Tire with a tread sub-layer containing multiple materials

Abstract

Tire (1) having a sub-layer (7) made up substantially of a base layer (71) disposed radially on the crown reinforcement (5) and axially between the median plane (CP) and a shoulder (60), said base layer (71) being made up of a rubber compound of given stiffness A, a covering layer (72) disposed radially on the base layer (71) and radially on the inside of the tread (6) and axially at least in sections situated between the median plane (CP) and the shoulder end (721), said covering layer (72) being made up of a rubber compound of given stiffness B, the stiffness A being less than the stiffness B, and the stiffness B being greater than the stiffness M.

Claims

1. A tire having an axis of rotation and a median plane (CP) perpendicular to the axis of rotation, comprising: a crown reinforcement, a tread radially on the outside of the crown reinforcement, the tread comprising material extending axially between two shoulders, the tread comprising a contact face intended to come into contact with a roadway when the tire is being driven on, the tread being made up of at least one rubber compound of given stiffness M, wherein the tread has furrows, oriented substantially circumferentially, each furrow having a respective bottom furrow width, and a sub-layer disposed radially on the outside of the crown reinforcement and radially on the inside of the tread, wherein at least on one side axially with respect to the median plane (CP), the sub-layer is formed by: a base layer disposed radially directly on the crown reinforcement and axially between the median plane (CP) and a shoulder, said base layer being made up of a rubber compound of given stiffness A, a covering layer disposed radially directly on the base layer and radially on the inside of the tread and axially separated in portions situated between the median plane (CP) and the shoulder, said covering layer being made up of a rubber compound of given stiffness B, wherein the portions are radially beneath the contact face of the tread and separations in the covering layer, each have a respective axial separation width, are arranged radially beneath the furrows, wherein for each respective separation that is radially in line with a respective furrow, each respective axial separation width is equal to the respective bottom furrow width, wherein a radially outer face of the covering layer is planar, the stiffness A being less than the stiffness B, and the stiffness B being greater than the stiffness M, and the dynamic shear modulus G* of material of the base layer, measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation, being less than 0.6 MPa.

2. The tire according to claim 1, wherein the dynamic shear modulus G* of the material of the base layer, measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation, is less than 0.5 MPa.

3. The tire according to claim 1, wherein the tg ? value measured at 23? C. at 10 Hz and under an alternating shear deformation of 10% of the material of the base layer is less than 0.3.

4. The tire according to claim 1, wherein the dynamic shear modulus G* of material of the covering layer, measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation, is strictly greater than 7 MPa.

5. The tire according to claim 4, wherein the dynamic shear modulus G* of the material of the covering layer, measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation, is strictly greater than 12 MPa.

6. The tire according to claim 4, wherein the tg ? value measured at 23? C. at 10 Hz and under an alternating shear deformation of 10% of the material of the covering layer is less than 0.3.

7. The tire according to claim 1, wherein the covering layer is formed by at least three portions that are separated axially.

8. The tire according to claim 1, wherein material visible at the bottom of each furrow is the same material as the material of which the tread is made.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The invention will now be described with the aid of the appended drawing, in which:

(2) FIG. 1 schematically shows a meridian section through a tire according to a first embodiment of the invention;

(3) FIG. 2 schematically shows a meridian section through a tire according to a second embodiment of the invention;

(4) FIG. 3 is a simplified depiction of a third embodiment of the invention;

(5) FIG. 4 shows a simplified depiction of a fourth embodiment of the invention;

(6) FIG. 5 is a simplified depiction of a fifth embodiment of the invention.

DETAILED DESCRIPTION OF THE DRAWINGS

(7) FIG. 1 shows a tire 1, an equatorial plane CP, two beads 2 and two sidewalls 3 each connected to a bead 2. The tire has a crown 4, which has a crown reinforcement 5 and a tread 6. The tread extends axially from one shoulder 60 to the other shoulder. The tread comprises a contact face 61 intended to come into contact with the roadway when the tire is being driven on. The tread 6 has tread blocks 63 that are separated by furrows 62 that are oriented substantially circumferentially. Each furrow 62 is delimited radially towards the inside by a furrow bottom 620.

(8) The crown also has a sub-layer 7 disposed radially on the outside of the crown reinforcement 5 and radially on the inside of the tread 6. This sub-layer is formed by two parts: a base layer 71 and a covering layer 72.

(9) The base layer 71 is disposed radially directly on the crown reinforcement 5. As is known per se, the crown reinforcement has layers of cords or of monofilament reinforcers that are generally coated with a thin layer of rubber. In the context of the present invention, the indication that the base layer 71 is disposed radially directly on the crown reinforcement 5 means that it is in contact with the cords or reinforcers, not taking the rubber coating thereof into account.

