FLUX-CORED WIRE FOR GAS-SHIELDED ARC WELDING

Abstract

A flux-cored wire for gas-shielded arc welding, including, in terms of mass % relative to a total mass of the wire, in the total of the steel outer sheath and the flux, C: 0.03 to 0.08%, Si: 0.1 to 0.6%, Mn: 1.5 to 2.8%, Cu: 0.01 to 0.5%, Ni: 0.35 to 0.98%, Ti: 0.05 to 0.25%, and B: 0.002 to 0.015%, Al: 0.05% or less, and including, in the flux, TiO.sub.2 conversion value: 3 to 8%, Al.sub.2O.sub.3 conversion value: 0.1 to 0.6%, SiO.sub.2 conversion value: 0.2 to 1.0%, ZrO.sub.2 conversion value: 0.20 to 0.65%, Mg: 0.2 to 0.8%, F conversion value: 0.05 to 0.25%, Na conversion value: 0.02 to 0.10%, and K conversion value: 0.05 to 0.20%.

Claims

1. A flux-cored wire for gas-shielded arc welding which has a steel outer sheath filled with a flux, comprising, in terms of mass % relative to a total mass of the wire, in the total of the steel outer sheath and the flux, C: 0.03 to 0.08%, Si: 0.1 to 0.6%, Mn: 1.5 to 2.8%, Cu: 0.01 to 0.5%, Ni: 0.35 to 0.98%, Ti: 0.05 to 0.25%, and B: 0.002 to 0.015%, Al: 0.05% or less, further comprising, in terms of mass % relative to a total mass of the wire, in the flux, the total of Ti oxides in terms of TiO.sub.2: 3 to 8%, the total of Al oxides in terms of Al.sub.2O.sub.3: 0.1 to 0.6%, the total of Si oxides in terms of SiO.sub.2: 0.2 to 1.0%, the total of Zr oxides in terms of ZrO.sub.2: 0.20 to 0.65%, Mg: 0.2 to 0.8%, the total of fluorine compounds in terms of F: 0.05 to 0.25%, the total of Na compounds in terms of Na: 0.02 to 0.10%, and the total of K compounds in terms of K: 0.05 to 0.20%, and the balance being Fe of the steel outer sheath, iron powder, Fe component of iron alloy powder and inevitable impurities.

2. The flux-cored wire for gas-shielded arc welding according to claim 1, further comprising, in terms of mass % relative to a total mass of the wire, in the flux, one or both of Bi and Bi oxides in terms of Bi: 0.003 to 0.010%.

Description

DETAILED DESCRIPTION

[0013] Hereinafter, the component composition of the flux-cored wire for gas-shielded arc welding of the present invention and reasons for limiting the component composition will be described. The content of each component is expressed in terms of mass % relative to a total mass of the flux-cored wire, and when representing the mass %, it is expressed simply as %.

[0014] [C: 0.03 to 0.08% in the Total of the Steel Outer Sheath and the Flux]

[0015] C has an effect of enhancing the strength of the weld metal. However, when C is less than 0.03%, the strength of the weld metal decreases. On the other hand, when C exceeds 0.08%, C is excessively retained in the weld metal, whereby the strength of the weld metal increases and the low-temperature toughness deteriorates. Accordingly, C is set to be 0.03 to 0.08% in the total of the steel outer sheath and the flux. C can be added from metal powder, alloy powder and the like from the flux, in addition to the components contained in the steel outer sheath.

[0016] [Si: 0.1 to 0.6% in the Total of the Steel Outer Sheath and the Flux]

[0017] Si partly becomes a weld slag at the time of welding, thereby improving the appearance and bead shape of the weld bead and contributing to improvement in welding workability. However, when Si is less than 0.1%, the effect of improving the appearance of the bead and the bead shape cannot be sufficiently obtained. On the other hand, when Si exceeds 0.6%, Si is excessively retained in the weld metal, whereby the low-temperature toughness of the weld metal deteriorates. Accordingly, Si is set to be 0.1 to 0.6% in the total of the steel outer sheath and the flux. Si can be added from metal Si, and alloy powder such as FeSi and FeSiMn from the flux, in addition to the components contained in the steel outer sheath.

