GAS SEPARATION MEMBRANE
20240335797 ยท 2024-10-10
Assignee
Inventors
- Toshiyuki Kawashima (Osaka, JP)
- Shunsuke NOMI (Osaka, JP)
- Yasuyuki SAKAKIBARA (Osaka, JP)
- Jianhua FANG (Shanghai, CN)
- Jingqiu YU (Hubei, CN)
- Xiaoxia GUO (Shanghai, CN)
Cpc classification
International classification
Abstract
An object of the present invention is to provide a gas separation membrane containing a novel sulfonated polyimide and having superior gas separation performance. The gas separation membrane of the present invention contains a sulfonated polyimide represented by the following general formula (1):
##STR00001##
wherein Ar is an aryl group, X is more than 0 and 1 or less, and M.sup.+ is H.sup.+ or a metal cation.
Claims
1. A gas separation membrane comprising a sulfonated polyimide represented by the following general formula (1): ##STR00011## wherein Ar is an aryl group, X is more than 0 and 1 or less, and M.sup.+ is H.sup.+ or a metal cation.
2. The gas separation membrane according to claim 1, wherein the aryl group is one or more aryl groups represented by the following chemical formulas (2) to (7): ##STR00012##
3. The gas separation membrane according to claim 1, wherein the metal cation is a mono- to tri-valent metal cation.
4. The gas separation membrane according to claim 2, wherein the metal cation is a mono- to tri-valent metal cation.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0024]
[0025]
[0026]
[0027]
[0028]
MODE FOR CARRYING OUT THE INVENTION
[0029] Hereinafter, embodiments of the present invention will be described.
<Gas Separation Membrane>
[0030] The gas separation membrane of the present invention contains a sulfonated polyimide represented by the following general formula (1):
##STR00004##
wherein Ar is an aryl group, X is more than 0 and 1 or less, and M.sup.+ is H.sup.+ or a metal cation.
[0031] The aryl group is not particularly limited, but is preferably one or more aryl groups represented by the following chemical formulas (2) to (7).
##STR00005##
[0032] The metal cation is not particularly limited, but is preferably a mono- to tri-valent metal cation, more preferably a divalent or trivalent metal cation, and still more preferably a trivalent metal cation. Examples of the monovalent metal cation include Li.sup.+, Na.sup.+, and K.sup.+. Examples of the divalent metal cation include Mg.sup.2+, Ca.sup.2+, and Zn.sup.2+. Examples of the trivalent metal cation include Al.sup.3+ and Fe.sup.3+.
<Synthesis of Monomer>
[0033] Both the dianhydride and the non-sulfonated diamine monomer are commercially available products, but the sulfonated diamine can be easily synthesized from 9,9-bis(4-aminophenyl) fluorene, which is a commercially available diamine monomer, via a one-step reaction (sulfonation). By using these, scale-up production of the sulfonated polyimide of the present invention is facilitated.
[0034] The sulfonated diamine 9,9-bis(4-aminophenyl) fluorene-2,7-disulfonic acid (BAPFDS) can be synthesized by modifying the method described in a document (X. Guo et al., Macromolecules 2002, 35, 6707-6713). One example of the sulfonation reaction is shown below.
##STR00006##
[0035] The detailed synthesis procedure is as follows. To a dry four-necked flask equipped with a mechanical stirrer, a nitrogen inlet and a nitrogen outlet were added 9,9-bis(4-aminophenyl) fluorene and concentrated sulfuric acid. The mixture was mechanically stirred at room temperature until the solid was completely dissolved. The reaction mixture was heated at 80 to 150? C. and maintained at this temperature for 1 to 20 hours. After cooling to room temperature, the reaction mixture was poured into ice water. The resulting precipitate was collected by filtration, redissolved in an aqueous sodium hydroxide solution, and then filtered again to make insoluble impurities to be removed. The filtrate was acidified and the precipitate was collected by filtration, washed thoroughly with deionized water, and finally dried in vacuum at 120? C. for 10 hours. The concentration of 9,9-bis(4-aminophenyl) fluorene was controlled in the range of 5 to 80 w/v %. Concentrated sulfuric acid is defined as having a sulfuric acid content greater than 95%.
