Concrete mix design and method for realizing dam or other massive structure by using the concrete mix design

Abstract

A concrete mix, including: cementitious content between 25 and 200 kg/m.sup.3; fly ash content between 25 and 175 kg/m.sup.3; dirty sand with fine aggregates between 3% and 20%; water content between 150 I/m.sup.3 and 250 l/m.sup.3; and a chemical admixture comprising one or more components selected from the following: an acrylic, formaldehyde-free polymer-based admixture, modified in aqueous solution; a surfactant admixture configured to entrain micro air bubbles in concrete; and an organic polymer comprising hydrophilic groups for increasing the viscosity of the mixture.

Claims

1. A method for realizing a dam or other massive structure, the method comprising the steps of: batching of massive self-compacting concrete (MSCC) comprising a concrete mix comprising: cementitious content comprising fly ash, the cementitious content less than 250 kg/m.sup.3; dirty sand comprising between 3% and 15% fine aggregates; water content between 150 l/m.sup.3 and 250 l/m.sup.3; and a chemical admixture comprising one or more components selected from the following: an acrylic, formaldehyde-free polymer-based admixture, modified in aqueous solution; a surfactant admixture configured to entrain micro air bubbles in concrete; and an organic polymer comprising hydrophilic groups for increasing the viscosity of the mixture; spreading the MSCC by placing it in one continuous lift across the entire surface of the dam or other massive structure; and waiting for self-compacting of the MSCC.

2. The method according to claim 1, wherein spreading the MSCC is realized by pumping the MSCC.

3. The method according to claim 1, wherein spreading the MSCC is realized without external vibration of the concrete.

4. The method according to claim 1, wherein the chemical admixture comprises all of the following components: an acrylic, formaldehyde-free polymer-based admixture, modified in aqueous solution; a surfactant admixture configured to entrain micro air bubbles in concrete; and an organic polymer comprising hydrophilic groups for increasing the viscosity of the mixture.

5. The method according to claim 1, wherein the acrylic formaldehyde-free polymer-based admixture has a density of 1.07 g/m.sup.3.

6. The method according to claim 1, wherein the acrylic formaldehyde-free polymer-based admixture has a dosage between 3 liter/m.sup.3 and 4 liter/m.sup.3 of cementitious content.

7. The method according to claim 1, wherein the acrylic formaldehyde-free polymer-based admixture has a dosage between 2% and 3% liter/m.sup.3 of the volume of the cementitious content.

8. The method according to claim 1, wherein the surfactant admixture has a density of 1.005 g/m.sup.3.

9. The method according to claim 1, wherein the surfactant admixture has a dosage between 0.7 liter/m.sup.3 and 1 liter/m.sup.3 of cementitious content.

10. The method according to claim 1, wherein the surfactant admixture has a dosage between 0.5% liter/m.sup.3 and 0.7% liter/m.sup.3 of the volume of the cementitious content.

11. The method according to claim 1, wherein the organic polymer admixture has a density of 1.022 g/m.sup.3.

12. The method according to claim 1, wherein the organic polymer admixture has a dosage between 4 liter/m.sup.3 and 5 liter/m.sup.3 of cementitious content.

13. The method according to claim 1, wherein the organic polymer admixture has a dosage between 2% liter/m.sup.3 and 5% liter/m.sup.3 of the volume of the cementitious content.

14. The method according to claim 1, wherein the concrete mix is self levelling and self compacting.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) Additional features and advantages of the present invention will become more evident from the approximate and thus non-limiting description of a preferred but non-exclusive embodiment of a concrete mix design and a method of placement for realizing dam or other massive structure by using the concrete mix design, as illustrated in the appended drawings, in which:

(2) FIG. 1a illustrates a Roller compacting concrete (RCC) method used for realizing a dam in the known prior art;

(3) FIG. 1b illustrates a Massive Self compacting concrete (MSCC) method used for realizing a dam according to a first embodiment of the present invention;

(4) FIG. 1c illustrates a Massive Self compacting concrete (MSCC) method used for realizing a dam according to a second embodiment of the present invention;

(5) FIGS. 2a, 2b illustrates a table and a graph of the sieve analysis composing the mix design;

(6) FIGS. 3a, 3b, 3c, 3d illustrates a table and a graph and a photo of the mix design analysis.

(7) With reference to the drawings, they serve solely to illustrate embodiments of the invention with the aim of better clarifying, in combination with the description, the inventive principles of the invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION

(8) The present invention refers to a concrete mix design and method for realizing dam 100 or other massive structure by using Self-compacting/Self-consolidating Concrete 101, particularly mass structural concrete.

(9) In particular, the specific concrete below described for the present invention is a massive self levelling concrete 101 (MSCC) which is different from concrete used for an known SCC.