[0018] [Mn: 1.5 to 2.8% in the Total of the Steel Outer Sheath and the Flux]

[0019] Mn, like Si, partly becomes a weld slag at the time of welding, thereby improving the appearance and bead shape of the bead and contributing to improvement in welding workability. In addition, Mn is retained in the weld metal, thereby having the effect of increasing the strength and the low-temperature toughness of the weld metal. However, when Mn is less than 1.5%, the bead appearance and the bead shape are poor, and the low-temperature toughness of the weld metal decreases. On the other hand, when Mn exceeds 2.8%, Mn is excessively retained in the weld metal and the strength of the weld metal increases, whereby the low-temperature toughness of the weld metal deteriorates instead. Accordingly, Mn is set to be 1.5 to 2.8% in the total of the steel outer sheath and the flux. Mn can be added from metal Mn, and alloy powder such as FeMn and FeSiMn from the flux, in addition to the components contained in the steel outer sheath.

[0020] [Cu: 0.01 to 0.5% in the Total of the Steel Outer Sheath and the Flux]

[0021] Cu has the effect of refining the structure of the weld metal and increasing low-temperature toughness and strength. However, when Cu is less than 0.01%, the strength and low-temperature toughness of the weld metal decrease. On the other hand, when Cu exceeds 0.5%, the strength of the weld metal becomes excessive and the low-temperature toughness decreases. Accordingly, Cu is set to be 0.01 to 0.5% in the total of the steel outer sheath and the flux. Cu can be added from metal Cu, and alloy powder such as CuZr and FeSiCu from the flux, in addition to Cu plating applied to the surface of the steel outer sheath.

[0022] [Ni: 0.35 to 0.98% in the Total of the Steel Outer Sheath and the Flux]

[0023] Ni has an effect of improving the low-temperature toughness of the weld metal. However, when Ni is less than 0.35%, the low-temperature toughness of the weld metal decreases. On the other hand, when Ni exceeds 0.98%, hot cracks tend to occur in the weld metal. Accordingly, Ni is set to be 0.35 to 0.98% in the total of the steel outer sheath and the flux. Ni can be added from metal Ni, and alloy powder such as FeNi from the flux, in addition to the components contained in the steel outer sheath.

[0024] [Ti: 0.05 to 0.25% in the Total of the Steel Outer Sheath and the Flux]

[0025] Ti has the effect of refining the structure of the weld metal and improving low-temperature toughness. However, when Ti is less than 0.05%, the low-temperature toughness of the weld metal decreases. On the other hand, when Ti exceeds 0.25%, an upper bainite structure that inhibits toughness is formed, and low-temperature toughness is lowered. Accordingly, Ti is set to be 0.05 to 0.25% in the total of the steel outer sheath and the flux. Ti can be added from metal Ti, and alloy powder such as FeTi from the flux, in addition to the components contained in the steel outer sheath.

[0026] [B: 0.002 to 0.015% in the Total of the Steel Outer Sheath and the Flux]

[0027] B has the effect of refining the microstructure of the weld metal by adding a trace amount and improving the low-temperature toughness of the weld metal. However, when B is less than 0.002%, the low-temperature toughness of the weld metal decreases. On the other hand, when B exceeds 0.015%, the low-temperature toughness of the weld metal decreases and hot cracks tend to occur in the weld metal. Accordingly, B is set to be 0.002 to 0.015% in the total of the steel outer sheath and the flux. B can be added from metal B, and alloy powder such as FeB and FeMnB from the flux, in addition to the components contained in the steel outer sheath.

[0028] [Al: 0.05% or Less in the Total of the Steel Outer Sheath and the Flux]

[0029] Al remains in the weld metal as an oxide and the toughness of the weld metal decreases. Especially when Al exceeds 0.05%, the toughness of the weld metal decreases. Accordingly, Al is set to 0.05% or less. Al may not be an essential element, and the content may be 0%.

[0030] [Total of Ti Oxides Contained in the Flux in Terms of TiO.sub.2: 3 to 8%]

[0031] Ti oxide contributes to the stabilization of the arc at the time of welding and has the effect of improving bead shape and contributing to the improvement of welding workability. Ti oxide also has the effect of adjusting the viscosity and melting point of the molten slag in the vertical upward welding and preventing metal sagging. However, when the total of Ti oxides in terms of TiO.sub.2 is less than 3%, the arc is unstable, the spatter generation amount increases, the bead appearance and the bead shape deteriorate, and the low-temperature toughness of the weld metal decreases. Metal sagging occurs and the bead appearance and bead shape become poor in vertical upward welding. On the other hand, when the total of Ti oxides in terms of TiO.sub.2 exceeds 8%, the arc is stable and the spatter generation amount is also small, but the Ti oxide excessively remains in the weld metal, whereby the low-temperature toughness decreases. Accordingly, the total of Ti oxides contained in the flux in terms of TiO.sub.2 is set to be 3 to 8%. The Ti oxide is added from rutile, titanium oxide, titanium slag, ilmenite or the like from the flux.