<Synthesis of Sulfonated Polyimide>
[0036] The sulfonated polyimide was synthesized by a conventional one-step high-temperature polymerization method. One specific example of the polymerization reaction is shown below.
##STR00007##
[0037] The detailed polymerization procedure is as follows. To a dry three-necked flask equipped with a magnetic stirrer, a nitrogen inlet, a nitrogen outlet, and a condenser were added a sulfonated diamine BAPEDS, an organic solvent, and an organic base under a stream of nitrogen. The mixture was stirred to completely dissolve the solid. Next, a non-sulfonated diamine, 1,4,5,8-naphthalenetetracarboxylic dianhydride (NTDA), and benzoic acid were added to the flask and the reaction mixture was stirred at room temperature for 30 minutes, and subsequently heated at 80? C. for 1 to 6 hours and at 180? C. for 1 to 10 hours continuously. The reaction mixture was cooled to room temperature and then isoquinoline was added. The reaction mixture was again heated at 180? C. for additional 2 to 10 hours. After cooling to room temperature, the highly viscous polymer solution was poured into methanol. The resulting fibrous precipitate was collected by filtration, washed thoroughly with methanol and dried in vacuo, affording a sulfonated polyimide in a triethylammonium salt form.
[0038] The non-sulfonated diamine is preferably [0039] 2,4,6-trimethyl-1,3-phenylenediamine (TrMPD), [0040] 2,3,5,6-tetramethyl-1,4-phenylenediamine (TeMPD), [0041] 2,2-bis(trifluoromethyl)benzidine (BTFBz), [0042] 3,7-diamino-2,8-dimethyldibenzothiophene sulfone (DDBT), [0043] 9,9-bis(4-aminophenyl) fluorene (BAPF), or [0044] 9,9-bis(4-amino-3,5-dimethylphenyl) fluorene (BADMPF) shown below.
##STR00008##
[0045] Examples of the organic solvent include, but are not limited to, m-cresol and p-chlorophenol. Examples of the organic base include, but are not limited to, triethylamine and pyridine. The molar ratio of the dianhydride (NTDA) to all diamines (BAPFDS+non-sulfonated diamine) is preferably controlled to 1:1, and the molar fraction of the sulfonated diamine BAPFDS in all diamines x is in the range of 0<x?1. The total monomer concentration is preferably controlled to 8 to 30 w/v %. The molar ratio of the organic base to BAPFDS is preferably controlled to 2 to 3:1. The molar ratio of benzoic acid to NTDA is preferably controlled to 0.5 to 3:1. The molar ratio of isoquinoline to NTDA is preferably controlled to 0.5 to 3:1.
<Solubility of Sulfonated Polyimide>
[0046] The sulfonated polyimide of the present invention is well dissolved in many organic solvents such as m-cresol, 1-methylpyrrolidone (NMP), N,N-dimethylacetamide (DMAc), and dimethyl sulfoxide (DMSO).
<Formation of Sulfonated Polyimide Membrane>
[0047] The sulfonated polyimide membrane can be formed, for example, by the following method. The sulfonated polyimide is dissolved in a suitable organic solvent to afford a homogeneous solution having a concentration of 5% or less. The resulting polymer solution is cast on a glass plate and heated at 60 to 150? C. for 0.5 to 10 hours, and thus the organic solvent is evaporated. The as-cast film is peeled off from the glass plate and immersed in a suitable non-solvent, whereby the remaining cast solvent is completely removed, and finally the film is dried at room temperature or an elevated temperature up to 150? C. The resulting sulfonated polyimide membrane is in a triethylammonium salt form. Examples of the suitable organic solvent include m-cresol, 1-methylpyrrolidone (NMP), N,N-dimethylacetamide (DMAc), N,N-dimethylformamide (DMF), and dimethyl sulfoxide (DMSO). The non-solvent is a liquid in which the sulfonated polyimide is insoluble, and examples thereof include methanol, ethanol, 1-propanol, isopropanol, acetone, and ethyl acetate.
