COMPOSITION FOR SOLID OXIDE FUEL CELL SEALANT, SEALANT USING SAME AND METHOD FOR PREPARING SAME

Abstract

The present specification relates to a composition for a solid oxide fuel cell sealant including B.sub.2O.sub.3 in 50 mol % to 85 mol %, wherein an adhesion temperature at which viscosity becomes 10.sup.4 dPa.Math.s is in a range of 750 C. to 850 C., a sealant using the same and a method for manufacturing the same.

Claims

1. A composition for a solid oxide fuel cell sealant comprising B.sub.2O.sub.3 in 50 mol % to 85 mol %, wherein an adhesion temperature at which viscosity becomes 10.sup.4 dPa.Math.s is in a range of 750 C. to 850 C.

2. The composition for a solid oxide fuel cell sealant of claim 1, comprising a composition for a solid oxide fuel cell sealant in 60 mol % to 70 mol % based on the content of the whole composition.

3. The composition for a solid oxide fuel cell sealant of claim 1, comprising only one or more materials selected from the group consisting of the B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO, BaO and SrO as a glass-based material.

4. The composition for a solid oxide fuel cell sealant of claim 1, comprising Al.sub.2O.sub.3 in 1 mol % to 20 mol % based on the content of the whole composition.

5. The composition for a solid oxide fuel cell sealant of claim 1, comprising BaO in 10 mol % to 35 mol % based on the content of the whole composition.

6. The composition for a solid oxide fuel cell sealant of claim 1, comprising the B.sub.2O.sub.3 in 50 mol % to 70 mol %, Al.sub.2O.sub.3 in 5 mol % to 15 mol % and BaO in 15 mol % to 30 mol %.

7. The composition for a solid oxide fuel cell sealant of claim 1, comprising the B.sub.2O.sub.3 in 50 mol % to 85 mol %, Al.sub.2O.sub.3 in 1 mol % to 20 mol %, BaO in 10 mol % to 35 mol %, CaO in 0 mol % to 10 mol %, and SrO in 0 mol % to 15 mol %.

8. The composition for a solid oxide fuel cell sealant of claim 1, further comprising CaO, wherein a content of the CaO is greater than 0 mol % and less than or equal to 10 mol % based on the content of the whole composition.

9. The composition for a solid oxide fuel cell sealant of claim 1, further comprising SrO, wherein a content of the SrO is greater than 0 mol % and less than or equal to 15 mol % based on the content of the whole composition.

10. The composition for a solid oxide fuel cell sealant of claim 7, which has a value adding up the content of the BaO and the SrO in a range of 15 mol % to 35 mol %.

11. The composition for a solid oxide fuel cell sealant of claim 1, which has a coefficient of thermal expansion value in a range of 810.sup.6/K to 1010.sup.6/K.

12. The composition for a solid oxide fuel cell sealant of claim 1, which has a glass transition temperature in a range of 450 C. to 600 C. after curing.

13. The composition for a solid oxide fuel cell sealant of claim 1, which has a softening temperature in a range of 550 C. to 700 C.

14. The composition for a solid oxide fuel cell sealant of claim 1, which is formed with one or more materials selected from the group consisting of the B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO, BaO and SrO.

15. The composition for a solid oxide fuel cell sealant of claim 1, which does not include organic substances.

16. A solid oxide fuel cell sealant comprising the composition for a solid oxide fuel cell sealant of claim 1.

17. The solid oxide fuel cell sealant of claim 16, which does not include organic substances.

18. A method for manufacturing a sealant for a solid oxide fuel cell comprising: providing the composition for a solid oxide fuel cell sealant of claim 1; melting the composition for a sealant; preparing glass for a sealant by slowly cooling the melted composition for a sealant; preparing powder by crushing the glass for a sealant; preparing a product for a sealant by placing the powder in a mold and extrusion molding; and sintering the product for a sealant.

19. A solid oxide fuel cell comprising: a cell of a solid oxide fuel cell including a fuel electrode, an electrolyte and an air electrode; the solid oxide fuel cell sealant of claim 16 provided on an upper surface and a lower surface of the cell of the fuel cell; and a separator provided on an upper surface and a lower surface of the sealant.