(10) A covering layer 72 disposed radially on the base layer and axially at least in portions situated between the median plane CP and the shoulder end 60 can also be seen. Note that, in this embodiment, the material of the tread 6 is visible in the groove bottom 620; the material of the covering layer 72 is thus coated (radially upwardly) by a very thin film of tread material 6.

(11) FIG. 2 shows a second embodiment of the invention, very similar to the one illustrated in FIG. 1: in this second embodiment, the material of the covering layer 72 is visible in the groove bottom 620.

(12) The materials used for the sub-layer 7 will now be discussed. In order to characterize them, the dynamic shear modulus G* measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation is used.

(13) Preferably, the material of the base layer 71 is characterized by a dynamic shear modulus G* measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation of less than 1.5 MPa and preferably less than 0.5 MPa; very advantageously, the dynamic shear modulus G* of this material, measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation, has a value of 0.3 MPa. These are conventional values for sub-layers of the usual configuration, that is to say ones that are made of a single material and extend axially from one shoulder of the tire to the other. Advantageously, the tg ? value measured at 23? C. at 10 Hz and under an alternating shear deformation of 10% of the material of the base layer 71 is less than 0.3 and very advantageously, the tg ? value is around 0.05.

(14) As for the covering layer 72, the material thereof is preferably characterized by a dynamic shear modulus G* measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation of greater than 7 MPa and preferably greater than 12 MPa; very advantageously, the dynamic shear modulus G* of this material, measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation, has a value greater than 20 MPa. In this way, good cornering stiffness is achieved and an excellent performance compromise is obtained, reconciling a drift thrust that is able to give the tire a good dynamic response and excellent rolling resistance. Advantageously, the tg ? value measured at 23? C. at 10 Hz and under an alternating shear deformation of 10% of the material covering layer 72 is less than 0.3.

(15) An example of an appropriate formulation for the material of the base layer 71, with a dynamic shear modulus G* measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation of 0.2 MPa, is as follows:

(16) TABLE-US-00001 TABLE 1 Component phr NR 100 Carbon black 4 6PPD 2.2 DPG 2.1 Stearic acid 3 ZnO 1.5 Resin 29.3 HTO 38
The formulations are given by weight (phr meaning percentage of the weight of elastomer).

(17) An example of an appropriate formulation for the material of the covering layer 72, with a dynamic shear modulus G* measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation of 25 MPa, is as follows:

(18) TABLE-US-00002 TABLE 2 Component phr NR 100 Carbon black 70 Phenol-formaldehyde resin 12 ZnO 3 Stearic acid 2 6PPD 2.5 HMT 4 Sulfur 3 CBS 2
The formulations are given by weight (phr meaning percentage of the weight of elastomer).

(19) As for the material of the tread, according to the invention, the stiffness M thereof is less than the stiffness B of the covering layer. Advantageously, the rubber compound has a dynamic shear modulus G* measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation of less than 4.0 MPa and preferably less than 2.5 MPa.

(20) The following Table 3 gives an example of a tread formulation:

(21) TABLE-US-00003 TABLE 3 Component phr SBR (a) 100 Silica (b) 110 Coupling agent (c) 9 Liquid plasticizer (d) 20 Resin plasticizer (e) 50 Black 5 Zinc oxide 3 Stearic acid 2 Antioxidant (f) 2 Accelerator (g) 2 DPG 2 Sulfur 1
The formulations are given by weight (phr meaning percentage of the weight of elastomer), with: (a) SBR with 27% stirene, 1,2-butadiene: 5%, cis-1,4-butadiene: 15%, trans-1,4-butadiene: 80% Tg ?48? C. (b) Zeosil1165MP silica from Solvay with BET surface area of 160 m.sup.2/g (c) SI69 TESPT silane from Evonik (d) Flexon 630 TDAE oil from Shell (e) Escorez 2173 resin from Exxon (f) Santoflex 6PPD antioxidant from Solutia (g) Santocure CBS accelerator from Solutia

(22) A person skilled in the art, who is a tire designer, could adopt embodiment variants in which the tread itself comprises several different materials that are superposed radially and/or juxtaposed axially.

