Single Crystal Piezoelectric RF Resonators and Filters

Abstract

A filter package comprising an array of piezoelectric films comprising an array of mixed single crystals that each comprise doped Aluminum Nitride, typically Al.sub.xGa.sub.(1-x)N or Sc.sub.xAl.sub.(1-x)N, that is sandwiched between an array of lower electrodes and an array of upper electrodes comprising metal layers and silicon membranes with cavities thereover: the array of lower electrodes being coupled to an interposer with a first cavity between the array of lower electrodes and the interposer; the array of silicon membranes having a known thickness and attached over the array of upper electrodes with an array of upper cavities, each upper cavity between a silicon membrane of the array and a common silicon cover; each upper cavity aligned with a piezoelectric film, an upper electrode and silicon membrane, the upper cavities having side walls comprising SiO.sub.2; the individual piezoelectric films, their upper electrodes and silicon membranes thereover being separated from adjacent piezoelectric films, upper electrodes and silicon membranes by a passivation material.

Claims

1. A filter package comprising an array of piezoelectric films comprising a an array of mixed single crystals that each comprise doped Aluminum Nitride that is sandwiched between an array of lower electrodes and an array of upper electrodes comprising metal layers and silicon membranes with cavities thereover: the array of lower electrodes being coupled to an interposer with a first cavity between the array of lower electrodes and the interposer; the array of silicon membranes having a known thickness and attached over the array of upper electrodes with an array of upper cavities, each upper cavity between a silicon membrane of the array and a common silicon cover; each upper cavity aligned with a piezoelectric film, an upper electrode and silicon membrane, the upper cavities having side walls comprising SiO.sub.2; the individual piezoelectric films, their upper electrodes and silicon membranes thereover being separated from adjacent piezoelectric films, upper electrodes and silicon membranes by a passivation material.

2. The filter package of claim 1 wherein the mixed single crystals are Al.sub.xGa.sub.(1-x)N or Sc.sub.xAl.sub.(1-x)N.

3. The filter package of claim 1 wherein the mixed single crystal is Sc.sub.xAl.sub.(1-x)N such that x0.25.

4. The filter package of claim 1 wherein the mixed single crystal is Sc.sub.xAl.sub.(1-x)N such that 0.05x0.13.

5. The filter package of claim 3 wherein each piezoelectric film of Sc.sub.xAl.sub.(1-x)N comprises a single crystal having C axis orientation.

6. The filter package of claim 3 wherein the piezoelectric films are further characterized by a surface roughness having a RMS (root mean square) of less than 1 nm and a rocking curve FWHM value of less than 500 arcsec.

7. The filter package of claim 3, wherein said piezoelectric films have a thickness of up to 2 microns.

8. The filter package of claim 1, wherein the said silicon membranes comprise single crystal silicon with an orientation selected from the group consisting of <100>, <110> and <111>.

9. The silicon membranes of claim 8 being doped, thereby having electrical resistivity equal or lower than 0.005 ohm cm.

10. The silicon membranes of claim 8, being n doped with a dopant selected from the group comprising Phosphorous, Antimony and Arsenic.

11. The filter package of claim 8 wherein the silicon membrane is doped with arsenic and has a thickness trimmed to a nominal range of 0.5 to 1.5 microns with tolerances of down to 5 Angstroms

12. The filter package of claim 8 wherein the cavities have a thickness of 3 microns within maximum tolerances of 5%.

13. The filter package of claim 1, wherein the said common silicon cover comprises silicon single crystal having an orientation selected from the group consisting of <100>, <110> and <111>.

14. The filter package of claim 13 wherein the common silicon cover is further characterized by an electrical resistivity higher than 5000 ohm cm.

15. The filter package of claim 14 wherein the orientation of the common silicon cover is <100> to tolerances of 0.5 and a thickness of 400 to 450 microns10 microns.

16. The filter package of claim 1, wherein thickness of said array of piezoelectric films is at least half the thickness of said array of silicon membranes.

17. The filter package of claim 1 wherein said array of silicon membranes has a thickness in the range of 0.5 micron to 10 microns and is coupled to the silicon cover by silicon oxide.

18. The filter package of claim 1 wherein the upper and lower electrodes each comprise at least one metal selected from the group consisting of aluminum, gold, tungsten and molybdenum.

19. The filter package of claim 19 wherein edges of the lower electrodes are stiffened by an under bump metallization material comprising a titanium adhesion layer followed by at least one layer comprising tungsten, tantalum or molybdenum.

20. The filter package of claim 20 wherein the under bump metallization material connects the lower electrode to copper pillars by a copper seed layer or to gold pillars by a gold seed layer.

21. The filter package of claim 1 wherein the lower electrode is coupled to the interposer by solder tipped copper pillars or by gold pillars.

22. The filter package of claim 1 wherein the upper electrodes comprise at least a metal adhesion layer selected from the group comprising titanium or chromium.

23. The filter package of claim 1 wherein the upper electrodes are multilayer

24. electrodes comprising at least one metal layer with a relatively low DC resistance and a second metal layer with a relatively high acoustic impedance.

25. The filter package of claim 1 wherein the upper electrodes are multilayer electrodes comprising a first layer of aluminum or gold and a second layer of tungsten or molybdenum.

26. The filter package of claim 25 wherein the at least one metal layer with a relatively low DC resistance comprises aluminum and is proximal to the piezoelectric layer, and the second metal layer with a relatively high acoustic impedance comprises tungsten or molybdenum, and the surface of which that is bonded to the silicon membrane and the contacted surface of the silicon membrane are characterized by having roughnesses with an RMS of less than 0.5 nm.

27. The filter package of claim 25 wherein there are no gold bonding layers and the aluminum is surface activated bonded to the mixed single crystals and the tungsten or molybdenum is surface activated bonded to the silicon membrane.

28. The filter package of claim 19 wherein a bonding adhesion layer selected from the group of titanium and chromium attaches the array of lower electrodes to the array of doped AlN single crystals.

29. The filter package of claim 1, wherein the passivation material is selected from the group consisting of polyimide, Benzocyclobutene (BCB), SiO.sub.2,Ta.sub.2O.sub.5, and Si.sub.3N.sub.4.

30. The filter package of claim 1 wherein the upper cavities between the silicon membrane and the silicon handle have side walls comprising residual silicon oxide.

31. The filter package of claim 1 wherein the upper cavities between the array of silicon membrane and the common silicon cover have a thickness of between 3 and 10 microns.

32. The filter package of claim 1 wherein a bottom surface of the array of piezoelectric crystals and metal contacts to the lower electrode and the surrounding of the metal bumps for coupling to the interposer are at least partially protected by a lower passivation layer.

33. The filter package of claim 33 wherein the lower passivation layer is selected from the group consisting of polyimide, Benzocyclobutene (BCB), SiO.sub.2, Ta.sub.2O.sub.5, and Si3N4.

34. The filter package of claim 1 wherein the silicon wafer is attached to the upper electrode by an adhesion layer adjacent to the upper electrode, a bonding layer and a further adhesion layer attached to the silicon wafer thereby creating a composite electrode.

35. The filter package of claim 1 wherein the silicon cover has a thickness of less than 200 microns.

36. The filter package of claim 1 wherein the silicon cover over the cavity is perforated with through-silicon via holes.

37. The filter package of claim 1 encapsulated in polymer over-mold/under-fill (MUF), wherein a barrier between the filter array and the interposer provides a perimeter wall of the lower cavity, wherein said barrier comprises at least one of an SU8 gasket around the filter array that is attached to the lower electrode and an epoxy dam attached to the interposer.

