Abstract
A hybrid die bonding method includes the following steps: dicing a wafer into a plurality of dies arranged on a plurality of target blocks of a carrier film, wherein surfaces of each of the dies having no solder and bump; cleaning particulate from first surfaces of the dies; separating sides and corners of second surfaces of the dies from the target blocks; turning the carrier film and transferring the dies to a first carrier, wherein the first surfaces of the dies contact the first carrier; removing the carrier film from the second surfaces of the dies; cleaning particulate from the second surfaces of the dies; and transferring the dies from the first carrier to a substrate, wherein a surface of the substrate having no solder and bump. As such, the method reduces the adhesive force between the dies and the carrier film.
Claims
1. A hybrid die bonding method, comprising the following steps of: dicing a wafer into a plurality of dies, the dies being distributed on a plurality of target blocks of a carrier film, and each die having no solder or bump on surfaces; removing particles on first surfaces of the plurality of dies; peeling off the plurality of sides and corners of the second surfaces of the dies from the target blocks; turning over the carrying film, and transferring the plurality of dies to a first carrier with first surfaces of the dies contacting the first carrier; removing the carrier film from the second surfaces of the dies; cleaning particles on the second surfaces of the dies; and transferring the dies from the first carrier to a substrate, the surface having no solder or bump on surfaces.
2. The hybrid die bonding method according to claim 1, wherein the step of removing particles on the first surfaces of the dies further includes a step of: de-bonding the carrier film.
3. The hybrid die bonding method according to claim 2, wherein the step of de-bonding the carrier film further includes the following step: the carrier film being a UV release film, and an ultraviolet light is irradiated on the carrier film.
4. The hybrid die bonding method according to claim 2, wherein the step of de-bonding the carrier film further includes the following step: the carrier film is a pyrolytic adhesive film, and the carrier film is heated.
5. The hybrid die bonding method according to claim 1, wherein the step of dicing the wafer into a plurality of dies further includes the following steps: dicing the wafer into a plurality of rows of die combinations, each row of die combinations comprising a plurality of dies, and the plurality of rows of die combinations being distributed on a plurality of rows of target block combinations of the carrier film, and each row of target block combinations comprising a plurality of target blocks; wherein, the step of peeling off the sides and the corners of the second surfaces of the dies from the target blocks further includes the following steps: raising the two target blocks of the two adjacent rows of target block combination upward or downwardly concave, so that the sides and the corners of the second surfaces of all the dies of the two adjacent rows of die combination being peeled off from all the target blocks of the two adjacent rows target block combinations; and after the two rows of die combination completing peeling off, continuing to perform peeling off process on the other two adjacent rows of die combinations until the peeling process being completed for all the rows of die combinations.
6. The hybrid die bonding method according to claim 1, wherein the step of peeling off the sides and the corners of the second surfaces of the dies from the target blocks further includes the step of: moving at least one pushing member upward to push connecting blocks between the target blocks in sequence, and the target blocks being raised upward, so that the sides and the corners of the second surfaces of the dies being peeled off from the target blocks.
7. The hybrid die bonding method according to claim 1, wherein the step of peeling off the sides and the corners of the second surfaces of the dies from the target blocks further includes the step of: a scraper moving horizontally along the surface of the carrier film to push connecting blocks between the target blocks in sequence, and the target blocks being raised upward, so that the sides and the corners of the second surfaces of the dies being peeled off from the target blocks.
8. The hybrid die bonding method according to claim 1, wherein the step of peeling off the sides and the corners of the second surfaces of the dies from the target blocks further includes the step of: at least one channel of an adsorption device providing a negative pressure to adsorb connecting blocks between the target blocks, and the target blocks being recessed downward, so that the sides and the corners of the second surfaces of the dies being peeled off from the target blocks.
9. The hybrid die bonding method according to claim 1, wherein the step of transferring the dies from the first carrier to the substrate further comprises the steps of: picking up the dies from the first carrier; moving the dies; and placing the dies on a substrate with first surfaces in contact with the substrate.