20. A method for manufacturing a solid oxide fuel cell comprising: preparing a cell of a solid oxide fuel cell including a fuel electrode, an electrolyte and an air electrode; laminating the sealant for a solid oxide fuel cell of claim 16 on an upper surface and a lower surface of the cell of the solid oxide fuel cell; and heating a laminate laminating the sealant to each of the upper surface and the lower surface of the cell of the solid oxide fuel cell.

21. (canceled)

Description

DESCRIPTION OF DRAWINGS

[0023] FIG. 1 mimetically illustrates a structure of a solid oxide fuel cell according to one embodiment of the present specification.

[0024] FIG. 2 illustrates a structure of a sealant for a solid oxide fuel cell according to one embodiment of the present specification.

[0025] FIG. 3(a) shows a result of observing an adhesion status of a sealant manufactured using a composition for a sealant including an organic substance binder or a solvent as in preparation methods in the art, and FIG. 3(b) shows a result of observing an adhesion status of a sealant manufactured using a composition for a sealant according to one embodiment of the present specification.

[0026] FIG. 4 and FIG. 5 show a result of observing a breakage of the sealant of a sealant manufactured using a composition for a sealant according to one embodiment of the present specification and the sealant of the comparative example.

MODE FOR DISCLOSURE

[0027] Hereinafter, the present specification will be described in more detail.

[0028] In the present specification, a description of one member being placed on another member includes not only a case of the one member adjoining the another member but a case of still another member being present between the two members.

[0029] In the present specification, a description of a certain part including certain constituents means capable of further including other constituents, and does not exclude other constituents unless particularly stated on the contrary.

[0030] One embodiment of the present specification provides a composition for a solid oxide fuel cell sealant including B.sub.2O.sub.3 in 50 mol % to 85 mol %.

[0031] A biggest problem in commercializing a solid oxide fuel cell may be gas sealing. As for current sealing technologies of a solid oxide fuel cell, using a glass-based sealant may be considered as a most typical method.

[0032] As the method of using a glass-based sealant in the art, a method of using glass powder in a form of tape or paste and using each in a cell of a fuel cell has been generally used. In other words, a form of tape or paste is normally used in order to be initially attached to a cell of a fuel cell.

[0033] However, when preparing a sealant in the form of tape or paste, organic substances such as a binder or a solvent are included therein in addition to glass powder, and a separate process removing the organic substances is required in a sealant manufacturing process. In addition, even when such an organic substance-removing process is included, a gas leak occurs due to bubbles generated during the organic substance-removing process, which leads to a problem of product defects.

[0034] In view of the above, the inventors of the present disclosure have, in using a sealant for a solid oxide fuel cell, accomplished the present disclosure manufacturing a sealant using a composition for a sealant formed only with glass-based materials instead of a common tape or paste form.

[0035] According to one embodiment of the present specification, the sealing composition is formed only with glass-based materials without including organic substances when manufacturing the sealant for a solid oxide fuel cell using the M method as described above, and therefore, no bubbles caused by organic substances are generated during a manufacturing process, which is effective in improving a problem of causing product defects due to a gas leak.

[0036] In other words, according to one embodiment of the present specification, the composition for a solid oxide fuel cell sealant may not include organic substances such as a binder or a solvent, and after manufacturing a sealant using such a composition for a sealant with no organic substances, the sealant may be used in a fuel cell right away, and since no bubbles caused by organic substances are generated during a sealant manufacturing process, a problem of product defects caused by bubble generation may be resolved.

[0037] According to one embodiment of the present specification, when the composition for a solid oxide fuel cell sealant includes B.sub.2O.sub.3 in 50 mol % to 85 mol % based on the content of the whole composition, a low melting point is obtained, which is effective in obtaining excellent chemical resistance while readily controlling thermal properties of glass.

[0038] Specifically, according to one embodiment of the present specification, the composition for a solid oxide fuel cell sealant including B.sub.2O.sub.3 in 50 mol % or greater based on the content of the whole composition is effective in securing excellent chemical resistance of glass, and including B.sub.2O.sub.3 in 85 mol % or less is effective in readily controlling viscosity and thermal properties through a proper combination with other compositions.

