CASTING COMPOUND AND PROCESS FOR THE PRODUCTION OF GELATIN PRODUCTS

Abstract

A casting compound for the production of gelatin products comprises a homogenous aqueous solution having: 4% to 16% by weight of gelatin having a molecular weight determined by gel chromatography of at least 130 kDa, where the proportion of the gelatin having a molecular weight exceeding 130 kDa is at least 35% by weight, 6% to 76% by weight of one or more sugar alcohols; 0% to 50% by weight of glucose syrup having a viscosity of less than 800 mPas, measured at a dry matter content of 80% by weight and a temperature of 50? C.; and 0% to 50% by weight of sucrose, where the glucose syrup and the sugar alcohol(s) together make up 25% to 76% by weight of the aqueous solution, and where the aqueous solution has a dry matter content of at least 78% by weight and/or a water activity (aw value) of less than 0.75.

Claims

1. A casting compound for producing gelatin products by pouring into solid hollow moulds, comprising a homogeneous aqueous solution containing the following constituents: 4 to 16 wt % of gelatin having a mean molecular weight, determined by gel chromatography, of at least 130 kDa, wherein the proportion of the gelatin having a molecular weight of more than 130 kDa is at least 35 wt %; 6 to 76 wt % of one or more sugar alcohols; 0 to 50 wt % of glucose syrup with a viscosity of less than 800 mPa.Math.s, measured with a dry matter content of 80 wt % and at a temperature of 50? C.; and 0 to 50 wt % of sucrose, wherein the glucose syrup and the sugar alcohol(s) together make up 25 to 76 wt % of the aqueous solution, and wherein the aqueous solution has a dry matter content of at least 78 wt % and/or a water activity (a.sub.w value) of less than 0.75.

2. The casting compound according to claim 1, wherein the homogeneous aqueous solution also contains one or more flavourings, colourings and/or acidifiers.

3. The casting compound according to claim 1, wherein the homogeneous aqueous solution also contains one or more nutrients and/or pharmaceutical active substances, in a proportion of less than 45 wt %.

4. The casting compound according to claim 1, also comprising one or more insoluble constituents, which are dispersed in the aqueous solution.

5. The casting compound according to claim 3, wherein the nutrients are selected from vitamins, minerals, plant extracts and peptides.

6. The casting compound according to claim 1, wherein the gelatin is contained in the aqueous solution in a proportion of from 5 to 12 wt %.

7. The casting compound according to claim 1, wherein the glucose syrup has a dextrose equivalent of 50 or more.

8. The casting compound according to claim 1, wherein the glucose syrup is contained in the aqueous solution in a proportion of from 8 to 40 wt %.

9. The casting compound according to claim 1, wherein the sucrose is contained in the aqueous solution in a proportion of from 15 to 45 wt %.

10. The casting compound according to claim 1, wherein the sugar alcohol(s) is/are contained in the aqueous solution in a proportion of from 10 to 30 wt %.

11. The casting compound according to claim 1, wherein the sugar alcohol(s) is/are selected from sorbitol, mannitol, erythritol and glycerol.

12. The casting compound according to claim 1, wherein the homogeneous aqueous solution also comprises one or more further hydrocolloids in a proportion of from 0.1 to 10 wt %.

13. A method for producing gelatin products, wherein the method comprises: producing a casting compound according to claim 1; pouring the casting compound at a temperature of 80? C. or more into solid hollow moulds; cooling the casting compound in the hollow moulds in order to obtain the gelatin products; and removing the gelatin products from the hollow moulds.

14. The method according to claim 13, wherein the casting compound cools in the hollow moulds within a period of time of less than 60 min.

15. The method according to claim 13, wherein the solid hollow moulds consist of a plastics material which is selected from silicone, polycarbonate or polyethylene terephthalate.

16. The method according to claim 13, wherein the gelatin products are treated with a release wax or are dusted with sucrose and/or citric acid after having been removed from the hollow moulds.