38. The filter package of claim 1, wherein the interposer comprises at least one via layer and one routing layer of copper encapsulated by a dielectric matrix and further comprises either copper pads coupled to copper pillars or gold pads coupled to gold pillars, and optionally further comprises solder tips on the copper pillars.

39. The filter package of claim 38, wherein the interposer comprises a polymer matrix selected from the group consisting of polyimide, epoxy, BT (Bismaleimide/Triazine), Polyphenylene Ether (PPE), Polyphenylene Oxide (PPO) and their blends

40. The filter package of claim 39, wherein the interposer further comprises glass fibers and/or ceramic fillers.

41. The filter package of claim 38, wherein the interposer comprises a Low Temperature Cofired Ceramic (LTCC) substrate.

42. The filter package of claim 38, wherein the interposer comprises a glass substrate with through glass vias.

Description

BRIEF DESCRIPTION OF FIGURES

[0184] For a better understanding of the invention and to show how it may be carried into effect, reference will now be made, purely by way of example, to the accompanying drawings.

[0185] With specific reference now to the drawings in detail, it is stressed that the particulars shown are by way of example and for purposes of illustrative discussion of the preferred embodiments of the present invention only, and are presented in the cause of providing what is believed to be the most useful and readily understood description of the principles and conceptual aspects of the invention. In this regard, no attempt is made to show structural details of the invention in more detail than is necessary for a fundamental understanding of the invention; the description taken with the drawings making apparent to those skilled in the art how the several forms of the invention may be embodied in practice. In particular, it will be appreciated that the schematic illustrations are not to scale, and the thickness of some very thin layers is exaggerated. In the accompanying drawings:

[0186] FIG. 1 is a schematic not-to-scale cross section representation of a Composite FBAR filter module which combines a plurality of Composite FBAR resonators coupled in half ladder or lattice arrangements or combinations thereof.

[0187] FIG. 2 is a simplified circuit of a ladder type RF filter configuration;

[0188] FIG. 3 is a graph showing the transmission response of the ladder filter configuration of FIG. 2;

[0189] FIG. 4 is a is a simplified circuit of a lattice type RF filter configuration;

[0190] FIG. 5 is a graph showing the transmission response of the lattice type filter configuration of FIG. 4;

[0191] FIG. 6 is a simplified circuit of a combined ladder and lattice type RF filter configuration;

[0192] FIG. 7 is a graph showing the transmission response of the filter configuration of FIG. 6;

[0193] FIG. 8 is a flowchart illustrating a method of fabricating the Composite FBAR structure of FIG. 1;

[0194] FIGS. 9 to 12 and 14 to 54 are schematic representations of the build up achieved by the steps of flowchart of FIGS. 8 and 9, and

[0195] FIG. 13 is a 180 XRD spectrum of single crystal Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST).

DESCRIPTION OF EMBODIMENTS

[0196] By way of example, a design for a Composite FBAR filter module with single crystal Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), AlN, Al.sub.xGa.sub.(1-x)N or, as suggested in this continuation, Sc.sub.xAl.sub.(x-1)N piezoelectric resonators is detailed hereunder with reference to FIG. 1, together with methods of manufacture with reference to FIG. 8.

[0197] With reference to FIG. 1 a Composite FBAR filter module 5 is schematically shown. The filter module 5 comprises a plurality of composite FBAR resonators coupled in half ladder or lattice arrangements or combination thereof. The composite FBAR resonators consist of piezoelectric films 18, 18 that may be Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), AlN, Al.sub.xGa.sub.(1-x)N or Sc.sub.xAl.sub.(x-1)N separated by a passivation material 54 such as SiO.sub.2, Si.sub.3N.sub.4, Ta.sub.2O.sub.5, polyimide or Benzocyclobutene (BCB) and sandwiched between electrodes 22, 60.

[0198] Sc.sub.xAl.sub.(x-1)N piezoelectric films 18, 18 are typically C-axis orientation and x is typically in the range 0.05x0.25 and preferably in the range 0.05x0.13. The films may have a root mean square (RMS) surface roughness of less than 1 nm and a rocking curve FWHM value of less than 500 arc sec.

[0199] In the method of construction described hereinbelow, it will be noted that both top and bottom electrodes 22, 60 are deposited onto the piezoelectric material 18 rather than by depositing a piezoelectric material on top of an electrode which is currently standard practice for FBAR filter construction. This enables a wider range of metals such as aluminum to be used as the bottom electrode; aluminum having increased conductivity and being less dense, enables decreasing the electrode weight and the subsequent mechanical damping it causes to the resonator. The upper electrode may be a composite electrode comprising a number of different metal layers including the silicon film 30. However, the electrode resonator material 18 is typically coupled to the silicon film 30 that is preferably single crystal silicon by other layers of upper electrode including a bonding layer (48, 50), adhesion layers 46, 46 and often by a relatively low DC resistance layer and a relatively high acoustic impedance layer.

[0200] Thus, in addition to the silicon membrane 30, the upper electrode typically includes titanium or chromium adhesion layers, a relatively low DC resistance layer of aluminum or gold, a relatively high acoustic impedance layer of tungsten or molybdenum, optionally followed by gold 50 or gold-indium 48 bonding layers. The silicon film 30 is typically a single crystal silicon and may have any of the following orientations: <100>, <111> and <110>. It typically has a thickness of 1 to 2 microns, but could be as little as 0.5 microns and as much as 10 microns thick. Although The single crystal silicon film 30 provides a mechanical support layer that has low acoustic losses and is itself attached by a layer of silicon oxide 34 using SOI technology to a cover 32 that is a thicker silicon wafer and is also known as a handle, providing a wafer on handle.

[0201] In some embodiments, the silicon membrane may be trimmed by reactive ion etch (RIE) to a pre-specified nominal thickness that in some embodiments, is no more than twice the thickness of the piezoelectric film, within a tolerance of 5 angstrom

[0202] Although the Silicon cover 32 is typically undoped and has a high resistivity that is typically over 5000 ohm cm, the silicon film 30 may be p or n doped to have a resistivity of as low as 0.005 ohm cm. Silicon doping technologies are well established and such doped membranes on handles are commercially available from Semiconductor Wafer Inc. (SWI) out of Taiwan, KST World out of Japan and OKMETIC out of Finland. In one embodiment, the membrane is n doped with arsenic.

[0203] Cavities 76 are provided within the silicon oxide layer 34 opposite the piezoelectric resonator films 18. The depth of the cavities is typically 3 to 10 microns. In one embodiment, the oxide layer bonding the membrane to the handle as supplied is 3 microns thick to tolerances of 5%, and thus the subsequent cavities are 3 microns deep. The bonding between the electrode 22 and the silicon film 30 may be achieved in a number of ways, such as by a gold-indium eutectic 48, a gold layer 50 or an AlN layer 52.

[0204] Preferably, however, the AlN layer 52 is not used as it can generate significant parasitic capacitance. Additionally, in some embodiments, both gold-indium and gold bonding layers may also be eliminated. This is achievable by using surface activated bonding (SAB). Essentially the two to be bonded surfaces are grown to a smooth sub nanometer roughness by crystal growth or smoothed and flattened to a sub nanometer surface roughness by CMP, and are then plasma activated and brought into contact under vacuum. This enables bonding without gold, gold-indium or AlN.

[0205] Usefully, therefore, the silicon film 30 and the electrode 22 may have mating surfaces that are both smooth to a root mean squared roughness (RMS) of less than 0.5 nm, facilitating high quality bonding. In this manner, silicon may be bonded to tungsten or molybdenum by surface activated bonding without gold being used at all. Aluminum may similarly be surface activated bonded to the piezoelectric single crystals using Surface Activated Bonding. This technology uses a plasma to activate both ultra smooth mating surfaces prior to bonding. The bonding is performed under vacuum and usually requires a sub 1 nm surface roughness that is achievable either by CMP or by single crystal growth or both. More details regarding are available at www.partow-tech.com and www.mhi-machinetool.comMitsubishi Heavy Industries Machine Tools from Japan.