10. The hybrid die bonding method according to claim 1, wherein the step of transferring the dies from the first carrier to the substrate further comprises the steps of: flipping the first carrier and transferring the dies to a second carrier, the second surfaces of the dies contacting with the second carrier; removing particles from the first surfaces of the dies; picking up the dies from the second carrier; moving the dies; and placing the dies on a substrate, the second surfaces of the dies contacting with the substrate.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0024] The present invention will be apparent to those skilled in the art by reading the following detailed description of a preferred embodiment thereof, with reference to the attached drawings, in which:
[0025] FIG. 1 is a schematic view of a first conventional method of die stripping.
[0026] FIG. 2 is a schematic view of a second conventional die lift-off method.
[0027] FIG. 3 is a flow chart of the hybrid die bonding method of the present invention.
[0028] FIG. 4 is a schematic view of chemical-mechanical polishing in step S100 of the hybrid die bonding method of the present invention.
[0029] FIG. 5A is a top view of the mechanical dicing in step S100 of the hybrid die bonding method of the present invention.
[0030] FIG. 5B is a schematic diagram of mechanical cutting in step S100B of the hybrid die bonding method of the present invention.
[0031] FIG. 6A is a top view of the dicing completed in step S100 of the hybrid method for fixing dies of the present invention.
[0032] FIG. 6B is a schematic view of the completion of dicing in step S100 of the hybrid die bonding method of the present invention.
[0033] FIG. 7 is a schematic view of step S200 of the hybrid die bonding method of the present invention.
[0034] FIG. 8 is a schematic view of step S300 of the hybrid die bonding method of the present invention.
[0035] FIG. 9A is a perspective view of the first pre-edge/corner peeling method in step S400 of the hybrid die bonding method of the present invention.
[0036] FIG. 9B is a top view of the first pre-edge/corner peeling method in step S400 of the hybrid die bonding method of the present invention.
[0037] FIG. 9C is a cross-sectional view taken along line A-A of FIG. 9B.
[0038] FIG. 10A is a perspective view of the second pre-edge/corner peeling method in step S400 of the hybrid die bonding method of the present invention.
[0039] FIG. 10B is a top view of the second pre-edge/corner peeling method in step 5400 of the hybrid bonding for fixing dies method of the present invention.
[0040] FIG. 10C is a cross-sectional view taken along line B-B of FIG. 10B.
[0041] 11A is a perspective view of the third pre-edge/corner peeling method in step 5400 of the hybrid die bonding method of the present invention.
[0042] FIG. 11B is a top view of the third pre-edge/corner peeling method in step 5400 of the hybrid die bonding method of the present invention.
[0043] FIG. 11C is a cross-sectional view taken along line C-C of FIG. 11B.
[0044] FIG. 12 is a schematic view of step 5500 of the hybrid die bonding method of the present invention.
[0045] FIG. 13 is a schematic view of step 5600 of the hybrid die bonding method of the present invention.
[0046] FIG. 14 is a schematic view of step 5700 of the hybrid die bonding method of the present invention.
[0047] FIG. 15 is a schematic view of the first mode of die transfer in step 5800 of the hybrid die bonding method of the present invention.
[0048] FIGS. 16 to 18 are schematic views of the second mode of die transfer in step S800 of the hybrid die bonding method of the present invention.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT
[0049] The accompanying drawings are included to provide a further understanding of the invention, and are incorporated in and constitute a part of this specification. The drawings illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.
[0050] FIG. 3 is a flow chart of the hybrid die bonding method of the present invention. As shown in FIG. 3, the present invention provides a hybrid die bonding method, which includes the following steps: Step S100: dicing a wafer 10 into a plurality of dies 11, and the distributing the dies 11 in a plurality of target blocks 21 of a carrier film 20. Each die 10 has no solder balls and no copper bumps on the surfaces. Step S200: removing the particles 12 on the first surfaces 111 of the dies 11. Step S300: de-bonding the carrier film 20. Step S400: peeling off a plurality of sides and corners of the second surfaces 112 of the dies 11 from the target blocks 21. Step S500: turning the carrier film 20 over, and transferring the dies 11 to a first carrier 30, the first surfaces 111 of the dies 11 contacting with the first carrier 30. Step S600: removing the carrier film 20 from the second surfaces 112 of the dies 11. Step S700: removing the particles 12 on the second surfaces 112 of the dies 11; and Step S800: transferring the dies 11 from the first carrier 30 to a substrate 40, the surface of the substrate 40 is free of solder balls and copper bumps. A variety of implementations of steps S100 to S800 will be described in further detail below.