[0032] [Total of Al Oxides Contained in the Flux in Terms of Al.sub.2O.sub.3: 0.1 to 0.6%]

[0033] Al oxide has the effect of adjusting the viscosity and melting point of the weld slag at the time of welding, and particularly preventing the metal sagging in the vertical upward welding. However, when the total of Al oxides in terms of Al.sub.2O.sub.3 is less than 0.1%, metal sagging occurs and the bead appearance and bead shape become poor in vertical upward welding. On the other hand, when the total of Al oxides in terms of Al.sub.2O.sub.3 exceeds 0.6%, the Al oxide excessively remains in the weld metal, whereby the low-temperature toughness decreases. Accordingly, the total of Al oxides contained in the flux in terms of Al.sub.2O.sub.3 is set to be 0.1 to 0.6%. The Al oxide can be added from alumina or the like from the flux.

[0034] [Total of Si Oxides Contained in the Flux in Terms of SiO.sub.2: 0.2 to 1.0%]

[0035] Si oxide has the effect of improving slag encapsulation by adjusting the viscosity and melting point of the molten slag and improving compatibility in the bead toe. However, when the total of Si oxides in terms of SiO.sub.2 is less than 0.2%, the slag encapsulation is deteriorated, the bead appearance is poor, and compatibility in the bead toe also becomes poor. On the other hand, when the total of Si oxides in terms of SiO.sub.2 exceeds 1.0%, the Si oxide excessively remains in the weld metal, whereby the low-temperature toughness decreases. Accordingly, the total of Si oxides contained in the flux in terms of SiO.sub.2 is set to be 0.2 to 1.0%. The Si oxide can be added from silica sand, zircon sand, sodium silicate or the like from the flux.

[0036] [Total of Zr Oxides Contained in the Flux in Terms of ZrO.sub.2: 0.20 to 0.65%]

[0037] Zr oxide has the effect of adjusting the viscosity and melting point of the weld slag, and particularly preventing the metal sagging in the vertical upward welding. However, when the total of Zr oxides in terms of ZrO.sub.2 less than 0.20%, metal sagging occurs in vertical upward welding and the bead appearance and the bead shape become poor. On the other hand, when the total of Zr oxides in terms of ZrO.sub.2 exceeds 0.65%, slag removability deteriorates. Accordingly, the total of Zr oxides contained in the flux in terms of ZrO.sub.2 is set to be 0.20 to 0.65%. The Zr oxide can be added from zircon sand, zirconium oxide or the like from the flux.

[0038] [Mg Contained in the Flux: 0.2 to 0.8%]

[0039] Mg functions as a strong deoxidizer, thereby having the effect of reducing oxygen in the weld metal and enhancing the low-temperature toughness of the weld metal. However, when Mg is less than 0.2%, the low-temperature toughness of the weld metal decreases. On the other hand, when Mg exceeds 0.8%, it reacts violently with oxygen in the arc at the time of welding, and the generation amounts of spatter and fume increase. Accordingly, Mg contained in the flux is set to be 0.2 to 0.8%. Mg can be added from metal Mg, and alloy powder such as AlMg from the flux.

[0040] [Total of Fluorine Compounds Contained in the Flux in Terms of F: 0.05 to 0.25%]

[0041] Fluorine compounds have the effect of stabilizing the arc. However, when the total of the fluorine compounds in terms of F is less than 0.05%, the arc becomes unstable. On the other hand, when the total of the fluorine compounds in terms of F exceeds 0.25%, the arc becomes unstable, and the generation amounts of spatter and fume increase. Further, in the vertical upward welding, metal sagging tends to occur and the bead appearance and the bead shape become poor. Accordingly, the total of the fluorine compounds contained in the flux in terms of F is set to be 0.05 to 0.25%. The fluorine compound can be added from CaF.sub.2, NaF, KF, LiF, MgF.sub.2, K.sub.2SiF.sub.6, K.sub.2ZrF.sub.6, Na.sub.2AlF.sub.6, AlF.sub.3 and the like, and the F conversion value is the total content of F contained therein.