[0206] The coated piezoelectric resonator array is attached to an interposer 85 by interconnects comprising solder 68 capped copper pillars 66, and is encapsulated in a polymer underfill/over-mold 72. A gasket 70 is provided around the filter, between the interposer 85 and the lower electrode 60 around the resonator array that defines the filter. The gasket 70 may consist of SU-8 attached to the lower electrode 60 and an epoxy dam 86 may be built up from the interposer 85. The gasket 70 and epoxy dam 86 work together to prevent the underfill/over-mold 72 that seals the unit from penetrating under the resonator array and define a cavity 92 between the lower electrode 60 and the interposer 85. Additional cavities 76 are provided over the piezoelectric films 18, 18 in the space between the silicon membrane 30 and cover 32, by selective removal of the silicon dioxide 34 by etching. A passivation material 54 separates the upper electrode 22, adhesion layers 20, 46, 46, bonding layers 48/50/52 and silicon membrane 30 into separate regions supporting pairs of parallel resonators and separating resonators that are connected in series.

[0207] An Under Bump Metallization (UBM) Layer 62 that comprises tungsten or tantalum or molybdenum (possibly with an adhesion layer of titanium), enables fabrication of the copper pillars 66 on the underside of the bottom electrode 60. Other remnants of the UBM 63 serve as stiffening raised frame around the perimeter of the lower electrode 60, which, being aluminum, has a very low weight. This raised frame structure is especially useful in Composite FBARs as it helps minimize lateral-wave spurious modes that otherwise lower the Q factor of the device, regardless of the mode number. With such a raised frame, only the main lateral mode is excited due to the new boundary conditions between the active and outside region of the resonator membrane 18 that are created by the raised frame 63. Additionally, with reference to FIGS. 2 to 7, it will be noted that filters comprise shunt resonators and series resonators. The extra weight of the UBM 63 layer on the electrode creates a mechanical damping effect that can assist in lowering the shunt resonator frequency response vs. the series resonator frequency response and thus improve the overall performance of the filter.

[0208] The Commercial FBAR filter market is dominated by Broadcom which uses Aluminum Nitride (AlN) as the piezoelectric thin-film material that best balances performance and manufacturability.

[0209] Specific embodiments of the technology disclosed herein below use Sc.sub.xAl.sub.(1-x)N which is expected to have fairly high Q and better K.sup.2.sub.eff values.

[0210] Because the fabrication method allows single crystal piezoelectric films to be fabricated, improved factors of merit (FOM) are expected when compared to the polycrystalline non-epitaxially grown films currently in use.

[0211] With reference to FIG. 2, a simplified circuit of a half ladder type filter configuration created by BAW resonators in series with shunt BAW resonators is shown. In a filter, resonators are combined in a ladder, wherein each rung or stage comprises two resonators: one in series and the other connected in shunt. With reference to FIG. 3, adding rungs to the ladder, improves the rejection of undesired frequencies, creating a signal with less out-of-band rejection (a steeper skirt) but this is at the expense of insertion loss and greater power consumption. With reference to FIG. 4, another resonator configuration may be a lattice, which, as shown in FIG. 5 has poorer cutoff but better out-of-band attenuation.

[0212] With reference to FIG. 6, the ladder and lattice type circuits may be combined to provide the transmission response shown in FIG. 7. The possible arrangements of resonators to create filters is beyond the scope of this application, but methods for fabricating resonators that are coupled in series and parallel are discussed hereunder with reference to FIGS. 42 and 43 and this enables arranging the resonators in the various ladder, lattice and combination arrangements.

[0213] Referring back to FIG. 1, in preferred embodiments, the resonator film 18 is a single crystal piezoelectric of BST, Al.sub.xGa.sub.(1-x)N, AlN or Sc.sub.xAl.sub.(1-x)N.

[0214] Like Al.sub.xGa.sub.(1-x)N or AlN, C axis Sc.sub.xAl.sub.(1-x)N has an HCP type Wurtzite crystal structures (C plane orientation). A strong C axis texture is the most important prerequisite for Sc.sub.xAl.sub.(1-x)N FBAR filters because the acoustic mode of the FBAR needs to be longitudinally activated and the piezoelectric axis of Sc.sub.xAl.sub.(1-x)N is along c-axis. The addition of scandium to AlN makes it easier to match lattice spacing of the film with that of the substrate.

[0215] Since there are no grain boundaries in a single crystal, the attenuation of the acoustic signal is minimal. This also minimizes the lost energy that is otherwise transferred into heat and which has to be dissipated.

[0216] Single crystal and strongly textured C axis Al.sub.xGa.sub.(1-x)N, AlN and Sc.sub.xAl.sub.(1-x)N films have smoother surfaces than randomly oriented films. This results in reduced scattering loss and higher Q-factors. Furthermore, rough surfaces, especially at high frequencies, are a major cause of the loss of the metal electrodes interfaces because of a skin effect. The smooth electrodepiezoelectric interfaces obtainable in highly textured and single crystal films with both upper and lower electrodes deposited thereupon are thus extremely advantageous.

[0217] Composite FBAR structures consist of a thin piezoelectric film 18 sandwiched between top and bottom electrodes 22, 60. In the past, the electrode 22 was first deposited and then the piezoelectric layer 18 was fabricated thereupon. This required the electrode 22 to be made from a heavy metal such as platinum, molybdenum, tungsten or gold, which allow the high deposition temperatures required for subsequent piezoelectric film deposition thereupon. However, most of these metals have poor DC resistance, potentially deteriorating the Q factor of the resonator. In preferred embodiments described herein the electrodes 22, 60 are deposited onto the piezoelectric film 18 using physical vapor techniques. This enables lightweight metals such as aluminum to be used, either on its own or in conjunction with other metal layers to form composite electrodes. Aluminum has a high conductivity and so a thinner electrode is possible. Aluminum is much less dense than refractory metals and so the weight of the electrodes and their damping effect is less. The quality and coupling of the resonators and filters thus formed are vastly superior to those of the prior art.

[0218] Aluminum is expected to readily adhere to C axis Al.sub.xGa.sub.(1-x)N, AlN and Sc.sub.xAl.sub.(1-x)N due to the Al ions of the piezoelectric film If, however, electrode adhesion proves difficult, an adhesion layer which adheres to both the single crystal and to the electrode may be used. For example, titanium may be appropriate. Such adhesion layers typically have thickness of tens of nanometers.

[0219] Alternatively, surface activated bonding as available from Partow Tech or Mitsubishi may be used. The metal, nitride, and silicon surfaces are first flattened and smoothed to high tolerances and then plasma activated and directly bonded under vacuum.

[0220] The mechanism used in ferroelectric Composite FBAR transducers is electrostriction which is the electric field induced piezoelectric effect. The top and bottom electrodes 22, 60 are used to apply direct current (DC) and radio frequency (RF) signals. The preferred Composite FBAR structure described herein consists of a thin film single crystal <111> Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST) or C-axis Al.sub.xGa.sub.(1-x)N, AlN or Sc.sub.xAl.sub.(1-x)N film 18 sandwiched between top and bottom aluminum electrodes 22, 60. The C axis Sc.sub.xAl.sub.(1-x)N film 18 converts mechanical to electrical energy and vice versa.

