USE OF A LYOCELL FIBER

Abstract

The present invention relates to the use of a lyocell fiber in a product comprising a non-woven substrate and a liquid containing a compound with a quaternary ammonium salt, wherein said lyocell fiber is contained in said non-woven substrate, and wherein said lyocell fiber contains an essentially water-insoluble salt incorporated in said fiber.

Claims

1-8. (canceled)

9. A product comprising a non-woven substrate and a solution comprising a compound with a quaternary ammonium salt, wherein said non-woven substrate comprises a lyocell fiber which comprises an essentially water-insoluble salt incorporated in said fiber.

10. The product according to claim 9, wherein said essentially water-insoluble salt has a solubility in water at 15 C. to 25 C. of 5 g/l or less.

11. The product according to claim 9, wherein said essentially water-insoluble salt is selected from the group consisting of salts of alkali metals, earth alkali metals, transition metals, aluminum and mixtures thereof.

12. The product according claim 9, wherein said essentially water-insoluble salt is an organic salt.

13. The product according to claim 9, wherein said essentially water-insoluble salt is selected from the group consisting of calcium carbonate, zinc oxide, calcium phosphate, magnesium hydroxide, aluminum hydroxide, calcium oxalate, barium carbonate, organic oxalates and mixtures thereof.

14. The product according to claim 9, wherein said lyocell fiber comprises said essentially water-insoluble salt in an amount of from 0.1 wt % to 50 wt. %, based on the weight of the dry fiber.

15. The product according to claim 9, wherein said non-woven substrate comprising said lyocell fiber is a melt-blown product.

16. The product according to claim 9, wherein said non-woven substrate comprises said lyocell fiber in an amount of from 5 wt. % to 100 wt. %, based on the weight of the dry substrate.

17. The product according to claim 10, wherein said essentially water-insoluble salt has a solubility in water at 15 C. to 25 C. of 3 g/l or less.

18. The product according to claim 17, wherein said essentially water-insoluble salt has a solubility in water at 15 C. to 25 C. of 1 g/l or less.

19. The product according to claim 18, wherein said essentially water-insoluble salt has a solubility in water at 15 C. to 25 C. of less than 0.1 g/l.

20. The product according to claim 14, wherein said lyocell fiber comprises said essentially water-insoluble salt in an amount of from 1 wt. % to 10 wt. %, based on the weight of the dry fiber.

21. The product according to claim 20, wherein said lyocell fiber comprises said essentially water-insoluble salt in an amount of from 2 wt. % to 7 wt. %, based on the weight of the dry fiber.

22. The product according to claim 16, wherein said non-woven substrate comprises said lyocell fiber in an amount of from 10 wt. % to 80 wt. %, based on the weight of the dry substrate.

23. The product according to claim 22, wherein said non-woven substrate comprises said lyocell fiber in an amount of from 20 wt. % to 60 wt. %, based on the weight of the dry substrate.

24. The product according to claim 23, wherein said non-woven substrate comprises said lyocell fiber in an amount of from 20 wt. % to 30 wt. %, based on the weight of the dry substrate.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0018] The use of a lyocell fiber containing an essentially water-insoluble salt incorporated in said fiber surprisingly solves the problem of wet or moist wipes discussed above.

[0019] Especially, by way of incorporating an essentially water-insoluble salt into the lyocell fiber, it has been found that there is no need for a further treatment or addition of further materials in the stage of producing the wet or moist wipe in order to avoid the problems discussed above.

[0020] The term lyocell is the generic name allocated by BISFA (The International Bureau for the Standardization of man made fibers) for cellulose fibers which are produced by dissolving cellulose in an organic solvent without the formation of a derivative and extruding fibers from said solution by means of a dry-wet spinning process or a melt-blown process. In this regard, an organic solvent is understood to be a mixture of an organic chemical and water. At present, N-methyl-morpholine-N-oxide (NMMO) is used as an organic solvent on a commercial scale.

