PLASTIC MOLDED BODY

Abstract

A plastic molded body has a surface including a non-fluororesin and a rough surface formed on the surface, in which a fluorine atom is incorporated into the molecular chain of a non-fluororesin forming the rough surface. The molded body maintains excellent liquid repellency for a long period of time and exhibits the same levels of drainage and liquid drop-off properties as the initial levels even when it is brought into contact with a liquid repeatedly.

Claims

1. A plastic molded body having a surface comprising a non-fluororesin and a rough surface formed on the surface, wherein a fluorine atom is incorporated into the molecular chain of a non-fluororesin forming the rough surface.

2. The plastic molded body according to claim 1, wherein the rough surface has a primary irregular surface and a secondary irregular surface which is finer than the primary irregular surface and formed within the primary irregular surface, and the fluorine atom is incorporated into the molecular chain of a non-fluororesin forming the secondary irregular surface.

3. The plastic molded body according to claim 2, wherein a much finer tertiary irregular surface is formed within the secondary irregular surface, and the fluorine atom is incorporated into the molecular chain of a non-fluororesin forming the tertiary irregular surface.

4. The plastic molded body according to claim 1, wherein when a droplet is dropped on the rough surface, an area ratio s represented by the projection area of a solid-liquid interface per unit area is 0.05 to 0.8.

5. The plastic molded body according to claim 4, wherein the rough surface has a rectangular irregular structure.

6. The plastic molded body according to claim 1, wherein when an arithmetic average roughness corresponding to an amplitude of the irregular structure forming the rough surface is represented by Ra and an average length of a pitch (R.sub.0) of the irregular structure is represented by RSm, the rough surface satisfies Ra/RSm5010.sup.3.

7. The plastic molded body according to claim 1 which is a package material used to contain a liquid substance.

8. The plastic molded body according to claim 7, wherein the package material has the form of a bottle, cap or spout, and the rough surface is formed on a part in contact with a liquid substance.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0037] FIG. 1 is a diagram showing the form of a liquid repellent rough surface formed in the plastic molded body of the present invention;

[0038] FIG. 2 is schematic diagrams of droplet contact patterns on the rough surface expressed by a Cassie-Baxter model and a Wenzel model;

[0039] FIG. 3 is an enlarged view of the form of the most preferred rough surface formed in the plastic molded body of the present invention;

[0040] FIG. 4 is a side sectional view of a package (a combination of a bottle and a cap) as an example of the plastic molded body of the present invention;

[0041] FIG. 5 is a side sectional view of a hinge cap which is another example of the plastic molded body of the present invention;

[0042] FIG. 6 is a plan view of the hinge cap shown in FIG. 5;

[0043] FIG. 7 is a diagram showing a method of a fluorine plasma etching treatment; and

[0044] FIG. 8 is a diagram showing the form of a rough surface formed in the present invention.

BEST MODE FOR CARRYING OUT THE INVENTION

[0045] In FIG. 1 which shows the form of a rough surface formed on the surface of the plastic molded body of the present invention, this surface is formed from a non-fluororesin, a rough surface 100 having fine irregularities is formed on this surface (in FIG. 1, the top of each convex portion of the rough surface 100 is represented by S), and a fluorine atom is incorporated into the molecular chain of the non-fluororesin forming this rough surface 100 by post-processing. For example, when the molecular chain of the non-fluororesin is represented by (CH.sub.2)n-, the fluorine atom is incorporated into part of this molecular chain to form a fluorine-containing part such as CHF, CF.sub.2 or CF.sub.3. The post-processing for incorporating the fluorine atom is carried out by fluorine plasma etching which will be described hereinafter.

[0046] The liquid repellency of a liquid on the above rough surface 100 will be described with reference to FIG. 2.

[0047] That is, in FIG. 2 which shows droplet contact patterns on the above rough surface 100, in a Cassie mode in which a droplet is situated on the rough surface 100, concave portions in the rough surface 100 become air pockets, and the droplet comes into composite contact with a solid and a gas (air). That is, in this composite contact, the radius R at the contact interface of the droplet is small and the liquid comes into contact with air having highest hydrophobicity, thereby developing high water repellency.

[0048] The theoretical formula (1) of the contact angle of the rough surface 100 in the Cassie mode is given below.

