SEPARATION OF HARDENED CONCRETE PASTE FROM AGGREGATE

Abstract

A method for separating hydrated concrete paste from aggregate includes the steps of providing a feedstock comprising waste concrete with a D10?0.1 mm and a D90?100 mm, passing the feedstock, a water containing liquid and carbon dioxide into a fragmentation vessel, where the wet feedstock is subjected to electric-pulse fragmentation, withdrawing fragmented solid material from the fragmentation vessel, separating the fragmented solid material from admixed liquid phase, separating the fragmented solid material into a fine fraction with a maximum particle size of 250 ?m to provide the carbonated recycled concrete paste and a coarse fraction, recycling the coarse fraction into the fragmentation vessel and/or discharging the coarse fraction as clean aggregate, use of the recycled concrete paste obtained thereby as supplementary cementitious material or filler.

Claims

1. A method for manufacturing carbonated recycled concrete paste and clean aggregate comprising the following steps: providing a feedstock comprising waste concrete with a D.sub.10?0.1 mm and a D.sub.90?100 mm passing the feedstock, a water containing liquid and carbon dioxide in an amount providing a concentration of at least 0.1 wt.-% carbon dioxide in the liquid into a fragmentation vessel, where the wet feedstock is subjected to electric-pulse fragmentation, withdrawing fragmented solid material from the fragmentation vessel, separating the fragmented solid material from admixed liquid phase, separating the fragmented solid material into a fine fraction with a maximum particle size of 250 ?m to provide carbonated recycled concrete paste and a coarse fraction, recycling the coarse fraction into the fragmentation vessel and/or discharging the coarse fraction as clean aggregate.

2. The method according to claim 1, wherein concrete demolition waste, concrete residues arising during building, cement partially hardened during too long storage, waste arising during cleaning of devices used in concreting, or mixtures of two or more thereof are used as the waste concrete.

3. The method according to claim 1, wherein the feedstock is obtained in a primary or secondary crushing of waste concrete by technologies that minimize the production of fine fractions and/or with a particle size distribution having a D.sub.90 of ?50 mm, and/or a D.sub.10?1 mm, determined with sieving.

4. The method according to claim 1, wherein the feedstock includes additional material that accelerates the carbonation process and/or improves the final properties of the carbonated recycled concrete paste or cement made with the carbonated recycled concrete paste or a building material made with the cement.

5. The method according to claim 4, wherein the additional material is selected from the group consisting of alkanolamines, halogenides, substances that improve dissolution of CO.sub.2 in the solution, enzymes, amino acids, ammonium salts, substances that regulate the pH during the carbonation, substances providing alkali metal ions, magnesium salts, polyacrylic acid, polyacrylamide, polyvinyl alcohol, polyvinylsulfonic acids, styrenesulfonate, organic acids, polysaccharides, phosphonates, polycarboxylates, water reducing agents, plasticizers, air entraining agents, retarders, rheology modifiers, fillers, pigments, reinforcing elements, self-healing agents, and mixtures of two or more thereof.

6. The method according to claim 1, wherein the liquid phase is water and/or is provided as part of the feedstock and/or liquid phase separated from the solid material is recirculated to the vessel.

7. The method according to claim 1, wherein exhaust gas from cement plants, lime plants, coal fired power plants, gas fired power plants, waste incinerators, or a mixture of such exhaust gases, is used as the carbon dioxide.

8. The method according to claim 1, wherein a carbon dioxide solution is used as the carbon dioxide.

9. The method according to claim 1, wherein a concentration of carbon dioxide in the liquid inside the vessel ranges from 0.1 to 20 wt.-%.

10. The method according to claim 1, wherein the temperature is set to range from 30 to 95? C.

11. The method according to claim 1, wherein electric pulses during electric-pulse fragmentation have a rise time of ?1 ?sec. and/or a voltage of ?90 kV.

12. The method according to claim 1, wherein the fragmented solid material is separated from the liquid phase by filtration or decanting.