[0021] In said process, the solution of the cellulose is usually extruded by means of a forming tool, whereby it is moulded. Via an air gap, the moulded solution gets into a precipitation bath, where the moulded body is obtained by precipitating the solution. The molded body is washed and optionally dried after further treatment steps. A process for the production of lyocell fibers is described, for instance, in U.S. Pat. No. 4,246,221. Lyocell fibers are distinguished by a high tensile strength, a high wet-modulus and a high loop strength.

[0022] Under the term incorporated in said fiber, the skilled artisan understands that the essentially water-insoluble salt is distributed within the cellulosic matrix of the fiber essentially throughout the whole cross-section of it.

[0023] It is well-known to modify cellulosic fibers and also lyocell fibers via the incorporation of various additives.

[0024] Incorporation of a modifying compound into a lyocell fiber can be achieved, as is known per se to the skilled artisan, by admixing the compound to the spinning solution before the spinning process and/or by admixing the compound to a precursor of the solution.

[0025] As a precursor of the spinning solution, starting and intermediate materials for the manufacture of the spinning solution are to be understood, especially [0026] the starting cellulose material employed, e.g. pulp [0027] the solvent employed (aqueous tertiary amine oxide, in the following the term NMMO is used as an abbreviation for all suitable amine oxides) [0028] a mixture of the starting cellulose material with the solvent NMMO, especially a suspension of the cellulose in an aqueous NMMO, starting from which the solution can be made.

[0029] WO 2009/036481 discloses a lyocell fiber containing a material selected from the group consisting of pearl powder, ground nacre and mixtures thereof incorporated therein.

[0030] In the following, a lyocell fiber containing an essentially water-insoluble salt incorporated therein, as employed by the present invention, is referred to as the modified lyocell fiber.

[0031] Under an essentially water-insoluble salt the skilled artisan understands a salt which has a very low solubility in water so that it is not washed out in the aqueous milieu of producing lyocell fibers including their aftertreatment, or is only washed out to an extent which is acceptable in terms of the ecological and economical requirements of a commercial production.

[0032] Preferably, the salt employed in the present invention has a solubility in water at 15 C. to 25 C. of 5 g/l or less, such as 3 g/l or less, 1 g/l or less, especially preferred less than 0.1 g/l.

[0033] Preferably, the salt is soluble under acidic conditions.

[0034] Typically, the lotion containing the compound with a quaternary ammonium salt, which is applied to a non-woven substrate in order to produce a wet or moist wipe, has a pH-value of about of smaller than 7, especially of from 3 to 6, such as of from 4.0 to 5.5.

[0035] If under these acidic conditions the salt contained in the fiber is soluble, it will dissociate to a certain extent. The cation of the salt then binds to the cellulose, thus masking the anionic charges of the cellulose without the need of the addition of further additives.

[0036] As an alternative, the modified lyocell fiber, or the non-woven substrate containing the modified lyocell fiber, can be treated with an acidic medium before the treatment with the lotion containing the quaternary ammonium salts. Again by way of such treatment the anionic charges of the cellulosic fiber would be masked. This alternative would enable the use of lotions with no acidic pH-value in the production stage of the wet or moist wipe. Furthermore, more stringent treatment conditions (such as the use of stronger acids) can be applied under this alternative.

[0037] Lyocell fibers typically contain an amount of about 20 mol to 50 mol, especially 25 mol to 40 mol carboxylic, i.e. anionic groups per g of fiber. Generally spoken, therefore, the objective is to provide a modified fiber in which, upon an acidic treatment of the fiber, a sufficient amount of cations from the salt contained in the fiber will be released in order to mask these anionic charges as completely as possible.

[0038] As is readily apparent, this objective can be solved on the basis of the skilled artisan's knowledge, by appropriately selecting the parameters of [0039] the nature of the salt and, thus, both its valence and its solubility [0040] the amount of salt contained in the fiber and [0041] the nature and amount of the acidic liquid with which the fibers and/or the non-woven substrate are treated.