<Proton Exchange>
[0048] A sulfonated polyimide membrane in a triethylammonium salt form is converted completely into a proton form by immersing the membrane in hydrochloric acid or an aqueous sulfuric acid solution at room temperature or at an elevated temperature up to 90? C. for a sufficiently long time (usually 5 to 48 hours). The sulfonated polyimide membrane is taken out and washed thoroughly with deionized water, whereby a trace amount of the residual free acid is removed. The sulfonated polyimide membrane is dried at room temperature or an elevated temperature up to 150? C. for a certain period of time (usually 1 to 24 hours). The concentration of hydrochloric acid or a sulfuric acid solution is variable, and preferably in the range of 0.01 to 1.0 M.
<Metal Cation Exchange>
[0049] The sulfonated polyimide membrane in a proton form is immersed in an aqueous solution of a selected salt at room temperature for a sufficiently long time (typically 1 to 48 hours), whereby the sulfonated polyimide membrane is thoroughly converted into a metal cation form. The sulfonated polyimide membrane is taken out and washed thoroughly with deionized water, whereby a trace amount of the residual free salt is removed. The sulfonated polyimide membrane is dried at room temperature or an elevated temperature up to 150? C. for a certain period of time (usually 1 to 24 hours). Examples of the salt include, but are not limited thereto, LiCl, NaCl, KCl, AgNO.sub.3, MgCl.sub.2, CaCl.sub.2, BaCl.sub.2, NiCl.sub.2, ZnCl.sub.2, CuCl.sub.2, Pb(NO.sub.3).sub.2, Al(NO.sub.3).sub.3, and Fe.sub.2 (SO.sub.4).sub.3. The concentration of the aqueous salt solution is variable, and preferably in the range of 0.01 to 1.0 M.
<Shape of Gas Separation Membrane>
[0050] The gas separation membrane of the present invention is not limited in its shape at all. That is, any conceivable membrane shape such as a flat membrane shape, a cylindrical shape or a spiral element shape is employable.
<Gas Permeation Test>
[0051] A pure gas permeation test was carried out using a GTR-1 ADFE gas sorption coefficient and diffusion coefficient tester (Japan) at 35? C. in the upstream pressure range of 0.1 to 0.5 MPa. The measurement was based on the vacuum time-lag method, and the gas permeability coefficient (P) was determined from the flux in a steady state in a period of 5 to 10 times the time lag (?). The effective membrane area was 15.2 cm.sup.2.
<Gas Separation Performance>
[0052]
EXAMPLES
[0053] Hereinafter, the present invention will be described with reference to Examples, but the present invention is not limited to these Examples.
Example 1
Synthesis of 9,9-bis(4-aminophenyl) fluorene-2,7-disulfonic acid (BAPFDS)
[0054] To a 500 mL dry four-necked flask equipped with a mechanical stirrer, a nitrogen inlet and a nitrogen outlet were added 50 g of 9,9-bis(4-aminophenyl) fluorene and 200 mL of concentrated sulfuric acid. The mixture was mechanically stirred at room temperature until the solid was completely dissolved. The reaction mixture was heated at 100? C. and maintained at this temperature for 5 hours. After cooling to room temperature, the reaction mixture was poured into 2 kg of ice water. The resulting precipitate was collected by filtration, redissolved in an aqueous sodium hydroxide solution, and then filtered again to make insoluble impurities to be removed. The filtrate was acidified and the precipitate was collected by filtration, washed thoroughly with deionized water, and finally dried in vacuum at 120? C. for 10 hours, affording 66.4 g of a red brick colored solid product (yield: 91%). The .sup.1H NMR spectrum of the product BAPFDS is shown in
Example 2
Synthesis of sulfonated polyimide (SPI-1) in triethylammonium salt form
[0055] SPI-1 was synthesized by random condensation polymerization of 1,4,5,8-naphthalenetetracarboxylic dianhydride (NTDA), BAPFDS synthesized in Example 1, and 3,7-diamino-2,8-dimethyldibenzothiophene sulfone (DDBT). The molar ratio of BAPFDS to DDBT was controlled to 1:1. The detailed synthesis procedure is as follows.