(10) There have been laboratory investigations to determine the feasibility of developing a normal weight, Self-compacting/Self-consolidating, portland cement based concrete mix design. It is envisioned that the mix design of the present invention has highly modified dosages (with respect to conventional Roller Compacted Concrete) of various admixes to enable the ability to flow freely and self-compact and thought to be outside of presently known building codes and practices.

(11) The massive self-compacting/self-leveling concrete 101 is being developed for use in mass and conventional concrete structures, both reinforced and unreinforced, to allow for little or no internal or external consolidation effort. Typical applications include, but are not limited to, gravity dams 100, arch dams 100, foundation slabs, runways, bridge abutments and other members, loch walls, ballast blocks, and other concrete structures.

(12) The concrete mix design provide that: Slump and cement content are related, mainly by water/cement ration (w/c), but also with the total amount of cement (and/or fly ash) and other variables. Slump is also effected by the gradation of the aggregate, the overall gradation as well as the amount of very fine material at the bottom end of the gradation. At the finer end of the gradation (minus #200 ASTM Sieve, minus 75 micron) the material can start to act like cement/fly ash in terms of influencing slump, but can add or subtract, so it gets fairly tricky, fairly quick. Sometimes the same material (minus 75 micron) can also effect the hardened properties (meaning it sometimes contributes to the strength, although this is again tricky). The very fine material in the aggregate can also effect the w/c that will influence the hardened properties (Strength, as well as others). Addition of chemical admixtures. Cement content, w/c, and other properties also effect the Modulus of Elasticity, an important hardened property.

(13) In particular, the mix design depends on a heavily influenced mix in terms of chemical admixtures to take advantage of advances in the industry.

(14) It is used a lower cement/fly ash content, for many reasons, some of which are heat of hydration (trying to reduce), as well as economy, as well as shrinkage.

(15) Further, it is using a dirty sand. This means that there is more fine material at the bottom end of the gradation that would be normally used for traditional structural or mass concrete.

(16) Below is described an example of realizing the concrete design mix: The cementitious (Cement+Fly Ash) would preferably be in the 250 kg minus range, ideally 200 kg minus, per m3 (low cementitious content). This compares to closer to circa 300 (and greater) kg for regular structural concrete. The fines content (minus 75 micron sieve size) would be significantly more that would be allowed for normal structural concrete. ASTM C33 sets a limit on passing the 75 micron sieve for fine aggregate to be 0 to 3%, up to 5% in some instances depending on the concrete use, and up to 7% for rock type and concrete use. For coarse aggregates the limit is basically 0, as there should be no passing the 75 micron in the coarse aggregate, although it is not uncommon to have a %1 or some fraction. We are looking to use a combined gradation of greater than %10, and possibly up to %15. This puts us in a different category than normal I believe.

(17) Water content of the mix design is comprised between 150 l/m.sup.3 and 250 l/m.sup.3 and preferably 200 l/m.sup.3.

(18) Regarding the chemical admixtures, they are showed and indicated in the table represented in FIG. 3a.

(19) In detail, chemical admixtures comprising one or more components, preferably all these components, selected between the following list: an acrylic, formaldehyde-free polymer-based admixture, modified in aqueous solution (Dynamon PW by MAPEI?); a surfactant admixture configured to entrain micro air bubbles in concrete (Mapeair AE 20 by MAPEI?); an organic polymer comprising hydrophilic groups for increasing the viscosity of the mixture (Viscofluid SCC/10 by MAPEI?).

(20) The acrylic formaldehyde-free polymer-based admixture has a density of 1.07 g/m.sup.3, a dosage comprised between 3 liter/m.sup.3 and 4 liter/m.sup.3 of cementitious content and a dosage comprised between 2% and 3% liter/m.sup.3 of the volume of the cementitious content.

(21) The surfactant admixture has a density of 1,005 g/m.sup.3, a dosage comprised between 0.7 liter/m.sup.3 and 1 liter/m.sup.3 of cementitious content and a dosage comprised between 0.5% liter/m.sup.3 and 0.7% liter/m.sup.3 of the volume of the cementitious content.

(22) The organic polymer admixture has a density of 1,022 g/m.sup.3, a dosage comprised between 4 liter/m.sup.3 and 5 liter/m.sup.3 of cementitious content and a dosage comprised between 2% liter/m.sup.3 and 5% liter/m.sup.3 of the volume of the cementitious content.

(23) Testing Standards:

(24) ASTM standards are the main referenced standards, although equivalent internationally recognized standards may be substituted.