13. The method according to claim 1, wherein the withdrawn liquid phase from which the solid material has been separated is recycled into the reaction vessel.

14. A method for manufacturing a composite cement comprising providing carbonated recycled concrete paste by a method according to claim 1 and mixing the carbonated recycled concrete paste with an hydraulic cement.

15. The method according to claim 14, wherein the composite cement comprises the carbonated recycled concrete paste as supplementary cementitious material and comprises from 95 to 5 wt.-% carbonated recycled concrete paste; or wherein the composite cement comprises the carbonated recycled concrete paste as filler and comprises from 1 to 60 wt.-% carbonated recycled concrete paste.

16. The method according to claim 15, wherein the hydraulic cement is Portland cement, Portland composite cement, calcium sulfoaluminate cement, calcium aluminate cement and/or dicalcium silicate cement, preferably a Portland cement according to DIN EN 197-1, calcium sulfoaluminate cement or calcium aluminate cement.

17. The method according to claim 14, wherein during subjecting the wet feedstock to electric pulse fragmentation the concentration of carbon dioxide and treatment time are adjusted to provide the carbonated recycled concrete paste with a carbonation degree of at least 50 wt.-%.

18. A method for manufacturing a calcium carbonate cement comprising providing carbonated recycled concrete paste by a method according to claim 1, wherein during subjecting the wet feedstock to electric pulse fragmentation the concentration of carbon dioxide and treatment time are adjusted to provide the carbonated recycled concrete paste with a carbonation degree of at least 50 wt.-%.

19. The method according to claim 14, wherein the composite cement comprises the carbonated recycled concrete paste as supplementary cementitious material and comprises from 70 to 10 wt.-% carbonated recycled concrete paste; or wherein the composite cement comprises the carbonated recycled concrete paste as filler and comprises from 5 to 40 wt.-% carbonated recycled concrete paste.

20. The method according to claim 19, wherein the composite cement comprises the carbonated recycled concrete paste as supplementary cementitious material and comprises from 50 to 20 wt.-% carbonated recycled concrete paste; or wherein the composite cement comprises the carbonated recycled concrete paste as filler and comprises from 10 to 20 wt.-% carbonated recycled concrete paste.

Description

[0031] According to the invention, waste concrete is converted into cRCP and clean aggregate by a particularly efficient separation of RCP from aggregate achieved by the combination of EPF and carbonation.

[0032] The method according to the invention relies on crushed waste concrete obtained as known per se as feedstock. Waste concrete covers all materials that occur in the use of cement, binder and hydraulically hardening building materials. One typical example is concrete demolition waste. Further examples are remains from hydraulically hardening building materials, like concrete and mortar prepared and then superfluous, and solid parts in the waste water from cleaning devices for concreting, like concrete trucks, mortar mixers, and moulds for precast concrete parts. It is contemplated that other waste materials of similar composition as waste concrete, i.e. rich in carbonatable Ca and/or Mg phases, e.g. bottom ashes, fly ashes, slags and mixtures thereof, can be carbonated to provide highly reactive SCM in the same way as waste concrete or supplement waste concrete in the feedstock. Rich in carbonatable Ca and/or Mg phases means that at least 12.5 wt.-% of the waste material calculated as oxides is CaO and/or MgO and at least 80 wt.-% of the CaO and MgO is in carbonatable phases before carbonation. Preferably, CaO and/or MgO constitute at least 20 wt.-%, more preferably at least 30 wt.-% and most preferred at least 50 wt.-% of the waste material. Preferably, at least 85 wt.-%, more preferably at least 90 wt.-% of the CaO and MgO are in carbonatable phases. Thus, while a part of the carbonatable CaO and MgO in the waste material might be already carbonated before carbonation, at least 10 wt.-% of the material calculated as oxides is carbonatable but not yet carbonated CaO and/or MgO.