[0221] To provide stiffening without substantial weight, a low acoustic-loss single crystal silicon membrane layer 30 with possible orientation of <111>, <100> or <110> may be coupled to the piezoelectric films 18. The silicon layer 30 may have a thickness in the range of 0.5 m to 10 m, with the lowest possible thickness being preferable for best performance high frequency resonators. It should be noted that in Composite FBARs there are odd and even resonance modes, where each mode exhibits peak Q and K.sup.2.sub.eff (coupling) as a function of the crystalline <111> Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST) or c-axis Sc.sub.xAl.sub.(1-x)N, AlN and Al.sub.xGa.sub.(1-x)N to silicon membrane thickness ratio. The peak K.sup.2.sub.eff values decrease with mode number because the fraction of acoustic displacement across the crystalline <111> Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST) or c-axis Sc.sub.xAl.sub.(1-x)N, AlN and Al.sub.xGa.sub.(1-x)N is reduced. However, the peak Q factor values increase with mode number, since the fraction of acoustic displacement across the low loss silicon layer increases. Hence, careful selection of the resonance mode is required for optimal FOM and low thickness silicon membranes with low thickness crystalline <111> Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST) or c-axis Sc.sub.xAl.sub.(1-x)N, AlN and Al.sub.xGa.sub.(1-x)N films are desired for higher frequencies filters. In should also be noted that higher harmonic modes naturally render a higher frequency for a given film thickness and this may alleviate the requirement for trimming. Consequently, operating an FBAR at its second or higher harmonic mode frequency can extend the FBAR operation frequency range, as long as its figure of merit (FOM) remains high. Cavities 76, 92 are provided above and below the piezoelectric 18 on silicon 30 combination. The structure is encapsulated with a polymer 72 and mounted on an interposer 85 and coupled thereto with copper pillars 66 that are typically about 40-50 nm wide and about 40 nm high and joined to upper contact pads 82 of the interposer 85 with solder 68. A polymer gasket 70 which may be fabricated from SU-8 to have a high form factor and/or a dam 86 (typically epoxy) may be provided around the perimeter of the filter structure to keep the polymer over-mold/under-fill (MUF) 72 from entering the lower cavity 92. The interposer 85 may be constructed using well established fabrication technologies.

[0222] The Composite FBAR shown in FIG. 1 has such a piezoelectric 18 on silicon membrane 30 Composite FBAR structure, preferably wherein the piezoelectric film 18 is a the crystalline <111> Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST) or c-axis Sc.sub.xAl.sub.(1-x)N, AlN and Al.sub.xGa.sub.(1-x)N and the electrodes 22, 60 are fabricated from lightweight aluminum.

[0223] Although RF resonators are primarily used as filters, they find other uses, including as sensors, for example. There is also interest in tunable resonators that can operate at different frequencies.

[0224] FIG. 8 shows the steps of the main process flow for fabricating an Composite FBAR filter, and schematic illustrations of the build-up are shown in FIGS. 9-12, 14-53.

[0225] With reference to FIGS. 8 and 9, the method consists of first obtaining and providing a removable wafer carrier with a release layerstep (a), a schematic, not to scale representation of this is shown in FIG. 9 which represents a c-axis <0001> 1 Sapphire wafer 10 with an un-doped Gallium Nitride (U-GaN) release layer C-axis <0001> 1 12 thereon. Such sapphire wafers 10 with U-GaN 12 deposited thereon are commercially available with diameters of 2, 4 and 6 in thicknesses of from 430 m to 1200 m, and have a polished surface with an RMS smoothness of less than 1 nm. The U-GaN layer 12 typically has a thickness of 4 m and a polished surface having an RMS of less than 1 nm ready for epitaxial growth thereon. These coated substrates were developed for the Light Emitting Diode (LED) industry and are commercially available from various Chinese manufacturers including San'an Optoelectronics Co., Ltd. (San'an) and Suzhou Nanowin Science and Technology Co., Ltd (NANOWIN).

[0226] Alternatively, an AlN single crystal wafer cleaved from a large single crystal such as a single crystal grown by the Czochralski method, and having an appropriate laser absorbing release film thereupon could be used.

[0227] A piezoelectric film comprising <111>Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), or c axis Sc.sub.xAl.sub.(1-x)N or Al.sub.xGa.sub.(1-x)N or AlN is now deposited onto the removable carrier 10step (b). With reference to FIG. 10, to aid heat dissipation and thus thickness distribution during subsequent deposition of a <111>Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), or c axis Sc.sub.xAl.sub.(1-x)N or Al.sub.xGa.sub.(1-x)N or AlN piezoelectric film, a metal layer 14 may deposited on the back of the sapphire wafer 10step (bi), i.e. the side opposite to the side coated with GaN 12. The thickness of the metal layer 14 depends on the metal used. In this instance, <111>Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), or c axis Sc.sub.xAl.sub.(1-x)N or Al.sub.xGa.sub.(1-x)N or AlN piezoelectric material 18 subsequently deposited (see below) titanium is a good candidate for the heat dissipating metal layer 14, and an appropriate thickness for the heat dissipating layer 14 is about 150 nm. The heat dissipating metal layer 14 may be deposited by sputtering, for example.

[0228] The Gallium Nitride release layer 12 is typically about 4 microns thick with an RMS roughness of less than 1 nm. Because of the lattice matching between the <0001> plane of the GaN 12 and Sapphire 10, Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), Sc.sub.xAl.sub.(1-x)N, Al.sub.xGa.sub.(1-x)N or AlN may be laid down as a single crystal film. Adjusting the percentage of gallium helps ensure lattice matching and thin films having a thickness of typically 200-400 nm in the case of BaxSr.sub.(1-x)TiO.sub.3 and 200 nm to 2000 nm in the case of Sc.sub.xAl.sub.(1-x)N, AlN or AlxGa(1x)N are then deposited in this manner using oxide molecular beam epitaxy (MBE).

[0229] In the case of Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), oxide MBE system might be used. In case of AlN or Sc.sub.xAl.sub.(1-x)N or AlxGa(1x)N, Plasma Assisted MBE (PA-MBE) or ammonia-based MBE system can be used with effusion cells selected from the group of Al, Sc and Gastep (bii).

[0230] When undoped GaN is deposited over Sapphire, the initially deposited film is more N-rich and more easily removed by plasma or chemical etch. Close to the end of deposition the GaN more Ga-rich and much harder to remove. This phenomenon may result with Ga residue remaining after Laser Lift Off (LLO) and GaN etch. Furthermore, extra and non-uniform etching of Ga residue may cause non-uniform etching of the single crystal Sc.sub.xAl.sub.(1-x)N, Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), Al.sub.xGa.sub.(1-x)N or AlN piezo electric layer that can significantly impact the performance of the resonator at the designated frequency.

[0231] For this reason, it is preferred to have an etch stop layer (dry and wet) to protect the Sc.sub.xAl.sub.(1-x)N, Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), Al.sub.xGa.sub.(1-x)N or AlN piezoelectric layer whilst residual GaN residue is removed after LLO.

[0232] The etch stop layer is required to be a non interfering match layer so not to create a lattice mismatch between the GaN sacrificial layer and Sc.sub.xAl.sub.(1-x)N, Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), Al.sub.xGa.sub.(1-x)N or AlN piezo layer that must follow the GaN to become single crystal for best-in-class resonator performance.

[0233] Additionally, the etch stop layer must also be easily removed using the preferred dry etch whilst the Sc.sub.xAl.sub.(1-x)N, Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), Al.sub.xGa.sub.(1-x)N or AlN is not attacked by the dry etchant. The etch stop layer is also required to demonstrate high melting point, well above the MBE deposition temperatures of 350 C. to 800 C. used to deposit the piezo films.

