METHOD FOR REMOVING LAYERS OF SILICON CARBIDE, AS WELL AS PROCESS AND APPARATUS FOR CLEANING EPITAXIAL REACTOR COMPONENTS

Abstract

The innovative method is for removing a silicon carbide layer from a bulk piece; the bulk piece comprises a graphite substrate underlying the silicon carbide layer; the method comprises in succession the steps of: a) submerging the bulk piece in a first solution containing nitric acid, b) submerging the bulk piece in a second solution containing hydrofluoric acid and an oxidizing agent, and typically c) submerging the bulk piece in a third solution containing preferably only or essentially deionized water until the layer detaches from the piece; this method can advantageously be used to clean components of an epitaxial reactor e.g. after their use in the reactor in silicon carbide deposition processes.

Claims

1. A method for removing a silicon carbide layer from a bulk piece, wherein said bulk piece comprises a substrate of graphite underlying the silicon carbide layer, wherein the method comprises the steps of: a) submerging said bulk piece in a first solution at a first predetermined temperature, wherein said first solution contains nitric acid at a first predetermined concentration, and keeping it submerged for a first predetermined time, then b) submerging said bulk piece in a second solution at a second predetermined temperature, wherein said second solution contains hydrofluoric acid at a second predetermined concentration and an oxidizing agent at a third predetermined concentration, and keeping it submerged for a second predetermined time.

2. The method of claim 1, wherein the method further comprises a step intended to cause the silicon carbide layer to detach from the bulk piece.

3. The method of claim 2, wherein said step is intended to cause detachment is in whole or in part overlapped with step b).

4. The method according to claim 1, wherein between step a) and step b) there is at least one intermediate step.

5. The method of claim 1, wherein step b) directly follows step a).

6. The method of claim 1, wherein the method comprises the step of: c) submerging said bulk piece in a third solution at a third predetermined temperature, wherein said third solution contains only or essentially water, in particular deionized water, and keeping it submerged at least until detachment of the silicon carbide layer from the bulk piece, wherein step c) follows step b).

7. The method of claim 1, wherein the method comprises the step of: d) subjecting said bulk piece to ultrasound after step b), at least until the silicon carbide layer detaches from the bulk piece.

8. The method according to claim 1, wherein the method comprises the steps of: e) submerging said bulk piece in a third solution at a third predetermined temperature, wherein said third solution contains only or essentially water, in particular deionized water, and subjecting said bulk piece to ultrasound while it is submerged in said third solution at least until detachment of the silicon carbide layer from the bulk piece, wherein step e) follows step b).

9. The method according to claim 1, wherein the method further comprises a washing step.

10. The method according to claim 1, wherein said oxidizing agent is an oxidizing salt, in particular chosen from potassium permanganate and potassium dichromate.

11. The method of claim 6, wherein said first predetermined temperature and/or said second predetermined temperature and/or said third predetermined temperature are chosen in a range from 10? C. to 45? C., in particular from 15? C. to 40? C.

12. The method of claim 8, wherein said first predetermined temperature and/or said second predetermined temperature and/or said third predetermined temperature are chosen in a range from 10? C. to 45? C., in particular from 15? C. to 40? C.

13. The method of claim 1, wherein said first predetermined time is greater than 3 hrs, and/or wherein said second predetermined time is greater than 3 hrs.

14. The method of claim 1, wherein said first predetermined concentration is greater than 60%, and/or wherein said second predetermined concentration is greater than 40%, and/or wherein said third predetermined concentration is a molar concentration of between 10 exp.sup.?3 and 10 exp.sup.?1.

15. A process for cleaning mechanical components of an epitaxial reactor, in particular a reactor for epitaxial deposition of silicon carbide on substrates, after their use in the reactor in deposition processes, wherein the process comprises the method of claim 1 applied to a mechanical component.

16. The process of claim 15, wherein, prior to steps a) and b) the mechanical component is treated such that the graphite substrate is at least partly exposed.

17. An apparatus for cleaning mechanical components of an epitaxial reactor, in particular a reactor for epitaxial deposition of silicon carbide on substrates, after their use in the reactor in deposition processes, wherein the apparatus is configured to implement the method of claim 1.