(25) Initial targets, fresh properties: Slumpno lower limit on slump, upper limit to be evaluated against the followability and Self-consolidation, tested by ASTM C143 and ASTM C230. Initial/Final Set TimeNo requirements for initial or final set time will be established in the initial trials, but will be tested in accordance with ASTM C403. TemperatureNo requirements for temperature shall be established in the initial trials, provide the mix is not subject to hot or cold placing temperature conditions as described by ACI, tested by ASTM C1064. Air content5%, +/?1%, by ASTM C231. Although lesser % of air contents are also to be considered.
Initial Targets, Hardened Properties, Mechanical: Unit weightNo target, but will be tested according to ASTM C138 Compressive strengthStrength targets will be between 10 and +/?30 Mpa at 365 days, ASTM C39 and ASTM C31 Tensile strengthNo target, but will be tested, ASTM C496 Modulus of ElasticityNo target, but will be tested, ASTM 469 Poisson ratioNo target, but will be tested, ASTM 469
Initial Targets, Hardened Properties, Thermal:

(26) (no thermal properties will be tested until satisfactory fresh and hardened mechanical properties are established. However, the following are test envisioned for the thermal properties testing: Adiabatic temperature rise Diffusivity Coefficient of thermal expansion Specific heat of concrete
Initial Targets, Materials: Portland CementType I/II, ASTM C150 Fly AshType F and C, ASTM C618 Mineral filler, both natural and manufactured, to be evaluated as a fly ash replacement WaterClean and potable, including: Water Soluble Chloride, ASTM C1218 AggregatesASTM C33, including: C127 Standard Test Method for Relative Density (Specific Gravity) and Absorption of Coarse Aggregate C128 Standard Test Method for Relative Density (Specific Gravity) and Absorption of Coarse Aggregate Sand equivalencyASTM D2419 Flakiness and ElongationBS 812 AdmixturesTo be determined in first stage of initial trials, generally conforming to the following: ASTM C494 ASTM C260
Initial Targets, Coarse Aggregate Grading

(27) TABLE-US-00001 Sieve Size Percentage passing indicated sieve size (mm) 20-40 10-20 4.75-10 63 100 40 85-100 100 20 0-20 85-100 12.5 100 10 0-5 0-20 85-100 4.75 0 0-5 0-20 2.36 0-5
Initial Targets, Fine Aggregate Grading

(28) TABLE-US-00002 Sieve Size Percentage passing indicated sieve size (mm) Sand 9.5 100 4.75 95-100 2.36 80-95 1.18 65-90 0.60 40-70 0.300 15-35 0.150 10-25 0.075 8-18 FM 3.5-2.3
Initial Targets, Mix Proportions:

(29) Mix proportions will be determined after initial review of proposed admixture types and dosages, as well as actual determination of: Aggregate specific gravities Aggregate absorptions Aggregate moisture contents
Initial Additional Testing, where Deemed Required: C29/C29M Test Method for Bulk Density (Unit Weight) and Voids in Aggregate C31 Standard Practice for Making and Curing Concrete Test Specimens in the Field C33 Standard Specification for Concrete Aggregates C39 Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens C40 Test Method for Organic Impurities in Fine Aggregates for Concrete C87 Test Method for Effect of Organic Impurities in Fine Aggregate on Strength of Mortar C88 Test Method for Soundness of Aggregates by Use of Sodium Sulfate or Magnesium Sulfate C94 Standard Specification for Ready-Mixed Concrete C117 Test Method for Materials Finer than 75-?m (No. 200) Sieve in Mineral Aggregates by Washing C123 Test Method for Lightweight Particles in Aggregate C125 Terminology Relating to Concrete and Concrete Aggregates C127 Standard Test Method for Relative Density (Specific Gravity) and Absorption of Coarse Aggregate C128 Standard Test Method for Relative Density (Specific Gravity) and Absorption of Fine Aggregate C131 Test Method for Resistance to Degradation of Small-Size Coarse Aggregate by Abrasion and Impact in the Los Angeles Machine C136 Test Method for Sieve Analysis of Fine and Coarse Aggregates C138 Standard Test Method for Density (Unit Weight), Yield, and Air Content (Gravimetric) of Concrete C142 Test Method for Clay Lumps and Friable Particles in Aggregates C150 Specification for Portland Cement C157 Standard Test Method for Length Change of Hardened Hydraulic-Cement, Mortar, and Concrete C227 Test Method for Potential Alkali Reactivity of Cement-Aggregate Combinations (Mortar-Bar Method) C230 Standard Specification for Flow Table for Use in Tests of Hydraulic Cement C231 Standard Test Method for Air Content of Freshly Mixed Concrete by the Pressure Method C289 Test Method for Potential Alkali-Silica Reactivity of Aggregates (Chemical Method) C294 Descriptive Nomenclature for Constituents of Concrete Aggregates C295 Guide for Petrographic Examination of Aggregates for Concrete C311 Test Methods for Sampling and Testing Fly Ash or Natural Pozzolans for Use in Portland-Cement Concrete C330 Specification for Lightweight Aggregates for Structural Concrete C331 Specification for Lightweight Aggregates for Concrete Masonry Units C332 Specification for Lightweight Aggregates for Insulating Concrete C342 Test Method for Potential Volume Change of Cement-Aggregate Combinations (Withdrawn 2001)4 C403 Standard Test Method for Time of Setting of Concrete Mixtures by Penetration Resistance C441 Test Method for Effectiveness of Pozzolans or Ground Blast-Furnace Slag in Preventing Excessive Expansion of Concrete Due to the Alkali-Silica Reaction C469 Standard Test Method for Static Modulus of Elasticity and Poisson's Ratio of Concrete in Compression C496 Standard Test Method for Splitting Tensile Strength of Cylindrical Concrete Specimens C535 Test Method for Resistance to Degradation of Large-Size Coarse Aggregate by Abrasion and Impact in the Los Angeles Machine C586 Test Method for Potential Alkali Reactivity of Carbonate Rocks as Concrete Aggregates (Rock-Cylinder Method) C595 Specification for Blended Hydraulic Cements C618 Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete C637 Specification for Aggregates for Radiation-Shielding Concrete C638 Descriptive Nomenclature of Constituents of Aggregates for Radiation-Shielding Concrete C666/C666M Test Method for Resistance of Concrete to Rapid Freezing and Thawing C989 Specification for Slag Cement for Use in Concrete and Mortars C1105 Test Method for Length Change of Concrete Due to Alkali-Carbonate Rock Reaction C1064 Standard Test Method for Temperature of Freshly Mixed Hydraulic-Cement Concrete C1157 Performance Specification for Hydraulic Cement C1218 Water Soluble Chloride C1240 Specification for Silica Fume Used in Cementitious Mixtures C1260 Test Method for Potential Alkali Reactivity of Aggregates (Mortar-Bar Method) C1293 Test Method for Determination of Length Change of Concrete Due to Alkali-Silica Reaction C1567 Test Method for Determining the Potential Alkali-Silica Reactivity of Combinations of Cementitious Materials and Aggregate (Accelerated Mortar-Bar Method) D75 Practice for Sampling Aggregates D422 Test Method for Particle-Size Analysis of Soils D2419 Test Method for Sand Equivalent Value of Soils and Fine Aggregate D3665 Practice for Random Sampling of Construction Materials E11 Specification for Woven Wire Test Sieve Cloth and Test Sieves ACI 318

(30) Regarding the method for realizing dam 100 or other massive structure by using the concrete mix design, one of the key concepts in the MSCC 101 concept of building dams 100 is to borrow the RCC method of placing concrete for the entire lift surface, but using gravity to accomplish the compaction effort, thus eliminating much of the required equipment.

(31) If the concrete can behave more closely to the properties of an ideal fluid, then it will be self-leveling, and no need for compaction effort.

(32) Assuming that the construction process would be similar to RCC construction and be placed in one continuous lift across the entire dam 100 surface with a massive self-leveling type of concrete, precast elements 7 could be used for the US and DS facing elements.

(33) These would be left in place after construction, and the erection process to be heavily automated. Conventional formwork 6 solutions could also be utilized.

(34) The overall placement of the MSCC 101 for the dam 100 construction aims to be similar to 3D printing, where the user directly deposit the material at the point needed for construction, and move forward at a rapid rate until completion with the minimal amount of unit processes involved during construction.

(35) So, the key steps in MSCC 101 Dam 100 construction are: Batching of MSCC 101; Positioning formworks 6; Delivery 1 of the MSCC 101 to the dam 100; Self levelling and self compacting of the MSCC 101; Removal of the formworks 6.

(36) In particular, with reference to FIGS. 1b and 1c, the first phases of MSCC 101 batching and delivery to dam 100 are advantageously performed through pumping means rather than by gravity. In fact the new concrete mix design allows to be pumped while the existing RCC cannot be pumped.

(37) This aspect is advantageous because the new concrete could be easily transported and placed at the dam 100 location.

(38) FIGS. 1b and 1c illustrate two embodiments of the method according to the present invention:

(39) FIG. 1b shows steps of using US and DS formworks 6 (made of plastic or metals or other materials) that contains the area to be poured by fresh MSCC 101;

(40) FIG. 1c shows steps of using US and DS precast 7 formworks that pile on one another, and pouring fresh MSCC 101 into the voids between them and produce a consolidated concrete structure.

(41) Further, it has to be noted that the new concrete mix design avoids the external vibrating phase of concrete otherwise provided for the RCC method (FIG. 1a), as well as the internal vibrating phase with conventional concrete.