[00001]$\begin{array}{cc}\begin{array}{c}\cos .Math..Math.{}^{*}=.Math.\left(1-{}_s\right).Math.\cos .Math..Math.+{}_s.Math.\cos .Math..Math.{}_E\\ =.Math.{}_s-1+{}_s.Math.\cos .Math..Math.{}_E\end{array}& \left(1\right)\end{array}$

[0049] .sub.E: contact angle

[0050] *: apparent contact angle

[0051] .sub.s: area ratio (projection area of solid-liquid interface per unit area)

[0052] As understood from this theoretical formula, as .sub.s becomes smaller, the apparent contact angle * becomes closer to 180 to exhibit super liquid repellency.

[0053] Meanwhile, when a droplet enters concave portions in a rough surface 1a, the droplet is not in composite contact but in contact only with a solid, which is represented by a Wenzel mode. In this Wenzel mode, the contact radius R at the contact interface of the droplet is large, and the theoretical formula (2) of the contact angle of the irregular surface is given below.

cos *=rcos.sub.E (2)

[0054] .sub.E: contact angle

[0055] *: apparent contact angle

[0056] R: irregularity degree (actual contact area/projection area of droplet)

[0057] As understood from this theoretical formula, as r becomes larger, the apparent contact angle * becomes closer to 180 to exhibit super liquid repellency.

[0058] Although it is known that liquid repellency is improved in both the Wenzel mode and the Cassie mode as described above, to improve drop-off properties and repeated drop-off properties, not the Wenzel mode but the Cassie mode is maintained stably. That is, the inventors of the present invention think that it is necessary to maintain the air pockets in the concave portions stably. That is, the interface between a liquid phase and a solid phase is large in the Wenzel mode with the result that physical adsorption force applied to the interface is large, whereby the contact angle is large to repel a liquid but a droplet does not easily drop off. It is considered that since the interface is small in the Cassie mode, an energy barrier which must be overcome when a droplet drops off is so low that the droplet drops off easily and repeatedly.

[0059] In the present invention, liquid repellency is chemically provided by incorporating a fluorine atom into the molecular chain of the non-fluororesin forming the rough surface 100 in order to effectively keep the contact of a droplet in the above Cassie mode. That is, when the liquid enters the concave portions in the rough surface 100, the contact pattern of the droplet becomes the Wenzel mode with the result that super liquid repellency in the Cassie mode is impaired. In the present invention, since liquid repellency is chemically provided to this rough surface la by incorporating a fluorine atom into the molecular chain, the entry of the liquid into the concave portions is effectively suppressed, thereby maintaining super liquid repellency in the Cassie mode stably.

[0060] In addition, in the present invention, in at least part of the rough surface 100, for example, the tops of the convex portions or the bottoms of the concave portions, a fluorine atom for developing chemical liquid repellency is incorporated into the molecular chain of the non-fluororesin forming this surface. Therefore, even when the liquid comes into contact with this rough surface 100 repeatedly, the fluorine atom is not removed and chemical liquid repellency is maintained stably with the result that super liquid repellency in the Cassie mode is not degraded and is maintained at the same high level as the initial level. Making use of this, excellent drainability (dripping prevention) and liquid drop-off properties (liquid dischargibility) can be maintained for a long period of time.

[0061] Further, since a film containing a fluorine atom is not formed but a fluorine atom is incorporated into the molecular chain of the non-fluororesin of the surface, the control of film thickness is not necessary and there are no variations in liquid repellency according to film thickness.

[0062] As for the irregularity degree of the above rough surface 100, to fully develop liquid repellency in the Cassie mode, the area ratio .sub.s represented by the area of the top S of the convex portion per unit area in the rough surface 100 is not less than 0.05, preferably not less than 0.08 and not more than 0.8, particularly preferably not more than 0.5 from the viewpoints of moldability and mechanical strength. For example, when a droplet is dropped on the rough surface 100, the area ratio .sub.s represented by the projection area of a solid-liquid interface per unit area is preferably 0.05 to 0.8, more preferably 0.08 to 0.5 so that the Cassie mode is preferably maintained stably.

[0063] The depth d in the rough surface 100 is preferably 5 to 200 m, particularly preferably 10 to 50 m.

[0064] The rough surface 100 may have an irregular structure shown in FIG. 8.