[0033] A preferred waste concrete is concrete demolition waste. Concrete demolition waste designates the crushed material obtained during demolition of concrete containing structures like buildings and road surfaces from which the foreign materials like wood, metal parts, brick parts, and plastic, have been substantially completely removed. According to the invention, the fraction with D.sub.10?0.1 mm, preferably D.sub.10?1 mm, most preferred D.sub.10?2 mm, and D.sub.90?100 mm, preferably D.sub.90?50 mm, most preferred D.sub.90?32 mm, resulting from concrete demolishing is particularly useful as feedstock.

[0034] In one embodiment the fine fraction is used. Recycled concrete fines (abbreviated RCF) designates the material obtained after crushing concrete demolition waste and separating the particles reusable as coarse aggregate (e.g. D90? 4 mm or ?8 mm or ?16 mm and usually designated recycled aggregate) and, if applicable, any foreign matter contained. The exact composition and particle size distribution of the concrete fines depends on the original binder and composition used in the concrete and on the demolishing and grinding procedures applied. Usually, the original aggregate is separated as much as possible and the RCF contain mostly the ground hardened binder paste together with fine sand/aggregates. Usually RCP is present in amounts of 30 to 80 wt.-% of the total RCF weight.

[0035] In a further embodiment, a coarse fraction, recycled aggregate (abbreviated RCA), is used as feedstock. In this embodiment the D.sub.10 is preferably ?2 mm. RCA is typically composed of coarse aggregate with adhering RCP and agglomerates of aggregate adhered together by RCP. Thus, the coarse fraction obtained as product still contains fine recycled aggregate, designated recycled sand (abbreviated RS). Therefore, in one embodiment the coarse fraction is separated into clean coarse aggregate and RS to allow separate use.

[0036] Another preferred waste concrete is concrete residues arising during building, e.g. but not limited to unused ready mix concrete and left over mortar. The residues are crushedoptionally groundto provide the feedstock according to the invention with particle sizes as described for concrete demolition waste. Also cement that has been stored too long and partially hydrated is useful, if needed after analogous crushing and/or grinding. Further, the waste arising during cleaning of devices used in concreting, e.g. molds for manufacturing pre-cast concrete elements, especially the filter cake from pre-cast plants, is suitable, if needed after crushing and/or grinding to particle sizes as described before and/or removal of (part of) the water.

[0037] The feedstock can be provided from one waste concrete or by mixing and/or co-grinding or co-crushing several waste concrete materials as well as other materials rich in carbonatable Ca and/or Mg phases. Typically, it is easier to use only one source, but using two or more allows optimization of the composition and converting otherwise unsuitable materials, i.e. ones that could not be used on their own. In one embodiment the starting material consists of one waste concrete or of a mixture of two or more waste concretes.

[0038] The feedstock is preferably obtained in a primary or secondary crushing of waste concrete, especially by technologies that minimize the production of fine fractions. Thus, suitable devices are for example, but not limited to, vertical shaft impactor (VSI) crushers, vibrating cone crushers e.g. Rhodax 4D?, standard cone crushers, vertical roller mills (VRM), high pressure grinding rollers (HPGR) or Smart Crusher? technologies.

[0039] The particle size of the feedstock is not critical, however, as finer materials are usually carbonated faster a D.sub.90 of ?50 mm, preferably ?32 mm, in some embodiments even ?16 mm or ?8 mm or ?4 mm, is typically desired. On the other hand, EPF is more effective on larger particles, so that a D.sub.10?0.1 mm, preferably ?1 mm or ?2 mm, in some embodiments even ?4 mm or ?8 mm or ?16 mm, is usually adjusted. If the feedstock has not the desired particle size distribution (abbreviated PSD), it can be easily adjusted with methods and devices known per se, like grinding, sieving, or classifying.

[0040] Particle size distribution is measured by sieving for sizes above 2 mm herein and determined by laser granulometry for sizes below 1 mm. In the 1-2 mm range the method is chosen depending on the particle size range of the material. For ranges extending mainly above 1 mm sieving is commonly applied, for ranges extending mainly below 1 mm laser granulometry is typically better.