[0234] One potential etch stop layer for C-axis Nitride based piezo films such as AlN, Sc.sub.xAl.sub.(1-x)N and Al.sub.xGa.sub.(1-x)N is Ta.sub.2N which has a melting point above 2000 C. Ta.sub.2N can be selectively etched using plasma made from XeF.sub.2 with a mixture of inert gas such as N.sub.2 or Ar at various mixtures and plasma power levels.

[0235] XeF.sub.2 does not attack AlN or the Sc.sub.xAl.sub.(1-x)N. However, because it attacks Silicon, the SOI bonded wafer must be protected during Ta.sub.2N removal. Typical thickness of Ta.sub.2N are at the range of 500 A to 1500 A.

[0236] Other etch stop layers candidates for C-axis Nitride based piezo films are all from the transition metal nitride and include TaN.sub.x, NbN.sub.x, WN.sub.x and MoN.sub.x where X>1.

[0237] Molecular beam epitaxy (MBE) is a high purity low energy deposition technique that allows for low point defect manufacturing. It is possible to control the aluminum to scandium ratio with high accuracy of 1% and this affects the Q factor and coupling of the film.

[0238] It will be noted that in the case of deposition of BST effusion cells with BaTiO.sub.3 and SrTiO.sub.3 are typically used, depositing the oxides, while for AlN, AlGaN and ScAlN free standing elements of Al and Ga or Sc are used together with a plasma to break the N.sub.2 into N for reaction which is not required with an MBE oxide machine. Alternatively, there are technologies that may be used to extract N2 from Ammonia in what is known as a hybrid machine between MOCVD and MBE.

[0239] The epitaxially grown C axis Sc.sub.xAl.sub.(1-x)N films may have a RMS (root mean square) surface roughness of less than 1 nm and rocking curve FWHM value lower than 500 arcsec. This helps to maximize the K.sup.2.sub.eff values of the resonator and minimizes the so called electrode skin effect at high frequencies.

[0240] As shown in FIG. 12, to facilitate deposition of a single crystal piezoelectric layer 18 of Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST, a buffer layer 16 of rutile TiO.sub.2 and/or SrTiO.sub.3 may first be deposited step b(ii).

[0241] To the best of our knowledge, Applicant is the first person to create a single crystal layer of Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST) resonator and FIG. 13 is a 180 XRD spectrum of the structure of FIG. 12 showing that a single crystal membrane of BST was obtained.

[0242] In prior art resonators, the lower electrode is first deposited and then the piezoelectric film is deposited thereon. Consequently, due to the high temperature fabrication of the piezoelectric film, refractory metals such as molybdenum, tungsten, platinum or gold are traditionally used for the lower electrode

[0243] Since in the present technology, the first electrode 22 is deposited onto the piezoelectric film, a wide range of metals may be used such as aluminum. It will be appreciated that aluminum has a relatively low DC resistance and mass when compared to these refractory metals, and thus using aluminum electrodes or combinations of aluminum and molybdenum or aluminum and tungsten is expected to increase the Q factor of the filter, especially at high frequencies.

[0244] FIG. 14 shows the equivalent structure with a piezoelectric film 18 of Sc.sub.xAl.sub.(1-x)N without a buffer layer 16. For simplicity, the remaining structures shown in FIGS. 15 to 53 do not show the buffer layer 18.

[0245] A first electrode layer 22 is now deposited over the piezoelectric membrane 10step (c). With reference to FIG. 16, to aid adhesion, an adhesion layer 20 such as a titanium or chromium layer that may be as little as 5 nm thick, but could be as much as 50 nm is first deposited onto the piezoelectric membrane 18step (ci). Then an aluminum electrode layer 22 having a thickness of, say, 50 nm to 150 nm is deposited thereoverstep (cii). Both the adhesion layer 20 and the electrode layer 22 may be deposited by sputtering, for example. Tolerances of 2% are achievable.

[0246] At a first approximation, the resonant frequency fR of a piezoelectric resonator is given by the following equation: fR=/L/2t where L is the longitudinal acoustic velocity in the normal direction of the piezoelectric layer, t is the thickness of the piezoelectric film and is the acoustic wavelength of the longitudinal wave.

[0247] However, in practice, the acoustic properties of the other layers of the resonator affect the resonator performance. In particular, the mass loading effect of the electrodes which tend to be made of heavy metals such as molybdenum and platinum, due to the need to withstand the fabrication temperature of the piezoelectric material.

[0248] Although described for depositing aluminum onto Sc.sub.xAl.sub.(1-x)N or onto Ba.sub.xSr.sub.(1-x)TiO.sub.3 (BST), Al.sub.xGa.sub.(1-x)N or AlN, it will be appreciated that PVD or CVD with otherwise, low density, high conductivity electrode materials 22 over different piezo layers may be used with the same method. For example, carbon nano-tubes (CNT) over single crystal Sc.sub.xAl.sub.(1-x)N AlN or Al.sub.xGa.sub.(1-x)N may be considered. Aluminum is particularly attractive for resonator electrodes since it has high electrical and thermal conductivity and a low density, so hardly lowers the overall Q factor of the resonator. However, previous manufacturing routes wherein the electrode was deposited prior to deposition of the piezoelectric, ruled out aluminum. In this regard it will be noted that adding an aluminum bottom electrode after etching away a Si carrier wafer and exposing the back side of the piezoelectric layer, has significant yield challenges and complicates the packaging process of the filter and thus lowers the final yield.

[0249] The piezoelectric film 18, adhesion layer 20 and aluminum electrode 22 are deposited over the entire sapphire wafer 10 as a continuous layer. (Instead of aluminum, electrode 22 may be another material, such as gold, for example).

[0250] A backing film on handle 28 is obtainedStep (d). This may be a commercially available silicon on insulator (SOI) product. The backing film on h handle 28 is typically a silicon wafer film 30 sandwiched to a silicon carrier 32 by a silicon oxide layer 34. The silicon wafer film may be doped to have a low resistivity.

[0251] A commercially available backing film on handle 28 obtainable from Semiconductor Wafer Inc. (www.semiwafer.com), KST World Corp (www.kstworld.co.jp) or OKMETIC (www.okmetic.com) that is suitable is shown schematically in FIG. 17 and consists of a silicon film 30 that comes in thicknesses in the typical range 1.5 to 10 m that is coupled by a SiO.sub.2 box 34 that is typically 3-10 m thick to a Silicon handle 32 that is typically at least 400 m thick. The silicon membrane may be trimmed to desired thicknesses and to tolerances of 4 angstrom tolerances using RIE, for example.

[0252] An alternative SOI product 36 shown in FIG. 18 is a silicon wafer 38 attached to a silicon carrier 42 by a silicon oxide layer 40, but with a preformed air cavity 44. Such a structure is commercially available from Icemos (www.icemostech.com).

[0253] Both SOI products 28, 36 may be obtained pre-coated with metal coatings on the silicon film 30, 38 aiding their attachment to the piezoelectric film-electrode sandwich.

[0254] In some embodiments, the silicon film is doped, typically n doped with arsenic to increase its conductivity. The silicon carrier is, however let undoped. In some embodiments, the silicon oxide layer may be 3 microns thick to tolerances of 5%.

[0255] With reference to FIG. 19, the commercially available film 30 (38) on handle 32 (42) product 28 (36) is attached to the electrode 22 of the stackstep (e).