[0065] That is, a droplet is supported by a Laplace pressure (p) represented by the irregular point angle and the pitch R.sub.0 of irregularities according to the formula (3) to form an air pocket. That is, when the irregular point angle becomes small, the pitch R.sub.0 becomes small and the irregular structure becomes like a frog, the Laplace pressure becomes so large that a droplet hardly enter irregularities, thereby developing liquid repellency.

[0066] Therefore, as understood from FIG. 8, when the arithmetic average roughness Ra representing the amplitude of the irregular structure is large and the average length RSm corresponding to the pitch R.sub.0 is small, the Laplace pressure becomes large, thereby developing liquid repellency. Therefore, Ra/RSm is preferably not less than 5010.sup.3, particularly preferably not less than 20010.sup.3.

p=cos (-)/(R.sub.0+hcos) (3)

[0067] In the present invention, the rough surface 100 which has the above fine irregularities can be easily formed by a transfer method using a metal stamper. That is, a stamper having a rough surface part corresponding to the above fine irregularities obtained by a resist method is heated at a suitable temperature and pressed against a predetermined part of the surface of a plastic molded body to transfer the rough surface part, thereby making it possible to form the above rough surface 100 on the surface of the plastic molded body. Therefore, the irregular surface of the stamper is formed on the surface 1 of the plastic molded body in such a manner that the irregularities are reversed.

[0068] In FIG. 1, the concave and convex shapes of the rough surface 100 are not particularly limited but concave portions and convex portions are preferably formed rectangular as shown in FIG. 1 so as to form air pockets stably. For example, when the concave portions are V-shaped, droplets easily enter the concave portions.

[0069] Further, incorporation into the molecular chain of the non-fluororesin forming the surface is carried out by etching using fluorine plasma.

[0070] This fluorine plasma etching may be carried out by a method known per se. For example, a CF.sub.4 gas or SiF.sub.4 gas is used, the surface of a plastic molded body on which the rough surface 100 is to be formed is arranged between a pair of electrodes, and a high-frequency electric field is applied to produce fluorine atom plasma (atomic fluorine) which is then collided with apart for forming the rough surface 100, whereby the fluorine atom is incorporated into the molecular chain of the non-fluororesin forming the surface (rough surface 1a). That is, the resin of the surface is gasified or decomposed and the fluorine atom is incorporated at the same time.

[0071] Therefore, super fine irregularities are formed by etching in an area where the fluorine atom is incorporated. The arithmetic average roughness Ra of the super fine irregularities is generally not more than 100 nm and Ra/RSm 510.sup.3.

[0072] Conditions such as the high-frequency voltage to be applied and the etching time are set to suitable ranges according to the roughness (area ratio .sub.s) of the rough surface 100. For example, in a liquid repellent durability test which is carried out in Examples to be described hereinafter, when the contact angle is measured after a droplet (sauce) is dropped 100 times, a contact angle which is not less than 90% of the initial contact angle should be obtained. The conditions under which this contact angle is obtained should be set by a preliminary laboratory test. Depending on the roughness of the rough surface 100, in general, when the element ratio (F/C) of a fluorine atom and a carbon atom per unit area is not less than 40%, specifically 50 to 300%, stable super high liquid repellency like the above liquid repellency can be secured without impairing surface strength. The element ratio can be calculated by analyzing the elemental composition of the surface with an X-ray photoelectron spectroscope.

[0073] In the above-described present invention, the rough surface 100 is not limited to those shown in FIG. 1 and FIG. 8 and is preferably formed with a fractal hierarchical structure.

[0074] For example, as shown in FIG. 3, it is preferred that secondary fine irregularities 165 should be formed on the primary irregularities 160 consisting of relatively large convex portions 160a and concave portions 160b. That is, since a droplet 170 is mounted on the secondary irregularities 165, air pockets (secondary air pockets) are formed between the droplet 170 and the secondary irregularities 165. That is, the secondary air pockets between the droplet 170 and the secondary irregularities 165 prevent entry into the concave portions 160b of the primary irregularities 160, thereby making it possible to prevent the elimination of the air pockets formed between the primary irregularities 160 and the droplet 170 more effectively, to keep the Cassie mode state more stably and to maintain drop-off properties and drainability (dripping prevention properties) more stably.

