MANUFACTURING METHOD OF FOAM SHEET FOR SHOES WITH TPU POWDER AND RECYCLED PU SCRAP POWDER

Abstract

The present invention relates to a manufacturing method for a foam sheet for shoes containing Thermoplastic polyurethane (TPU) powder and recycled Polyurethane (PU) scrap powder, and for an eco-friendly polyurethane foam composition including water foam, firstly the recycled PU scrap powder is mixed with polyol, and then the processing speed in a process is controlled through a side-feeder to react while adding the TPU powder and recycled PU scrap powder secondarily, thereby preventing a rise in viscosity of the raw material, so that even if a larger amount of recycled materials is used than before, it is possible to form foam sheets for shoes, such as shoe insoles or foam packages for shoe uppers, with the same level of product quality as conventional products.

Claims

1. A manufacturing method of foam sheet for shoes containing a Thermoplastic polyurethane (TPU) powder and a recycled polyurethane (PU) scrap powder using a polyurethane foam composition, which comprises polyol, isocyanate, a chain extender, and 0.1-2 wt % of water as a foaming agent, the method comprising: (a) mixing a polyol with 10?20% of a recycled PU scrap powder by weight based on the total weight of the Polyurethane foam block composition; (b) adding 5?30% of TPU powder, based on the total weight of the polyurethane foam composition, and 10?30% by weight of recycled PU scrap powder based on the total weight of the polyurethane foam composition to resultant composite of step (a) through a side-feeder for reacting to produce polyurethane block foam; (c) cutting the polyurethane block foam into a predetermined thickness to form a polyurethane foam sheet; (d) bonding the polyurethane foam sheet and the fabric; and (e) putting the polyurethane foam sheet bonded with the fabric into a mold and molding and cutting the molded polyurethane foam sheet bonded with fabric into a predetermined shape of a product by a heat press.

2. The method for manufacturing a foam sheet for shoes containing the recycled PU scrap powder of claim 1, wherein the recycled PU scrap powder is pulverized into a size of an average particle size of 50 to 300 ?m.

3. The method for the manufacture of a foam sheet for shoes containing TPU powder and recycled PU scrap powder of claim 1, wherein the TPU powder is used anyone selected from virgin TPU with an average particle size of 50?300 ?m and recycled TPU with an average particle size of 50?300 ?m or combination thereof.

4. The method for the manufacture of a foam sheet for shoes containing TPU powder and recycled PU scrap powder of claim 1, wherein the adhesive agent used in the step of binding the polyurethane foam sheet with the fabric is a liquid adhesive or hot melt film made of one resin composition selected from thermoplastic polyurethane (TPU) or ethylene vinyl acetate (EVA).

5. The manufacturing method of the foam sheet for shoes containing the TPU powder and the recycled PU scrap powder of claim 1, wherein the predetermined shape of the product is any one of a foam package for shoe upper or shoes insole.

6-10. (canceled)

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0024] FIG. 1 is a process flow chart showing a method for manufacturing a foam sheet for shoes according to the present invention.

DETAILED EMBODIMENTS OF THE PRESENT INVENTION

[0025] Hereinafter, a method for manufacturing a foam sheet for shoes containing TPU powder and recycled PU scrap powder of the present invention will be described with reference to the drawings. However, the method is intended to be exemplary so that a person with ordinary skills in the art to which the present invention belongs can easily implement the present invention, and does not imply that the technical ideas and categories of the present invention are limited.

[0026] In general, polyurethane resin is a resin produced based on a urethane bond generated by the reaction of an isocyanate group (NCO) and a hydroxyl group (OH) in a polymer, and its raw materials may include polyol, isocyanate, and a chain extender, etc. By adjusting the ratio of soft and hard segments that make up polyurethane, it is possible to design a variety of polyurethane foams, from elastic products such as rubber to hard products such as plastic.

[0027] The polyurethane resin has excellent film strength and adhesive strength, thereby being able to manufacture a thin coating film. The coating film has excellent elasticity, thereby being able to be manufactured into a soft-porous film or sheet, thereby imparting moisture permeability and air permeability. In addition, the polyurethane resin has excellent cold resistance, and is processed without using a plasticizer, thereby reducing workability problems caused by the plasticizer.