[0256] There are a number of ways that the silicon film 30 (38) may be attached to the electrode 22. For example, with reference to FIG. 20 an adhesion layer such as titanium or chromium 46 may be deposited onto the electrode layer 22 and this can be coated with an adhesive layer consisting of a gold-indium eutectic alloy 48 comprising 0.6% gold and 99.4% indium. The AuIn eutectic melts at 156 C. and by hot pressing at about 200 C., the adhesion layer may be attached to the silicon membrane 30 of the SOI wafer 28. Optionally, a titanium bonding layer 46 is attached to the silicon membrane 30 and an adhesive layer of gold-indium eutectic alloy 48 is attached to this. The two adhesion layers are fused together by the hot processing. The bonding layers created by this technique are rather thick, and the process is capable of some variation. With reference to FIG. 21, an alternative process relies on the fact that both the exposed surface of the silicon wafer film 30 (38) and the surface of the electrode layer 22 are very smooth. By coating both surfaces with adhesion layers of titanium 46, 46 that are typically 2-4 nm thick and may be deposited by sputtering, and then depositing pure gold 50 (50) coatings of thicknesses of 10-100 nm (currently 75 nm) onto the adhesion layers 46 (46) the two gold coatings 50, 50 may be brought together at room temperature and the coatings fused together (see for example Shimatsu, T. & Uomoto, M. (2010). Atomic diffusion bonding of wafers with thin nanocrystalline metal films. Journal of Vacuum Science Technology B: Microelectronics and Nanometer Structures. 28 (4). pp. 706-714.). This technique requires a lower temperature and a thinner gold layer 50 than the AuIn layer shown in FIG. 20.

[0257] Lower temperature bonding, such as bonding at room temperature using surface activated bonding is desirable to maximize yield as the different coefficients of thermal expansion of the sapphire substrate and the silicon membranes could cause cracking at higher temperatures.

[0258] With reference to FIG. 22, a further alternative process is to again coat both surfaces with adhesion layers of titanium 46, 46 that are typically 2-4 nm thick, and then deposit aluminum nitride 52 (52) coatings having thicknesses of 10-40 nm onto the adhesion layers 46 (46). The two aluminum nitride 52 (52) coatings may be activated with Ar plasma and when brought into contact at room temperature and pressure, fuse together. The bond can be strengthened by annealing at 300 C. in a N.sub.2 atmosphere, typically for a period of 3 hr. However, if a low resistivity doped silicon membrane is used, the AlN dielectric bonding layer is inappropriate because of parasitic capacitances that lower the FBAR response and performance.

[0259] It will be appreciated that the stack of titanium adhesion layers 20, 46, 46 and the gold-indium or gold bonding layers 48, 50 serve with the aluminum electrode 22 layer as the upper electrode. This composite electrode can take advantage of the inherent characteristics such as DC resistance, acoustic impedance and weight (density) of the different materials, to provide different properties to the composite electrode.

[0260] In some embodiments, the upper electrodes comprise a layer with a relatively low DC resistance such as aluminum or gold, and a second layer with a relatively high acoustic impedance such as tungsten or molybdenum. It has been found possible to ensure that the upper surface of the second layer is very smooth, having a RMS roughness of equal to or less than 0.5 nm. This is achievable by CMP, for example. Similarly, the silicon membrane can have a similar ultra smooth surface, also achievable by CMP, for example. When these ultra smooth flat surfaces are activated by plasma and brought together into contact under vacuum, these smooth surfaces may bond together, enabling gold free bonding. This surface activated bonding technique is available from Partow-tech and from Mitsubishi Heavy Industries Machine Tools, Japan.

[0261] An alternative composite electrode may include an aluminum lower layer and gold-indium/gold/AlN bonding layers with an intermediate double layer of titanium or chromium, and tungsten or molybdenum between the aluminum and the bonding layer. This type of structure is only appropriate with non-doped silicon membranes having high resistivity.

[0262] Titanium, tungsten and molybdenum may all be deposited by sputtering, and the titanium or chromium layer may serve as an adhesion layer. The addition of a titanium, tungsten or molybdenum layer not only increases the acoustic impedance but additionally serves as a barrier layer between the gold of the bonding layer and the aluminum layer. In such a structure, the thickness of the aluminum layer may be as little as 50 nm. The titanium-tungsten or titanium-molybdenum is typically also 50 nm or slightly thicker. In such structures the gold bonding layer may be reduced to the minimum thickness that allows bonding while the aluminum, titanium-tantalum, titanium-tungsten or titanium-molybdenum serve as the main metals of the composite electrode, since they provide a desirable balance of low DC resistivity with high acoustic impedance.

[0263] In general, it is advisable to process at as low a temperature as possible to minimize the likelihood of damage to the piezoelectric film and its electrodes and to further minimize warpage of the stack due to differences in the coefficient of thermal expansion of silicon and sapphire. It is further advised that the bonding layer thickness should be as thin as possible in order to enhance the Q factor value but that higher bonding layer thicknesses are also possible thorough careful balancing of the DC resistance, weight and acoustic impedances of the composite electrode.

[0264] Once the silicon film and handle 28 is attached, the sapphire substrate 10 may be removedstep (f). If a thermal layer such as titanium 14 is deposited on the back of the substrate, this may be removed by chemical mechanical polishing, for example, giving the structure shown schematically in FIG. 23.

[0265] Then, the GaN 12 may be irradiated through the sapphire substrate 10 using a 248 nm excimer laser to disassociate the GaN 12 enabling lift off of the sapphire substrate 10. Such a pulsed laser, with a square waveform is available from IPG Photonics. This process is known as laser lift off and results in the structure shown schematically in FIG. 24.

[0266] Residual GaN 12 may be removed using Inductively Coupled Plasma (ICP) with Cl.sub.2, BCl.sub.3 and Ar for exampleFIG. 25. This can be achieved at temperatures of below 150 C., avoiding heat treatment of the piezoelectric thin film 18 and of the aluminum 22 and other layers. The Inductively Coupled Plasma (ICP) is a commercially available process, used by NMC (North Microelectrics) China Tool and by SAMCO INC, for example.

[0267] The piezo etch stop layer may be removed by induction coupled plasma using a mixture of XeF.sub.2 and Ar for example.

[0268] After removing the GaN 12 a thickness measurement and trimming process of the piezoelectric film 18 may be required to obtain perfect frequency response which is related to the film thicknessstep (g). The trimming process uses Ar+ Ion beam milling and this process may be used to tailor any metal adhesion, barrier or oxide layers such as SiO.sub.2 Al.sub.2O.sub.3, AlN, W, Mo, Ta, Al, Cu, Ru, Ni or Fe where the wafers is held in a 4 axis chuck and rotated accordingly. A commercially available system known as InoScan is available from Meyer Burger, Germany. A trimmed piezoelectric layer 18 is shown in FIG. 26 which is flipped over. It should be noted that in order to obtain high performance RF filters with a high yield, the thickness of the piezoelectric layer may need to be trimmed to tolerances of tenths of a nanometer, typically 4 angstroms.

[0269] The same ICP process that is used to clean the back side of the piezoelectric 18 may then be used to pattern the piezoelectric layer 18 into arrays of piezoelectric islands for fabricating filters and the likestep (h). By way of example only, a schematic top view is shown in FIG. 27 and a side view in FIG. 28. Although rectangular islands of piezoelectric are shown, the islands may, of course, have any shape as dictated by the shape of the lithography mask tool. It will be noted that patterning the piezoelectric layer 18 into separate membranes just after the laser lift off processing reduces the risk of the piezoelectric layer cracking due to stress release across the wafer.