[0051] FIG. 4 is a schematic view of chemical-mechanical polishing in step S100 of the hybrid die bonding method of the present invention, and FIGS. 5A and 5B are respectively a top view and a schematic view of the mechanical dicing in step S100 of the hybrid die bonding method of the present invention. Step S100 further includes the following steps: chemical-mechanical polishing (CMP), a copper frame (not shown) is disposed on the first surface of the wafer 10 to form a plurality of logic circuit layers and a plurality of peripheral channels are formed on the periphery of the logic circuit layers; then, as shown in FIG. 4, a polishing pad (not shown) is disposed on a platform 50, the wafer 10 is placed on the polishing pad, and the copper frame is removed by chemical-mechanical polishing; and machine dicing, as shown in FIGS. 5A and 5B, using a diamond dicing knife 60 to cut a plurality of scribe lines 13 directly on the wafer 10, so that the wafer 10 is diced into a plurality of dies 11 .
[0052] In other embodiments, laser dicing or plasma dicing can replace mechanical dicing and directly cut a plurality of dicing lines on the wafer, so that the wafer is diced into a plurality of dies.
[0053] FIG. 6A and FIG. 6B are respectively a top view and a schematic view after the dicing is completed in step S100 of the hybrid die bonding method of the present invention. As shown in FIG. 6A and FIG. 6B, because the chemical-mechanical polishing will polish the surface of the wafer 10 to become very smooth, and the activation energy of chemical-mechanical polishing is relatively large, the particles 12 generated during the dicing process are easily attached to the surfaces of the dies 11.
[0054] Actually, as shown in FIG. 6A, the wafer 10 is diced into a plurality of rows of die combinations 14, each row of die combinations 14 includes a plurality of dies 11, and the plurality of rows of die combinations 14 are distributed on the carrier film 20 in the plurality of rows of target block combinations 22, each row of target block combinations 22 includes a plurality of target blocks 21.
[0055] FIG. 7 is a schematic view of step S200 of the hybrid die bonding method of the present invention. In step S200, as shown in FIG. 7, a nozzle 70 sprays high-pressure gas, high-pressure liquid, or a mixture or plasma of high-pressure gas and high-pressure liquid on the first surfaces 111 of the dies 11, and the high-pressure gas, high-pressure liquid, or a mixture or plasma of high-pressure gas and high-pressure liquid can blow or disperse the particles 12 from the first surfaces 111 of the dies 11, so that the particles 12 on the first surfaces 111 of the dies 11 are completely removed.
[0056] FIG. 8 is a schematic view of step S300 of the hybrid die bonding method of the present invention. In step S300, as shown in FIG. 8, the carrier film 20 is a UV release film or a thermal release film (pyrolytic adhesive film); when the carrier film 20 is a UV release film, a UV lamp 80 emits an ultraviolet light, and the ultraviolet light is irradiated on the carrier film 20; when the carrier film 20 is a pyrolytic adhesive film, a heating device 90 is applied to heat up the carrier film 20. Ultraviolet light can reduce the viscosity of UV release film, and high temperature can reduce the viscosity of pyrolytic adhesive film. After the step S300 is completed, because the viscosity of the carrier film 20 is reduced, the adhesive effect of the dies 11 being attached to the carrier film 20 is reduced, but the adhesiveness of the carrier film 20 is still sufficient to fix the dies 11 and the dies 11 do not detach from the carrier film 20.