[0056] To a 100 mL dry 3-necked flask equipped with a magnetic stirrer, a nitrogen inlet, a nitrogen outlet, and a condenser were added 1.016 g (2 mmol) of BAPFDS, 18 mL of m-cresol, and 0.65 mL of triethylamine under a stream of nitrogen. The mixture was stirred to completely dissolve the solid. Next, 0.5487 g (2 mmol) of DDBT, 1.073 g (4 mmol) of NTDA and 0.976 g of benzoic acid were added to the flask, and the reaction mixture was stirred at room temperature for 30 minutes, and subsequently heated at 80? C. for 4 hours and further at 180? C. for 5 hours continuously. The reaction mixture was cooled to room temperature, and then 1.032 g of isoquinoline was added. The reaction mixture was again heated at 180? C. for additional 10 hours. After cooling to room temperature, the highly viscous polymer solution was diluted with 5 mL of m-cresol and then poured into methanol. The resulting fibrous precipitate was collected by filtration, washed thoroughly with methanol, and dried in vacuo, affording a sulfonated polyimide (SPI-1) in a triethylammonium salt form. The viscosity reduction of SPI-1 is 1.26 dL/g at 31? C. when the polymer concentration in DMSO is 0.5 g/dL.
Example 3
Synthesis of sulfonated polyimide (SPI-2) in triethylammonium salt form
[0057] SPI-2 was synthesized in the same manner as in Example 2 except that the molar ratio of BAPFDS to DDBT was controlled to 1:2. The viscosity reduction of SPI-2 is 1.62 dL/g at 31? C. when the polymer concentration in DMSO is 0.5 g/dL.
Example 4
Synthesis of sulfonated polyimide (SPI-3) in triethylammonium salt form
[0058] SPI-3 was synthesized in the same manner as in Example 2 except that the molar ratio of BAPFDS to DDBT was controlled to 2:1. The viscosity reduction of SPI-3 is 1.34 dL/g at 31? C. when the polymer concentration in DMSO is 0.5 g/dL.
Example 5
Synthesis of sulfonated polyimide (SPI-4) in triethylammonium salt form
[0059] SPI-4 was synthesized in the same manner as in Example 2 except that BTFBz was used as a non-sulfonated diamine instead of DDBT and the molar ratio of BAPFDS to BTFBz was controlled to 1:1. The viscosity reduction of SPI-4 is 2.12 dL/g at 31? C. when the polymer concentration in DMSO is 0.5 g/dL.
Example 6
(Formation of Sulfonated Polyimide Membrane)
[0060] The sulfonated polyimides synthesized in Examples 2 to 5 were each dissolved in NMP, affording 5% homogeneous solutions. The resulting polymer solution was cast on a glass plate and the NMP was evaporated at 80? C. for 6 hours. The resulting cast film was peeled off from the glass plate, immersed in methanol to completely remove residual NMP, and finally dried in a vacuum oven at 120? C. for 10 hours, affording a sulfonated polyimide membrane. The resulting sulfonated polyimide membrane is in a triethylammonium salt form.
Example 7
(Proton Exchange)
[0061] Each of the sulfonated polyimide membranes in the form of a triethylammonium salt was immersed in a 0.1 M aqueous hydrochloric acid solution at room temperature for a 24 hours in total, thereby being converted completely into a proton form. Each of the membranes was taken out and washed thoroughly with deionized water, and thus a trace amount of the residual free acid was removed. The membrane was then dried at 120? C. for 10 hours.