[0042] In a preferred embodiment of the present invention, the essentially water-insoluble salt employed may be selected from the group consisting of salts of alkali metals, earth alkali metals, transition metals, aluminum and mixtures thereof.

[0043] Further preferably, the salt is an organic salt.

[0044] Especially preferred, the salt is selected from the group consisting of calcium carbonate, zinc oxide, calcium phosphate, magnesium hydroxide, aluminum hydroxide, calcium oxalate, barium carbonate, organic oxalates and mixtures thereof.

[0045] The lyocell fiber used according to the present invention preferably contains said an organic salt in an amount of from 0.1 wt % to 50 wt. %, preferably of from 1 wt. % to 10 wt. %, especially preferred of from 2 wt. % to 7 wt. %, based on the weight of the dry fiber.

[0046] The quaternary ammonium salt employed for making the wet or moist wipe is preferably a quaternary ammonium chloride.

[0047] Especially, said quaternary ammonium salt may be selected from the group consisting of n alkylbenzyldimethylammoniumchloride (BAC or ABDAC), di-n-alkyldimethyl ammoniumchloride (DDAC), n-alkyldimethylethylbenzylammonium chloride (ADEBAC), n-alkyltrimethylammonium chloride, octyldecyldimethylammonium chloride, didecyldimethylammonium chloride, dioctyldimethylammonium chloride, benzethonium chloride and mixtures thereof.

[0048] The non-woven substrate containing the modified lyocell fiber can be manufactured by means known to the skilled artisan. In a preferred embodiment of the present invention, the non-woven substrate containing the modified lyocell fiber is a melt-blown product. The manufacture of melt-blown products from solutions of cellulose in NMMO is known, e.g. from, inter alia, WO 98/26122, WO 99/47733, WO 98/07911, U.S. Pat. No. 6,197,230, WO 99/64649, WO 05/106085, EP 1 358 369 and WO 2007/124521.

[0049] Preferably, the non-woven substrate contains the modified lyocell fiber in an amount of from 5 wt. % to 100 wt. %, preferably 10 wt. % to 50 wt. %, especially preferred 20 wt. % to 30 wt. %, based on the weight of the dry substrate.

[0050] Under a non-woven substrate containing the modified lyocell fiber in an amount of 100 wt. %, the skilled artisan understands a substrate that essentially consists of said modified lyocell fiber, such as a melt-blown non-woven product produced from a solution of cellulose in NMMO. The presence of minor amounts of additives, such as for surface treatment of the fiber and/or the non-woven substrate, is not excluded thereby.

[0051] As known per se, the non-woven substrate may contain a mixture of the modified lyocell fiber with hydrophobic fibers, such as PP fibers, PES fibers and mixtures thereof.

[0052] The present invention also relates to a product comprising a non-woven substrate and a solution containing a compound with a quaternary ammonium salt, wherein a lyocell fiber is contained in said non-woven substrate, and wherein said lyocell fiber contains an essentially water-insoluble salt incorporated in said fiber.

[0053] As to the details of the fiber employed in the product of the present invention, i.e. the wet or moist wipe, the nature of the salt and other preferred embodiments, reference may be made to the above paragraphs.

EXAMPLES

Example 1: Improvement of Release Properties of BAC by Incorporation of CaCO.SUB.3

[0054] Lyocell fibers having 1.1 wt %; 2.9 wt %; 4.1 wt %; 4.8 wt % and 6.2 wt % (based on bone-dry fiber), respectively, CaCO.sub.3 incorporated therein were produced according to the state of the art. Thus, a 13 wt % spinning dope of cellulose in aqueous NMMO was prepared containing the above-named concentrations of CaCO3. Subsequent spinning of the dope using the lyocell process led to the final fiber (1.7 dtex, 38 mm).

[0055] These air-dried fibers were mingled with 400 wt % (based on air-dried fibers) aqueous BAC-solution (alkyldimethylbenzylammonium chloride, 1000 ppm), and the release properties were determined using the titration method explained below in example 4. The aqueous BAC solution was adjusted to an acidic pH.