[0057] In other embodiments, when the carrier film 20 is a low-viscosity film (e.g., blue film), the carrier film 20 does not need to be de-bonded to perform step S400, so step S300 in the those embodiments can be omitted.
[0058] FIGS. 9A, 9B, and 9C are respectively a perspective view, a top view and a cross-sectional view along line A-A in FIG. 9B in step S400 of the hybrid die bonding method of the present invention. FIGS. 10A, 10B, and 10C are respectively a perspective view, a top view and a cross-sectional view along the line B-B in FIG. 10B in the second pre-edge/corner peeling method in step S400 of the hybrid die bonding method of the present invention. FIGS. 11A, 11B, and 11C are respectively a perspective view, a top view and a cross-sectional view along the line C-C in FIG. 11B of the third pre-edge/corner peeling method in step S400 of the hybrid die bonding method of the present invention. The three pre-edge/corner peeling methods in step S400 will be described in detail below with reference to the drawings.
[0059] In the first pre-edge/corner peeling method, as shown in FIG. 9A, FIG. 9B and FIG. 9C, at least one pushing member 100 moves upward, and sequentially pushes the connecting blocks 23 between the target blocks 21, the target blocks 21 are raised upward, so that the sides and the corners of the second surfaces 112 of the dies 11 are peeled off from the target blocks 21. More specifically, the plurality of pushing members 100 are arranged in a row, and each pushing member 100 is aligned with the connection block 23 between the two target blocks 21 of the two adjacent rows of target block combinations 22. The pushing members 100 move upward synchronously, and each pushing member 100 pushes the connecting block 23 between the two target blocks 21 of the two adjacent rows of target block combinations 22, and the two target blocks 21 of the two adjacent rows of target block combinations 22 are raised upward , so that, so that the sides and the corners of the second surfaces 112 of all the dies 11 of the two adjacent rows of die combinations 14 are peeled off from the two adjacent rows of target block combinations 22; after the two rows of die combinations 14 has completed the peeling process, the pushing members 100 continue to perform the peeling process on the other two rows of die combinations 14 until all the rows of die combinations 14 have completed the peeling process.
[0060] In the second pre-edge/corner peeling method, as shown in FIGS. 10A, 10B and 10C, a scraper 110 moves horizontally along the surface of the carrier film 20, and sequentially pushes the connecting blocks 23 between the target blocks 21. The target blocks 21 are raised upward, so that the sides and the corners of the second surfaces 112 of the dies 11 are peeled off from the target blocks 21. More specifically, the scraper 110 moves horizontally along the surface of the carrier film 20 to the connecting block 23 between the two adjacent rows of target block combinations 22; the scraper 110 pushes the connecting blocks 23 of the two adjacent rows of target block combinations 22, and the two adjacent rows of target block combinations 22 are raised upward, so that the sides and the corners of the second surfaces 112 of all the dies 11 of the two adjacent rows of die combinations 14 are peeled off from all the target blocks 21 of the two adjacent rows of target block combinations 22. After the two rows of die combinations 14 have completed the peeling process, the scraper 110 continues to perform the peeling process on the other two rows of die combinations 14 until all the rows of die combinations 14 complete the peeling process.
[0061] In the third pre-edge/corner peeling method, as shown in FIGS. 11A, 11B, and 11C, at least one channel 1201 of an adsorption device 120 provides a negative pressure 1202, and sequentially adsorbs the connecting blocks 23 between the target blocks 21. The target blocks 21 are recessed downward, so that the sides and the corners of the second surfaces 112 of the dies 11 are peeled off from the target blocks 21. More specifically, the plurality of channels 1201 of the adsorption device 120 are arranged in a row, and each channel 1201 is aligned with the connecting block 23 between the two target blocks 21 of the two adjacent rows of target block combinations 22; the channels 1201 are synchronized to provide a negative pressure 1202, and each channel 1201 adsorbs the two target blocks 21 of the two adjacent rows of target block combinations 22 by the negative pressure 1202, and the two target blocks of the two adjacent rows of target block combinations 22 are recessed downward, so that the sides and the corners of the second surfaces 112 of all the dies 11 of the two adjacent rows of die combinations 14 are peeled off from all the target blocks 21 of the two adjacent rows of target block combinations 22. After the two rows of die combinations 14 have completed the peeling process, the adsorption device 120 continues to perform the peeling process on the other two rows of die combinations 14 until all the rows of die combinations 14 complete the peeling process.