Example 8
(Metal Cation Exchange)
[0062] Sulfonated polyimide membranes in the proton form were immersed in 0.1 M aqueous salt solutions (LiCl, NaCl, KCl, CaCl.sub.2, Al(NO.sub.3).sub.3) at room temperature for 24 hours, and the membranes were confirmed to have been converted thoroughly into a metal cation form. Each of the membranes was taken out and washed thoroughly with deionized water, and thus a trace amount of the residual free salt was removed. The membrane was then dried at 120? C. for 10 hours.
[Ft-Ir Spectrum]
[0063]
Example 9
(Gas Separation Performance)
[0064] The permeability coefficient and the selectivity of the sulfonated polyimide membranes in a proton form or a metal cation form at 35? C. and 0.1 MPa (upstream pressure) are shown in Table 1.
TABLE-US-00001 TABLE 1 Permeability coefficient Selectivity () (unit: Barrer) CO.sub.2/ CO.sub.2/ O.sub.2/ Film Cation CO.sub.2 O.sub.2 N.sub.2 CH.sub.4 N.sub.2 CH.sub.4 N.sub.2 SPI-1 Al.sup.3+ 320 46.2 7.07 9.31 45.3 34.4 6.53 Ca.sup.2+ 141 19.1 3.03 2.92 46.5 48.3 6.63 Mg.sup.2+ 96.3 15.8 2.63 2.03 36.6 47.4 6.01 K.sup.+ 136 17.1 3.62 7.08 37.6 49.5 4.72 Na.sup.+ 131 18.3 3.56 6.55 36.8 52 5.14 Li.sup.+ 100 11.9 2.23 1.78 44.8 56.2 5.34 H.sup.+ 247 37 8.10 7.00 30.5 35.3 4.57 SPI-2 Al.sup.3+ 461 74.3 14.3 12.8 32.2 36.0 5.20 Ca.sup.2+ 280 41.5 8.74 8.30 32.0 33.7 4.75 K.sup.+ 373 45.8 10.5 10.5 34.2 35.5 4.20 Li.sup.+ 188 25.8 5.58 4.46 33.7 42.2 4.62 SPI-3 Ca.sup.2+ 94.3 11.4 2.00 1.59 47.2 59.3 5.70 K.sup.+ 87.6 9.53 1.77 1.51 49.5 58.0 5.38 Na.sup.+ 86.5 11.0 1.32 1.29 65.5 67.1 8.33 SPI-4 H.sup.+ 180 28.4 5.87 5.30 30.7 34.0 4.84 1 Barrer = 10.sup.?10 cm.sup.3 (STP) cm.sup.?1 s.sup.?1 cmHg.sup.?1
Comparative Example 1
[0065] The 5-membered ring sulfonated polyimide reported by Y. K. Kim et al. has a chemical structure represented by the following general formula (2) (Y. K. Kim et al., J. Membr. Sci., 226 (2003) 145-158).
##STR00009##
[0066] The sulfonated polyimide is synthesized via random condensation polymerization of 3,3,4,4-benzophenone tetracarboxylic dianhydride, 2,2-benzidine disulfonic acid, and m-phenylenediamine. The molar ratio of m-phenylenediamine to 2,2-benzidine disulfonic acid is controlled to 9:1 and 8:2. For He/N.sub.2 and O.sub.2/N.sub.2, the separation performance of sulfonated polyimide membranes of proton type, lithium cation type, sodium cation type, and potassium cation type has been reported, and the data are shown in Table 2. To our knowledge, the document cited above is almost the only publication that reports the effect of various metal cations on the gas separation performance of sulfonated polyimide membranes. In the document, Y. K. Kim et al. report that 5-membered sulfonated polyimide membranes synthesized from 3,3,4,4-benzophenone tetracarboxylic dianhydride, 2,2-benzidine disulfonic acid, and m-phenylenediamine have considerably high selectivity for O.sub.2/N.sub.2 and He/N.sub.2 gas pairs in a proton form, but their permeability coefficients of O.sub.2 and He are very low. Furthermore, it has been reported that the selectivity was significantly reduced when the membranes were converted into a metal cation form (Li.sup.+, Na.sup.+, and K.sup.+).
