Ammonia removal in freshwater and saltwater systems

Abstract

An ammonia adsorption product is described which may be used for fresh caught fish and bait. The product may comprise functionalized tectosilicate compound and a buffer. High concentrations of ammonia produced by fish waste can be lethal, even though oxygen availability is rich enough to keep fish breathing. The product is a user-friendly, sustainable, affordable product which is able to extend the life of the fish by safely removing ammonia by an ion-exchange mechanism. This product can convert toxic ammonia into ammonium and uptake ammonium by releasing sodium ions in the water.

Claims

1. A method for producing an ammonia removal agent for water environments, comprising: obtaining a tectosilicate compound wherein the tectosilicate compound is chabazite; functionalizing the tectosilicate compound, comprising soaking the tectosilicate compound in a synthetic freshwater solution for 24 hours and removing ions from the tectosilicate compound that have a lower ion selectivity than ammonium ions wherein the synthetic freshwater solution consists of: 0.075 g/L of sodium; 0.00312 g/L of potassium; 0.024 g/L of magnesium; 0.193 g/L of chloride 0.043 g/L of calcium; 0.0048 g/L of bicarbonate; 0.096 g/L of sulfate; and 0.310 g/L of alkalinity; washing the functionalized tectosilicate compound in deionized water; and drying the functionalized tectosilicate compound.

2. The method of claim 1, further comprising washing the tectosilicate compound in deionized water and drying the tectosilicate compound prior to soaking the tectosilicate compound in the synthetic freshwater solution.

3. The method of claim 2, wherein the tectosilicate compound is washed using a shaker table for 24 hours to remove small particles.

4. The method of claim 1, wherein removing ions from the tectosilicate compound comprises removing sodium ions from the tectosilicate compound.

5. The method of claim 4, wherein functionalizing the tectosilicate compound reduces a percentage of sodium ionically bound to the compound by at least 50 percent.

6. The method of claim 1, wherein the functionalized tectosilicate compound is dried in an oven at 110 C. for 5 hours.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) For a fuller understanding of the invention, reference should be made to the following detailed description, taken in connection with the accompanying drawings, in which:

(2) FIG. 1 is a graph of ammonia buildup in a closed aquatic system for a variety of fish.

(3) FIG. 2 is a graph of the composition of chabazite before and after pretreatment.

(4) FIG. 3 is an x-ray diffraction plot of chabazite pretreated using freshwater.

(5) FIG. 4 is an x-ray diffraction plot of chabazite pretreated using 2M NaCl.

(6) FIG. 5A is a graph of the ammonium adsorption nonlinear isotherm in freshwater

(7) FIG. 5B is a graph of the ammonium adsorption nonlinear isotherm in saltwater

(8) FIG. 6 illustrates the relationship of ammonia to ammonium concentration as a function of pH.

(9) FIG. 7 is a graph of ammonia concentration for an in-vitro experiment.

(10) FIG. 8 is a flowchart of an exemplary method for producing an ammonia removal agent for water environments.

(11) FIG. 9 is a flowchart of an exemplary method for controlling an ammonia level in a water environment.

DETAILED DESCRIPTION OF THE INVENTION

(12) Caught fish are often kept alive by placing the fish in a bucket, livewell, or other container or closed system. In addition, live bait is often used for fishing and must be kept in a similar container prior to use. Because the volume of water is limited in these close systems, an aeration pump is often installed to replenish dissolved oxygen levels in the water. While aeration systems may maintain oxygen levels in the water to sustain the fish, other contaminates may build up in the closed system and poison the fish. For example, waste products discharged by the fish may increase ammonia concentration in the water and may build to levels that will kill the fish despite an adequate level of dissolved oxygen in the water.

(13) Various embodiments may comprise one or more treated, functionalized zeolite compounds with a high ammonium absorption capacity. Zeolites are microporous mineral compounds commercially used as adsorbents. The porous structure can accommodate a wide variety of cations such as Nat, Ca.sup.2+, K.sup.+, and Mg.sup.2+. In addition, once these cations are adsorbed by the zeolite, they can be exchanged for other cations when the zeolite is in contact with a solution containing the other cations. While there are a large number of available zeolites, various embodiments comprise chabazite because it is inexpensive, readily available from many areas of the world, and has a cation-exchange capacity. Chabazite (available from St. Cloud Mining Company) is a tectosilicate mineral with the formula (Ca,Na.sub.2,K.sub.2,Mg)Al.sub.2Si.sub.4O.sub.12.6H.sub.2O.