[0041] The method according to the invention is especially suitable for the valorization of the fraction below 4 mm which was subjected to at least one previous mechanical treatment and where a selective separation of the RCP did not occur efficiently. It is likewise suitable to separate RCP from coarse aggregate, i.e. valorization of the fraction above 4 mm or above 8 mm. However, the method according to the invention also works well with a feedstock having a broad particle size distribution with a D.sub.10 of about 0.1 mm and a D.sub.90 of about 100 mm.

[0042] It is possible to include additional material into the feedstock that accelerates the carbonation process and/or improves the final properties of the cRCP or of the cement containing it or a building material made with it. This also applies to the embodiment where the feedstock consists of one or more waste concrete(s).

[0043] Typically, additional material will be included in an amount from 0.001 to 1 wt.-% with respect to the total feedstock. Usually, substances that improve the properties of the cement or hydraulic building material made with the cRCP are added to the cement or building material, but some can also accelerate the carbonation. In the latter case their addition to the feedstock is advantageous. Preferably, substances for enhancing the carbonating process or mixtures of two or more thereof are used as additional material.

[0044] Suitable materials include amines like alkanolamines, for example primary amines like monoethanolamine (MEA) and diglycolamine (DGA), secondary amines like diethanolamine (DEA) and diisopropanolamine (DIPA), and tertiary amines like methyldiethanolamine (MDEA) and triethanolamine (TEA), or mixtures thereof, halogenides, ethylenediaminetetraacetic acid (EDTA) or other substances that improve dissolution of CO.sub.2 in the solution. Additionally enzymes such as carbonic anhydrase can be used to enhance carbonation efficiency and modify the properties of the reaction products. Also amino acids, e.g. aspartic acid, serine, arginine, as well as ammonium salts, e.g. ammonium chloride, ammonium sulfate and ammonium nitrate, are useful, especially to provide the calcium carbonate component of the cRCP in a metastable form. Such forms show e.g. a reactivity as calcium carbonate cement not found in calcite. It is to be noted that these additions may have not only one action but can exercise a double role. They can e.g. modify the hydration process of the final binder as well as modify the carbonation process. The effect can largely depend on the dosage.

[0045] Moreover it is possible to add substances that regulate the pH during the carbonation process in order to enhance the precipitation of calcium carbonate. These include metal hydroxides and carbonates and similar water soluble substances.

[0046] It is also possible to add substances providing alkali metal ions so that sulfate ions present are kept in the liquid as alkali sulfate as described in not prior published EP 21185792.5, the content of which is incorporated herein in its entirety.

[0047] Further, it is possible to add substances that modify the morphology of the precipitating calcium carbonate during the carbonation process. This provides the advantage of building less dense shales of hydrates-carbonates product and enables higher carbonation and hydration degrees. Suitable are for example magnesium salts, polyacrylic acid, polyacrylamide, polyvinyl alcohol, polyvinylsulfonic acids, styrenesulfonate, citric acid and other organic acids, polysaccharides and phosphonates, polycarboxylates.

[0048] Furthermore, it is possible to add admixtures that modify properties of the hydraulic building material or the building structure made from the composite cement comprising the SCM according to the invention already to the starting material (usually those will be added to the building material or cement).

[0049] Often used admixtures are water reducing agents and plasticizers like for example, but not exclusively, organic compounds with one or more from carboxylate, sulfonate, phosphonate, phosphate or alcohol functional groups. These serve to achieve a good consistency, i.e. flowability, of the paste with a smaller amount of water. Since a decrease of water/binder ratio normally provides an increase of strength, such admixtures are commonly used.

[0050] Air entraining agents are also able to improve flowability and can be used for this aim or for other reasons such as, but not limited to, density modifications, compactibility improvements etc. Useful air entraining agents are e.g. surface active substances, especially ones based on soaps from natural resins or synthetic nonionic and ionic tensides.