[0039] According to one embodiment of the present specification, the composition for a solid oxide fuel cell sealant may include B.sub.2O.sub.3 in 50 mol % to 75 mol %, preferably in 55 mol % to 75 mol %, and more preferably in 60 mol % to 70 mol % based on the content of the whole composition.

[0040] In addition, according to one embodiment of the present specification, the composition for a sealant may further include a glass-based material. In addition, according to one embodiment of the present specification, the composition for a sealant may be formed only with B.sub.2O.sub.3 and a glass-based material.

[0041] In the present specification, the glass-based material does not necessarily include SiO, and may include metal oxides or nonmetal oxides. In addition, materials commonly used as a glass-based material in manufacturing a sealant of a solid oxide fuel cell may be used, and are not particularly limited.

[0042] According to one embodiment of the present specification, the composition for a sealant may include a glass-based material, and for example, the composition for a sealant may further include one or more materials selected from the group consisting of Al.sub.2O.sub.3, CaO, BaO and SrO. However, according to one embodiment of the present specification, the composition for a sealant does not include organic substances, and the organic substance may mean a solvent or a binder.

[0043] In other words, according to one embodiment of the present specification, the composition for a sealant may only include one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO, BaO and SrO as a glass-based material. Alternatively, according to one embodiment of the present specification, the composition for a sealant may only include one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, BaO and SrO as a glass-based material. Alternatively, according to one embodiment of the present specification, the composition for a sealant may only include one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO and BaO as a glass-based material. Alternatively, according to one embodiment of the present specification, the composition for a sealant may only include one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, and BaO as a glass-based material.

[0044] In addition, according to one embodiment of the present specification, the composition for a sealant may be formed only with one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO, BaO and SrO. Alternatively, according to one embodiment of the present specification, the composition for a sealant may be formed only with one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, BaO and SrO. Alternatively, according to one embodiment of the present specification, the composition for a sealant may be formed only with one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO and BaO. Alternatively, according to one embodiment of the present specification, the composition for a sealant may be formed only with one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, and BaO.

[0045] According to one embodiment of the present specification, the composition for a sealant may include Al.sub.2O.sub.3 in 1 mol % to 20 mol %, and may preferably in 5 mol % to 15 mol % based on the content of the whole composition.

[0046] According to one embodiment of the present specification, Al.sub.2O.sub.3 being 1 mol % or greater in the composition for a sealant based on the content of the whole composition is effective in obtaining excellent mechanical strength by stabilizing chemical bonding state of glass, and Al.sub.2O.sub.3 being 20 mol % or less is effective in readily producing glass.

[0047] According to one embodiment of the present specification, the composition for a sealant may include BaO in 10 mol % to 35 mol % and more preferably in 15 mol % to 30 mol % based on the content of the whole composition.

[0048] According to one embodiment of the present specification, BaO being 10 mol % or greater in the composition for a sealant based on the content of the whole composition is effective in securing excellent chemical resistance as well as controlling the same thermal properties compared to other alkaline-earth metal oxides added for controlling thermal properties, and BaO being 35 mol % or less is effective in preventing devitrification as well as readily forming glass.

[0049] According to one embodiment of the present specification, the composition for a sealant may not include SiO.sub.2. In other words, the composition for a sealant may include SiO.sub.2 in 0 mol %.

[0050] In addition, according to one embodiment of the present specification, the composition for a sealant may not include P.sub.2O.sub.5. In other words, the composition for a sealant may include P.sub.2O.sub.5 in 0 mol %.

[0051] In addition, according to one embodiment of the present specification, the composition for a sealant may further include or may not include CaO.

[0052] In addition, according to one embodiment of the present specification, the composition for a sealant may or may not include SrO.

[0053] According to one embodiment of the present specification, the composition for a sealant may include B.sub.2O.sub.3 in 50 mol % to 85 mol %, Al.sub.2O.sub.3 in 1 mol % to 20 mol %, and BaO in 10 mol % to 35 mol %.

[0054] In addition, according to one embodiment of the present specification, the composition for a sealant may include B.sub.2O.sub.3 in 50 mol % to 70 mol %, Al.sub.2O.sub.3 in 5 mol % to 15 mol %, and BaO in 15 mol % to 30 mol %.