[0075] On the rough surface 100 having this hierarchical structure, the secondary irregularities 165 on the surface of the primary irregularities 160 should have a surface roughness that ensures the formation of the secondary air pockets which prevent a droplet on the secondary irregularities 165 from entering the concave portions 160b of the primary irregularities 160. For example, the ratio Ra/RSm of the arithmetic average roughness and the average length is preferably not less than 5010.sup.3, particularly preferably not less than 20010.sup.3.

[0076] The above primary irregularities 160 should have the same area ratio and the same depth d of the irregularities as those of the rough surface 100 shown in FIG. 1, thereby fully developing liquid repellency in the Cassie mode.

[0077] Although the second irregularities 165 are most preferably formed on the entire surface of the primary irregularities 160 from the viewpoint of preventing the droplet 170 from entering the concave portions 160b of the primary irregularities 160 more effectively, they should be formed at the upper ends of at least the convex portions 160a of the primary irregularities 160.

[0078] The rough surface 100 having the above hierarchical structure can be formed by forming a fine secondary irregular surface on the irregular surface of a stamper for forming primary irregularities by blasting and transferring the fine secondary irregular surface by using the stamper.

[0079] In the present invention, in at least part of an area on the primary irregularities 160 on which the secondary irregularities 165 have been formed as described above, specifically, portions which become the tops of the convex portions 160a of the primary irregularities 160 and portions which become the bottom portions of the concave portions 160b, a fluorine atom is incorporated into the molecular chain of the non-fluororesin forming the surface by fluorine plasma etching. In that area, tertiary irregularities which are finer than the secondary irregularities are formed by etching at the time of incorporating the fluorine atom. The arithmetic average roughness Ra of the tertiary irregularities is not more than 100 nm like the super fine irregularities formed by the above-described etching and Ra/RSm 510.sup.3.

[0080] In the above-described present invention, although the surface of this plastic molded body is formed by using the non-fluororesin, as this non-fluororesin, that is, a resin containing no fluorine, any thermoplastic resin, thermosetting resin or photocurable resin may be used as long as the rough surface 100 having the above irregularities can be formed and the fluorine atom can be incorporated into the molecular chain by fluorine plasma etching. A suitable resin may be selected according to the purpose of this molded body and may have a multi-layer structure.

[0081] In general, in the package field, olefin-based resins typified by polyethylene, polypropylene and a copolymer of ethylene or propylene and another olefin, and polyesters such as polyethylene terephthalate (PET), polyethylene isophthalate and polyethylene naphthalate are typical resins for forming the surface.

[0082] The plastic molded body of the present invention may be various in form, making use of the long service life and excellent liquid repellency of the above-described rough surface 100 and can be effectively used as a package for containing drinks, seasoning liquids and drug liquids due to excellent drainability.

[0083] In FIG. 4 which shows a preferred example of the package, this package includes a plastic bottle having a mouth portion 1 and a cap (screw cap) 3 attached to the mouth portion 1, and a liquid is contained in the plastic bottle.

[0084] In this package, although not shown in this plastic bottle, the lower part of the mouth portion 1 is connected to a curved shoulder portion connected to a barrel portion whose lower end is closed by a bottom portion.

[0085] In this plastic bottle, a screw thread 5 for holding the cap 3 is formed on the outer surface, an annular projection 7 is formed below the screw thread 5, and a support ring 9 for holding the bottle at the time of transport is formed below the annular projection 7.

[0086] Meanwhile, the cap 3 has a top panel portion 10 and a cylindrical side wall 11 extending downward from the periphery of the top panel portion 10, a sealing liner 13 is formed on the inner surface (especially a peripheral portion) of the top panel portion 10, and a screw thread 15 to be mated with the screw thread 5 of the mouth portion 1 of the bottle is formed on the inner surface of the cylindrical side wall 11.

[0087] That is, the cap 3 is attached to the mouth portion 1 by screw mating, and the upper part of the mouth portion 1 comes into close contact with the liner 13 when the cap 3 is attached, thereby sealing the inside of the bottle.

[0088] To ensure this sealing, the liner 13 has a relatively long inner ring 13a and a relatively short outer ring 13b, the upper end part of the mouth portion 1 enters a space between them, and the inner side face, the upper end face and the outer side face of this upper end part come into close contact with the liner 13 to ensure sealability.