18. The apparatus of claim 17, comprising at least one tub and means adapted to create in said tub said first solution or then said second solution and comprising means for manipulating at least one mechanical component.

19. The apparatus of claim 18, comprising a first tub and a second tub, means adapted to create said first solution in said first tub, and means adapted to create said second solution in said second tub.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0016] This matter will become clearer from the detailed description below, to be considered in conjunction with the accompanying drawings, in which:

[0017] FIG. 1 shows an example flow chart for creating a method for removing a silicon carbide layer from a bulk piece,

[0018] FIG. 2A shows an example of a bulk piece before applying the method of FIG. 1 and FIG. 2B shows an example of a bulk piece after applying the method of FIG. 1,

[0019] FIG. 3 shows an example of creating an apparatus for cleaning mechanical components of an epitaxial reactor, and

[0020] FIGS. 4A and 4B show examples of a mechanical component to be cleaned in two distinct phases before cleaning.

[0021] It should be noted that the technical characteristics illustrated below in relation to specific examples of implementation are not to be considered limiting of the present invention, which is defined in its main aspects by the claims attached hereto.

[0022] It should also be noted that the technical characteristics illustrated below in relation to specific examples of implementation are not to be considered closely linked to each other and therefore mutually binding.

DETAILED DESCRIPTION

[0023] The innovative method works to remove a silicon carbide layer from a bulk piece; FIG. 1 shows an example flowchart 100 for implementation of the method.

[0024] As shown by way of example in FIG. 2A, a bulk piece 200 to be treated comprises a substrate 210 of graphite underlying a layer 220 of silicon carbide. In this example, the layer 220 comprises a thin (e.g. 20-200 nm=nanometers) under-layer 222 of silicon carbide and a thick (e.g. 20-200 um=micrometers) under-layer 224 of silicon carbide overlying the under-layer 222, i.e. adjacent; the sub-layer 222 derives for example from a pre-treatment of the substrate 210 and the sub-layer 224 derives for example from a plurality of spurious depositions (therefore it may be considered to comprise a plurality of overlapping, i.e., adjacent, sub-layers).

[0025] Depending on the applications, if the silicon carbide layer is formed from two or more silicon carbide sub-layers, they may be the same or different. For example, sub-layer 222 and the sub-layer 224 are different because they arise from different processes. For example, any sub-layers forming sub-layer 224 are the same because they derive from the same or, at least, similar processes, such as epitaxial deposition processes of silicon carbide on substrates made in epitaxial reactors.

[0026] The innovative method according to the example in FIG. 1 comprises the steps of: [0027] a) submerging (block 110 of diagram 100) the bulk piece 200 in a first solution at a first predetermined temperature, wherein said first solution contains nitric acid at a first predetermined concentration, and keeping it submerged for a first predetermined time, [0028] and then [0029] b) submerging (block 120 of plot 100) the bulk piece 200 in a second solution at a second predetermined temperature, wherein said second solution contains hydrofluoric acid at a second predetermined concentration and an oxidizing agent at a third predetermined concentration, and keeping it submerged for a second predetermined time.

[0030] As an experienced person in the field may understand, neither of these two steps aims to attack or corrode the silicon carbide layer, but to operate essentially on the substrate, and to cause, or at least promote, detachment of the layer from the substrate. In fact, neither nitric acid, hydrofluoric acid, nor oxidizing agent (individually or in any combination thereof) is capable of significantly attacking or corroding silicon carbide. In addition, if the goal was to attack or corrode the silicon carbide, the removal time for the layer would depend significantly on its thickness.

[0031] The first step causes a phenomenon known as intercalation that occurs essentially in graphite (nitric acid intercalates particularly well in graphite), particularly in the area of graphite that borders the silicon carbide layer. This phenomenon leads to an increase in the size of the graphite reticle and therefore the creation of tensions at the interface between graphite and silicon carbide.

[0032] Subsequently, the second step causes oxidations extended to the interface between graphite and silicon carbide that are allowed by the previous intercalation; the oxides that thus form can be attacked by hydrofluoric acid.