[0055] In addition, according to one embodiment of the present specification, the composition for a sealant may include B.sub.2O.sub.3 in 60 mol % to 70 mol %, Al.sub.2O.sub.3 in 5 mol % to 15 mol %, and BaO in 15 mol % to 30 mol %.

[0056] According to one embodiment of the present specification, the composition for a sealant may include CaO in 0 mol % to 10 mol % based on the content of the whole composition.

[0057] In other words, according to one embodiment of the present specification, the CaO content in the composition for a sealant may be greater than or equal to 0 mol % and less than or equal to 10 mol % based on the content of the whole composition.

[0058] Alternatively, according to one embodiment of the present specification, the CaO content in the composition for a sealant may be greater than 0 mol % and less than or equal to 10 mol % based on the content of the whole composition.

[0059] In addition, according to one embodiment of the present specification, the composition for a sealant may include SrO in 0 mol % to 15 mol % based on the content of the whole composition.

[0060] In other words, according to one embodiment of the present specification, the SrO content in the composition for a sealant may be greater than or equal to 0 mol % and less than or equal to 15 mol % based on the content of the whole composition.

[0061] Alternatively, according to one embodiment of the present specification, the SrO content in the composition for a sealant may be greater than 0 mol % and less than or equal to 15 mol % based on the content of the whole composition.

[0062] According to one embodiment of the present specification, the composition for a sealant may include B.sub.2O.sub.3 in 50 mol % to 85 mol %, Al.sub.2O.sub.3 in 1 mol % to 20 mol %, BaO in 10 mol % to 35 mol %, CaO in 0 mol % to 10 mol %, and SrO in 0 mol % to 15 mol %.

[0063] In addition, according to one embodiment of the present specification, the value adding up the content of the BaO and the SrO in the composition for a sealant may be in a range of 15 mol % to 35 mol %. In other words, when the value adding up the content of the BaO and the SrO in the composition for a sealant according to one embodiment of the present specification is 15 mol % or greater, an effect of securing excellent chemical resistance while securing the same level of thermal property controlling property as other alkaline earth metal oxides added for thermal property control is obtained, and the value being 35 mol % or less readily forms glass and is effective in preventing devitrification.

[0064] According to one embodiment of the present specification, in the composition for a sealant, BaO may contribute to enhancing chemical resistance or devitrification property of glass. However, BaO being included in an excessively high amount may increase glass density and may have adverse influence on the environment. Meanwhile, when the BaO content is too low, the effects of BaO addition may not be properly achieved. Comparably, SrO is an alkaline earth metal oxide, and may contribute to enhancing devitrification property and acid resistance of glass. However, when SrO is included in an excessively high amount, a coefficient of thermal expansion or density may increase, and a devitrification property may go through degradation. Meanwhile, when SrO is included in an excessively low amount, the effects of SrO addition as described above may not be properly achieved.

[0065] According to one embodiment of the present specification, the composition for a sealant may have a coefficient of thermal expansion value in a range of 810.sup.6/K to 1010.sup.6/K, and preferably in a range of 910.sup.6/K to 1010.sup.6/K.

[0066] According to one embodiment of the present specification, when the composition for a sealant has a coefficient of thermal expansion in a range of 810.sup.6/K to 1210.sup.6/K, a coefficient of thermal expansion difference with a subject to adhere is small resulting in no residual stress, which is effective for stable adhesion.

[0067] In addition, according to one embodiment of the present specification, a glass transition temperature (T.sub.g) of the composition for a sealant may be in a range of 450 C. to 600 C. after curing, and more preferably in a range of 500 C. to 600 C. According to one embodiment of the present specification, when the composition for a sealant has a glass transition temperature in a range of 450 C. to 600 C., it is a temperature range lower than a solid oxide fuel cell operating temperature, and therefore, it is effective in avoiding a risk of breakage occurring usually near a glass transition temperature caused by stress.

[0068] In addition, according to one embodiment of the present specification, the composition for a sealant may have a softening temperature in a range of 550 C. to 700 C., and more preferably in a range of 600 C. to 700 C. According to one embodiment of the present specification, when the composition for a sealant has a softening temperature in a range of 550 C. to 700 C., it is a temperature and viscosity region readily exhibiting effects by additional additives such as a filler while having minimum viscosity for adhesion, which is effective in readily responding to technical problems near a solid oxide fuel cell operating temperature.