17. A gelatin product produced in accordance with the method according to claim 13.

18. The casting compound according to claim 1, wherein the gelatin has a mean molecular weight, determined by gel chromatography, of at least 145 kDa.

19. The casting compound according to claim 1, wherein the proportion of the gelatin having a molecular weight of more than 130 kDa is at least 45 wt %.

20. The casting compound according to claim 1, wherein the glucose syrup has a viscosity of less than 700 mPa.Math.s.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0022] The casting compound according to the invention achieves the stated object by means of the cooperation of the contained components within the above-mentioned quantity ranges. An essential feature of the invention is the selection of a high-molecular gelatin with a mean molecular weight, determined by gel chromatography, of at least 130 kDa, wherein the proportion of the gelatin having a molecular weight above 130 kDa is at least 35 wt %. Such gelatins can be obtained from various collagen-containing materials, in particular from connective tissue or bones of pigs, cattle, poultry or fish.

[0023] Flavourings, colourings and/or acidifiers can be contained as further components in the casting compound, in particular in the homogeneous aqueous solution, wherein the typical quantity proportions of such additives are known from the prior art. The conventional edible acids, preferably citric acids, are used as acidifier.

[0024] The casting compound according to the invention, in addition to the above-described components, can also contain further constituents, provided these do not have a negative effect on the specified advantageous properties of the casting compound. In a preferred embodiment, the casting compound comprises one or more nutrients and/or pharmaceutical active substances, wherein these can be dissolved or dispersed in the homogeneous aqueous solution depending on the degree of solubility. In the first case, the proportion of such components is preferably less than 45 wt %, more preferably less than 35 wt %.

[0025] Preferred nutrients in the casting compound according to the invention are selected from vitamins, minerals, plant extracts, and peptides, in particular collagen peptides (collagen hydrolysate). The corresponding gelatin products can be enriched confectionery products (fortified gummies) or dietary supplements.

[0026] The casting compound according to the invention can also be used for the production of medicinal products (for example in the form of chewable tablets), and in this case contain pharmaceutical active substances, for example painkillers such as acetylsalicylic acid, paracetamol, or ibuprofen. The suitability of the casting compound for the use of solid hollow moulds, in contrast to the mogul technique, makes it possible to observe the hygiene standards applicable in this area (GMP guidelines).

[0027] The gelatin can be contained in the aqueous solution in a proportion of from 4 to 16 wt %, wherein a proportion of from 5 to 12 wt % is preferred, in particular from 6 to 10 wt %. Within this range, gelatin products that have a typical texture, in particular a high elasticity, are obtained.

[0028] Glucose syrup and sucrose can be contained in the aqueous solution in a proportion of, in each case, up to 50 wt %. However, these components can also be omitted for the production of sugar-free products and can be compensated for by a higher proportion of sugar alcohols.

[0029] With use of glucose syrup, this preferably has a viscosity of less than 800 mPa.Math.s, more preferably of less than 700 mPa.Math.s, measured with a dry matter content of 80 wt % and at a temperature of 50? C. The glucose syrup is conveniently a highly hydrolysed glucose syrup with a dextrose equivalent of 50 or more, preferably of 60 or more.

[0030] Apart from in the case of sugar-free products, the aqueous solution preferably contains a proportion of from 8 to 40 wt % of glucose syrup, more preferably from 15 to 28 wt %.

[0031] Sucrose, that is to say commercially available sugar, is preferably contained in the aqueous solution (apart from in the case of sugar-free products) in a proportion of from 15 to 45 wt %, more preferably from 20 to 40 wt %.

[0032] The aqueous solution also comprises one or more sugar alcohols in a proportion of from 6 to 76 wt %, preferably from 10 to 30 wt %. Due to the use of these sugar substitutes, the quantity of sugar and/or glucose syrup can be reduced on the one hand, and on the other hand the sugar alcohols also contribute to the favourable rheological properties of the costing compound.