[0042] [Total of Na Compounds Contained in the Flux in Terms of Na: 0.02 to 0.10%]

[0043] The Na compound acts as an arc stabilizer and a slag former. When the total of the Na compounds in terms of Na is less than 0.02%, the concentration of the arc decreases in all position welding and becomes unstable, and the spatter generation amount increases. On the other hand, when the total of the Na compounds in terms of Na exceeds 0.10%, the arc excessively concentrates and the arc itself becomes thin, so that metal sagging tends to occur in vertical upward welding. Accordingly, the total of the Na compounds contained in the flux in terms of Na is set to be 0.02 to 0.10%. The Na compound can be added from a solid component of water glass composed of sodium silicate, and powders such as NaF, Na.sub.2AlF.sub.6 and sodium titanate and the like from the flux, and the Na conversion value is the total content of Na contained therein.

[0044] [Total of K Compounds Contained in the Flux in Terms of K: 0.05 to 0.20%]

[0045] Like the Na compound, the K compound acts as an arc stabilizer and a slag former, when the total of the K compounds in terms of K is less than 0.05%, the arc becomes unstable in all position welding, and the spatter generation amount increases. On the other hand, when the total of K compound in terms of K exceeds 0.20%, slag encapsulation and slag removability become poor in all position welding and shape and appearance of the bead also become poor. The K compound can be added from a solid component of water glass composed of potassium silicate, and powders such as potassium feldspar, K.sub.2SiF.sub.6, K.sub.2ZrF.sub.6 and potassium titanate and the like from the flux, and the K conversion value is the total content of K contained therein.

[0046] [One or Both of Bi and Bi Oxides Contained in the Flux in Terms of Bi: 0.0 03 to 0.010%]

[0047] Bi promotes peeling of the weld slag from the weld metal and improves slag removability. When one or both of Bi and Bi oxides in terms of Bi is less than 0.003%, the effect of promoting slag removal is insufficient. On the other hand, when one or both of Bi and Bi oxides in terms of Bi exceeds 0.010%, cracks may occur in the weld metal and the low-temperature toughness decreases. Accordingly, one or both of Bi and Bi oxides contained in the flux in terms of Bi is 0.003 to 0.010%. The Bi and Bi oxides are added from metal Bi, oxidized Bi and the like.

[0048] The flux-cored wire for gas-shielded arc welding of the present invention has a structure in which a steel outer sheath is formed into a pipe shape and a flux is filled inside the steel outer sheath. As a kind of wire, wires can be broadly divided into wires with seamless steel outer sheath obtained by welding a joint of the formed steel outer sheath and wires without a seam on the steel outer sheath without welding a joint of the steel outer sheath. In the present invention, it is possible to adopt a wire of any sectional structure, but a wire without a seam on the steel outer sheath can be subjected to a heat treatment for reducing the total amount of hydrogen in the wire, and since there is no moisture absorption of the flux after production, the amount of diffusible hydrogen of the weld metal can be reduced and the low temperature cracking resistance can be improved, which are more preferable.

[0049] The balance of the flux-cored wire for gas-shielded arc welding of the present invention is Fe of the steel outer sheath, iron powder added for component adjustment, Fe component of iron alloy powder such as FeMn and FeSi alloys and inevitable impurities. Although the flux filling rate is not particularly limited, it is preferably 8 to 20% relative to the total mass of the wire from the viewpoint of productivity.

EXAMPLES

[0050] Hereinafter, the effects of the present invention will be specifically described.

[0051] SPCC specified in JIS G 3141 as the components shown in Table 1 as a steel outer sheath was used to form into a U-shape in the process of forming a steel outer sheath, then a wire without a seam on the steel outer sheath by welding a joint of the formed steel outer sheath was formed and drawn to prototype flux-cored wires of various components shown in Table 1 and Table 2. The wire diameter was set to be 1.2 mm.