(14) The ion selectivity series for chabazite is:
Ti.sup.+>K.sup.+>Rb.sup.+>NH.sub.4.sup.+>Pb.sup.2+>Na.sup.+>Ba.sup.2+>Sr.sup.2+>Ca.sup.2+>Li.sup.+

(15) Thus, chabazite that has been functionalized with a common and readily available ion such as Na.sup.+ will tend to give up the Na.sup.+ ion in favor of NH.sub.4.sup.+ (ammonium). This property can be exploited to use Na.sup.+ functionalized chabazite to selectively remove ammonium from water.

(16) Experimentation was conducted to determine the ammonia accumulation rate over time for closed systems of various volumes containing live fish in both freshwater and saltwater. These tests involved bass with a commercial water conditioner, bass without the conditioner, pinfish and blowfish, and shrimp. Ammonia concentration was determined using the salicylate method (HACH Method 10031) and the results are shown in FIG. 1. These tests indicated an ammonia accumulation rate of 0.210.03 mg HN.sub.3N/specimen/hr for freshwater fish and 0.810.17 mg HN.sub.3N/specimen/hr for saltwater fish.

(17) Next, a procedure was developed to treat and functionalize chabazite pellets to maximize ammonium adsorption capacity. Chabzite pellets having a size range of 1-2 mm were washed in deionized (DI) water using a shaker table for 24 hours to remove small particles. The washed pellets were then oven dried at 110 C.

(18) Two pretreatment methods were used to develop products specific to freshwater and saltwater uses. For freshwater uses, the washed and dried chabazite was soaked in freshwater/synthetic freshwater for 24 hours to remove sodium ions, then washed with DI water and oven dried at 110 C. for 5 hours. The composition of the synthetic freshwater is provided in Table 1. For saltwater uses, the washed and dried chabazite was soaked in a 2M NaCl solution for 24 hours to uptake sodium ions, then washed with DI water and oven dried at 110 C. for 5 hours.

(19) TABLE-US-00001 TABLE 1 Synthetic Freshwater Composition Ion Freshwater (g/L) Sodium (Na.sup.+) 0.075 Potassium (K.sup.+) 0.00312 Magnesium (Mg.sup.2+) 0.024 Chloride (Cl.sup.) 0.193 Calcium (Ca.sup.2+) 0.043 Bicarbonate (HCO.sub.3.sup.) 0.0048 Sulfate (SO.sub.4.sup.2) 0.096 Alkalinity 0.310

(20) FIG. 2 shows the chemical composition of the chabazite before and after treatment. The Na.sup.+ composition decreased sharply for the treated freshwater chabazite (CF in FIG. 2) and a less sharp increase in Na.sup.+ composition for the saltwater chabazite (CS in FIG. 2). Approximately half of the Ca.sup.2+ ions were released from the freshwater chabazite and essentially all Ca.sup.2+ was released from the saltwater chabazite. There was no appreciable change in the K.sup.+ and Mg.sup.2+ composition.

(21) The functionalized chabazite was then coated with an environmentally friendly blue dye (PSP0002 Lake and Pond Dye available from Outdoor Water Solutions).

(22) FIGS. 3 and 4 illustrate that the crystalline structure of the freshwater chabazite and the saltwater chabazite, respectively, are unchanged after treatment. The additional peaks evident in FIG. 4 are due to the presence of the blue dye.

(23) The ammonium adsorption isotherm using the Langmuir and Freundlich models were then determined for both the freshwater and saltwater chabazite. This testing was performed using the synthetic freshwater characterized in Table 1 and synthetic saltwater (available from Instant Ocean) characterized in Table 2. The ammonium adsorption isotherm results are presented in FIGS. 5A and 5B (nonlinear isotherm) and Table 3.

(24) TABLE-US-00002 TABLE 2 Synthetic Saltwater Composition Ion Saltwater (g/L).sup.7 Sodium (Na.sup.+) 10.780 Potassium (K.sup.+) 0.42 Magnesium (Mg.sup.2+) 1.32 Chloride (Cl.sup.) 19.290 Calcium (Ca.sup.2+) 0.400 Bicarbonate (HCO.sub.3.sup.) 0.200 Sulfate (SO.sub.4.sup.2) 2.66 Alkalinity 0.241

(25) TABLE-US-00003 TABLE 3 Isotherm Constants for Ammonium Adsorption in Both Freshwater and Saltwater Langmuir q.sub.o b Freundlich (mg/g) (L/mg) R.sup.2 K 1/n R.sup.2 Linear Freshwater 10.83 0.07 0.99 0.85 0.63 0.98 Saltwater 38.91 0.001 0.024 0.027 1.038 0.92 Non- Freshwater 11.10 0.06 0.99 1.10 0.54 0.99 linear Saltwater 7.80 0.006 0.92 0.11 0.72 0.90

(26) Proper pH control may be used to affect the ammonia chemistry according to the equation NH.sub.3+H.sup.+.Math.NH.sub.4.sup.++H.sub.2O. The higher the pH, the more the equilibrium moves to the left, favoring ammonia formation. The lower the pH, the more the equilibrium is shifted to the right, favoring ammonium formation. As shown in FIG. 6, a pH of about 7 favors essentially 100 percent formation of ammonium. To achieve a pH of 7, a buffer comprising Na.sub.2HPO.sub.4 and NaH.sub.2PO.sub.4 were added to both the freshwater and saltwater chabazite.