[0033] The sugar alcohol(s) is/are preferably selected from sorbitol, mannitol, xylitol, erythritol and glycerol, wherein sorbitol is particularly preferred.

[0034] In accordance with a variant of the invention, the homogeneous aqueous solution also comprises one or more further hydrocolloids, in particular pectin, in order to modify the properties of the gelatin products (for example temperature stability and elasticity). The proportion of further hydrocolloids is preferably from 0.1 to 10 wt %, in particular from 0.2 to 5 wt %.

[0035] The casting compound according to the invention is suitable, as described above, for the production of gelatin products by casting in solid hollow moulds, in particular made of a plastics material.

[0036] The present invention therefore also relates to a method for producing gelatin products, said method comprising the following steps: [0037] producing a casting solution according to the invention; [0038] pouring the casting solution at a temperature of 80? C. or more into solid hollow moulds; [0039] cooling the casting solution in the hollow moulds in order to obtain the gelatin products; and [0040] removing the gelatin products from the hollow moulds.

[0041] The cooling of the casting solution in the hollow moulds is performed preferably within a period of time of less than 60 min., more preferably less than 45 min. This constitutes a significant advantage compared to casting in hollow moulds in a starch moulding powder, where the gelatin products can usually only be removed after a drying time of from 24 to 72 hours.

[0042] In principle any material, in particular plastics material, which is temperature stable (up to approximately 95? C.) and which is suitable for contact with foodstuffs, can be used for the solid hollow moulds. Hollow moulds made of silicone, which on account of its flexibility enables easy demoulding of the gelatin products, are particularly preferred.

[0043] Further examples of suitable plastics materials are polycarbonate (PC) or polyethylene terephthalate (PET), for example. Hollow moulds can be produced from thin films of these plastics by means of thermoforming, similarly to the known blister packs for medicinal drugs. These materials are more economical than silicone, which opens up the possibility of producing individualised hollow moulds, for example having inscriptions which are impressed into the gelatin products. These hollow moulds can then be discarded after relatively few product cycles.

[0044] Once the gelatin products have been removed from the hollow moulds, they can be either treated with a release wax or dusted with sucrose and/or citric acid, depending on the desired look.

[0045] The present invention also relates to gelatin products produced in accordance with the method according to the invention. In spite of their new composition, these products, when consumed, have the typical texture expected of gelatin products by consumers.

[0046] As already mentioned in the introduction, the term gelatin products within the scope of the present invention includes all confectionery products, dietary supplements, or medicinal products having the corresponding composition, regardless of their external form. Typical examples of such products are gummy sweets, fruit gummies, fortified gummies, chewable tablets, etc.

[0047] The gelatin products according to the invention preferably have a dry matter content of at least 78 wt % and/or a water activity (a.sub.w value) of less than 0.75. As already described in conjunction with the casting compound according to the invention, there is no, or only an insignificant increase of the dry matter content during the cooling and setting.

[0048] These and further advantages of the invention will be explained in greater detail on the basis of the following examples.

EXAMPLES

[0049] Gelatin products were produced in accordance with the method described hereinafter from six different casting compounds according to the invention (Examples 1 to 6) and one casting compound, not according to the invention, as Comparative Example.

[0050] For this purpose, the gelatin was firstly dissolved completely in hot water (70 to 80? C.), then sorbitol and as appropriate glycerol was/were added, and the mixture was stirred homogeneously and was heated again to 70 to 80? C.

[0051] In parallel, a so-called sugar slurry was produced by boiling glucose syrup, sucrose, and sorbitol (and as appropriate pectin) in water under pressure to at least 125? C. The sugar slurry cooled to approximately 110? C. and the gelatin/sorbitol solution were combined, and the mixture was degassed under vacuum and cooled to 80? C. During the degassing, the water content of the composition was also reduced to such an extent that the dry matter content was at least 78 wt %.