[0028] In addition, the polyol is an active hydrogen compound used to react with isocyanate to prepare polyurethane, wherein the polyol has two or more active hydrogen groups such as hydroxyl groups, carboxyl groups, and amine groups in the molecule, and directly affects the physical properties of the polyurethane by using various types according to molecular structure, molecular weight, functionalities, and OH-values.

[0029] For example, polyurethane using polyester polyol has higher tensile strength, hardness and elongation than polyurethane using polyether polyol, is superior in flame retardancy, has excellent drug resistance and chemical resistance, is resistant to oxidation, and has excellent adhesion to various fabrics woven with polyester or nylon. However, unlike polyether polyol, it has a weak water resistance due to its hydrolyzing property. However, since polyurethane using polyether polyol has excellent elasticity, can be used under high temperature and high humidity environment, and shows excellent durability against acid and alkali, it is preferable to use them alone or in combination depending on the application.

[0030] In a production of the polyurethane (PU) resin, polyurethane is produced by mixing polyether made by polymerization of ethylene oxide with diisocyanate, and Urethane is a mixed amide-ester that occurs when an alcohol group reacts with isocyanate. When triol is used instead of diol, cross-linking occurs to produce thermosetting polyurethane.

[0031] According to aspect(s) of the present invention, the foam sheet for shoes is manufactured by using a polyurethane foam composition comprising polyol, isocyanate, chain extender, and water in a range of 0.1-2 wt % as a foaming agent. The polyurethane foam composition may contain a recycle PU scrap powder in a range of 20?50 wt %, which is an average particle size in a range of 50?300 ?m and TPU powder in a range of 5?30 wt %, which is the average particle size in a range of 50?300 ?m based on the polyurethane foam composition total weight.

[0032] According to aspects of the present invention, a foam sheet having a hardness (ASKER C-Type) of 8 to 40 and a density of 0.05 to 0.35 g/cm.sup.3 may be formed by including 0.1 to 2 wt % of water as a foaming agent based on the total weight of the polyurethane foam composition. The foam sheet may be used for a shoes insole, a foam package for shoes uppers, etc. Water as a foaming agent may be mixed with the polyol component in advance or mixed with the polyol component at the same time as mixing with the isocyanate component later.

[0033] The foaming agent may contain a predetermined amount of water, which is a low carbon source, in consideration of workability and eco-friendliness, thereby minimizing carbon emission and producing a polyurethane foam molded body having a desired density, and reacting water with an isocyanate compound to produce carbon dioxide gas. According to aspects of the present invention, it has been studied that a method of dispersing air or nitrogen gas in a polyol component in advance by using hydrocarbons such as carbon dioxide, chlorofluorocarbons, and the like, hydrocarbons such as pentane and cyclopentane, fluorinated hydrocarbons, or an air loading device as a foaming agent widely used in the past is not only poor in workability, but also undesirable in consideration of environmental hazards such as carbon emission and expensive energy costs.

[0034] According to aspects of the present invention, it is possible to significantly reduce molding time by containing thermoplastic polyurethane (TPU) powder having an average particle size of 50 to 300 ?m in an amount of 5 to 30% by weight based on the total weight of the polyurethane foam composition. Based on the fact that the thermoplastic polyurethane (TPU) powder has excellent physical and chemical miscibility with a polyurethane (PU) foam composition which is a polymer resin of the same kind, the thermoplastic polyurethane (TPU) powder is dispersed into a particle size having the most suitable kneadability, thereby obtaining excellent moldability by a heat press and excellent product quality such as homogeneity, elasticity, durability.

[0035] The TPU powder can adjust the particle size or the content thereof within a specified range according to the hardness and density of the desired molded body. if the average particle size of TPU powder is less than 50 ?m, the blending property with the polyurethane foam composition is deteriorated, and if the average particle size of TPU powder exceeds 300 ?m, the dispersibility becomes poor, thereby increasing the defect rate of the product manufactured after molding.

[0036] In addition, if a TPU powder in the polyurethane foam composition is less than 5 wt %, the effect of shortening the molding time by the heat press is insignificant. if the TPU powder in the polyurethane foam composition is more than 30 wt %, the setting of the process conditions for uniformly forming the hardness of the molded product is limited, and thus it is difficult to manufacture the foam molded product having the desired elasticity, i.e., cushionability.

[0037] The thermoplastic polyurethane (TPU) is a typical (AB)n-type copolymer and has a structure in which a hard segment and a soft segment are repeated. As a result of its thermal behavior and surface characteristics, it is highly durable, highly abrasive, flexible and workable, and is widely used as a material for surface coatings and artificial leather. It focuses on the fact that it is an elastomer capable of plastic processing by heat even if a separate plasticizer agent is not added.