[0069] In the present specification, the softening temperature means a temperature at which a material starts to deform or soften by heating, and is measured using a dilatometer apparatus while observing changes obtained by thermal expansion measurement.

[0070] According to one embodiment of the present specification, the composition for a sealant may have an adhesion temperature in a range of 750 C. to 850 C., and more preferably in a range of 800 C. to 850 C.

[0071] In the present specification, the adhesion temperature means a temperature at which a sealant adheres to an upper surface and a lower surface of the cell of the fuel cell during a sealing process of the solid oxide fuel cell afterword. Specifically, the adhesion temperature refers to a temperature at which viscosity of the composition for a sealant according to one embodiment of the present specification becomes 10.sup.4 dPa.Math.s.

[0072] One embodiment of the present specification provides a solid oxide fuel cell sealant including the composition for a solid oxide fuel cell sealant described above.

[0073] In other words, according to one embodiment of the present specification, the sealant may be manufactured using a composition for a sealant not including organic substances, and the sealant itself also does not include organic substances such as a solvent or a binder.

[0074] One embodiment of the present specification provides a method for manufacturing a sealant for a solid oxide fuel cell including providing the composition for a solid oxide fuel cell sealant described above; melting the composition for a sealant; preparing glass for a sealant by slowly cooling the melted composition for a sealant; preparing powder by crushing the glass for a sealant; preparing a product for a sealant by placing the powder in a mold and extrusion molding; and sintering the product for a sealant.

[0075] In the present specification, as for the composition for a solid oxide fuel cell, the descriptions provided above may all be identically applied.

[0076] In other words, according to one embodiment of the present specification, the composition for a solid oxide fuel cell may be formed with one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO, BaO and SrO, and may not include organic substances such as a solvent or a binder.

[0077] Specifically, according to one embodiment of the present specification, the providing of the composition for a solid oxide fuel cell sealant may provide the composition for a solid oxide fuel cell sealant by preparing the glass-based material such as B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO, BaO and SrO described above in a proper content, and mixing them without using organic substances.

[0078] In addition, according to one embodiment of the present specification, the melting of the composition for a sealant may include heating the glass-based material such as B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO, BaO and SrO described above until it has a liquid form, and may be carried out by increasing the temperature from room temperature to a range of 1200 C. to 1400 C.

[0079] According to one embodiment of the present specification, in the preparing of glass for a sealant by slowly cooling the melted composition for a sealant, the slow cooling may include, in a heat treatment process, a process of slowly cooling at a high temperature, or a process of reheating to a certain temperature and slowly cooling.

[0080] In addition, one embodiment of the present specification may include, after preparing glass for a sealant by slowly cooling the melted composition for a sealant, preparing powder by crushing the glass for a sealant again, and by placing the powder prepared as above in a mold and extrusion molding, a product for a sealant in a desired shape may be obtained without requiring a separate process of preparing to a tape or paste form.

[0081] In other words, according to one embodiment of the present specification, the product for a sealant may be formed with one or more materials selected from the group consisting of B.sub.2O.sub.3, Al.sub.2O.sub.3, CaO, BaO and SrO, and may not include organic substances such as a solvent or a binder.

[0082] In addition, according to one embodiment of the present specification, a product for a sealant having a desired structure may be prepared depending on the shape of a mold placing the powder, and a sealant having a ring shape may be prepared by employing a shape inside a mold as a ring shape.

[0083] In other words, the shape inside a mold may be made or prepared so as to correspond to a shape of a sealant to prepare, and although the structure is preferably a ring shape generally, the shape is not particularly limited.

[0084] In addition, according to one embodiment of the present specification, the material placed inside a mold is formed only with a glass-based material as described above and does not include organic substances such as a solvent and/or a binder, and therefore, there is an advantage in that a separate organic substance preparation process is not required.