[0089] Not shown in FIG. 4, a tamper evident band (TE band) is generally formed at the lower end of the cylindrical side wall 11 of the cap 3 through a breakable weakened line and removed from the cap 3 when the cap 3 is removed from the mouth portion 1 by opening the bottle, thereby clearly showing the opening record of the cap 3 to a general consumer and preventing wrongful use such as a prank.

[0090] In the above package, after the cap 3 is removed from the mouth portion 1 of the bottle, a liquid contained in the bottle is poured out from the mouth portion 1 by inclining the bottle. As understood from this, the spout of the package to which the cap 3 (threaded cap) is attached is the upper end face X of the mouth portion 1 of the bottle.

[0091] That is, when the plastic molded body of the present invention is applied to this plastic bottle, the above-described irregular surface 100 is formed on the upper end face (may be simply referred to as spout hereinafter) X of the mouth portion 1 of the bottle.

[0092] Further, although the mouth portion 1 of the bottle is the spout X in the above-described example, the plastic molded body of the present invention may be applied to a cap.

[0093] In FIG. 5 and FIG. 6, this hinge cap (50 in these figures) is used by attaching to the mouth portion 1 of the same plastic bottle as the package shown in FIG. 4. In the example of FIG. 4, the cap is referred to as screw cap which is attached to the mouth portion 1 by screw mating whereas the cap employed in this example is referred to as hinge cap.

[0094] That is, the cap 50 includes a cap body 51 which is fixed by fitting onto the mouth portion 1 of the bottle and a hinge lid 55 which is hinge connected to the cap body 51 through a hinge band 53.

[0095] The cap body 51 includes a top panel 61 and a cylindrical side wall 63 extending downward from the periphery of the top panel 61, and an annular projection 65 extending downward is formed on the inner surface of the top panel 61 with a space between it and the cylindrical side wall 63. That is, the upper part of the bottle mouth portion 1 is fitted in the space between the cylindrical side wall 63 and the annular projection 65 by plugging, whereby the cap body 51 is firmly fixed to the bottle mouth portion 1.

[0096] An opening 67 which is a flow channel at the time of pouring out a content liquid is formed in the center part of the top panel 61, and a spouting cylinder 69 is formed upright around the opening 67 on the top surface of the top panel 61.

[0097] In general, this opening 67 is closed before it is sold and used after the package is produced, and the wall of this part is peeled off to form the opening 67 when a general consumer pours out the content liquid from the bottle for the first time.

[0098] Meanwhile, the hinge lid 55 includes a top panel portion 71 and a skirt portion 73 extending from the periphery of the top panel portion 71, and the end part of the skirt portion 73 is connected to the hinge band 53 which is connected to the upper end of the cylindrical side wall 63 of the cap body 51. The hinge lid 55 is opened and closed by turning with the hinge band 53 as a fulcrum point.

[0099] A seal ring 75 is formed on the inner wall (top wall in FIG. 6) of the top panel portion 71 of the hinge lid 55, and a sealing flange 77 is formed at an end part on a side opposite to the hinge band 53 of the top panel portion 71.

[0100] That is, when the hinge lid 55 is closed, the outer surface of the seal ring 75 comes into close contact with the inner surface of the spouting cylinder 69, thereby ensuring sealability when the opening 67 for pouring out the content liquid is formed.

[0101] The sealing flange 77 is provided to facilitate turning for opening and closing the hinge lid 55.

[0102] Since the content liquid is poured out from the spouting cylinder 69 by opening the hinge lid 55 in this hinge cap, the upper end of the spouting cylinder 69 expands a little outward like a trumpet.

[0103] The upper end part of this spouting cylinder 69, especially a part on a side opposite to the hinge band 53 is a spout X. That is, since the opened hinge lid 55 is existent on the side where the hinge band 53 is existent, the content liquid is poured out to the side opposite to the side where the hinge band 53 is existent.

[0104] As understood from the above explanation, in this hinge cap, the above-described rough surface 100 is formed in a part which becomes at least the spout X of the upper end of the spouting cylinder 69.