[0062] [After the step S400 is completed, the sides and the corners of the second surfaces 112 of the dies 11 are peeled off from the carrier film 20, and the centers of the second surfaces 112 of the dies 11 are still attached to the center of the carrier film 20.
[0063] FIG. 12 is a schematic view of step S500 of the hybrid die bonding method of the present invention. In step S500, as shown in FIG. 12, before the carrier film 20 is turned over, the dies 11 are located above the carrier film 20, and after the carrier film 20 is turned over, the dies 11 are located below the carrier film 20. Because the viscosity of the carrier film 20 is still enough to stick to the centers of the dies 11, the dies 11 will not be detached from the carrier film 20 and fly out during the turning process of the carrier film 20, so that the dies 11 can be smoothly transferred to the first carrier 30.
[0064] FIG. 13 is a schematic view of step S600 of the hybrid die bonding method of the present invention. In step S600, as shown in FIG. 13, one side or one corner of the carrier film 20 is pulled upwards, then pulled sideways, and finally the carrier film 20 is gradually removed from the second surfaces 112 of the dies 11.
[0065] FIG. 14 is a schematic view of step S700 of the hybrid die bonding method of the present invention. In step S700, as shown in FIG. 14, the nozzle 70 sprays high-pressure gas, high-pressure liquid, or a mixture or plasma of high-pressure gas and high-pressure liquid to blow off or disperse the particles 12 from the second surfaces 112 of the dies 11, so that the particles 12 on the second surfaces 112 of the dies 11 are completely removed.
[0066] FIG. 15 is a schematic view of the first die transfer method in step S800 of the hybrid die bonding method of the present invention, and FIGS. 16 to 18 are the second die transfer method in step S800 of the hybrid die bonding method of the present invention. The two die transfer methods in step S800 will be described in detail below with reference to the drawings.
[0067] In the first die transfer method, as shown in FIG. 15, a pickup device 130 picks up a die 11 from the first carrier 30; the pickup device 130 moves the die 11; and the pickup device 130 places the die 11 on the substrate 40. The first surface 111 of the die 11 contacts with the substrate 40. The first die transfer method is repeatedly performed until all the dies 11 are transferred to the substrate 40.
[0068] The second die transfer method, as shown in FIG. 16, turns the first carrier 30 over, transfers the dies 11 to a second carrier 140, and the second surfaces 112 of the dies 11 contact with the second carrier 140. As shown in FIG. 17, the particles 12 on the first surfaces 111 of the dies 11 are removed. Specifically, the nozzle 70 sprays high-pressure gas, high-pressure liquid, or a mixture or plasma of high-pressure gas and high-pressure liquid to blow off or disperse the particles 12 from the first surfaces 111 of the dies 11, so that the particles 12 on the first surfaces 111 of the dies 11 are completely removed. As shown in FIG. 18, the pickup device 130 picks up a die 11 from the second carrier 140; the pickup device 130 moves the die 11; and the pickup device 130 place the die 11 on the substrate 40 with the second surface 112 of the die 11 in contact with the substrate 40. The second die transfer method is repeatedly performed until all the dies 11 are transferred to the substrate 40.
[0069] In summary, the present invention can peel off the sides and corners of the dies 11 from the carrier film 20, reducing the adhesive effect of the dies 11 being attached to the carrier film 20, thereby the dies 11 on the carrier film 20 can be transferred to the first carrier 30 in one run, and the carrier film 20 can be easily removed directly from the second surfaces 112 of the dies 11. Therefore, the transfer speed of the dies 11 is relatively fast, the efficiency is high, and the cost is low.