[0270] An induction coupled plasma (ICP) using Cl.sub.2+BCl.sub.3+Ar, CF.sub.4+O.sub.2 or Cl.sub.2+O.sub.2+Ar and SF.sub.6+O.sub.2 is then applied to respectively remove the aluminum, adhesion layers, the high acoustic impedance layer, bonding layer and silicon membrane 30 down to expose the top surface of the silicon oxide 34 creating trenches 21step (i). A top view of the structure is shown in FIG. 29 and a side view in FIG. 30. With reference to FIG. 54, usefully, the high acoustic impedance layer 22, bonding layer 48/50/52, adhesion layers 46 are traversed by the trench 21 created by the ICP which penetrates into the silicon membrane 30. Then the trench 21 is re-patterned with photoresist and a narrower trench 27 is etched through the rest of the silicon layer 30 into the silicon dioxide 34. This creates a stepped interface between the silicon membrane 30 and the subsequently deposited passivation layer 54 (see below) and enables secure anchoring of the passivation layer 54 to the silicon membrane 30 in step (j) since the surface of the interface can still be several microns, even if the silicon membrane 30 itself is only a micron or so thick. The silicon membrane 30 has to be fully traversed since silicon is a conductor, albeit not a particularly good one. The narrower trench 27 that separates the individual silicon membranes is typically 3 to 10 micron wide so that the individual silicon membranes are insulated from each other by a barrier of the passivation material 54 that may be 3 to 10 microns wide. The depth of the cavities is also typically 3-10 microns.

[0271] The induction coupled plasma (ICP) process operates at a temperature of less than 150 C. and does not adversely affect the piezoelectric membranes 18, 18 which are protected by the photo-resist mask. Inductively Coupled Plasma (ICP) is a commercially available process, used by NMC (Beijing North Microelectronics) China Tool and by SAMCO INC, for example.

[0272] A schematic top view of the resulting structure is shown in FIG. 29 and a schematic side view is shown in FIG. 30.

[0273] A passivation layer 54 such as SiO.sub.2, Si.sub.3N.sub.4, Ta.sub.2O.sub.5, a photo-sensitive Polyimide or BCB (Benzocyclobutene) is applied into the trenches 21 thus producedstep (j). The same passivation material 54 may be used to cover the piezoelectric islands 18, 18 with windows then being opened down through the passivation layer to the piezoelectric islands. Where a photosensitive polyimide or BCB is used, this is achieved by selective exposure, which is a precision process that includes the known series of sub-processes such as spin-coat, exposure, development and cure of photo-sensitive polymer passivation layers. Photo-sensitive polyimide passivation materials are available from HD Microsystems and are a standard industry solution for Flip Chip and Wafer Level Chip Scale Packages (WL-CSP) devices such as that described in this specification. Photo-sensitive BCB is commercially available as Cyclotene from Dow Chemicals.

[0274] Ta.sub.2O.sub.5, SiO.sub.2 and Si.sub.3N.sub.4 may be deposited using PE-CVD processes as known.

[0275] A schematic top view of the resulting structure is shown in FIG. 31 and a schematic side view is shown in FIG. 32.

[0276] The upper electrodes are now appliedstep (k). An adhesion layer 58 such as titanium is first depositedstep 3(ki)FIG. 33, and then the top electrode 60 is then depositedstep (kii)FIG. 34. Both the adhesion layer 58 and the electrode 60 may be deposited by sputtering, for example. Tolerances of 5% are acceptable and easily obtainable.

[0277] Couplings are now applied to connect the structure to an interposer, described below. Firstly, an Under Bump Metallization (UBM) layer 62 may now be appliedstep (l) by depositing a layer of metal that may be Ti/W, Ti/Ta or Ti/Mo (typically about 25 nm titanium, followed by about 50 nm of tungsten, tantalum or molybdenumstep (li), FIG. 35. Sputtering may be used.

[0278] The structure may then be covered with a layer of copper 64 that is typically about 1 m thick, by sputtering, for examplestep (lii)see FIG. 36; the Under Bump Metallization layer 62 keeps the copper 64 and aluminum 60 separate.

[0279] Next, copper pillars 66 may be fabricatedstep (liii), FIG. 37. These are typically about 40-50 m in diameter and about 40 m high. They may be fabricated by depositing a layer of photoresist 65, patterning and then electroplating copper 66 into the pattern.

[0280] With reference to FIG. 38, solder 68 may then be deposited into the pattern to cap the copper pillars 66step (liv). This could be achieved by electroplating or electro-less plating a suitable material into the photoresist pattern used for fabricating the copper pillars 66. Then the photoresist is stripped awaystep (lv), FIG. 39.

[0281] The copper layer 64 around the copper pillars 66 is now etched awaystep (lvi), FIG. 40. This may be accomplished by exposing to a solution of ammonium hydroxide at an elevated temperature. Alternatively, copper chloride or other commercially available Cu micro-etch solution may be used as the etchant. The UBM 62 is now selectively removedstep (vii), FIG. 41, leaving perimeter sections 63 over what will become the edges of the upper electrode to add weight to the edges of the effective resonators. Such raised frame structure is especially effective in Composite FBARs to help minimize lateral-wave spurious modes that otherwise lower the Q factor of the device, regardless of the mode number. With such structures, only the main lateral mode is excited due to the new boundary conditions created by the raised frame between the active and outside region of the resonator membrane 18. Additionally, the extra load of the UBM 63 layer over the resonators provides a damping effect that can assist in lowering the shunt resonator frequency response vs. the series resonator frequency response and thus improve the overall performance of the filter.

[0282] With reference to FIG. 42, by way of schematic illustration only, top and side views of a pair of piezoelectric capacitors coupled in parallel is shown, and with reference to FIG. 43, by way of schematic illustration only, top and side views of a pair of piezoelectric capacitors coupled in series is shown. The superfluous aluminum 60 beyond that required for the electrode may be selectively removed by applying an inductively coupled plasma comprising Cl.sub.2+BCl.sub.3+Ar and the excess parts of the titanium adhesion layer 58 thereby exposed may be selectively removed by reactive induction etching away with CF.sub.4 and O.sub.2.

[0283] It will be noted that the extra weight of the UBM 63 layer provides mechanical damping that can lower the shunt resonator frequency response vs. the series resonator frequency response, and thus improve the overall performance of the filter.

[0284] Alternatively, gold pillars may be created instead of copper pillars and attached to their related gold deposited pads on the interposer by a gold to gold bonding process. In one embodiment, such gold pillars maybe deposited by applying firstly a gold seed layer, preferably having a thickness of several hundredths nanometer over the UBM 63 layer followed by pattern electroplated of the gold pillars using photo-resist cavities. In another embodiment, such gold pillars maybe created using a paste consisting of sub micron gold particles in an organic binder. A screen printing method may used to apply the gold paste into the photo-resist trenches followed by low temperature sintering at a temperature in the range of 70 C. to 100 C. in air to create the gold bumps. Following the sintering process, the photo-resist is stripped away and the gold seed layer and UBM layer are etched using HF. In a third embodiment, the gold pillars may be created by using a wire bonding machine to create ball bond bumps, eliminating the need for a gold seed layer.

[0285] With reference to FIG. 44, a polymer gasket 70 may now be fabricated around an array or resonators defining a filterStep (n). This may be achieved using SU-8 technology. SU-8 is a commonly used epoxy-based negative photoresist whereby the parts exposed to UV become cross-linked, while the remainder of the film remains soluble and can be washed away during development. SU8 can be deposited as a viscous polymer that can be spun or spread over a thickness ranging from below 1 m to beyond 300 m. It is an attractive material since it can be deposited as a tall thin wall that can be about 55 m high and thus compatible with the solder capped copper pillars, whilst having a width of from 10 to 30 m.