[0038] A recycled PU scrap used in the present invention may be, for example, obtained from the manufacturing method of a dotted shoes insole using an adhesive resin mixed with hydrophobic nano-silica of Korean Patent No. 10-2131606 developed by the inventor of the present application, about 35 to 40% of the scrap generated after cutting the shape of the shoes insole in a package in which the foam and the fabric are combined can be easily separated into a foam and a fabric, respectively, and recycled.

[0039] As described above, the PU scrap separated from the fabric is mixed with the recycled PU scrap powder crushed to the size of the average particle size of 50?300 ?m through the step-by-step grinding process into the raw material (polyol), so that the formability is not deteriorated, but also the elasticity is good, which is advantageous to ensure the quality of the product stably.

[0040] Accordingly, according to an aspect of the present invention, an eco-friendly polyurethane (PU) foam composition made by a water foam may include a predetermined amount of Thermoplastic polyurethane (TPU) powder with an average particle size of 50 to 300 ?m, and the polyurethane foam sheet formed therefrom is placed in a mold for molding. By reducing the molding process time of the polyurethane foam sheet by half by heat press, product productivity can be greatly improved, expensive energy costs can be reduced, and carbon emissions can be dramatically reduced.

[0041] In addition, according to an aspect of the present invention, firstly mixing recycled PU scrap powder with polyol and then secondarily adding TPU powder and recycled PU scrap powder by controlling the process conditions and processing speed through a side-feeder, thereby viscosity of the raw materials can be prevented from being increased. Accordingly, it is possible to form foam sheets for shoes, such as shoes insoles or foam packages for shoes uppers, with the same level of product quality as before, even if a larger amount of recycled materials are used than a conventional method.

[0042] As shown in FIG. 1, a method for manufacturing a foam sheet for shoes containing TPU powder and recycled PU scrap powder according to the present invention uses a polyurethane foam composition composed of polyol, isocyanate, chain extender, and 0.1-2 wt % of water as a foaming agent, the method may include: a step of producing a polyurethane foam composition in which recycled PU scrap powder is uniformly mixed with the polyol at a ratio of 10 to 20% by weight based on the total weight of the polyurethane foam composition S100; a step of preparing a polyurethane block foam by reacting a polyurethane foam composition by adding 5-30 wt % of TPU powder and 10-30 wt % of recycled PU scrap powder based on the total weight of the polyurethane foam composition through a side-feeder and reacting the same S200; a step of forming a polyurethane foam sheet by cutting the polyurethane block foam to a predetermined thickness S300; a step of bonding the polyurethane foam sheet cut to a predetermined thickness with a fabric S400; and a step of putting the polyurethane foam sheet in the mold and molding and cutting into a predetermined shape by putting the fabric into the mold and molding and cutting into the predetermined shape by a heat press S500.

[0043] First, in the stage of preparing the polyurethane foam composition S100, a raw material may include polyol, isocyanate, chain extender, and 0.1?2% of water by weight as a foaming agent based on the total weight of the polyurethane foam composition, the recycled PU scrap powder in a rate of 10?20% by weight based on the total weight of the polyurethane foam composition is mixed with the polyol, and if the recycled PU scrap powder exceeds 20% by weight based on the total weight of the polyurethane foam composition, the viscosity of the raw material will increase, and it will be difficult to knead for the subsequent foam reaction, so the reactivity will be poor.

[0044] For the reason mentioned above, conventionally, it was recognized as a general limit to recycle waste by limiting the content of recycled PU scrap powder mixed into the polyurethane foam composition to less than 20% by weight, but, the process technology according to an aspect of the present invention that can include up to 50% of recycled PU scrap powder and TPU powder 5?30% by weight based on the total weight of the polyurethane foam composition by providing a separate side-feeder that can be injected into the recycled PU scrap powder as a secondary input is provided.

[0045] Accordingly, according to an aspect of the present invention, the process conditions and processing speed are adjusted through a side-feeder provided in the step of manufacturing polyurethane block foam S200, and TPU powder 5 to 30 wt % is added based on the total weight of the polyurethane foam composition and 10 to 30% by weight of recycled PU scrap powder, respectively, an increase in the viscosity of the raw materials is prevented, thus, making the product for shoes insoles, shoes uppers, or a foam sheet for shoes of the same quality as a conventional method, even though a larger amount of recycled materials is used than the conventional method.