[0085] According to one embodiment of the present specification, the sintering of the composition for a sealant may be carried out at a temperature range of higher than or equal to the softening temperature described above and lower than or equal to the softening temperature+30 C. Carrying out the sintering at a temperature higher than or equal to the softening temperature is effective in manufacturing a sealant denser than a pore structure, and carrying out the sintering at a temperature lower than or equal to the softening temperature+30 C. is effective in preventing sealant shape collapse occurring during a sintering process, a problem of adhesion with a support, or defects of breakage caused by cooling after adhesion.

[0086] According to one embodiment of the present specification, a sealant having excellent chemical durability and/or long-term durability may be manufactured through the sintering of the composition for a sealant.

[0087] One embodiment of the present specification provides a solid oxide fuel cell including a cell of a solid oxide fuel cell including a fuel electrode, an electrolyte and an air electrode; the solid oxide fuel cell sealant described above provided on an upper surface and a lower surface of the cell of the fuel cell; and a separator provided on an upper surface and a lower surface of the sealant.

[0088] A fuel cell formed with an electrolyte, an air electrode and a fuel electrode is referred to as a cell of a fuel cell (unit cell), and since the amount of electric energy produced by one unit cell is very limited, a laminated structure (stack) having a form of connecting unit cells in series is manufactured in order to use a fuel cell in power generation. In order to form a stack, an air electrode and a fuel electrode of each unit cell are electrically connected, and a separator is used to prevent mixing of fuel and air. Such a solid oxide fuel cell structure is mimetically illustrated in FIG. 1.

[0089] In forming a laminated structure using the separator, a sealant is installed to prevent mixing of hydrogen gas, a fuel, and air, to prevent a gas leak and for insulation between cells. A solid oxide fuel cell may be divided into a flat plate-type, a cylinder-type, a laminate-type and the like, and although the shape is not particularly limited in the present specification, sealing between constituents and a separator is particularly important in a flat plate-type fuel cell.

[0090] In the present specification, as for descriptions on the fuel electrode, the electrolyte and the air electrode, descriptions generally used in the art may be used in the same manner.

[0091] In the present specification, as for descriptions on the solid oxide fuel cell, descriptions generally used in the art may be used in the same manner.

[0092] One embodiment of the present specification provides a method for manufacturing a solid oxide fuel cell including preparing a cell of a solid oxide fuel cell including a fuel electrode, an electrolyte and an air electrode; laminating the sealant for a solid oxide fuel cell described above on an upper surface and a lower surface of the cell of the solid oxide fuel cell; and heating a laminate laminating the sealant to each of the upper surface and the lower surface of the cell of the solid oxide fuel cell.

[0093] According to one embodiment of the present specification, the heating is preferably carried out in a range of 750 C. to 850 C. In order to have an adhesive property, the sealant for a solid oxide fuel cell according to one embodiment of the present specification forms proper viscosity through the heating of a laminate resulting in wetting at the upper surface and the lower surface of the cell of the fuel cell, and by behaving in a similar manner as a solid after cooling the same, sealing of the solid oxide fuel cell may be accomplished.

[0094] Hereinafter, the present specification will be described in detail with reference to examples in order to specifically describe the present specification. However, the examples M according to the present specification may be modified to various different forms, and the scope of the present specification is not construed as being limited to the examples described below. The examples of the present specification are provided in order to more fully describe the present specification for those having average knowledge in the art.

<Example> Examples 1 to 6

[0095] Manufacture of Sealant

[0096] Raw materials of each component were combined so as to have compositions (based on mol %) listed in the following Table 1, and the result was melted through heating for 5 hours at a temperature of 1200 C. using a platinum crucible. During the melting, a platinum stirrer was inserted, and the result was stirred for 1 hour to homogenize glass. Subsequently, the melted glass was slowly cooled at 600 C. to obtain glass of each example. Meanwhile, the obtained glass was crushed, and then the particles were sorted by sizes of 10 m to 20 m level and selectively used. The result was extrusion molded to have a shape in which only a cell shape edge is present using a press method, then heated to a temperature higher than a softening point of each composition by 30 C., and maintained for 30 minutes to manufacture a sealant. A shape of a final sealant manufactured as above is illustrated in FIG. 2.

Comparative Example

[0097] A sealant was manufactured in the same manner as in the example except that raw materials of each component were combined so as to have a composition (based on mol %) listed in the comparative example of the following Table 1.