[0056] It becomes apparent that with increased incorporation of CaCO.sub.3 the concentration of accessible active substance increases. In table 1 the results of the titrations of the different CaCO.sub.3 fiber types are summarized.

TABLE-US-00001 TABLE 1 Evaluation of titrations of the different CaCO3 incorporated fibers. Release of Fiber type BAC [%] 1.1% CaCO.sub.3 75 2.9% CaCO.sub.3 77 4.1% CaCO.sub.3 80 4.8% CaCO.sub.3 86 6.2% CaCO.sub.3 90

Example 2: Improvement of Release Properties of BAC by Incorporation of ZnO

[0057] Lyocell fibers having 1.5 wt %; 2 wt %; 2.5 wt % and 3.0 wt % (based on bone-dry fiber), respectively, ZnO incorporated therein were produced according to the state of the art. Thus, a 13 wt % spinning dope of cellulose in aqueous NMMO was prepared containing the above-named concentrations of ZnO. Subsequent spinning of the dope using the lyocell process led to the final fiber (1.7 dtex, 38 mm).

[0058] These air-dried fibers were mingled with 400 wt % (based on air-dried fibers) aqueous BAC-solution (alkyldimethylbenzylammonium chloride, 1000 ppm), and the release properties were determined using the titration method explained below in example 4. The aqueous BAC solution was adjusted to an acidic pH.

In table 2 the results of the titrations of the different ZnO fiber types are summarized.

TABLE-US-00002 TABLE 2 Evaluation of titrations of the different ZnO incorporated fibers. Release of Fiber type BAC [%] 1.5% ZnO 85 2% ZnO 90 2.5% ZnO 90 3% ZnO 92

Example 3: At Least Twofold Increase of BAC Release Properties by Incorporation of Insoluble Salts

[0059] The fiber types mentioned in example 1 and 2 were compared with standard lyocell fibers not containing a water-insoluble salt regarding their BAC release properties.

[0060] It becomes apparent that the fiber types employed according to the present invention compared to the standard lyocell fibers show an at least twofold release of BAC.

[0061] The quaternary release was determined using the titration method described in example 4. In table 3, the results of the titrations of the different fiber types are summarized.

TABLE-US-00003 TABLE 3 Titration results of different fiber types. Release of Fiber type BAC (%) TENCEL standard 29 4.8% CaCO.sub.3 86 2% ZnO 90

Example 4: Determination of BAC Release Properties Using a 2-Phase-Titration

[0062] The cationic substance (BAC or other QACs) to be determined is titrated using sodium dodecylsulfate in a two-phase system containing water and a chlorinated solvent (dichloromethane, chloroform, . . . ) using bromophenol blue as indicator.

[0063] Cationic substances form a complex with bromophenyl blue which is soluble in the chlorinated solvent. Titration of this complex with the anionic surfactant leads to a replacement of the indicator anion and the new formed complex passes over to the aqueous phase. At the end of the titration the released indicator colors the chlorinated phase blue/violet, whereas the aqueous phase recolors yellowish/colorless.

Example 5: Fiber Data of the Fibers with Improved QAC Release Properties

[0064] The fiber data of the fiber types described in examples 1 and 2 was determined. Table 4 shows that the fiber data does not change with the incorporation of the mentioned salts.

TABLE-US-00004 TABLE 4 Fiber data Cross Incorporation section FFk FDk [%] [dtex] [cN/tex] [%] Standard lyocell 0 1.7 30.5 12 fiber 4.1% CaCO.sub.3 4.1 1.35 30.5 12.1 4.8% CaCO.sub.3 4.8 1.84 28.8 12.9 6.2% CaCO.sub.3 6.2 1.76 28 12.9 3% ZnO 3 1.82 34.2 13.4 2.5% ZnO 2.5 1.68 36.7 13 2% ZnO 2 1.84 33 13.5 1.5% ZnO 1.5 1.7 34.06 13.6 FFk: Tenacity conditioned FDk: Elongation conditioned (FDk).