[0105] The rough surface 100 may extend downward on the inner surface of the spouting cylinder 69, preferably not to a part in close contact with the seal ring 75 of the above-described hinge lid 55. When the rough surface 100 extends up to this part, sealability may deteriorate.

[0106] In FIG. 5 and FIG. 6, the hinge lid 55 is used as a member that ensures sealability after the opening 67 is formed. There is a cap having a structure that a screw lid is used in place of the hinge lid 55. That is, the screw lid is attached to the cap body 1 detachably by screw mating. Since all the periphery of the upper end of the spouting cylinder 69 becomes the spout X in this case, the rough surface 100 is formed at all the periphery.

[0107] In the above example, a plastic material forming the plastic bottle having the mouth portion 1 is not particularly limited and various thermoplastic resins, for example, olefin-based resins such as polyethylene and polypropylene and polyester resins typified by polyethylene terephthalate (PET) may be used like known plastic bottles. Since the upper end surface of the mouth portion 1 of this bottle becomes the spout X and the rough surface 100 composed of an irregular surface is formed on this part, a polyester resin is most preferred from the viewpoints of the shape stability and strength of the irregular surface 100.

[0108] When the irregular surface 100 is formed on the spout X which is on the cap side, this bottle may be made of glass or metal.

[0109] Further, a plastic material forming the caps 3 and 50 is not particularly limited and various thermoplastic resins, for example, olefin-based resins such as polyethylene and polypropylene may be used like known plastic caps.

[0110] When the rough surface 100 is formed on the spout X which is on the bottle side, this cap may be a screw cap made of metal.

[0111] Further, the liner material 13 formed on the cap 3 is formed from a known elastic material, for example, an ethylene-propylene copolymer elastomer or thermoplastic elastomer such as styrene-based elastomer.

[0112] To form the above-described rough surface 100 on the spout X of the mouth portion 1 of the above-described bottle or the spouts X of the caps 3 and 50, a predetermined stamper is pressed against this spout X to form predetermined irregularities and then fluorine plasma etching is carried out.

[0113] As shown in FIG. 7, this plasma etching may be carried out by fixing one electrode 200 to the lower part (upper part of the container mouth portion 1 or the upper part of the spouting cylinder 69) of the spout X, opposing the other electrode 201 to the above electrode 200 in such a manner that the spout X is interposed between these electrodes and applying a high-frequency electric field while a fluorine-containing gas is blown into a space between the electrodes

[0114] In FIGS. 4 to 6, the plastic molded body of the present invention is applied to the bottles and the caps. The present invention is not limited to these as a matter of course and may be applied to, for example, a spout which is used as a spouting tool and attached to a bag-like container.

[0115] Further, to form the rough surface 100 on the above-described bottles and caps, the bottle and the cap are molded by predetermined means in advance and the rough surface 100 is formed at a predetermined site by transfer using the above-described stamper.

[0116] The shapes of the irregularities on the rough surface 100 are arbitrary as long as they are designed to ensure that a liquid flows over the irregularities.

[0117] Since the plastic molded body of the present invention maintains excellent liquid repellency for a long period of time and has a rough surface which exhibits the same levels of drainability and drop-off properties as the initial levels even when it is brought into contact with a liquid repeatedly, it is effectively applied to a package material such as a cap or container. By forming the above-described rough surface 100 on the spout, it can discharge a liquid without dripping. When the above-described rough surface 100 is formed on the entire inner surface of the container, a viscous paste-like product typified by ketchup or mayonnaise can be discharged smoothly and completely without leaving it in the container.

EXAMPLES

[0118] The following examples are provided to explain the excellent characteristic properties of the present invention.

(1) Substrate;

[0119] * material: low-density polyethylene

[0120] Grade: LJ8041 (Japan Polyethylene Corporation) [0121] Size: 58 mm (length)58 mm (width)3 mm (thickness)

(2) Stamper;

* Production Method

[0122] * Primary irregularity stamper

[0123] A master was produced by photolithography to obtain a stamper having primary irregularities engraved by Ni electroforming.

[0124] Primary irregularities

[0125] s=0.2 (s=20 m, d=30 m, pitch=100 m)

Secondary Irregularity Stamper

[0126] The master produced by Cu electroforming was wet etched to form a rough surface so as to obtain a stamper having secondary irregularities engraved by Ni electroforming.