[0098] Manufacture of Fuel Cell

[0099] 1. Slurry Preparation

[0100] Solid electrolyte slurry was prepared by mixing an electrolyte with a dispersant, a plasticizer and an acryl-based binder. In addition, negative electrode support layer slurry was prepared by mixing an electrolyte with NiO, a pore forming agent, a dispersant, a plasticizer and an acryl-based binder.

[0101] 2. Tape Preparation and Lamination

[0102] The prepared slurry was coated on a doctor blade to prepare a solid electrolyte layer, a negative electrode functional layer, and a negative electrode support layer tape. Each tape was laminated to prepare a laminate for a solid oxide fuel cell (SOFC).

[0103] 3. Sintering

[0104] The laminate for a solid oxide fuel cell was sintered in a range of 1000 C. to 1600 C. to form an electrolyte and a fuel electrode.

[0105] 4. Air Electrode Preparation

[0106] An air electrode material and ESL441 as a binder were prepared into a paste using a 3 roll mill. The air electrode composition paste was coated using a screen printing method and dried to form an air electrode, and then the result was sintered to prepare a cell.

[0107] 5. Sealing and Driving

[0108] After placing a sealant between a separating material and the prepared cell, the result was heated to a sealing temperature and then cooled to a temperature to operate.

<Experimental Example 1> Measurement of Thermal Expansion Coefficient

[0109] For the glass of each of the examples, an average thermal expansion coefficient (CTE) was measured using a dilatometer.

<Experimental Example 2> Measurement of Adhesion Temperature

[0110] For the glass of each of the examples, viscosity was measured using a high temperature viscometer, and a temperature T4 at which the viscosity became 10.sup.4 dPa.Math.s was measured.

[0111] Experimental results evaluating specific compositions of the compositions for a sealant according to Examples 1 to 6 of the present specification, and properties of the compositions are shown in the following Table 1.

TABLE-US-00001 TABLE 1 B.sub.2O.sub.3 Al.sub.2O.sub.3 CaO BaO SrO Total T4 CTE Example 70 15 15 100 816 12 1 Example 60 12.5 7.5 20 100 808 11.6 2 Example 60 12.5 27.5 100 808 11.2 3 Example 60 10 30 100 826 10.4 4 Example 60 7.5 2.5 30 100 840 10.8 5 Example 60 5 5 15 15 100 820 11.8 6 Comparative 64 10 4 6 16 100 920 8.8 Example * T4: Adhesion temperature (temperature at which viscosity became 10.sup.4 dPa .Math. s) [unit: C.] * CTE: Thermal expansion coefficient [unit: 10.sup.6/K]

Experimental Example 3

[0112] Performance of each of the fuel cells was measured using an existing sealant including an organic substance binder or a solvent and the sealant of the present disclosure, and adhesion statuses of the sealants were observed. Observation results are shown in FIG. 3.

[0113] Specifically, FIG. 3(a) shows a result of observing an adhesion status of the sealant manufactured using the composition for a sealant including an organic substance binder or a solvent as in preparation methods in the art, and (b) shows a result of observing an adhesion status of the sealant manufactured using the composition for a sealant according to one embodiment of the present specification. As shown in FIG. 3, it was seen that contact failure of the sealant caused by bubble generation was identified in FIG. 3(a), and a problem of bubble generation did not occur in FIG. 3(b).

Experimental Example 4

[0114] Breakage of the sealant of the example and the sealant of the comparative example was observed. The results are shown in FIGS. 4 and 5. It was seen that, when referring to FIG. 4, breakage was discovered in the sealant of the comparative example, and when referring to FIG. 5, there was a difference in that no breakage was discovered in the sealant of the example.

<Experimental Example 5> Measurement of Cell Performance

[0115] As for cell performance of the example and the comparative example, performance was measured by flowing 2000 cc of air to an air electrode per the cell of the fuel cell at 600 C., and flowing 500 cc of hydrogen to a fuel electrode through current sweep using a Potentiostat, and the results are shown in Table 2.

TABLE-US-00002 TABLE 2 OCV (V) OPD (mW @0.5 A) Comparative 0.700 140 Example Example 0.900 380 * OCV: Open-circuit voltage * OPD: Operation power density (0.5 A, 600 C.)