[0051] Other admixtures that influence workability are retarders. They mainly aim at prolonging the time that a specified consistency is maintained. Retarders slow the setting and/or hardening of the binder paste. Suitable substances are for example, but not exclusively, phosphates, borates, salts of Pb, Zn, Cu, As, Sb, lignosulphonates, hydroxycarboxylic acids and their salts, phosphonates, sugars (saccharides).

[0052] It is also possible to add admixtures that are designed to modify the rheology properties, i.e. rheology modifiers like e.g. polycarboxylates, lignosulfonates, starch, Karoo gum, bentonite clay, polyvinyl alcohol, and mixtures thereof.

[0053] All admixtures are used in the amounts known as such, wherein the amount is adapted to a specific binder and special needs in the known manner.

[0054] Additives can be added as well to the starting material, but usually those are added to the composite cement or the hydraulic building material. Usual and useful additives are e.g. fillers (especially limestone and other stone dust), pigments, reinforcing elements, self-healing agents etc. All these can be added in the amounts known per se.

[0055] Separation of RCP from aggregate takes place in a fragmentation vessel by the combined action of EPF and carbonation. For this, the feedstock is introduced into the vessel together with a water containing liquid phase and carbon dioxide. In a preferred embodiment the liquid phase is only water, but other liquid components are possible. Preferably, the feedstock is introduced continuously to an electric-pulse fragmentation reactor, together with the liquid phase and carbon dioxide.

[0056] All or part of the liquid phase, especially the water, can also be provided as part of the feedstock, i.e. already mixed with it. For example, the waste concrete or a part thereof can be in the form of a suspension or water has been added in prior steps. It is also possible that a feedstock contains more liquid or water than desired, in that case the feedstock is concentrated before introduction into the fragmentation vessel.

[0057] The carbon dioxide for use in the method according to the invention can be introduced in gaseous, liquid, solid or supercritical form. Gaseous CO.sub.2 used for the carbonation can be used in pure form or in the form of mixtures with other gases, such as air, oxygen, nitrogen or argon. Preferred are carbon dioxide-comprising gas mixtures available on an industrial scale.

[0058] One especially preferred source of CO.sub.2 is exhaust gas, preferably exhaust gas having a high CO.sub.2 content like from 10 to 30 Vol.-% or higher, based on the total volume of the exhaust gas. Particularly preferred are exhaust gases from cement or lime plants, coal or gas fired power plants, and waste incinerators.

[0059] The CO.sub.2 concentration is not restricted, preferably it ranges from 1 to 100 Vol.-%, more preferred from 2 to 95 Vol.-%, and most preferred from 5 to 90 Vol.-%.

[0060] In one preferred embodiment a carbon dioxide solution is used. In this case it is advantageous to use the CO.sub.2 solution at least partly as the liquid introduced into the fragmentation vessel. Most preferred an aqueous carbon dioxide solution is used. The CO.sub.2 solution can preferably be obtained by absorbing CO.sub.2 from exhaust gases into an aqueous liquid.

[0061] Usually, a CO.sub.2 concentration in the liquid inside the vessel ranging from 0.1 to 20 wt.-%, preferably from 0.5 to 10 wt.-%, most preferred from 1 to 5 wt.-%, is suitable. If a solution with high carbon dioxide concentration is used to provide carbon dioxide, additional water may be added to obtain the desired concentration. All introduced water is preferably water recycled within the method according to the invention. If a combination of gaseous and dissolved carbon dioxide is used for carbonation, the concentration of CO.sub.2 in the solution can be lower, e.g. down to 0.00001 wt.-% carbon dioxide or ?0.0001 wt.-%, or ?0.001 wt.-%, or ?0.01 wt.-%. The concentration of carbon dioxide inside the vessel can also be easily increased by adding dry ice, i.e. solid carbon dioxide, when needed. Solid carbon dioxide can also be used alone as carbon dioxide. In a preferred embodiment the water inside the fragmentation vessel is saturated with CO.sub.2.

[0062] The fragmentation vessel can operate at room temperature, but also between 30 and 95? C. In one embodiment a temperature of ?40? C. is used, which was found to be advantageous for the formation of metastable amorphous calcium carbonate.