[0070] Furthermore, when the viscosity of the carrier film 20 is relatively high, the present invention can reduce the viscosity of the carrier film 20 first, and then peel off the sides and corners of the die 11 from the carrier film 20, so as to reduce the viscosity of the carrier film 20 as well as reduce the adhesive effect of the dies 11 being attached to the carrier film 20, thereby the dies 11 on the carrier film 20 can be transferred to the first carrier 30 in one run, and the carrier film 20 can be easily removed directly from the second surfaces 112 of the dies 11. Therefore, the transfer speed of the dies 11 is faster, the efficiency is higher, and the cost is lower.
[0071] In addition, the present invention can complete the peeling process for the two adjacent rows of die combinations 14 in one run, and all the rows of die combinations 14 can go through the peeling process several times, and then the sides and corners of the second surfaces 112 of the dies 11 can be peeled off from the target blocks 21, which greatly shortens the pre-edge/corner peeling time of the dies 11 and improves the pre-edge/corner peeling efficiency of the dies 11.
[0072] In addition, the present invention can completely remove the particles 12 on the first surfaces 111 and the second surfaces 112 of the dies 11, regardless of whether the first surfaces 111 or the second surfaces 112 of the dies 11 are to be bonded to the substrate 40. The bonding yield of the die 11 and the substrate 40 can be improved, and the die 11 and the substrate 40 will not co-encapsulate air bubbles to form a void. The bonding yield of the stacked dies 11 can also be improved.
[0073] In addition, the second die transfer method of the present invention can remove the particles 12 on the first surfaces 111 of the die 11 again, so as to prevent the residual particles from remaining 12 on the first surfaces 111 of the dies 11. Furthermore, the bonding yield between the die 11 and the substrate 40 or the bonding yield when the dies 11 are stacked on each other can be improved.
[0074] It is worth noting that the second die transfer method can also further turn the second carrier 140 over, transfer the dies 11 to the first carrier 30, and the first surfaces 111 of the dies 11 contact with the first carrier 30, and remove the particles 12 on the second surfaces 112 of the dies 11 to prevent the residual particles 12 from remaining on the second surfaces 112 of the dies 11, thereby improving the bonding yield between the die 11 and the substrate 40 or bonding yield when the dies 11 are stacked on each other.
[0075] If the dies 11 are repeatedly transferred to the first carrier 30 and the second carrier 140, the number of times of cleaning the first surface 111 and the second surface of the dies 11 can be increased, and the particles 12 on the first surfaces 111 and the second surfaces are removed to the extent that no particles remain, so as to ensure the best bonding yield between the dies 11 and the substrate 40 or when the dies 11 are stacked on each other.
[0076] More importantly, because the method of the present invention is developed for hybrid bonding technology, and the hybrid bonding technology is a tin-free bonding method, the present invention mainly uses the technology of dicing the wafer into dies without solder balls and without copper bumps. The substrate 40 without solder balls and without copper bumps is selected to emphasize that the method of the present invention is limited to use in hybrid bonding technology.
[0077] It should be noted that when performing tin-free packaging, the surfaces of the die 11 and the substrate 40 are very important. The surfaces of the die 11 and the substrate 40 will be directly connected to each other after the chemical-mechanical polishing process, so the surfaces of the die 11 and the substrate 40 must be close to the extent of a mirror surface, i.e., very smooth. The reason is that a slight change in the surface roughness may cause the bonding of the die 11 and the substrate 40 to fail. After the chemical-mechanical polishing process, due to the different materials, the degree of polishing is also different. Generally, the acceptable range of the error of the polishing degree, that is, the surface roughness Ra, is about ±10 nm, and if Ra exceeds 10 nm, two kinds of defects are prone to occur: (1) The copper contacts are over-polished; (2) Too much copper contact is reserved, and the base of the substrate 40 is over-polished.
[0078] Although the present invention has been described with reference to the preferred embodiments thereof, it is apparent to those skilled in the art that a variety of modifications and changes may be made without departing from the scope of the present invention which is intended to be defined by the appended claims.