(23) In the embodiment of the invention illustrated in FIGS. 1 and 2, the covering layer 72 is axially continuous between the two shoulders 60. FIG. 3 shows a third embodiment, in which a covering layer 721 is formed by several portions that are separated axially, said covering layer being interrupted under the furrows 62. At the interruption, the material that is visible at the furrow bottom 620 is the same as the material of the tread 6. Overall, this embodiment makes it possible to significantly improve the rolling resistance at the cost of a very modest worsening in the cornering stiffness. Advantageously, the material visible at the bottom of the furrow 620 is the same material as the material of which the tread 6 is made (that is to say the predominant material in the tread).

(24) FIG. 4 illustrates a fourth embodiment of the invention, very similar to the one illustrated in FIG. 3: in this fourth embodiment, at the interruption, the material visible at the furrow bottom 620 is the same as the material of the base layer (71) situated radially beneath the furrow in question; thus, it can be seen that the material of the base layer 71 is visible at the bottom of the furrow 62a and of the furrow 62b.

(25) In order to improve the rolling resistance and at the same time to improve the cornering stiffness, it is possible to use wedge-shaped elements 630 in the wearing part of the tread. FIG. 5 illustrates a fifth embodiment, in which a covering layer 722, axially at some tread blocks 63, is extended radially outwards by a wedge-shaped reinforcing element 630 (seen in meridian section). This reinforcing element 630 extends radially from the radially outer surface 722S of the covering layer 722 towards the outside of the tread 6 to a radial height greater than 75% of the radial thickness of the tread. Said reinforcing element 630 is of variable axial width, from a maximum value less than 50% of the axial width of said tread block, said axial width decreasing radially upwardly. The angle formed in radial section by the two lateral walls of said reinforcing element 630 is preferably between 10? and 50?, specifically for example 40?, as illustrated in FIG. 3. The tread has such a reinforcing element 630 on either side of each furrow 62. Each reinforcing element is advantageously made up of the same rubber compound as the covering layer 722, thereby making it possible to extrude them in one and the same operation with the covering layer 722.

Tests

(26) As control, use is made of a tire R having a tread made of a compound with a dynamic shear modulus G* measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation of 3.0 MPa, and a single-material sub-layer extending axially from one shoulder of the tire to the other and having a thickness that is radially substantially constant; as seen in radial section, the profile of this sub-layer is the same as the profile of the assembly of the base layer 71; this sub-layer is formed by a compound having a dynamic shear modulus G* measured at 23? C. and under an alternating shear stress at a frequency of 10 Hz and at 10% deformation of 0.2 MPa. A first test tire T1 is in accordance with the example of the invention that is illustrated in FIG. 1, using the materials illustrated in Tables 1 to 3. A second test tire T2 is in accordance with the example of the invention that is illustrated in FIG. 3 (covering layer 721 interrupted), using the materials illustrated in Tables 1 to 3. A third test tire T3 is in accordance with the example of the invention that is illustrated in FIG. 5 (this example combines an interrupted covering layer with reinforcing elements 630 on either side of each furrow 62, these two embodiment aspects being able to be used independently of one another), using the materials illustrated in Tables 1 to 3. The rolling resistance value (kg/T) and cornering stiffness value Dz (N/?) are with respect to the base 100 for the control R and expressed as relative values with respect to the base 100 for the tires according to the invention. The measurement of the cornering stiffness of a tire makes it possible to evaluate the road holding of a vehicle through the capacity thereof to react during an action on the steering wheel or to follow the trajectory of a bend. This cornering stiffness is measured on an apparatus and consists in causing a tire mounted on a rim and inflated to a nominal pressure to roll on a bonded metal strip, by means of a machine of the Flat Track type. The measurement is taken when the tire is rolling at 80 km/h with a chain of stresses varying the load, cornering and camber conditions. The rolling resistance can be measured in accordance with the standard ISO28580.

(27) TABLE-US-00004 TABLE 4 Cornering stiffness Rolling resistance (with respect to a base 100) (with respect to a base 100) Tire R 100% 100% Tire T1 (FIG. 1) 89% 110% Tire T2 (FIG. 3) 84% 110% Tire T3 (FIG. 5) 118% 113%
It will be noted that the invention allows the performance compromise between rolling resistance and cornering stiffness to be moved; it allows a very significant improvement in the rolling resistance at the cost of a reduction in the cornering stiffness that is quite acceptable for applications to passenger vehicles in which the desired performance is especially rolling comfort. It will also be noted that, by adopting the fifth embodiment, a very large increase both in rolling resistance and in cornering stiffness is achieved.

(28) The scope of protection of the invention is not limited to the examples given hereinabove. The invention is embodied in each novel characteristic and each combination of characteristics, which includes every combination of any features which are stated in the claims, even if this feature or combination of features is not explicitly stated in the examples.