[0063] The carbonation preferably takes place at atmospheric pressure, but the vessel can also be operated under vacuum or at an overpressure, e.g. at an absolute pressure of up to 5 bar, or up to 3 bar or up to 1.5 bar.

[0064] High voltage pulses are applied to the liquid phase inside the vessel and cause fragmentation of the feedstock. Concurrent, wet carbonation of the RCP synergistically promotes detachment of RCP from the aggregate. Unlike mechanical attrition forces EPF leaves the aggregate itself not or only scarcely fragmented. The intensity and number of discharges are adjusted to steer the selectivity of the process. High energy/intensity pulsation promotes selectivity allowing a reduction in the number of pulses/cycles, while the effect of removing the liberated fines is maintained. Suitable voltages range from at least 20 kV to 50 kV for electro-hydraulic crushing or more than 90 kV for electro-dynamic fragmentation. According to the invention from 30 to 200 kV are preferred. Rise times can range from 0.1 to 5 ?sec., preferably rise times of <2 ?sec. are used. Devices suitable for EPF are known as such. Continuously operating devices are preferred.

[0065] As product of the combined carbonation and EPF a liquid phase containing a fragmented solid material is obtained. The solid material is withdrawn from the fragmentation vessel either together with the liquid phase or as far as possible separately from the liquid phase. The solid material is separated from such liquid phase still admixed with or adhering to it, for example by filtration or decanting or pressing. It is an advantage of the combined carbonation and electric-pulse fragmentation that the solid material is mainly aggregate and calcium carbonate, both of which are not soluble and settle to the bottom of the liquid phase. There, the solid material can be withdrawn from the vessel with very little liquid.

[0066] The liquid phase withdrawn together with the solid material is preferably recycled into the fragmentation vessel. Liquid phase can also be withdrawn from the vessel at a different point than that where the solid material is withdrawn. For such withdrawn liquid phase it is also preferred to recycle it. For recycling the liquid phase can be passed back directly into the vessel and/or used in preparation steps of the feedstock. Withdrawn liquid phase can also be partly or completely discharged or used elsewhere, e.g. but not limited to as mixing water for concrete.

[0067] The solid material is divided into at least two fractions according to particle size, e.g. by sieving or classifying, with a cut-off size of 250 ?m, preferably 150 ?m, more preferred 125 ?m, most preferred 90 ?m, to obtain the carbonated recycled concrete paste as the fine fraction and a coarse fraction containing the aggregate. Preferably, the solid material is sieved to provide the carbonated RCP as the fraction with particles smaller than 250 ?m or 150 ?m or 125 ?m or 90 ?m. The fraction with coarser particle size comprises sand and coarser aggregate as well as possibly feedstock not completely fragmented. Depending on whether the amount of not yet fragmented feedstock is acceptable or too high, the coarse fraction is recycled into the fragmentation vessel or discharged from the process as clean aggregate.

[0068] In case RCP remains only on a part of the aggregate separable via particle size, it is preferred to further separate the fraction with coarser particle size according to this size. The clean aggregate is then discharged and the material with RCP adhering to aggregate recycled into the process.

[0069] The fraction recovered with a particle size <250 ?m, preferably <125 ?m, can be used for further processing as constituent in raw meal preparation for clinker production or as a filler in cement products. Alternatively, when due to the conditions during subjecting the wet feedstock to EPF cRCP with high carbonation degree is recovered as fine fraction it can be used directly as SCM replacing clinker in cement production. In a preferred embodiment, carbon dioxide concentration and treatment time for EPF are adjusted to ensure the desired carbonation degree, preferably also one or more other parameters like temperature, pulse intensity, pressure and/or particle size in the wet feedstock are chosen and set to optimize, i.e. enhance, carbonation. RS (aggregate with sizes from 0.125 or 0.250 mm-2 or 4 mm) and RA (aggregate with sizes >2 or >4 mm) are recovered clean enough to be used in the formulation of new concrete