TABLE-US-00001 TABLE 1 Wire component (mass %) Flux TiO.sub.2 Wire Total of steel outer sheath and flux conversion Category symbol C Si Mn Cu Ni Ti B Al value Examples W1 0.04 0.19 1.86 0.22 0.55 0.12 0.0082 0.01 4.5 of present W2 0.07 0.46 1.54 0.39 0.72 0.21 0.0051 0.02 5.2 invention W3 0.03 0.15 2.71 0.12 0.36 0.08 0.0037 0.01 5.9 W4 0.04 0.43 1.98 0.32 0.81 0.12 0.0141 0.03 7.1 W5 0.07 0.37 1.95 0.28 0.65 0.24 0.0046 0.04 5.3 W6 0.05 0.58 2.14 0.02 0.58 0.09 0.0064 0.01 6.5 W7 0.06 0.12 2.18 0.33 0.43 0.17 0.0092 0.02 7.8 W8 0.04 0.36 2.05 0.15 0.97 0.05 0.0058 5.6 W9 0.03 0.44 1.79 0.48 0.57 0.22 0.0035 0.01 4.4 W10 0.08 0.37 1.86 0.17 0.74 0.14 0.0067 0.04 3.9 W11 0.05 0.25 2.12 0.21 0.66 0.11 0.0029 0.02 6.8 W12 0.04 0.18 2.03 0.08 0.51 0.15 0.0025 0.03 5.2 W13 0.05 0.22 1.91 0.06 0.82 0.21 0.0073 3.1 W14 0.04 0.36 2.28 0.33 0.39 0.07 0.0095 0.01 6.4 W15 0.05 0.41 2.16 0.27 0.75 0.13 0.0117 0.02 7.2 Wire component (mass %) Flux Al.sub.2O.sub.3 SiO.sub.2 ZrO.sub.2 F Na K Wire conversion conversion conversion conversion conversion conversion Bi conversion Category symbol value value value Mg value value value value Others Examples W1 0.31 0.51 0.41 0.52 0.11 0.04 0.08 Balance of present W2 0.18 0.45 0.36 0.31 0.21 0.07 0.11 0.004 Balance invention W3 0.52 0.38 0.33 0.28 0.12 0.03 0.15 Balance W4 0.43 0.35 0.52 0.44 0.09 0.05 0.09 0.007 Balance W5 0.12 0.48 0.46 0.38 0.07 0.06 0.13 0.009 Balance W6 0.48 0.67 0.38 0.64 0.14 0.03 0.17 Balance W7 0.25 0.43 0.27 0.51 0.21 0.05 0.20 Balance W8 0.36 0.71 0.55 0.28 0.18 0.10 0.05 0.006 Balance W9 0.31 0.56 0.46 0.78 0.15 0.08 0.17 Balance W10 0.57 0.62 0.34 0.35 0.12 0.04 0.12 0.005 Balance W11 0.33 0.28 0.21 0.54 0.17 0.02 0.08 Balance W12 0.19 0.33 0.29 0.22 0.24 0.07 0.14 0.008 Balance W13 0.27 0.51 0.64 0.62 0.18 0.05 0.09 Balance W14 0.43 0.21 0.22 0.55 0.09 0.04 0.16 Balance W15 0.35 0.96 0.31 0.49 0.06 0.06 0.07 Balance 1) One or more of CaF.sub.2, AlF.sub.3, NaF, K.sub.2SiF.sub.6, K.sub.2ZrF.sub.6, and Na.sub.3AlF.sub.6 were used as fluorine compounds. 2) One or more of sodium silicate, NaF and Na.sub.3AlF.sub.6 were used as Na compounds. 3) One or more of potassium silicate, K.sub.2SiF.sub.6, and K.sub.2ZrF.sub.6 were used as K compounds. 4) Others: Fe of the steel outer sheath, iron powder, Fe component of iron alloy and inevitable impurities