TABLE-US-00002 TABLE 2 Gas permeabilities and selectivities of the M-SPI precursors at 25? C. M-SPI Permeability (Barrer.sup.a) Selectivity precursors He O.sub.2 N.sub.2 He/N.sub.2 O.sub.2/N.sub.2 H-SPI 1091 13.12 0.56 0.06 219 9.3 Li-SPI 1091 14.51 0.93 0.17 85.4 5.5 Na-SPI 1091 16.49 1.24 0.23 71.7 5.4 K-SPI 1091 18.63 1.36 0.27 69.0 5.0 Li-SPI 1082 17.20 1.22 0.49 35.1 2.5 Na-SPI 1082 19.57 1.49 0.70 27.9 2.1 K-SPI 1082 22.23 1.61 0.98 22.7 1.6 .sup.aBarrer = 1 ? 10.sup.?10 cm.sup.3 (STP) cm/cm.sup.2 s cmHg.
Note: The membrane H-SPI 1091 is a proton-type sulfonated polyimide, and the molar ratio of m-phenylenediamine to 2,2-benzidine disulfonic acid is 9:1. The membrane K-SPI 1082 is a potassium cation-type sulfonated polyimide, and the molar ratio of m-phenylenediamine to 2,2-benzidine disulfonic acid is 8:2.
[0067] The 5-membered ring sulfonated polyimide membrane in a cation form shows a very low oxygen permeability coefficient and only moderate or very low O.sub.2/N.sub.2 selectivity. H-SPI 1091 is the only one with high O.sub.2/N.sub.2 selectivity (9.3) but the oxygen permeability coefficient thereof is lowest (0.56 Barrer). Furthermore, the metal cation exchange treatment significantly reduces the selectivity. The O.sub.2/N.sub.2 separation performance of the present invention is clearly much better than that of the 5-membered sulfonated polyimide membrane reported by Y. K. Kim et al.
Comparative Example 2
[0068] Chemical structures of 6-membered ring sulfonated polyimides reported by K. Tanaka et al. (K. Tanaka et al., Polymer 47 (2006) 4370-4377) and the corresponding non-sulfonated polyimide membrane are shown below. The polyimides are synthesized from 1,4,5,8-naphthalenetetracarboxylic dianhydride (NTDA) and 2,2-bis(4-(4-aminophenoxy)-3-sulfophenyl) hexafluoropropane (BAPHFDS), and the non-sulfonated product is synthesized from NTDA and 2,2-bis(4-(4-aminophenoxy)) hexafluoropropane (BAPHF). For H.sub.2/CH.sub.4, CO.sub.2/N.sub.2, and O.sub.2/N.sub.2, the separation performance (1 atm, 35? C.) of both triethylammonium salt-type and proton-type sulfonated polyimide membranes and the corresponding non-sulfonated polyimide membrane has been reported, and the data are shown in Table 3. Data for metal cation exchange membranes are not reported.
##STR00010##
TABLE-US-00003 TABLE 3 Permeability coefficient P Selectivity (10.sup.?10 cm.sup.3 (STP) cm/(cm.sup.2 s cmHg)) P.sub.H.sub.
[0069] The membranes reported by K. Tanaka et al. show moderately high selectivity for H.sub.2/CH.sub.4, CO.sub.2/N.sub.2, and O.sub.2/N.sub.2, but show considerably low permeability coefficients of CO.sub.2 and O.sub.2, indicating much lower separation performance than the present invention.
INDUSTRIAL APPLICABILITY
[0070] The gas separation membrane of the present invention can be used as a separation membrane that allows a specific gas to permeate therethrough, separating the gas from a mixed gas.