[0070] The carbonated RCP according to the invention is especially useful as filler and/or SCM in composite cements. The very efficient detaching of RCP from aggregate achieved by the EPF acting directly at the boundary between aggregate and RCP in combination with carbonation results in a fine product usually having a high carbonation degree of the cRCP of at least 50 wt.-%, often at least 65 wt.-%, even at least 80 wt.-%, of the CaO and MgO being carbonated, i.e. obtained in the form of a calcium or magnesium carbonate or hydrogen carbonate or other carbonate compound. Such cRCP is considered an SCM herein. In contrast, a simple subjecting to abrasive forces in the presence of carbon dioxide, even high amounts of CO.sub.2, is not able to achieve enough carbonation for use as SCM within useful treatment times. It takes too long until the RCP is detached and available for carbonation. For manufacturing composite cements the carbonated RCP obtained by the method according to the invention is mixed with an hydraulic cement. In case cRCP is not sufficiently carbonated for use as SCM, e.g. due to very low CO.sub.2 concentrations or short treatment times, it can still be used as filler to replace mineral fillers like limestone, and, thus, is a valuable material. The carbonated RCP behaves substantially as filler when the carbonation degree is up to 40 wt.-% or up to 30 wt.-%. Also, a use as component of cement raw meal is possible and preferred at very low carbonation degrees like up to 20 wt.-% or up to 10 wt.-%.

[0071] Hydraulic cements suitable for the use of the carbonated recycled concrete paste to make composite cements are for example, but not limited to, Portland cement, Portland composite cement, calcium sulfoaluminate cement, calcium aluminate cement and dicalcium silicate cement. Preferred hydraulic cements are Portland cements according to DIN EN 197-1, calcium sulfoaluminate cement and calcium aluminate cement. Especially preferred are Portland cements according to DIN EN 197-1.

[0072] Typically, the composite cement obtained from blending a carbonated RCP according to the invention as SCM with a hydraulic cement comprises from 5 to 95 wt.-% cement and from 95 to 5 wt.-% SCM. Preferably, it contains from 30 to 90 wt.-% cement and from 70 to 10 wt.-% SCM, more preferred from 50 to 80 wt.-% cement and from 50 to 20 wt.-% SCM.

[0073] For use as filler the amount of carbonated RCP according to the invention ranges from 1 to 60 wt.-%, preferably from 5 to 40 wt.-%, most preferred from 10 to 20 wt.-%.

[0074] In addition, usual admixtures and/or additives as described above for adding to the feedstock can be added to the composite cement. The composite cement can also comprise one or more other SCM, i.e. the composite cement can be a ternary, quaternary, . . . blend. Suitable other SCM are e.g. but not limited to fly ash, ground granulated blast furnace slag, and calcined clay. Naturally, the amounts of all components in a specific composite cement add up to 100%, so if SCM and hydraulic cement are the sole components their amounts add up to 100%, when there are other components, the amount of SCM and hydraulic cement is less than 100%.

[0075] For use, the composite cement is transformed into a hydraulic building material, e.g. into mortar or concrete, by mixing with water. Typically, a water to binder weight ratio (w/b) from 0.1 to 1, preferably from 0.15 to 0.75, and more preferred from 0.35 to 0.65 is used. The carbonated RCP according to the invention as SCMand if applicable one or more further SCMs that are optionally addedare included into the amount of binder for calculating the w/b ratio. The mortar or concrete usually also contains aggregates as well as optionally admixtures and/or additives. Admixtures and additives have been described before.

[0076] The composite cements obtained according to the invention are useful for all applications where ordinary Portland cement and known composite cements are used, especially concrete, mortar, and construction chemical products such as screed, tile adhesive etc.

[0077] Usually, aggregate and admixtures are added when making a hydraulically hardening building material like concrete or mortar from the composite cement. The known aggregate and usual admixtures are used in the usual amounts. For construction chemical products like floor screed or tile adhesive any necessary aggregate and admixture is typically added to the composite cement to form a dry mix, as far as possible. The aggregate and admixture are chosen depending on use in a manner well known per se.