TABLE-US-00002 TABLE 2 Wire component (mass %) Flux TiO.sub.2 Wire Total of steel outer sheath and flux conversion Category symbol C Si Mn Cu Ni Ti B Al value Comparative W16 0.02 0.22 1.85 0.09 0.48 0.14 0.0074 0.02 5.3 Examples W17 0.09 0.38 2.26 0.14 0.45 0.22 0.0062 0.01 6.4 W18 0.04 0.04 1.88 0.37 0.39 0.08 0.0085 0.03 4.8 W19 0.05 0.66 2.16 0.28 0.77 0.09 0.0043 7.2 W20 0.08 0.48 1.42 0.32 0.87 0.15 0.0058 0.01 5.5 W21 0.04 0.31 2.92 0.25 0.44 0.22 0.0037 0.02 6.1 W22 0.04 0.16 1.75 0.004 0.41 0.17 0.0045 0.02 7.3 W23 0.06 0.54 2.23 0.56 0.83 0.21 0.0075 0.01 4.5 W24 0.06 0.27 2.11 0.18 0.32 0.13 0.0093 0.03 3.9 W25 0.04 0.33 2.06 0.29 1.01 0.16 0.0102 0.07 5.9 W26 0.04 0.42 1.72 0.33 0.48 0.03 0.0048 6.4 W27 0.05 0.45 2.16 0.26 0.55 0.28 0.0078 0.02 6.1 W28 0.05 0.38 2.34 0.17 0.73 0.09 0.0011 0.02 7.5 W29 0.07 0.27 2.05 0.38 0.64 0.21 0.0162 0.01 7.2 W30 0.05 0.34 1.94 0.41 0.77 0.17 0.0038 2.4 W31 0.04 0.46 2.14 0.29 0.85 0.16 0.0051 0.02 8.7 W32 0.05 0.31 1.94 0.15 0.79 0.19 0.0063 5.2 Wire component (mass %) Flux Al.sub.2O.sub.3 SiO.sub.2 ZrO.sub.2 F Na K Wire conversion conversion conversion conversion conversion conversion Bi conversion Category symbol value value value Mg value value value value Others Comparative W16 0.34 0.55 0.21 0.13 0.13 0.05 0.12 Balance Examples W17 0.04 0.61 0.52 0.55 0.17 0.04 0.17 0.004 Balance W18 0.65 0.35 0.61 0.37 0.08 0.06 0.07 Balance W19 0.26 0.43 0.18 0.44 0.09 0.07 0.16 0.007 Balance W20 0.17 0.29 0.48 0.28 0.24 0.05 0.02 Balance W21 0.19 0.44 0.24 0.63 0.11 0.04 0.11 Balance W22 0.25 0.13 0.22 0.58 0.08 0.08 0.08 Balance W23 0.43 0.74 0.68 0.39 0.13 0.07 0.07 0.001 Balance W24 0.51 0.64 0.28 0.87 0.19 0.03 0.18 Balance W25 0.36 0.75 0.47 0.29 0.21 0.04 0.17 Balance W26 0.22 0.61 0.33 0.73 0.04 0.06 0.13 0.005 Balance W27 0.15 0.54 0.25 0.55 0.26 0.07 0.09 0.007 Balance W28 0.24 0.35 0.48 0.47 0.09 0.01 0.12 Balance W29 0.38 0.42 0.31 0.51 0.18 0.14 0.14 Balance W30 0.52 0.56 0.29 0.39 0.12 0.09 0.08 0.012 Balance W31 0.29 0.63 0.43 0.56 0.17 0.05 0.23 Balance W32 0.32 1.06 0.35 0.52 0.15 0.04 0.08 Balance 1) One or more of CaF.sub.2, AlF.sub.3, NaF, K.sub.2SiF.sub.6, K.sub.2ZrF.sub.6, and Na.sub.3AlF.sub.6 were used as fluorine compounds. 2) One or more of sodium silicate, NaF and Na.sub.3AlF.sub.6 were used as Na compounds. 3) One or more of potassium silicate, K.sub.2SiF.sub.6, and K.sub.2ZrF.sub.6 were used as K compounds. 4) Others: Fe of the steel outer sheath, iron powder, Fe component of iron alloy and inevitable impurities

[0052] The prototype wires were evaluated for welding workability by horizontal fillet welding and vertical upward fillet welding using a steel plate specified in JIS Z G3126 SLA365, and was evaluated for mechanical characteristics as a deposited metal test. These welding conditions are shown in Table 3.

TABLE-US-00003 TABLE 3 Plate Welding Welding thickness Welding Shielding Current Voltage speed Test item position (mm) method gas Groove (A) (V) (cm/min) Welding Horizontal 12 Automatic Ar-20% T shaped 270 29 50 workability fillet MAG CO.sub.2 25 horizontal evaluation L/min fillet Vertical 12 Semi- T shaped 210 23 about 10 upward automatic horizontal MAG fillet Deposited Downward 20 Automatic In 270 29 30 metal test MAG conformity with JIS Z 3111

[0053] The welding workability was evaluated by investigating the stability of the arc, the generation state of spatter and fume, the slag removability and the appearance and shape of the bead in the horizontal fillet welding test, and by investigating, in particular, existence of molten metal sagging, the appearance and shape of the bead in the vertical upward welding test.