[0052] Citric acid was then added as acidifier to the charge, and the casting compound was filled into hollow moulds made of silicone (Examples 1 to 5 and Comparative Example) or into hollow moulds in a PET blister pack (Example 6). For this purpose, a laboratory casting installation from the company Winkler and D?nnebier S??warenmaschinen GmbH was used. The filling quantity was in each case between 1 and 5 g.

[0053] After a cooling time of at most 60 min. at less than 12? C. ambient temperature, the gelatin products according to the invention (gummy sweets/chewable tablets) could be demoulded. The products can then be lubricated as desired using a release wax or dusted with sugar and citric acid and then packaged.

[0054] In Table 1 below, the respective compositions of the finished casting compound prior to filling into the hollow moulds are specified for Examples 1 to 6 and the Comparative Example. Various parameters of the casting compound, the production method, and the produced gelatin products are also specified.

TABLE-US-00001 TABLE 1 Comp. Ex. Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Composition Gelatin (Standard) 7.3 of the casting Gelatin MW > 130 kDa, 7.3 7.3 10.0 7.0 8.4 5.5 compound in proportion > 130 kDa at kg least 35% Glucose syrup DE 42 42.1 Glucose syrup DE 60 39.1 9.1 16.6 17.6 18.5 38.7 Sucrose 33.4 31.4 41.4 36.2 38.2 39.1 20.8 Sorbitol 6.9 16.9 16.6 16.6 17.5 13.3 Glycerol 3.3 Pectin 0.4 Water 15.3 15.3 15.3 18.7 18.7 14.4 16.3 Citric acid 50% ig 2.0 2.0 2.0 2.0 2.0 2.0 2.0 Temperature . . . of the gelatin solution 65 70 72 70 70 70 70 in ? C. at the time of addition of the sugar slurry . . . when boiling the 125 125 125 125 128 130 130 sugar slurry . . . of the sugar slurry at 110 105 115 110 115 120 110 the time of addition of the gelatin solution . . . of the casting solution 90 80 92 91 83 90 80 after addition of the citric acid Dry matter content of the casting 82 81 84 78 78 83 82 compound prior to pouring in wt % a.sub.wvalue (25? C. ) of the casting Moulding 0.701 0.699 0.755 0.684 0.691 0.713 compound prior to pouring not possible, Temperature of the feeder head in ? C. therefore 88 88 88 88 88 80 Core temperature after pouring into no products n/a 70 67 69 73 71 hollow moulds in ? C. could be Water content of the gelatin products produced! 19.6 19.7 23.0 18.8 19.5 21.3 in wt % Dry matter content of the gelatin 80.4 80.3 76.9 81.2 80.5 78.7 products in wt % Bloom strength after 1 day 1019 558 874 985 1243 420 of the gelatin after 1 week 1023 839 1021 1283 1538 453 products in g after 4 weeks 976 1098 950 1830 1423 507

[0055] The Comparative Example corresponds to the typical recipe for a mogul installation according to the prior art, with a standard gelatin, low-hydrolysed glucose syrup (DE 42), and without sugar alcohols. This casting compound could be moulded only with difficulty on account of filament formation and air inclusions and was still too soft and too tacky after a cooling time of 60 min. to be removed from the silicone moulds. In the case of the gelatin products according to Example 1, which were produced from a casting compound comprising high-molecular gelatin, highly hydrolysed glucose syrup (DE 60) and sorbitol, these could be removed already after less than 60 min.

[0056] In Examples 2 to 5, which contained modified proportions of sucrose, glucose syrup and sorbitol, and also in the case of Example 6 with additional glycerol, a demoulding of the products was possible already after at most 40 min., wherein the end products had different textures in part (for example shorter, more solid texture in the case of Example 4, which additionally contained pectin).

[0057] By varying the recipe of the casting compound according to the invention, the texture properties of the produced gelatin products could be modified depending on the dry matter content content, gelatin dosing, and sugar composition.