[0046] The polyurethane block foam formed as described above may have further processed, which include: a step of forming a polyurethane foam sheet by cutting the polyurethane block foam to a predetermined thickness within 1-10 mm (usually such as 2, 4, 5, 6 mm, etc.) S300 and a step of bonding the polyurethane foam sheet cut to a predetermined thickness with the fabric S400. The adhesive used in the step S400 of bonding the polyurethane foam sheet with a fabric is preferably a liquid adhesive or a hot melt film composed of any one resin composition selected from thermoplastic polyurethane (TPU) or ethylene vinyl acetate (EVA) having excellent compatibility with the polyurethane foam sheet.

[0047] The adhesive made of the thermoplastic polyurethane (TPU) or ethylene vinyl acetate (EVA) is eco-friendly by not using a solvent, has good workability and productivity, and is advantageous in securing adhesion to various fabrics due to characteristics of a flexible material. In particular, excellent durability can be secured by maintaining strong adhesion to the polyurethane foam sheet for a long period of time.

[0048] Next, the foam sheet for shoes is manufactured through a step S500 in which the polyurethane foam sheet bonded with the fabric is put into a mold and molded and cut into a product of a predetermined shape by a heat press. Typically, when a polyurethane foam sheet bonded with the fabric is put into a mold and molded by a heat press having a temperature of 150 to 200? C. and a pressure of 40 to 60 kgf/cm.sup.2, the molding time required therefor can be greatly reduced. In the case of a shoes insole, the molding time can be reduced from about 100 seconds in a conventional art to 40 to 60 seconds in the present invention, and the foam package for shoes uppers can be reduced from about 40 seconds in a conventional art to about 10 to 30 seconds in the present invention.

[0049] According to the present invention, the thermoplastic polyurethane (TPU) powder having an average particle size of 50-300 ?m is contained in a ratio of 5-30 wt % based on the total weight of the polyurethane foam composition, thereby improving the moldability of the polyurethane foam composition and shortening the molding time by half in the step 400 of processing the polyurethane foam composition into a shoes insole shape by a heat press.

[0050] In addition, firstly, recycled PU scrap powder with an average particle size of 50?300 ?m is mixed with polyol, and then the processing speed is adjusted through a side-feeder to mix TPU powder and recycled PU scrap powder secondarily. By adding the TPU powder and the recycled PU scrap powder secondly into the first mixed composition for reacting, an increase in the viscosity of the raw materials can be prevented, despite using a larger amount of recycled materials than conventional method before.

[0051] It is possible to form foam sheets for shoes, such as foam packages for shoes insoles or shoe uppers, with product quality equivalent to those of conventional products.

[0052] That is, according to aspect(s) of the present invention, since TPU powder is included in the polyurethane foam composition, even if a heat press operation is performed under the same temperature and pressure conditions, the molding time to be processed into a foam sheet for shoes can be reduced to a half level. In addition, a large amount of PU foam scrap generated in a manufacturing process such as a shoes insole can be recycled, thereby being environmentally friendly and reducing costs.

[0053] The thermoplastic polyurethane (PU) powder is highly chemically compatible with the polyurethane foam composition of the same kind, and is highly moldable by a heat press as it is dispersed in a suitable size. If the average particle size of the TPU is less than 50 ?m, the dispersibility of the polyurethane foam composition is poor, and if the average particle size of the TPU exceeds 300 ?m, the dispersibility becomes poor, so there is a fear that the defect rate of the product manufactured after molding may increase. In addition, for the same reason, it is preferable that the maximum particle size of the particles contained in the TPU powder may not be exceeded 500 ?m.

[0054] The TPU powder may be either virgin TPU or recycled TPU used alone or may be used by mixing them in a predetermined ratio. For example, a recycled TPU can be obtained by recovering and crushing a discarded airbag for shoes.

[0055] Hereinafter, a method for manufacturing a foam sheet for shoes containing TPU powder and recycled PU scrap powder according to an aspect of the present invention will be described in detail, and an aspect of the present invention will be described through preferred embodiments that can be easily performed by a person with ordinary skills in the art to which the present invention belongs.