[0054] In the deposited metal test, welding was conducted according to JIS Z 3111, X-ray radiography was performed according to JIS Z 3106 to investigate existence of weld defect, then a tensile test piece (AO) and impact test piece (V notch specimen) were taken from the center part in the plate thickness direction of the deposited metal, and mechanical tests were performed. Evaluation of toughness was performed by a Charpy impact test at 60 C. The test was repeatedly for each test piece, and a test piece having an average of three absorption energies of 60 J or more was evaluated as good. For the evaluation of the tensile test, a test piece having a tensile strength of 570 to 720 MPa or more was evaluated as good. These results are summarized in Tables 4 and 5.

TABLE-US-00004 TABLE 4 Vertical upward Horizontal fillet welding test result welding test result Deposited metal test result Stability Spatter Fume Slag Appearance Existence Appearance X-ray Tensile Absorption Overall Wire of generation generation remov- and shape of metal and shape radiography strength energy at evalu- Category symbol arc state state ability of bead sagging of bead test result (MPa) 60 C. (J) ation Examples W1 Stable Less Less Good Good None Good No defect 599 87 of present W2 Stable Less Less Good Very good None Good No defect 624 101 invention W3 Stable Less Less Good Good None Good No defect 706 91 W4 Stable Less Less Good Very good None Good No defect 669 82 W5 Stable Less Less Good Very good None Good No defect 658 73 W6 Stable Less Less Good Good None Good No defect 674 93 W7 Stable Less Less Good Good None Good No defect 671 106 W8 Stable Less Less Good Very good None Good No defect 681 98 W9 Stable Less Less Good Good None Good No defect 608 95 W10 Stable Less Less Good Very good None Good No defect 647 86 W11 Stable Less Less Good Good None Good No defect 654 97 W12 Stable Less Less Good Very good None Good No defect 615 105 W13 Stable Less Less Good Good None Good No defect 613 97 W14 Stable Less Less Good Good None Good No defect 679 84 W15 Stable Less Less Good Good None Good No defect 677 72

TABLE-US-00005 TABLE 5 Vertical upward Horizontal fillet welding test result welding test result Deposited metal test result Wire Stability Spatter Fume Slag Appearance Existence Appearance X-ray Tensile Absorption Overall sym- of generation generation remov- and shape of metal and shape radiography strength energy at evalu- Category bol arc state state ability of bead sagging of bead test result (MPa) 60 C. (J) ation Com- W16 Stable Less Less Good Good None Good No defect 566 48 x parative W17 Stable Less Less Very Good Yes Poor No defect 735 54 x Examples good W18 Stable Less Less Good Poor None Poor No defect 623 42 x W19 Stable Less Less Very Good Yes Poor No defect 688 52 x good W20 Unstable Much Less Good Poor None Good No defect 593 46 x W21 Stable Less Less Good Good None Good No defect 748 52 x W22 Stable Less Less Good Poor None Good No defect 559 55 x W23 Stable Less Less Poor Good None Good No defect 738 53 x W24 Stable Much Much Good Good None Good No defect 655 38 x W25 Stable Less Less Good Good None Good Crater 654 41 x cracking W26 Unstable Less Less Very Good None Good No defect 582 44 x good W27 Unstable Much Less Very Poor Yes Poor No defect 673 51 x good W28 Unstable Much Less Good Good None Good No defect 686 37 x W29 Stable Less Less Good Good Yes Poor Crater 678 43 x cracking W30 Unstable Much Less Very Poor Yes Poor Crater 648 47 x good cracking W31 Stable Less Less Poor Poor None Poor No defect 669 49 x W32 Stable Less Less Good Good None Good No defect 618 52 x

[0055] Wire symbols W1 to W15 in Tables 1 and 4 are examples of the present invention, and wire symbols W16 to W32 in Tables 2 and 5 are comparative examples. The wire symbols W1 to W15 which are examples of the present invention have C, Mn, Cu, Ni, Ti, B, Al, the total of Ti oxides in terms of TiO.sub.2, the total of Al oxides in terms of Al.sub.2O.sub.3, the total of Si oxides in terms of SiO.sub.2, the total of Zr oxides in terms of ZrO.sub.2, Mg, the total of the fluorine compounds in terms of F, the total of the Na compounds in terms of Na, and the total of the K compounds in terms of K within the ranges specified in the present invention. Thus, the result were extremely satisfactory such that welding workability in the horizontal fillet welding test was good, there was no metal sagging in the vertical upward welding test, there were no weld defect in the deposited metal test, and good values of the tensile strength and absorption energy of the deposited metal were obtained. Since the wire symbols W2, W4, W5, W8, W10 and W12 contained an appropriate amount in terms of Bi, slag removability was very good.