[0286] At this stage, as shown in FIG. 45, the array of filters may be attached to a tape 72 with the copper pillars 66 and SU8 gasket 70 side facing downwards, and the silicon handle 32 may be thinned down to about 90 micronsstep (o), using chemical mechanical polishing (CMP), to produce the structure shown in FIG. 46. Other possible thinning techniques include mechanical grinding, chemical polishing, wet etching together with atmospheric downstream plasma (ADP) and dry chemical etching (DCE), for example,

[0287] Unless a SOI substrate 36 having prefabricated cavities 44FIG. 18was used, cavities 76 are now formed in the SiO.sub.2 34 layerstep (p). Through silicon via etching (TSV) is used to drill holes 74 through the thinned down silicon handle 32 to the SiO.sub.2 box 34step p(i), FIG. 47 opposite each of the piezoelectric films 18, 18.

[0288] The Silicon Oxide 34 may then be selectively etched away with HF vapor in accordance with the formula SiO.sub.2+4HF(g).fwdarw.SiF.sub.4(g)+H.sub.2O through the silicon via holes 74 to form cavities 76,step p(ii), FIG. 48. Dry vapor etching is preferable to a wet etch since this enables penetration of small features and prevents the membrane and cover from sticking together.

[0289] Up until this stage, the filters are fabricated in arrays using on wafer fabrication techniques. The array is now diced into separate filter unitsstep (q).

[0290] Dicing may take place by mechanical blades, plasma or laser. Plasma or laser may be preferred with some designs in order to avoid membrane damages. Such dicing tools are available by Disco Japan.

[0291] An interposer 85 is now procured step (r). By way of enablement only, a two layer interposer 80 may be fabricated by copper electroplating of pads 80 and vias 82 into photoresist on a sacrificial copper substrate, followed by laminating with a dielectric material 84 having a polymer matrix such as polyimide, epoxy or BT (Bismaleimide/Triazine), Polyphenylene Ether (PPE), Polyphenylene Oxide (PPO) or their blends, either provided as a film, or as a pre-preg reinforced with glass fibers for additional stiffness. More details may be found in U.S. Pat. No. 7,682,972 to Hurwitz et al. titled Advanced multilayer coreless structures and method for their fabrication incorporated herein by reference. There are, however, alternative established manufacturing routes for fabricating appropriate interposers. An appropriate interposer 85 with copper pads 80 and vias 82 in a dielectric with polymer matrix 84 is shown in FIG. 49.

[0292] Alternatively, an interposer with a low temperature cofired ceramic LTCC matrix may be used.

[0293] Alternatively again, an interposer substrate of glass with through glass vias may be used.

[0294] In general, the interposer 85 should be thin so that the overall package remains thin. However, it will be appreciated that different resonators 18, 18 may be interconnected via routing layers within the interposer 85, and additional layers may be built up if required.

[0295] With reference to FIG. 50, usefully an epoxy dam structure 86 may first be deposited on the interposer surfacestep (s). The epoxy dam structure 86 may be fabricated by silk-screening an epoxy polymer, or by laminating a dry-film epoxy dam barrier that is photo-imageable. The last method is preferred as it provides high position accuracy with respect to the SU8 gasket 70 on the filter die. It should be noted that dry films may be deposited in several layers to achieve desired thicknesses. As with the gasket 70 around each filter array, the dam 86 could also be fabricated from SU-8. The dam 86 is designed to fit around the gasket 70 and could be slightly larger or smaller in area than the area surrounded by the gasket 70 to be positioned on the inside or outside of the gasket 70. Indeed two dams 86 (one encircling and the encircled by the gasket) or a plurality of gaskets 70 could be provided.

[0296] As shown in FIG. 51, the interposer may then be attached to the Composite FBAR resonator array by aligning and melting the solder caps 68 on the copper pillars 66step (t).

[0297] As shown in FIG. 52, the array device may be encapsulated in polymer 90step (u); the dams 86 and SU8 gaskets 70 working together preventing under fill of the cavity 92 within the gasket 70.

[0298] In this manner, the closely aligned SU8 connected to the Composite FBAR array and the epoxy dam connected to the substrate prevents under-fill 72 from filling the cavity 92 under the piezo resonators 18, 18.

[0299] The array of resonators is then diced into separate filter modulesstage (v), giving the structure shown in FIG. 1, for testing, packaging and shipment.

[0300] The interposer 85 may be a functional substrate with embedded inductors, lines and couplers. It should be noted the interposer 85 may subsequently be placed on the same IC Substrate together with controllers, power amplifiers and switches to generate a fully integrated Front End Module (FEM). This allows all components to be designed together to achieve optimum system performance.

[0301] Thus single crystal Composite FBARs are shown and described.

[0302] In resonator/filter designs with a Ba.sub.xSr.sub.(1-x)TiO.sub.3 piezoelectric layer, the top electrode may be split into two sections: the Al electrode itself and a separated Al line that runs bias voltage to the piezoelectric membrane and causes it to resonate. This bias voltage is usually between 5V to 40V, the voltage depending on the resonator frequency. For example, Tests performed on 2700 Piezo thick BST at 19V have caused the BST to resonate at 6.5 GHz.

[0303] Single crystal Ba.sub.xSr.sub.(1-x)TiO.sub.3 Filters are potentially tunable using capacitors build around the filter on the same silicon carrier. It has been established by numerous research groups that single crystal BST has a tunability ratio of 1:8 or even 1:10 whereas amorphous or polycrystalline BST has only has 1:3 to 1:4 tunability.

[0304] Single crystal BST, AlN, ScAlN and AlGaN FBAR resonators and thus filters have the following advantages: [0305] Such filters may save up to half of the RF power wasted as heat in prior art filters because the single crystal orientation enables polarization of the excited acoustic wave. [0306] Single crystal piezo have higher K.sup.2.sub.eff values thus enabling resonators and filters with larger bandwidths. [0307] The filters disclosed herein may operate at higher frequencies since the thickness of the ultra-thin piezoelectric membrane necessary for high frequencies is supported by an additional silicon membrane (composite FBAR). [0308] Having a composite electrode and structure that includes a silicon membrane, such filters may have second or higher harmonic mode frequencies that can extend the operating frequency range of the FBAR [0309] Single crystal BST, AlN and AlGaN FBARs disclosed herein use well-known MEMS and LED FAB manufacturing processes rather than dedicated and expensive Si FABs. This may simplify and reduce the investment and total cost to manufacture the filter device. [0310] Single crystal FBARs manufacturing processes disclosed herein use the low cost back-end processes well established and with high yields available by multiple wafer bumping and assembly houses.

[0311] Although discussed hereinabove with reference to communication filters, it will be appreciated that thickness-shear-based Composite FBARs and surface generated acoustic wave-based Composite FBARs are also used in other applications. For example they are widely used in biosensors since they provide high sensitivity for the detection of biomolecules in liquids.

[0312] In this continuation in part, the use of Sc.sub.xAl.sub.(1-x)N piezoelectric films with the novel structure and deposition method of the parent application is discussed and novel electrode combinations are disclosed, for example the upper electrode (facing the silicon handle side) may be gold, gold-tungsten, gold-molybdenum, tungsten, molybdenum or without a layer of gold for bonding to the silicon and the lower electrode facing the interposer may be aluminum, where surface activated bonding is used. The substrate may be glass with through glass vias.

[0313] Thus persons skilled in the art will appreciate that the present invention is not limited to what has been particularly shown and described hereinabove. Rather the scope of the present invention is defined by the appended claims and includes both combinations and sub combinations of the various features described hereinabove as well as variations and modifications thereof, which would occur to persons skilled in the art upon reading the foregoing description.

[0314] In the claims, the word comprise, and variations thereof such as comprises, comprising and the like indicate that the components listed are included, but not generally to the exclusion of other components.