Example 1: Manufacturing of Shoes Insole

[0056] The shoes insole manufactured in accordance with the present invention is a method of polymerizing a polyurethane foam composition, which includes polyol, isocyanate, chain extender, and a foaming agent as water, and the method may include the following five steps.

[0057] Step 1: Polyurethane foam composition comprising polyol and isocyanate and water as foaming agent in the range of 0.1?2% by weight based on the total weight, the polyurethane foam composition mixed with recycled PU scrap powder with an average particle size of 150 ?m for the polyol at the ratio of 10?20% by weight was prepared.

[0058] Step 2: Based on the total weight of the polyurethane foam composition through the side-feeder, 5?30% of TPU powder with an average particle size of 150 ?m and 10?30% of recycled PU scrap powder were added and reacted to produce polyurethane block foam.

[0059] Step 3: The polyurethane block foam was cut into 4 mm thick to form a polyurethane foam sheet.

[0060] Step 4: The polyurethane foam sheet cut into 4 mm thickness was bonded with polyester fiber fabric using a thermoplastic polyurethane (TPU) hot melt film.

[0061] Step 5: The polyurethane foam sheet bonded with the above fabric was put into a mold, molded and cut into a drawn insole shape by a heat press with a temperature of 170? C. and a pressure of 50 kgf/cm.sup.2 to manufacture the shoes insole.

[0062] In the case of manufacturing a shoes insole such as in Example 1, in order to measure the molding time of processing the polyurethane foam sheet combined with the fabric by the heat press according to the ratio of recycled PU scrap powder and TPU powder included in the polyurethane foam composition in the first and the second steps, in the fifth step to process the polyurethane foam sheet into the shape of the shoes insole as in the comparative example 1, the same type of polyurethane foam sheet not containing TPU powder as in the comparative example 1 was tested in comparison with the molding time to process the shoes insole shape, Accordingly, the average value of the results of the evaluation of the molding time, formability, and appearance condition several times is shown in Table 1 below.

TABLE-US-00001 TABLE 1 Example Example Example Example Example Example Example category 1-1 1-2 1-3 1-4 1-5 1-6 1 (step 1) PU scrap 10 10 15 15 20 20 15 powder(w %) (step 2) TPU 5 10 15 20 25 30 0 powder(w %) (step 2) PU scrap 30 25 20 20 15 10 0 powder(w %) (step 5) Molding 60 57 53 50 45 40 100 time(sec.) Formability and good good good good good good good appearance

[Example 2] Manufacturing of Foam Package for Shoes Upper

[0063] The foam package for the shoes upper manufactured in accordance with the present invention is a method of polymerization of a polyurethane foam composition, which comprises polyol, isocyanate, chain extender, and water as a foaming agent, and may include the following five steps.

[0064] Step 1: Polyurethane foam composition comprising polyol, and isocyanate, chain extender, water as foaming agent in the range of 0.1?2% by weight based on the total weight of the Polyurethane foam composition, the polyol is mixed with recycled PU scrap powder with an average particle size of 150 ?m for the polyol at the ratio of 10?20% by weight.

[0065] Step 2: Based on the total weight of the polyurethane foam composition through the side-feeder, 5?30% of TPU powder with an average particle size of 150 ?m and 10?30% by weight of recycled PU scrap powder were added and reacted to produce polyurethane block foam.

[0066] Step 3: The polyurethane block foam was cut into 2 mm thick to form a polyurethane foam sheet.

[0067] Step 4: The polyurethane foam sheet cut into 2 mm thickness was bonded with PU skin film fabric using thermoplastic polyurethane (TPU) hot melt film.

[0068] Step 5: The polyurethane foam sheet combined with the above fabric was put into a mold, and the foam package for the shoes upper was formed and cut into a foam package for the shoes upper by a heat press with a temperature of 170? C. and a pressure of 50 kgf/cm.sup.2.

[0069] In the case of manufacturing a foam package for the shoes upper as shown in the embodiment 2, in order to measure the molding time of processing the polyurethane foam sheet combined with the fabric by the heat press according to the ratio of recycled PU scrap powder and TPU powder included in the polyurethane foam composition in the first and the second steps, the molding time of processing the polyurethane foam sheet which did not contain TPU powder into the foam package shape for the shoes upper was tested compared to the molding time of processing the polyurethane foam sheet for the shoes upper into the foam package shape as in the comparative example 2, Accordingly, the average value of the results of the evaluation of the molding time, formability, and appearance condition several times is shown in Table 2 below.