[0056] Among the comparative examples, since the wire symbol W16 contained less C, the tensile strength of the deposited metal was low. Also, since the wire symbol W16 contained less Mg, the absorption energy of the deposited metal was also low.

[0057] Since the wire symbol W17 contained much C, the tensile strength of the deposited metal was high and the absorption energy was low. Also, since the total of Al oxides in terms of Al.sub.2O.sub.3 was small, metal sagging occurred and the appearance and shape of the bead was poor in the vertical upward welding test.

[0058] Since the wire symbol W18 contained less Si, the appearance and shape of the bead was poor in both the horizontal fillet welding test and the vertical upward welding test. Also, since the total of Al oxides in terms of Al.sub.2O.sub.3 was large, the absorption energy of the deposited metal was low.

[0059] Since the wire symbol W19 contained much Si, the absorption energy of the deposited metal was low. In addition, since the total of Zr oxides in terms of ZrO.sub.2 was small, metal sagging occurred and the appearance and shape of the bead was poor in the vertical upward welding test.

[0060] Since the wire symbol W20 had less Mn, the appearance and shape of the bead was poor in the horizontal fillet welding test, and the absorption energy of the deposited metal was low. Also, since the total of the K compounds in terms of K was small, the arc was unstable and the spatter generation amount was large in the horizontal fillet welding test.

[0061] Since the wire symbol W21 contained much Mn, the tensile strength of the deposited metal was high and the absorption energy was low.

[0062] Since the wire symbol W22 had less Cu, the tensile strength of the deposited metal was low and the absorption energy was also low. Also, since the total of Si oxides in terms of SiO.sub.2 was small, slag encapsulation was poor and the appearance and shape of the bead were poor in the horizontal fillet welding test.

[0063] Since the wire symbol W23 contained much Cu, the tensile strength of the deposited metal was high and the absorption energy was low. Also, since the total of Zr oxides in terms of ZrO.sub.2 was large, slag removability was poor in the horizontal fillet welding test. Since the Bi conversion value was small, the effect of improving the slag removability was not obtained.

[0064] Since the wire symbol W24 contained less Ni, the absorption energy of the deposited metal was low. Also, since the wire symbol W24 contained much Mg, spatter and fume were much generated in the horizontal fillet welding test.

[0065] Since the wire symbol W25 contained much Ni, crater cracking occurred in the deposited metal test. In addition, since the wire symbol W25 contained much Al, the absorption energy of the deposited metal was low.

[0066] Since the wire symbol W26 contained less Ti, the absorption energy of the deposited metal was low. Also, since the total of the fluorine compounds in terms of F was small, the arc was unstable in the horizontal fillet welding test.

[0067] Since the wire symbol W27 contained much Ti, the absorption energy of the deposited metal was low. Also, since the total of the fluorine compounds in terms of F was large, the arc was unstable, the spatter generation amount was large, the appearance and shape of the bead were also poor in the horizontal fillet welding test, and metal sagged and the appearance and shape of the bead were poor in the vertical upward welding test.

[0068] Since the wire symbol W28 contained less B, the absorption energy of the deposited metal was low. Also, since the total of the Na compounds in terms of Na was small, the arc was unstable and the spatter generation amount was large in the horizontal fillet welding test.

[0069] Since the wire symbol W29 contained much B, crater cracking occurred in the deposited metal test, and the absorption energy of the deposited metal was low. Also, since the total of the Na compounds in terms of Na was large, metal sagged and the appearance and shape of the bead were poor in the vertical upward welding test.

[0070] In the wire symbol W30, since the total of Ti oxides in terms of TiO.sub.2 was small, the arc was unstable, the spatter generation amount was large and the appearance and shape of the bead were poor in the horizontal fillet welding test, and metal sagging occurred and the appearance and shape of the bead were poor in the vertical upward welding test. Also, since the Bi conversion value was large, crater cracking occurred in the deposited metal test, and the absorption energy of the deposited metal was low.

[0071] In the wire symbol W31, since the total of Ti oxides in terms of TiO.sub.2 was large, the absorption energy of the deposited metal was low. Also, since the total of the K compounds in terms of K was large, slag removability was poor and the shape and appearance of the bead were also poor in horizontal fillet welding test and vertical upward welding test.

[0072] In the wire symbol W32, since the total of Si oxides in terms of SiO.sub.2 was large, the absorption energy of the deposited metal was low.