[0078] A calcium carbonate cement is manufactured according to the invention by providing the carbonated recycled concrete paste through the separation method according to the invention. It hardens by a dissolution-precipitation reaction and can reach compressive strengths of at least 40 MPa as reported by C. W. Hargis et al., Calcium carbonate cement: a carbon capture, utilization, and storage (CCSU) technique, mentioned before.

[0079] The invention will be illustrated further with reference to the attached FIG. 2, without restricting the scope to the specific embodiment described. The invention includes all combinations of described and especially of preferred features that do not exclude each other.

[0080] If not otherwise specified any amount in % or parts is by weight and in the case of doubt referring to the total weight of the composition/mixture concerned. A characterization as approximately, around and similar expression in relation to a numerical value means that up to 10% higher and lower values are included, preferably up to 5% higher and lower values, and in any case at least up to 1% higher and lower values, the exact value being the most preferred value or limit.

[0081] The term substantially free means that a particular material is not purposefully added to a composition, and is only present in trace amounts or as an impurity. As used herein, unless indicated otherwise, the term free from means that a composition does not comprise a particular material, i.e. the composition comprises 0 weight percent of such material.

[0082] In FIG. 2 a preferred mode for carrying out the method according to the invention is illustrated. Waste concrete in a stock 1 is introduced together with water (or a liquid containing water) from a tank 2 and carbon dioxide from a source like a gas supply means 3 (or an exhaust gas line) to a fragmentation vessel 4.

[0083] Inside the vessel, the liquid phase is subjected to high voltage discharge pulses applied by a generator not shown. Typically, the liquid phase flows through the vessel allowing a continuous process. However, the fragmentation vessel can also be operated in batch mode. In that case several vessels can be operated in parallel to obtain a quasi-continuous process.

[0084] In the embodiment shown in FIG. 2 most of the water is withdrawn separately from the wet solid material. The water is passed into a treatment device 5. Therein, carbon dioxide can be added if desired. Possibly present solid material can be separated from the water if needed, and e.g. passed to a sieving device. Treated water is then recirculated into the tank 2 and thus recycled.

[0085] The solid material, optionally after further separation from water which is passed into the treatment device 5, is fed to a sieving device 6. Therein, it is divided into a fine fraction with particle sizes <125 ?m consisting essentially of carbonated recycled concrete paste, and a coarser fraction comprising clean aggregate and possibly aggregate still bearing some hardened concrete paste. If water separates from the solids in the sieving device or in later steps it can be passed into the treatment device 5.

[0086] For a continuous process a separator 7 is used, which divides the coarser fraction into clean aggregate and solid material needing further fragmentation. The latter is recycled into the fragmentation vessel 4. The clean aggregate is discharged to a silo or other storage device or direct use designated 8. The clean aggregate can also be split into several fractions with different sizes.

[0087] The carbonated recycled concrete paste is also discharged to a silo or other storage device or direct use designated 9. If applicable, still present water is passed from the storage of the cRCP into the water treatment device.

[0088] The recirculated process liquid may contain (unreacted) CO.sub.2 in solution and can be recirculated back to the treatment vessel. The recirculation may include reconditioning the input of fresh CO.sub.2 in order to adjust its concentration/saturation within the process liquid.

LIST OF REFERENCE NUMBERS

[0089] 1 stock of feedstock [0090] 2 tank for liquid, especially water [0091] 3 carbon dioxide source [0092] 4 fragmentation vessel [0093] 5 treatment device [0094] 6 sieving device [0095] 7 separator [0096] 8 silo, storage device, use [0097] 9 silo, storage device, use [0098] a clean aggregate [0099] cf coarse fraction [0100] CO.sub.2 carbon dioxide [0101] cRCP carbonated recycled concrete paste [0102] f feedstock [0103] S fragmented solid material [0104] W liquid, especially water