Secondary Irregularities

[0127] Ra/RSm=26410.sup.3 [0128] (Ra=933 nm, RSm=3.5 m)

[0129] Fractal stamper having primary irregularities+secondary irregularities

[0130] Shot blast was made on the above primary irregularity stamper to obtain a stamper having secondary irregularities engraved on the primary irregularities.

Primary Irregularities

[0131] s=0.2 (s=20 m, d=30 m, pitch=100 m)

Secondary Irregularities

[0132] Ra/RSm=9210.sup.3 [0133] (Ra=305 nm, RSm=3.3 m)

(3) Transfer Molding;

[0134] The stamper was heated at 240 C. by infrared radiation heating with a halogen lamp and pressed against the substrate for 1 second and then the substrate was cooled to transfer mold primary irregularities and secondary irregularities.

(4) Carbon Fluoride Plasma Treatment

[0135] * Plasma device

[0136] Discharge system: surface wave plasma

[0137] Power source: 1500 W@2.45 GHz

[0138] Treatment conditions

[0139] Degree of vacuum: 4 Pa

[0140] Raw material gas: CF.sub.4 100 sccm

[0141] Plasma irradiation time: 20 seconds, 200 seconds

(5) Evaluation of Performance

(5-1) Evaluation of Irregular Shape

[0142] Measurement method

[0143] For the transferred surface of the substrate, primary irregularities and secondary irregularities were measured with a white light interferometer, and third irregularities were measured with an atomic force microscope (AFM) to calculate the area ratio s, arithmetic average roughness Ra and average length RSm. [0144] Measurement conditions of white light interferometer

[0145] Measurement instrument: New View 7300 of ZYGO Corporation

[0146] 50-times objective lens

[0147] 2.0-times eyepiece lens

[0148] Long wavelength cut-off value c=13.846155 m

[0149] Short wavelength cut-off value s=346.155 nm [0150] Measurement conditions of AFM

[0151] Measurement instrument: Nano Scope III of Veeco Instruments Inc.

[0152] Long wavelength cut-off value c=0.0824 m

(5-2) Evaluation of Fluorine Atom Content

[0153] * Measurement method

[0154] The wide-band spectrum of the surface of the substrate was analyzed by using an X-ray photoelectron spectroscope to measure the amounts of elements existent on the surface so as to calculate the ratio (F/C) of the fluorine atom and the carbon atom. [0155] Measurement instrument [0156] K-Alpha of Thermo Fisher Scientific Inc.

(5-3) Evaluation of Liquid-Repellency-Drop-Off Properties

[0157] * Test method

[0158] 4 L of a real liquid was dropped on the surface of the substrate to take a picture of a droplet shape from the side. The contact angle was measured by image analysis.

[0159] The surface of the substrate was gradually inclined to take an inclination angle when the droplet dropped off as a drop-off angle.

Real liquid

[0160] Water

[0161] Soy sauce

[0162] Sauce

[0163] cooking oil [0164] measurement instrument: Drop Master 700 of Kyowa Interface Science Co., Ltd. [0165] evaluation criterion

[0166] When the contact angle is 130 or more, it is judged that the molded body has liquid repellency. When the drop-off angle is 20 or less, it is judged that the molded body has drop-off properties.

(5-4) Evaluation of Liquid Repellent Durability

[0167] * Test method

[0168] A 40 L droplet of the real liquid was dropped on the substrate inclined at 25 an arbitrary number of times to contaminate the surface of the substrate.

[0169] The contact angle of the real liquid with the surface of the contaminated substrate was measured (amount of a droplet: 4 L).

Real liquid

[0170] Sauce

[0171] Cooking oil [0172] Measurement instrument: manufactured by Kyowa Interface Science Co., Ltd. [0173] Evaluation criterion

[0174] By comparing the contact angle 0 when the number of dropping times is 0 and the contact angle 100 when the number of dropping times is 100 from the relationship between the number of dropping times and the contact angle, when 100/00.9, it is judged that the molded body has liquid repellent durability.

[0175] The evaluation results are shown in Table 1.

EXPLANATION OF REFERENCE NUMERALS

[0176] 100: rough surface [0177] 160: primary irregularities [0178] 160a: concave portion [0179] 160b: convex portion [0180] 165: secondary irregularities [0181] 170: droplet