[0033] The Applicant tried to simplify the treatment, combining nitric acid, hydrofluoric acid and strong oxidizer (particularly potassium permanganate or potassium dichromate) in a single solution, but did not achieve the desired results. Obviously, the three compounds react with each other, in particular by altering the concentration of the individual reagents and thus altering the intercalation and/or oxidation processes.

[0034] In particular, step a) and step b) are carried out in such a way as to accentuate and exploit the phenomena described above.

[0035] Step b) may directly follow step a), i.e. without any intermediate treatment; in any case, between step a) and step b) it may also take more or less time, for example 1 second or 1 minute or 1 hour. Alternatively, between step a) and step b) there may be at least one intermediate step.

[0036] Typically, the method further comprises a step to cause the silicon carbide layer to detach, at least partially, from the bulk piece because simply dipping in the solution referred to in step b) is unlikely to cause such detachment. This phase to cause detachment could be carried out, for example, by subjecting the bulk piece to sound waves, in particular ultrasound or megasound, or by subjecting the bulk piece to a stream of bubbles, in particular of inert gases. It should not be ruled out that, according to some examples of implementation, such a phase aimed at causing detachment may be in whole or in part overlapped with phase b).

[0037] Typically and after step b), the method also comprises the step of: [0038] c) immersing (block 130 of diagram 100) the bulk piece 200 in a third solution at a third predetermined temperature, wherein said third solution preferably contains only or essentially water, in particular deionized water, until detachment (at least partial) of the layer 220 of silicon carbide from the bulk piece 200.

[0039] The result after step b) is shown, for example, in FIG. 2B, where the layer 220 is detached (in this case completely) from substrate 210.

[0040] It should not be ruled out that detachment of the layer 220 of silicon carbide may, in some cases, cause partial detachment of graphite from the substrate 210, for example small graphite fragments.

[0041] There may be alternatives to step c), such as step d) or step e) as described below, to detach the layer from the substrate.

[0042] Step d) involves, after step b), subjecting the bulk piece to ultrasound until detachment (at least partial) of the silicon carbide layer from the bulk piece.

[0043] Step e) involves, after step b), submerging the bulk piece in a third solution at a third predetermined temperature (the third solution preferably contains only or essentially water, in particular deionized water) and subjecting the bulk piece to ultrasound while submerging it in the third solution until detachment (at least partial) of the silicon carbide layer from the bulk piece.

[0044] It is worth making a clarification on the language used in the previous paragraphs. Clearly, if a solution contains only one chemical (e.g. water) it is not, strictly, a solution; the term solution was used only to facilitate the formulation of the concept. Furthermore, the term essentially contains means that the remaining content is in quantities irrelevant for the treatment.

[0045] Typically, the method further comprises a washing step. There can also be more than one wash, for example, a wash immediately after step a) and/or a wash immediately after step b) and/or a wash of the bulk piece after detachment of the silicon carbide layer.

[0046] The oxidizing agent is preferably an oxidizing salt, particularly chosen from potassium permanganate and potassium bichromate and other similar oxidizing salts. It should be noted that not all oxidizing agents conventionally used for the treatment of silicon or graphite are effective in the detachment process.

[0047] The first predetermined temperature and/or the second predetermined temperature and/or the third predetermined temperature may be chosen in the range from 10? C. to 45? C., in particular from 15? C. to 40? C. In particular, these temperatures may correspond to room temperature.

[0048] The first time, i.e. the duration of step a), is typically on the order of hours, in particular greater than 3 hours.

[0049] The second time, i.e. the duration of step b), is typically on the order of hours, in particular greater than 3 hours.

[0050] Such immersion times may depend on the size and geometry of the bulk part and the concentration of acid used.

[0051] The first predetermined concentration, i.e. nitric acid, is preferably greater than 60%.

[0052] The second predetermined concentration, i.e. hydrofluoric acid, is preferably greater than 40%.

[0053] The third predetermined concentration, i.e. oxidizing agent, is a molar concentration preferably between 10 exp?3 (=10.sup.?3) and 10 exp?1 (=10.sup.?1).

[0054] The innovative method described and claimed herein finds particularly advantageous application in the cleaning of mechanical components of an epitaxial reactor, in particular a reactor for epitaxial deposition of silicon carbide on substrates, after their use in the reactor in deposition processes.