TABLE-US-00002 TABLE 2 Example Example Example Example Example Example Comparative category 2-1 2-2 2-3 2-4 2-5 2-6 Examples 2 (1 step) PU Scrap 10 10 15 15 20 20 15 Powder(w %) (2 step) TPU 5 10 15 20 25 30 0 powder(w %) (2 step) PU scrap 30 25 20 20 15 10 0 powder(w %) (5 step) Forming 25 23 22 20 18 15 40 time(seconds) Formability and good good good good good good good appearance

[0070] As shown in [Table 1] and [Table 2], the shoes insole manufactured by embodiments 1-1 to 1-6 and the foam package for shoes uppers manufactured by embodiments 2-1 to 2-6 are found to have excellent moldability, adhesion between the fabric and the polyurethane foam sheet, and appearance quality, as shown in each the comparative example 1 or the comparative example 2.

[0071] However, when the content of the TPU powder exceeds 30 w %, a part of the TPU powder present in the polyurethane foam sheet is melted during the molding operation by the heat press, and thus the density and hardness of the insole product may be uneven as a part of the overflow phenomenon is observed in a joint portion where the fabric and the polyurethane foam sheet are bonded.

[0072] As described above, the present invention may include the TPU powder of a predetermined particle size in the eco-friendly polyurethane foam composition at an appropriate ratio, thereby reducing a time required for molding the polyurethane foam sheet bonded by fabric into a shoes insole shape by a heat press to a half level, thereby significantly improving product productivity and reducing expensive energy costs.

[0073] According to an aspect of the present invention, firstly, recycled PU scrap powder having a predetermined particle size is mixed with polyol in a polyurethane foam composition, by adjusting process conditions and processing speed through a side-feeder, TPU powder and recycled PU scrap powder are added and reacted secondarily to prevent an increase in the viscosity of the raw material.

[0074] It was confirmed that a foam sheet for shoes, such as a foam package for a shoe upper, can be formed the same quality as existing ones even if a larger amount of recycled material, i.e. recycled PU scrap powder, is used than before.

Experimental Examples

[0075] In order to confirm the exemplary characteristics of the polyurethane foam composition according to the present invention, two kinds of polyurethane foam sheets (shoes insole, shoes upper foam package) containing 20 wt % of thermoplastic polyurethane (TPU) powder having an average particle size of about 150 ?m and 35 wt % of recycled PU scrap powder were manufactured under the same conditions as existing heat presses (temperature 150-200? C. & pressure 40-60 kgf/cm.sup.2), the results of several tests on the physical properties thereof are shown in [Table 3].

TABLE-US-00003 TABLE 3 Foam package Properties unit Shoes insoles for shoes upper hardness 30/29/29/30/29 19/19/19/20/20 (ASKER C) density g/cm.sup.3 0.148/0.148/0.148 0.142/0.143/0.143 Tear Strength kgf/cm 3.1/3.0/3.1 2.4/2.4/2.6 Tensile strength kgf/cm.sup.2 6.4/6.1/6.6 5.6/5.3/5.4 Elongation rate % 105/105/111 123/110/118 Shrinkage rate % 0.18/0.17/0.15 0.09/0.05/0.05 hardness: ASKER C type Durometer based on JIS K 7312.

[0076] As shown in Table 3, the foam sheet for shoes containing the TPU powder and the recycled PU scrap powder according to the present invention reduces molding time by heat press to a half level compared to that of the conventional art. However, it is confirmed that the overall physical properties such as tear strength, tensile strength, elongation, shrinkage, etc. can be manufactured at the same level as conventional polyurethane foam sheets without having TPU powder. The polyurethane foam molded body has a hardness range of ASKER C-Type 8?40 and density 0.05?0.35 g/cm.sup.3.

[0077] According the foam sheet for shoes containing the TPU powder and the recycled PU scrap powder manufactured by aspect(s) of the present invention can be substituted, modified, and changed in various forms within a range not departing from the scope and spirit of the invention. In particular, the present invention is eco-friendly to the environment and reduces productivity and manufacturing costs.

[0078] Accordingly, the present invention can be applied to various kinds of foam packages for shoe insoles and shoe uppers, which require uniform moldability and durability, as well as various applications requiring functions such as molding materials, buffering materials, and fillers used inner parts of clothes, bags, sporting goods, household goods, and industrial goods manufactured with fibers, natural and synthetic leather, plastics, etc.