(27) Product preparation steps are summarized as follows: Freshwater Chabazite 1. Chabazite (30 g) pretreated by synthetic freshwater at for 24 hrs (200 mL synthetic freshwater and 1 mL 5 g/L blue dye solution). 2. Wash by DI water and dry in the oven at 110 C. for 5 hours. 3. Mix with 0.8 Na.sub.2HPO.sub.4 and 0.3 g NaH.sub.2PO.sub.4. 4. Pack in a porous bag (30 g per bag). Saltwater Chabazite 1. Chabazite (30 g) pretreated by 2M NaCl for 24 hrs (200 mL 2M NaCl and 1 mL 5 g/L blue dye solution). 2. Wash by DI water and dry in the oven at 110 C. for 5 hours. 3. Mix with 0.8 Na.sub.2HPO.sub.4 and 0.3 g NaH.sub.2PO.sub.4. 4. Pack in a porous bag (30 g per bag).

(28) Using the above preparation steps, porous containers of the freshwater chabazite were prepared and an in-vitro test was conducted using synthetic freshwater. A high-performance ammonia ion selective electrode was used to measure ammonia concentration in a container with the freshwater chabazite in a porous bag and a control. Aeration was used in both. The experimental results are shown in FIG. 7. For the experimental specimen, k.sub.experimental=0.250.02 mg NH.sub.3N/L/h. For the control specimen, k.sub.control=0.470.01 mg NH.sub.3N/L/h.

(29) In-vivo tests were then performed using live fish in an experimental container with the prepared chabazite and live fish in a container without chabazite as a control. Aeration was used in both. Prepared chabazite was added into water every three hours. Testing was performed for both freshwater and saltwater systems. In freshwater, functionalized chabazite removed 18.94.8% of NH.sub.3N within 24 hours. In seawater, functionalized chabazite was ineffective.

(30) In various embodiments, spent chabazite may be regenerated by removing the adsorbed ammonium ions and replacing them with sodium ions (or other suitable ions).

(31) Table 4 presents the cost of materials for the chabazite system. The total cost compares favorably to commercial water conditioners which range from $4-10.

(32) TABLE-US-00004 TABLE 4 Material Costs for Chabazite, Dye, and Buffer Component Cost/Day Chabazite $1.48 Dye $0.77 Buffer $0.13 Bag $0.64 Other $0.50 TOTAL $3.53

DEFINITION OF CLAIM TERMS

(33) Ammonium: a positively charged polyatomic ion with the chemical formula NH.sub.4.sup.+. It may be formed by the protonation of ammonia (NH.sub.3).

(34) Buffer: an aqueous solution consisting of a mixture of a weak acid and its conjugate base, or vice versa. Its pH changes very little when a small or moderate amount of strong acid or base is added to it and thus it may be used to prevent changes in the pH of a solution.

(35) Chabazite: a tectosilicate mineral with the formula (Ca,Na.sub.2,K.sub.2,Mg)Al.sub.2Si.sub.4O.sub.12.6H.sub.2O.

(36) Functionalize: to change surface properties of a material by adding or removing functional groups.

(37) Ion selectivity: the affinity a compound shows for reacting with different ions. An ion with a higher ion selectivity will tend to displace an ion in the compound that has a lower ion selectivity.

(38) Tectosilicate compound: a silicates compound having a three-dimensional framework of silicate tetrahedra with SiO.sub.2 or a 1:2 ratio.

REFERENCES

(39) [1] D. W. Breck, Zeolite Molecular Sieves: Structure, Chemistry, and Use. Wiley, New York. 1974. [2] M. Orr, What Does That Number Really Mean? Aquarium Water Testing Methods, Results and Interpretation, Sea Scope, 2008, vol. 24, pp 1-2. [3] R. M. Durborow, D. M. Crosby and M. W. Brunso, Ammonia in Fish Ponds, Southern Regional Aquaculture Center, 1992, No. 463. [4] S. S. Verma, Wonders of Zeolite, Chemical Business, 2012, 26(2), pp. 10-12.

(40) It will be seen that the advantages set forth above, and those made apparent from the foregoing description, are efficiently attained and since certain changes may be made in the above construction without departing from the scope of the invention, it is intended that all matters contained in the foregoing description or shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense.

(41) It is also to be understood that the following claims are intended to cover all of the generic and specific features of the invention herein described, and all statements of the scope of the invention which, as a matter of language, might be said to fall therebetween.