beam for the vehicle according to various embodiments of the present invention includes a pipe making process S10, a heating process S20, a hot stamping process S30, and a bending process S40.

(11) First, in the pipe making process S10, a steel plate P having a predetermined thickness is pipe-molded between both molding rolls R1 and R2 to produce a circular pipe PP.

(12) In this case, the steel plate P may be formed of a cold-rolled steel plate having a thickness of 1 mm, but is not particularly limited thereto and a boron steel plate to which boron is added may be adopted.

(13) Herein, a tensile strength of the cold-rolled steel plate may be 550 MPa, but is not particularly limited thereto.

(14) In addition, in the heating process S20 performed subsequently to the pipe making process S10, the circular pipe PP is heated up to a set temperature in a heating furnace HT.

(15) In this case, the heating furnace HT may be a high-frequency heating furnace, but is not particularly limited thereto. For this purpose, a heating furnace HT capable of heating the circular pipe PP to the set temperature within a predetermined time may be adopted, and the heating furnace may be an electric heating furnace.

(16) Herein, the set temperature is preferably 900 C. and the set temperature may be applied differently depending on the material, but in general, in the case of a hot stamping material, unlike the conventional high-strength steel, a steel plate of a ferrite structure having a tensile strength of approximately 500 to 800 MPa before molding is made into austenite and thereafter, high-temperature molded at a high temperature of 900 C. or higher and thereafter, rapidly cooled to be obtained as a martensitic structure having a high tensile strength of approximately 1300 to 1800 MPa.

(17) In addition, in the hot stamping process S30, while the circular pipe PP having flexibility while being heated in the heating furnace HT is input between an upper mold M1 and a lower mold M2, the circular pipe PP is pressurized and molded into a molding beam and thereafter, the molding beam B is rapidly cooled to produce a high-strength molding beam B.

(18) Herein, the upper mold M1 and the lower mold M2 may be formed of general hot stamping molds and referring to FIG. 5, a lower surface F1 of the molding beam B is formed by a flat horizontal surface by the lower mold M2 and an upper surface F2 is molded into a concave portion T so as to contact the lower surface F1 at one side by the upper mold M1, and as a result, the molding beam B is molded to a straight type beam material forming at least two closed cross-sections SP1 and SP2 between the lower surface F1 and the upper surface F2.

(19) In addition, in the bending process S40, the high-strength molding beam B is curvature-molded at a predetermined curvature through a curvature molding machine having a plurality of bending rolls BR.

(20) In this case, referring to FIG. 6, the lower surface F1 is disposed on an exterior of a curvature radius and the high-strength molding beam B is thus curvature-molded and a final high-strength molding beam B produced as such may be applied as a bumper beam BB having a tensile strength of 1800 MPa.

(21) Accordingly, according to the manufacturing method for the bumper beam of the vehicle of the present invention, the circular pipe PP produced by the pipe making molding is heated at the high temperature of 900 C. in the heating furnace HT in the pipe making process S10 and thereafter, molded to the molding beam B having at least two closed cross-sections SP1 and SP2 in the hot stamping mold to secure the strength by the rapid cooling and thereafter, curvature-molded to have a predetermined curvature through the curvature molding machine to be manufactured into a high-strength light vehicular bumper beam BB.

(22) In this case, the circular pipe PP by the pipe making molding is applied as the material for the bumper beam BB and the welded portion welding both ends of the existing steel plate material may be excluded. Therefore, an additional welding process may not be performed, and as a result, the process is simplified to reduce the cost.

(23) While the concave portion T connecting the lower surface F1 and the upper surface F2 of the molding beam B contacts the lower surface F1, the molding beam B is molded to form two closed cross-sections SP1 and SP2 and the thickness of the steel plate which becomes the material may be reduced by 10% or more as compared with the related art due to the advantage of the structural rigidity of the circular pipe PP, and as a result, a capability of withstanding collision can be improved and a weight of the bumper beam BB can be reduced.

(24) In addition, a direction of stress concentrated on the curvature radius direction inner cross-section can be distributed to the concave portion T in the curvature molding by removing the existing welded portion to prevent the non-uniform dent from being generated due to the heel tap.

(25) For convenience in explanation and accurate definition in the appended claims, the terms upper or lower, inner or outer and etc. are used to describe features of the exemplary embodiments with reference to the positions of such features as displayed in the figures.

(26) The foregoing descriptions of specific exemplary embodiments of the present invention have been presented for purposes of illustration and description. They are not intended to be exhaustive or to limit the invention to the precise forms disclosed, and obviously many modifications and variations are possible in light of the above teachings. The exemplary embodiments were chosen and described in order to explain certain principles of the invention and their practical application, to thereby enable others skilled in the art to make and utilize various exemplary embodiments of the present invention, as well as various alternatives and modifications thereof. It is intended that the scope of the invention be defined by the Claims appended hereto and their equivalents.