[0055] For these applications, the bulk part is a mechanical component of an epitaxial reactor made of graphite and covered, for example, by a thin silicon carbide layer before its use in the reactor; the thickness of this thin silicon carbon layer must be less than 1 micron (or even less). This can be, for example, a part of the reactor chamber or a reactor heater or another component that can be subject to spurious depositions during epitaxial silicon carbide deposition processes; typically such spurious deposition creates a thick silicon carbide layer, which can range in thickness from several tens to hundreds of microns (and can be [as thin as] a few millimeters).

[0056] According to some such applications, a process for cleaning mechanical components of an epitaxial reactor comprises such an innovative method, but can also comprise other steps.

[0057] According to some such applications, an apparatus for cleaning mechanical components of an epitaxial reactor is configured to accomplish such an innovative method.

[0058] An example of such an apparatus is shown in FIG. 3 and referred to collectively with reference 300.

[0059] The apparatus 300 comprises a first tub 310, a second tub 320, and a third tub 330. The first tub 310 is provided with a first cavity 312 adapted to hold the first solution 314. The second tub 320 is provided with a second cavity 322 adapted to hold the second solution 324. The third tub 330 is provided with a third cavity 322 adapted to hold the third solution 324.

[0060] Apparatus 300 may comprise means (not shown in FIG. 3) for creating the specific solutions according to the innovative methods described herein. In the example of FIG. 3, there is a tub for each solution and so the first solution is created in the first tub, the second solution is created in the second tub, and the third solution is created in the third tub. Alternatively, for example, there can be only one tub; so the first solution is created in the tub, then the first treatment of the component, then the tub is emptied, then the second solution is created in the tub, then the second treatment of the component, then the tub is emptied, then the third solution is created in the tub, then the third treatment of the component, then the tub is emptied.

[0061] The apparatus 300 may further comprise means (not shown in FIG. 3) for manipulating the components to be cleaned, in particular for soaking before treatment and extracting a component into and from the solution(s) after treatment.

[0062] FIGS. 4A and 4B schematically show examples of a mechanical component 400 to be cleaned prior to a cleaning treatment. The heart 410 of such component is made of graphite and is enclosed (in this case entirely) by a silicon carbide layer 420. This is, in particular, a component of a reactor for the epitaxial deposition of silicon carbide onto substrates; the graphite of such components is polycrystalline, so it is not HOPG (=Highly Ordered Pyrolytic Graphite); the silicon carbide deposited in this type of reactor is crystalline and of type 4H or 6H or 3C and therefore also the silicon carbide layer (spurious) to be removed from the component is type 4H or 6H or 3C.

[0063] Note, particularly in FIG. 4A, that the thickness of the layer is much lower on the low, right and left sides; for example, this layer may correspond to the thin layer of native silicon carbide. Note, particularly in FIG. 4A, that the thickness of the layer is very high on the high side; for example, this top layer could correspond to the overlap of native silicon carbide and silicon carbide due to spurious depositions. FIG. 4A, indicates, by way of example, a portion of the component 400 that may correspond to the maximum piece 200 discussed above.

[0064] Considering, for example, component 400, before steps a) and b), may advantageously be treated such that at least part of the graphite substrate is exposed. FIG. 4B shows two (but it could be many more) excavations 430 and 440 passing through the silicon carbide layer 410 and reaching the graphite substrate 410; according to this example, the excavations are present at the top layer where the thickness of silicon carbide is high, i.e. where spurious depositions have occurred.

[0065] It is evident from FIG. 4B that intercalation (discussed earlier) in the graphite of component 400 is facilitated by exposure by the presence of excavations that expose the graphite itself to bath substances.

[0066] It should be noted that the method described and claimed herein can also be applied outside the microelectronic industry, wherever there is a need to remove a silicon carbide layer from a bulk piece comprising an underlying graphite substrate.

[0067] Advantageously, the silicon carbide obtained by separation due to such a method can be recycled, for example, also in areas different than the original one of the microelectronics.

[0068] Advantageously, graphite obtained by separation due to such a method may be recycled, for example, also in areas different than the original one of the microelectronics.

[0069] Such recycling proceedings are advantageous and independently claimable aspects of the subject described herein.